Resistive switching characteristics of HfO<sub><i>x</i></sub>-based resistance random access memory under photoelectric synergistic regulation

Wang Ying; Huang Hui-Xiang; Huang Xiang-Lin; Guo Ting-Ting

doi:10.7498/aps.72.20230797

Abstract

Cu/HfO_x/Pt and Cu/HfO_x-ZnO/Pt resistance random access memory (RRAM) devices are prepared by magnetron sputtering. The results show that the Cu/HfO_x/Pt device has the stable bipolar resistive switching characteristics, good retention (as long as 10⁴ s), and a switching ratio greater than 10³. The current conduction mechanism of HfO_x device is ohmic conduction at low resistance, while space charge limited current (SCLC) mechanism dominates at high resistance, and the conductive filament is composed of oxygen vacancies. Owing to the low content and random distribution of oxygen defects in the HfO_x film, the endurance and uniformity of the device are poor. Compared with HfO_x device, HfO_x-ZnO device exhibits lower operating voltage and better uniformity and stability. The main reason is that ZnO material has smaller formation energy of oxygen vacancy, which can produce more oxygen defects under electric field to participate in the resistive switching behavior of the device, thereby reducing the operating voltage and improving the uniformity of the device. In addition, owing to the existence of the interface between HfO_x and ZnO film, the random distribution of oxygen defects is inhibited, that is, the random fracture and formation of conductive filament are inhibited, which is beneficial to improving the uniformity of the device. In addition, the resistive switching behaviors of Cu/HfO_x/Pt and Cu/HfO_x-ZnO/Pt RRAM devices under different intensities of 255 nm ultraviolet illumination are studied. For Cu/HfO_x/Pt device, the light of 255 nm wavelength shows little effect on its resistive switching characteristics. For the Cu/HfO_x-ZnO/Pt RRAM device, the operating voltage and stability of the device can be improved by increasing the light intensity. Although the switching ratio of the device decreases with the increase of light intensity, the device can exhibit multiple resistance states by adjusting different light intensities to achieve multi-level storage. Finally, the analysis of the I-V curves of the devices indicates that the two types of devices show similar resistive switching mechanisms under the illumination of light or no light, which can be explained by the resistive switching mechanism of oxygen vacancy conductive filament. Therefore, a physical model based on the oxygen vacancy conductive filament is established to explain the resistive switching behavior of the device in this paper.

Keywords:

Authors and contacts

School of Materials Science and Engineering, Chang’an University, Xi’an 710061, China

Corresponding author: Guo Ting-Ting, guott@chd.edu.cn

Funds: Project supported by the Young Scientists Fund of the National Natural Science Foundation of China (Grant No. 51802025) and the Natural Science Foundation Research Plan of Shaanxi Province, China (Grant No. 2020JQ-384).

FullText HTML : translate this paragraph

References

[1]	Guo T, Elshekh H, Yu Z, Yu B, Wang D, Kadhim M S, Chen Y Z, Hou W T, Sun B 2019 Mater. Today Commun. 20 100540 Google Scholar
[2]	Yoo S J, Agbenyeke R E, Choi H, Jeon K, Ryu J J, Eom T, Park B K, Chung T M, Jeong D S, Song W 2022 Appl. Surf. Sci. 577 151936 Google Scholar
[3]	Killedar S T, Ahir N A, Morankar P J, Tiwari A P, Kim D K 2020 Opt. Mater. 109 110333 Google Scholar
[4]	龚少康, 周静, 王志青, 朱茂聪, 沈杰, 吴智, 陈文 2021 70 197301 Google Scholar Gong S K, Zhou J, Wang Z Q, Zhu M C, Shen J, Wu Z, Chen W 2021 Acta Phys. Sin. 70 197301 Google Scholar
[5]	Guo T T, Huang H X, Huang X L, Wang Y, Duan L, Xu Z 2022 J. Alloys Compd. 921 166218 Google Scholar
[6]	More K D, Narwade V N, Halge D I, Dadge J W, Bogle K A 2020 Physica B 595 412339 Google Scholar
[7]	He H K, Yang R, Zhou W, Huang H M, Xiong J, Gan L, Zhai T Y, Guo X 2018 Small 14 1800079 Google Scholar
[8]	Zhou H, Wei X D, Wei W, Ye C, Zhang R L, Zhang L, Xia Q, Huang H, Wang B 2019 Surf. Coat. Tech. 359 150 Google Scholar
[9]	张娇娇, 周龙, 王洪强, 董广志, 樊慧庆 2023 铸造技术 44 23 Google Scholar Zhang J J, Zhou L, Wang H Q, Dong G Z, Fan H Q 2023 Foundry Technology 44 23 Google Scholar
[10]	Wang Y H, He Z Q, Lai X B, Liu B Y, Chen Y B, Zhang L W, Wang F P 2021 J. Alloys Compd. 873 159809 Google Scholar
[11]	Strukov D B, Snider G S, Stewart D R, Williams R S 2008 Nature 453 80 Google Scholar
[12]	Zhang L, Huang H, Ye C, Chang K C, Zhang R L, Xia Q, Wei X D, Wei W, Wang W F 2018 Semicond. Sci. Tech. 33 085013 Google Scholar
[13]	代月花, 潘志勇, 陈真, 王菲菲, 李宁, 金波, 李晓风 2016 65 073101 Google Scholar Dai Y H, Pan Z Y, Chen Z, Wang F F, Li N, Jin B, Li X F 2016 Acta Phys. Sin. 65 073101 Google Scholar
[14]	Leydecker T, Herder M, Pavlica E, Bratina G, Hecht S, Orgiu E, Samorì P 2016 Nat Nanotechnol. 11 769 Google Scholar
[15]	Lee Y J, Liu K H, Peng Y, Yen M C, Tamada K 2020 Nat. Commun. 12 4460 Google Scholar
[16]	曾凡菊, 谭永前, 唐孝生, 张小梅, 尹海峰 2021 70 157301 Google Scholar Zeng F J, Tan Y Q, Tang X S, Zhang X M, Yin H F 2021 Acta Phys. Sin. 70 157301 Google Scholar
[17]	Ge N N, Gong C H, Yuan X C, Zeng H Z, Wei X H 2018 RSC Adv. 8 29499 Google Scholar
[18]	Kao M C, Chen H Z, Chen K H, Shi J B, Chen K P 2020 Thin Solid Films 697 137816 Google Scholar
[19]	Chen Z L, Yu Y, Jin L F, Li Y F, Li Q Y, Li T T, Li J, Zhao H L, Zhang Y T, Dai H T 2021 J. Mater Chem. C 8 2178 Google Scholar
[20]	Singh L, Kaushik V, Rajput S, Kumar M 2021 J. Lightwave Technol. 39 5869 Google Scholar
[21]	Ungureanu M, Zazpe R, Golmar F, Stoliar P, Llopis R, Casanova F, Hueso L E 2012 Adv. Mater. 24 2496 Google Scholar
[22]	Zhu X J, Lu W D 2018 Acs Nano 12 1242 Google Scholar
[23]	Russo P, Xiao M, Liang R, Zhou N Y 2018 Adv Funct. Mater. 28 17062301 Google Scholar
[24]	Xie S, Pei L, Li M Y, Zhu Y D, Cheng X Y, Ding H Q, Xiong R 2018 J. Alloys Compd. 778 141 Google Scholar
[25]	Xue W H, Ci W J, Xu X H, Liu G 2020 Chin. Phys. B. 29 048401 Google Scholar
[26]	Sharath S U, Bertaud T, Kurian J, Hildebrandt E, Walczyk C, Calka P, Zaumseil P, Sowinska M, Walczyk D, Gloskovskii A, Schroeder T, Alff L 2014 Appl. Phys. Lett. 104 063502 Google Scholar
[27]	Guo T T, Wang Y X, Duan L, Fan J B, Wang Z Z 2021 Vacuum 189 110224 Google Scholar
[28]	Bon C Y, Kim D, Lee K, Choi S, Yoo S I 2020 AIP Adv. 10 115117 Google Scholar
[29]	Kannadasan N, Shanmugam N, Cholan S, Sathishkumar K, Viruthagiri G, Poonguzhali R 2014 Current Appl. Phys. 14 1760 Google Scholar
[30]	Pereira L, Barquinha P, Fortunato E, Martins R 2005 Mater. Sci Engineer B 118 210 Google Scholar
[31]	Praksgh R, Sharma S, Kumar A, Kaur D 2019 Appl. Phys. Lett. 115 052108 Google Scholar
[32]	Wu P, Zhang J, Lu J G, Li X F, Wu C J, Sun R J, Feng L S, Jiang Q J, Lu B, Pan X H 2014 IEEE T Electron. Dev. 61 1431 Google Scholar
[33]	Liu P, She G W, Liao Z L, Wang Y, Wang Z Z, Shi W S, Zhang X H, Lee S T, Chen D M 2009 Appl. Phys. Lett. 94 635 Google Scholar
[34]	Laiho R, Poloskin D S, Stepanov Y P, Vlasenko M P, Vlasenko L S, Zakhvalinskii V S 2009 J Appl. Phys. 106 56 Google Scholar
[35]	Wang X J, Wang Y Y, Feng M, Wang K Y, Tian Y M 2020 Current Appl. Phys. 20 261104 Google Scholar
[36]	Tan T T, Du Y H, Sun Y L, Zhang H, Cao A, Zha G Q 2019 J. Mater. Sci. 30 13445 Google Scholar

Cited By

图 1 HfO_x-ZnO样品的测试示意图(a)和TEM图像(b)

Figure 1. Test schematic (a) and TEM images (b) of HfO_x-ZnO samples.

DownLoad: Full-Size Img PowerPoint

图 2 (a), (b) HfO_x薄膜的XPS能谱; (c), (d) ZnO薄膜的XPS能谱

Figure 2. (a), (b) XPS spectra of HfO_x film; (c), (d) XPS spectra of ZnO film.

DownLoad: Full-Size Img PowerPoint

图 3 器件的双极性I-V曲线(插图为电形成过程)　(a) HfO_x; (b) HfO_x-ZnO

Figure 3. Bipolar I-V curves of the device (Inset shows the forming process): (a) HfO_x; (b) HfO_x-ZnO.

DownLoad: Full-Size Img PowerPoint

图 4 两种器件的阻变性能　(a)操作电压分布; (b)电阻分布; (c)耐受性; (d)保持性

Figure 4. Switching properties of two samples: (a) Statistical distribution of switching voltages; (b) statistical distribution of resistances; (c) endurance; (d) retention properties.

DownLoad: Full-Size Img PowerPoint

图 5 薄膜的UV-Vis光谱图(插图为光学带隙)　(a) HfO_x; (b) HfO_x-ZnO

Figure 5. UV-Vis spectra of the films (Inset shows Tauc plot): (a) HfO_x; (b) HfO_x-ZnO.

DownLoad: Full-Size Img PowerPoint

图 6 不同强度光照下器件的I-V曲线(插图为电形成过程)(a) HfO_x; (b) HfO_x-ZnO; (c) HfO_x-ZnO器件开启电压随光照强度的变化

Figure 6. Bipolar I-V curves of the device under different light intensity: (The inset shows the forming process): (a) HfO_x; (b) HfO_x-ZnO; (c) forming voltage of HfO_x-ZnO device changes with the light intensity.

DownLoad: Full-Size Img PowerPoint

图 7 HfO_x-ZnO器件不同强度光照下的阻变性能　(a)—(e)耐受性; (f)操作电压分布

Figure 7. Resistive switching performance of the HfO_x-ZnO device under different light intensities: (a)–(e) Endurance; (f) statistical distribution of switching voltages.

DownLoad: Full-Size Img PowerPoint

图 8 HfO_x-ZnO器件的多级存储的性能　(a)高低阻值; (b)保持性

Figure 8. Multilevel memory performance of HfO_x-ZnO device: (a) High and low resistances; (b) retention properties.

DownLoad: Full-Size Img PowerPoint

图 9 器件的阻变机制　(a) HfO_x; (b) HfO_x-ZnO; (c) Cu/HfO_x/Pt器件LRS阻值与温度的关系

Figure 9. Resistive switching mechanism of devices: (a) HfO_x; (b) HfO_x-ZnO; (c) relationship between LRS resistance and temperature of Cu/HfO_x/Pt.

DownLoad: Full-Size Img PowerPoint

图 10 HfO_x-ZnO器件的电阻开关物理微观过程

Figure 10. Physical microscopic process of the resistance switch of the HfO_x-ZnO device.

DownLoad: Full-Size Img PowerPoint

map

[1]	Guo T, Elshekh H, Yu Z, Yu B, Wang D, Kadhim M S, Chen Y Z, Hou W T, Sun B 2019 Mater. Today Commun. 20 100540 Google Scholar
[2]	Yoo S J, Agbenyeke R E, Choi H, Jeon K, Ryu J J, Eom T, Park B K, Chung T M, Jeong D S, Song W 2022 Appl. Surf. Sci. 577 151936 Google Scholar
[3]	Killedar S T, Ahir N A, Morankar P J, Tiwari A P, Kim D K 2020 Opt. Mater. 109 110333 Google Scholar
[4]	龚少康, 周静, 王志青, 朱茂聪, 沈杰, 吴智, 陈文 2021 70 197301 Google Scholar Gong S K, Zhou J, Wang Z Q, Zhu M C, Shen J, Wu Z, Chen W 2021 Acta Phys. Sin. 70 197301 Google Scholar
[5]	Guo T T, Huang H X, Huang X L, Wang Y, Duan L, Xu Z 2022 J. Alloys Compd. 921 166218 Google Scholar
[6]	More K D, Narwade V N, Halge D I, Dadge J W, Bogle K A 2020 Physica B 595 412339 Google Scholar
[7]	He H K, Yang R, Zhou W, Huang H M, Xiong J, Gan L, Zhai T Y, Guo X 2018 Small 14 1800079 Google Scholar
[8]	Zhou H, Wei X D, Wei W, Ye C, Zhang R L, Zhang L, Xia Q, Huang H, Wang B 2019 Surf. Coat. Tech. 359 150 Google Scholar
[9]	张娇娇, 周龙, 王洪强, 董广志, 樊慧庆 2023 铸造技术 44 23 Google Scholar Zhang J J, Zhou L, Wang H Q, Dong G Z, Fan H Q 2023 Foundry Technology 44 23 Google Scholar
[10]	Wang Y H, He Z Q, Lai X B, Liu B Y, Chen Y B, Zhang L W, Wang F P 2021 J. Alloys Compd. 873 159809 Google Scholar
[11]	Strukov D B, Snider G S, Stewart D R, Williams R S 2008 Nature 453 80 Google Scholar
[12]	Zhang L, Huang H, Ye C, Chang K C, Zhang R L, Xia Q, Wei X D, Wei W, Wang W F 2018 Semicond. Sci. Tech. 33 085013 Google Scholar
[13]	代月花, 潘志勇, 陈真, 王菲菲, 李宁, 金波, 李晓风 2016 65 073101 Google Scholar Dai Y H, Pan Z Y, Chen Z, Wang F F, Li N, Jin B, Li X F 2016 Acta Phys. Sin. 65 073101 Google Scholar
[14]	Leydecker T, Herder M, Pavlica E, Bratina G, Hecht S, Orgiu E, Samorì P 2016 Nat Nanotechnol. 11 769 Google Scholar
[15]	Lee Y J, Liu K H, Peng Y, Yen M C, Tamada K 2020 Nat. Commun. 12 4460 Google Scholar
[16]	曾凡菊, 谭永前, 唐孝生, 张小梅, 尹海峰 2021 70 157301 Google Scholar Zeng F J, Tan Y Q, Tang X S, Zhang X M, Yin H F 2021 Acta Phys. Sin. 70 157301 Google Scholar
[17]	Ge N N, Gong C H, Yuan X C, Zeng H Z, Wei X H 2018 RSC Adv. 8 29499 Google Scholar
[18]	Kao M C, Chen H Z, Chen K H, Shi J B, Chen K P 2020 Thin Solid Films 697 137816 Google Scholar
[19]	Chen Z L, Yu Y, Jin L F, Li Y F, Li Q Y, Li T T, Li J, Zhao H L, Zhang Y T, Dai H T 2021 J. Mater Chem. C 8 2178 Google Scholar
[20]	Singh L, Kaushik V, Rajput S, Kumar M 2021 J. Lightwave Technol. 39 5869 Google Scholar
[21]	Ungureanu M, Zazpe R, Golmar F, Stoliar P, Llopis R, Casanova F, Hueso L E 2012 Adv. Mater. 24 2496 Google Scholar
[22]	Zhu X J, Lu W D 2018 Acs Nano 12 1242 Google Scholar
[23]	Russo P, Xiao M, Liang R, Zhou N Y 2018 Adv Funct. Mater. 28 17062301 Google Scholar
[24]	Xie S, Pei L, Li M Y, Zhu Y D, Cheng X Y, Ding H Q, Xiong R 2018 J. Alloys Compd. 778 141 Google Scholar
[25]	Xue W H, Ci W J, Xu X H, Liu G 2020 Chin. Phys. B. 29 048401 Google Scholar
[26]	Sharath S U, Bertaud T, Kurian J, Hildebrandt E, Walczyk C, Calka P, Zaumseil P, Sowinska M, Walczyk D, Gloskovskii A, Schroeder T, Alff L 2014 Appl. Phys. Lett. 104 063502 Google Scholar
[27]	Guo T T, Wang Y X, Duan L, Fan J B, Wang Z Z 2021 Vacuum 189 110224 Google Scholar
[28]	Bon C Y, Kim D, Lee K, Choi S, Yoo S I 2020 AIP Adv. 10 115117 Google Scholar
[29]	Kannadasan N, Shanmugam N, Cholan S, Sathishkumar K, Viruthagiri G, Poonguzhali R 2014 Current Appl. Phys. 14 1760 Google Scholar
[30]	Pereira L, Barquinha P, Fortunato E, Martins R 2005 Mater. Sci Engineer B 118 210 Google Scholar
[31]	Praksgh R, Sharma S, Kumar A, Kaur D 2019 Appl. Phys. Lett. 115 052108 Google Scholar
[32]	Wu P, Zhang J, Lu J G, Li X F, Wu C J, Sun R J, Feng L S, Jiang Q J, Lu B, Pan X H 2014 IEEE T Electron. Dev. 61 1431 Google Scholar
[33]	Liu P, She G W, Liao Z L, Wang Y, Wang Z Z, Shi W S, Zhang X H, Lee S T, Chen D M 2009 Appl. Phys. Lett. 94 635 Google Scholar
[34]	Laiho R, Poloskin D S, Stepanov Y P, Vlasenko M P, Vlasenko L S, Zakhvalinskii V S 2009 J Appl. Phys. 106 56 Google Scholar
[35]	Wang X J, Wang Y Y, Feng M, Wang K Y, Tian Y M 2020 Current Appl. Phys. 20 261104 Google Scholar
[36]	Tan T T, Du Y H, Sun Y L, Zhang H, Cao A, Zha G Q 2019 J. Mater. Sci. 30 13445 Google Scholar

[1]	Shi Xiao-Hong, Chen Jing-Jin, Cao Xin-Rui, Wu Shun-Qing, Zhu Zi-Zhong. Formation of oxygen vacancies in Li-rich Mn-based cathode material Li_1.167Ni_0.167Co_0.167Mn_0.5O₂. Acta Physica Sinica, 2022, 71(17): 178202. doi: 10.7498/aps.71.20220274
[2]	Zhu Mao-Cong, Shao Ya-Jie, Zhou Jing, Chen Wen, Wang Zhi-Qing, Tian Jing. Resistive properties of CuInS₂ quantum dots regulated by niobium-doped lead zirconate titanate ferroelectric films. Acta Physica Sinica, 2022, 71(20): 207301. doi: 10.7498/aps.71.20220911
[3]	Zhou Zheng, Huang Peng, Kang Jin-Feng. Non-volatile memory based in-memory computing technology. Acta Physica Sinica, 2022, 71(14): 148507. doi: 10.7498/aps.71.20220397
[4]	Gong Shao-Kang, Zhou Jing, Wang Zhi-Qing, Zhu Mao-Cong, Shen Jie, Wu Zhi, Chen Wen. Size-controlled resistive switching performance and regulation mechanism of SnO₂ QDs. Acta Physica Sinica, 2021, 70(19): 197301. doi: 10.7498/aps.70.20210608
[5]	Zeng Fan-Ju, Tan Yong-Qian, Tang Xiao-Sheng, Zhang Xiao-Mei, Yin Hai-Feng. Progress of lead-free perovskite and its resistance switching performance. Acta Physica Sinica, 2021, 70(15): 157301. doi: 10.7498/aps.70.20210065
[6]	Tang Hui, Tang Xin-Gui, Jiang Yan-Ping, Liu Qiu-Xiang, Li Wen-Hua. Oxygen vacancy effect on ionic conductivity and relaxation phenomenon of Sr_xBa_1–xNb₂O₆ ceramics. Acta Physica Sinica, 2019, 68(22): 227701. doi: 10.7498/aps.68.20190562
[7]	Wang Ze-Pu, Fu Nian, Yu Han, Xu Jing-Wei, He Qi, Zheng Shu-Kai, Ding Bang-Fu, Yan Xiao-Bing. Enhancing oxygen vacancy photocatalytic efficiency of bismuth tungstate using In-doped W site. Acta Physica Sinica, 2019, 68(21): 217102. doi: 10.7498/aps.68.20191010
[8]	Yu Zhi-Qiang, Liu Min-Li, Lang Jian-Xun, Qian Kai, Zhang Chang-Hua. Resistive switching characteristics and resistive switching mechanism of Au/TiO2/FTO memristor. Acta Physica Sinica, 2018, 67(15): 157302. doi: 10.7498/aps.67.20180425
[9]	Zhang Zhi-Chao, Wang Fang, Wu Shi-Jian, Li Yi, Mi Wei, Zhao Jin-Shi, Zhang Kai-Liang. Influneces of different oxygen partial pressures on switching properties of Ni/HfOx/TiN resistive switching devices. Acta Physica Sinica, 2018, 67(5): 057301. doi: 10.7498/aps.67.20172194
[10]	Guo Jia-Jun, Dong Jing-Yu, Kang Xin, Chen Wei, Zhao Xu. Effect of transition metal element X (X=Mn, Fe, Co, and Ni) doping on performance of ZnO resistive memory. Acta Physica Sinica, 2018, 67(6): 063101. doi: 10.7498/aps.67.20172459
[11]	Li Ping, Xu Yu-Tang. Monte Carlo simulation of time-dependent dielectric breakdown of oxide caused by migration of oxygen vacancies. Acta Physica Sinica, 2017, 66(21): 217701. doi: 10.7498/aps.66.217701
[12]	Dai Yue-Hua, Pan Zhi-Yong, Chen Zhen, Wang Fei-Fei, Li Ning, Jin Bo, Li Xiao-Feng. Orientation and concentration of Ag conductive filament in HfO2-based resistive random access memory: first-principles study. Acta Physica Sinica, 2016, 65(7): 073101. doi: 10.7498/aps.65.073101
[13]	Dai Guang-Zhen, Jiang Xian-Wei, Xu Tai-Long, Liu Qi, Chen Jun-Ning, Dai Yue-Hua. Effect of oxygen vacancy on lattice and electronic properties of HfO2 by means of density function theory study. Acta Physica Sinica, 2015, 64(3): 033101. doi: 10.7498/aps.64.033101
[14]	Jiang Xian-Wei, Lu Shi-Bin, Dai Guang-Zhen, Wang Jia-Yu, Jin Bo, Chen Jun-Ning. Research of data retention for charge trapping memory by first-principles. Acta Physica Sinica, 2015, 64(21): 213102. doi: 10.7498/aps.64.213102
[15]	Jiang Ran, Du Xiang-Hao, Han Zu-Yin, Sun Wei-Deng. Cluster distribution for oxygen vacancy in Ti/HfO2/Pt resistive switching memory device. Acta Physica Sinica, 2015, 64(20): 207302. doi: 10.7498/aps.64.207302
[16]	Chen Ran, Zhou Li-Wei, Wang Jian-Yun, Chen Chang-Jun, Shao Xing-Long, Jiang Hao, Zhang Kai-Liang, Lü Lian-Rong, Zhao Jin-Shi. Multilevel switching mechanism for resistive random access memory based on Cu/SiOx/Al structure. Acta Physica Sinica, 2014, 63(6): 067202. doi: 10.7498/aps.63.067202
[17]	Dai Guang-Zhen, Dai Yue-Hua, Xu Tai-Long, Wang Jia-Yu, Zhao Yuan-Yang, Chen Jun-Ning, Liu Qi. First principles study on influence of oxygen vacancy in HfO2 on charge trapping memory. Acta Physica Sinica, 2014, 63(12): 123101. doi: 10.7498/aps.63.123101
[18]	Gong Yu, Chen Bai-Hua, Xiong Liang-Ping, Gu Mei, Xiong Jie, Gao Xiao-Ling, Luo Yang-Ming, Hu Sheng, Wang Yu-Hua. Effect of oxygen vacancies on the fluorescence and phosphorescence properties of Ca5MgSi3O12：Eu2+, Dy3+. Acta Physica Sinica, 2013, 62(15): 153201. doi: 10.7498/aps.62.153201
[19]	Yang Jin, Zhou Mao-Xiu, Xu Tai-Long, Dai Yue-Hua, Wang Jia-Yu, Luo Jing, Xu Hui-Fang, Jiang Xian-Wei, Chen Jun-Ning. Composite interfaces and electrode properties of resistive random access memory devices. Acta Physica Sinica, 2013, 62(24): 248501. doi: 10.7498/aps.62.248501
[20]	Yao Ming-Zhen, Gu Mu. Theoretical study on defects associated with oxygen vacancy in PbWO4 crystal. Acta Physica Sinica, 2003, 52(2): 459-462. doi: 10.7498/aps.52.459

Catalog

Vol. 72, Issue 19 - 2023-10-05

Metrics

Abstract views: 2446
PDF Downloads: 69
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板

Resistive switching characteristics of HfO_x-based resistance random access memory under photoelectric synergistic regulation

Abstract

Authors and contacts

Corresponding author: Guo Ting-Ting, guott@chd.edu.cn

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Authors

Referees

About Journal

About

Search

Article

留言板

Resistive switching characteristics of HfOx-based resistance random access memory under photoelectric synergistic regulation

Abstract

Authors and contacts

Corresponding author: Guo Ting-Ting, guott@chd.edu.cn

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Publishing process

Authors

Referees

About Journal

About

Resistive switching characteristics of HfO_x-based resistance random access memory under photoelectric synergistic regulation