Development and application of vapor deposition technology in atomic manufacturing

Guo Qin-Min; Qin Zhi-Hui

doi:10.7498/aps.70.20201436

Abstract

With the development of future information devices towards smaller size, lower power consumption and higher performance, the size of materials used to build devices will be further reduced. Traditional “top-down” technology has encountered a bottleneck in the development of information devices on a nanoscale, while the vapor deposition technology has attracted great attention due to its ability to construct nanostructures on an atomic scale, and is considered to have the most potential to break through the existing manufacturing limits and build nano-structures directly with atoms as a “bottom-up” method. During molecular beam epitaxy, atoms and molecules of materials are deposited on the surface in an “atomic spray painting” way. By such a method, some graphene-like two-dimensional materials (e.g., silicene, germanene, stanene, borophene) have been fabricated with high quality and show many novel electronic properties, and the ultrathin films (several atomic layers) of other materials have been grown to achieve certain purposes, such as NaCl ultrathin layers for decoupling the interaction of metal substrate with the adsorbate. In an atomic layer deposition process, which can be regarded as a special modification of chemical vapor deposition, the film growth takes place in a cyclic manner. The self- limited chemical reactions are employed to insure that only one monolayer of precursor (A) molecules is adsorbed on the surface, and the subsequent self- limited reaction with the other precursor (B) allows only one monolayer of AB materials to be built. And the self- assembled monolayers composed of usually long- chain molecules can be introduced as the active or inactive layer for area- selective atomic layer deposition growth, which is very useful in fabricating nano- patterned structures. As the reverse process of atomic layer deposition, atomic-layer etching processes can remove certain materials in atomic precision. In this paper we briefly introduce the principles of the related technologies and their applications in the field of nano- electronic device processing and manufacturing, and find how to realize the precise control of the thickness and microstructure of functional materials on an atomic scale.

Keywords:

Authors and contacts

Guo Qin-Min¹,
Qin Zhi-Hui²

1.
State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China
2.
Key Laboratory for Micro/Nano Optoelectronic Devices of Ministry of Education, School of Physics and Electronics, Hunan University, Changsha 410082, China

Corresponding author: Qin Zhi-Hui, zhqin@hnu.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 51772087) and the Strategic Priority Research Program (B) of Chinese Academy of Sciences (Grant No. XDB30000000)

FullText HTML : translate this paragraph

References

[1]	冯黎, 朱雷 2020 功能材料与器件学报 26 191 Feng L, Zhu L 2020 J. Funct. Mater. Devices 26 191
[2]	庞玉莲, 邹应全 2015 信息记录材料 16 36 Google Scholar Pang Y L, Zou Y Q 2015 Info. Rec. Mater. 16 36 Google Scholar
[3]	Striccoli M 2017 Science 357 353 Google Scholar
[4]	Okazaki S 2015 Microelectron. Eng. 133 23 Google Scholar
[5]	Hong F, Blaikie R 2019 Adv. Opt. Mater. 7 1801653 Google Scholar
[6]	王霞, 吕浩, 赵秋玲, 张帅一, 谭永炎 2016 光谱学与光谱分析 36 3461 Wang X, Lü H, Zhao Q L, Zhang S Y, Tan Y Y 2016 Spectrosc. Spect. Anal. 36 3461
[7]	Fang F Z 2016 Front. Mech. Eng. Chin. 11 325 Google Scholar
[8]	Luo C, Li J F, Yang X, Wu X, Zhong S Y, Wang C L, Sun L T 2020 ACS Appl. Nano Mater. 3 4747
[9]	Martín-Palma R J, Lakhtakia A 2013 Engineered Biomimicry (Boston: Elsevier) pp383−398
[10]	LaPedus M 2018 工艺与制造 35 39 LaPedus M 2018 Prog. Fabri. 35 39
[11]	Ashurbekova K, Ashurbekova K, Botta G, Yurkevich O, Knez M 2020 Nanotechnology 31 342001 Google Scholar
[12]	Kulkarni A K 1994 B. Mater. Sci. 17 1379 Google Scholar
[13]	Mattox D M 1992 Plat. Surf. Finish. 79 60
[14]	Mattox D M 1998 Plat. Surf. Finish. 85 49
[15]	Zhu D M, Miller R A, Nagaraj B A, Bruce R W 2001 Surf. Coat. Technol. 138 1 Google Scholar
[16]	Muratore C, Walton S G, Leonhardt D, Fernsler R F 2006 J. Vac. Sci. Technol., A 24 25
[17]	Kumar T S, Prabu S B, Manivasagam G 2014 J. Mater. Eng. Perform. 23 2877 Google Scholar
[18]	Yang R B, Bachmann J, Pippel E, Berger A, Woltersdorf J, Gösele U, Nielsch K 2009 Adv. Mater. 21 3170 Google Scholar
[19]	Bao Q H, Chen C Z, Wang D G, Ji Q M, Lei T Q 2005 Appl. Surf. Sci. 252 1538 Google Scholar
[20]	Cho A Y, Arthur J R 1975 Prog. Solid State Chem. 10 157 Google Scholar
[21]	Hong M 1995 J. Cryst. Growth 150 277 Google Scholar
[22]	Spirkoska D, Colombo C, Heiss M, Abstreiter G, Morral A F I 2008 J. Phys. Condens. Matter 20 454225 Google Scholar
[23]	Wang X Q, Yoshika A 2011 Thin Film Growth (Sawston Cambridge: Woodhead Publishing) pp288−316
[24]	Howson R P, Spencer A G, Lewin R W 1988 Vacuum 38 947
[25]	Kelly P J, Arnell R D 2000 Vacuum 56 159 Google Scholar
[26]	Shi J Z, Chen C Z, Yu H J, Zhang S J 2008 B. Mater. Sci. 31 877 Google Scholar
[27]	Brauer G, Szyszka B, Vergohl M, Bandorf R 2010 Vacuum 84 1354 Google Scholar
[28]	Kopecky D, Vrnata M, Kopecka J 2015 Chem. Listy 109 183
[29]	von Wenckstern H, Kneiss M, Hassa A, Storm P, Splith D, Grundmann M 2020 Phys. Status Solidi B 257 1900626 Google Scholar
[30]	Dabrowska-Szata M 2003 Mater. Chem.Phys. 81 257 Google Scholar
[31]	Ichimiya A 2005 J. Jpn. Soc. Tribologis. 50 731
[32]	Wood C 1981 Surf. Sci. 108 L441
[33]	Chang C Z, Zhang J S, Feng X, Shen J, Zhang Z C, Guo M H, Li K, Ou Y B, Wei P, Wang L L, Ji Z Q, Feng Y, Ji S H, Chen X, Jia J F, Dai X, Fang Z, Zhang S C, He K, Wang Y Y, Lu L, Ma X C, Xue Q K 2013 Science 340 167 Google Scholar
[34]	Zhang J S, Chang C Z, Tang P Z, Zhang Z C, Feng X, Li K, Wang L L, Chen X, Liu C X, Duan W H, He K, Xue Q K, Ma X C, Wang Y Y 2013 Science 339 1582 Google Scholar
[35]	Fei F, Zhang S, Zhang M, Shah S A, Song F, Wang X, Wang B 2019 Adv. Mater. 32 1904593
[36]	Guo Q M, Qin Z H, Liu C D, Zang K, Yu Y H, Cao G Y 2010 Surf. Sci. 604 1820 Google Scholar
[37]	Li L F, Lu S Z, Pan J B, Qin Z H, Wang Y Q, Wang Y L, Cao G Y, Du S X, Gao H J 2014 Adv. Mater. 26 4820 Google Scholar
[38]	Qin Z H, Pan J B, Lu S Z, Yan S, Wang Y L, Du S X, Gao H J, Cao G Y 2017 Adv. Mater. 29 1606046 Google Scholar
[39]	Liao M H, Zang Y Y, Guan Z Y, Li H W, Gong Y, Zhu K J, Hu X P, Zhang D, Xu Y, Wang Y Y, He K, Ma X C, Zhang S C, Xue Q K 2018 Nat. Phys. 14 344 Google Scholar
[40]	秦志辉 2017 66 216802 Google Scholar Qin Z H 2017 Acta Phys. Sin. 66 216802 Google Scholar
[41]	Qin Z 2013 Chin. Phys. B 22 098108 Google Scholar
[42]	Cahangirov S, Topsakal M, Aktürk E, Şahin H, Ciraci S 2009 Phys. Rev. Lett. 102 236804 Google Scholar
[43]	Liu C C, Feng W X, Yao Y G 2011 Phys. Rev. Lett. 107 076802 Google Scholar
[44]	Le Lay G 2015 Nat. Nanotechnol. 10 202 Google Scholar
[45]	Dávila M E, Xian L, Cahangirov S, Rubio A, Le Lay G 2014 New J. Phys. 16 095002 Google Scholar
[46]	Derivaz M, Dentel D, Stephan R, Hanf M C, Mehdaoui A, Sonnet P, Pirri C 2015 Nano Lett. 15 2510 Google Scholar
[47]	Meng L, Wang Y L, Zhang L Z, Du S X, Wu R T, Li L F, Zhang Y, Li G, Zhou H T, Hofer W A, Gao H J 2013 Nano Lett. 13 685 Google Scholar
[48]	Feng B J, Zhang J, Zhong Q, Li W B, Li S, Li H, Cheng P, Meng S, Chen L, Wu K H 2016 Nat. Chem. 8 564
[49]	Feng B, Zhang J, Zhong Q, Li W, Li S, Li H, Cheng P, Meng S, Chen L, Wu K 2016 Nat. Chem. 8 563 Google Scholar
[50]	Penev E S, Kutana A, Yakobson B I 2016 Nano Lett. 16 2522 Google Scholar
[51]	Li L F, Wang Y L, Xie S Y, Li X B, Wang Y Q, Wu R T, Sun H B, Zhang S B, Gao H J 2013 Nano Lett. 13 4671 Google Scholar
[52]	Guo Q, Zhong Y, Huang M, Lu S, Yu Y 2020 Thin Solid Films 693 137709 Google Scholar
[53]	Guo Q M, Qin Z H, Huang M, Mantsevich V N, Cao G Y 2016 Chin. Phys. B 25 036801 Google Scholar
[54]	Beinik I, Barth C, Hanbucken M, Masson L 2015 Sci. Rep. 5 8223 Google Scholar
[55]	Kwong P, Seidel S, Gupta M 2015 J. Vac. Sci. Technol., A 33 031504 Google Scholar
[56]	McGinn P J 2019 ACS Comb. Sci. 21 501 Google Scholar
[57]	Nie Z, Shi Y, Qin S, Wang Y, Jiang H, Zheng Q, Cui Y, Meng Y, Song F, Wang X, Turcu I C E, Wang X, Xu Y, Shi Y, Zhao J, Zhang R, Wang F 2019 Commun. Phys. 2 103 Google Scholar
[58]	Triboulet R 2014 Prog. Cryst. Growth Charact. Matter. 60 1 Google Scholar
[59]	Wang X R, Yushin G 2015 Energy Environ. Sci. 8 1889 Google Scholar
[60]	Yu S J, Pak K, Kwak M J, Joo M, Kim B J, Oh M S, Baek J, Park H, Choi G, Kim D H, Choi J, Choi Y, Shin J, Moon H, Lee E, Im S G 2018 Adv. Eng. Mater. 20 1700622 Google Scholar
[61]	Keyshar K, Gong Y J, Ye G L, Brunetto G, Zhou W, Cole D P, Hackenberg K, He Y M, Machado L, Kabbani M, Hart A H C, Li B, Galvao D S, George A, Vajtai R, Tiwary C S, Ajayan P M 2015 Adv. Mater. 27 4640 Google Scholar
[62]	Matsuda T, Sato J, Ishikawa T, Ogino A, Nagatsu M 2009 Diam. Relat. Mater. 18 548 Google Scholar
[63]	Shukla B, Saito T, Yumura M, Iijima S 2009 Chem. Commun. 342 2
[64]	Chen H C, Su W R, Yeh Y C 2020 ACS Appl. Mater. Interfaces 12 32905 Google Scholar
[65]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Zhang Y, Dubonos S V, Grigorieva I V, Firsov A A 2004 Science 306 666 Google Scholar
[66]	Kim M, Safron N S, Han E, Arnold M S, Gopalan P 2010 Nano Lett. 10 1125 Google Scholar
[67]	Kim Y, Choi D S, Kim H J, Kim H, Kim T Y, Rhyu S H, Lee K S, Yoon D H, Yang W S 2014 J. Ceram. Process. Res. 15 269
[68]	Fang W J, Hsu A L, Song Y, Kong J 2015 Nanoscale 7 20335 Google Scholar
[69]	Sun H, Xu J, Wang C, Ge G, Jia Y, Liu J, Song F, Wan J 2016 Carbon 108 356 Google Scholar
[70]	Sun H, Fu C, Shen X, Yang W, Guo P, Lu Y, Luo Y, Yu B, Wang X, Wang C, Xu J, Liu J, Song F, Wang G, Wan J 2017 Nanotechnology 28 245604 Google Scholar
[71]	Tan H, Wang D G, Guo Y B 2018 Coatings 8 40 Google Scholar
[72]	Jessen B S, Gammelgaard L, Thomsen M R, Mackenzie D M A, Thomsen J D, Caridad J M, Duegaard E, Watanabe K, Taniguchi T, Booth T J, Pedersen T G, Jauho A P, Boggild P 2019 Nat. Nanotechnol. 14 340 Google Scholar
[73]	Wu J, Li Y, Pan D, Jiang C, Jin C, Song F, Wang G, Wan J 2019 Carbon 147 434 Google Scholar
[74]	Jia K, Ci H, Zhang J, Sun Z, Ma Z, Zhu Y, Liu S, Liu J, Sun L, Liu X, Sun J, Yin W, Peng H, Lin L, Liu Z 2020 Angew. Chem. Int. Ed. 59 17214 Google Scholar
[75]	Li X, Cai W, Colombo L, Ruoff R S 2009 Nano Lett. 9 4268 Google Scholar
[76]	Puurunen R L 2005 J. Appl. Phys. 97 121301 Google Scholar
[77]	Kol'tsov S I, Aleskovskii V B 1967 Zh. Prikl. Khim. 40 907
[78]	Kol'tsov S I, Aleskovskii V B 1969 Zh. Prikl. Khim. 42 1023
[79]	Suntola T, Antson J U.S. Patent 4058430 [1977-11-15]
[80]	Longo E, Mantovan R, Cecchini R, Overbeek M D, Longo M, Trevisi G, Lazzarini L, Tallarida G, Fanciulli M, Winter C H, Wiemer C 2020 Nano Res. 13 570 Google Scholar
[81]	Ahvenniemi E, Karppinen M 2016 Dalton Trans. 45 10730 Google Scholar
[82]	Leskelä M, Ritala M 2003 Angew. Chem. Int. Ed. 42 5548 Google Scholar
[83]	Yang H C, Waldman R Z, Chen Z W, Darling S B 2018 Nanoscale 10 20505 Google Scholar
[84]	Griffiths M B E, Pallister P J, Mandia D J, Barry S T 2016 Chem. Mater. 28 44 Google Scholar
[85]	Ahn J, Ahn C, Jeon S, Park J 2019 Appl. Sci. 9 1990 Google Scholar
[86]	Marichy C, Bechelany M, Pinna N 2012 Adv. Mater. 24 1017 Google Scholar
[87]	Ovanesyan R A, Filatova E A, Elliott S D, Hausmann D M, Smith D C, Agarwal S 2019 J. Vac. Sci. Technol., A 37 060904 Google Scholar
[88]	Solanki R, Huo J, Freeouf J L, Miner B 2002 Appl. Phys. Lett. 81 3864 Google Scholar
[89]	Andou Y, Nishida H, Endo T 2006 Chem. Commun. 501 8
[90]	Amitonova L V, de Boer J F 2020 Light-Sci. Appl. 9 81 Google Scholar
[91]	Clary J, Norman S, Funke H, Su D, Musgrave C, Weimer A 2020 Nanotechnology 31 175703 Google Scholar
[92]	Cao K, Cai J, Chen R 2020 Chem. Mater. 32 2195 Google Scholar
[93]	Shimamura H, Nakamura T 2010 Polym. Degrad. Stab. 95 21 Google Scholar
[94]	Klesko J P, Kerrigan M M, Winter C H 2016 Chem. Mater. 28 700 Google Scholar
[95]	Kerrigan M M, Klesko J P, Winter C H 2017 Chem. Mater. 29 7458 Google Scholar
[96]	Knisley T J, Kalutarage L C, Winter C H 2013 Coord. Chem. Rev. 257 3222 Google Scholar
[97]	Eigenfeld N T, Gray J M, Brown J J, Skidmore G D, George S M, Bright V M 2014 Adv. Mater. 26 3962 Google Scholar
[98]	Knisley T J, Saly M J, Heeg M J, Roberts J L, Winter C H 2011 Organometallics 30 5010 Google Scholar
[99]	Krozer A, Rodahl M 1997 J. Vac. Sci. Technol., A 15 1704 Google Scholar
[100]	Chen R, Bent S F 2006 Adv. Mater. 18 1086 Google Scholar
[101]	Wojtecki R, Mettry M, Fine Nathel N F, Friz A, De Silva A, Arellano N, Shobha H 2018 ACS Appl. Mater. Interfaces 10 38630 Google Scholar
[102]	Koenig M, Lahann J 2017 Beilstein J. Nanotechnol. 8 1250 Google Scholar
[103]	Chang Y H, Liu C M, Tseng Y C, Chen C, Chen C C, Cheng H E 2010 Nanotechnology 21 225602 Google Scholar
[104]	Kim S W, Han T H, Kim J, Gwon H, Moon H S, Kang S W, Kim S O, Kang K 2009 ACS Nano 3 1085 Google Scholar
[105]	Ban C M, George S M 2016 Adv. Mater. Interfaces 3 1600762 Google Scholar
[106]	Liu L, Karuturi S K, Su L T, Tok A I Y 2011 Energy Environ. Sci. 4 209 Google Scholar
[107]	Mackus A J M, Bol A A, Kessels W M M 2014 Nanoscale 6 10941 Google Scholar
[108]	Skoog S A, Elam J W, Narayan R J 2013 Int. Mater. Rev. 58 113 Google Scholar
[109]	Szilagyi I M, Teucher G, Harkonen E, Farm E, Hatanpaa T, Nikitin T, Khriachtchev L, Rasanen M, Ritala M, Leskela M 2013 Nanotechnology 24 245701 Google Scholar
[110]	Gebhard M, Mitschker F, Hoppe C, Aghaee M, Rogalla D, Creatore M, Grundmeier G, Awakowicz P, Devi A 2018 Plasma Process. Polym. 15 e1700209 Google Scholar
[111]	Kim K M, Jang J S, Yoon S G, Yun J Y, Chung N K 2020 Materials 13 2008 Google Scholar
[112]	Choudhury D, Sarkar S K 2014 Chem. Vapor Depos. 20 130 Google Scholar
[113]	Yoshimura T 2016 Macromol. Symp. 361 141 Google Scholar
[114]	Poodt P, Cameron D C, Dickey E, George S M, Kuznetsov V, Parsons G N, Roozeboom F, Sundaram G, Vermeer A 2012 J. Vac. Sci. Technol., A 30 010802 Google Scholar
[115]	Poodt P, van Lieshout J, Illiberi A, Knaapen R, Roozeboom F, van Asten A 2013 J. Vac. Sci. Technol., A 31 01A108
[116]	Sharma K, Hall R A, George S M 2015 J. Vac. Sci. Technol., A 33 01A132 Google Scholar
[117]	Mousa M B M, Ovental J S, Brozena A H, Oldham C J, Parsons G N 2018 J. Vac. Sci. Technol., A 36 031517 Google Scholar
[118]	Satpati A K, Arroyo-Curras N, Ji L, Yu E T, Bard A J 2013 Chem. Mater. 25 4165 Google Scholar
[119]	Venkatraman K, Gusley R, Lesak A, Akolkar R 2019 J. Vac. Sci. Technol., A 37 020901 Google Scholar
[120]	Elam J W 2012 Atomic Layer Deposition of Nanostructured Materials (Weinheim: Wiley-VCH Verlag GmbH & Co. KGaA) pp227−249
[121]	Chen R, Kim H, McIntyre P C, Porter D W, Bent S F 2005 Appl. Phys. Lett. 86 191910 Google Scholar
[122]	Lee H B R, Bent S F 2012 Atomic Layer Deposition of Nanostructured Materials (Weinheim: Wiley-VCH Verlag GmbH & Co. KGaA) pp193−225
[123]	Hashemi F S M, Prasittichai C, Bent S F 2014 J. Phys. Chem. C 118 10957 Google Scholar
[124]	Minaye Hashemi F S, Prasittichai C, Bent S F 2015 ACS Nano 9 8710 Google Scholar
[125]	Hashemi F S M, Bent S F 2016 Adv. Mater. Interfaces 3 1600464 Google Scholar
[126]	Seo S, Yeo B C, Han S S, Yoon C M, Yang J Y, Yoon J, Yoo C, Kim H J, Lee Y B, Lee S J, Myoung J M, Lee H B R, Kim W H, Oh I K, Kim H 2017 ACS Appl. Mater. Interfaces 9 41607 Google Scholar
[127]	Farm E, Kemell M, Santala E, Ritala M, Leskela M 2010 J. Electrochem. Soc. 157 K10 Google Scholar
[128]	Lee W, Prinz F B 2009 J. Electrochem. Soc. 156 G125 Google Scholar
[129]	Horiike Y, Tanaka T, Nakano M, Iseda S, Sakaue H, Nagata A, Shindo H, Miyazaki S, Hirose M 1990 J. Vac. Sci. Technol., A 8 1844 Google Scholar
[130]	Athavale S D 1996 J. Vac. Sci. Technol., B 14 3702 Google Scholar
[131]	Dimiev A, Kosynkin D V, Sinitskii A, Slesarev A, Sun Z, Tour J M 2011 Science 331 1168 Google Scholar
[132]	Faraz T, Roozeboom F, Knoops H, Kessels W M M 2015 ECS J. Solid State SC 4 N5023
[133]	Lee Y, DuMont J W, George S M 2015 Chem. Mater. 27 3648 Google Scholar
[134]	Oehrlein G, Metzler D, Li C 2015 ECS J. Solid State SC 4 N5041
[135]	Kauppinen C, Khan S A, Sundqvist J, Suyatin D B, Suihkonen S, Kauppinen E I, Sopanen M 2017 J. Vac. Sci. Technol., A 35 060603 Google Scholar
[136]	Kim K S, Ji Y J, Nam Y, Kim K H, Singh E, Lee J Y, Yeom G Y 2017 Sci. Rep. 7 2462 Google Scholar
[137]	Kim K S, Kim K H, Nam Y, Jeon J, Yim S, Singh E, Lee J Y, Lee S J, Jung Y S, Yeom G Y, Kim D W 2017 ACS Appl. Mater. Interfaces 9 11967 Google Scholar
[138]	Park J W, Kim D S, Mun M K, Lee W O, Kim K S, Yeom G Y 2017 J. Phys. D: Appl. Phys. 50 254007 Google Scholar
[139]	Shinoda K, Miyoshi N, Kobayashi H, Kurihara M, Izawa M, Ishikawa K, Hori M 2017 ECS Trans. 80 3
[140]	Abdulagatov A I, George S M 2018 Chem. Mater. 30 8465 Google Scholar
[141]	Cheng Y, Wang K, Qi Y, Liu Z 2020 Acta Phys.-Chim. Sin. 2021 37
[142]	Wang M, Fu L, Gan L, Zhang C, Rummeli M, Bachmatiuk A, Huang K, Fang Y, Liu Z 2013 Sci. Rep. 3 1238 Google Scholar

Cited By

图 1 MBE系统结构示意图

Figure 1. Schematic diagram of MBE system.

DownLoad: Full-Size Img PowerPoint

图 2 RHEED系统示意图和漫反射现象随着薄膜生长的关系示意图

Figure 2. Schematic diagram of RHEED, and the relationship between diffuse reflection and film coverage during growth.

DownLoad: Full-Size Img PowerPoint

图 3 (a) Pt(111)表面锗烯的理论计算结构; (b)−(g) 不同位置的Ge原子对以及Ge单原子与最近邻基底Pt原子间电子局域函数的计算模拟; (h)−(j) 锗烯的实验结果(LEED, STM图像及表观高度)^[37]

Figure 3. (a) Theoretical model of germanene on Pt (111) surface, and the electron localization functions of the cross-sections between the germanium pairs (b)−(f) and between one germanium atom and its nearest Pt neighbor (g). (h)−(j) The experimental results of LEED pattern, STM image and the apparent height along the indicated line in the STM image, respectively^[37].

DownLoad: Full-Size Img PowerPoint

图 4 (a) Cu(111)表面制备的锗烯; (b), (c) Cu(111)基底和锗烯的原子分辨图像; (d) 双层锗烯的吸附结构模型; (e) 相应的STM图像模拟, 与实验结果(c)吻合; (f) 单层(红色)和双层(黑色)锗烯的电子结构(STS谱), 插图为Cu(111)基底STS谱用于标定针尖状态^[38]

Figure 4. (a) STM image of germanene on Cu(111); (b), (c) the atomic-resolved STM images of Cu (111) substrate and germanene, respectively; (d) the adsorption model of bilayer germanene; (e) the simulated STM image with the features fitting very well with the experimental observations; (f) the STS of monolayer (red) and bilayer (black) germanene, and inset is STS taken on the bare Cu(111) to verify the condition of the tip^[38].

DownLoad: Full-Size Img PowerPoint

图 5 (a)−(c) 在Cu(111)表面MBE生长的不同取向的硒化铜蜂窝状结构的STM图像; (d) 用于标定针尖状态的Cu(111)表面标准STS谱; (e) CuSe结构的STS谱^[52]

Figure 5. (a)−(c) The STM images of honeycomb structures with equivalent orientations on Cu(111) by means of MBE growth; (d) the standard STS of Cu(111) for checking tip status; (e) electronic structure (STS) of CuSe structures^[52].

DownLoad: Full-Size Img PowerPoint

图 6 (a) 在Cu(100)上外延生长的NaCl薄膜^[36], 以及在其上的CoPc分子轨道的实验(b)和理论(c)图像^[53]

Figure 6. (a) MBE growth of NaCl layers on Cu(100)^[36], on top of which the quasi-free molecular orbital of adsorbed CoPc can be observed. (b) and (c) are the STM image and theoretical simulation of molecular orbital, respectively^[53].

DownLoad: Full-Size Img PowerPoint

图 7 两种主要的石墨烯的CVD生长机制^[75]　(a) 偏析机制; (b) 表面化学反应机制

Figure 7. Two main mechanisms of CVD growth of graphene^[75] (a) Segregation mechanism; (b) surface reaction mechanism.

DownLoad: Full-Size Img PowerPoint

图 8 原子层沉积系统示意图

Figure 8. Schematic diagram of atomic layer deposition system.

DownLoad: Full-Size Img PowerPoint

图 9 Al₂O₃层的ALD制备过程^[76]

Figure 9. The ALD process of Al₂O₃^[76].

DownLoad: Full-Size Img PowerPoint

图 10 (a) ALD与其他方式镀膜效果比较; (b) 在深高宽比Si结构上原子沉积Cu₂S薄膜的SEM照片^[120]

Figure 10. (a) The coating effects of ALD and other methods; (b) cross-sectional SEM images of ALD Cu₂S film on silicon trench structure^[120].

DownLoad: Full-Size Img PowerPoint

图 11 气体前驱体暴露量和沉积温度对原子层沉积镀膜速率的影响

Figure 11. Effects of gaseous precursor exposure and deposition temperature on deposition rate of atomic layers.

DownLoad: Full-Size Img PowerPoint

图 12 在SiO₂/H-Si表面选区ALD沉积High-k氧化铪制作MOSFET原型^[121]

Figure 12. The area-selective ALD of high-k hafnium oxide on SiO₂/H-Si surface to fabricate MOSFET prototype.^[121]

DownLoad: Full-Size Img PowerPoint

图 13 (a) 左边选区ALD的原理示意图, 右边为自组装钝化层的单体分子结构; (b) 自组装薄膜的缺陷(pinhole)影响ALD沉积过程的选择性; (c) 自组装分子的光聚合官能团(二炔基)在光诱导下聚合有效抑制缺陷产生; (d) 通过选区ALD沉积ZnO掩膜刻蚀后的微结构, 结构最窄宽度约为15 nm^[101]

Figure 13. (a) Schematic diagram of area-selective ALD growth (left), and the monomer molecular structures forming inactive SAMs (right); (b) the pinhole defect affects the selectivity of ALD deposition; (c) photopolymeric functional groups (diacetylenyl) of SAMs can effectively inhibit defect formation in terms of photo-induced polymerization; (d) SEM micrograph of the microstructure obtained by etching with ZnO mask of area-selective ALD, and the width of narrowest structure reaches 15 nm^[101].

DownLoad: Full-Size Img PowerPoint

图 14 ALE和ALD过程对比示意图^[132]

Figure 14. Schematic diagram of ALE process compared with ALD^[132].

DownLoad: Full-Size Img PowerPoint

图 15 双层石墨烯ALE刻蚀前后的光学显微图像(a), (b)以及相应的AFM图像(c), (d)和在各位点的拉曼谱(e)^[136]

Figure 15. Optical microscopic images (a), (b) and AFM images (c), (d) of bilayer graphene before and after one cycle of ALE etching. (e) Raman spectrum of graphene taken at twelve points indicated in (a), (b) before and after etching^[136].

DownLoad: Full-Size Img PowerPoint

图 16 单层石墨烯经过一个循环的ALE刻蚀前后的拉曼光谱^[136]

Figure 16. Raman spectrum of monolayer graphene before and after one cycle of ALE^[136].

DownLoad: Full-Size Img PowerPoint

图 17 (a)−(f) 经过PS纳米球掩膜的石墨烯加工过程; (g) 铜箔表面具有纳米模板的石墨烯^[142]

Figure 17. (a)−(f) The growth and etching processes of graphene via PS nanoparticle mask; (g) the nano-patterned template graphene on Cu foil^[142].

DownLoad: Full-Size Img PowerPoint

map

[1]	冯黎, 朱雷 2020 功能材料与器件学报 26 191 Feng L, Zhu L 2020 J. Funct. Mater. Devices 26 191
[2]	庞玉莲, 邹应全 2015 信息记录材料 16 36 Google Scholar Pang Y L, Zou Y Q 2015 Info. Rec. Mater. 16 36 Google Scholar
[3]	Striccoli M 2017 Science 357 353 Google Scholar
[4]	Okazaki S 2015 Microelectron. Eng. 133 23 Google Scholar
[5]	Hong F, Blaikie R 2019 Adv. Opt. Mater. 7 1801653 Google Scholar
[6]	王霞, 吕浩, 赵秋玲, 张帅一, 谭永炎 2016 光谱学与光谱分析 36 3461 Wang X, Lü H, Zhao Q L, Zhang S Y, Tan Y Y 2016 Spectrosc. Spect. Anal. 36 3461
[7]	Fang F Z 2016 Front. Mech. Eng. Chin. 11 325 Google Scholar
[8]	Luo C, Li J F, Yang X, Wu X, Zhong S Y, Wang C L, Sun L T 2020 ACS Appl. Nano Mater. 3 4747
[9]	Martín-Palma R J, Lakhtakia A 2013 Engineered Biomimicry (Boston: Elsevier) pp383−398
[10]	LaPedus M 2018 工艺与制造 35 39 LaPedus M 2018 Prog. Fabri. 35 39
[11]	Ashurbekova K, Ashurbekova K, Botta G, Yurkevich O, Knez M 2020 Nanotechnology 31 342001 Google Scholar
[12]	Kulkarni A K 1994 B. Mater. Sci. 17 1379 Google Scholar
[13]	Mattox D M 1992 Plat. Surf. Finish. 79 60
[14]	Mattox D M 1998 Plat. Surf. Finish. 85 49
[15]	Zhu D M, Miller R A, Nagaraj B A, Bruce R W 2001 Surf. Coat. Technol. 138 1 Google Scholar
[16]	Muratore C, Walton S G, Leonhardt D, Fernsler R F 2006 J. Vac. Sci. Technol., A 24 25
[17]	Kumar T S, Prabu S B, Manivasagam G 2014 J. Mater. Eng. Perform. 23 2877 Google Scholar
[18]	Yang R B, Bachmann J, Pippel E, Berger A, Woltersdorf J, Gösele U, Nielsch K 2009 Adv. Mater. 21 3170 Google Scholar
[19]	Bao Q H, Chen C Z, Wang D G, Ji Q M, Lei T Q 2005 Appl. Surf. Sci. 252 1538 Google Scholar
[20]	Cho A Y, Arthur J R 1975 Prog. Solid State Chem. 10 157 Google Scholar
[21]	Hong M 1995 J. Cryst. Growth 150 277 Google Scholar
[22]	Spirkoska D, Colombo C, Heiss M, Abstreiter G, Morral A F I 2008 J. Phys. Condens. Matter 20 454225 Google Scholar
[23]	Wang X Q, Yoshika A 2011 Thin Film Growth (Sawston Cambridge: Woodhead Publishing) pp288−316
[24]	Howson R P, Spencer A G, Lewin R W 1988 Vacuum 38 947
[25]	Kelly P J, Arnell R D 2000 Vacuum 56 159 Google Scholar
[26]	Shi J Z, Chen C Z, Yu H J, Zhang S J 2008 B. Mater. Sci. 31 877 Google Scholar
[27]	Brauer G, Szyszka B, Vergohl M, Bandorf R 2010 Vacuum 84 1354 Google Scholar
[28]	Kopecky D, Vrnata M, Kopecka J 2015 Chem. Listy 109 183
[29]	von Wenckstern H, Kneiss M, Hassa A, Storm P, Splith D, Grundmann M 2020 Phys. Status Solidi B 257 1900626 Google Scholar
[30]	Dabrowska-Szata M 2003 Mater. Chem.Phys. 81 257 Google Scholar
[31]	Ichimiya A 2005 J. Jpn. Soc. Tribologis. 50 731
[32]	Wood C 1981 Surf. Sci. 108 L441
[33]	Chang C Z, Zhang J S, Feng X, Shen J, Zhang Z C, Guo M H, Li K, Ou Y B, Wei P, Wang L L, Ji Z Q, Feng Y, Ji S H, Chen X, Jia J F, Dai X, Fang Z, Zhang S C, He K, Wang Y Y, Lu L, Ma X C, Xue Q K 2013 Science 340 167 Google Scholar
[34]	Zhang J S, Chang C Z, Tang P Z, Zhang Z C, Feng X, Li K, Wang L L, Chen X, Liu C X, Duan W H, He K, Xue Q K, Ma X C, Wang Y Y 2013 Science 339 1582 Google Scholar
[35]	Fei F, Zhang S, Zhang M, Shah S A, Song F, Wang X, Wang B 2019 Adv. Mater. 32 1904593
[36]	Guo Q M, Qin Z H, Liu C D, Zang K, Yu Y H, Cao G Y 2010 Surf. Sci. 604 1820 Google Scholar
[37]	Li L F, Lu S Z, Pan J B, Qin Z H, Wang Y Q, Wang Y L, Cao G Y, Du S X, Gao H J 2014 Adv. Mater. 26 4820 Google Scholar
[38]	Qin Z H, Pan J B, Lu S Z, Yan S, Wang Y L, Du S X, Gao H J, Cao G Y 2017 Adv. Mater. 29 1606046 Google Scholar
[39]	Liao M H, Zang Y Y, Guan Z Y, Li H W, Gong Y, Zhu K J, Hu X P, Zhang D, Xu Y, Wang Y Y, He K, Ma X C, Zhang S C, Xue Q K 2018 Nat. Phys. 14 344 Google Scholar
[40]	秦志辉 2017 66 216802 Google Scholar Qin Z H 2017 Acta Phys. Sin. 66 216802 Google Scholar
[41]	Qin Z 2013 Chin. Phys. B 22 098108 Google Scholar
[42]	Cahangirov S, Topsakal M, Aktürk E, Şahin H, Ciraci S 2009 Phys. Rev. Lett. 102 236804 Google Scholar
[43]	Liu C C, Feng W X, Yao Y G 2011 Phys. Rev. Lett. 107 076802 Google Scholar
[44]	Le Lay G 2015 Nat. Nanotechnol. 10 202 Google Scholar
[45]	Dávila M E, Xian L, Cahangirov S, Rubio A, Le Lay G 2014 New J. Phys. 16 095002 Google Scholar
[46]	Derivaz M, Dentel D, Stephan R, Hanf M C, Mehdaoui A, Sonnet P, Pirri C 2015 Nano Lett. 15 2510 Google Scholar
[47]	Meng L, Wang Y L, Zhang L Z, Du S X, Wu R T, Li L F, Zhang Y, Li G, Zhou H T, Hofer W A, Gao H J 2013 Nano Lett. 13 685 Google Scholar
[48]	Feng B J, Zhang J, Zhong Q, Li W B, Li S, Li H, Cheng P, Meng S, Chen L, Wu K H 2016 Nat. Chem. 8 564
[49]	Feng B, Zhang J, Zhong Q, Li W, Li S, Li H, Cheng P, Meng S, Chen L, Wu K 2016 Nat. Chem. 8 563 Google Scholar
[50]	Penev E S, Kutana A, Yakobson B I 2016 Nano Lett. 16 2522 Google Scholar
[51]	Li L F, Wang Y L, Xie S Y, Li X B, Wang Y Q, Wu R T, Sun H B, Zhang S B, Gao H J 2013 Nano Lett. 13 4671 Google Scholar
[52]	Guo Q, Zhong Y, Huang M, Lu S, Yu Y 2020 Thin Solid Films 693 137709 Google Scholar
[53]	Guo Q M, Qin Z H, Huang M, Mantsevich V N, Cao G Y 2016 Chin. Phys. B 25 036801 Google Scholar
[54]	Beinik I, Barth C, Hanbucken M, Masson L 2015 Sci. Rep. 5 8223 Google Scholar
[55]	Kwong P, Seidel S, Gupta M 2015 J. Vac. Sci. Technol., A 33 031504 Google Scholar
[56]	McGinn P J 2019 ACS Comb. Sci. 21 501 Google Scholar
[57]	Nie Z, Shi Y, Qin S, Wang Y, Jiang H, Zheng Q, Cui Y, Meng Y, Song F, Wang X, Turcu I C E, Wang X, Xu Y, Shi Y, Zhao J, Zhang R, Wang F 2019 Commun. Phys. 2 103 Google Scholar
[58]	Triboulet R 2014 Prog. Cryst. Growth Charact. Matter. 60 1 Google Scholar
[59]	Wang X R, Yushin G 2015 Energy Environ. Sci. 8 1889 Google Scholar
[60]	Yu S J, Pak K, Kwak M J, Joo M, Kim B J, Oh M S, Baek J, Park H, Choi G, Kim D H, Choi J, Choi Y, Shin J, Moon H, Lee E, Im S G 2018 Adv. Eng. Mater. 20 1700622 Google Scholar
[61]	Keyshar K, Gong Y J, Ye G L, Brunetto G, Zhou W, Cole D P, Hackenberg K, He Y M, Machado L, Kabbani M, Hart A H C, Li B, Galvao D S, George A, Vajtai R, Tiwary C S, Ajayan P M 2015 Adv. Mater. 27 4640 Google Scholar
[62]	Matsuda T, Sato J, Ishikawa T, Ogino A, Nagatsu M 2009 Diam. Relat. Mater. 18 548 Google Scholar
[63]	Shukla B, Saito T, Yumura M, Iijima S 2009 Chem. Commun. 342 2
[64]	Chen H C, Su W R, Yeh Y C 2020 ACS Appl. Mater. Interfaces 12 32905 Google Scholar
[65]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Zhang Y, Dubonos S V, Grigorieva I V, Firsov A A 2004 Science 306 666 Google Scholar
[66]	Kim M, Safron N S, Han E, Arnold M S, Gopalan P 2010 Nano Lett. 10 1125 Google Scholar
[67]	Kim Y, Choi D S, Kim H J, Kim H, Kim T Y, Rhyu S H, Lee K S, Yoon D H, Yang W S 2014 J. Ceram. Process. Res. 15 269
[68]	Fang W J, Hsu A L, Song Y, Kong J 2015 Nanoscale 7 20335 Google Scholar
[69]	Sun H, Xu J, Wang C, Ge G, Jia Y, Liu J, Song F, Wan J 2016 Carbon 108 356 Google Scholar
[70]	Sun H, Fu C, Shen X, Yang W, Guo P, Lu Y, Luo Y, Yu B, Wang X, Wang C, Xu J, Liu J, Song F, Wang G, Wan J 2017 Nanotechnology 28 245604 Google Scholar
[71]	Tan H, Wang D G, Guo Y B 2018 Coatings 8 40 Google Scholar
[72]	Jessen B S, Gammelgaard L, Thomsen M R, Mackenzie D M A, Thomsen J D, Caridad J M, Duegaard E, Watanabe K, Taniguchi T, Booth T J, Pedersen T G, Jauho A P, Boggild P 2019 Nat. Nanotechnol. 14 340 Google Scholar
[73]	Wu J, Li Y, Pan D, Jiang C, Jin C, Song F, Wang G, Wan J 2019 Carbon 147 434 Google Scholar
[74]	Jia K, Ci H, Zhang J, Sun Z, Ma Z, Zhu Y, Liu S, Liu J, Sun L, Liu X, Sun J, Yin W, Peng H, Lin L, Liu Z 2020 Angew. Chem. Int. Ed. 59 17214 Google Scholar
[75]	Li X, Cai W, Colombo L, Ruoff R S 2009 Nano Lett. 9 4268 Google Scholar
[76]	Puurunen R L 2005 J. Appl. Phys. 97 121301 Google Scholar
[77]	Kol'tsov S I, Aleskovskii V B 1967 Zh. Prikl. Khim. 40 907
[78]	Kol'tsov S I, Aleskovskii V B 1969 Zh. Prikl. Khim. 42 1023
[79]	Suntola T, Antson J U.S. Patent 4058430 [1977-11-15]
[80]	Longo E, Mantovan R, Cecchini R, Overbeek M D, Longo M, Trevisi G, Lazzarini L, Tallarida G, Fanciulli M, Winter C H, Wiemer C 2020 Nano Res. 13 570 Google Scholar
[81]	Ahvenniemi E, Karppinen M 2016 Dalton Trans. 45 10730 Google Scholar
[82]	Leskelä M, Ritala M 2003 Angew. Chem. Int. Ed. 42 5548 Google Scholar
[83]	Yang H C, Waldman R Z, Chen Z W, Darling S B 2018 Nanoscale 10 20505 Google Scholar
[84]	Griffiths M B E, Pallister P J, Mandia D J, Barry S T 2016 Chem. Mater. 28 44 Google Scholar
[85]	Ahn J, Ahn C, Jeon S, Park J 2019 Appl. Sci. 9 1990 Google Scholar
[86]	Marichy C, Bechelany M, Pinna N 2012 Adv. Mater. 24 1017 Google Scholar
[87]	Ovanesyan R A, Filatova E A, Elliott S D, Hausmann D M, Smith D C, Agarwal S 2019 J. Vac. Sci. Technol., A 37 060904 Google Scholar
[88]	Solanki R, Huo J, Freeouf J L, Miner B 2002 Appl. Phys. Lett. 81 3864 Google Scholar
[89]	Andou Y, Nishida H, Endo T 2006 Chem. Commun. 501 8
[90]	Amitonova L V, de Boer J F 2020 Light-Sci. Appl. 9 81 Google Scholar
[91]	Clary J, Norman S, Funke H, Su D, Musgrave C, Weimer A 2020 Nanotechnology 31 175703 Google Scholar
[92]	Cao K, Cai J, Chen R 2020 Chem. Mater. 32 2195 Google Scholar
[93]	Shimamura H, Nakamura T 2010 Polym. Degrad. Stab. 95 21 Google Scholar
[94]	Klesko J P, Kerrigan M M, Winter C H 2016 Chem. Mater. 28 700 Google Scholar
[95]	Kerrigan M M, Klesko J P, Winter C H 2017 Chem. Mater. 29 7458 Google Scholar
[96]	Knisley T J, Kalutarage L C, Winter C H 2013 Coord. Chem. Rev. 257 3222 Google Scholar
[97]	Eigenfeld N T, Gray J M, Brown J J, Skidmore G D, George S M, Bright V M 2014 Adv. Mater. 26 3962 Google Scholar
[98]	Knisley T J, Saly M J, Heeg M J, Roberts J L, Winter C H 2011 Organometallics 30 5010 Google Scholar
[99]	Krozer A, Rodahl M 1997 J. Vac. Sci. Technol., A 15 1704 Google Scholar
[100]	Chen R, Bent S F 2006 Adv. Mater. 18 1086 Google Scholar
[101]	Wojtecki R, Mettry M, Fine Nathel N F, Friz A, De Silva A, Arellano N, Shobha H 2018 ACS Appl. Mater. Interfaces 10 38630 Google Scholar
[102]	Koenig M, Lahann J 2017 Beilstein J. Nanotechnol. 8 1250 Google Scholar
[103]	Chang Y H, Liu C M, Tseng Y C, Chen C, Chen C C, Cheng H E 2010 Nanotechnology 21 225602 Google Scholar
[104]	Kim S W, Han T H, Kim J, Gwon H, Moon H S, Kang S W, Kim S O, Kang K 2009 ACS Nano 3 1085 Google Scholar
[105]	Ban C M, George S M 2016 Adv. Mater. Interfaces 3 1600762 Google Scholar
[106]	Liu L, Karuturi S K, Su L T, Tok A I Y 2011 Energy Environ. Sci. 4 209 Google Scholar
[107]	Mackus A J M, Bol A A, Kessels W M M 2014 Nanoscale 6 10941 Google Scholar
[108]	Skoog S A, Elam J W, Narayan R J 2013 Int. Mater. Rev. 58 113 Google Scholar
[109]	Szilagyi I M, Teucher G, Harkonen E, Farm E, Hatanpaa T, Nikitin T, Khriachtchev L, Rasanen M, Ritala M, Leskela M 2013 Nanotechnology 24 245701 Google Scholar
[110]	Gebhard M, Mitschker F, Hoppe C, Aghaee M, Rogalla D, Creatore M, Grundmeier G, Awakowicz P, Devi A 2018 Plasma Process. Polym. 15 e1700209 Google Scholar
[111]	Kim K M, Jang J S, Yoon S G, Yun J Y, Chung N K 2020 Materials 13 2008 Google Scholar
[112]	Choudhury D, Sarkar S K 2014 Chem. Vapor Depos. 20 130 Google Scholar
[113]	Yoshimura T 2016 Macromol. Symp. 361 141 Google Scholar
[114]	Poodt P, Cameron D C, Dickey E, George S M, Kuznetsov V, Parsons G N, Roozeboom F, Sundaram G, Vermeer A 2012 J. Vac. Sci. Technol., A 30 010802 Google Scholar
[115]	Poodt P, van Lieshout J, Illiberi A, Knaapen R, Roozeboom F, van Asten A 2013 J. Vac. Sci. Technol., A 31 01A108
[116]	Sharma K, Hall R A, George S M 2015 J. Vac. Sci. Technol., A 33 01A132 Google Scholar
[117]	Mousa M B M, Ovental J S, Brozena A H, Oldham C J, Parsons G N 2018 J. Vac. Sci. Technol., A 36 031517 Google Scholar
[118]	Satpati A K, Arroyo-Curras N, Ji L, Yu E T, Bard A J 2013 Chem. Mater. 25 4165 Google Scholar
[119]	Venkatraman K, Gusley R, Lesak A, Akolkar R 2019 J. Vac. Sci. Technol., A 37 020901 Google Scholar
[120]	Elam J W 2012 Atomic Layer Deposition of Nanostructured Materials (Weinheim: Wiley-VCH Verlag GmbH & Co. KGaA) pp227−249
[121]	Chen R, Kim H, McIntyre P C, Porter D W, Bent S F 2005 Appl. Phys. Lett. 86 191910 Google Scholar
[122]	Lee H B R, Bent S F 2012 Atomic Layer Deposition of Nanostructured Materials (Weinheim: Wiley-VCH Verlag GmbH & Co. KGaA) pp193−225
[123]	Hashemi F S M, Prasittichai C, Bent S F 2014 J. Phys. Chem. C 118 10957 Google Scholar
[124]	Minaye Hashemi F S, Prasittichai C, Bent S F 2015 ACS Nano 9 8710 Google Scholar
[125]	Hashemi F S M, Bent S F 2016 Adv. Mater. Interfaces 3 1600464 Google Scholar
[126]	Seo S, Yeo B C, Han S S, Yoon C M, Yang J Y, Yoon J, Yoo C, Kim H J, Lee Y B, Lee S J, Myoung J M, Lee H B R, Kim W H, Oh I K, Kim H 2017 ACS Appl. Mater. Interfaces 9 41607 Google Scholar
[127]	Farm E, Kemell M, Santala E, Ritala M, Leskela M 2010 J. Electrochem. Soc. 157 K10 Google Scholar
[128]	Lee W, Prinz F B 2009 J. Electrochem. Soc. 156 G125 Google Scholar
[129]	Horiike Y, Tanaka T, Nakano M, Iseda S, Sakaue H, Nagata A, Shindo H, Miyazaki S, Hirose M 1990 J. Vac. Sci. Technol., A 8 1844 Google Scholar
[130]	Athavale S D 1996 J. Vac. Sci. Technol., B 14 3702 Google Scholar
[131]	Dimiev A, Kosynkin D V, Sinitskii A, Slesarev A, Sun Z, Tour J M 2011 Science 331 1168 Google Scholar
[132]	Faraz T, Roozeboom F, Knoops H, Kessels W M M 2015 ECS J. Solid State SC 4 N5023
[133]	Lee Y, DuMont J W, George S M 2015 Chem. Mater. 27 3648 Google Scholar
[134]	Oehrlein G, Metzler D, Li C 2015 ECS J. Solid State SC 4 N5041
[135]	Kauppinen C, Khan S A, Sundqvist J, Suyatin D B, Suihkonen S, Kauppinen E I, Sopanen M 2017 J. Vac. Sci. Technol., A 35 060603 Google Scholar
[136]	Kim K S, Ji Y J, Nam Y, Kim K H, Singh E, Lee J Y, Yeom G Y 2017 Sci. Rep. 7 2462 Google Scholar
[137]	Kim K S, Kim K H, Nam Y, Jeon J, Yim S, Singh E, Lee J Y, Lee S J, Jung Y S, Yeom G Y, Kim D W 2017 ACS Appl. Mater. Interfaces 9 11967 Google Scholar
[138]	Park J W, Kim D S, Mun M K, Lee W O, Kim K S, Yeom G Y 2017 J. Phys. D: Appl. Phys. 50 254007 Google Scholar
[139]	Shinoda K, Miyoshi N, Kobayashi H, Kurihara M, Izawa M, Ishikawa K, Hori M 2017 ECS Trans. 80 3
[140]	Abdulagatov A I, George S M 2018 Chem. Mater. 30 8465 Google Scholar
[141]	Cheng Y, Wang K, Qi Y, Liu Z 2020 Acta Phys.-Chim. Sin. 2021 37
[142]	Wang M, Fu L, Gan L, Zhang C, Rummeli M, Bachmatiuk A, Huang K, Fang Y, Liu Z 2013 Sci. Rep. 3 1238 Google Scholar

[1]	Qiu Peng, Liu Heng, Zhu Xiao-Li, Tian Feng, Du Meng-Chao, Qiu Hong-Yu, Chen Guan-Liang, Hu Yu-Yu, Kong De-Lin, Yang Jin, Wei Hui-Yun, Peng Ming-Zeng, Zheng Xin-He. Atomic layer deposition and application of group III nitrides semiconductor and their alloys. Acta Physica Sinica, 2024, 73(3): 038102. doi: 10.7498/aps.73.20230832
[2]	Qu Zi-Han, Zhao Yang, Ma Fei, You Jing-Bi. Preparation of high-performance large-area perovskite solar cells by atomic layer deposition of metal oxide buffer layer. Acta Physica Sinica, 2024, 73(9): 098802. doi: 10.7498/aps.73.20240218
[3]	Li Zhong-Xiang, Wang Shu-Ya, Huang Zi-Qiang, Wang Chen, Mu Qing. Preparation of Al₂O₃ tunnel barrier layer in atome-level controlled Josephson junction. Acta Physica Sinica, 2022, 71(21): 218102. doi: 10.7498/aps.71.20220820
[4]	Dai Li-Zhi, Hu Xiao-Xue, Liu Peng, Tian Ye. DNA origami mediated precise fabrication of nanostructures in multi scales. Acta Physica Sinica, 2021, 70(6): 068201. doi: 10.7498/aps.70.20201689
[5]	Liu Zi-Yuan, Pan Jin-Bo, Zhang Yu-Yang, Du Shi-Xuan. First principles calculation of two-dimensional materials at an atomic scale. Acta Physica Sinica, 2021, 70(2): 027301. doi: 10.7498/aps.70.20201636
[6]	Zhong Xiao-Yan, Li Zhuo. Atomic scale characterization of three-dimensional structure, magnetic properties and dynamic evolutions of materials by transmission electron microscopy. Acta Physica Sinica, 2021, 70(6): 066801. doi: 10.7498/aps.70.20202072
[7]	Zhan Hai-Yang, Xing Fei, Zhang Li. Analysis of optical measurement precision limit for close-to-atomic scale manufacturing. Acta Physica Sinica, 2021, 70(6): 060703. doi: 10.7498/aps.70.20201924
[8]	Li Sheng-Kai, Hao Qing, Peng Tian-Huan, Chen Zhuo, Tan Wei-Hong. Nucleic acid-metal complex and its application in atomic-scale manufacturing. Acta Physica Sinica, 2021, 70(2): 028102. doi: 10.7498/aps.70.20201430
[9]	Yang Bei, Li Qian, Liu Hua-Jie, Fan Chun-Hai. Recent progress of frame nucleic acids studies towards atomic fabrications. Acta Physica Sinica, 2021, 70(2): 026201. doi: 10.7498/aps.70.20201437
[10]	Li Ye, Wang Xi-Xi, Wei Hui-Yun, Qiu Peng, He Ying-Feng, Song Yi-Meng, Duan Zhang, Shen Cheng-Tao, Peng Ming-Zeng, Zheng Xin-He. Enhancement of interface transportation for quantum dot solar cells using ultrathin InN by atomic layer deposition. Acta Physica Sinica, 2021, 70(18): 187702. doi: 10.7498/aps.70.20210554
[11]	Wang Xing-Yue, Zhang Hui, Ruan Zi-Lin, Hao Zhen-Liang, Yang Xiao-Tian, Cai Jin-Ming, Lu Jian-Chen. Research progress of monolayer two-dimensional atomic crystal materials grown by molecular beam epitaxy in ultra-high vacuum conditions. Acta Physica Sinica, 2020, 69(11): 118101. doi: 10.7498/aps.69.20200174
[12]	Liu Ke, Ma Wen-Quan, Huang Jian-Liang, Zhang Yan-Hua, Cao Yu-Lian, Huang Wen-Jun, Zhao Cheng-Cheng. Three-color InAs/GaAs quantum dot infrared photodetector with AlGaAs inserting layer. Acta Physica Sinica, 2016, 65(10): 108502. doi: 10.7498/aps.65.108502
[13]	Zhu Meng-Yao, Lu Jun, Ma Jia-Lin, Li Li-Xia, Wang Hai-Long, Pan Dong, Zhao Jian-Hua. Molecular-beam epitaxy of high-quality diluted magnetic semiconductor (Ga, Mn)Sb single-crystalline films. Acta Physica Sinica, 2015, 64(7): 077501. doi: 10.7498/aps.64.077501
[14]	Wang Meng, Ou Yun-Bo, Li Fang-Sen, Zhang Wen-Hao, Tang Chen-Jia, Wang Li-Li, Xue Qi-Kun, Ma Xu-Cun. Molecular beam epitaxy of single unit-cell FeSe superconducting films on SrTiO3(001). Acta Physica Sinica, 2014, 63(2): 027401. doi: 10.7498/aps.63.027401
[15]	Li Yong, Li Hui-Qi, Xia Yang, Liu Bang-Wu. Study on atomic layer deposition preparation of core-shell structured nanometer materials. Acta Physica Sinica, 2013, 62(19): 198102. doi: 10.7498/aps.62.198102
[16]	Dong Ya-Bin, Xia Yang, Li Chao-Bo, Lu Wei-Er, Rao Zhi-Peng, Zhang Yang, Zhang Xiang, Ye Tian-Chun. Investigation on the relationship between the properties of atomic layer deposition ZnO film and the dose of precursor. Acta Physica Sinica, 2013, 62(14): 147306. doi: 10.7498/aps.62.147306
[17]	Yan Da-Wei, Li Li-Sha, Jiao Jin-Ping, Huang Hong-Juan, Ren Jian, Gu Xiao-Feng. Capacitance characteristics of atomic layer deposited Al2O3/n-GaN MOS structure. Acta Physica Sinica, 2013, 62(19): 197203. doi: 10.7498/aps.62.197203
[18]	Su Shao-Jian, Wang Wei, Zhang Guang-Ze, Hu Wei-Xuan, Bai An-Qi, Xue Chun-Lai, Zuo Yu-Hua, Cheng Bu-Wen, Wang Qi-Ming. Epitaxial growth of Ge0.975Sn0.025alloy films on Si(001) substrates by molecular beam epitaxy. Acta Physica Sinica, 2011, 60(2): 028101. doi: 10.7498/aps.60.028101
[19]	Zhang Yan-Hui, Chen Ping-Ping, Li Tian-Xin, Yin Hao. InNSb single crystal films prepared on GaAs (001) substrates by molecular beam epitaxy. Acta Physica Sinica, 2010, 59(11): 8026-8030. doi: 10.7498/aps.59.8026
[20]	JING CHAO, JIN XIAO-FENG, DONG GUO-SHENG, GONG XIAO-YAN, YU LI-MING, ZHENG WEI-MIN. EXCHANGE BIASING IN MOLECULAR-BEAM-EPITAXY-GROWN Fe/Fe50Mn50 BILAYERS. Acta Physica Sinica, 2000, 49(10): 2022-2026. doi: 10.7498/aps.49.2022

Catalog

Vol. 70, Issue 2 - 2021-01-20

Metrics

Abstract views: 13604
PDF Downloads: 434
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板