In this paper, a two-dimensional subwavelength periodic titanium (Ti) disk array integrated in micro-bridge structure is proposed to enhance the absorption of terahertz (THz) microbolometer. Based on the rigorous coupled wave analysis (RCWA) method, THz absorption characteristics of Ti disk arrays with different structure parameters in micro-bridge structure arrays are studied. Periodic disk array structure reduces the surface plasmon frequency of Ti, excites the spoof surface plasmons in the THz band and leads to resonance enhanced absorption. The resonance absorption frequency is determined by the structural parameters of Ti disk array including period and diameter while the absorption rate of THz wave is greatly affected by the thickness of Ti disks. The resonant cavity in micro-bridge structure can reduce the resonance frequency and enhance the coupling efficiency. The micro-bridge structure designed in this paper breaks the diffraction limit and traps the THz wave with a small period (37 μm). An absorption of nearly 90% is achieved at 3.5 THz. The structure meets the requirements of small size, high absorption and good process compatibility of the THz microbolometer.
[1] Qin B Y, Li Z, Hu F R, Hu C, Chen T, Zhang H, Zhao Y H 2018 IEEE Trans. Terahertz Sci. Technol. 8 149
Google Scholar
[2] Peng Y, Qi B B, Jiang X K, Zhu Z, Zhao H W, Zhu Y M 2018 Appl. Phys. B 124 81
Google Scholar
[3] Kanda N, Konishi K, Nemoto N, Midorikawa K, Kuwata-Gonokami M 2017 Sci. Rep. 7 42540
Google Scholar
[4] Pan S, Du C H, Qi X B,Liu P K 2017 Sci. Rep. 7 7265
Google Scholar
[5] Sirkeli V P, Yilmazoglu O, Preu S, FrankoKüppers, Hartnagel H L 2018 Sens. Lett. 16 1
Google Scholar
[6] Hussin R, Liu L J, Luo Y 2017 IEEE Trans. Electron Devices 64 4450
Google Scholar
[7] Li K, Hao Y, Jin X Q, Lu W 2018 J. Phys. D: Appl. Phys. 51 035104
Google Scholar
[8] Uzawa Y, Kroug M, Kojima T, Makise K, Gonzalez A, Saito S, Fujii Y, Kaneko K, Terai H, Wang Z 2017 IEEE Trans. Appl. Supercond. 27 1500705
Google Scholar
[9] Zhou T, Li H, Wan W J, Fu Z L, Cao J C 2017 AIP Adv. 7 105215
Google Scholar
[10] Liang Z Q, Li S B, Liu Z J, Jiang Y D, Li W Z, Wang T, Wang J 2015 J. Mater. Sci.-Mater. Electron. 26 5400
Google Scholar
[11] Nemoto N, Kanda N, Imai R, Konishi K, Miyoshi M, Kurashina S 2016 IEEE Trans. Terahertz Sci. Technol. 6 175
Google Scholar
[12] Gou J, Niu Q C, Liang K, Wang J, Jiang Y D 2018 Nanoscale Res. Lett. 13 74
Google Scholar
[13] Corcos D, Kaminski N, Shumaker E, Markish O, Elad D, Morf T, Drechsler U, Saha W T S, Kull L, Wood K, Pfeiffer U R, Grzyb J 2015 IEEE Trans. Terahertz Sci. Technol. 5 902
Google Scholar
[14] Coppinger M J,Sustersic N A, Kolodzey J, Allik T H 2011 Opt. Eng. 50 053206
Google Scholar
[15] Laman N, Grischkowsky D 2008 Appl. Phys. Lett. 93 051105
Google Scholar
[16] Simoens F, Meilhan J 2014 Philos. Trans. R. Soc. A 372 20130111
Google Scholar
[17] Gou J, WangJ, Zheng X, Gu D E, Yu H, Jiang Y D 2015 RSC Adv. 5 84252
Google Scholar
[18] Gou J, Wang J, Li W Z, Tai H L, Gu D E, Jiang Y D 2013 J. Infrared, Millimeter, Terahertz Waves 34 431
Google Scholar
[19] Alves F, Karamitros A, Grbovic D, Kearney B, Karunasiri G 2012 Opt. Eng. 51 063801
Google Scholar
[20] Nguyen D T, Simoens F, Ouvrier-Buffet J L, Meilhan J, Coutaz J L 2012 IEEE Trans. Terahertz Sci. Technol. 2 299
Google Scholar
[21] Oden J, Jérome M, Jérémy L D, Jean-François R, Frédéric G, Jean-Louis C, François S 2013 Opt. Express 21 4817
Google Scholar
[22] Zhu P, Shi H, Guo L J 2012 Opt. Express 20 12521
Google Scholar
[23] Pors A, Moreno E, Martin-Moreno L, Pendry J B, Garcia-Vidal F J 2012 Phys. Rev. Lett. 108 223905
Google Scholar
[24] O'Hara J, Averitt R, Taylor A 2004 Opt. Express 12 6397
Google Scholar
[25] Pendry J B, Martín-Moreno L, Garcia-Vidal F J 2004 Science 305 847
Google Scholar
[26] Robertson K W, Lapierre R R, Krich J J 2019 Opt. Express 27 A133
Google Scholar
[27] Weismann M, Gallagher D F G, Panoiu N C 2015 J. Opt. 17 125612
Google Scholar
[28] Li L 1997 J. Opt. Soc. Am. A 14 2758
Google Scholar
[29] Moharam M G, Gaylord T K 1983 J. Opt. Soc. Am. 73 1105
Google Scholar
[30] Ordal M A, Bell R J, Alexander R W, Newquist L A, Querry M R 1988 Appl. Opt. 27 1203
Google Scholar
[31] Cataldo G, Beall J A, Cho H M, Mcandrew B, Niemack M D, Wollack E J 2012 Opt. Lett. 37 4200
Google Scholar
[32] Dragoman M, Dragoman D 2008 Prog. Quantum Electron. 32 1
Google Scholar
[33] Ebbesen T W, Lezec H J, Ghaemi H F, Thio T, Wolff P A 1998 Nature 391 667
Google Scholar
-
图 1 吸收结构图 (a) 太赫兹微测辐射热计焦平面阵列的探测单元微桥结构; (b)二维亚波长Ti圆盘阵列俯视图; (c) 周期Ti圆盘阵列剖面图; (d) 增加反射层的吸收结构; (e) 增加反射层及支撑层的吸收结构; (f) 直角坐标系下的入射平面波与吸收结构模型
Figure 1. Absorption structures: (a) Pixel structure of THz microbolometer focal plane array (FPA); (b) top view of a two-dimensional subwavelength Ti disk array; (c) sectional view of a periodic Ti disk array; (d) absorption structure with a reflection layer; (e) absorption structure with reflection layer and supporting layer; (f) absorption structure illuminated by a plane wave with a rectangular Cartesian coordinate system attached.
图 2 Ti与Si3N4的材料参数 (a) Ti在不同频率下的nTi与kTi值; (b) Si3N4在不同频率下的
${n_{{\rm{S}}{{\rm{i}}_3}{{\rm{N}}_4}}}$ 与$ {k_{{\rm{S}}{{\rm{i}}_3}{{\rm{N}}_4}}} $ 值Figure 2. Material parameters of Ti and Si3N4: (a) nTi and kTi values of Ti at different frequencies; (b)
${n_{{\rm{S}}{{\rm{i}}_3}{{\rm{N}}_4}}}$ and$ {k_{{\rm{S}}{{\rm{i}}_3}{{\rm{N}}_4}}} $ values of Si3N4 at different frequencies.
图 3 单层周期Ti圆盘阵列的太赫兹波吸收特性 (a)周期Ti圆盘阵列的太赫兹波反射率(R)、透射率(T)与吸收率(A)曲线(p = 37 μm, d = 14 μm, t = 10 nm), 插图为厚度10 nm的连续Ti薄膜的太赫兹波反射率(R)、透射率(T)与吸收率(A)曲线; (b)不同直径周期比(d/p)的Ti圆盘阵列在3.5 THz频率处的太赫兹波吸收率
Figure 3. Terahertz wave absorption characteristics of single-layer periodic Ti disk array: (a) Terahertz wave reflection (R), transmission (T), and absorption (A) curves for periodic Ti disk arrays (p = 37 μm, d = 14 μm, t = 10 nm), inset: Reflection (R), transmission (T), and absorption (A) curves for a continuous Ti film with a thickness of 10 nm; (b) terahertz wave absorption at 3.5 THz for Ti disk arrays with different ratios of diameter and period (d/p).
图 4 带有真空腔、反射层与支撑层的Ti圆盘阵列的太赫兹波吸收特性 (a) 增加真空腔与反射层后连续Ti薄膜与Ti圆盘阵列(p = 37 μm, d = 28 μm)在不同频率下的太赫兹波反射率、透过率与吸收率; (b) 增加支撑层后连续Ti薄膜与不同直径(d)的Ti圆盘阵列(p = 37 μm)在不同频率下的太赫兹波吸收率
Figure 4. Terahertz wave absorption characteristics of periodic Ti disk arrays with resonant cavity reflection layer and supporting layer: (a) Terahertz wave reflection (R), transmission (T) and absorption (A) curves for continuous Ti film and periodic Ti disk arrays with resonant cavity and reflection layer (p = 37 μm, d = 28 μm); (b) terahertz absorption curve for continuous Ti film and periodic Ti disk arrays with different diameters (d) and a supporting layer (p = 37 μm).
图 5 不同Si3N4支撑层厚度与Ti圆盘厚度的吸收结构的太赫兹波吸收特性 (a)不同Si3N4支撑层厚度(h)的吸收结构在不同频率下的太赫兹波吸收率(p = 37 μm, d = 34 μm, t = 10 nm); (b)不同Ti圆盘厚度(t)的吸收结构在不同频率下的太赫兹波吸收率, 插图为不同Ti圆盘厚度(t)的吸收结构在3.5 THz下的峰值吸收率(p = 37 μm, d = 34 μm)
Figure 5. Terahertz wave absorption characteristics of periodic Ti disk arrays with different thicknesses of supporting layer and Ti disks: (a) Terahertz absorption at different frequencies for absorption structures with different thicknesses (h) of Si3N4 support layers (p = 37 μm, d = 34 μm, t = 10 nm); (b) terahertz absorption at different frequencies for absorption structures with different thicknesses (t) of Ti disks; Inset: Peak absorption rate at 3.5 THz for absorbing structures with different thicknesses (t) of Ti disks (p = 37 μm, d = 34 μm).
图 6 共振吸收频率(3.5 THz)下吸收结构的电场分布 (a) yz平面上吸收结构的电场分布; (b) xy平面上吸收结构的电场分布(p = 37 μm, d = 34 μm, t = 40 nm)
Figure 6. Electric field distribution of the absorption structure at the resonance absorption frequency (3.5 THz): (a) Electric field distribution in the yz plane; (b) electric field distribution in the xy plane (p = 37 μm, d = 34 μm, t = 40 nm).
-
[1] Qin B Y, Li Z, Hu F R, Hu C, Chen T, Zhang H, Zhao Y H 2018 IEEE Trans. Terahertz Sci. Technol. 8 149
Google Scholar
[2] Peng Y, Qi B B, Jiang X K, Zhu Z, Zhao H W, Zhu Y M 2018 Appl. Phys. B 124 81
Google Scholar
[3] Kanda N, Konishi K, Nemoto N, Midorikawa K, Kuwata-Gonokami M 2017 Sci. Rep. 7 42540
Google Scholar
[4] Pan S, Du C H, Qi X B,Liu P K 2017 Sci. Rep. 7 7265
Google Scholar
[5] Sirkeli V P, Yilmazoglu O, Preu S, FrankoKüppers, Hartnagel H L 2018 Sens. Lett. 16 1
Google Scholar
[6] Hussin R, Liu L J, Luo Y 2017 IEEE Trans. Electron Devices 64 4450
Google Scholar
[7] Li K, Hao Y, Jin X Q, Lu W 2018 J. Phys. D: Appl. Phys. 51 035104
Google Scholar
[8] Uzawa Y, Kroug M, Kojima T, Makise K, Gonzalez A, Saito S, Fujii Y, Kaneko K, Terai H, Wang Z 2017 IEEE Trans. Appl. Supercond. 27 1500705
Google Scholar
[9] Zhou T, Li H, Wan W J, Fu Z L, Cao J C 2017 AIP Adv. 7 105215
Google Scholar
[10] Liang Z Q, Li S B, Liu Z J, Jiang Y D, Li W Z, Wang T, Wang J 2015 J. Mater. Sci.-Mater. Electron. 26 5400
Google Scholar
[11] Nemoto N, Kanda N, Imai R, Konishi K, Miyoshi M, Kurashina S 2016 IEEE Trans. Terahertz Sci. Technol. 6 175
Google Scholar
[12] Gou J, Niu Q C, Liang K, Wang J, Jiang Y D 2018 Nanoscale Res. Lett. 13 74
Google Scholar
[13] Corcos D, Kaminski N, Shumaker E, Markish O, Elad D, Morf T, Drechsler U, Saha W T S, Kull L, Wood K, Pfeiffer U R, Grzyb J 2015 IEEE Trans. Terahertz Sci. Technol. 5 902
Google Scholar
[14] Coppinger M J,Sustersic N A, Kolodzey J, Allik T H 2011 Opt. Eng. 50 053206
Google Scholar
[15] Laman N, Grischkowsky D 2008 Appl. Phys. Lett. 93 051105
Google Scholar
[16] Simoens F, Meilhan J 2014 Philos. Trans. R. Soc. A 372 20130111
Google Scholar
[17] Gou J, WangJ, Zheng X, Gu D E, Yu H, Jiang Y D 2015 RSC Adv. 5 84252
Google Scholar
[18] Gou J, Wang J, Li W Z, Tai H L, Gu D E, Jiang Y D 2013 J. Infrared, Millimeter, Terahertz Waves 34 431
Google Scholar
[19] Alves F, Karamitros A, Grbovic D, Kearney B, Karunasiri G 2012 Opt. Eng. 51 063801
Google Scholar
[20] Nguyen D T, Simoens F, Ouvrier-Buffet J L, Meilhan J, Coutaz J L 2012 IEEE Trans. Terahertz Sci. Technol. 2 299
Google Scholar
[21] Oden J, Jérome M, Jérémy L D, Jean-François R, Frédéric G, Jean-Louis C, François S 2013 Opt. Express 21 4817
Google Scholar
[22] Zhu P, Shi H, Guo L J 2012 Opt. Express 20 12521
Google Scholar
[23] Pors A, Moreno E, Martin-Moreno L, Pendry J B, Garcia-Vidal F J 2012 Phys. Rev. Lett. 108 223905
Google Scholar
[24] O'Hara J, Averitt R, Taylor A 2004 Opt. Express 12 6397
Google Scholar
[25] Pendry J B, Martín-Moreno L, Garcia-Vidal F J 2004 Science 305 847
Google Scholar
[26] Robertson K W, Lapierre R R, Krich J J 2019 Opt. Express 27 A133
Google Scholar
[27] Weismann M, Gallagher D F G, Panoiu N C 2015 J. Opt. 17 125612
Google Scholar
[28] Li L 1997 J. Opt. Soc. Am. A 14 2758
Google Scholar
[29] Moharam M G, Gaylord T K 1983 J. Opt. Soc. Am. 73 1105
Google Scholar
[30] Ordal M A, Bell R J, Alexander R W, Newquist L A, Querry M R 1988 Appl. Opt. 27 1203
Google Scholar
[31] Cataldo G, Beall J A, Cho H M, Mcandrew B, Niemack M D, Wollack E J 2012 Opt. Lett. 37 4200
Google Scholar
[32] Dragoman M, Dragoman D 2008 Prog. Quantum Electron. 32 1
Google Scholar
[33] Ebbesen T W, Lezec H J, Ghaemi H F, Thio T, Wolff P A 1998 Nature 391 667
Google Scholar
DownLoad:
Catalog
Metrics
- Abstract views: 8786
- PDF Downloads: 75
- Cited By: 0