石榴石型固态电解质表界面问题及优化的研究进展

张念; 任国玺; 章辉; 周櫈; 刘啸嵩

doi:10.7498/aps.69.20201533

摘要

随着对能源存储设备输出和安全性能等方面需求的不断提升, 全固态电池展示了替代传统液态锂离子电池占据新能源市场的潜力. 石榴石型Li₇La₃Zr₂O₁₂固体电解质具有高离子导率且对于锂金属稳定, 是最受人瞩目的固体电解质材料之一. 但是, 固-固界面不良接触导致的巨大界面电阻以及由于锂的不均匀沉积和分解导致的锂枝晶生长等问题严重阻碍了全固态电池的发展. 本综述针对石榴石型全固态电池突出的界面问题, 详细论述了Li₇La₃Zr₂O₁₂表面碳酸锂问题的研究现状; 讨论了锂金属负极和固态电解质的界面浸润性以及锂枝晶生长问题, 给出了构建理想界面的关键因素; 阐述了优化正极与石榴石型固体电解质界面的具体方法以及改善界面润湿性的思路. 本文还展望了未来石榴石型全固态锂离子电池可能的发展方向, 为全固态锂离子电池的发展和应用提供了借鉴.

关键词:

Abstract

With the increasing demand for storage devices with higher energy output and better safety performance, all-solid-state batteries show their potential to replace the traditional liquid-based Li-ion batteries in the future storage market. Garnet-type Li₇La₃Zr₂O₁₂ is one of the most attractive solid electrolyte materials because of its high ionic conductivity and stability to lithium metal. However, the large interfacial resistance originating from the insufficient solid-solid contact and the penetration of the lithium dendrite due to the inhomogeneous dissolution and deposition of lithium, hinder the all-solid-state batteries from developing. Focusing on the main interfacial problems in garnet-type all-solid battery, this review provides a fundamental understanding of the Li₂CO₃ issues in Li₇La₃Zr₂O₁₂ solid electrolyte and addresses the key factors influencing Li/ Li₇La₃Zr₂O₁₂/cathode interfacial wettability and the growth of Li dendrite, thus giving the key factors of constructing ideal interfaces. Finally, the possible research direction of garnet-type all-solid-state battery in the future is also prospected, which provides a guidance for developing and using all-solid-state batteries.

Keywords:

作者及机构信息

1.
中国科学院上海微系统与信息技术研究所, 功能材料国家重点实验室, 上海　200050

2.
天目湖先进储能技术研究院, 溧阳　213300

3.
上海科技大学物质学院, 上海　201210

通信作者: 刘啸嵩, xliu3@mail.sim.ac.cn

基金项目: 国家自然科学基金(批准号: 11905283, U1632269, 11227902)和国家重点基础研究发展计划(批准号: 2019YFA0405600)资助的课题

Authors and contacts

1.
State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Microsystem and Information Technology, Chinese Academy of Sciences, Shanghai 200050, China

2.
Tianmu Lake Institute of Advanced Energy Storage Technologies, Liyang 213300, China

3.
School of Physical Science and Technology, Shanghai Tech University, Shanghai 201210, China

Corresponding author: Liu Xiao-Song, xliu3@mail.sim.ac.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 11905283, U1632269, 11227902) and the National Key R&D Program of China (Grant No. 2019YFA0405600)

文章全文 : translate this paragraph

参考文献

[1]	Xu M, Fei L, Zhang W, Li T, Lu W, Zhang N, Lai Y, Zhang Z, Fang J, Zhang K, Li J, Huang H 2017 Nano. Lett. 17 1670 Google Scholar
[2]	Xu Q, Li J Y, Sun J K, Yin Y X, Wan L J, Guo Y G 2017 Adv. Energy Mater. 7 1601481 Google Scholar
[3]	Yang C P, Yin Y X, Zhang S F, Li N W, Guo Y G 2015 Nat. Commun. 6 8058 Google Scholar
[4]	Cheng X B, Zhang R, Zhao C Z, Zhang Q 2017 Chem. Rev. 117 10403 Google Scholar
[5]	Luo W, Gong Y, Zhu Y, Li Y, Yao Y, Zhang Y, Fu K K, Pastel G, Lin C F, Mo Y, Wachsman E D, Hu L 2017 Adv. Mater. 29 Google Scholar
[6]	Zhou F, Xin S, Liang H W, Song L T, Yu S H 2014 Angew. Chem. Int. Ed. Engl. 53 11552 Google Scholar
[7]	Xin S, You Y, Wang S, Gao H C, Yin Y X, Guo Y G 2017 ACS Energy Lett. 2 1385 Google Scholar
[8]	Yu B C, Park K, Jang J H, Goodenough J B 2016 ACS Energy Lett. 1 633 Google Scholar
[9]	Lin D, Zhuo D, Liu Y, Cui Y 2016 J. Am. Chem. Soc. 138 11044 Google Scholar
[10]	Zheng G, Wang C, Pei A, Lopez J, Shi F, Chen Z, Sendek A D, Lee H W, Lu Z, Schneider H, Safont-Sempere M M, Chu S, Bao Z, Cui Y 2016 ACS Energy Lett. 1 1247 Google Scholar
[11]	Sacci R L, Black J M, Balke N, Dudney N J, More K L, Unocic R R 2015 Nano Lett. 15 2011 Google Scholar
[12]	Chang H J, Ilott A J, Trease N M, Mohammadi M, Jerschow A, Grey C P 2015 J. Am. Chem. Soc. 137 15209 Google Scholar
[13]	Xu R C, Xia X H, Zhang S Z, Xie D, Wang X L, Tu J P 2018 Electrochim. Acta 284 177 Google Scholar
[14]	Liu J, Xu J, Lin Y, Li J, Lai Y, Yuan C, Zhang J, Zhu K 2013 Acta Chim. Sinica 71 869 Google Scholar
[15]	Kobayashi T, Imade Y, Shishihara D, Homma K, Nagao M, Watanabe R, Yokoi T, Yamada A, Kanno R, Tatsumi T 2008 J. Power Sources 182 621 Google Scholar
[16]	Kim H, Ding Y, Kohl P A 2012 J. Power Sources 198 281 Google Scholar
[17]	Anantharamulu N, Rao K K, Rambabu G, Kumar B V, Radha V, Vithal M 2011 J. Mater. Sci. 46 2821 Google Scholar
[18]	Bonanos N, Knight K, Ellis B 1995 Solid State Ionics 79 161 Google Scholar
[19]	Kanno R, Murayama M 2001 J. Electrochem. Soc. 148 A742 Google Scholar
[20]	Zhang Z, Zhang L, Liu Y, Yu C, Yan X, Xu B, Wang L M 2018 J. Alloys Compd. 747 227 Google Scholar
[21]	Senevirathne K, Day C S, Gross M D, Lachgar A, Holzwarth N 2013 Solid State Ionics 233 95 Google Scholar
[22]	Mizuno F, Hayashi A, Tadanaga K, Tatsumisago M 2005 Adv. Mater. 17 918 Google Scholar
[23]	Ferraresi G, El Kazzi M, Czornomaz L, Tsai C L, Uhlenbruck S, Villevieille C 2018 ACS Energy Lett. 3 1006 Google Scholar
[24]	Murugan R, Thangadurai V, Weppner W 2007 Angew. Chem. Int. Ed. Engl. 46 7778 Google Scholar
[25]	Awaka J, Kijima N, Hayakawa H, Akimoto J 2009 J. Solid State Chem. 182 2046 Google Scholar
[26]	Zhou W, Wang S, Li Y, Xin S, Manthiram A, Goodenough J B 2016 J. Am. Chem. Soc. 138 9385 Google Scholar
[27]	Haruyama J, Sodeyama K, Tateyama Y 2017 ACS Appl. Mater. Interfaces 9 286 Google Scholar
[28]	Han X, Gong Y, Fu K K, He X, Hitz G T, Dai J, Pearse A, Liu B, Wang H, Rubloff G, Mo Y, Thangadurai V, Wachsman E D, Hu L 2017 Nat. Mater. 16 572 Google Scholar
[29]	Porz L, Swamy T, Sheldon B W, Rettenwander D, Frömling T, Thaman H L, Berendts S, Uecker R, Carter W C, Chiang Y M 2017 Adv. Energy Mater. 7 1701003 Google Scholar
[30]	Sharafi A, Meyer H M, Nanda J, Wolfenstine J, Sakamoto J 2016 J. Power Sources 302 135 Google Scholar
[31]	Cheng L, Crumlin E J, Chen W, Qiao R, Hou H, Franz Lux S, Zorba V, Russo R, Kostecki R, Liu Z, Persson K, Yang W, Cabana J, Richardson T, Chen G, Doeff M 2014 Phys. Chem. Chem. Phys. 16 18294 Google Scholar
[32]	Sharafi A, Kazyak E, Davis A L, Yu S, Thompson T, Siegel D J, Dasgupta N P, Sakamoto J 2017 Chem. Mater. 29 7961 Google Scholar
[33]	Huo H, Luo J, Thangadurai V, Guo X, Nan C W, Sun X 2019 ACS Energy Lett. 5 252 Google Scholar
[34]	Xia W, Xu B, Duan H, Guo Y, Kang H, Li H, Liu H 2016 ACS Appl. Mater. Interfaces 8 5335 Google Scholar
[35]	Wagner R, Rettenwander D, Redhammer G J, Tippelt G, Sabathi G, Musso M E, Stanje B, Wilkening M, Suard E, Amthauer G 2016 Inorg. Chem. 55 12211 Google Scholar
[36]	Cheng L, Wu C H, Jarry A, Chen W, Ye Y, Zhu J, Kostecki R, Persson K, Guo J, Salmeron M, Chen G, Doeff M 2015 ACS Appl. Mater. Interfaces 7 17649 Google Scholar
[37]	Sharafi A, Yu S, Naguib M, Lee M, Ma C, Meyer H M, Nanda J, Chi M, Siegel D J, Sakamoto J 2017 J. Mater. Chem. A 5 13475 Google Scholar
[38]	Ma C, Rangasamy E, Liang C, Sakamoto J, More K L, Chi M 2015 Angew. Chem. Int. Ed. Engl. 54 129 Google Scholar
[39]	Truong L, Thangadurai V 2011 Chem. Mater. 23 3970 Google Scholar
[40]	Truong L, Thangadurai V 2012 Inorg. Chem. 51 1222 Google Scholar
[41]	Brugge R H, Hekselman A K O, Cavallaro A, Pesci F M, Chater R J, Kilner J A, Aguadero A 2018 Chem. Mater. 30 3704 Google Scholar
[42]	Liu X, Chen Y, Hood Z D, Ma C, Yu S, Sharafi A, Wang H, An K, Sakamoto J, Siegel D J, Cheng Y, Jalarvo N H, Chi M 2019 Energy Environ. Sci. 12 945 Google Scholar
[43]	Zhang N, Long X, Wang Z, Yu P, Han F, Fu J, Ren G, Wu Y, Zheng S, Huang W 2018 ACS Appl. Energy Mater. 1 5968 Google Scholar
[44]	Lan W J, Dong L, Lu R Z, Chen H Y 2019 Int. J. Electrochem. Sci. 14 9695 Google Scholar
[45]	Rao R P, Gu W, Sharma N, Peterson V K, Avdeev M, Adams S 2015 Chem. Mater. 27 2903 Google Scholar
[46]	Li Y, Chen X, Dolocan A, Cui Z, Xin S, Xue L, Xu H, Park K, Goodenough J B 2018 J. Am. Chem. Soc. 140 6448 Google Scholar
[47]	Cheng L, Liu M, Mehta A, Xin H, Lin F, Persson K, Chen G, Crumlin E J, Doeff M 2018 ACS Appl. Energy Mater. 1 7244 Google Scholar
[48]	Wang C, Xie H, Ping W, Dai J, Feng G, Yao Y, He S, Weaver J, Wang H, Gaskell K, Hu L 2019 Energy Storage Mater. 17 234 Google Scholar
[49]	Li Y, Xu B, Xu H, Duan H, Lu X, Xin S, Zhou W, Xue L, Fu G, Manthiram A, Goodenough J B 2017 Angew. Chem. Int. Ed. Engl. 56 753 Google Scholar
[50]	Xu B, Li W, Duan H, Wang H, Guo Y, Li H, Liu H 2017 J. Power Sources 354 68 Google Scholar
[51]	Wu J F, Pu B W, Wang D, Shi S Q, Zhao N, Guo X X, Guo X 2019 ACS Appl. Mater. Interfaces 11 898 Google Scholar
[52]	Huo H, Chen Y, Zhao N, Lin X, Luo J, Yang X, Liu Y, Guo X, Sun X 2019 Nano Energy 61 119 Google Scholar
[53]	Harry K J, Hallinan D T, Parkinson D Y, MacDowell A A, Balsara N P 2014 Nat. Mater. 13 69 Google Scholar
[54]	Ren Y, Shen Y, Lin Y, Nan C-W 2015 Electrochem. Commun. 57 27 Google Scholar
[55]	Tsai C L, Roddatis V, Chandran C V, Ma Q, Uhlenbruck S, Bram M, Heitjans P, Guillon O 2016 ACS Appl. Mater. Interfaces 8 10617 Google Scholar
[56]	Aguesse F, Manalastas W, Buannic L, Lopez Del Amo J M, Singh G, Llordes A, Kilner J 2017 ACS Appl Mater Interfaces 9 3808 Google Scholar
[57]	Wu B, Wang S, Lochala J, Desrochers D, Liu B, Zhang W, Yang J, Xiao J 2018 Energy Environ. Sci. 11 1803 Google Scholar
[58]	Han F, Westover A S, Yue J, Fan X, Wang F, Chi M, Leonard D N, Dudney N J, Wang H, Wang C 2019 Nat. Energy 4 187 Google Scholar
[59]	Chen Y T, Jena A, Pang W K, Peterson V K, Sheu H S, Chang H, Liu R S 2017 J.Phys. Chem. C 121 15565 Google Scholar
[60]	Wang S, Xu H, Li W, Dolocan A, Manthiram A 2018 J. Am. Chem. Soc. 140 250 Google Scholar
[61]	Fu J, Yu P, Zhang N, Ren G, Zheng S, Huang W, Long X, Li H, Liu X 2019 Energy Environ. Sci. 12 1404 Google Scholar
[62]	Chen Y, He M, Zhao N, Fu J, Huo H, Zhang T, Li Y, Xu F, Guo X 2019 J. Power Sources 420 15 Google Scholar
[63]	Huo H, Chen Y, Li R, Zhao N, Luo J, Pereira da Silva J G, Mücke R, Kaghazchi P, Guo X, Sun X 2020 Energy Environ. Sci. 13 127 Google Scholar
[64]	Miara L, Windmuller A, Tsai C L, Richards W D, Ma Q, Uhlenbruck S, Guillon O, Ceder G 2016 ACS Appl. Mater. Interfaces 8 26842 Google Scholar
[65]	Zhang W, Richter F H, Culver S P, Leichtweiss T, Lozano J G, Dietrich C, Bruce P G, Zeier W G, Janek J 2018 ACS Appl. Mater. Interfaces 10 22226 Google Scholar
[66]	Yamada H, Ito T, Hongahally Basappa R, Bekarevich R, Mitsuishi K 2017 J. Power Sources 368 97 Google Scholar
[67]	Bucci G, Swamy T, Chiang Y M, Carter W C 2017 J. Mater. Chem. A 5 19422 Google Scholar
[68]	Kim K H, Iriyama Y, Yamamoto K, Kumazaki S, Asaka T, Tanabe K, Fisher C A J, Hirayama T, Murugan R, Ogumi Z 2011 J. Power Sources 196 764 Google Scholar
[69]	Ohta S, Kobayashi T, Seki J, Asaoka T 2012 J. Power Sources 202 332 Google Scholar
[70]	Kato T, Hamanaka T, Yamamoto K, Hirayama T, Sagane F, Motoyama M, Iriyama Y 2014 J. Power Sources 260 292 Google Scholar
[71]	Ren Y, Liu T, Shen Y, Lin Y, Nan C W 2016 J. Materiomics 2 256 Google Scholar
[72]	Liu B, Fu K, Gong Y, Yang C, Yao Y, Wang Y, Wang C, Kuang Y, Pastel G, Xie H, Wachsman E D, Hu L 2017 Nano Lett. 17 4917 Google Scholar
[73]	Han F, Yue J, Chen C, Zhao N, Fan X, Ma Z, Gao T, Wang F, Guo X, Wang C 2018 Joule 2 497 Google Scholar
[74]	Salmeron M 2018 Top. Catal. 61 2044 Google Scholar
[75]	Liu X, Yang W, Liu Z 2014 Adv. Mater. 26 7710 Google Scholar
[76]	Cai J, Dong Q, Han Y, Mao B-H, Zhang H, Karlsson P G, Åhlund J, Tai R Z, Yu Y, Liu Z 2019 Nucl. Sci. Tech. 30 81
[77]	Ren G, Zhang N, Feng X, Zhang H, Yu P, Zheng S, Zhou D, Tian Z, Liu X 2020 Chin. Phys. B 29 016101 Google Scholar
[78]	Chen L, Li Y, Li S P, Fan L Z, Nan C W, Goodenough J B 2018 Nano Energy 46 176 Google Scholar
[79]	Raj R, Wolfenstine J 2017 J. Power Sources 343 119 Google Scholar
[80]	Krauskopf T, Dippel R, Hartmann H, Peppler K, Mogwitz B, Richter F H, Zeier W G, Janek J 2019 Joule 3 2030 Google Scholar
[81]	Zhou G M, Tian H Z, Jin Y, Tao X Y, Liu B F, Zhang R F, Seh Z W, Zhuo D, Liu Y Y, Sun J, Zhao J, Zu C X, Wu D S, Zhang Q F, Cui Y 2017 PNAS 114 840 Google Scholar
[82]	Xu S, McOwen D W, Zhang L, Hitz G T, Wang C, Ma Z, Chen C, Luo W, Dai J, Kuang Y, Hitz E M, Fu K, Gong Y, Wachsman E D, Hu L 2018 Energy Storage Mater. 15 458 Google Scholar

施引文献

图 1 (a) 熔融的金属锂在各种界面上的浸润角; (b) 计算得到的Li–Li₂CO₃和Li–LLZO界面的附着功(W_ad)、接触角(θ)以及原子结构^[32]

Fig. 1. (a) The contact angle of molten metallic Li on different surfaces; (b) calculated work of adhesion (W_ad), contact angle (θ), and atomic structure for the Li–Li₂CO₃ and Li–LLZO interfaces^[32].

下载: 全尺寸图片幻灯片

图 2 (a) 利用铂金坩埚代替传统Al₂O₃坩埚可以有效减少暴露空气后LLZO表面碳酸锂的形成^[34]; (b) 利用快速热脉冲的处理方法可以有效去除碳酸锂, 并且使得锂损失最小化^[48]; (c) 通过添加LiF, Li₃PO₄等疏水添加剂, 或者在表面制造缺锂层, 都可以有效抑制碳酸锂的形成^[33,51]; (d) 通过快速酸处理可以除去表面碳酸锂, 得到稳定接触的界面^[52]

Fig. 2. (a) Using Pt crucible instead of alumina crucible can effectively reduce the Li₂CO₃formation on LLZO after exposed to air^[34]; (b) the rapid thermal pulsing treatment can effectively remove the Li₂CO₃ impurity and minimize Li loss^[48]; (c) adding inorganic additives such as LiF and Li₃PO₄, or creating Li-deficient compounds on the surface can eliminate Li₂CO₃ contaminants^[33,51]; (d) improving Li/LLZO interface contact by removing Li₂CO₃ via rapid acid treatment^[52].

下载: 全尺寸图片幻灯片

图 3 (a) 利用Ge作为界面缓冲材料优化Li/LLZO界面^[5]; (b) 中子深度分析装置示意图及LLZO原位探测结果^[58]; (c) 利用MoS₂作为界面缓冲材料优化Li/LLZO界面, 和界面转化反应及极化原理示意图^[61]

Fig. 3. (a) Using Ge as buffer layer to modify Li/LLZO interface^[5]; (b) schematic of the experimental set-up for operando Neutron depth profiling and the results for LLZO cell^[58]; (c) schematic diagram of the conversion reaction and the chemical evolution of the MoS₂-coating layer in the polarization process^[61].

下载: 全尺寸图片幻灯片

图 4 (a) 利用添加Nb缓冲层可以有效改善激光脉冲沉积过程中LiCoO₂/LLZO界面稳定性^[70]; (b) 利用快速热退火的方法将V₂O₅电极材料制备到LLZO片上^[72]; (c) 利用Li_2.3-_xC_0.7+_xB_0.3-_xO₃与碳酸锂反应生成LCBO改善LiCoO₂/LLZO界面示意图以及全固态电池在常温下的循环特性^[73]

Fig. 4. (a) Using Nb as buffer layer can modify the stability of LiCoO₂/LLZO interface during Pulsed Laser Deposition (PLD) process^[70]; (b) using rapid thermal annealing to melt V₂O₅ cathode onto LLZO pellet^[72]; (c) schematics of the interphase-engineered all-ceramic cathode/electrolyte by using the reaction of Li_2.3-_xC_0.7+_xB_0.3-_xO₃ with Li₂CO₃. The all sold battery can cycle well over 100 times at room temperature^[73].

下载: 全尺寸图片幻灯片

图 5 石榴石型全固态电池未来可能的研究方向^[63,78,82]

Fig. 5. Possible research directions for garnet-based all solid battery in the future^[63,78,82].

下载: 全尺寸图片幻灯片

表 1 计算得到的在298.15 K下LLZO发生水合以及碳酸化反应所需的吉布斯自由能, 其中, 前4项是反应过程中有Li⁺/H⁺交换作用对应的能量, 后2项为直接反应对应的能量^[37]

Table 1. Calculated Gibbs free energy for the hydration and carbonation of LLZO at 298.15 K. The first 4 reactions involve Li⁺/H⁺ ion exchange and the last 2 reactions assume direct hydration and carbonation of LLZO^[37].

LLZO与空气中的水和二氧化碳可能的反应过程	吉布斯自由能 ΔG/kJ·mol^–1
Li₅₆La₂₄Zr₁₆O₉₆+H₂O(g) → Li₅₅HLa₂₄Zr₁₆O₉₆+LiOH	–33
LiOH+1/2 CO₂(g) → 1/2 Li₂CO₃+1/2 H₂O(g)	–33.6
Li₅₆La₂₄Zr₁₆O₉₆+CO₂(g) → Li₅₄La₂₄Zr₁₆O₉₅+Li₂CO₃	+21.5
Li₂O+CO₂(g)→Li₂CO₃	–147.6
Li₅₆La₂₄Zr₁₆O₉₆+H₂O(g) → Li₅₄La₂₄Zr₁₆O₉₅+2 LiOH	+82.8
Li₅₆La₂₄Zr₁₆O₉₆+CO₂(g) → Li₅₄La₂₄Zr₁₆O₉₅+Li₂CO₃	+15.6

下载: 导出CSV

map

[1]	Xu M, Fei L, Zhang W, Li T, Lu W, Zhang N, Lai Y, Zhang Z, Fang J, Zhang K, Li J, Huang H 2017 Nano. Lett. 17 1670 Google Scholar
[2]	Xu Q, Li J Y, Sun J K, Yin Y X, Wan L J, Guo Y G 2017 Adv. Energy Mater. 7 1601481 Google Scholar
[3]	Yang C P, Yin Y X, Zhang S F, Li N W, Guo Y G 2015 Nat. Commun. 6 8058 Google Scholar
[4]	Cheng X B, Zhang R, Zhao C Z, Zhang Q 2017 Chem. Rev. 117 10403 Google Scholar
[5]	Luo W, Gong Y, Zhu Y, Li Y, Yao Y, Zhang Y, Fu K K, Pastel G, Lin C F, Mo Y, Wachsman E D, Hu L 2017 Adv. Mater. 29 Google Scholar
[6]	Zhou F, Xin S, Liang H W, Song L T, Yu S H 2014 Angew. Chem. Int. Ed. Engl. 53 11552 Google Scholar
[7]	Xin S, You Y, Wang S, Gao H C, Yin Y X, Guo Y G 2017 ACS Energy Lett. 2 1385 Google Scholar
[8]	Yu B C, Park K, Jang J H, Goodenough J B 2016 ACS Energy Lett. 1 633 Google Scholar
[9]	Lin D, Zhuo D, Liu Y, Cui Y 2016 J. Am. Chem. Soc. 138 11044 Google Scholar
[10]	Zheng G, Wang C, Pei A, Lopez J, Shi F, Chen Z, Sendek A D, Lee H W, Lu Z, Schneider H, Safont-Sempere M M, Chu S, Bao Z, Cui Y 2016 ACS Energy Lett. 1 1247 Google Scholar
[11]	Sacci R L, Black J M, Balke N, Dudney N J, More K L, Unocic R R 2015 Nano Lett. 15 2011 Google Scholar
[12]	Chang H J, Ilott A J, Trease N M, Mohammadi M, Jerschow A, Grey C P 2015 J. Am. Chem. Soc. 137 15209 Google Scholar
[13]	Xu R C, Xia X H, Zhang S Z, Xie D, Wang X L, Tu J P 2018 Electrochim. Acta 284 177 Google Scholar
[14]	Liu J, Xu J, Lin Y, Li J, Lai Y, Yuan C, Zhang J, Zhu K 2013 Acta Chim. Sinica 71 869 Google Scholar
[15]	Kobayashi T, Imade Y, Shishihara D, Homma K, Nagao M, Watanabe R, Yokoi T, Yamada A, Kanno R, Tatsumi T 2008 J. Power Sources 182 621 Google Scholar
[16]	Kim H, Ding Y, Kohl P A 2012 J. Power Sources 198 281 Google Scholar
[17]	Anantharamulu N, Rao K K, Rambabu G, Kumar B V, Radha V, Vithal M 2011 J. Mater. Sci. 46 2821 Google Scholar
[18]	Bonanos N, Knight K, Ellis B 1995 Solid State Ionics 79 161 Google Scholar
[19]	Kanno R, Murayama M 2001 J. Electrochem. Soc. 148 A742 Google Scholar
[20]	Zhang Z, Zhang L, Liu Y, Yu C, Yan X, Xu B, Wang L M 2018 J. Alloys Compd. 747 227 Google Scholar
[21]	Senevirathne K, Day C S, Gross M D, Lachgar A, Holzwarth N 2013 Solid State Ionics 233 95 Google Scholar
[22]	Mizuno F, Hayashi A, Tadanaga K, Tatsumisago M 2005 Adv. Mater. 17 918 Google Scholar
[23]	Ferraresi G, El Kazzi M, Czornomaz L, Tsai C L, Uhlenbruck S, Villevieille C 2018 ACS Energy Lett. 3 1006 Google Scholar
[24]	Murugan R, Thangadurai V, Weppner W 2007 Angew. Chem. Int. Ed. Engl. 46 7778 Google Scholar
[25]	Awaka J, Kijima N, Hayakawa H, Akimoto J 2009 J. Solid State Chem. 182 2046 Google Scholar
[26]	Zhou W, Wang S, Li Y, Xin S, Manthiram A, Goodenough J B 2016 J. Am. Chem. Soc. 138 9385 Google Scholar
[27]	Haruyama J, Sodeyama K, Tateyama Y 2017 ACS Appl. Mater. Interfaces 9 286 Google Scholar
[28]	Han X, Gong Y, Fu K K, He X, Hitz G T, Dai J, Pearse A, Liu B, Wang H, Rubloff G, Mo Y, Thangadurai V, Wachsman E D, Hu L 2017 Nat. Mater. 16 572 Google Scholar
[29]	Porz L, Swamy T, Sheldon B W, Rettenwander D, Frömling T, Thaman H L, Berendts S, Uecker R, Carter W C, Chiang Y M 2017 Adv. Energy Mater. 7 1701003 Google Scholar
[30]	Sharafi A, Meyer H M, Nanda J, Wolfenstine J, Sakamoto J 2016 J. Power Sources 302 135 Google Scholar
[31]	Cheng L, Crumlin E J, Chen W, Qiao R, Hou H, Franz Lux S, Zorba V, Russo R, Kostecki R, Liu Z, Persson K, Yang W, Cabana J, Richardson T, Chen G, Doeff M 2014 Phys. Chem. Chem. Phys. 16 18294 Google Scholar
[32]	Sharafi A, Kazyak E, Davis A L, Yu S, Thompson T, Siegel D J, Dasgupta N P, Sakamoto J 2017 Chem. Mater. 29 7961 Google Scholar
[33]	Huo H, Luo J, Thangadurai V, Guo X, Nan C W, Sun X 2019 ACS Energy Lett. 5 252 Google Scholar
[34]	Xia W, Xu B, Duan H, Guo Y, Kang H, Li H, Liu H 2016 ACS Appl. Mater. Interfaces 8 5335 Google Scholar
[35]	Wagner R, Rettenwander D, Redhammer G J, Tippelt G, Sabathi G, Musso M E, Stanje B, Wilkening M, Suard E, Amthauer G 2016 Inorg. Chem. 55 12211 Google Scholar
[36]	Cheng L, Wu C H, Jarry A, Chen W, Ye Y, Zhu J, Kostecki R, Persson K, Guo J, Salmeron M, Chen G, Doeff M 2015 ACS Appl. Mater. Interfaces 7 17649 Google Scholar
[37]	Sharafi A, Yu S, Naguib M, Lee M, Ma C, Meyer H M, Nanda J, Chi M, Siegel D J, Sakamoto J 2017 J. Mater. Chem. A 5 13475 Google Scholar
[38]	Ma C, Rangasamy E, Liang C, Sakamoto J, More K L, Chi M 2015 Angew. Chem. Int. Ed. Engl. 54 129 Google Scholar
[39]	Truong L, Thangadurai V 2011 Chem. Mater. 23 3970 Google Scholar
[40]	Truong L, Thangadurai V 2012 Inorg. Chem. 51 1222 Google Scholar
[41]	Brugge R H, Hekselman A K O, Cavallaro A, Pesci F M, Chater R J, Kilner J A, Aguadero A 2018 Chem. Mater. 30 3704 Google Scholar
[42]	Liu X, Chen Y, Hood Z D, Ma C, Yu S, Sharafi A, Wang H, An K, Sakamoto J, Siegel D J, Cheng Y, Jalarvo N H, Chi M 2019 Energy Environ. Sci. 12 945 Google Scholar
[43]	Zhang N, Long X, Wang Z, Yu P, Han F, Fu J, Ren G, Wu Y, Zheng S, Huang W 2018 ACS Appl. Energy Mater. 1 5968 Google Scholar
[44]	Lan W J, Dong L, Lu R Z, Chen H Y 2019 Int. J. Electrochem. Sci. 14 9695 Google Scholar
[45]	Rao R P, Gu W, Sharma N, Peterson V K, Avdeev M, Adams S 2015 Chem. Mater. 27 2903 Google Scholar
[46]	Li Y, Chen X, Dolocan A, Cui Z, Xin S, Xue L, Xu H, Park K, Goodenough J B 2018 J. Am. Chem. Soc. 140 6448 Google Scholar
[47]	Cheng L, Liu M, Mehta A, Xin H, Lin F, Persson K, Chen G, Crumlin E J, Doeff M 2018 ACS Appl. Energy Mater. 1 7244 Google Scholar
[48]	Wang C, Xie H, Ping W, Dai J, Feng G, Yao Y, He S, Weaver J, Wang H, Gaskell K, Hu L 2019 Energy Storage Mater. 17 234 Google Scholar
[49]	Li Y, Xu B, Xu H, Duan H, Lu X, Xin S, Zhou W, Xue L, Fu G, Manthiram A, Goodenough J B 2017 Angew. Chem. Int. Ed. Engl. 56 753 Google Scholar
[50]	Xu B, Li W, Duan H, Wang H, Guo Y, Li H, Liu H 2017 J. Power Sources 354 68 Google Scholar
[51]	Wu J F, Pu B W, Wang D, Shi S Q, Zhao N, Guo X X, Guo X 2019 ACS Appl. Mater. Interfaces 11 898 Google Scholar
[52]	Huo H, Chen Y, Zhao N, Lin X, Luo J, Yang X, Liu Y, Guo X, Sun X 2019 Nano Energy 61 119 Google Scholar
[53]	Harry K J, Hallinan D T, Parkinson D Y, MacDowell A A, Balsara N P 2014 Nat. Mater. 13 69 Google Scholar
[54]	Ren Y, Shen Y, Lin Y, Nan C-W 2015 Electrochem. Commun. 57 27 Google Scholar
[55]	Tsai C L, Roddatis V, Chandran C V, Ma Q, Uhlenbruck S, Bram M, Heitjans P, Guillon O 2016 ACS Appl. Mater. Interfaces 8 10617 Google Scholar
[56]	Aguesse F, Manalastas W, Buannic L, Lopez Del Amo J M, Singh G, Llordes A, Kilner J 2017 ACS Appl Mater Interfaces 9 3808 Google Scholar
[57]	Wu B, Wang S, Lochala J, Desrochers D, Liu B, Zhang W, Yang J, Xiao J 2018 Energy Environ. Sci. 11 1803 Google Scholar
[58]	Han F, Westover A S, Yue J, Fan X, Wang F, Chi M, Leonard D N, Dudney N J, Wang H, Wang C 2019 Nat. Energy 4 187 Google Scholar
[59]	Chen Y T, Jena A, Pang W K, Peterson V K, Sheu H S, Chang H, Liu R S 2017 J.Phys. Chem. C 121 15565 Google Scholar
[60]	Wang S, Xu H, Li W, Dolocan A, Manthiram A 2018 J. Am. Chem. Soc. 140 250 Google Scholar
[61]	Fu J, Yu P, Zhang N, Ren G, Zheng S, Huang W, Long X, Li H, Liu X 2019 Energy Environ. Sci. 12 1404 Google Scholar
[62]	Chen Y, He M, Zhao N, Fu J, Huo H, Zhang T, Li Y, Xu F, Guo X 2019 J. Power Sources 420 15 Google Scholar
[63]	Huo H, Chen Y, Li R, Zhao N, Luo J, Pereira da Silva J G, Mücke R, Kaghazchi P, Guo X, Sun X 2020 Energy Environ. Sci. 13 127 Google Scholar
[64]	Miara L, Windmuller A, Tsai C L, Richards W D, Ma Q, Uhlenbruck S, Guillon O, Ceder G 2016 ACS Appl. Mater. Interfaces 8 26842 Google Scholar
[65]	Zhang W, Richter F H, Culver S P, Leichtweiss T, Lozano J G, Dietrich C, Bruce P G, Zeier W G, Janek J 2018 ACS Appl. Mater. Interfaces 10 22226 Google Scholar
[66]	Yamada H, Ito T, Hongahally Basappa R, Bekarevich R, Mitsuishi K 2017 J. Power Sources 368 97 Google Scholar
[67]	Bucci G, Swamy T, Chiang Y M, Carter W C 2017 J. Mater. Chem. A 5 19422 Google Scholar
[68]	Kim K H, Iriyama Y, Yamamoto K, Kumazaki S, Asaka T, Tanabe K, Fisher C A J, Hirayama T, Murugan R, Ogumi Z 2011 J. Power Sources 196 764 Google Scholar
[69]	Ohta S, Kobayashi T, Seki J, Asaoka T 2012 J. Power Sources 202 332 Google Scholar
[70]	Kato T, Hamanaka T, Yamamoto K, Hirayama T, Sagane F, Motoyama M, Iriyama Y 2014 J. Power Sources 260 292 Google Scholar
[71]	Ren Y, Liu T, Shen Y, Lin Y, Nan C W 2016 J. Materiomics 2 256 Google Scholar
[72]	Liu B, Fu K, Gong Y, Yang C, Yao Y, Wang Y, Wang C, Kuang Y, Pastel G, Xie H, Wachsman E D, Hu L 2017 Nano Lett. 17 4917 Google Scholar
[73]	Han F, Yue J, Chen C, Zhao N, Fan X, Ma Z, Gao T, Wang F, Guo X, Wang C 2018 Joule 2 497 Google Scholar
[74]	Salmeron M 2018 Top. Catal. 61 2044 Google Scholar
[75]	Liu X, Yang W, Liu Z 2014 Adv. Mater. 26 7710 Google Scholar
[76]	Cai J, Dong Q, Han Y, Mao B-H, Zhang H, Karlsson P G, Åhlund J, Tai R Z, Yu Y, Liu Z 2019 Nucl. Sci. Tech. 30 81
[77]	Ren G, Zhang N, Feng X, Zhang H, Yu P, Zheng S, Zhou D, Tian Z, Liu X 2020 Chin. Phys. B 29 016101 Google Scholar
[78]	Chen L, Li Y, Li S P, Fan L Z, Nan C W, Goodenough J B 2018 Nano Energy 46 176 Google Scholar
[79]	Raj R, Wolfenstine J 2017 J. Power Sources 343 119 Google Scholar
[80]	Krauskopf T, Dippel R, Hartmann H, Peppler K, Mogwitz B, Richter F H, Zeier W G, Janek J 2019 Joule 3 2030 Google Scholar
[81]	Zhou G M, Tian H Z, Jin Y, Tao X Y, Liu B F, Zhang R F, Seh Z W, Zhuo D, Liu Y Y, Sun J, Zhao J, Zu C X, Wu D S, Zhang Q F, Cui Y 2017 PNAS 114 840 Google Scholar
[82]	Xu S, McOwen D W, Zhang L, Hitz G T, Wang C, Ma Z, Chen C, Luo W, Dai J, Kuang Y, Hitz E M, Fu K, Gong Y, Wachsman E D, Hu L 2018 Energy Storage Mater. 15 458 Google Scholar

[1]	耿晓彬, 李顶根, 徐波. 固态电解质电池锂枝晶生长机械应力-热力学相场模拟研究. , 2023, 72(22): 220201. doi: 10.7498/aps.72.20230824
[2]	杨源, 胡乃方, 金永成, 马君, 崔光磊. 富锂正极材料在全固态锂电池中的研究进展. , 2023, 72(11): 118801. doi: 10.7498/aps.72.20230258
[3]	吴成伟, 谢国锋, 周五星. 全固态锂离子电池内部热输运研究前沿. , 2022, 71(2): 026501. doi: 10.7498/aps.71.20211887
[4]	孙盟杰, 何志群, 郑毅帆, 邵宇川. EDTA/SnO₂双层复合电子传输层在钙钛矿电池中的应用. , 2022, 71(13): 137201. doi: 10.7498/aps.71.20220074
[5]	周逸凡, 杨慕紫, 佘峰权, 龚力, 张晓琪, 陈建, 宋树芹, 谢方艳. X射线光电子能谱在固态锂离子电池界面研究中的应用. , 2021, 70(17): 178801. doi: 10.7498/aps.70.20210180
[6]	姬超, 梁春军, 由芳田, 何志群. 界面修饰对有机-无机杂化钙钛矿太阳能电池性能的影响. , 2021, 70(2): 028402. doi: 10.7498/aps.70.20201222
[7]	游逸玮, 崔建文, 张小锋, 郑锋, 吴顺情, 朱梓忠. 锂磷氧氮(LiPON)固态电解质与Li负极界面特性. , 2021, 70(13): 136801. doi: 10.7498/aps.70.20202214
[8]	陆敬予, 柯承志, 龚正良, 李德平, 慈立杰, 张力, 张桥保. 原位表征技术在全固态锂电池中的应用. , 2021, 70(19): 198102. doi: 10.7498/aps.70.20210531
[9]	张桥保, 龚正良, 杨勇. 硫化物固态电解质材料界面及其表征的研究进展. , 2020, 69(22): 228803. doi: 10.7498/aps.69.20201581
[10]	刘玉龙, 辛明杨, 丛丽娜, 谢海明. 聚氧乙烯基聚合物固态电池的界面研究进展. , 2020, 69(22): 228202. doi: 10.7498/aps.69.20201588
[11]	曹文卓, 李泉, 王胜彬, 李文俊, 李泓. 金属锂在固态电池中的沉积机理、策略及表征. , 2020, 69(22): 228204. doi: 10.7498/aps.69.20201293
[12]	余启鹏, 刘琦, 王自强, 李宝华. 全固态金属锂电池负极界面问题及解决策略. , 2020, 69(22): 228805. doi: 10.7498/aps.69.20201218
[13]	冯吴亮, 王飞, 周星, 吉晓, 韩福东, 王春生. 固态电解质与电极界面的稳定性. , 2020, 69(22): 228206. doi: 10.7498/aps.69.20201554
[14]	拱越, 谷林. 全固态电池中界面的结构演化和物质输运. , 2020, 69(22): 226801. doi: 10.7498/aps.69.20201160
[15]	张宝宝, 张成云, 张正龙, 郑海荣. 表面等离激元调控化学反应. , 2019, 68(14): 147102. doi: 10.7498/aps.68.20190345
[16]	李晓果, 张欣, 施则骄, 张海娟, 朱成军, 詹义强. n-i-p结构钙钛矿太阳能电池界面钝化的研究进展. , 2019, 68(15): 158803. doi: 10.7498/aps.68.20190468
[17]	曾娴, 杨朝晖, 张晓华. 高分子薄膜表征技术. , 2016, 65(17): 176801. doi: 10.7498/aps.65.176801
[18]	廖文英, 范万德, 李园, 陈君, 卜凡华, 李海鹏, 王新亚, 黄鼎铭. 新型全固态准晶体结构大模场光纤特性研究. , 2014, 63(3): 034206. doi: 10.7498/aps.63.034206
[19]	郭艳艳, 侯蓝田. 全固态八边形大模场光子晶体光纤的设计. , 2010, 59(6): 4036-4041. doi: 10.7498/aps.59.4036
[20]	鲁远甫, 谢仕永, 薄勇, 崔前进, 宗楠, 高宏伟, 彭钦军, 崔大复, 许祖彦. 高功率准连续波腔内和频全固态黄光激光器. , 2009, 58(2): 970-974. doi: 10.7498/aps.58.970

计量

文章访问数: 12419
PDF下载量: 486
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板