Research progress of flexible magnetic films and devices

Yang Hua-Li; Xie Ya-Li; Lu Zeng-Xing; Wang Zhi-Ming; Li Run-Wei

doi:10.7498/aps.71.20212354

Abstract

With the rise of the internet of things, humanoid robots, and mobile healthcare services, etc., flexible electronic materials and devices have received extensive attention. Sensors and memories based on magnetic materials are important components of electronic devices. With the development of flexible film material preparation technology, one has prepared high-quality flexible and even stretchable magnetic metal and oxide films, which exhibit not only greater deformation capability, but also new physical effects and responses. Most recent studies show that flexible magnetoelectronic devices are advantageous in non-contact sensing, highly sensitive strain detection, and super-resolution tactile sensing, showing their broad application prospects. In this work, the research progress of this emerging field is reviewed from the aspects of the preparation of flexible magnetic materials, the regulation of physical properties and the applications of devices, and the future development trend is also presented.

Keywords:

Authors and contacts

Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Materials Technology and Engineering, Chinese Acedemy of Sciences, Ningbo 315201, China

Corresponding author: Li Run-Wei, runweili@nimte.ac.cn

Funds: Project supported by the Key Program of the National Natural Science Foundation of China (Grant No. 51931011) and the K.C. Wong Education Foundation (Grant No. GJTD-2020-11).

FullText HTML : translate this paragraph

References

[1]	Bauer S, Bauer-Gogonea S, Graz I, Kaltenbrunner M, Keplinger C, Schwödiauer R 2014 Adv. Mater. 26 149 Google Scholar
[2]	Zhang F, Zang Y, Huang D, Di C A, Zhu D 2015 Nat. Commun. 6 8356 Google Scholar
[3]	Kim D H, Lu N, Ma R, Kim Y S, Kim R H, Wang S, Wu J, Won Sang M, Tao H, Islam A, Yu Ki J, Kim T i, Chowdhury R, Ying M, Xu L, Li M, Chung H J, Keum H, McCormick M, Liu P, Zhang Y W, Omenetto Fiorenzo G, Huang Y, Coleman T, Rogers John A 2011 Science 333 838 Google Scholar
[4]	Someya T, Bauer S, Kaltenbrunner M 2017 MRS Bull. 42 124 Google Scholar
[5]	Bartolozzi C, Natale L, Nori F, Metta G 2016 Nat. Mater. 15 921 Google Scholar
[6]	Sundaram S, Kellnhofer P, Li Y, Zhu J Y, Torralba A, Matusik W 2019 Nature 569 698 Google Scholar
[7]	Guo Q, Wang Z, Xu X, Jiang Y 2017 Chin. J. Engn. 39 1775 Google Scholar
[8]	Hua Q, Sun J, Liu H, Bao R, Yu R, Zhai J, Pan C, Wang Z L 2018 Nat. Commun. 9 244 Google Scholar
[9]	Li F, Li S, Cao J, Liu Y, Shang J, Li R 2020 Mater. Rev. 34 1059 Google Scholar
[10]	Parkin S, Xin J, Kaiser C, Panchula A, Roche K, Samant M 2003 Proc. IEEE 91 661 Google Scholar
[11]	Thiele J U, Maat S, Fullerton E E 2003 Appl. Phys. Lett. 82 2859 Google Scholar
[12]	Fan X, Kim S, Kou X, Kolodzey J, Zhang H, Xiao J Q 2010 Appl. Phys. Lett. 97 212501 Google Scholar
[13]	Dai G, Zhan Q, Liu Y, Yang H, Zhang X, Chen B, Li R W 2012 Appl. Phys. Lett. 100 122407 Google Scholar
[14]	Hertel R 2013 Spin 3 1340009 Google Scholar
[15]	Hirai T, Sepehri Amin H, Hasegawa K, Koyama T, Iguchi R, Ohkubo T, Chiba D, Uchida K I 2021 Appl. Phys. Lett. 118 022403 Google Scholar
[16]	Xu Y, Liu X, Guo W 2014 Nanoscale 6 12929 Google Scholar
[17]	Chen Y F, McCord J, Freudenberger J, Kaltofen R, Schmidt O G 2009 J. Appl. Phys. 105 07c302 Google Scholar
[18]	Yen M, Lai Y H, Kuo C Y, Chen C T, Chang C F, Chu Y H 2020 Adv. Funct. Mater. 30 2004597 Google Scholar
[19]	Qiao X Y, Wen X C, Wang B M, Bai Y H, Zhan Q F, Xu X H, Li R W 2017 Appl. Phys. Lett. 111 132405 Google Scholar
[20]	Lu Z, Yang Y, Wen L, Feng J, Lao B, Zheng X, Li S, Zhao K, Cao B, Ren Z, Song D, Du H, Guo Y, Zhong Z, Hao X, Wang Z, Li R W 2021 npj Flex. Electron. 6 9 Google Scholar
[21]	Li H, Zhan Q, Liu Y, Liu L, Yang H, Zuo Z, Shang T, Wang B, Li R W 2016 Acs Nano 10 4403 Google Scholar
[22]	Dai G, Xing X, Shen Y, Deng X 2019 J. Phys. D:Appl. Phys. 53 055001 Google Scholar
[23]	Ota S, Ando A, Chiba D 2018 Nat. Electron. 1 124 Google Scholar
[24]	Ge J, Wang X, Drack M, Volkov O, Liang M, Cañón Bermúdez G S, Illing R, Wang C, Zhou S, Fassbender J, Kaltenbrunner M, Makarov D 2019 Nat. Commun. 10 4405 Google Scholar
[25]	Wu Y Z, Liu Y W, Zhou Y L, Man Q K, Hu C, Asghar W, Li F L, Yu Z, Shang J, Liu G, Liao M Y, Li R W 2018 Sci. Robot. 3 eaat0429 Google Scholar
[26]	Almansouri A S, Alsharif N A, Khan M A, Swanepoel L, Kaidarova A, Salama K N, Kosel J 2019 Adv. Mater. Technol. 4 1900493 Google Scholar
[27]	Bermudez G S C, Fuchs H, Bischoff L, Fassbender J, Makarov D 2018 Nat. Electron. 1 589 Google Scholar
[28]	Zhang X S, Zhan Q F, Dai G H, Liu Y W, Zuo Z H, Yang H L, Chen B, Li R W 2013 J. Appl. Phys. 113 17A901 Google Scholar
[29]	Cao D, Wang Z, Pan L, Feng H, Cheng X, Zhu Z, Wang J, Liu Q, Han G 2016 Appl. Phys. A-Mater. 122 938 Google Scholar
[30]	Dai G H, Zhan Q F, Yang H L, Liu Y W, Zhang X S, Zuo Z H, Chen B, Li R W 2013 J. Appl. Phys. 114 173913 Google Scholar
[31]	Tang Z H, Wang B M, Yang H L, Xu X Y, Liu Y W, Sun D D, Xia L X, Zhan Q F, Chen B, Tang M H, Zhou Y C, Wang J L, Li R W 2014 Appl. Phys. Lett. 105 103504 Google Scholar
[32]	Liu Y W, Wang B M, Zhan Q F, Tang Z H, Yang H L, Liu G, Zuo Z H, Zhang X S, Xie Y L, Zhu X J, Chen B, Wang J L, Li R W 2014 Sci. Rep. 4 6615 Google Scholar
[33]	Merabtine S, Zighem F, Faurie D, Garcia-Sanchez A, Lupo P, Adeyeye A O 2018 Nano Lett. 18 3199 Google Scholar
[34]	Gao G Q, Jin C, Zheng W C, Pang X, Zheng D X, Bai H L 2018 Epl 123 17002 Google Scholar
[35]	Ha T D, Chen J W, Yen M, Lai Y H, Wang B Y, Chin Y Y, Wu W B, Lin H J, Juang J Y, Chu Y H 2020 ACS Appl. Mater. Inter. 12 46874 Google Scholar
[36]	Asai R, Ota S, Namazu T, Takenobu T, Koyama T, Chiba D 2016 J. Appl. Phys. 120 083906 Google Scholar
[37]	Ota S, Hibino Y, Bang D, Awano H, Kozeki T, Akamine H, Fujii T, Namazu T, Takenobu T, Koyama T, Chiba D 2016 Appl. Phys. Express 9 043004 Google Scholar
[38]	Zhao S, Zhou Z, Li C, Peng B, Hu Z, Liu M 2018 Acs Nano 12 7167 Google Scholar
[39]	Matsumoto H, Ota S, Koyama T, Chiba D 2021 Appl. Phys. Lett. 118 022406 Google Scholar
[40]	Wen X C, Wang B M, Sheng P, Hu S, Yang H L, Pei K, Zhan Q F, Xia W X, Xu H, Li R W 2017 Appl. Phys. Lett. 111 142403 Google Scholar
[41]	Chen X Y, Wang B M, Wen X C, Sheng P, Pravarthana D, Yang H L, Xie Y L, Liu H G, Xu X H, Lib R W 2020 J. Magn. Magn. Mater. 505 166750 Google Scholar
[42]	Liu J, Chen J, Zhang Y, Fu S, Chai G, Cao C, Zhu X, Guo Y, Cheng W, Jiang D, Zhao Z, Zhan Q 2021 ACS Appl. Mater. Inter. 13 29975 Google Scholar
[43]	Zhu Q, Tang R, Peng F, Xu S, Liang G, Zhao R, Fang Y, You L, Su X 2021 Phys. Rev. Appl. 16 054006 Google Scholar
[44]	Yu Y, Zhan Q F, Wei J W, Wang J B, Dai G H, Zuo Z H, Zhang X S, Liu Y W, Yang H L, Zhang Y, Xie S H, Wang B M, Li R W 2015 Appl. Phys. Lett. 106 162405 Google Scholar
[45]	Liu W, Ma R, Liu M, Wang H 2018 ACS Appl. Mater. Inter. 10 32331 Google Scholar
[46]	Liu W, Liu M, Ma R, Zhang R, Zhang W, Yu D, Wang Q, Wang J, Wang H 2018 Adv. Funct. Mater. 28 1705928 Google Scholar
[47]	Peng B, Xie Q Y, Zhang W L, Zhong Z Y 2007 J. Appl. Phys. 101 09C511 Google Scholar
[48]	Karboul-Trojet W, Faurie D, Aït-Yahiatène E, Roussigné Y, Mazaleyrat F, Chérif S M 2012 J. Appl. Phys. 111 07A926 Google Scholar
[49]	Zhang J, Lee W K, Tu R, Rhee D, Zhao R, Wang X, Liu X, Hu X, Zhang X, Odom T W, Yan M 2021 Nano Lett. 21 5430 Google Scholar
[50]	Yang Q, Cheng Y, Li Y, Zhou Z, Liang J, Zhao X, Hu Z, Peng R, Yang H, Liu M 2020 Adv. Electron. Mater. 6 2000246 Google Scholar
[51]	Meiklejohn W H, Bean C P 1957 Phys. Rev. 105 904 Google Scholar
[52]	Nogués J, Schuller I K 1999 J. Magn. Magn. Mater. 192 203 Google Scholar
[53]	Ali M, Adie P, Marrows C H, Greig D, Hickey B J, Stamps R L 2007 Nat. Mater. 6 70 Google Scholar
[54]	Salazar-Alvarez G, Sort J, Suriñach S, Baró M D, Nogués J 2007 J. Am. Chem. Soc. 129 9102 Google Scholar
[55]	Cain W C, Kryder M H 1990 J. Appl. Phys. 67 5722 Google Scholar
[56]	Zhang Y, Zhan Q F, Rong X, Li H H, Zuo Z H, Liu Y W, Wang B M, Li R W 2016 IEEE Trans. Magn. 52 2529722 Google Scholar
[57]	Zhang X S, Zhan Q F, Dai G H, Liu Y W, Zuo Z H, Yang H L, Chen B, Li R W 2013 Appl. Phys. Lett. 102 022412 Google Scholar
[58]	Sheng P, Xie Y L, Bai Y H, Wang B M, Zhang L, Wen X C, Yang H L, Chen X Y, Li X G, Li R W 2019 Appl. Phys. Lett. 115 242403 Google Scholar
[59]	Zhang Z, Liu E, Zhang W, Wong P K J, Xu Z, Hu F, Li X, Tang J, Wee A T S, Xu F 2019 ACS Appl. Mater. Inter. 11 8258 Google Scholar
[60]	Shi X, Mi W, Zhang Q, Zhang X 2020 Appl. Phys. Lett. 117 132401 Google Scholar
[61]	Huang J, Wang H, Wang X, Gao X, Liu J, Wang H 2020 ACS Appl. Mater. Inter. 12 39920 Google Scholar
[62]	Jin C, Zhu Y, Han W, Liu Q, Hu S, Ji Y, Xu Z, Hu S, Ye M, Chen L 2020 Appl. Phys. Lett. 117 252902 Google Scholar
[63]	Thai Duy H, Yen M, Lai Y H, Kuo C Y, Chen C T, Tanaka A, Tsai L Z, Zhao Y F, Duan C G, Lee S F, Chang C F, Juang J Y, Chu Y H 2020 Nanoscale 12 3284 Google Scholar
[64]	Du D, Manzo S, Zhang C, Saraswat V, Genser K T, Rabe K M, Voyles P M, Arnold M S, Kawasaki J K 2021 Nat. Commun. 12 2494 Google Scholar
[65]	Ling Y, Hu Y, Wang H, Niu B, Chen J, Liu R, Yuan Y, Wang G, Wu D, Xu M, Han Z, Du J, Xu Q 2021 ACS Appl. Mater. Inter. 13 24285 Google Scholar
[66]	Hong S S, Gu M, Verma M, Harbola V, Wang B Y, Lu D, Vailionis A, Hikita Y, Pentcheva R, Rondinelli J M, Hwang H Y 2020 Science 368 71 Google Scholar
[67]	Liu E, Fache T, Cespedes-Berrocal D, Zhang Z, Petit-Watelot S, Mangin S, Xu F, Rojas-Sanchez J C 2019 Phys. Rev. Appl. 12 044074 Google Scholar
[68]	Wong G D H, Ang C C I, Gan W, Law W C, Xu Z, Xu F, Seet C S, Lew W S 2021 Appl. Phys. Lett. 119 042402 Google Scholar
[69]	Wong G D H, Xu Z, Gan W, Ang C C I, Law W C, Tang J, Zhang W, Wong P K J, Yu X, Xu F, Wee A T S, Seet C S, Lew W S 2021 Acs Nano 15 8319 Google Scholar
[70]	Faurie D, Zighem F, Garcia-Sanchez A, Lupo P, Adeyeye A O 2017 Appl. Phys. Lett. 110 091904 Google Scholar
[71]	Melzer M, Lin G G, Makarov D, Schmidt O G 2012 Adv. Mater. 24 6468 Google Scholar
[72]	Melzer M, Kaltenbrunner M, Makarov D, Karnaushenko D, Karnaushenko D, Sekitani T, Someya T, Schmidt O G 2015 Nat. Commun. 6 6080 Google Scholar
[73]	Hicks C W, Brodsky D O, Yelland E A, Gibbs A S, Bruin J A N, Barber M E, Edkins S D, Nishimura K, Yonezawa S, Maeno Y, Mackenzie A P 2014 Science 344 283 Google Scholar
[74]	Mun J H, Lee H, Kim J U, Kang M, Hong A R, Jang H S, Han K S, Kim D H 2020 J. Magn. Magn. Mater. 511 166968 Google Scholar
[75]	Zhang S, Zhan Q, Yu Y, Liu L, Li H, Yang H, Xie Y, Wang B, Xie S, Li R W 2016 Appl. Phys. Lett. 108 102409 Google Scholar
[76]	Li J C, Zhan Q F, Zhang S L, Wei J W, Wang J B, Pan M J, Xie Y L, Yang H L, Zhou Z, Xie S H, Wang B M, Li R W 2017 Sci. Rep. 7 2837 Google Scholar
[77]	Zhao J P, Guo Q H, Yin H Z, Zou J T, Zhao Z J, Cheng W J, Jiang D M, Zhan Q F 2020 Chin. Phys. B 29 117501 Google Scholar
[78]	Guo Q H, Cheng W J, Zhan Q F 2021 J. Mag. Mater. Dev. 52 6 Google Scholar
[79]	Wang Z, Zhou Z, Cheng W, Jiang D, Zhan Q 2020 J. Magn. Magn. Mater. 513 167126 Google Scholar
[80]	Ji D, Cai S, Paudel T R, Sun H, Zhang C, Han L, Wei Y, Zang Y, Gu M, Zhang Y, Gao W, Huyan H, Guo W, Wu D, Gu Z, Tsymbal E Y, Wang P, Nie Y, Pan X 2019 Nature 570 87 Google Scholar
[81]	Lu D, Baek D J, Hong S S, Kourkoutis L F, Hikita Y, Hwang H Y 2016 Nat. Mater. 15 1255 Google Scholar
[82]	Jiang J, Bitla Y, Huang C W, et al. 2017 Sci. Adv. 3 e1700121 Google Scholar
[83]	Dong G H, Li S Z, Yao M T, Zhou Z Y, Zhang Y Q, Han X, Luo Z L, Yao J X, Peng B, Hu Z Q, Huang H B, Jia T T, Li J Y, Ren W, Ye Z G, Ding X D, Sun J, Nan C W, Chen L Q, Li J, Liu M 2019 Science 366 475 Google Scholar
[84]	Chu Y H 2017 npj Quantum Mater. 2 67 Google Scholar
[85]	Bitla Y, Chu Y H 2017 FlatChem 3 26 Google Scholar
[86]	Liu H J, Wang C K, Su D, Amrillah T, Hsieh Y H, Wu K H, Chen Y C, Juang J Y, Eng L M, Jen S U, Chu Y H 2017 ACS Appl. Mater. Interf. 9 7297 Google Scholar
[87]	Huang J, Wang H, Sun X, Zhang X, Wang H 2018 ACS Appl. Mater. Interf. 10 42698 Google Scholar
[88]	Liu J, Feng Y, Tang R, Zhao R, Gao J, Shi D, Yang H 2018 Adv. Electron. Mater. 4 1700522 Google Scholar
[89]	Fan J, Xie Y, Qian F, Ji Y, Hu D, Tang R, Liu W, Zhang L, Tong W, Ma C, Yang H 2019 J. Alloys Compd. 806 753 Google Scholar
[90]	Hou W, Zhou Z, Zhang L, Zhao S, Peng B, Hu Z, Ren W, Ye Z G, Jiang Z D, Liu M 2019 ACS Appl. Mater. Interf. 11 21727 Google Scholar
[91]	Li C I, Lin J C, Liu H J, Chu M W, Chen H W, Ma C H, Tsai C Y, Huang H W, Lin H J, Liu H L, Chiu P W, Chu Y H 2016 Chem. Mater. 28 3914 Google Scholar
[92]	Kum H S, Lee H, Kim S, Lindemann S, Kong W, Qiao K, Chen P, Irwin J, Lee J H, Xie S, Subramanian S, Shim J, Bae S H, Choi C, Ranno L, Seo S, Lee S, Bauer J, Li H, Lee K, Robinson J A, Ross C A, Schlom D G, Rzchowski M S, Eom C B, Kim J 2020 Nature 578 75 Google Scholar
[93]	Zhang Y, Shen L, Liu M, Li X, Lu X, Lu L, Ma C, You C, Chen A, Huang C, Chen L, Alexe M, Jia C L 2017 Acs Nano 11 8002 Google Scholar
[94]	Chen Z, Li F, Huang Q W, Liu F, Wang F F, Ringer S P, Luo L S, Zhang S J, Chen L Q, Liao X Z 2020 Sci. Adv. 6 eabc7156 Google Scholar
[95]	Lu Z, Liu J, Feng J, Zheng X, Yang L H, Ge C, Jin K J, Wang Z, Li R W 2020 APL Mater. 8 051105 Google Scholar
[96]	Shrestha S, Coile M, Zhu M, Souri M, Kim J, Pandey R, Brill J W, Hwang J, Kim J W, Seo A 2020 ACS Appl. Nano Mater. 3 6310 Google Scholar
[97]	An F, Qu K, Zhong G, Dong Y, Ming W, Zi M, Liu Z, Wang Y, Qi B, Ding Z, Xu J, Luo Z, Gao X, Xie S, Gao P, Li J 2020 Adv. Funct. Mater. 30 2003495 Google Scholar
[98]	Loong L M, Lee W, Qiu X, Yang P, Kawai H, Saeys M, Ahn J H, Yang H 2016 Adv. Mater. 28 4983 Google Scholar
[99]	Melzer M, Makarov D, Schmidt O G 2020 J. Phys. D 53 083002 Google Scholar
[100]	Perez N, Melzer M, Makarov D, Ueberschaer O, Ecke R, Schulz S E, Schmidt O G 2015 Appl. Phys. Lett. 106 153501 Google Scholar
[101]	Wu W, Zhang L, Cai J, Fang B, Luo J, Zeng Z 2019 Appl. Phys. Lett. 115 052401 Google Scholar
[102]	Chen J Y, Wang J P 2018 Nat. Electron. 1 96 Google Scholar
[103]	Ota S, Ando A, Sekitani T, Koyama T, Chiba D 2019 Appl. Phys. Lett. 115 202401 Google Scholar
[104]	Yan Y C, Hu Z, Yang Z B, Yuan W Z, Song C Y, Pan J, Shen Y J 2021 Sci. Robot. 6 abc8801 Google Scholar
[105]	Bhatti S, Ma C, Liu X, Piramanayagam S N 2019 Adv. Electron. Mater. 5 1800467 Google Scholar
[106]	Li S, Cao P, Li F, Asghar W, Wu Y, Xiao H, Liu Y, Zhou Y, Yang H, Zhang Y, Shang J, Makarov D, Li R-W 2022 Nano Energy 92 106754 Google Scholar
[107]	Doan Nguyen B, Zheng Y, Becerra L, Marangolo M, Almanza M, LoBue M 2021 Phys. Rev. Appl. 15 064045 Google Scholar
[108]	Zhao Y, Peng R, Guo Y, Liu Z, Dong Y, Zhao S, Li Y, Dong G, Hu Y, Zhang J, Peng Y, Yang T, Tian B, Zhao Y, Zhou Z, Jiang Z, Luo Z, Liu M 2021 Adv. Funct. Mater. 31 2009376 Google Scholar
[109]	Zheng W C, Zheng D X, Wang Y C, Li D, Jin C, Bai H L 2019 J. Magn. Magn. Mater. 481 227 Google Scholar
[110]	Wang Z G, Wang X J, Li M H, Gao Y, Hu Z Q, Nan T X, Liang X F, Chen H H, Yang J, Cash S, Sun N X 2016 Adv. Mater. 28 9370 Google Scholar
[111]	Parkin S S P, Roche K P, Suzuki T 1992 Jpn. J. Appl. Phys., Part 2 31 L1246 Google Scholar
[112]	Chen Y F, Mei Y F, Kaltofen R, et al. 2008 Adv. Mater. 20 3224 Google Scholar
[113]	Guo M, Yang C, Gao D, Li Q, Zhang A, Feng J, Yang H, Tao R, Fan Z, Zeng M, Zhou G, Lu X, Liu J M 2020 J. Mater. Sci. Technol. 44 42 Google Scholar
[114]	Luby Š, Anwarzai B, Áč V, Majkova E, Senderák R 2012 Vacuum 86 718 Google Scholar
[115]	Liu L P, Zhan Q F, Yang H L, Li H H, Zhang S L, Liu Y W, Wang B M, Tan X H, Li R W 2016 AIP Adv. 6 035206 Google Scholar
[116]	Fuji Y, Kaji S, Hara M, Higashi Y, Hori A, Okamoto K, Nagata T, Baba S, Yuzawa A, Otsu K, Masunishi K, Ono T, Fukuzawa H 2018 Appl. Phys. Lett. 112 062405 Google Scholar
[117]	Fuji Y, Higashi Y, Kaji S, Masunishi K, Nagata T, Yuzawa A, Okamoto K, Baba S, Ono T, Hara M 2019 Jpn. J. Appl. Phys. 58 SD0802 Google Scholar
[118]	Matsumoto H, Ota S, Ando A, Chiba D 2019 Appl. Phys. Lett. 114 132401 Google Scholar
[119]	Chen X, Mi W 2021 J. Mater. Chem. C 9 9400 Google Scholar
[120]	Boutry Clementine M, Negre M, Jorda M, Vardoulis O, Chortos A, Khatib O, Bao Z 2018 Sci. Robot. 3 eaau6914 Google Scholar
[121]	Viry L, Levi A, Totaro M, Mondini A, Mattoli V, Mazzolai B, Beccai L 2014 Adv. Mater. 26 2659 Google Scholar

Cited By

图 1 柔性磁性薄膜和器件的主要研究内容: 包括柔性磁性薄膜制备方法(直接生长法^[19]、牺牲层+转移法^[20]、预应力生长法^[21]等)、应力调控规律(对磁各向异性、磁共振、磁畴^[22]等的调控)、柔性磁性功能器件设计(磁传感器^[21]、应力传感器^[23]、触觉传感器^[24]等)、器件应用(人机交互^[27]、电子皮肤^[25]、生理信号监测^[26]等)

Figure 1. Research topics of flexible magnetic films and devices. The topics include the fabrication methods (such as direct growth method^[19], sacrifice layer and transfer method^[20], pre-strained growth method^[21], etc.); the strain modulation properties (of magnetic anisotropy, magnetic resonance, and magnetic domain^[22], etc.); the design of flexible functional devices (such as magnetic sensors^[21], stress sensors^[23], and tactile sensors^[24], etc.); as well as its applications (in human-machine interface^[27], electronic skin^[25], and bio signal monitoring^[26], etc.).

DownLoad: Full-Size Img PowerPoint

图 2 不同测试构型下应变对FeGa薄膜磁滞回线的调控规律(1 Oe = 10³/(4π) A/m)^[13]　(a)磁场H平行于易磁化轴K_u, 拉应变+ε垂直于易磁化轴K_u; (b) H垂直于K_u, 拉应变+ε平行于 K_u; (c) H平行于K_u, 压应变–ε垂直于 K_u; (d) H垂直于K_u, 压应变–ε平行于K_u

Figure 2. Stress-regulation of the magnetic hysteresis loops of FeGa films under various configurations^[13]: (a) The magnetic field (H) in parallel with the easy axis (K_u ) and tensile strain (+ε) perpendicular to K_u; (b) H perpendicular to K_u and +ε in parallel with K_u ; (c) H in parallel with K_u and compressive strain (–ε) in parallel with K_u; (d) H perpendicular to K_u and –ε in parallel with K_u.

DownLoad: Full-Size Img PowerPoint

图 3 应力对CoFeB薄膜磁弹各向异性的调控规律^[40]　(a)薄膜在不同磁场下的各向异性磁电阻测量曲线; (b)不同磁场下θ_H和θ_M的角度关联曲线; (c)不同应力下薄膜的归一化扭矩曲线; (d)磁弹各向异性常数随应力的依赖关系

Figure 3. Stress-modulation of the magnetic anisotropy of CoFeB films^[40]: (a) The anisotropic magnetoresistance curves under various magnetic field strength; (b) correlation of θ_H and θ_M at different magnetic fields; (c) normalized torque curves of the film at various stress; (d) dependence of the magnetoelastic anisotropy constant on external stress.

DownLoad: Full-Size Img PowerPoint

图 4 应变对FeGa^[30], Fe, Co, Ni^[41], CoFeB^[40], TbFeCo^[37], Pd/Co/Pd^[39], 褶皱结构CoFeB^[42], BaM^[43]薄膜磁各向异性能的调控效果. 其中, 褶皱结构CoFeB的磁各向异性能由文献[42]估算. 虚线代表普通块体金属的断裂拉伸应变极限

Figure 4. Regulation of the magnetic anisotropy by external strain in FeGa^[30], Fe, Co, Ni^[41], CoFeB^[40], TbFeCo^[37], Pd/Co/Pd^[39], wrinkled CoFeB^[42], and BaM^[43]. The magnetic anisotropy of wrinkled CoFeB was estimated from Ref. [42]. The vertical dashed line stands for the maximum tensile strain without crack in bulk metals.

DownLoad: Full-Size Img PowerPoint

图 5 (a)不同应力状态下FeGa薄膜的磁畴结构^[22], 从左到右分别表示FeGa薄膜样品在凸模具上(未取下)、从凸模具上取下并展平、在凹模具上(未取下)、从凹模具上取下并展平时的磁畴结构; (b)通过电子束刻蚀控制Ni薄膜应力, 调控微区磁畴结构^[49], 从左到右分别表示样品制备过程、薄膜形貌、微区应力示意图、磁畴结构

Figure 5. (a) Magnetic domain structure of FeGa film with different stress configurations^[22] (from left to right): with FeGa film attached on a convex mold, removed from the convex mold and flattened, attach on a concave mold, removed from the concave mold and flattened; (b) modulation of the magnetic domain structure of Ni film with micro-patterned stress by E-beam lithography^[49]. The sample fabrication process, topography of the film, stress distribution, and magnetic domain structures are shown from left to right.

DownLoad: Full-Size Img PowerPoint

图 6 通过交换偏置效应表征应力对反铁磁性的调控规律示意图^[58]　(a)应力平行于初始钉扎方向时对反铁磁磁矩调控的两种状态; (b)应力不影响反铁磁磁矩取向时, 交换偏置异质结的磁滞回线特征; (c)应力改变反铁磁磁矩取向时, 交换偏置异质结的磁滞回线特征

Figure 6. Schematic diagram showing the stress modulation of antiferromagnetic films through the exchange bias effect^[58]: (a) Two possible antiferromagnetic configurations under the influence of external stress applied parallel to the initial pinning direction (IPD); (b) the corresponding hysteresis loop of exchange bias structure with the direction of the antiferromagnetic moment unchanged; (c) the corresponding hysteresis loop of exchange bias structure with the direction of the antiferromagnetic moment rotated by 90°.

DownLoad: Full-Size Img PowerPoint

图 7 应力对CoFeB/IrMn交换偏置效应的调控规律^[58]　(a), (b)不同应力下, 磁场沿着(a)和垂直于(b)钉扎方向时磁滞回线的变化; (c)磁场沿着钉扎方向和垂直于钉扎方向时, 剩磁比随应力的变化规律; (d)磁场垂直于钉扎方向时交换偏置场随应力的变化规律

Figure 7. Stress modulation of the exchange bias effect for the CoFeB/IrMnbilayers^[58]: (a), (b) Typical hysteresis loops under different stress measured at θ = 0° (a) and θ = 90° (b) with the initial pinning direction (IPD) set along the x direction; (c) temperature dependence of M_r/M_s measured at θ = 0° and 90°; (d) stress dependence of H_eb measured at θ = 90°.

DownLoad: Full-Size Img PowerPoint

图 8 磁各向异性可调控的柔性磁性薄膜制备方法^[30]　(a)薄膜的制备过程示意图; (b), (c)不同压应力下生长的薄膜沿着(b)和垂直于(c)压应力方向(y方向)的磁滞回线曲线

Figure 8. Preparation of flexible magnetic films with tunable magnetic anisotropy^[30]: (a) Schematic diagram of the preparation process; (b), (c) magnetic hysteresis loops with magnetic field applied along (b) and perpendicular to (c) the compressive stress direction (y direction).

DownLoad: Full-Size Img PowerPoint

图 9 应力稳定的柔性磁性薄膜制备方法^[19]　(a)薄膜的制备过程示意图; (b)所制备薄膜的矩形比随外加应力的变化关系(黑线为常规方法生长样品的对比数据)

Figure 9. Preparation of flexible magnetic films with stress-invariant magnetic anisotropy^[19]: (a) Schematic diagram of the fabrication process of CoFeB films with pre-induced magnetic anisotropy; (b) the strain dependence of M_r/M_s for CoFeB films grown with pre-induced magnetic anisotropy (data with films grown without pre-induced magnetic anisotropy are indicated as a comparison).

DownLoad: Full-Size Img PowerPoint

图 10 具有周期性“褶皱结构”的柔性磁性薄膜制备方法^[75]　(a)保持拉伸状态生长磁性薄膜; (b)在诱导出褶皱结构的衬底上生长磁性薄膜

Figure 10. Fabrication of flexible magnetic films with periodic wrinkled structures^[75]: (a) Schematic diagram of growing FeGa film on a pre-strained substrate; (b) schematic diagram of growing FeGa film on a periodic wrinkled substrate.

DownLoad: Full-Size Img PowerPoint

图 11 (a)云母晶体结构以及沿(001)方向的晶格俯视图; (b)部分基于云母衬底柔性氧化物薄膜工作总结^[84]

Figure 11. (a) Crystal structure of mica and its lattice structure in the (001) plane; (b) a summary of typical flexible oxide films grown on mica substrate^[84].

DownLoad: Full-Size Img PowerPoint

图 12 基于水溶性Sr₃Al₂O₆牺牲层法的柔性La_0.67Sr_0.33MnO₃薄膜制备^[95]　(a) Sr₃Al₂O₆和SrTiO₃的晶体结构示意图; (b)不同晶向Sr₃Al₂O₆与典型钙钛矿氧化物SrTiO₃的晶格匹配关系; (c)不同晶向柔性La_0.67Sr_0.33MnO₃薄膜的制备

Figure 12. Fabrication of flexible La_0.67Sr_0.33MnO₃ film based on Sr₃Al₂O₆ sacrifice layer^[95]: (a) Crystal structures of Sr₃Al₂O₆ and SrTiO₃; (b) schematic diagram of the lattice match relationship between Sr₃Al₂O₆ and SrTiO₃ along different crystal orientation; (c) schematic diagram of the preparation of flexible La_0.67Sr_0.33MnO₃ film with various crystal orientations.

DownLoad: Full-Size Img PowerPoint

图 13 基于水溶性Ca_3–_xSr_xAl₂O₆ (0≤x≤3) (CSAO)牺牲层法的柔性SrRuO₃薄膜性能(1 emu/cm³ = 10³ A/m) ^[20]　(a) SrRuO₃与不同牺牲层Sr₃Al₂O₆ (SAO)和CSAO的匹配关系, CSAO和SAO作为牺牲层得到的SRO分别为正交相和四方相; (b)两种牺牲层与晶向对SRO薄膜磁各向异性的调制

Figure 13. Magnetic properties of flexible SrRuO₃ films fabricated by using water soluble Ca_3–_xSr_xAl₂O₆ (0≤x≤3) (CSAO) as sacrifice layer^[20]: (a) Comparison of lattice constants between SrRuO₃ and different sacrifice layers of Sr₃Al₂O₆ (SAO) and CSAO, the obtained SrRuO₃ are of orthorhombic and tetragonal structure, respectively; (b) magnetic anisotropy of the obtained flexible SrRuO₃ films.

DownLoad: Full-Size Img PowerPoint

图 14 柔性巨磁电阻器件和性能^[72]　(a)褶皱结构的GMR器件; (b)光学形貌和扫描电镜下的表面形貌, 标尺分别为200 μm和100 μm; (c)器件的GMR曲线

Figure 14. Flexible giant magnetoresistance device and its property^[72]: (a) GMR device with wrinkled structure; (b) surface morphology under optical and SEM, the scale bars are 200 μm and 100 μm, respectively; (c) GMR curves of the wrinkled and flat device.

DownLoad: Full-Size Img PowerPoint

图 15 可拉伸自旋阀器件和性能^[21]　(a)器件结构示意图; (b)生长示意图; (c)可拉伸褶皱结构示意图; (d)拉伸状态下的GMR数值、磁灵敏度和电阻变化

Figure 15. Stretchable spin-valve device and its property^[21]: (a) Schematic diagram of the device; (b) the device fabrication setups; (c) schematic show of the periodic wrinkled device; (d) variation of the GMR ration, magnetic sensitivity, and resistance at different tensile strain.

DownLoad: Full-Size Img PowerPoint

图 16 可感受应力方向的GMR传感器^[23]　(a)器件结构示意图; (b)不同应变下, 器件磁电阻随着x方向磁场的变化; (c)不同应变下, 器件磁电阻随着y方向磁场的变化; (d)不同方向施加应变时, 电阻变化率随应变大小的变化规律

Figure 16. GMR sensor that can detect the stress direction^[23]: (a) Device structure; magnetoresistance at various stress with field along x (b) and y (c) direction; (d) resistivity change ratio as a function of strain at various strain directions.

DownLoad: Full-Size Img PowerPoint

图 17 基于GMR效应的双模式柔性传感器^[24]　(a)器件结构示意图; (b)器件的靠近-接触双模式传感原理; (c)器件在弯曲状态下的光学照片; (d)将传感器固定在木手指上用于传感; (e)当固定有传感器的木手指靠近、接触、远离贴附有磁体的花瓣时器件的电阻变化

Figure 17. GMR-based bimodal flexible sensor^[24]: (a) Schematic structure of the GMR-based bimodal flexible sensor; (b) mechanisms of the touchless (proximity) and tactile (pressure) sensing modes; (c) photograph of the sensor in bent state. (d) a photograph of the sensor wrapped around a wooden model finger; (e) change of the electrical resistance upon an interaction event where the finger bearing the sensor approaches, touches and retreats from the magnet-decorated flower petal.

DownLoad: Full-Size Img PowerPoint

图 18 基于巨磁阻抗效应的触觉传感器^[25]　(a)器件结构示意图; (b)器件的力敏特性; (c)将传感器的模拟信号转换成数字-频率信号的电路示意图; (d)外加压力作用下器件的数字-频率响应

Figure 18. Flexible tactile sensor based on the GMI effect^[25]: (a) Schematic illustration of the device structure; (b) relation between changes in impedance and applied pressures shows the sensitivity of the tactile sensor in the ultralow pressure range; (c) schematic diagram showing the circuit that converts analog signals recorded from the sensor into digital-frequency signals; (d) the digital-frequency response of the device changed with applied pressure.

DownLoad: Full-Size Img PowerPoint

表 1 部分磁性薄膜和器件的拉伸性能比较

Table 1. Stretchability of selected magnetic films and devices.

材料和器件制备方法		极限应变		文献
材料和器件制备方法		单轴	双轴	文献
金属与合金	PI上沉积的CoFeB薄膜	1.6%		[70]
	PEN上沉积的Co薄膜	2%	2%	[39]
	具有周期裂纹的自旋阀器件	29%		[71]
	具有周期褶皱结构的自旋阀器件	50%		[21]
	转移至VHB上的 GMR器件	270%		[72]
氧化物	块体Sr₂RuO₄	1%		[73]
	生长在云母衬底上的 BaM单晶薄膜	1.3%		[43]
	转移至PI上的La_0.7Ca_0.3MnO₃单晶薄膜	8%	5%	[66]

DownLoad: CSV

map

[1]	Bauer S, Bauer-Gogonea S, Graz I, Kaltenbrunner M, Keplinger C, Schwödiauer R 2014 Adv. Mater. 26 149 Google Scholar
[2]	Zhang F, Zang Y, Huang D, Di C A, Zhu D 2015 Nat. Commun. 6 8356 Google Scholar
[3]	Kim D H, Lu N, Ma R, Kim Y S, Kim R H, Wang S, Wu J, Won Sang M, Tao H, Islam A, Yu Ki J, Kim T i, Chowdhury R, Ying M, Xu L, Li M, Chung H J, Keum H, McCormick M, Liu P, Zhang Y W, Omenetto Fiorenzo G, Huang Y, Coleman T, Rogers John A 2011 Science 333 838 Google Scholar
[4]	Someya T, Bauer S, Kaltenbrunner M 2017 MRS Bull. 42 124 Google Scholar
[5]	Bartolozzi C, Natale L, Nori F, Metta G 2016 Nat. Mater. 15 921 Google Scholar
[6]	Sundaram S, Kellnhofer P, Li Y, Zhu J Y, Torralba A, Matusik W 2019 Nature 569 698 Google Scholar
[7]	Guo Q, Wang Z, Xu X, Jiang Y 2017 Chin. J. Engn. 39 1775 Google Scholar
[8]	Hua Q, Sun J, Liu H, Bao R, Yu R, Zhai J, Pan C, Wang Z L 2018 Nat. Commun. 9 244 Google Scholar
[9]	Li F, Li S, Cao J, Liu Y, Shang J, Li R 2020 Mater. Rev. 34 1059 Google Scholar
[10]	Parkin S, Xin J, Kaiser C, Panchula A, Roche K, Samant M 2003 Proc. IEEE 91 661 Google Scholar
[11]	Thiele J U, Maat S, Fullerton E E 2003 Appl. Phys. Lett. 82 2859 Google Scholar
[12]	Fan X, Kim S, Kou X, Kolodzey J, Zhang H, Xiao J Q 2010 Appl. Phys. Lett. 97 212501 Google Scholar
[13]	Dai G, Zhan Q, Liu Y, Yang H, Zhang X, Chen B, Li R W 2012 Appl. Phys. Lett. 100 122407 Google Scholar
[14]	Hertel R 2013 Spin 3 1340009 Google Scholar
[15]	Hirai T, Sepehri Amin H, Hasegawa K, Koyama T, Iguchi R, Ohkubo T, Chiba D, Uchida K I 2021 Appl. Phys. Lett. 118 022403 Google Scholar
[16]	Xu Y, Liu X, Guo W 2014 Nanoscale 6 12929 Google Scholar
[17]	Chen Y F, McCord J, Freudenberger J, Kaltofen R, Schmidt O G 2009 J. Appl. Phys. 105 07c302 Google Scholar
[18]	Yen M, Lai Y H, Kuo C Y, Chen C T, Chang C F, Chu Y H 2020 Adv. Funct. Mater. 30 2004597 Google Scholar
[19]	Qiao X Y, Wen X C, Wang B M, Bai Y H, Zhan Q F, Xu X H, Li R W 2017 Appl. Phys. Lett. 111 132405 Google Scholar
[20]	Lu Z, Yang Y, Wen L, Feng J, Lao B, Zheng X, Li S, Zhao K, Cao B, Ren Z, Song D, Du H, Guo Y, Zhong Z, Hao X, Wang Z, Li R W 2021 npj Flex. Electron. 6 9 Google Scholar
[21]	Li H, Zhan Q, Liu Y, Liu L, Yang H, Zuo Z, Shang T, Wang B, Li R W 2016 Acs Nano 10 4403 Google Scholar
[22]	Dai G, Xing X, Shen Y, Deng X 2019 J. Phys. D:Appl. Phys. 53 055001 Google Scholar
[23]	Ota S, Ando A, Chiba D 2018 Nat. Electron. 1 124 Google Scholar
[24]	Ge J, Wang X, Drack M, Volkov O, Liang M, Cañón Bermúdez G S, Illing R, Wang C, Zhou S, Fassbender J, Kaltenbrunner M, Makarov D 2019 Nat. Commun. 10 4405 Google Scholar
[25]	Wu Y Z, Liu Y W, Zhou Y L, Man Q K, Hu C, Asghar W, Li F L, Yu Z, Shang J, Liu G, Liao M Y, Li R W 2018 Sci. Robot. 3 eaat0429 Google Scholar
[26]	Almansouri A S, Alsharif N A, Khan M A, Swanepoel L, Kaidarova A, Salama K N, Kosel J 2019 Adv. Mater. Technol. 4 1900493 Google Scholar
[27]	Bermudez G S C, Fuchs H, Bischoff L, Fassbender J, Makarov D 2018 Nat. Electron. 1 589 Google Scholar
[28]	Zhang X S, Zhan Q F, Dai G H, Liu Y W, Zuo Z H, Yang H L, Chen B, Li R W 2013 J. Appl. Phys. 113 17A901 Google Scholar
[29]	Cao D, Wang Z, Pan L, Feng H, Cheng X, Zhu Z, Wang J, Liu Q, Han G 2016 Appl. Phys. A-Mater. 122 938 Google Scholar
[30]	Dai G H, Zhan Q F, Yang H L, Liu Y W, Zhang X S, Zuo Z H, Chen B, Li R W 2013 J. Appl. Phys. 114 173913 Google Scholar
[31]	Tang Z H, Wang B M, Yang H L, Xu X Y, Liu Y W, Sun D D, Xia L X, Zhan Q F, Chen B, Tang M H, Zhou Y C, Wang J L, Li R W 2014 Appl. Phys. Lett. 105 103504 Google Scholar
[32]	Liu Y W, Wang B M, Zhan Q F, Tang Z H, Yang H L, Liu G, Zuo Z H, Zhang X S, Xie Y L, Zhu X J, Chen B, Wang J L, Li R W 2014 Sci. Rep. 4 6615 Google Scholar
[33]	Merabtine S, Zighem F, Faurie D, Garcia-Sanchez A, Lupo P, Adeyeye A O 2018 Nano Lett. 18 3199 Google Scholar
[34]	Gao G Q, Jin C, Zheng W C, Pang X, Zheng D X, Bai H L 2018 Epl 123 17002 Google Scholar
[35]	Ha T D, Chen J W, Yen M, Lai Y H, Wang B Y, Chin Y Y, Wu W B, Lin H J, Juang J Y, Chu Y H 2020 ACS Appl. Mater. Inter. 12 46874 Google Scholar
[36]	Asai R, Ota S, Namazu T, Takenobu T, Koyama T, Chiba D 2016 J. Appl. Phys. 120 083906 Google Scholar
[37]	Ota S, Hibino Y, Bang D, Awano H, Kozeki T, Akamine H, Fujii T, Namazu T, Takenobu T, Koyama T, Chiba D 2016 Appl. Phys. Express 9 043004 Google Scholar
[38]	Zhao S, Zhou Z, Li C, Peng B, Hu Z, Liu M 2018 Acs Nano 12 7167 Google Scholar
[39]	Matsumoto H, Ota S, Koyama T, Chiba D 2021 Appl. Phys. Lett. 118 022406 Google Scholar
[40]	Wen X C, Wang B M, Sheng P, Hu S, Yang H L, Pei K, Zhan Q F, Xia W X, Xu H, Li R W 2017 Appl. Phys. Lett. 111 142403 Google Scholar
[41]	Chen X Y, Wang B M, Wen X C, Sheng P, Pravarthana D, Yang H L, Xie Y L, Liu H G, Xu X H, Lib R W 2020 J. Magn. Magn. Mater. 505 166750 Google Scholar
[42]	Liu J, Chen J, Zhang Y, Fu S, Chai G, Cao C, Zhu X, Guo Y, Cheng W, Jiang D, Zhao Z, Zhan Q 2021 ACS Appl. Mater. Inter. 13 29975 Google Scholar
[43]	Zhu Q, Tang R, Peng F, Xu S, Liang G, Zhao R, Fang Y, You L, Su X 2021 Phys. Rev. Appl. 16 054006 Google Scholar
[44]	Yu Y, Zhan Q F, Wei J W, Wang J B, Dai G H, Zuo Z H, Zhang X S, Liu Y W, Yang H L, Zhang Y, Xie S H, Wang B M, Li R W 2015 Appl. Phys. Lett. 106 162405 Google Scholar
[45]	Liu W, Ma R, Liu M, Wang H 2018 ACS Appl. Mater. Inter. 10 32331 Google Scholar
[46]	Liu W, Liu M, Ma R, Zhang R, Zhang W, Yu D, Wang Q, Wang J, Wang H 2018 Adv. Funct. Mater. 28 1705928 Google Scholar
[47]	Peng B, Xie Q Y, Zhang W L, Zhong Z Y 2007 J. Appl. Phys. 101 09C511 Google Scholar
[48]	Karboul-Trojet W, Faurie D, Aït-Yahiatène E, Roussigné Y, Mazaleyrat F, Chérif S M 2012 J. Appl. Phys. 111 07A926 Google Scholar
[49]	Zhang J, Lee W K, Tu R, Rhee D, Zhao R, Wang X, Liu X, Hu X, Zhang X, Odom T W, Yan M 2021 Nano Lett. 21 5430 Google Scholar
[50]	Yang Q, Cheng Y, Li Y, Zhou Z, Liang J, Zhao X, Hu Z, Peng R, Yang H, Liu M 2020 Adv. Electron. Mater. 6 2000246 Google Scholar
[51]	Meiklejohn W H, Bean C P 1957 Phys. Rev. 105 904 Google Scholar
[52]	Nogués J, Schuller I K 1999 J. Magn. Magn. Mater. 192 203 Google Scholar
[53]	Ali M, Adie P, Marrows C H, Greig D, Hickey B J, Stamps R L 2007 Nat. Mater. 6 70 Google Scholar
[54]	Salazar-Alvarez G, Sort J, Suriñach S, Baró M D, Nogués J 2007 J. Am. Chem. Soc. 129 9102 Google Scholar
[55]	Cain W C, Kryder M H 1990 J. Appl. Phys. 67 5722 Google Scholar
[56]	Zhang Y, Zhan Q F, Rong X, Li H H, Zuo Z H, Liu Y W, Wang B M, Li R W 2016 IEEE Trans. Magn. 52 2529722 Google Scholar
[57]	Zhang X S, Zhan Q F, Dai G H, Liu Y W, Zuo Z H, Yang H L, Chen B, Li R W 2013 Appl. Phys. Lett. 102 022412 Google Scholar
[58]	Sheng P, Xie Y L, Bai Y H, Wang B M, Zhang L, Wen X C, Yang H L, Chen X Y, Li X G, Li R W 2019 Appl. Phys. Lett. 115 242403 Google Scholar
[59]	Zhang Z, Liu E, Zhang W, Wong P K J, Xu Z, Hu F, Li X, Tang J, Wee A T S, Xu F 2019 ACS Appl. Mater. Inter. 11 8258 Google Scholar
[60]	Shi X, Mi W, Zhang Q, Zhang X 2020 Appl. Phys. Lett. 117 132401 Google Scholar
[61]	Huang J, Wang H, Wang X, Gao X, Liu J, Wang H 2020 ACS Appl. Mater. Inter. 12 39920 Google Scholar
[62]	Jin C, Zhu Y, Han W, Liu Q, Hu S, Ji Y, Xu Z, Hu S, Ye M, Chen L 2020 Appl. Phys. Lett. 117 252902 Google Scholar
[63]	Thai Duy H, Yen M, Lai Y H, Kuo C Y, Chen C T, Tanaka A, Tsai L Z, Zhao Y F, Duan C G, Lee S F, Chang C F, Juang J Y, Chu Y H 2020 Nanoscale 12 3284 Google Scholar
[64]	Du D, Manzo S, Zhang C, Saraswat V, Genser K T, Rabe K M, Voyles P M, Arnold M S, Kawasaki J K 2021 Nat. Commun. 12 2494 Google Scholar
[65]	Ling Y, Hu Y, Wang H, Niu B, Chen J, Liu R, Yuan Y, Wang G, Wu D, Xu M, Han Z, Du J, Xu Q 2021 ACS Appl. Mater. Inter. 13 24285 Google Scholar
[66]	Hong S S, Gu M, Verma M, Harbola V, Wang B Y, Lu D, Vailionis A, Hikita Y, Pentcheva R, Rondinelli J M, Hwang H Y 2020 Science 368 71 Google Scholar
[67]	Liu E, Fache T, Cespedes-Berrocal D, Zhang Z, Petit-Watelot S, Mangin S, Xu F, Rojas-Sanchez J C 2019 Phys. Rev. Appl. 12 044074 Google Scholar
[68]	Wong G D H, Ang C C I, Gan W, Law W C, Xu Z, Xu F, Seet C S, Lew W S 2021 Appl. Phys. Lett. 119 042402 Google Scholar
[69]	Wong G D H, Xu Z, Gan W, Ang C C I, Law W C, Tang J, Zhang W, Wong P K J, Yu X, Xu F, Wee A T S, Seet C S, Lew W S 2021 Acs Nano 15 8319 Google Scholar
[70]	Faurie D, Zighem F, Garcia-Sanchez A, Lupo P, Adeyeye A O 2017 Appl. Phys. Lett. 110 091904 Google Scholar
[71]	Melzer M, Lin G G, Makarov D, Schmidt O G 2012 Adv. Mater. 24 6468 Google Scholar
[72]	Melzer M, Kaltenbrunner M, Makarov D, Karnaushenko D, Karnaushenko D, Sekitani T, Someya T, Schmidt O G 2015 Nat. Commun. 6 6080 Google Scholar
[73]	Hicks C W, Brodsky D O, Yelland E A, Gibbs A S, Bruin J A N, Barber M E, Edkins S D, Nishimura K, Yonezawa S, Maeno Y, Mackenzie A P 2014 Science 344 283 Google Scholar
[74]	Mun J H, Lee H, Kim J U, Kang M, Hong A R, Jang H S, Han K S, Kim D H 2020 J. Magn. Magn. Mater. 511 166968 Google Scholar
[75]	Zhang S, Zhan Q, Yu Y, Liu L, Li H, Yang H, Xie Y, Wang B, Xie S, Li R W 2016 Appl. Phys. Lett. 108 102409 Google Scholar
[76]	Li J C, Zhan Q F, Zhang S L, Wei J W, Wang J B, Pan M J, Xie Y L, Yang H L, Zhou Z, Xie S H, Wang B M, Li R W 2017 Sci. Rep. 7 2837 Google Scholar
[77]	Zhao J P, Guo Q H, Yin H Z, Zou J T, Zhao Z J, Cheng W J, Jiang D M, Zhan Q F 2020 Chin. Phys. B 29 117501 Google Scholar
[78]	Guo Q H, Cheng W J, Zhan Q F 2021 J. Mag. Mater. Dev. 52 6 Google Scholar
[79]	Wang Z, Zhou Z, Cheng W, Jiang D, Zhan Q 2020 J. Magn. Magn. Mater. 513 167126 Google Scholar
[80]	Ji D, Cai S, Paudel T R, Sun H, Zhang C, Han L, Wei Y, Zang Y, Gu M, Zhang Y, Gao W, Huyan H, Guo W, Wu D, Gu Z, Tsymbal E Y, Wang P, Nie Y, Pan X 2019 Nature 570 87 Google Scholar
[81]	Lu D, Baek D J, Hong S S, Kourkoutis L F, Hikita Y, Hwang H Y 2016 Nat. Mater. 15 1255 Google Scholar
[82]	Jiang J, Bitla Y, Huang C W, et al. 2017 Sci. Adv. 3 e1700121 Google Scholar
[83]	Dong G H, Li S Z, Yao M T, Zhou Z Y, Zhang Y Q, Han X, Luo Z L, Yao J X, Peng B, Hu Z Q, Huang H B, Jia T T, Li J Y, Ren W, Ye Z G, Ding X D, Sun J, Nan C W, Chen L Q, Li J, Liu M 2019 Science 366 475 Google Scholar
[84]	Chu Y H 2017 npj Quantum Mater. 2 67 Google Scholar
[85]	Bitla Y, Chu Y H 2017 FlatChem 3 26 Google Scholar
[86]	Liu H J, Wang C K, Su D, Amrillah T, Hsieh Y H, Wu K H, Chen Y C, Juang J Y, Eng L M, Jen S U, Chu Y H 2017 ACS Appl. Mater. Interf. 9 7297 Google Scholar
[87]	Huang J, Wang H, Sun X, Zhang X, Wang H 2018 ACS Appl. Mater. Interf. 10 42698 Google Scholar
[88]	Liu J, Feng Y, Tang R, Zhao R, Gao J, Shi D, Yang H 2018 Adv. Electron. Mater. 4 1700522 Google Scholar
[89]	Fan J, Xie Y, Qian F, Ji Y, Hu D, Tang R, Liu W, Zhang L, Tong W, Ma C, Yang H 2019 J. Alloys Compd. 806 753 Google Scholar
[90]	Hou W, Zhou Z, Zhang L, Zhao S, Peng B, Hu Z, Ren W, Ye Z G, Jiang Z D, Liu M 2019 ACS Appl. Mater. Interf. 11 21727 Google Scholar
[91]	Li C I, Lin J C, Liu H J, Chu M W, Chen H W, Ma C H, Tsai C Y, Huang H W, Lin H J, Liu H L, Chiu P W, Chu Y H 2016 Chem. Mater. 28 3914 Google Scholar
[92]	Kum H S, Lee H, Kim S, Lindemann S, Kong W, Qiao K, Chen P, Irwin J, Lee J H, Xie S, Subramanian S, Shim J, Bae S H, Choi C, Ranno L, Seo S, Lee S, Bauer J, Li H, Lee K, Robinson J A, Ross C A, Schlom D G, Rzchowski M S, Eom C B, Kim J 2020 Nature 578 75 Google Scholar
[93]	Zhang Y, Shen L, Liu M, Li X, Lu X, Lu L, Ma C, You C, Chen A, Huang C, Chen L, Alexe M, Jia C L 2017 Acs Nano 11 8002 Google Scholar
[94]	Chen Z, Li F, Huang Q W, Liu F, Wang F F, Ringer S P, Luo L S, Zhang S J, Chen L Q, Liao X Z 2020 Sci. Adv. 6 eabc7156 Google Scholar
[95]	Lu Z, Liu J, Feng J, Zheng X, Yang L H, Ge C, Jin K J, Wang Z, Li R W 2020 APL Mater. 8 051105 Google Scholar
[96]	Shrestha S, Coile M, Zhu M, Souri M, Kim J, Pandey R, Brill J W, Hwang J, Kim J W, Seo A 2020 ACS Appl. Nano Mater. 3 6310 Google Scholar
[97]	An F, Qu K, Zhong G, Dong Y, Ming W, Zi M, Liu Z, Wang Y, Qi B, Ding Z, Xu J, Luo Z, Gao X, Xie S, Gao P, Li J 2020 Adv. Funct. Mater. 30 2003495 Google Scholar
[98]	Loong L M, Lee W, Qiu X, Yang P, Kawai H, Saeys M, Ahn J H, Yang H 2016 Adv. Mater. 28 4983 Google Scholar
[99]	Melzer M, Makarov D, Schmidt O G 2020 J. Phys. D 53 083002 Google Scholar
[100]	Perez N, Melzer M, Makarov D, Ueberschaer O, Ecke R, Schulz S E, Schmidt O G 2015 Appl. Phys. Lett. 106 153501 Google Scholar
[101]	Wu W, Zhang L, Cai J, Fang B, Luo J, Zeng Z 2019 Appl. Phys. Lett. 115 052401 Google Scholar
[102]	Chen J Y, Wang J P 2018 Nat. Electron. 1 96 Google Scholar
[103]	Ota S, Ando A, Sekitani T, Koyama T, Chiba D 2019 Appl. Phys. Lett. 115 202401 Google Scholar
[104]	Yan Y C, Hu Z, Yang Z B, Yuan W Z, Song C Y, Pan J, Shen Y J 2021 Sci. Robot. 6 abc8801 Google Scholar
[105]	Bhatti S, Ma C, Liu X, Piramanayagam S N 2019 Adv. Electron. Mater. 5 1800467 Google Scholar
[106]	Li S, Cao P, Li F, Asghar W, Wu Y, Xiao H, Liu Y, Zhou Y, Yang H, Zhang Y, Shang J, Makarov D, Li R-W 2022 Nano Energy 92 106754 Google Scholar
[107]	Doan Nguyen B, Zheng Y, Becerra L, Marangolo M, Almanza M, LoBue M 2021 Phys. Rev. Appl. 15 064045 Google Scholar
[108]	Zhao Y, Peng R, Guo Y, Liu Z, Dong Y, Zhao S, Li Y, Dong G, Hu Y, Zhang J, Peng Y, Yang T, Tian B, Zhao Y, Zhou Z, Jiang Z, Luo Z, Liu M 2021 Adv. Funct. Mater. 31 2009376 Google Scholar
[109]	Zheng W C, Zheng D X, Wang Y C, Li D, Jin C, Bai H L 2019 J. Magn. Magn. Mater. 481 227 Google Scholar
[110]	Wang Z G, Wang X J, Li M H, Gao Y, Hu Z Q, Nan T X, Liang X F, Chen H H, Yang J, Cash S, Sun N X 2016 Adv. Mater. 28 9370 Google Scholar
[111]	Parkin S S P, Roche K P, Suzuki T 1992 Jpn. J. Appl. Phys., Part 2 31 L1246 Google Scholar
[112]	Chen Y F, Mei Y F, Kaltofen R, et al. 2008 Adv. Mater. 20 3224 Google Scholar
[113]	Guo M, Yang C, Gao D, Li Q, Zhang A, Feng J, Yang H, Tao R, Fan Z, Zeng M, Zhou G, Lu X, Liu J M 2020 J. Mater. Sci. Technol. 44 42 Google Scholar
[114]	Luby Š, Anwarzai B, Áč V, Majkova E, Senderák R 2012 Vacuum 86 718 Google Scholar
[115]	Liu L P, Zhan Q F, Yang H L, Li H H, Zhang S L, Liu Y W, Wang B M, Tan X H, Li R W 2016 AIP Adv. 6 035206 Google Scholar
[116]	Fuji Y, Kaji S, Hara M, Higashi Y, Hori A, Okamoto K, Nagata T, Baba S, Yuzawa A, Otsu K, Masunishi K, Ono T, Fukuzawa H 2018 Appl. Phys. Lett. 112 062405 Google Scholar
[117]	Fuji Y, Higashi Y, Kaji S, Masunishi K, Nagata T, Yuzawa A, Okamoto K, Baba S, Ono T, Hara M 2019 Jpn. J. Appl. Phys. 58 SD0802 Google Scholar
[118]	Matsumoto H, Ota S, Ando A, Chiba D 2019 Appl. Phys. Lett. 114 132401 Google Scholar
[119]	Chen X, Mi W 2021 J. Mater. Chem. C 9 9400 Google Scholar
[120]	Boutry Clementine M, Negre M, Jorda M, Vardoulis O, Chortos A, Khatib O, Bao Z 2018 Sci. Robot. 3 eaau6914 Google Scholar
[121]	Viry L, Levi A, Totaro M, Mondini A, Mattoli V, Mazzolai B, Beccai L 2014 Adv. Mater. 26 2659 Google Scholar

[1]	Xiong Jia-Cheng, Huang Zhe-Qun, Zhang Heng, Wang Qi-Xiang, Cui Ke-Hang. Spectral regulation in thermophotovoltaic devices. Acta Physica Sinica, 2024, 73(14): 144402. doi: 10.7498/aps.73.20240629
[2]	Guo Xi, Zuo Ya-Lu, Cui Bao-Shan, Shen Tie-Long, Sheng Yan-Bin, Xi Li. Ion irradiation modulated magnetic properties of materials and its applications. Acta Physica Sinica, 2024, 73(13): 136101. doi: 10.7498/aps.73.20240541
[3]	Li Han-Nan, Peng Yan. Theoretical study of influence of laser pulse chirp on terahertz emission characteristics of gas induced by two-color laser field. Acta Physica Sinica, 2024, 73(6): 060701. doi: 10.7498/aps.73.20231806
[4]	Yuan Guo-Liang, Wang Chen-Hao, Tang Wen-Bin, Zhang Rui, Lu Xu-Bing. Structure, performance regulation and typical device applications of HfO₂-based ferroelectric films. Acta Physica Sinica, 2023, 72(9): 097703. doi: 10.7498/aps.72.20222221
[5]	Li Lu, Zhang Yang-Kun, Shi Dong-Xia, Zhang Guang-Yu. Cotrollable growth of monolayer MoS₂ films and their applications in devices. Acta Physica Sinica, 2022, 71(10): 108102. doi: 10.7498/aps.71.20212447
[6]	Xiong Zheng-Wei, Yang Jiang, Wang Yu, Yang Lu, Guan Xian, Cao Lin-Hong, Wang Jin, Gao Zhi-Peng. Preparation of FeNiMo/SiO₂ composite core and regulation of soft magnetic properties. Acta Physica Sinica, 2022, 71(15): 157502. doi: 10.7498/aps.71.20212317
[7]	Li Pei-Gen, Zhang Ji-Hai, Tao Ye, Zhong Ding-Yong. Two-dimensional magnetic transition metal halides: molecular beam epitaxy growth and physical property modulation. Acta Physica Sinica, 2022, 71(12): 127505. doi: 10.7498/aps.71.20220727
[8]	Nie Xiao-Lei, Yu Hao-Cheng, Zhu Wan-Ting, Sang Xia-Han, Wei Ping, Zhao Wen-Yu. Design, fabrication and performance evaluation of graphene/Bi_0.5Sb_1.5Te₃ flexible thermoelectric films and in-plane heat dissipation devices. Acta Physica Sinica, 2022, 71(15): 157301. doi: 10.7498/aps.71.20220358
[9]	Wang Hai-Yu, Liu Ying-Jie, Xun Lu-Lu, Li Jing, Yang Qing, Tian Qi-Yun, Nie Tian-Xiao, Zhao Wei-Sheng. Research progress of preparation of large-scale two-dimensional magnetic materials and manipulation of Curie temperature. Acta Physica Sinica, 2021, 70(12): 127301. doi: 10.7498/aps.70.20210223
[10]	Tan Cong-Bing, Zhong Xiang-Li, Wang Jin-Bin. Polar topological structures in ferroelectric materials. Acta Physica Sinica, 2020, 69(12): 127702. doi: 10.7498/aps.69.20200311
[11]	Lan Shun, Pan Hao, Lin Yuan-Hua. Fabrication and applications of flexible inorganic ferroelectric thin films. Acta Physica Sinica, 2020, 69(21): 217708. doi: 10.7498/aps.69.20201365
[12]	Chen Zhen-Ni, Liu Sheng-Li, Wang Hai-Yun, Cheng Jie. Stress mechanism of Y1-xGdxBCO thin film with Gd substitution prepared by F-free metal organic deposition method. Acta Physica Sinica, 2017, 66(15): 156101. doi: 10.7498/aps.66.156101
[13]	Chai Lei, Zhong Min. Recent research progress in perovskite solar cells. Acta Physica Sinica, 2016, 65(23): 237902. doi: 10.7498/aps.65.237902
[14]	Zheng Li, Guo Jian-Zhong. A controllable circular ring acoustic focused field. Acta Physica Sinica, 2016, 65(4): 044305. doi: 10.7498/aps.65.044305
[15]	Lan Lin-Feng, Zhang Peng, Peng Jun-Biao. Research progress on oxide-based thin film transisitors. Acta Physica Sinica, 2016, 65(12): 128504. doi: 10.7498/aps.65.128504
[16]	Chen Li-Xiang, Zhang Yuan-Ying. Research progress on preparation, manipulation, and remote sensing applications of high-order orbital angular momentum of photons. Acta Physica Sinica, 2015, 64(16): 164210. doi: 10.7498/aps.64.164210
[17]	Liu Hao, Xue Yu-Ming, Qiao Zai-Xiang, Li Wei, Zhang Chao, Yin Fu-Hong, Feng Shao-Jun. Progress of application research on Cu2ZnSnS4 thin film and its device. Acta Physica Sinica, 2015, 64(6): 068801. doi: 10.7498/aps.64.068801
[18]	Zhang Fu-Li, Zhao Xiao-Peng. Tunable split ring resonator and its effect. Acta Physica Sinica, 2007, 56(8): 4661-4667. doi: 10.7498/aps.56.4661
[19]	Yu Bai-Lin, Tang Xin-Feng, Qi Qiong, Zhang Qing-Jie. Preparation and thermal transport properties of CoSb3 nano-compounds. Acta Physica Sinica, 2004, 53(9): 3130-3135. doi: 10.7498/aps.53.3130
[20]	LIANG FENG, YAN XUE-JIAN. PROPERTY, APPLICATION AND PREPARATION OF DIAMOND-LIKE FILM. Acta Physica Sinica, 1999, 48(6): 1095-1102. doi: 10.7498/aps.48.1095

Catalog

Vol. 71, Issue 9 - 2022-05-05

Metrics

Abstract views: 15256
PDF Downloads: 725
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板