Application of X-ray photoelectron spectroscopy to study interfaces for solid-state lithium ion battery

Zhou Yi-Fan; Yang Mu-Zi; She Feng-Quan; Gong Li; Zhang Xiao-Qi; Chen Jian; Song Shu-Qin; Xie Fang-Yan

doi:10.7498/aps.70.20210180

Abstract

Solid-state lithium-ion batteries have attracted much attention due to their high safety, high energy densities and other advantages. However, solid-state lithium-ion batteries cannot realize large-scale commercial use. There are key scientific and technical issues that have not been resolved, especially interface issues, such as high resistance and instability of the interface. The X-ray photoelectron spectroscopy (XPS), as an important surface analysis method, can perform qualitative and semi-quantitative chemical analysis of the interface, which makes XPS can be widely used to study the solid-state lithium-ion battery interfaces. In this paper, we review the recent research progress of solid-state lithium-ion battery interfaces by using XPS, and summarize and review the XPS experimental principle, experimental method, experimental results and their effects on interface performance. The XPS analysis methods for solid-state lithium-ion batteries include ex-situ XPS, in-situ XPS reflecting the real-time changes of the battery interface, and operando XPS based on the actual working conditions of the battery. The ex-situ XPS can study oxide solid electrolyte interfaces, sulfide solid electrolyte interfaces and artificial solid electrolyte interface (SEI) layers to access information about the chemical composition of the interface, predict the performance of the interface, obtain the chemical distribution in space, and evaluate the chemical structure and irregularity of the interface. With ultraviolet photoemission spectroscopy (UPS) the interface work function, energy band bending and energy structure of the full battery can be obtained. In-situ XPS can effectively study the process of chemical reactions between the electrolyte and the electrode. The key prerequisite is the controllable in-situ construction of the electrolyte/electrode interface. In-situ XPS research can directly study the electrochemical changes of the interface. In-situ XPS/UPS can study the energy level alignment of solid-state lithium-ion batteries, indicating that a space charge layer is formed at the solid electrolyte interface, and the energy band bending occurs. The degree of energy band bending is reflected in the binding energy shifts of the related elements at the interface. The change of the energy structure in the deposition process can be determined by the binding energy shifts of the related elements at the interface and the change of the interface work function. Operando XPS performs XPS characterization at the same time under the working condition of the battery. Operando XPS can be combined with electrochemical characterization to observe the effects of interface reaction and solid electrolyte decomposition products on electrochemical performance, thereby determining the main components that affect electrochemical performance. It can also be combined with the ex-situ XPS to study the interface reaction mechanism and influencing factors. The information obtained includes the chemical states of elements after the interface reaction has occurred, the evolution of interface elements in the process of real-time interface reaction, the energy structure change and interface component overpotential, thus having a better understanding of interface composition, interfacial structure change, kinetics of interface reaction, and interfacial ion migration of the solid-state lithium ion batteries.

Keywords:

Authors and contacts

1.
Instrumental Analysis & Research Center, Sun Yat-sen University, Guangzhou 510275, China
2.
School of Materials Science and Engineering, Sun Yat-sen University, Guangzhou 510275, China
3.
School of Chemistry, Sun Yat-sen University, Guangzhou 510275, China

Corresponding author: Xie Fang-Yan, xiefy@mail.sysu.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 21576301, 51973244)

FullText HTML : translate this paragraph

References

[1]	Scrosati B, Garche J 2010 J. Power Sources 195 2419 Google Scholar
[2]	Wen J, Yu Y, Chen C 2012 Mater. Express 2 197 Google Scholar
[3]	Xiang Y, Li X, Cheng Y, Sun X, Yang Y 2020 Mater. Today 36 139 Google Scholar
[4]	Wang H, Liu Y, Li Y, Cui Y 2019 Electrochem. Energy Rev. 2 509 Google Scholar
[5]	Kim J G, Son B, Mukherjee S, Schuppert N, Bates A, Kwon O, Choi M J, Chung H Y, Park S 2015 J. Power Sources 282 299 Google Scholar
[6]	Wang P, Qu W, Song W L, Chen H, Chen R, Fang D 2019 Adv. Funct. Mater. 29 1900950
[7]	Shen Z, Zhang W, Zhu G, Huang Y, Feng Q, Lu Y 2020 Small Methods 4 1900592 Google Scholar
[8]	Xu L, Tang S, Cheng Y, Wang K, Liang J, Liu C, Cao Y, Wei F, Mai L 2018 Joule 2 1991 Google Scholar
[9]	Colclasure A M, Smith K A, Kee R J 2011 Electrochim. Acta 58 33 Google Scholar
[10]	Chen W, Ou Z, Tang H, Wang H, Yang Y 2008 Electrochim. Acta 53 4414 Google Scholar
[11]	Wang A, Kadam S, Li H, Shi S, Qi Y 2018 NPJ Comput. Mater. 4 15 Google Scholar
[12]	Schwöbel A, Jaegermann W, Hausbrand R 2016 Solid State Ionics 288 224 Google Scholar
[13]	Brundle C R 1974 J. Vac. Sci. Technol. 11 212 Google Scholar
[14]	Watts J F, Wolstenholme J 2003 An Introduction to Surface Analysis by XPS and AES (Chichester: John Wiley & Sons) pp1–14
[15]	Watts J F, Wolstenholme J 2003 An Introduction to Surface Analysis by XPS and AES (Chichester: John Wiley & Sons) pp59–76
[16]	Meunier G, Dormoy R, Levasseur A 1989 Mater. Sci. Eng., B 3 19 Google Scholar
[17]	Ueda S 2013 J. Electron Spectrosc. Relat. Phenom. 190 235 Google Scholar
[18]	Zhao W, Yi J, He P, Zhou H 2019 Electrochem. Energy Rev. 2 574 Google Scholar
[19]	Reddy M V, Julien C M, Mauger A, Zaghib K 2020 Nanomaterials 10 1606 Google Scholar
[20]	Manthiram A, Yu X, Wang S 2017 Nat. Rev. Mater. 2 16103 Google Scholar
[21]	Murugan R, Thangadurai V, Weppner W 2007 Angew. Chem. Int. Ed. 46 7778 Google Scholar
[22]	Sudo R, Nakata Y, Ishiguro K, Matsui M, Hirano A, Takeda Y, Yamamoto O, Imanishi N 2014 Solid State Ionics 262 151 Google Scholar
[23]	Luo W, Gong Y, Zhu Y, Fu K K, Dai J, Lacey S D, Wang C, Liu B, Han X, Mo Y, Wachsman E D, Hu L 2016 J. Am. Chem. Soc. 138 12258 Google Scholar
[24]	Meng J, Zhang Y, Zhou X, Lei M, Li C 2020 Nat. Commun. 11 3716 Google Scholar
[25]	Sharafi A, Yu S, Naguib M, Lee M, Ma C, Meyer H M, Nanda J, Chi M, Siegel D J, Sakamoto J 2017 J. Mater. Chem. A 5 13475 Google Scholar
[26]	Wu J F, Pu B W, Wang D, Shi S Q, Zhao N, Guo X, Guo X 2019 ACS Appl. Mater. Interfaces 11 898 Google Scholar
[27]	Samson A J, Hofstetter K, Bag S, Thangadurai V 2019 Energy Environ. Sci. 12 2957 Google Scholar
[28]	Li Y, Wang Z, Cao Y, Du F, Chen C, Cui Z, Guo X 2015 Electrochim. Acta 180 37 Google Scholar
[29]	Ohta S, Kobayashi T, Asaoka T 2011 J. Power Sources 196 3342 Google Scholar
[30]	Zhu Y, He X, Mo Y 2016 J. Mater. Chem. A 4 3253 Google Scholar
[31]	Han F, Zhu Y, He X, Mo Y, Wang C 2016 Adv. Energy Mater. 6 1501590 Google Scholar
[32]	Wolfenstine J, Allen J L, Read J, Sakamoto J 2013 J. Mater. Sci. 48 5846 Google Scholar
[33]	Tan D H S, Banerjee A, Chen Z, Meng Y S 2020 Nat. Nanotechnol. 15 170 Google Scholar
[34]	Connell J G, Zhu Y, Zapol P, Tepavcevic S, Sharafi A, Sakamoto J, Curtiss L A, Fong D D, Freeland J W, Markovic N M 2018 ACS Appl. Mater. Interfaces 10 17471 Google Scholar
[35]	Zhu J, Zhao J, Xiang Y, Lin M, Wang H, Zheng B, He H, Wu Q, Huang J Y, Yang Y 2020 Chem. Mater. 32 4998 Google Scholar
[36]	Sharafi A, Meyer H M, Nanda J, Wolfenstine J, Sakamoto J 2016 J. Power Sources 302 135 Google Scholar
[37]	Yu S, Siegel D J 2017 Chem. Mater. 29 9639 Google Scholar
[38]	Pesci F M, Brugge R H, Hekselman A K O, Cavallaro A, Chater R J, Aguadero A 2018 J. Mater. Chem. A 6 19817 Google Scholar
[39]	Han F, Westover A S, Yue J, Fan X, Wang F, Chi M, Leonard D N, Dudney N J, Wang H, Wang C 2019 Nat. Energy 4 187 Google Scholar
[40]	Haruyama J, Sodeyama K, Tateyama Y 2017 ACS Appl. Mater. Interfaces 9 286 Google Scholar
[41]	Zarabian M, Bartolini M, Pereira-Almao P, Thangadurai V 2017 J. Electrochem. Soc. 164 A1133 Google Scholar
[42]	Liu Y, Sun Q, Liu J, Norouzi Banis M, Zhao Y, Wang B, Adair K, Hu Y, Xiao Q, Zhang C, Zhang L, Lu S, Huang H, Song X, Sun X 2020 ACS Appl. Mater. Interfaces 12 2293 Google Scholar
[43]	Trevey J E, Jung Y S, Lee S H 2011 Electrochim. Acta 56 4243 Google Scholar
[44]	Mizuno F, Hayashi A, Tadanaga K, Tatsumisago M 2005 Adv. Mater. 17 918 Google Scholar
[45]	Kanno R, Murayama M 2001 J. Electrochem. Soc. 148 A742 Google Scholar
[46]	Kanno R, Hata T, Kawamoto Y, Irie M 2000 Solid State Ionics 130 97 Google Scholar
[47]	Kamaya N, Homma K, Yamakawa Y, Hirayama M, Kanno R, Yonemura M, Kamiyama T, Kato Y, Hama S, Kawamoto K, Mitsui A 2011 Nat. Mater. 10 682 Google Scholar
[48]	Kudu Ö U, Famprikis T, Fleutot B, Braida M-D, Le Mercier T, Islam M S, Masquelier C 2018 J. Power Sources 407 31 Google Scholar
[49]	Mizuno F, Hayashi A, Tadanaga K, Tatsumisago M 2006 Solid State Ionics 177 2721 Google Scholar
[50]	Liu Z, Fu W, Payzant E A, Yu X, Wu Z, Dudney N J, Kiggans J, Hong K, Rondinone A J, Liang C 2013 J. Am. Chem. Soc. 135 975 Google Scholar
[51]	Dietrich C, Weber D A, Culver S, Senyshyn A, Sedlmaier S J, Indris S, Janek J, Zeier W G 2017 Inorg. Chem. 56 6681 Google Scholar
[52]	Seino Y, Ota T, Takada K, Hayashi A, Tatsumisago M 2014 Energy Environ. Sci. 7 627 Google Scholar
[53]	Wenzel S, Randau S, Leichtweiß T, Weber D A, Sann J, Zeier W G, Janek J 2016 Chem. Mater. 28 2400 Google Scholar
[54]	Zhou P, Wang J, Cheng F, Li F, Chen J 2016 Chem. Commun. 52 6091 Google Scholar
[55]	Boulineau S, Courty M, Tarascon J M, Viallet V 2012 Solid State Ionics 221 1 Google Scholar
[56]	Zhu Y, He X, Mo Y 2015 ACS Appl. Mater. Interfaces 7 23685 Google Scholar
[57]	Auvergniot J, Cassel A, Foix D, Viallet V, Seznec V, Dedryvère R 2017 Solid State Ionics 300 78 Google Scholar
[58]	Gao Y, Wang D, Li Y C, Yu Z, Mallouk T E, Wang D 2018 Angew. Chem. Int. Ed. 57 13608 Google Scholar
[59]	Koerver R, Walther F, Aygün I, Sann J, Dietrich C, Zeier W G, Janek J 2017 J. Mater. Chem. A 5 22750 Google Scholar
[60]	Du M, Liao K, Lu Q, Shao Z 2019 Energy Environ. Sci. 12 1780 Google Scholar
[61]	Ni X, Qian T, Liu X, Xu N, Liu J, Yan C 2018 Adv. Funct. Mater. 28 1706513 Google Scholar
[62]	Zhang L, Zhang K, Shi Z, Zhang S 2017 Langmuir 33 11164 Google Scholar
[63]	Shi X, Pang Y, Wang B, Sun H, Wang X, Li Y, Yang J, Li H W, Zheng S 2020 Mater. Today Nano 10 100079 Google Scholar
[64]	Fan X, Ji X, Han F, Yue J, Chen J, Chen L, Deng T, Jiang J, Wang C 2018 Sci. Adv. 4 eaau9245 Google Scholar
[65]	Chang X, Liu H, Yang H, Di J, Tang W, Fu H, Li M, Liu R 2020 J. Materiomics 6 54 Google Scholar
[66]	Nagao K, Suyama M, Kato A, Hotehama C, Deguchi M, Sakuda A, Hayashi A, Tatsumisago M 2019 ACS Appl. Energy Mater. 2 3042 Google Scholar
[67]	Liang J Y, Zhang X D, Zeng X X, Yan M, Yin Y X, Xin S, Wang W P, Wu X W, Shi J L, Wan L J, Guo Y G 2020 Angew. Chem. Int. Ed. 59 6585 Google Scholar
[68]	Tripathi A M, Su W N, Hwang B J 2018 Chem. Soc. Rev. 47 736 Google Scholar
[69]	Sicolo S, Fingerle M, Hausbrand R, Albe K 2017 J. Power Sources 354 124 Google Scholar
[70]	Wenzel S, Leichtweiss T, Krüger D, Sann J, Janek J 2015 Solid State Ionics. 278 98 Google Scholar
[71]	Liu Z, Li G, A. Borodin, Liu X, Li Y, Endres F 2019 J. Solid State Electrochem. 23 2107 Google Scholar
[72]	Jones S D, Akridge J R, Shokoohi F K 1994 Solid State Ionics 69 357 Google Scholar
[73]	Lacivita V, Artrith N, Ceder G 2018 Chem. Mater. 30 7077 Google Scholar
[74]	Lacivita V, Westover A S, Kercher A, Phillip N D, Yang G, Veith G, Ceder G, Dudney N J 2018 J. Am. Chem. Soc. 140 11029 Google Scholar
[75]	Yu X, Bates J B, Jellison G E, Hart F X 1997 J. Electrochem. Soc. 144 524 Google Scholar
[76]	Schwöbel A, Hausbrand R, Jaegermann W 2015 Solid State Ionics 273 51 Google Scholar
[77]	Nazri G 1988 MRS Proc. 135 117
[78]	Nazri G 1989 Solid State Ionics 34 97 Google Scholar
[79]	Maier J, Bunsenges B 1985 Phys. Chem. 89 355
[80]	Guo X, Chen C 2016 Acta. Chim. Slov. 63 3
[81]	Bañares M A 2005 Catal. Today 100 71 Google Scholar
[82]	Palomares V, Sharma N 2019 Front. Energy Res. 7 10 Google Scholar
[83]	Wu X, Villevieille C, Novák P, El Kazzi M 2018 Phys. Chem. Chem. Phys. 20 11123 Google Scholar
[84]	Nelson Weker J, Toney M F 2015 Adv. Funct. Mater. 25 1622 Google Scholar
[85]	Wood K N, Steirer K X, Hafner S E, et al. 2018 Nat. Commun. 9 2490 Google Scholar

Cited By

图 1 SSLIB中的界面、界面问题和解决策略示意图

Figure 1. Illustration of the interfaces, interface issues, and solving strategies in SSLIB.

DownLoad: Full-Size Img PowerPoint

图 2 XPS测量的能级示意图

Figure 2. Schematic diagram of energy level in XPS measurement.

DownLoad: Full-Size Img PowerPoint

图 3 (a)立方相Li₇La₃Zr₂O₁₂(c-LLZO)晶体结构示意图^[27]; (b)空气中不同暴露时间的LLZO微米粉体表面的O1s谱图变化

Figure 3. (a) Crystal structure of cubic Li₇La₃Zr₂O₁₂(c-LLZO)^[27]; (b) O1s spectra of LLZO micro particles exposed to air for different times.

DownLoad: Full-Size Img PowerPoint

图 4 (a) 原始和放电后的Li₇La₃Zr₂O₁₂(LLZO)表面的Zr 3d分峰拟合结果^[31]; (b)原始Li_1.3Al_0.3Ti_1.7(PO₄)₃(LATP)、化学失效LATP、电化学失效LATP的Ti 2p谱图^[35]; LiCoO₂衬底上LLZO薄膜不同刻蚀深度的(c)Co 2p峰以及(d)Li 1s和Co 3p峰的XPS深度剖析谱图^[41]

Figure 4. (a) Peak deconvolution of Zr 3d spectra of fresh and discharged Li₇La₃Zr₂O₁₂ (LLZO)^[31]; (b) Ti 2p XPS spectra of the Li_1.3Al_0.3Ti_1.7(PO₄)₃ (LATP)-pristine, chem-LATP(chemical failure), and EC-LATP(electrochemical failure) surface^[35]; XPS depth profiles of (c) Co 2p spectra, (d) Li 1s and Co 3p spectra of LLZO thin film on LiCoO₂ at different depth^[41].

DownLoad: Full-Size Img PowerPoint

图 5 (a) Li₁₀GeP₂S₁₂的晶体结构示意图^[47]; (b) Li₂S-P₂S₅体系中不同成分的部分材料的晶体结构示意图^[48]

Figure 5. (a) Crystal structure of Li₁₀GeP₂S₁₂^[47]; (b) crystal structures of some materials within Li₂S-P₂S₅ binary system^[48].

DownLoad: Full-Size Img PowerPoint

图 6 (a) 循环后的Li/Li₁₀GeP₂S₁₂界面的XPS深度剖析谱图, S 2p, Ge 3d, P 2p, Li 1s^[58]; (b) 在不同截止电压(4.0—5.0 V)循环25次后的集流体/正极界面随时间变化的S 2p深度剖析谱图^[59]

Figure 6. (a) XPS depth profiles of cycled Li/Li₁₀GeP₂S₁₂ interface: XPS spectra of S 2p, Ge 3d, P 2p, Li 1s^[58]; (b) S 2p XPS depth profiles after 25 cycles for different upper cut-off voltage (4.0–5.0 V) as a function of different etching time^[59].

DownLoad: Full-Size Img PowerPoint

图 7 (a) 循环后LiFSI修饰的Li₃PS₄的F 1s和P 2p(右)谱图, 循环后未处理的Li₃PS₄的P 2p(左)谱图^[64]; (b) Li/Li_2.9B_0.9S_0.1O_3.1对称电池恒流充放电循环前后的阻抗图^[66]; (c)刻蚀得到的Li/Li_2.9B_0.9S_0.1O_3.1区域表面/界面/体相的B 1s, S 2p, O 1s, Li 1s谱图^[66]

Figure 7. (a) F 1s and P 2p (right) spectra of LiFSI-treated Li₃PS₄ from cycled cell, P 2p (left) spectra of untreated Li₃PS₄ from cycled cell^[64]; (b) impedance plots of the Li/ Li_2.9B_0.9S_0.1O_3.1 symmetric cell before and after the galvanostatic test for cycles^[66]; (c) XPS spectra of B 1s, S 2p, O 1s, Li 1s for the outermost surface, interface, and electrolyte bulk regions uncovered by etching of Li/Li_2.9B_0.9S_0.1O_3.1 interface area^[66].

DownLoad: Full-Size Img PowerPoint

图 8 (a) DAISY-BAT系统的示意图^[69]; (b)利用离子枪溅射金属靶材构筑界面以实现原位XPS的过程示意图^[70]

Figure 8. (a) Scheme of the DAISY-BAT system^[69]; (b) scheme of performing in situ XPS using ion gun to sputter the fixed metal target to build the interface^[70].

DownLoad: Full-Size Img PowerPoint

图 9 (a) LLTO表面不同锂沉积时间的Ti 2p, La 3d, O 1s谱以及Ti 2p瀑布图^[70]; (b) 31 nm金属锂沉积过程中Li₁₀GeP₂S₁₂表面的S 2p, Ge 3d和P 2p-Ge 3p谱图^[53]; (c) Li_2.94PO_3.5N_0.31的结构和磷酸盐结构中N的结合情况示意图^[73,74]; (d)金属锂沉积过程中LiPON表面的O 1s, N 1s, P 2p, Li 1s和价带图^[76]

Figure 9. (a) Ti 2p, La 3d, O 1s detail spectra and Ti 2p waterfall plot for different Li metal deposition times on LLTO surface^[70]; (b) S 2p, Ge 3d, and P 2p-Ge 3p detail spectra during 31 nm Li metal deposition on Li₁₀GeP₂S₁₂ surface^[53]; (c) scheme of Li_2.94PO_3.5N_0.31 structure and possible N configurations in phosphate structures^[73,74]; (d) O 1s, N 1s, P 2p, Li 1s, and valence band spectra of LiPON surface during Li metal deposition^[76].

DownLoad: Full-Size Img PowerPoint

图 10 (a)电化学电池的负极界面原位XPS测试示意图; (b)不同电势下Li/Ga-LLZO界面的O 1s, Li 1s, La 4d, Zr 3d谱图^[71]; (c)原位XPS装置示意图; (d)电化学极化中混合正极的S 2p谱图^[59]

Figure 10. (a) Scheme of the configuration of the anode surface of electrochemical cell for in situ XPS; (b) in situ XPS spectra of O 1s, Li 1s, La 4d, and Zr 3d at the Li/Ga-doped LLZO interphase as a function of potential^[71]; (c) scheme of the measurement setup for in situ XPS; (d) S 2p spectra of composite cathode during electrochemical polarization^[59].

DownLoad: Full-Size Img PowerPoint

图 11 (a) LiPON沉积过程中LiCoO₂表面的Co 2p, O 1s, P 2p和价带谱图; (b) LiCoO₂内层电子结合能, LiPON P 2p电子结合能和表面功函数在沉积过程中的变化; (c)金属锂沉积过程中LiPON内层电子结合能的变化; (d)Li/LiPON/LiCoO₂ SSLIB的能带图^[12]

Figure 11. (a) Co 2p, O 1s, P 2p and valence band spectra of LiCoO₂ surface during the deposition of LiPON; (b) evolution of the core level binding energies of the LiCoO₂ substrate and the P 2p binding energy of the covering LiPON layer as a function of deposition time; (c) evolution of the binding energies during the stepwise evaporation of lithium on top of LiPON; (d) energy band diagram of Li/LiPON/LiCoO₂ SSLIB^[12].

DownLoad: Full-Size Img PowerPoint

图 12 (a)全固态operando XPS电池的结构示意图^[83]; (b) Operando XPS电池和标准电池工作电极的循环伏安测试结果^[83]; (c) S 2p, P 2p, Co 3p-Li 1s-Fe 3p谱图在operando XPS测试过程中的变化^[83]

Figure 12. (a) An operando XPS cell design for all-solid-state batteries^[83]; (b) cyclic voltammetry measurements of the work electrodes of the operando XPS cell and a standard test cell^[83]; (c) evolution of S 2p, P 2p, and Co 3p-Li 1s-Fe 3p core level spectra recorded during the operando XPS measurements^[83].

DownLoad: Full-Size Img PowerPoint

图 13 (a)虚拟电极法实现operando XPS测试的原理图和原始、充电、放电状态下Li₂S-P₂S₅表面的Li 1s谱图变化^[85]; (b)各XPS谱图及拟合结果在operando XPS过程中的变化^[85]

Figure 13. (a) Schematic of operando XPS measurements via virtual electrode cycling and the evolution of Li 1s spectra on Li₂S-P₂S₅ surface during the cycling process^[85]; (b) evolution of XPS spectra showing peak deconvolution during operando XPS measurements^[85].

DownLoad: Full-Size Img PowerPoint

图 14 (a) SEI各组分充电过程中结合能的位移^[85]; (b) SEI各组分的过电位及得到的SEI结构示意图^[85]

Figure 14. (a) Binding energy shifts of each SEI phase composition during charging process^[85]; (b) overpotential of each SEI phase composition during charging process and scheme of SEI structure after charging based on the overpotential^[85].

DownLoad: Full-Size Img PowerPoint

map

[1]	Scrosati B, Garche J 2010 J. Power Sources 195 2419 Google Scholar
[2]	Wen J, Yu Y, Chen C 2012 Mater. Express 2 197 Google Scholar
[3]	Xiang Y, Li X, Cheng Y, Sun X, Yang Y 2020 Mater. Today 36 139 Google Scholar
[4]	Wang H, Liu Y, Li Y, Cui Y 2019 Electrochem. Energy Rev. 2 509 Google Scholar
[5]	Kim J G, Son B, Mukherjee S, Schuppert N, Bates A, Kwon O, Choi M J, Chung H Y, Park S 2015 J. Power Sources 282 299 Google Scholar
[6]	Wang P, Qu W, Song W L, Chen H, Chen R, Fang D 2019 Adv. Funct. Mater. 29 1900950
[7]	Shen Z, Zhang W, Zhu G, Huang Y, Feng Q, Lu Y 2020 Small Methods 4 1900592 Google Scholar
[8]	Xu L, Tang S, Cheng Y, Wang K, Liang J, Liu C, Cao Y, Wei F, Mai L 2018 Joule 2 1991 Google Scholar
[9]	Colclasure A M, Smith K A, Kee R J 2011 Electrochim. Acta 58 33 Google Scholar
[10]	Chen W, Ou Z, Tang H, Wang H, Yang Y 2008 Electrochim. Acta 53 4414 Google Scholar
[11]	Wang A, Kadam S, Li H, Shi S, Qi Y 2018 NPJ Comput. Mater. 4 15 Google Scholar
[12]	Schwöbel A, Jaegermann W, Hausbrand R 2016 Solid State Ionics 288 224 Google Scholar
[13]	Brundle C R 1974 J. Vac. Sci. Technol. 11 212 Google Scholar
[14]	Watts J F, Wolstenholme J 2003 An Introduction to Surface Analysis by XPS and AES (Chichester: John Wiley & Sons) pp1–14
[15]	Watts J F, Wolstenholme J 2003 An Introduction to Surface Analysis by XPS and AES (Chichester: John Wiley & Sons) pp59–76
[16]	Meunier G, Dormoy R, Levasseur A 1989 Mater. Sci. Eng., B 3 19 Google Scholar
[17]	Ueda S 2013 J. Electron Spectrosc. Relat. Phenom. 190 235 Google Scholar
[18]	Zhao W, Yi J, He P, Zhou H 2019 Electrochem. Energy Rev. 2 574 Google Scholar
[19]	Reddy M V, Julien C M, Mauger A, Zaghib K 2020 Nanomaterials 10 1606 Google Scholar
[20]	Manthiram A, Yu X, Wang S 2017 Nat. Rev. Mater. 2 16103 Google Scholar
[21]	Murugan R, Thangadurai V, Weppner W 2007 Angew. Chem. Int. Ed. 46 7778 Google Scholar
[22]	Sudo R, Nakata Y, Ishiguro K, Matsui M, Hirano A, Takeda Y, Yamamoto O, Imanishi N 2014 Solid State Ionics 262 151 Google Scholar
[23]	Luo W, Gong Y, Zhu Y, Fu K K, Dai J, Lacey S D, Wang C, Liu B, Han X, Mo Y, Wachsman E D, Hu L 2016 J. Am. Chem. Soc. 138 12258 Google Scholar
[24]	Meng J, Zhang Y, Zhou X, Lei M, Li C 2020 Nat. Commun. 11 3716 Google Scholar
[25]	Sharafi A, Yu S, Naguib M, Lee M, Ma C, Meyer H M, Nanda J, Chi M, Siegel D J, Sakamoto J 2017 J. Mater. Chem. A 5 13475 Google Scholar
[26]	Wu J F, Pu B W, Wang D, Shi S Q, Zhao N, Guo X, Guo X 2019 ACS Appl. Mater. Interfaces 11 898 Google Scholar
[27]	Samson A J, Hofstetter K, Bag S, Thangadurai V 2019 Energy Environ. Sci. 12 2957 Google Scholar
[28]	Li Y, Wang Z, Cao Y, Du F, Chen C, Cui Z, Guo X 2015 Electrochim. Acta 180 37 Google Scholar
[29]	Ohta S, Kobayashi T, Asaoka T 2011 J. Power Sources 196 3342 Google Scholar
[30]	Zhu Y, He X, Mo Y 2016 J. Mater. Chem. A 4 3253 Google Scholar
[31]	Han F, Zhu Y, He X, Mo Y, Wang C 2016 Adv. Energy Mater. 6 1501590 Google Scholar
[32]	Wolfenstine J, Allen J L, Read J, Sakamoto J 2013 J. Mater. Sci. 48 5846 Google Scholar
[33]	Tan D H S, Banerjee A, Chen Z, Meng Y S 2020 Nat. Nanotechnol. 15 170 Google Scholar
[34]	Connell J G, Zhu Y, Zapol P, Tepavcevic S, Sharafi A, Sakamoto J, Curtiss L A, Fong D D, Freeland J W, Markovic N M 2018 ACS Appl. Mater. Interfaces 10 17471 Google Scholar
[35]	Zhu J, Zhao J, Xiang Y, Lin M, Wang H, Zheng B, He H, Wu Q, Huang J Y, Yang Y 2020 Chem. Mater. 32 4998 Google Scholar
[36]	Sharafi A, Meyer H M, Nanda J, Wolfenstine J, Sakamoto J 2016 J. Power Sources 302 135 Google Scholar
[37]	Yu S, Siegel D J 2017 Chem. Mater. 29 9639 Google Scholar
[38]	Pesci F M, Brugge R H, Hekselman A K O, Cavallaro A, Chater R J, Aguadero A 2018 J. Mater. Chem. A 6 19817 Google Scholar
[39]	Han F, Westover A S, Yue J, Fan X, Wang F, Chi M, Leonard D N, Dudney N J, Wang H, Wang C 2019 Nat. Energy 4 187 Google Scholar
[40]	Haruyama J, Sodeyama K, Tateyama Y 2017 ACS Appl. Mater. Interfaces 9 286 Google Scholar
[41]	Zarabian M, Bartolini M, Pereira-Almao P, Thangadurai V 2017 J. Electrochem. Soc. 164 A1133 Google Scholar
[42]	Liu Y, Sun Q, Liu J, Norouzi Banis M, Zhao Y, Wang B, Adair K, Hu Y, Xiao Q, Zhang C, Zhang L, Lu S, Huang H, Song X, Sun X 2020 ACS Appl. Mater. Interfaces 12 2293 Google Scholar
[43]	Trevey J E, Jung Y S, Lee S H 2011 Electrochim. Acta 56 4243 Google Scholar
[44]	Mizuno F, Hayashi A, Tadanaga K, Tatsumisago M 2005 Adv. Mater. 17 918 Google Scholar
[45]	Kanno R, Murayama M 2001 J. Electrochem. Soc. 148 A742 Google Scholar
[46]	Kanno R, Hata T, Kawamoto Y, Irie M 2000 Solid State Ionics 130 97 Google Scholar
[47]	Kamaya N, Homma K, Yamakawa Y, Hirayama M, Kanno R, Yonemura M, Kamiyama T, Kato Y, Hama S, Kawamoto K, Mitsui A 2011 Nat. Mater. 10 682 Google Scholar
[48]	Kudu Ö U, Famprikis T, Fleutot B, Braida M-D, Le Mercier T, Islam M S, Masquelier C 2018 J. Power Sources 407 31 Google Scholar
[49]	Mizuno F, Hayashi A, Tadanaga K, Tatsumisago M 2006 Solid State Ionics 177 2721 Google Scholar
[50]	Liu Z, Fu W, Payzant E A, Yu X, Wu Z, Dudney N J, Kiggans J, Hong K, Rondinone A J, Liang C 2013 J. Am. Chem. Soc. 135 975 Google Scholar
[51]	Dietrich C, Weber D A, Culver S, Senyshyn A, Sedlmaier S J, Indris S, Janek J, Zeier W G 2017 Inorg. Chem. 56 6681 Google Scholar
[52]	Seino Y, Ota T, Takada K, Hayashi A, Tatsumisago M 2014 Energy Environ. Sci. 7 627 Google Scholar
[53]	Wenzel S, Randau S, Leichtweiß T, Weber D A, Sann J, Zeier W G, Janek J 2016 Chem. Mater. 28 2400 Google Scholar
[54]	Zhou P, Wang J, Cheng F, Li F, Chen J 2016 Chem. Commun. 52 6091 Google Scholar
[55]	Boulineau S, Courty M, Tarascon J M, Viallet V 2012 Solid State Ionics 221 1 Google Scholar
[56]	Zhu Y, He X, Mo Y 2015 ACS Appl. Mater. Interfaces 7 23685 Google Scholar
[57]	Auvergniot J, Cassel A, Foix D, Viallet V, Seznec V, Dedryvère R 2017 Solid State Ionics 300 78 Google Scholar
[58]	Gao Y, Wang D, Li Y C, Yu Z, Mallouk T E, Wang D 2018 Angew. Chem. Int. Ed. 57 13608 Google Scholar
[59]	Koerver R, Walther F, Aygün I, Sann J, Dietrich C, Zeier W G, Janek J 2017 J. Mater. Chem. A 5 22750 Google Scholar
[60]	Du M, Liao K, Lu Q, Shao Z 2019 Energy Environ. Sci. 12 1780 Google Scholar
[61]	Ni X, Qian T, Liu X, Xu N, Liu J, Yan C 2018 Adv. Funct. Mater. 28 1706513 Google Scholar
[62]	Zhang L, Zhang K, Shi Z, Zhang S 2017 Langmuir 33 11164 Google Scholar
[63]	Shi X, Pang Y, Wang B, Sun H, Wang X, Li Y, Yang J, Li H W, Zheng S 2020 Mater. Today Nano 10 100079 Google Scholar
[64]	Fan X, Ji X, Han F, Yue J, Chen J, Chen L, Deng T, Jiang J, Wang C 2018 Sci. Adv. 4 eaau9245 Google Scholar
[65]	Chang X, Liu H, Yang H, Di J, Tang W, Fu H, Li M, Liu R 2020 J. Materiomics 6 54 Google Scholar
[66]	Nagao K, Suyama M, Kato A, Hotehama C, Deguchi M, Sakuda A, Hayashi A, Tatsumisago M 2019 ACS Appl. Energy Mater. 2 3042 Google Scholar
[67]	Liang J Y, Zhang X D, Zeng X X, Yan M, Yin Y X, Xin S, Wang W P, Wu X W, Shi J L, Wan L J, Guo Y G 2020 Angew. Chem. Int. Ed. 59 6585 Google Scholar
[68]	Tripathi A M, Su W N, Hwang B J 2018 Chem. Soc. Rev. 47 736 Google Scholar
[69]	Sicolo S, Fingerle M, Hausbrand R, Albe K 2017 J. Power Sources 354 124 Google Scholar
[70]	Wenzel S, Leichtweiss T, Krüger D, Sann J, Janek J 2015 Solid State Ionics. 278 98 Google Scholar
[71]	Liu Z, Li G, A. Borodin, Liu X, Li Y, Endres F 2019 J. Solid State Electrochem. 23 2107 Google Scholar
[72]	Jones S D, Akridge J R, Shokoohi F K 1994 Solid State Ionics 69 357 Google Scholar
[73]	Lacivita V, Artrith N, Ceder G 2018 Chem. Mater. 30 7077 Google Scholar
[74]	Lacivita V, Westover A S, Kercher A, Phillip N D, Yang G, Veith G, Ceder G, Dudney N J 2018 J. Am. Chem. Soc. 140 11029 Google Scholar
[75]	Yu X, Bates J B, Jellison G E, Hart F X 1997 J. Electrochem. Soc. 144 524 Google Scholar
[76]	Schwöbel A, Hausbrand R, Jaegermann W 2015 Solid State Ionics 273 51 Google Scholar
[77]	Nazri G 1988 MRS Proc. 135 117
[78]	Nazri G 1989 Solid State Ionics 34 97 Google Scholar
[79]	Maier J, Bunsenges B 1985 Phys. Chem. 89 355
[80]	Guo X, Chen C 2016 Acta. Chim. Slov. 63 3
[81]	Bañares M A 2005 Catal. Today 100 71 Google Scholar
[82]	Palomares V, Sharma N 2019 Front. Energy Res. 7 10 Google Scholar
[83]	Wu X, Villevieille C, Novák P, El Kazzi M 2018 Phys. Chem. Chem. Phys. 20 11123 Google Scholar
[84]	Nelson Weker J, Toney M F 2015 Adv. Funct. Mater. 25 1622 Google Scholar
[85]	Wood K N, Steirer K X, Hafner S E, et al. 2018 Nat. Commun. 9 2490 Google Scholar

[1]	Li Mei, Zhong Shu-Ying, Hu Jun-Ping, Sun Bao-Zhen, Xu Bo. Migration properties of Li⁺in Li_1+xAl_xTi_2–x(PO₄)₃. Acta Physica Sinica, 2024, 73(13): 138201. doi: 10.7498/aps.73.20240044
[2]	You Yi-Wei, Cui Jian-Wen, Zhang Xiao-Feng, Zheng Feng, Wu Shun-Qing, Zhu Zi-Zhong. Properties of lithium phosphorus oxynitride (LiPON) solid electrolyte - Li anode interfaces. Acta Physica Sinica, 2021, 70(13): 136801. doi: 10.7498/aps.70.20202214
[3]	Zhang Qiao-Bao, Gong Zheng-Liang, Yang Yong. Advance in interface and characterizations of sulfide solid electrolyte materials. Acta Physica Sinica, 2020, 69(22): 228803. doi: 10.7498/aps.69.20201581
[4]	Feng Wu-Liang, Wang Fei, Zhou Xing, Ji Xiao, Han Fu-Dong, Wang Chun-Sheng. Stability of interphase between solid state electrolyte and electrode. Acta Physica Sinica, 2020, 69(22): 228206. doi: 10.7498/aps.69.20201554
[5]	Zhang Nian, Ren Guo-Xi, Zhang Hui, Zhou Deng, Liu Xiao-Song. Research progress of interface problems and optimization of garnet-type solid electrolyte. Acta Physica Sinica, 2020, 69(22): 228806. doi: 10.7498/aps.69.20201533
[6]	Guo Li-Qiang, Tao Jian, Wen Juan, Cheng Guang-Gui, Yuan Ning-Yi, Ding Jian-Ning. Corn starch solid electrolyte gated proton/electron hybrid synaptic transistor. Acta Physica Sinica, 2017, 66(16): 168501. doi: 10.7498/aps.66.168501
[7]	Ma Hao, Liu Lei, Lu Xue-Sen, Liu Su-Ping, Shi Jian-Ying. Electronic structure and transport properties of cathode material Li2FeSiO4 for lithium-ion battery. Acta Physica Sinica, 2015, 64(24): 248201. doi: 10.7498/aps.64.248201
[8]	Yang Fa-Zhan, Shen Li-Ru, Wang Shi-Qing, Tang De-Li, Jin Fa-Ya, Liu Hai-Feng. UV Raman and XPS studies of hydrogenous diamond-like carbon films prepared by PECVD. Acta Physica Sinica, 2013, 62(1): 017802. doi: 10.7498/aps.62.017802
[9]	Han Lu-Hui, Zhang Chong-Hong, Zhang Li-Qing, Yang Yi-Tao, Song Yin, Sun You-Mei. X-ray photoelectron spectroscopy study on GaN crystal irradiated by slow highly charged ions. Acta Physica Sinica, 2010, 59(7): 4584-4590. doi: 10.7498/aps.59.4584
[10]	Wu Hai-Fei, Zhang Han-Jie, Liao Qing, Lu Yun-Hao, Si Jian-Xiao, Li Hai-Yang, Bao Shi-Ning, Wu Hui-Zhen, He Pi-Mo. Mn/PbTe(111) interface behavior studied by photoemission. Acta Physica Sinica, 2009, 58(2): 1310-1315. doi: 10.7498/aps.58.1310
[11]	Wang Guo-Dong, Zhang Wang, Zhang Wen-Hua, Li Zong-Mu, Xu Fa-Qiang. Synchrotron radiation photoemission studies on Fe/ZnO(0001) interface. Acta Physica Sinica, 2007, 56(6): 3468-3472. doi: 10.7498/aps.56.3468
[12]	LI Ya, Chen Ling-Yan, Zhang Zhe, Wu Yong-Gang, Qiao Yi, Xu Wei-Xin. . Acta Physica Sinica, 2001, 50(1): 79-82. doi: 10.7498/aps.50.79
[13]	BAN DA-YAN, FANG RONG-CHUAN, XUE JIAN-GENG, LU ER-DONG, XU SHI-HONG, XU PENG-SHOU. VALENCE BAND OFFSETS OF Si/ZnS POLAR INTERFACES: A SYNCHROTRON RADIATION PHOTOEMISSION STUDY. Acta Physica Sinica, 1997, 46(9): 1817-1825. doi: 10.7498/aps.46.1817
[14]	Shen Dian-Hong, Bao Chang-Lin, Lu Hua, Zhang Xiao-Jun, Lin Zhang-Da. . Acta Physica Sinica, 1995, 44(2): 259-265. doi: 10.7498/aps.44.259
[15]	CHEN YAN, DONG GUO-SHENG, ZHANG MING, Jin Xiao-Feng, LU ER-DONG, PAN HAI-BING, XU PENG-SHOU, ZHANG XIN-YI, FAN CHAO-YANG. . Acta Physica Sinica, 1995, 44(1): 145-151. doi: 10.7498/aps.44.145
[16]	LU XUE-KUN, HOU XIAO-YUAN, DONG GUO-SHENG, DING XUN-MIN. PHOTOELECTRON SPECTROSCOPY STUDIES OF α-P/GaAs (100) INTERFACES. Acta Physica Sinica, 1992, 41(4): 689-696. doi: 10.7498/aps.41.689
[17]	SHI YI-SHENG, ZHAO TE-XIU, LIU HONG-TU, WANG XIAO-PING. XPS AND AES STUDY FOR Pd/W/Si(lll) BILAYER INTERFACE. Acta Physica Sinica, 1992, 41(11): 1849-1855. doi: 10.7498/aps.41.1849
[18]	MENG GE, SHEN DIAN-HONG, LI NAN, XIE KAN, LIN ZHANG-DA, WANG YU-HE, LI LIN. XPS STUDIES OF Ti/BiSMUTH-BASED SUPERCONDUCTOR INTERFACE REACTIONS. Acta Physica Sinica, 1991, 40(12): 1992-1998. doi: 10.7498/aps.40.1992
[19]	ZHONG ZHAN-TIAN, WANG DA-WEN, LIAO XIAN-BO, FAN YUE, LI CHENG-FANG, MOU SHAN-MING. XPS AND AES STUDY FOR Au/a-Si:H INTERFACE. Acta Physica Sinica, 1991, 40(2): 275-280. doi: 10.7498/aps.40.275
[20]	ZHU BIN, WANG DA-ZHI, YU WEN-HAI. CONDUCTANCE OF HIGH-VALENCE IONS IN MONTMORILLONITE SOLID ELECTROLYTES. Acta Physica Sinica, 1988, 37(8): 1307-1314. doi: 10.7498/aps.37.1307

Catalog

Vol. 70, Issue 17 - 2021-09-05

Metrics

Abstract views: 13128
PDF Downloads: 514