Magnetic field effects in non-magnetic luminescent materials: from organic semiconductors to halide perovskites

Tao Cong; Wang Jing-Min; Niu Mei-Ling; Zhu Lin; Peng Qi-Ming; Wang Jian-Pu

doi:10.7498/aps.71.20211872

Abstract

Magnetic field effects (MFEs) are used to describe the changes of the photophysical properties (including photoluminescence, electroluminescence, injectedcurrent, photocurrent, etc.) when materials and devices are subjected to the external magnetic field. The MFEs in non-magnetic luminescent materials and devices were first observed in organic semiconductor. In the past two decades, the effects have been studied extensively as an emerging physical phenomenon, and also used as a unique experimental method to explore the processes such as charge transport, carrier recombination, and spin polarization in organic semiconductors. Recent studies have found that the MFEs can also be observed in metal halide perovskites with strong spin-orbital coupling. Besides, for expanding the research domain of MFEs, these findings can also be utilized to study the physical mechanism in metal halide perovskites, and then provide an insight into the improving of the performance of perovskite devices. In this review, we focus on the magnetic field effects on the electroluminescence and photoluminescence changes of organic semiconductors and halide perovskites. We review the mainstream of theoretical models and representative experimental phenomena which have been found to date, and comparatively analyze the luminescence behaviors of organic semiconductors and halide perovskites under magnetic fields. It is expected that this review can provide some ideas for the research on the MFEs of organic semiconductors and halideperovskites, and contribute to the research of luminescence in organic materials and halideperovskites.

Keywords:

Authors and contacts

Key Laboratory of Flexible Electronics (KLOFE) & Institute of Advanced Materials (IAM), Jiangsu National Synergetic Innovation Center for Advanced Materials (SICAM), Nanjing Tech University (NanjingTech), Nanjing 211816, China

Corresponding author: Peng Qi-Ming, iamqmpeng@njtech.edu.cn ; Wang Jian-Pu, iamjpwang@njtech.edu.cn

Funds: Projected supported by the National Natural Science Foundation-Outstanding Youth Foundation of China (Grant No. 62022040), the Young Scientists Fund of the National Natural Science Foundation of China (Grant No. 11804156), the National Natural Science Foundation of China (Grant No. 51972171), and the Postgraduate Research & Practice Innovation Program of Jiangsu Province, China (Grant Nos. KYCX21_1102, KYCX21_1089).

FullText HTML : translate this paragraph

References

[1]	Sun D, Ehrenfreund E, Vardeny Z V 2014 Chem. Commun. 50 1781 Google Scholar
[2]	Sagar R U R, Zhang X, Wang J, Xiong C 2014 J. Appl. Phys. 115 123708 Google Scholar
[3]	Wang J, Chepelianskii A, Gao F, Greenham N C 2012 Nat. Commun. 3 1191 Google Scholar
[4]	Gautam B R, Nguyen T D, Ehrenfreund E, Vardeny Z V 2012 Phys. Rev. B 85 205207 Google Scholar
[5]	Hu B, Yan L, Shao M 2009 Adv. Mater. 21 1500 Google Scholar
[6]	Devir-Wolfman A H, Khachatryan B, Gautam B R, Tzabary L, Keren A, Tessler N, Vardeny Z V, Ehrenfreund E 2014 Nat. Commun. 5 4529 Google Scholar
[7]	Fert A 2008 Rev. Mod. Phys. 80 1517 Google Scholar
[8]	Gruenberg P A 2008 R. Mod. Phys. 80 1531 Google Scholar
[9]	Sternlicht H, Nieman G C, Robinson G W 1963 J. Chem. Phys. 38 1326 Google Scholar
[10]	Michel-Beyerle M E, Haberkorn R, Bube W, Steffens E, Schröder H, Neusser H J, Schlag E W, Seidlitz H 1976 Chem. Phys. 17 139 Google Scholar
[11]	Kalinowski J, Cocchi M, Virgili D, Di Marco P, Fattori V 2003 Chem. Phys. Lett. 380 710 Google Scholar
[12]	Shao M, Yan L, Pan H, Ivanov I, Hu B 2011 Adv. Mater. 23 2216 Google Scholar
[13]	Nguyen T D, Sheng Y, Rybicki J E, Wohlgenannt M 2008 Sci. Technol. Adv. Mater. 9 024206 Google Scholar
[14]	Mermer Ö, Veeraraghavan G, Francis T L, Sheng Y, Nguyen D T, Wohlgenannt M, Köhler A, Al-Suti M K, Khan M S 2005 Phys. Rev. B 72 205202 Google Scholar
[15]	Bloom F L, Wagemans W, Koopmans B 2008 J. Appl. Phys. 103 07F320 Google Scholar
[16]	Bloom F L, Wagemans W, Kemerink M, Koopmans B 2007 Phys. Rev. Lett. 99 257201 Google Scholar
[17]	Zhang Y, Liu R, Lei Y L, Xiong Z H 2009 Appl. Phys. Lett. 94 083307 Google Scholar
[18]	Yan L, Shao M, Graeff C F O, Hummelgen I, Ma D, Hu B 2012 Appl. Phys. Lett. 100 013301 Google Scholar
[19]	Nguyen T D, Sheng Y, Rybicki J, Veeraraghavan G, Wohlgenannt M 2007 J. Mater. Chem. 17 1995 Google Scholar
[20]	Mahato R N, Luelf H, Siekman M H, Kersten S P, Bobbert P A, de Jong M P, De Cola L, van der Wiel W G 2013 Science 341 257 Google Scholar
[21]	Wang Y, Sahin-Tiras K, Harmon N J, Wohlgenannt M, Flatte M E 2016 Phys. Rev. X 6 011011
[22]	Manser J S, Christians J A, Kamat P V 2016 Chem. Rev. 116 12956 Google Scholar
[23]	Li J, Xu L, Wang T, Song J, Chen J, Xue J, Dong Y, Cai B, Shan Q, Han B, Zeng H 2017 Adv. Mater. 29 1603885 Google Scholar
[24]	Xiao Z, Kerner R A, Zhao L, Tran N L, Lee K M, Koh T W, Scholes G D, Rand B P 2017 Nat. Photonics 11 108 Google Scholar
[25]	Yuan M, Li Na Q, Comin R, Walters G, Sabatini R, Voznyy O, Hoogland S, Zhao Y, Beauregard E M, Kanjanaboos P, Lu Z, Kim D H, Sargent E H 2016 Nat. Nanotechnol. 11 872 Google Scholar
[26]	Wang J, Wang N, Jin Y, Si J, Tan Z K, Du H, Cheng L, Dai X, Bai S, He H, Ye Z, Lai M L, Friend R H, Huang W 2015 Adv. Mater. 27 2311 Google Scholar
[27]	Cho H, Jeong S H, Park M H, Kim Y H, Wolf C, Lee C L, Heo J H, Sadhanala A, Myoung N, Yoo S, Im S H, Friend R H, Lee T W 2015 Science 350 1222 Google Scholar
[28]	Wang N, Cheng L, Ge R, Zhang S, Miao Y, Zou W, Yi C, Sun Y, Cao Y, Yang R, Wei Y, Guo Q, Ke Y, Yu M, Jin Y, Liu Y, Ding Q, Di D, Yang L, Xing G, Tian H, Jin C, Gao F, Friend R H, Wang J, Huang W 2016 Nat. Photonics 10 699 Google Scholar
[29]	Yang X, Zhang X, Deng J, Chu Z, Jiang Q, Meng J, Wang P, Zhang L, Yin Z, You J 2018 Nat. Commun. 9 570 Google Scholar
[30]	Tan Z K, Moghaddam R S, Lai M L, Docampo P, Higler R, Deschler F, Price M, Sadhanala A, Pazos L M, Credgington D, Hanusch F, Bein T, Snaith H J, Friend R H 2014 Nat. Nanotechnol. 9 687 Google Scholar
[31]	Cao Y, Wang N, Tian H, Guo J, Wei Y, Chen H, Miao Y, Zou W, Pan K, He Y, Cao H, Ke Y, Xu M, Wang Y, Yang M, Du K, Fu Z, Kong D, Dai D, Jin Y, Li G, Li H, Peng Q, Wang J, Huang W 2018 Nature 562 249 Google Scholar
[32]	Ema K, Umeda K, Toda M, Yajima C, Arai Y, Kunugita H, Wolverson D, Davies J J 2006 Phys. Rev. B 73 241310 Google Scholar
[33]	Hsiao Y C, Wu T, Li M, Hu B 2015 Adv. Mater. 27 2899 Google Scholar
[34]	Pavliuk M V, Fernandes D L A, El-Zohry A M, Abdellah M, Nedelcu G, Kovalenko M V, Sa J 2016 Adv. Opt. Mater. 4 2004 Google Scholar
[35]	Zhang C, Sun D, Sheng C X, Zhai Y X, Mielczarek K, Zakhidov A, Vardeny Z V 2015 Nat. Phys. 11 428 Google Scholar
[36]	Even J, Pedesseau L, Jancu J M, Katan C 2013 Phys. Status Solidi-Rapid Res. Lett. 8 31 Google Scholar
[37]	Pan R, Wang K, Li Y, Yu H, Li J, Xu L 2021 Adv. Electron. Mater. 7 2100026 Google Scholar
[38]	Niedermeier U 2010 Ph. D. Dissertation (Darmstadt: Technische Universität)
[39]	Frankevich E L, Lymarev A A, Sokolik I, Karasz F E, Blumstengel S, Baughman R H, Horhold H H 1992 Phys. Rev. B 46 9320 Google Scholar
[40]	Kepler R G, Caris J C, Avakian P, Abramson E 1963 Phys. Rev. Lett. 10 400 Google Scholar
[41]	Johnson R C, Merrifield R E, Avakian P, Flippen R B 1967 Phys. Rev. Lett. 19 285 Google Scholar
[42]	Merrifield R E 1971 Magnetic Effects on Triplet Exciton Interactions (Germany: Walter de Gruyter GmbH) pp481–498
[43]	Scharff T, Ratzke W, Zipfel J, Klemm P, Bange S, Lupton J M 2021 Nat. Commun. 12 2071 Google Scholar
[44]	Bobbert P A, Nguyen T D, van Oost F W A, Koopmans B, Wohlgenannt M 2007 Phys. Rev. Lett. 99 216801 Google Scholar
[45]	Desai P, Shakya P, Kreouzis T, Gillin W P, Morley N A, Gibbs M R J 2007 Phys. Rev. B 75 094423 Google Scholar
[46]	Desai P, Shakya P, Kreouzis T, Gillin W P 2007 J. Appl. Phys. 102 073710 Google Scholar
[47]	Hu B, Wu Y 2007 Nat. Mater. 6 985 Google Scholar
[48]	Pope M, Swenberg C 1999 Electronic Processes in Organic Crystals and Polymers (2nd Ed) (Oxford: Oxford University Press) pp1–191
[49]	Ohta N 1996 J. Phys. Chem. 100 7298 Google Scholar
[50]	Peng Q, Li W, Zhang S, Chen P, Li F, Ma Y 2013 Adv. Opt. Mater. 1 362 Google Scholar
[51]	Turro N J 1991 Modern Molecular Photochemistry (Sausalito: University Science Books) pp28–32
[52]	Bagnich S A, Niedermeier U, Melzer C, Sarfert W, von Seggern H 2009 J. Appl. Phys. 106 113702 Google Scholar
[53]	Prigodin V N, Bergeson J D, Lincoln D M, Epstein A J 2006 Synth. Met. 156 757 Google Scholar
[54]	Yoshida Y, Fujii A, Ozaki M, Yoshino K, Frankevich E 2005 Mol. Cryst. Liq. Cryst. 426 19 Google Scholar
[55]	Bergeson J D, Prigodin V N, Lincoln D M, Epstein A J 2008 Phys. Rev. Lett. 100 067201 Google Scholar
[56]	Prigodin V N, Epstein A J 2010 Synth. Met. 160 244 Google Scholar
[57]	Wu Y, Xu Z, Hu B, Howe J 2007 Phys. Rev. B 75 035214 Google Scholar
[58]	Martin J L, Bergeson J D, Prigodin V N, Epstein A J 2010 Synth. Met. 160 291 Google Scholar
[59]	Hayashi H 2004 Introduction to Dynamic Spin Chemistry-Magnetic Field Effects on Chemical and Biochemical Reactions (Singapore: World Scientific Printers (S) Pte Ltd) pp1–268
[60]	Ganzorig C, Fujihira M 2002 Appl. Phys. Lett. 81 3137 Google Scholar
[61]	Sinha S, Monkman A P 2003 Appl. Phys. Lett. 82 4651 Google Scholar
[62]	Davis A H, Bussmann K 2004 J. Vac. Sci. Technol. A 22 1885 Google Scholar
[63]	Wilkinson J, Davis A H, Bussmann K, Long J P 2005 Appl. Phys. Lett. 86 111109 Google Scholar
[64]	Popovic Z D, Aziz H 2005 J. Appl. Phys. 98 013510 Google Scholar
[65]	Merrifield R E 1968 J. Chem. Phys. 48 4318 Google Scholar
[66]	彭其明 2015 博士学位论文 (吉林: 吉林大学) Peng Q M 2015 Ph. D. Dissertation (Jilin: Jilin University) (in Chinese)
[67]	Liu R, Zhang Y, Lei Y L, Chen P, Xiong Z H 2009 J. Appl. Phys. 105 093719 Google Scholar
[68]	Wagemans W, Bloom F L, Bobbert P A, Wohlgenannt M, Koopmans B 2008 J. Appl. Phys. 103 07f303 Google Scholar
[69]	Wagemans W, Koopmans B 2011 Phys. Status Solidi B 248 1029 Google Scholar
[70]	Ern V, Merrifield R E 1968 Phys. Rev. Lett. 21 609 Google Scholar
[71]	Wolf S A, Awschalom D D, Buhrman R A, Daughton J M, von Molnar S, Roukes M L, Chtchelkanova A Y, Treger D M 2001 Science 294 1488 Google Scholar
[72]	Žutić I, Fabian J, Das Sarma S 2004 Rev. Mod. Phys. 76 323 Google Scholar
[73]	Rocha A R, Garcia-Suarez V M, Bailey S W, Lambert C J, Ferrer J, Sanvito S 2005 Nat. Mater. 4 335 Google Scholar
[74]	Brocklehurst B 1969 Nature 221 921 Google Scholar
[75]	Wohlgenannt M, Jiang X M, Vardeny Z V 2003 Synth. Met. 137 1069 Google Scholar
[76]	Karabunarliev S, Bittner E R 2003 Phys. Rev. Lett. 90 057402 Google Scholar
[77]	Cinchetti M, Heimer K, Wuestenberg J P, Andreyev O, Bauer M, Lach S, Ziegler C, Gao Y, Aeschlimann M 2009 Nat. Mater. 8 115 Google Scholar
[78]	Dediu V, Murgia M, Matacotta F C, Taliani C, Barbanera S 2002 Solid State Commun. 122 181 Google Scholar
[79]	Xiong Z H, Wu D, Vardeny Z V, Shi J 2004 Nature 427 821 Google Scholar
[80]	Zhang S, Rolfe N J, Desai P, Shakya P, Drew A J, Kreouzis T, Gillin W P 2012 Phys. Rev. B 86 075206 Google Scholar
[81]	Tang X, Hu Y, Jia W, Pan R, Deng J, Deng J, He Z, Xiong Z 2018 ACS Appl. Mater. Interfaces 10 1948 Google Scholar
[82]	Tang X T, Pan R H, Zhao X, Zhu H Q, Xiong Z H 2020 J. Phys. Chem. Lett. 11 2804 Google Scholar
[83]	Peng Q, Gao N, Li W, Chen P, Li F, Ma Y 2013 Appl. Phys. Lett. 102 193304 Google Scholar
[84]	Chen P, Xiong Z, Peng Q, Bai J, Zhang S, Li F 2014 Adv. Opt. Mater. 2 142 Google Scholar
[85]	Congreve D N, Lee J, Thompson N J, Hontz E, Yost S R, Reusswig P D, Bahlke M E, Reineke S, Van Voorhis T, Baldo M A 2013 Science 340 334 Google Scholar
[86]	Sun D L, Basel T P, Gautam B R, Han W, Jiang X, Parkin S S P, Vardeny Z V 2013 Appl. Phys. Lett. 103 042411 Google Scholar
[87]	Sutherland B R, Sargent E H 2016 Nat. Photonics 10 295 Google Scholar
[88]	Shi D, Adinolfi V, Comin R, Yuan M, Alarousu E, Buin A, Chen Y, Hoogland S, Rothenberger A, Katsiev K, Losovyj Y, Zhang X, Dowben P A, Mohammed O F, Sargent E H, Bakr O M 2015 Science 347 519 Google Scholar
[89]	Stranks S D, Eperon G E, Grancini G, Menelaou C, Alcocer M J P, Leijtens T, Herz L M, Petrozza A, Snaith H J 2013 Science 342 341 Google Scholar
[90]	Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[91]	Jeong J, Kim M, Seo J, Lu H, Ahlawat P, Mishra A, Yang Y, Hope M A, Eickemeyer F T, Kim M, Yoon Y J, Choi I W, Darwich B P, Choi S J, Jo Y, Lee J H, Walker B, Zakeeruddin S M, Emsley L, Rothlisberger U, Hagfeldt A, Kim D S, Grätzel M, Kim J Y 2021 Nature 592 381 Google Scholar
[92]	Umari P, Mosconi E, De Angelis F 2014 Sci. Rep. 4 4467
[93]	Papavassiliou G C, Koutselas I B, Lagouvardos D J, Kapoutsis J, Terzis A, Papaioannou G J 1994 Mol. Cryst. Liq. Cryst. 253 103 Google Scholar
[94]	Kim M, Im J, Freeman A J, Ihm J, Jin H 2014 Proc. Nat. l Acad. Sci. USA 111 6900 Google Scholar
[95]	Rossi D, Liu X, Lee Y, Khurana M, Puthenpurayil J, Kim K, Akimov A V, Cheon J, Son D H 2020 Nano Lett. 20 7321 Google Scholar
[96]	Ehrenfreund E, Vardeny V 2019 Magnetic Field Effects in Organic Semiconductors; Low and High Fields, Steady State and Time Resolved (Abingdon: CRC Press/Taylor & Francis) pp277–298
[97]	Vardeny Z V, Wohlgenannt M 2017 World Scientific Reference on Spin in Organics (Singapore: World Scientific) pp345–353
[98]	帅志刚 2020 有机光电材料理论与计算 (北京: 科学出版社) 第268—314页 Shuai Z G 2020 Theory and Calculation of Organic Optoelectronic Materials (Beijing: Science Press) pp268–314 (in Chinese)

Cited By

图 1 基于Alq₃的OLED (a)电致发光和(b)电流的磁场效应^[11]

Figure 1. Magnetic field effects on (a) electroluminescence and (b) current of Alq₃-based OLED^[11].

DownLoad: Full-Size Img PowerPoint

图 2 Alq₃器件在不同电压下的(a) MC和(b) MEL^[13]; (c) Ru(bpy)₃器件在不同电压下的MEL^[12]; (d)不同长度一维结构器件的MR^[20]; 延迟荧光器件在不同温度下的(e) MC和(f) MEL^[21]

Figure 2. The (a) MC and (b) MEL of Alq₃-based OLED at different voltages^[13]; (c) the MEL of Ru(bpy)₃-based OLED at different voltages^[12]; (d) the MR in the device with one-dimensional structure^[20]; the (e) MC and (f) MEL of delayed fluorescence OLED at different temperatures ^[21] .

DownLoad: Full-Size Img PowerPoint

图 3 OLED中载流子相互作用决定的激发态类型^[38]

Figure 3. Excited states in OLED determined by the interactions between carriers ^[38] .

DownLoad: Full-Size Img PowerPoint

图 4 (a)自由载流子、电子-空穴对和激子的跃迁能级示意图及相关速率常数, 其中S和T分别表示单线态和三线态, G表示EHP的形成率, $ {k}_{\mathrm{d}}^{\mathrm{S}} $和$ {k}_{\mathrm{d}}^{\mathrm{T}} $分别代表单线态和三线态EHP的离解速率常数, $ {k}_{\mathrm{r}}^{\mathrm{S}} $和$ {k}_{\mathrm{r}}^{\mathrm{T}} $为单线态和三线态EHP的复合速率常数; (b)电子、空穴在磁场下以不同频率$ \omega $进动示意图

Figure 4. (a) Transition rate constants of free carriers, electron-hole pairs and excitons. S and T represent singlet and triplet states, respectively. G represents the formation rate of EHP. $ {k}_{\mathrm{d}}^{\mathrm{S}} $ and $ {k}_{\mathrm{d}}^{\mathrm{T}} $ represent the dissociation rate constants of singlet and triplet EHPs, respectively, $ {k}_{\mathrm{r}}^{\mathrm{S}} $ and $ {k}_{\mathrm{r}}^{\mathrm{T}} $ are the recombination rate constants of singlet and triplet EHPs. (b) The Larmor precession of electrons and holes with different frequency ω under a magnetic field.

DownLoad: Full-Size Img PowerPoint

图 5 三线态-三线态淬灭(TTA)模型示意图^[66]

Figure 5. Schematic diagram of the triplet-triplet annihilation (TTA) model ^[66] .

DownLoad: Full-Size Img PowerPoint

图 6 (a)双极化子的形成过程; (b)外磁场下双极化子形成概率减小; (c)利用双极化子模型拟合磁场效应^[44]

Figure 6. (a) Formation process of the bipolaron; (b) the probability of the bipolaron formation decreases under the external magnetic field; (c) fitting the magnetic field effect with the bipolaron model ^[44].

DownLoad: Full-Size Img PowerPoint

图 7 (a)无外加磁场和(b)有外加磁场下三线态激子对自由载流子的散射作用^[38]

Figure 7. Scattering effects of triplet excitons on free carriers (a) without and (b) with an external magnetic field ^[38].

DownLoad: Full-Size Img PowerPoint

图 8 (a)有机光电器件中的自旋极化效应, 其中绿线为外磁场方向^[3]; (b)自旋极化下荧光发射被强烈抑制而磷光发射增强^[43]

Figure 8. (a) Spin polarization in OLED, where the green line is the direction of the external magnetic field^[3] ; (b) the fluorescence is strongly suppressed while the phosphorescence is enhanced by TSP^[43] .

DownLoad: Full-Size Img PowerPoint

图 9 金属卤化物钙钛矿的晶胞结构^[87]

Figure 9. Crystal structure of the metal halide perovskites^[87].

DownLoad: Full-Size Img PowerPoint

图 10 (a)钙钛矿中不同自旋态的子能带偏离k空间的Γ点^[36]; (b)导带与价带表现出自旋极化方向相反的分裂^[94]

Figure 10. (a) Sub-bands with different spins states deviate from the Γ point in the k space of perovskites^[36]; (b) the conduction band and valence band show opposite spin splitting depending on the spin polarization direction^[94] .

DownLoad: Full-Size Img PowerPoint

图 11 (a)电子-空穴对中Δg机制示意图; (b) 5 mA恒定电流下的MEL; (c)钙钛矿薄膜的MPL; (d) 0和5 T磁场下左右圆偏振旋光光谱; (e) 18 K温度下薄膜的圆偏振度与磁场的关系^[35]

Figure 11. (a) Schematic diagram of the Δg mechanism of electron-hole pairs; (b) the MEL at a constant current of 5 mA; (c) the MPL of the perovskite film; (d) the left and right circularly polarized optical rotation spectra at 0 and 5 T; (e) the relationship between the degree of circularly polarization and the magnetic field at 18 K ^[35] .

DownLoad: Full-Size Img PowerPoint

图 12 (a)钙钛矿薄膜在不同激发光强下的MPL; (b)钙钛矿光伏器件在不同激发光强下的MC; (c)正MC和负MPL的线形特征; (d)钙钛矿中的电子-空穴对模型示意图^[33]

Figure 12. (a) MPL of the perovskite film with different excitation intensities at room temperature; (b) MC of the perovskite solar cell with different excitation intensities; (c) linear characteristics of positive MC and negative MPL; (d) schematic diagram of the electron-hole pair model in perovskites ^[33] .

DownLoad: Full-Size Img PowerPoint

图 13 (a) (C₄H₉NH₃)₂PbBr₄的PL谱, 其中Γ₁和Γ₂为暗态, Γ₅为亮态; (b)自旋驰豫(左图)和自旋翻转(右图)示意图; (c) PL随磁场的变化^[32]

Figure 13. (a) PL spectra of (C₄H₉NH₃)₂PbBr₄, where Γ₁ and Γ₂ are dark states, and Γ₅ is bright state; (b) schematic diagram of the spin relaxation (left) and spin flip (right); (c) the PL changes under the magnetic fields^[32] .

DownLoad: Full-Size Img PowerPoint

图 14 (a) 0 ℃下, CsPbBr₃薄膜有/无500 mT的PL光谱; (b)无磁场和(c)有磁场的瞬态PL光谱; (d)无磁场和(e)有磁场下515 nm处复合动力学轨迹^[34]

Figure 14. (a) The PL spectra of CsPbBr₃ film with/without a magnetic field of 500 mT at 0 ℃; the time resolved PL spectra in the obsence (b) and presence (c) of a magnetic field; the recombination kinetics extracted from the time resolved PLs in the obsence (d) and presence (e) of a magnetic field ^[34].

DownLoad: Full-Size Img PowerPoint

表 1 光生载流子复合动力学常数^[34]

Table 1. Recombination kinetic constants of photogenerated carrier ^[34] .

Power/(mW· cm^–2)	Magnet OFF		Magnet ON
Power/(mW· cm^–2)	Fast decay/ps	Slow decay/ps	Fast decay/ps	Slow decay/ps
198	138$ \pm $9 (55%)	1038$ \pm $65 (45%)	104$ \pm $6 (63%)	959$ \pm $55 (37%)
305	138$ \pm $8 (55%)	1031$ \pm $31 (45%)	100$ \pm $4 (64%)	886$ \pm $25 (36%)
450	131$ \pm $5 (57%)	1000$ \pm $34 (43%)	101$ \pm $5 (65%)	892$ \pm $23 (35%)

DownLoad: CSV

map

[1]	Sun D, Ehrenfreund E, Vardeny Z V 2014 Chem. Commun. 50 1781 Google Scholar
[2]	Sagar R U R, Zhang X, Wang J, Xiong C 2014 J. Appl. Phys. 115 123708 Google Scholar
[3]	Wang J, Chepelianskii A, Gao F, Greenham N C 2012 Nat. Commun. 3 1191 Google Scholar
[4]	Gautam B R, Nguyen T D, Ehrenfreund E, Vardeny Z V 2012 Phys. Rev. B 85 205207 Google Scholar
[5]	Hu B, Yan L, Shao M 2009 Adv. Mater. 21 1500 Google Scholar
[6]	Devir-Wolfman A H, Khachatryan B, Gautam B R, Tzabary L, Keren A, Tessler N, Vardeny Z V, Ehrenfreund E 2014 Nat. Commun. 5 4529 Google Scholar
[7]	Fert A 2008 Rev. Mod. Phys. 80 1517 Google Scholar
[8]	Gruenberg P A 2008 R. Mod. Phys. 80 1531 Google Scholar
[9]	Sternlicht H, Nieman G C, Robinson G W 1963 J. Chem. Phys. 38 1326 Google Scholar
[10]	Michel-Beyerle M E, Haberkorn R, Bube W, Steffens E, Schröder H, Neusser H J, Schlag E W, Seidlitz H 1976 Chem. Phys. 17 139 Google Scholar
[11]	Kalinowski J, Cocchi M, Virgili D, Di Marco P, Fattori V 2003 Chem. Phys. Lett. 380 710 Google Scholar
[12]	Shao M, Yan L, Pan H, Ivanov I, Hu B 2011 Adv. Mater. 23 2216 Google Scholar
[13]	Nguyen T D, Sheng Y, Rybicki J E, Wohlgenannt M 2008 Sci. Technol. Adv. Mater. 9 024206 Google Scholar
[14]	Mermer Ö, Veeraraghavan G, Francis T L, Sheng Y, Nguyen D T, Wohlgenannt M, Köhler A, Al-Suti M K, Khan M S 2005 Phys. Rev. B 72 205202 Google Scholar
[15]	Bloom F L, Wagemans W, Koopmans B 2008 J. Appl. Phys. 103 07F320 Google Scholar
[16]	Bloom F L, Wagemans W, Kemerink M, Koopmans B 2007 Phys. Rev. Lett. 99 257201 Google Scholar
[17]	Zhang Y, Liu R, Lei Y L, Xiong Z H 2009 Appl. Phys. Lett. 94 083307 Google Scholar
[18]	Yan L, Shao M, Graeff C F O, Hummelgen I, Ma D, Hu B 2012 Appl. Phys. Lett. 100 013301 Google Scholar
[19]	Nguyen T D, Sheng Y, Rybicki J, Veeraraghavan G, Wohlgenannt M 2007 J. Mater. Chem. 17 1995 Google Scholar
[20]	Mahato R N, Luelf H, Siekman M H, Kersten S P, Bobbert P A, de Jong M P, De Cola L, van der Wiel W G 2013 Science 341 257 Google Scholar
[21]	Wang Y, Sahin-Tiras K, Harmon N J, Wohlgenannt M, Flatte M E 2016 Phys. Rev. X 6 011011
[22]	Manser J S, Christians J A, Kamat P V 2016 Chem. Rev. 116 12956 Google Scholar
[23]	Li J, Xu L, Wang T, Song J, Chen J, Xue J, Dong Y, Cai B, Shan Q, Han B, Zeng H 2017 Adv. Mater. 29 1603885 Google Scholar
[24]	Xiao Z, Kerner R A, Zhao L, Tran N L, Lee K M, Koh T W, Scholes G D, Rand B P 2017 Nat. Photonics 11 108 Google Scholar
[25]	Yuan M, Li Na Q, Comin R, Walters G, Sabatini R, Voznyy O, Hoogland S, Zhao Y, Beauregard E M, Kanjanaboos P, Lu Z, Kim D H, Sargent E H 2016 Nat. Nanotechnol. 11 872 Google Scholar
[26]	Wang J, Wang N, Jin Y, Si J, Tan Z K, Du H, Cheng L, Dai X, Bai S, He H, Ye Z, Lai M L, Friend R H, Huang W 2015 Adv. Mater. 27 2311 Google Scholar
[27]	Cho H, Jeong S H, Park M H, Kim Y H, Wolf C, Lee C L, Heo J H, Sadhanala A, Myoung N, Yoo S, Im S H, Friend R H, Lee T W 2015 Science 350 1222 Google Scholar
[28]	Wang N, Cheng L, Ge R, Zhang S, Miao Y, Zou W, Yi C, Sun Y, Cao Y, Yang R, Wei Y, Guo Q, Ke Y, Yu M, Jin Y, Liu Y, Ding Q, Di D, Yang L, Xing G, Tian H, Jin C, Gao F, Friend R H, Wang J, Huang W 2016 Nat. Photonics 10 699 Google Scholar
[29]	Yang X, Zhang X, Deng J, Chu Z, Jiang Q, Meng J, Wang P, Zhang L, Yin Z, You J 2018 Nat. Commun. 9 570 Google Scholar
[30]	Tan Z K, Moghaddam R S, Lai M L, Docampo P, Higler R, Deschler F, Price M, Sadhanala A, Pazos L M, Credgington D, Hanusch F, Bein T, Snaith H J, Friend R H 2014 Nat. Nanotechnol. 9 687 Google Scholar
[31]	Cao Y, Wang N, Tian H, Guo J, Wei Y, Chen H, Miao Y, Zou W, Pan K, He Y, Cao H, Ke Y, Xu M, Wang Y, Yang M, Du K, Fu Z, Kong D, Dai D, Jin Y, Li G, Li H, Peng Q, Wang J, Huang W 2018 Nature 562 249 Google Scholar
[32]	Ema K, Umeda K, Toda M, Yajima C, Arai Y, Kunugita H, Wolverson D, Davies J J 2006 Phys. Rev. B 73 241310 Google Scholar
[33]	Hsiao Y C, Wu T, Li M, Hu B 2015 Adv. Mater. 27 2899 Google Scholar
[34]	Pavliuk M V, Fernandes D L A, El-Zohry A M, Abdellah M, Nedelcu G, Kovalenko M V, Sa J 2016 Adv. Opt. Mater. 4 2004 Google Scholar
[35]	Zhang C, Sun D, Sheng C X, Zhai Y X, Mielczarek K, Zakhidov A, Vardeny Z V 2015 Nat. Phys. 11 428 Google Scholar
[36]	Even J, Pedesseau L, Jancu J M, Katan C 2013 Phys. Status Solidi-Rapid Res. Lett. 8 31 Google Scholar
[37]	Pan R, Wang K, Li Y, Yu H, Li J, Xu L 2021 Adv. Electron. Mater. 7 2100026 Google Scholar
[38]	Niedermeier U 2010 Ph. D. Dissertation (Darmstadt: Technische Universität)
[39]	Frankevich E L, Lymarev A A, Sokolik I, Karasz F E, Blumstengel S, Baughman R H, Horhold H H 1992 Phys. Rev. B 46 9320 Google Scholar
[40]	Kepler R G, Caris J C, Avakian P, Abramson E 1963 Phys. Rev. Lett. 10 400 Google Scholar
[41]	Johnson R C, Merrifield R E, Avakian P, Flippen R B 1967 Phys. Rev. Lett. 19 285 Google Scholar
[42]	Merrifield R E 1971 Magnetic Effects on Triplet Exciton Interactions (Germany: Walter de Gruyter GmbH) pp481–498
[43]	Scharff T, Ratzke W, Zipfel J, Klemm P, Bange S, Lupton J M 2021 Nat. Commun. 12 2071 Google Scholar
[44]	Bobbert P A, Nguyen T D, van Oost F W A, Koopmans B, Wohlgenannt M 2007 Phys. Rev. Lett. 99 216801 Google Scholar
[45]	Desai P, Shakya P, Kreouzis T, Gillin W P, Morley N A, Gibbs M R J 2007 Phys. Rev. B 75 094423 Google Scholar
[46]	Desai P, Shakya P, Kreouzis T, Gillin W P 2007 J. Appl. Phys. 102 073710 Google Scholar
[47]	Hu B, Wu Y 2007 Nat. Mater. 6 985 Google Scholar
[48]	Pope M, Swenberg C 1999 Electronic Processes in Organic Crystals and Polymers (2nd Ed) (Oxford: Oxford University Press) pp1–191
[49]	Ohta N 1996 J. Phys. Chem. 100 7298 Google Scholar
[50]	Peng Q, Li W, Zhang S, Chen P, Li F, Ma Y 2013 Adv. Opt. Mater. 1 362 Google Scholar
[51]	Turro N J 1991 Modern Molecular Photochemistry (Sausalito: University Science Books) pp28–32
[52]	Bagnich S A, Niedermeier U, Melzer C, Sarfert W, von Seggern H 2009 J. Appl. Phys. 106 113702 Google Scholar
[53]	Prigodin V N, Bergeson J D, Lincoln D M, Epstein A J 2006 Synth. Met. 156 757 Google Scholar
[54]	Yoshida Y, Fujii A, Ozaki M, Yoshino K, Frankevich E 2005 Mol. Cryst. Liq. Cryst. 426 19 Google Scholar
[55]	Bergeson J D, Prigodin V N, Lincoln D M, Epstein A J 2008 Phys. Rev. Lett. 100 067201 Google Scholar
[56]	Prigodin V N, Epstein A J 2010 Synth. Met. 160 244 Google Scholar
[57]	Wu Y, Xu Z, Hu B, Howe J 2007 Phys. Rev. B 75 035214 Google Scholar
[58]	Martin J L, Bergeson J D, Prigodin V N, Epstein A J 2010 Synth. Met. 160 291 Google Scholar
[59]	Hayashi H 2004 Introduction to Dynamic Spin Chemistry-Magnetic Field Effects on Chemical and Biochemical Reactions (Singapore: World Scientific Printers (S) Pte Ltd) pp1–268
[60]	Ganzorig C, Fujihira M 2002 Appl. Phys. Lett. 81 3137 Google Scholar
[61]	Sinha S, Monkman A P 2003 Appl. Phys. Lett. 82 4651 Google Scholar
[62]	Davis A H, Bussmann K 2004 J. Vac. Sci. Technol. A 22 1885 Google Scholar
[63]	Wilkinson J, Davis A H, Bussmann K, Long J P 2005 Appl. Phys. Lett. 86 111109 Google Scholar
[64]	Popovic Z D, Aziz H 2005 J. Appl. Phys. 98 013510 Google Scholar
[65]	Merrifield R E 1968 J. Chem. Phys. 48 4318 Google Scholar
[66]	彭其明 2015 博士学位论文 (吉林: 吉林大学) Peng Q M 2015 Ph. D. Dissertation (Jilin: Jilin University) (in Chinese)
[67]	Liu R, Zhang Y, Lei Y L, Chen P, Xiong Z H 2009 J. Appl. Phys. 105 093719 Google Scholar
[68]	Wagemans W, Bloom F L, Bobbert P A, Wohlgenannt M, Koopmans B 2008 J. Appl. Phys. 103 07f303 Google Scholar
[69]	Wagemans W, Koopmans B 2011 Phys. Status Solidi B 248 1029 Google Scholar
[70]	Ern V, Merrifield R E 1968 Phys. Rev. Lett. 21 609 Google Scholar
[71]	Wolf S A, Awschalom D D, Buhrman R A, Daughton J M, von Molnar S, Roukes M L, Chtchelkanova A Y, Treger D M 2001 Science 294 1488 Google Scholar
[72]	Žutić I, Fabian J, Das Sarma S 2004 Rev. Mod. Phys. 76 323 Google Scholar
[73]	Rocha A R, Garcia-Suarez V M, Bailey S W, Lambert C J, Ferrer J, Sanvito S 2005 Nat. Mater. 4 335 Google Scholar
[74]	Brocklehurst B 1969 Nature 221 921 Google Scholar
[75]	Wohlgenannt M, Jiang X M, Vardeny Z V 2003 Synth. Met. 137 1069 Google Scholar
[76]	Karabunarliev S, Bittner E R 2003 Phys. Rev. Lett. 90 057402 Google Scholar
[77]	Cinchetti M, Heimer K, Wuestenberg J P, Andreyev O, Bauer M, Lach S, Ziegler C, Gao Y, Aeschlimann M 2009 Nat. Mater. 8 115 Google Scholar
[78]	Dediu V, Murgia M, Matacotta F C, Taliani C, Barbanera S 2002 Solid State Commun. 122 181 Google Scholar
[79]	Xiong Z H, Wu D, Vardeny Z V, Shi J 2004 Nature 427 821 Google Scholar
[80]	Zhang S, Rolfe N J, Desai P, Shakya P, Drew A J, Kreouzis T, Gillin W P 2012 Phys. Rev. B 86 075206 Google Scholar
[81]	Tang X, Hu Y, Jia W, Pan R, Deng J, Deng J, He Z, Xiong Z 2018 ACS Appl. Mater. Interfaces 10 1948 Google Scholar
[82]	Tang X T, Pan R H, Zhao X, Zhu H Q, Xiong Z H 2020 J. Phys. Chem. Lett. 11 2804 Google Scholar
[83]	Peng Q, Gao N, Li W, Chen P, Li F, Ma Y 2013 Appl. Phys. Lett. 102 193304 Google Scholar
[84]	Chen P, Xiong Z, Peng Q, Bai J, Zhang S, Li F 2014 Adv. Opt. Mater. 2 142 Google Scholar
[85]	Congreve D N, Lee J, Thompson N J, Hontz E, Yost S R, Reusswig P D, Bahlke M E, Reineke S, Van Voorhis T, Baldo M A 2013 Science 340 334 Google Scholar
[86]	Sun D L, Basel T P, Gautam B R, Han W, Jiang X, Parkin S S P, Vardeny Z V 2013 Appl. Phys. Lett. 103 042411 Google Scholar
[87]	Sutherland B R, Sargent E H 2016 Nat. Photonics 10 295 Google Scholar
[88]	Shi D, Adinolfi V, Comin R, Yuan M, Alarousu E, Buin A, Chen Y, Hoogland S, Rothenberger A, Katsiev K, Losovyj Y, Zhang X, Dowben P A, Mohammed O F, Sargent E H, Bakr O M 2015 Science 347 519 Google Scholar
[89]	Stranks S D, Eperon G E, Grancini G, Menelaou C, Alcocer M J P, Leijtens T, Herz L M, Petrozza A, Snaith H J 2013 Science 342 341 Google Scholar
[90]	Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[91]	Jeong J, Kim M, Seo J, Lu H, Ahlawat P, Mishra A, Yang Y, Hope M A, Eickemeyer F T, Kim M, Yoon Y J, Choi I W, Darwich B P, Choi S J, Jo Y, Lee J H, Walker B, Zakeeruddin S M, Emsley L, Rothlisberger U, Hagfeldt A, Kim D S, Grätzel M, Kim J Y 2021 Nature 592 381 Google Scholar
[92]	Umari P, Mosconi E, De Angelis F 2014 Sci. Rep. 4 4467
[93]	Papavassiliou G C, Koutselas I B, Lagouvardos D J, Kapoutsis J, Terzis A, Papaioannou G J 1994 Mol. Cryst. Liq. Cryst. 253 103 Google Scholar
[94]	Kim M, Im J, Freeman A J, Ihm J, Jin H 2014 Proc. Nat. l Acad. Sci. USA 111 6900 Google Scholar
[95]	Rossi D, Liu X, Lee Y, Khurana M, Puthenpurayil J, Kim K, Akimov A V, Cheon J, Son D H 2020 Nano Lett. 20 7321 Google Scholar
[96]	Ehrenfreund E, Vardeny V 2019 Magnetic Field Effects in Organic Semiconductors; Low and High Fields, Steady State and Time Resolved (Abingdon: CRC Press/Taylor & Francis) pp277–298
[97]	Vardeny Z V, Wohlgenannt M 2017 World Scientific Reference on Spin in Organics (Singapore: World Scientific) pp345–353
[98]	帅志刚 2020 有机光电材料理论与计算 (北京: 科学出版社) 第268—314页 Shuai Z G 2020 Theory and Calculation of Organic Optoelectronic Materials (Beijing: Science Press) pp268–314 (in Chinese)

[1]	Xi Yu-Ying, Han Yue, Li Guo-Hui, Zhai Ai-Ping, Ji Ting, Hao Yu-Ying, Cui Yan-Xia. Application of heterostructures in halide perovskite photovoltaic devices. Acta Physica Sinica, 2020, 69(16): 167804. doi: 10.7498/aps.69.20200591
[2]	Li Zhen-Chao, Chen Zi-Ming, Zou Guang-Rui-Xing, Yip Hin-Lap, Cao Yong. Applications of organic additives in metal halide perovskite light-emitting diodes. Acta Physica Sinica, 2019, 68(15): 158505. doi: 10.7498/aps.68.20190307
[3]	Wang Ji-Fei, Lin Dong-Xu, Yuan Yong-Bo. Recent progress of ion migration in organometal halide perovskite. Acta Physica Sinica, 2019, 68(15): 158801. doi: 10.7498/aps.68.20190853
[4]	Zhao Wan-Ying, Ku Zhi-Liang, Jin Zuan-Ming, Liu Wei-Min, Lin Xian, Dai Ye, Yan Xiao-Na, Ma Guo-Hong, Yao Jian-Quan. Photoinduced charge carrier dynamics and spectral band filling in organometal halide perovskites. Acta Physica Sinica, 2019, 68(1): 018401. doi: 10.7498/aps.68.20181854
[5]	Li Zhi-Hao, Cao Liang, Guo Yu-Xian. Electronic structure of a 3, 4, 9, 10-perylene-tetracarboxylic-dianhydride thin film revealed by synchrotron-based resonant photoemission spectroscopy. Acta Physica Sinica, 2017, 66(22): 224101. doi: 10.7498/aps.66.224101
[6]	Huang Chao, Liu Ling-Yun, Fang Jun, Zhang Wen-Hua, Wang Kai, Gao Pin, Xu Fa-Qiang. High magnetic field influence on the molecular orientation and the morphology of iron phthalocyanine thin films. Acta Physica Sinica, 2016, 65(15): 156101. doi: 10.7498/aps.65.156101
[7]	He Chao, Zhang Xu, Liu Zhi, Cheng Bu-Wen. Recent progress in Ge and GeSn light emission on Si. Acta Physica Sinica, 2015, 64(20): 206102. doi: 10.7498/aps.64.206102
[8]	Cao Ning-Tong, Zhang Lei, Lü Lu, Xie Hai-Peng, Huang Han, Niu Dong-Mei, Gao Yong-Li. van der Waals heterostructure about CuPc/MoS2(0001). Acta Physica Sinica, 2014, 63(16): 167903. doi: 10.7498/aps.63.167903
[9]	Liu Rui-Lan, Wang Xu-Liang, Tang Chao. Identification for hole transporting properties of NPB based on particle swarm optimization algorithm. Acta Physica Sinica, 2014, 63(2): 028105. doi: 10.7498/aps.63.028105
[10]	Jian Lei, Tan Ying-Xiong, Li Quan, Zhao Ke-Qing. Charge transport properties of truxene derivatives molecules. Acta Physica Sinica, 2013, 62(18): 183101. doi: 10.7498/aps.62.183101
[11]	Zhang Yong, Liu Ya-Li, Jiao Wei, Chen Lin, Xiong Zu-Hong. Magnetoconductance effect in organic light-emitting devices. Acta Physica Sinica, 2012, 61(11): 117106. doi: 10.7498/aps.61.117106
[12]	Wang Jin, Jiang Wen-Long, Hua Jie, Wang Guang-De, Han Qiang, Chang Xi, Zhang Gang. Influence of magnetic field on efficiency and current in Co-based organic light emitting diode. Acta Physica Sinica, 2010, 59(11): 8212-8217. doi: 10.7498/aps.59.8212
[13]	Liu Rong, Zhang Yong, Lei Yan-Lian, Chen Ping, Zhang Qiao-Ming, Xiong Zu-Hong. Tuning effect of magnetic-field in organic light emitting diodes using LiF layer. Acta Physica Sinica, 2010, 59(6): 4283-4289. doi: 10.7498/aps.59.4283
[14]	Wang Run-Sheng, Meng Wei-Min, Peng Ying-Quan, Ma Chao-Zhu, Li Rong-Hua, Xie Hong-Wei, Wang Ying, Zhao Ming, Yuan Jian-Ting. The theory of physical doping in organic semiconductor. Acta Physica Sinica, 2009, 58(11): 7897-7903. doi: 10.7498/aps.58.7897
[15]	Lei Yan-Lian, Liu Rong, Zhang Yong, Tan Xing-Wen, Xiong Zu-Hong. Effects of magnetic field on current in polymer photovoltaic cell. Acta Physica Sinica, 2009, 58(2): 1269-1275. doi: 10.7498/aps.58.1269
[16]	Hu Yue, Rao Hai-Bo, Li Jun-Fei. Numerical model of ITO /organic semiconductor/metal organic light emitting device. Acta Physica Sinica, 2008, 57(9): 5928-5932. doi: 10.7498/aps.57.5928
[17]	Li Xun-Shuan, Peng Ying-Quan, Yang Qing-Sen, Xing Hong-Wei, Lu Fei-Ping. Analytical model of charge transport at organic semiconductor interfaces. Acta Physica Sinica, 2007, 56(9): 5441-5445. doi: 10.7498/aps.56.5441
[18]	Ren Jun-Feng, Zhang Yu-Bin, Xie Shi-Jie. Current spin polarization in ferromagnetic/organic semiconductor/ferromagnetic system. Acta Physica Sinica, 2007, 56(8): 4785-4790. doi: 10.7498/aps.56.4785
[19]	Wang Zhen, He Zheng-Hong, Tan Xing-Wen, Tao Min-Long, Li Guo-Qing, Xiong Zu-Hong. Magnetic field effects on organic electroluminescence. Acta Physica Sinica, 2007, 56(5): 2979-2985. doi: 10.7498/aps.56.2979
[20]	LU MING, XU SHAO-HUI, ZHANG SONG-TAO, HE JUN, XIONG ZU-HONG, DENG ZHEN-BO, DING XUN-MIN. OPTICAL PROPERTIES OF ORGANIC MICROCAVITY BASED ON POROUS SILICON BRAGG REFLECTOR. Acta Physica Sinica, 2000, 49(10): 2083-2088. doi: 10.7498/aps.49.2083

Catalog

Vol. 71, Issue 6 - 2022-03-20

Metrics

Abstract views: 7663
PDF Downloads: 180
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板