Study on physical properties and magnetism controlling of two-dimensional magnetic materials

Jiang Xiao-Hong; Qin Si-Chen; Xing Zi-Yue; Zou Xing-Yu; Deng Yi-Fan; Wang Wei; Wang Lin

doi:10.7498/aps.70.20202146

Abstract

Two-dimensional (2D) materials represented by graphene and molybdenum disulfide (MoS₂) have attracted much attention in recent years due to their advantages in electrical, thermal, optical and mechanical properties. As a branch of 2D materials, 2D magnetic materials have special properties such as magnetic anisotropy and single-layer magnetic order. Especially, their magnetism can also be controlled by a variety of physical fields, and it possesses various physical properties and potential applications. Therefore, they have received widespread attention of researchers gradually. In this article, we summarize the types, synthesis methods, basic characteristics and characterization methods of 2D magnetic materials in detail, and the magnetism controlling of 2D magnetic materials as well. Finally, a simple outlook on the research directions and future challenges of 2D magnetic materials is given.

Keywords:

Authors and contacts

1.
Xi’an Key Laboratory of Biomedical Materials & Engineering, Xi’an Key Laboratory of Flexible Electronics, Shanxi Key Laboratory of Flexible Electronics, MIIT Key Laboratory of Flexible Electronics, Xi’an Institute of Flexible Electronics, Institute of Flexible Electronics, Northwestern Polytechnical University, Xi’an 710072, China
2.
Key Laboratory of Flexible Electronics, Institute of Advanced Materials, Nanjing Tech University, Nanjing 211816, China

Corresponding author: Wang Wei, iamwwang@njtech.edu.cn ; Wang Lin, iamlwang@njtech.edu.cn

Funds: Project supported by the National Key R&D Program of China (Grant No. 2020YFA0308900), the National Natural Science Foundation of China (Grant Nos. 92064010, 61801210, 91833302), the Natural Science Foundation of Jiangsu Province, China (Grant No. BK20180686), the Funding for “Distinguished Professors” and “High-level Talents in Six Industries” of Jiangsu Province, China (Grant No. XYDXX-021), the Fundamental Research Fund for the Central Universities, China, the Key Research and Development Program of Shaanxi Province, China (Grant Nos. 2020GXLH-Z-020, 2020GXLH-Z-027), and the Creative Innovation Seed Fund of Northwestern Polytechnical University for Postgraduate Students, China (Grant No. CX2020287)

FullText HTML : translate this paragraph

References

[1]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Zhang Y, Dubonos S V, Grigorieva I V, Firsov A A 2004 Science 306 666 Google Scholar
[2]	Koppens F H L, Mueller T, Avouris P, Ferrari A C, Vitiello M S, Polini M 2014 Nat. Nanotechnol. 9 780 Google Scholar
[3]	Sangwan V K, Hersam M C 2018 Annu. Rev. Phys. Chem. 69 299 Google Scholar
[4]	Wang Q H, Kalantar-Zadeh K, Kis A, Coleman J N, Strano M S 2012 Nat. Nanotechnol. 7 699 Google Scholar
[5]	Wang W, Wu X, Zhang J 2015 J. Nanomater. 2015 198126 Google Scholar
[6]	Zhang X Y, Hou L L, Ciesielski A, Samori P 2016 Adv. Energy Mater. 6 1600671 Google Scholar
[7]	Fu J B, Xu W Q, Chen X, Zhang S F, Zhang W J, Suo P, Lin X, Wang J, Jin Z M, Liu W M, Ma G H 2020 J. Phys. Chem. C 124 10719 Google Scholar
[8]	Liu B W, Zhang Z, Liao K, Wu R, Zhu C, Xie H G, Zha C Y, Yin Y, Jiang X H, Qin S C, Wang W, Ouyang G, Qin T S, Wang L, Huang W 2020 Appl. Surf. Sci. 523 146371 Google Scholar
[9]	Zong X R, Hu H M, Ouyang G, Wang J W, Shi R, Zhang L, Zeng Q S, Zhu C, Chen S H, Cheng C, Wang B, Zhang H, Liu Z, Huang W, Wang T H, Wang L, Chen X L 2020 Light-Sci. Appl. 9 114 Google Scholar
[10]	Chen X L, Zhou Z S, Deng B C, Wu Z F, Xia F N, Cao Y, Zhang L, Huang W, Wang N, Wang L 2019 Nano Today 27 99 Google Scholar
[11]	Gatensby R, McEvoy N, Lee K, Hallam T, Berner N C, Rezvani E, Winters S, O'Brien M, Duesberg G S 2014 Appl. Surf. Sci. 297 139 Google Scholar
[12]	Ou Z W, Wang T, Tang J B, Zong X R, Wang W, Guo Q B, Xu Y H, Zhu C, Wang L, Huang W, Xu H X 2020 Adv. Opt. Mater. 8 2000201 Google Scholar
[13]	Voevodin A A, Waite A R, Bultman J E, Hu J J, Muratore C 2015 Surf. Coat. Technol. 280 260 Google Scholar
[14]	Reinwald M, Wurstbauer U, Doppe M, Kipferl W, Wagenhuber K, Tranitz H P, Weiss D, Wegscheider W 2005 J. Cryst. Growth 278 690 Google Scholar
[15]	Nazmul A M, Banshchikov A G, Shimizu H, Tanaka M 2001 J. Cryst. Growth 227 874 Google Scholar
[16]	Kobune M, Furotani R, Fujita S, Kikuchi K, Kikuchi T, Fujisawa H, Shimizu M, Fukumuro N 2016 Jpn. J. Appl. Phys. 55 10ta01 Google Scholar
[17]	Paek W B, Kim J, Lim S H 2004 Phys. Status Solidi B 241 1521 Google Scholar
[18]	Redjdal N, Salah H, Hauet T, Menari H, Cherif S M, Gabouze N, Azzaz M 2014 Thin Solid Films 552 164 Google Scholar
[19]	Bhuvaneswari P V, Ramamurthi K, Babu R R, Babu S M 2015 Appl. Phys. A 120 1113 Google Scholar
[20]	Mohamed R B, Nasina M R, Shaik K, Narayananellore S K, Kuppan M 2014 J. Supercond. Novel. Magn. 27 2147 Google Scholar
[21]	Awana G, Cox C, Venkat G, Morrison K, Zhou Z X, Backes D 2020 Mater. Res. Express 7 106406 Google Scholar
[22]	Farrell I L, Hyndman A R, Reeves R J, Williams G V M, Granville S 2017 Thin Solid Films 625 24 Google Scholar
[23]	Miao Y P, Huang Y H, Fang Q L, Yang Z, Xu K W, Ma F, Chu P K 2016 J. Mater. Sci. 51 9514 Google Scholar
[24]	Kaloni T P 2014 J. Phys. Chem. C 118 25200 Google Scholar
[25]	Mao Y L, Guo G, Yuan J M, Zhong J X 2019 Appl. Surf. Sci. 464 236 Google Scholar
[26]	Ersan F, Arkin H, Akturk E 2017 RSC Adv. 7 37815 Google Scholar
[27]	Roldan R, Goerbig M O, Fuchs J N 2010 Semicond. Sci. Technol. 25 034005 Google Scholar
[28]	Romero-Muniz C, Pou P, Perez R 2020 Carbon 159 102 Google Scholar
[29]	Mermin N D, Wagner H 1966 Phys. Rev. Lett. 17 1133 Google Scholar
[30]	Gong C, Li L, Li Z L, Ji H W, Stern A, Xia Y, Cao T, Bao W, Wang C Z, Wang Y A, Qiu Z Q, Cava R J, Louie S G, Xia J, Zhang X 2017 Nature 546 265 Google Scholar
[31]	Huang B, Clark G, Navarro-Moratalla E, Klein D R, Cheng R, Seyler K L, Zhong D, Schmidgall E, McGuire M A, Cobden D H, Yao W, Xiao D, Jarillo-Herrero P, Xu X D 2017 Nature 546 270 Google Scholar
[32]	Deng Y J, Yu Y J, Song Y C, Zhang J Z, Wang N Z, Sun Z Y, Yi Y F, Wu Y Z, Wu S W, Zhu J Y, Wang J, Chen X H, Zhang Y B 2018 Nature 563 94 Google Scholar
[33]	Meena S, Anudeep K 2020 J. Supercond. Novel. Magn. 33 1447 Google Scholar
[34]	Sheng H H, Zhu Y J, Bai D M, Wu X S, Wang J L 2020 Nanotechnology 31 315713 Google Scholar
[35]	Yang J J, Wang J, Liu Q, Xu R, Sun Y L, Li Z P, Gao F M, Xia M R 2020 J. Magn. Magn. Mater. 502 851 Google Scholar
[36]	Serri M, Cucinotta G, Poggini L, Serrano G, Sainctavit P, Strychalska-Nowak J, Politano A, Bonaccorso F, Caneschi A, Cava R J, Sessoli R, Ottaviano L, Klimczuk T, Pellegrini V, Mannini M 2020 Adv. Mater. 32 2000566 Google Scholar
[37]	Yang J T, Zhou Y, Guo Q L, Dedkov Y, Voloshina E 2020 RSC Adv. 10 851 Google Scholar
[38]	Kargar F, Coleman E A, Ghosh S, Lee J, Gomez M J, Liu Y H, Magana A S, Barani Z, Mohammadzadeh A, Debnath B, Wilson R B, Lake R K, Balandin A A 2020 ACS Nano 14 2424 Google Scholar
[39]	Wildes A R, Lancon D, Chan M K, Weickert F, Harrison N, Simonet V, Zhitomirsky M E, Gvozdikova M V, Ziman T, Ronnow H M 2020 Phys. Rev. B 101 024415 Google Scholar
[40]	Sun Y, Luo X 2019 Phys. Status Solidi B 256 1900052 Google Scholar
[41]	Ito N, Kikkawa T, Barker J, Hirobe D, Shiomi Y, Saitoh E 2019 Phys. Rev. B 100 060402 Google Scholar
[42]	Kang S, Kang S, Yu J 2019 J. Electron. Mater. 48 1441 Google Scholar
[43]	Xu C S, Feng J S, Xiang H J, Bellaiche L 2018 Npj Comput. Mater. 4 57 Google Scholar
[44]	Liu H T, Bao L H, Zhou Z, Che B Y, Zhang R Z, Bian C, Ma R S, Wu L M, Yang H F, Li J J, Gu C Z, Shen C M, Du S X, Gao H J 2019 Nano Lett. 19 4551 Google Scholar
[45]	Zheng G L, Xie W Q, Albarakati S, Algarni M, Tan C, Wang Y H, Peng J Y, Partridge J, Farrar L, Yi J B, Xiong Y M, Tian M L, Zhao Y J, Wang L 2020 Phys. Rev. Lett. 125 047202 Google Scholar
[46]	Zhu R, Zhang W, Shen W, Wong P K J, Wang Q X, Liang Q J, Tian Z, Zhai Y, Qiu C W, Wee A T S 2020 Nano Lett. 20 5030 Google Scholar
[47]	Deng Y J, Yu Y J, Shi M Z, Guo Z X, Xu Z H, Wang J, Chen X H, Zhang Y B 2020 Science 367 895 Google Scholar
[48]	Miao N H, Xu B, Zhu L G, Zhou J, Sun Z M 2018 J. Am. Chem. Soc. 140 2417 Google Scholar
[49]	Cortie D L, Causer G L, Rule K C, Fritzsche H, Kreuzpaintner W, Klose F 2020 Adv. Funct. Mater. 30 1901414 Google Scholar
[50]	Li H, Ruan S C, Zeng Y J 2019 Adv. Mater. 31 1900065 Google Scholar
[51]	Jiang S W, Li L Z, Wang Z F, Mak K F, Shan J 2018 Nat. Nanotechnol. 13 549 Google Scholar
[52]	Li X X, Wu X J, Yang J L 2014 J. Am. Chem. Soc. 136 11065 Google Scholar
[53]	Lv P, Li Y L, Wang J F 2020 Phys. Chem. Chem. Phys. 22 11266 Google Scholar
[54]	Wang X Z, Du K Z, Liu Y Y F, Hu P, Zhang J, Zhang Q, Owen M H S, Lu X, Gan C K, Sengupta P, Kloc C, Xiong Q H 2016 2 D Mater. 3 031009 Google Scholar
[55]	Xie Q Y, Wu M, Chen L M, Bai G, Zou W Q, Wang W, He L 2019 Chin. Phys. B 28 056102 Google Scholar
[56]	McGuire M A, Dixit H, Cooper V R, Sales B C 2015 Chem. Mater. 27 4165 Google Scholar
[57]	McGuire M A, Clark G, Santosh K C, Chance W M, Jellison G E, Cooper V R, Xu X D, Sales B C 2017 Phys. Rev. Mater. 1 014001 Google Scholar
[58]	Abramchuk M, Jaszewski S, Metz K R, Osterhoudt G B, Wang Y P, Burch K S, Tafti F 2018 Adv. Mater. 30 085401 Google Scholar
[59]	Song T C, Cai X H, Tu M W Y, Zhang X O, Huang B V, Wilson N P, Seyler K L, Zhu L, Taniguchi T, Watanabe K, McGuire M A, Cobden D H, Xiao D, Yao W, Xu X D 2018 Science 360 1214 Google Scholar
[60]	Jiang P H, Wang C, Chen D C, Zhong Z C, Yuan Z, Lu Z Y, Ji W 2019 Phys. Rev. B 99 144401 Google Scholar
[61]	Chen W O, Sun Z Y, Wang Z J, Gu L H, Xu X D, Wu S W, Gao C L 2019 Science 366 983 Google Scholar
[62]	Zhang Y J, Wu X H, Lyu B B, Wu M H, Zhao S X, Chen J Y, Jia M Y, Zhang C S, Wang L, Wang X W, Chen Y Z, Mei J W, Taniguchi T, Watanabe K, Yan H G, Liu Q H, Huang L, Zhao Y, Huang M Y 2020 Nano Lett. 20 729 Google Scholar
[63]	Seyler K L, Zhong D, Huang B, Linpeng X Y, Wilson N P, Taniguchi T, Watanabe K, Yao W, Xiao D, McGuire M A, Fu K M C, Xu X D 2018 Nano Lett. 18 3823 Google Scholar
[64]	Zhang J Y, Zhao B, Zhou T, Xue Y, Ma C L, Yang Z Q 2018 Phys. Rev. B 97 085401 Google Scholar
[65]	Plumb K W, Clancy J P, Sandilands L J, Shankar V V, Hu Y F, Burch K S, Kee H Y, Kim Y J 2014 Phys. Rev. B 90 041112 Google Scholar
[66]	Kim H S, Shankar V V, Catuneanu A, Kee H Y 2015 Phys. Rev. B 91 241110 Google Scholar
[67]	Zhou Y G, Lu H F, Zu X T, Gao F 2016 Sci. Rep. 6 19407 Google Scholar
[68]	He J J, Ma S Y, Lyu P B, Nachtigall P 2016 J. Mater. Chem. C 4 2518 Google Scholar
[69]	Kong T, Stolze K, Timmons E I, Tao J, Ni D R, Guo S, Yang Z, Prozorov R, Cava R J 2019 Adv. Mater. 31 1808074 Google Scholar
[70]	Son S, Coak M J, Lee N, Kim J, Kim T Y, Hamidov H, Cho H, Liu C, Jarvis D M, Brown P A C, Kim J H, Park C H, Khomskii D I, Saxena S S, Park J G 2019 Phys. Rev. B 99 041402 Google Scholar
[71]	Tian S J, Zhang J F, Li C H, Ying T P, Li S Y, Zhang X, Liu K, Lei H C 2019 J. Am. Chem. Soc. 141 5326 Google Scholar
[72]	Kong T, Guo S, Ni D R, Cava R J 2019 Phys. Rev. Mater. 3 084419 Google Scholar
[73]	Prayitno T B, Ishii F 2019 J. Phys. Soc. Jpn. 88 104705 Google Scholar
[74]	Yan Z P, Li N N, Wang L Y, Yu Z H, Li M T, Zhang J B, Li X D, Yang K, Gao G Y, Wang L 2020 J. Phys. Chem. C 124 23317 Google Scholar
[75]	Feng Y L, Wu X M, Hu L, Gao G Y 2020 J. Mater. Chem. C 8 14353 Google Scholar
[76]	Zhu Y Y, Li H L, Chen T, Liu D S, Zhou Q H 2020 Vacuum 182 109694 Google Scholar
[77]	Teng S K, Mao X J, Liu Z, Liu Y, Xu X T, Li L Y, Xie X J, Fan S S, Zhou G X, Li J, Li J 2020 New J. Phys. 22 103061 Google Scholar
[78]	Han H C, Zheng H L, Wang Q S, Yan Y 2020 Phys. Chem. Chem. Phys. 22 26917 Google Scholar
[79]	Liu H N, Wang X S, Wu J X, Chen Y S, Wan J, Wen R, Yang J B, Liu Y, Song Z G, Xie L M 2020 ACS Nano 14 10544 Google Scholar
[80]	Bernasconi M, Marra G L, Benedek G, Miglio L, Balkanski M, Scagliotti M, Julien C, Jouanne M 1988 Phys. Rev. B 38 12089 Google Scholar
[81]	Susner M A, Chyasnavichyus M, McGuire M A, Ganesh P, Maksymovych P 2017 Adv. Mater. 29 1602852 Google Scholar
[82]	Lancon D, Ewings R A, Guidi T, Formisano F, Wildes A R 2018 Phys. Rev. B 98 134414 Google Scholar
[83]	Joy P A, Vasudevan S 1992 Phys. Rev. B 46 5425 Google Scholar
[84]	Wildes A R, Simonet V, Ressouche E, Ballou R, McIntyre G J 2017 J. Phys.-Condens. Mater. 29 056102 Google Scholar
[85]	Gusmeao R, Sofer Z, Pumera M 2019 Adv. Funct. Mater. 29 1805975 Google Scholar
[86]	Vaclavkova D, Delhomme A, Faugeras C, Potemski M, Bogucki A, Suffczynski J, Kossacki P, Wildes A R, Gremaud B, Saul A 2020 2D Mater. 7 035030 Google Scholar
[87]	Kuo C T, Neumann M, Balamurugan K, Park H J, Kang S, Shiu H W, Kang J H, Hong B H, Han M, Noh T W, Park J G 2016 Sci. Rep. 6 20904 Google Scholar
[88]	Du K Z, Wang X Z, Liu Y, Hu P, Utama M I B, Gan C K, Xiong Q H, Kloc C 2016 ACS Nano 10 1738 Google Scholar
[89]	Lee J U, Lee S, Ryoo J H, Kang S, Kim T Y, Kim P, Park C H, Park J G, Cheong H 2016 Nano Lett. 16 7433 Google Scholar
[90]	Xing W Y, Qiu L Y, Wang X R, Yao Y Y, Ma Y, Cai R R, Jia S, Xie X C, Han W 2019 Phys. Rev. X 9 011026 Google Scholar
[91]	Xie Q Y, Liu Y, Wu M, Lu H Y, Wang W, He L, Wu X S 2019 Mater. Lett. 246 60 Google Scholar
[92]	Carteaux V, Moussa F, Spiesser M 1995 Europhys. Lett. 29 251 Google Scholar
[93]	Zhuang H L L, Xie Y, Kent P R C, Ganesh P 2015 Phys. Rev. B 92 035407 Google Scholar
[94]	Wang Z, Zhang T Y, Ding M, Dong B J, Li Y X, Chen M L, Li X X, Huang J Q, Wang H W, Zhao X T, Li Y, Li D, Jia C K, Sun L D, Guo H H, Ye Y, Sun D M, Chen Y S, Yang T, Zhang J, Ono S P, Han Z, Zhang Z D 2018 Nat. Nanotechnol. 13 554 Google Scholar
[95]	Li Y F, Wang W, Guo W, Gu C Y, Sun H Y, He L, Zhou J, Gu Z B, Nie Y F, Pan X Q 2018 Phys. Rev. B 98 125127 Google Scholar
[96]	Zhang J X, Cai X C, Xia W, Liang A J, Huang J W, Wang C W, Yang L X, Yuan H T, Chen Y L, Zhang S L, Guo Y F, Liu Z K, Liu G 2019 Phys. Rev. Lett. 123 047203 Google Scholar
[97]	Lohmann M, Su T, Niu B, Hou Y S, Alghamdi M, Aldosary M, Xing W Y, Zhong J N, Jia S, Han W, Wu R Q, Cui Y T, Shi J 2019 Nano Lett. 19 2397 Google Scholar
[98]	Ostwal V, Shen T T, Appenzeller J 2020 Adv. Mater. 32 1906021 Google Scholar
[99]	Lin M W, Zhuang H L L, Yan J Q, Ward T Z, Puretzky A A, Rouleau C M, Gai Z, Liang L B, Meunier V, Sumpter B G, Ganesh P, Kent P R C, Geohegan D B, Mandrus D G, Xiao K 2016 J. Mater. Chem. C 4 315 Google Scholar
[100]	Gonzalez-Herrero H, Gomez-Rodriguez J M, Mallet P, Moaied M, Palacios J J, Salgado C, Ugeda M M, Veuillen J Y, Yndurain F, Brihuega I 2016 Science 352 437 Google Scholar
[101]	Nair R R, Sepioni M, Tsai I L, Lehtinen O, Keinonen J, Krasheninnikov A V, Thomson T, Geim A K, Grigorieva I V 2012 Nat. Phys. 8 199 Google Scholar
[102]	Avsar A, Tan J Y, Taychatanapat T, Balakrishnan J, Koon G K W, Yeo Y, Lahiri J, Carvalho A, Rodin A S, O'Farrell E C T, Eda G, Neto A H C, Ozyilmaz B 2014 Nat. Commun. 5 4875 Google Scholar
[103]	Gao D Q, Xue Q X, Mao X Z, Wang W X, Xu Q, Xue D S 2013 J. Mater. Chem. C 1 5909 Google Scholar
[104]	Ma Y D, Dai Y, Guo M, Niu C W, Zhu Y T, Huang B B 2012 ACS Nano 6 1695 Google Scholar
[105]	Arnold F, Stan R M, Mahatha S K, Lund H E, Curcio D, Dendzik M, Bana H, Travaglia E, Bignardi L, Lacovig P, Lizzit D, Li Z S, Bianchi M, Miwa J A, Bremholm M, Lizzit S, Hofmann P, Sanders C E 2018 2D Mater. 5 045009 Google Scholar
[106]	Yu W, Li J, Herng T S, Wang Z S, Zhao X X, Chi X, Fu W, Abdelwahab I, Zhou J, Dan J D, Chen Z X, Chen Z, Li Z J, Lu J, Pennycook S J, Feng Y P, Ding J, Loh K P 2019 Adv. Mater. 31 1903779 Google Scholar
[107]	Chua R, Yang J, He X Y, Yu X J, Yu W, Bussolotti F, Wong P K J, Loh K P, Breese M B H, Goh K E J, Huang Y L, Wee A T S 2020 Adv. Mater. 32 2000693 Google Scholar
[108]	Liu H T, Xue Y Z, Sho J A, Guzman R A, Zhan P P, Zhou Z, He Y G, Bian C, Wu L M, Ma R S, Chen J C, Yan J H, Yang H T, Shen C M, Zhou W, Bao L H, Gao H J 2019 Nano Lett. 19 8572 Google Scholar
[109]	May A F, Calder S, Cantoni C, Cao H B, McGuire M A 2016 Phys. Rev. B 93 014411 Google Scholar
[110]	Zhuang H L L, Kent P R C, Hennig R G 2016 Phys. Rev. B 93 134407 Google Scholar
[111]	Tan C, Lee J, Jung S G, Park T, Albarakati S, Partridge J, Field M R, McCulloch D G, Wang L, Lee C 2018 Nat. Commun. 9 1554 Google Scholar
[112]	Seo J, Kim D Y, An E S, Kim K, Kim G Y, Hwang S Y, Kim D W, Jang B G, Kim H, Eom G, Seo S Y, Stania R, Muntwiler M, Lee J, Watanabe K, Taniguchi T, Jo Y J, Lee J, Min B I, Jo M H, Yeom H W, Choi S Y, Shim J H, Kim J S 2020 Sci. Adv. 6 eaay8912 Google Scholar
[113]	Duong D L, Yun S J, Lee Y H 2017 ACS Nano 11 11803 Google Scholar
[114]	May A F, Ovchinnikov D, Zheng Q, Hermann R, Calder S, Huang B, Fei Z Y, Liu Y H, Xu X D, McGuire M A 2019 ACS Nano 13 4436 Google Scholar
[115]	Li Z X, Xia W, Su H, Yu Z H, Fu Y P, Chen L M, Wang X, Yu N, Zou Z Q, Guo Y F 2020 Sci. Rep. 10 15345 Google Scholar
[116]	Li J H, Li Y, Du S Q, Wang Z, Gu B L, Zhang S C, He K, Duan W H, Xu Y 2019 Sci. Adv. 5 eaaw5685 Google Scholar
[117]	Zhang D Q, Shi M J, Zhu T S, Xing D Y, Zhang H J, Wang J 2019 Phys. Rev. Lett. 122 206401 Google Scholar
[118]	Ge J, Liu Y Z, Li J H, Li H, Luo T C, Wu Y, Xu Y, Wang J 2020 Natl. Sci. Rev. 7 1280 Google Scholar
[119]	Hu C W, Gordon K N, Liu P F, Liu J Y, Zhou X Q, Hao P P, Narayan D, Emmanouilidou E, Sun H Y, Liu Y T, Brawer H, Ramirez A P, Ding L, Cao H B, Liu Q H, Dessau D, Ni N 2020 Nat. Commun. 11 97 Google Scholar
[120]	Aliev Z S, Amiraslanov I R, Nasonova D I, Shevelkov A V, Abdullayev N A, Jahangirli Z A, Orujlu E N, Otrokov M M, Mamedov N T, Babanly M B, Chulkov E V 2019 J. Alloys Compd. 789 443 Google Scholar
[121]	Hu C W, Ding L, Gordon K N, Ghosh B, Tien H J, Li H X, Linn A G, Lien S W, Huang C Y, Mackey S, Liu J Y, Reddy P V S, Singh B, Agarwal A, Bansil A, Song M, Li D S, Xu S Y, Lin H, Cao H B, Chang T R, Dessau D, Ni N 2020 Sci. Adv. 6 eaba4275 Google Scholar
[122]	Jiang Z, Wang P, Xing J P, Jiang X, Zhao J J 2018 ACS Appl. Mater. Interfaces 10 39032 Google Scholar
[123]	Zhang T L, Wang Y M, Li H X, Zhong F, Shi J, Wu M H, Sun Z Y, Shen W F, Wei B, Hu W D, Liu X F, Huang L, Hu C G, Wang Z C, Jiang C B, Yang S X, Zhang Q M, Qu Z 2019 ACS Nano 13 11353 Google Scholar
[124]	Yan S N, Wang P F, Wang C Y, Xu T, Li Z, Cao T J, Chen M Y, Pan C, Cheng B, Sun L T, Liang S J, Miao F 2019 Sci. China Inform. Sci. 62 220407 Google Scholar
[125]	Qing X M, Li H, Zhong C G, Zhou P X, Dong Z C, Liu J M 2020 Phys. Chem. Chem. Phys. 22 17255 Google Scholar
[126]	Ferrenti A M, Klemenz S, Lei S M, Song X Y, Ganter P, Lotsch B V, Schoop L M 2020 Inorg. Chem. 59 1176 Google Scholar
[127]	Li W, Yang Z Y, Hou Y L, Gao S 2020 Prog. Chem. 32 1437 Google Scholar
[128]	Lu H Y, Wang W, Liu Y, Chen L M, Xie Q Y, Yin H D, Cheng G F, He L 2020 Appl. Surf. Sci. 504 144405 Google Scholar
[129]	Yu J X, Li J, Zhang W F, Chang H X 2015 Chem. Sci. 6 6705 Google Scholar
[130]	Li J, Zhao B, Chen P, Wu R, Li B, Xia Q, Guo G, Luo J, Zang K, Zhang Z, Ma H, Sun G, Duan X, Duan X F 2018 Adv. Mater. 30 e1801043 Google Scholar
[131]	Zhang Y, Chu J W, Yin L, Shifa T A, Cheng Z Z, Cheng R Q, Wang F, Wen Y, Zhan X Y, Wang Z X, He J 2019 Adv. Mater. 31 1900056 Google Scholar
[132]	Yuan J T, Balk A, Guo H, Fang Q Y, Patel S, Zhao X H, Terlier T, Natelson D, Crooker S, Lou J 2019 Nano Lett. 19 3777 Google Scholar
[133]	Kang L X, Ye C, Zhao X X, Zhou X Y, Hu J X, Li Q, Liu D, Das C M, Yang J F, Hu D Y, Chen J Q, Cao X, Zhang Y, Xu M Z, Di J, Tian D, Song P, Kutty G, Zeng Q S, Fu Q D, Deng Y, Zhou J D, Ariando A, Miao F, Hong G, Huang Y Z, Pennycook S J, Yong K T, Ji W, Wang X R S, Liu Z 2020 Nat. Commun. 11 3729 Google Scholar
[134]	Yang P F, Zou X L, Zhang Z P, Hong M, Shi J P, Chen S L, Shu J P, Zhao L Y, Jiang S L, Zhou X B, Huan Y H, Xie C Y, Gao P, Chen Q, Zhang Q, Liu Z F, Zhang Y F 2018 Nat. Commun. 9 979 Google Scholar
[135]	Cui F F, Zhao X X, Xu J J, Tang B, Shang Q Y, Shi J P, Huan Y H, Liao J H, Chen Q, Hou Y L, Zhang Q, Pennycook S J, Zhang Y F 2020 Adv. Mater. 32 1905896 Google Scholar
[136]	Dangol R, Dai Z F, Chaturvedi A, Zheng Y, Zhang Y, Dinh K N, Li B, Zong Y, Yan Q Y 2018 Nanoscale 10 4890 Google Scholar
[137]	Liu L, Yao T, Tan X G, Liu Q H, Wang Z Q, Shen D C, Sun Z H, Wei S Q, Xie Y 2012 Small 8 3752 Google Scholar
[138]	Feng J, Sun X, Wu C Z, Peng L L, Lin C W, Hu S L, Yang J L, Xie Y 2011 J. Am. Chem. Soc. 133 17832 Google Scholar
[139]	Yang H, Wang F, Zhang H S, Guo L H, Hu L Y, Wang L F, Xue D J, Xu X H 2020 J. Am. Chem. Soc. 142 4438 Google Scholar
[140]	Yang Z Y, Zhang H H, Xu J J, Ma R Z, Sasaki T, Zeng Y J, Ruan S C, Hou Y L 2020 Natl. Sci. Rev. 7 841 Google Scholar
[141]	De Siena M C, Creutz S E, Regan A, Malinowski P, Jiang Q N, Kluherz K T, Zhu G M, Lin Z, De Yoreo J J, Xu X D, Chu J H, Gamelin D R 2020 Nano Lett. 20 2100 Google Scholar
[142]	Liu S S, Yuan X, Zhou Y C, Sheng Y, Huang C, Zhang E Z, Ling J W, Liu Y W, Wang W Y, Zhang C, Zou J, Wang K Y, Xiu F X 2017 Npj 2D Mater. Appl. 1 1 Google Scholar
[143]	Liu Z L, Wu X, Shao Y, Qi J, Cao Y, Huang L, Liu C, Wang J O, Zheng Q, Zhu Z L, Ibrahim K, Wang Y L, Gao H J 2018 Sci. Bull. 63 419 Google Scholar
[144]	Liu Z L, Lei B, Zhu Z L, Tao L, Qi J, Bao D L, Wu X, Huang L, Zhang Y Y, Lin X, Wang Y L, Du S X, Pantelides S T, Gao H J 2019 Nano Lett. 19 4897 Google Scholar
[145]	Gong Y, Guo J W, Li J H, Zhu K J, Liao M H, Liu X Z, Zhang Q H, Gu L, Tang L, Feng X, Zhang D, Li W, Song C L, Wang L L, Yu P, Chen X, Wang Y Y, Yao H, Duan W H, Xu Y, Zhang S C, Ma X C, Xue Q K, He K 2019 Chin. Phys. Lett. 36 089901 Google Scholar
[146]	Wen Y, Liu Z H, Zhang Y, Xia C X, Zhai B X, Zhang X H, Zhai G H, Shen C, He P, Cheng R Q, Yin L, Yao Y Y, Sendeku M G, Wang Z X, Ye X B, Liu C S, Jiang C, Shan C X, Long Y W, He J 2020 Nano Lett. 20 3130 Google Scholar
[147]	Kimura A, Matsuno J, Okabayashi J, Fujimori A, Shishidou T, Kulatov E, Kanomata T 2001 Phys. Rev. B 63 224420 Google Scholar
[148]	Fei Z Y, Huang B, Malinowski P, Wang W B, Song T C, Sanchez J, Yao W, Xiao D, Zhu X Y, May A F, Wu W D, Cobden D H, Chu J H, Xu X D 2018 Nat. Mater. 17 778 Google Scholar
[149]	Pathak S, Sharma M 2014 J. Appl. Phys. 115 043906 Google Scholar
[150]	Zhang G P, Hubner W, Lefkidis G, Bai Y H, George T F 2009 Nat. Phys. 5 499 Google Scholar
[151]	Su J W, Wang M S, Liu G H, Li H Q, Han J B, Zhai T Y 2020 Adv. Sci. 7 2001722 Google Scholar
[152]	Liu B, Liu S S, Yang L, Chen Z D, Zhang E Z, Li Z H, Wu J, Ruan X Z, Xiu F X, Liu W Q, He L, Zhang R, Xu Y B 2020 Phys. Rev. Lett. 125 267205 Google Scholar
[153]	Cai L, Yu C L, Liu L Y, Xia W, Zhou H A, Zhao L, Dong Y Q, Xu T, Wang Z D, Guo Y F, Zhao Y G, Zhang J S, Yang L Y, Yang L X, Jiang W J 2020 Appl. Phys. Lett. 117 192401 Google Scholar
[154]	Gibson G A, Schultz S 1993 J. Appl. Phys. 73 4516 Google Scholar
[155]	Niu B, Su T, Francisco B A, Ghosh S, Kargar F, Huang X, Lohmann M, Li J X, Xu Y D, Taniguchi T, Watanabe K, Wu D, Balandin A, Shi J, Cui Y T 2020 Nano Lett. 20 553 Google Scholar
[156]	Bonilla M, Kolekar S, Ma Y J, Diaz H C, Kalappattil V, Das R, Eggers T, Gutierrez H R, Phan M H, Batzill M 2018 Nat. Nanotechnol. 13 289 Google Scholar
[157]	Zhou X H, Brzostowski B, Durajski A P, Liu M Z, Xiang J, Jiang T R, Wang Z Q, Chen S W, Li P G, Zhong Z H, Drzewinski A, Jarosik M W, Szczesniak R, Lai T S, Guo D H, Zhong D Y 2020 J. Phys. Chem. C 124 9416 Google Scholar
[158]	Tian Y, Gray M J, Ji H W, Cava R J, Burch K S 2016 2 D Mater. 3 025035 Google Scholar
[159]	Zhang X D, Xie Y 2013 Chem. Soc. Rev. 42 8187 Google Scholar
[160]	Heron J T, Trassin M, Ashraf K, Gajek M, He Q, Yang S Y, Nikonov D E, Chu Y H, Salahuddin S, Ramesh R 2011 Phys. Rev. Lett. 107 217202 Google Scholar
[161]	Cao T, Li Z L, Louie S G 2015 Phys. Rev. Lett. 114 236602 Google Scholar
[162]	Li X X, Yang J L 2014 J. Mater. Chem. C 2 7071 Google Scholar
[163]	Pan H 2014 Sci. Rep. 4 7524 Google Scholar
[164]	Li T X, Jiang S W, Sivadas N, Wang Z F, Xu Y, Weber D, Goldberger J E, Watanabe K, Taniguchi T, Fennie C J, Mak K F, Shan J 2019 Nat. Mater. 18 1303 Google Scholar
[165]	Song T C, Fei Z Y, Yankowitz M, Lin Z, Jiang Q N, Hwangbo K, Zhang Q, Sun B S, Taniguchi T, Watanabe K, McGuire M A, Graf D, Cao T, Chu J H, Cobden D H, Dean C R, Xiao D, Xu X D 2019 Nat. Mater. 18 1298 Google Scholar
[166]	Wang Y, Wang C, Liang S J, Ma Z C, Xu K, Liu X W, Zhang L L, Admasu A S, Cheong S W, Wang L Z, Chen M Y, Liu Z L, Cheng B, Ji W, Miao F 2020 Adv. Mater. 32 2004533 Google Scholar
[167]	Zhang W, Zhang L, Wong P K J, Yuan J R, Vinai G, Torelli P, van der Laan G, Feng Y P, Wee A T S 2019 ACS Nano 13 8997 Google Scholar
[168]	Zhang L M,Huang X Y, Dai H W, Wang M S, Cheng H, Tong L, Li Z, Han X T, Wang X, Ye L, Han J B 2020 Adv. Mater. 32 2002032 Google Scholar
[169]	Cao Y, Fatemi V, Demir A, Fang S, Tomarken S L, Luo J Y, Sanchez-Yamagishi J D, Watanabe K, Taniguchi T, Kaxiras E, Ashoori R C, Jarillo-Herrero P 2018 Nature 556 80 Google Scholar
[170]	Cao Y, Fatemi V, Fang S, Watanabe K, Taniguchi T, Kaxiras E, Jarillo-Herrero P 2018 Nature 556 43 Google Scholar
[171]	Jiang T, Liu H R, Huang D, Zhang S, Li Y G, Gong X G, Shen Y R, Liu W T, Wu S W 2014 Nat. Nanotechnol. 9 825 Google Scholar
[172]	Alegria L D, Ji H, Yao N, Clarke J J, Cava R J, Petta J R 2014 Appl. Phys. Lett. 105 053512 Google Scholar
[173]	Zhong D, Seyler K L, Linpeng X Y, Cheng R, Sivadas N, Huang B, Schmidgall E, Taniguchi T, Watanabe K, McGuire M A, Yao W, Xiao D, Fu K M C, Xu X D 2017 Sci. Adv. 3 e1603113 Google Scholar

Cited By

图 1 二维磁性材料的简单分类

Figure 1. Simple classification of two-dimensional magnetic materials.

DownLoad: Full-Size Img PowerPoint

图 2 (a) Al₂O₃辅助机械剥离Fe₃GeTe₂薄片的示意图^[32]; (b)在Al₂O₃薄膜上剥落Fe₃GeTe₂薄片的光学图片^[32]; (c) CVD法合成FeTe纳米片的过程示意图^[133]; (d)薄层FeTe纳米片的光学图片^[133]; (e)超声液相剥离二维NiPS₃的原理图^[136]; (f) NiPS₃薄片AFM图^[136]; (g)分子束外延生长VSe₂的原理图^[143]; (h)单层VSe₂的AFM图^[143]

Figure 2. (a) Schematic of Fe₃GeTe₂ exfoliated by Al₂O₃-assisted mechanical method^[32]; (b) optical image of typical few-layer Fe₃GeTe₂ flakes exfoliated on top of an Al₂O₃ thin film^[32]; (c) schematic illustration of FeTe nanosheet growth route by CVD^[133]; (d) optical image of few-layer FeTe flakes^[133]; (e) schematic illustration of NiPS₃ growth route by liquid exfoliation^[136]; (f) the AFM image of NiPS₃ flakes^[136]; (g) schematic illustration of VSe₂ growth route by molecular beam epitaxy^[143]; (h) the AFM image of monolayer VSe₂^[143].

DownLoad: Full-Size Img PowerPoint

图 3 (a)磁圆二色性原理图; (b)和(c)双层和三层CrI₃自旋滤波器磁隧道结隧穿电流和反射磁圆二色性(RMCD)随外磁场(μ₀H_⊥)变化的函数关系曲线, 偏置电压分别为–290 mV和235 mV, 绿色(橙色)曲线表示递减(递增)磁场^[59]; (d)不同温度下, 厚度为48 nm的Fe₃GeTe₂样品RMCD信号随磁场的变化关系^[148]; (e)磁光克尔效应原理图; (f)双层Cr₂Ge₂Te₆在不同温度下的克尔旋转信号^[30]; (g) CrI₃的磁光克尔转角与外加磁场的关系^[31]; (h)不同温度下, Ta₃FeS₆纳米片极向磁光克尔随磁场的变化^[151]; (i)在空气环境4个月前后, Ta₃FeS₆纳米片的MOKE信号随磁场变化^[151]

Figure 3. (a) Schematic diagram of magnetic circular dichroism; (b) and (c) tunneling current and reflective magnetic circular dichroism (RMCD) as a function of out-of-plane magnetic field (μ₀H_⊥) of double spin-filter magnetic tunnel junctions from bilayer and trilayer CrI₃ at a selected bias voltage –290 mV and 235 mV, respectively, green (orange) curve corresponds to decreasing (increasing) magnetic field^[59]; (d) comparison of RMCD sweeps for Fe₃GeTe₂ of thickness 48 nm as a function of the magnetic field, respectively^[148]; (e) schematic diagram of magneto-optic Kerr effect; (f) Kerr rotation signals of bilayer Cr₂Ge₂Te₆ vary with temperature^[30]; (g) the magneto-optic Kerr signals of different CrI₃ layers as a function of the magnetic field^[31]; (h) the polar MOKE signal of Ta₃FeS₆ nanosheet as a function of magnetic field at different temperatures^[151]; (i) MOKE signal of Ta₃FeS₆ nanosheet as a function of magnetic field acquired before and after 4 months aging under atmospheric conditions^[151].

DownLoad: Full-Size Img PowerPoint

图 4 (a)磁力显微镜工作原理图; (b)单层/双层/三层VSe₂薄片的MFM相位图像^[106]; (c)图(b)中白色虚线对应的MFM图像的地形高度和MFM相位剖面图^[106]; (d), (e) Fe₃GeTe₂分别在204和103 K时MFM图像, (d)的插图为300 K时的MFM图像, 图中白色矩形勾画出了相同的区域^[148]; (f) 200 nm厚的CrI₃薄片MFM信号作为磁场的函数图^[155]; (g) 25 nm厚的CrI₃薄片MFM信号作为磁场的函数图^[155]; (h)表层和内层的堆叠顺序和自旋方向机理图^[155]; (i)扫描隧道显微镜原理图^[155]; (j)在热解石墨烯衬底上形成的单层VSe₂扫描隧道显微镜图, 单层VSe₂优先在阶梯边缘成核^[156]; (k)在MoS₂衬底上形成的单层VSe₂扫描隧道显微镜图, VSe₂在MoS₂衬底上形成更均匀的单层膜^[156]; (l) H型双层CrBr₃层间的铁磁性耦合^[61]; (m), (n) R型双层CrBr₃层间的反铁磁性耦合^[61]; (o)八面体的FeCl₆单元(顶图)和六边形1T-FeCl₂结构的示意图(底图)^[157]; (p)具有两种非等边的六边形1T-FeCl₂的STM图像^[157]

Figure 4. (a) Schematic diagram of magnetic force microscope (MFM); (b) MFM phase image of monolayer/bilayer/trilayer VSe₂ flake^[106]; (c) topography height and MFM phase profiles of the MFM image corresponding to the white dashed line in panel (b)^[106]; (d), (e) MFM domain images for Fe₃GeTe₂ at 204 K and 103 K, respectively, inset of (d) is the MFM image at 300 K, and the white rectangles outline the same area^[148]; (f) MFM signal as a function of magnetic field for 200 nm CrI₃ flake; (g) MFM signal as a function of magnetic field for 25 nm CrI₃ flake^[155]; (h) illustration of the stacking orders and spin configurations insurface and inner layers^[155]; (i) schematic diagram of scanning tunneling microscope^[155]; (j) the STM image of VSe₂ monolayer on HOPG, VSe₂ monolayer islands preferentially nucleate at step edges on HOPG^[156]; (k) the STM image of VSe₂ monolayer on MoS₂, the growth of VSe₂ monolayer on MoS₂ is more uniform and gives rise to larger monolayer islands^[156]; (l) ferromagnetic coupling between H-type bilayer CrBr₃ layers^[61]; (m), (n) antiferromagnetic coupling between R-type bilayer CrBr₃ layers^[61]; (o) schematic illustration of an octahedral FeCl₆ unit (top) and a hexagonal island of FeCl₂ with a 1T structure (bottom)^[157]; (p) STM image of 1T-FeCl₂ with two non-equallateral hexagons^[157].

DownLoad: Full-Size Img PowerPoint

图 5 (a)少层FePS₃拉曼随温度依赖的mapping图^[89]; (b)不同厚度下, 少层FePS₃的P_1a拉曼峰强度随温度的变化^[89]; (c)薄层Cr₂Ge₂Te₆样品$ {\rm{E}}_{\rm{g}}^{1} $和$ {\rm{E}}_{\rm{g}}^{2} $拉曼峰随温度依赖的mapping图^[158]; (d)不同温度下薄层Cr₂Ge₂Te₆样品的原始拉曼图^[158]; (e)单层CrI₃偏振拉曼光谱随磁场的演化过程^[62]; (f)单层CrI₃的拉曼强度与磁圆二色的结果比较^[62]; (g)双层CrI₃偏振拉曼光谱随磁场的演化过程^[62]; (h)双层CrI₃的拉曼强度与磁圆二色的结果比较^[62]; (i)反常霍尔效应的三种机制; (j)四层Fe₃GeTe₂的剩余霍尔电阻随温度的变化^[32]; (k) 2 K温度下, 不同厚度的Fe₃GeTe₂纳米片的反常霍尔电阻R_xy随磁场的变化关系^[111]; (l)不同温度下, 单个Fe₃GeTe₂的反常霍尔电阻随磁场的变化曲线^[142]; (m)不同温度下, Fe₃GeTe₂/MnTe异质结的反常霍尔电阻随磁场的变化曲线^[142]

Figure 5. (a) Temperature dependent Raman mapping of few layers FePS₃ temperature dependent^[89]; (b) the Raman intensity as a function of temperature for different thickness FePS₃ of P_1a mode^[89]; (c) temperature dependent Raman spectra mapping for Cr₂Ge₂Te₆ of the $ {\rm{E}}_{\rm{g}}^{1} $ and $ {\rm{E}}_{\rm{g}}^{2} $ modes^[158]; (d) the original Raman diagram of few layer Cr₂Ge₂Te₆ at different temperatures^[158]; (e) the evolution process of polarization Raman spectra for monolayer CrI₃ with magnetic field^[62]; (f) comparison of Raman strength and MCD for monolayer CrI₃^[62]; (g) the evolution process of polarization Raman spectra of bilayer CrI₃ with magnetic field^[62]; (h) comparison of Raman strength and MCD for bilayer CrI₃^[62]; (i) the mechanism of anomalous Hall effect; (j) the remanent Hall resistance ${R}_{xy}^{\rm r}$ as a function of temperature for four-layer Fe₃GeTe₂^[32]; (k) the R_xy as a function of magnetic field for different thickness Fe₃GeTe₂ nanosheet at 2 K^[111]; (l) the R_xy as a function of magnetic field for Fe₃GeTe₂ heterojunction at different temperatures^[142]; (m) the R_xy as a function of magnetic field for Fe₃GeTe₂/MnTe heterojunction at different temperatures^[142]

DownLoad: Full-Size Img PowerPoint

图 6 (a)顶部: 双栅极双层CrI₃场效应器件的示意性侧视图, 其中双分子层CrI₃被封装在少层石墨烯中, 石墨烯作为平面外输运测量的源极和漏极; 底部: 单双层样品器件的光学显微图. 左下图, 用于单层CrI₃的磁化率测量的电极结构, 比例尺为50 μm; 右下图, 用于双层CrI₃的磁化率测量的电极结构, 比例尺为20 μm; 红色虚线为双层样品的边界^[51]. (b)单层CrI₃的磁性随栅极电压(底轴)和诱导掺杂密度(顶轴)变化的函数^[51]. (c)双层CrI₃中, 在4 K下掺杂密度-磁场相图^[51]. (d)少数层h-BN/Cr₂Ge₂Te₆/h-BN范德瓦耳斯异质结器件^[94]. (e) 40 K, 负门电压下磁光克尔角随磁场的变化^[94]. (f) 40 K, 正门电压下磁光克尔角随磁场的变化^[94]

Figure 6. (a) Top: A schematic side view of a dual-gate bilayer CrI₃ field-effect device. Bilayer CrI₃ is encapsulated in few-layer graphene, which also serves as source and drain electrodes for out-of plane transport measurements. Bottom: An optical micrograph for monolayer and bilayer CrI₃ sample devices. Scale bars, 50 μm (left panel) and 20 μm (right panel). The metallic ring structure (left panel) is used to create a magnetic field for the susceptibility measurement for monolayer CrI₃. The electrode structure (right panel) is used for the susceptibility measurement for bilayer CrI₃, the red dashed line marks the boundary of a bilayer sample in the right panel^[51]. (b) The magnetic properties of monolayer CrI₃ as a function of gate voltage (bottom axis) and induced doping density (top axis)^[51]. (c) Doping density-magnetic field phase diagram at 4 K for monolayer CrI₃^[51]. (d) Schematic diagram of a few-layered h-BN/Cr₂Ge₂Te₆/h-BN heterojunction^[94]. (e) Kerr angle as a function of magnetic field at 40 K for negative gate voltages^[94]. (f) Kerr angle as a function of magnetic field at 40 K for positive gate voltages^[94].

DownLoad: Full-Size Img PowerPoint

图 7 (a) Fe₃GeTe₂的磁结构随厚度和温度的变化^[32]; (b)在三层Fe₃GeTe₂样品中获得的电导与门电压的关系, 测试温度为330 K, 插图为Fe₃GeTe₂离子场晶体管^[32]示意图, 其中S, D分别代表源电极和漏电极, V_n表示探测电压, 固态栅极覆盖了样品和周围电极^[32]; (c)三层Fe₃GeTe₂在特定栅压下(T = 10 K和T = 240 K)的反常霍尔电阻随磁场的变化曲线^[32]; (d)三层Fe₃GeTe₂温度和栅压的相图^[32]; (e)在栅极电压V_g = 2.1 V时, 四层Fe₃GeTe₂在室温附近的反常霍尔电阻随磁场的变化^[32]

Figure 7. (a) Phase diagram of Fe₃GeTe₂ (FGT) as a function of layer number and temperature^[32]. (b) conductance as a function of gate voltage V_g measured in a trilayer FGT device. Data are obtained at T = 330 K, the inset shows a schematic of the FGT device structure and measurement setup, S and D label the source and drain electrodes, respectively, and V_n labels the voltage probes. The solid electrolyte covers both the FGT flake and the side gate^[32]. (c) R_xy as a function of external magnetic field recorded at representative gate voltages obtained at T = 10 K and T = 240 K^[32]; (d) the phase diagram of the trilayer FGT sample as a function of the gate voltage and temperature^[32]; (e) R_xy of four-layer FGT as a function of magnetic field under a gate voltage of V_g = 2.1 V at room temperature^[32].

DownLoad: Full-Size Img PowerPoint

图 8 (a) CrI₃晶体结构, 分别为单斜相(左)和六方相(右)^[164]; (b) CrI₃隧道结的光学图片^[164]; (c) CrI₃隧道结的侧面示意图^[164]; (d), (e) 在施加压力前(d)后(e)两个2层(2L)和两个5层(5L)区域, 在3.5 K时, MCD随磁场的变化^[164]; (f)双层CrI₃隧道结中, 不同压力下, 隧道电流随磁场的变化^[165]; (g)双层CrI₃隧道结施加压力前后RMCD信号随磁场的变化^[165]; (h)高压实验装置示意图^[165]; (i), (j), (k)三层CrI₃中其中任意三点的RMCD随磁场的变化^[165]

Figure 8. (a) Crystal structure of CrI₃, the monoclinic phase (left) and the hexagonal phase (right)^[164]; (b) the optical image of CrI₃ tunnel junction^[164]; (c) the side view of the CrI₃ tunnel junction^[164]; (d), (e) the MCD for 2L and 5L CrI₃ before (d) and after (e) pressured as a function of the magnetic field under the temperature of 3.5 K^[164]; (f) the tunnel current for bilayer CrI₃ as a function of the magnetic field under different pressures^[165]; (g) the RMCD signal for bilayer CrI₃ tunnel junction as a function of the magnetic field before and after pressured^[165]; (h) schematic of high-pressure experimental set-up^[165]; (i), (j), (k) the RMCD signal for any three points of trilayer CrI₃ as a function of the magnetic field^[165].

DownLoad: Full-Size Img PowerPoint

图 9 (a) Fe₃GeTe₂及FePS₃/Fe₃GeTe₂异质结的克尔旋转角随磁场的变化曲线^[168]; (b) Fe₃GeTe₂及FePS₃/Fe₃GeTe₂/FePS₃异质结的克尔旋转角随磁场的变化曲线^[168]; (c)双层反铁磁/铁磁异质结FePS₃/Fe₃GeTe₂和(d)三层反铁磁/铁磁/反铁磁异质结FePS₃/Fe₃GeTe₂/FePS₃表现出的交换偏置现象^[168]; (e) Fe₃GeTe₂及FePS₃/Fe₃GeTe₂异质结的克尔旋转角随温度的变化曲线^[168]; (f) Fe₃GeTe₂及FePS₃/Fe₃GeTe₂/FePS₃异质结的克尔旋转角随温度的变化曲线^[168]

Figure 9. (a) The Kerr rotations as a function of magnetic field for Fe₃GeTe₂ (FGT, yellow curves) and FePS₃/Fe₃GeTe₂ (FPS/FGT, green curves)^[168]; (b) the Kerr rotations as a function of magnetic field for FGT (yellow curves) and FePS₃/Fe₃GeTe₂/FePS₃ (FPS/FGT/FPS, green curves)^[168]; the exchange bias phenomenon for (c) bilayer antiferromagnetic/ferromagnetic heterojunction FPS/FGT and (d) trilayer antiferromagnetic/ferromagnetic/antiferromagnetic heterojunction FPS/FGT/FPS under the different external magnetic fields^[168]; (e) the Kerr rotations as a function of the temperature for FGT (red curve) and FPS/FGT (blue curve)^[168]; (f) the Kerr rotation as a function of the temperature for FGT (red curve) and FPS/FGT/FPS (blue curve)^[168].

DownLoad: Full-Size Img PowerPoint

map

[1]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Zhang Y, Dubonos S V, Grigorieva I V, Firsov A A 2004 Science 306 666 Google Scholar
[2]	Koppens F H L, Mueller T, Avouris P, Ferrari A C, Vitiello M S, Polini M 2014 Nat. Nanotechnol. 9 780 Google Scholar
[3]	Sangwan V K, Hersam M C 2018 Annu. Rev. Phys. Chem. 69 299 Google Scholar
[4]	Wang Q H, Kalantar-Zadeh K, Kis A, Coleman J N, Strano M S 2012 Nat. Nanotechnol. 7 699 Google Scholar
[5]	Wang W, Wu X, Zhang J 2015 J. Nanomater. 2015 198126 Google Scholar
[6]	Zhang X Y, Hou L L, Ciesielski A, Samori P 2016 Adv. Energy Mater. 6 1600671 Google Scholar
[7]	Fu J B, Xu W Q, Chen X, Zhang S F, Zhang W J, Suo P, Lin X, Wang J, Jin Z M, Liu W M, Ma G H 2020 J. Phys. Chem. C 124 10719 Google Scholar
[8]	Liu B W, Zhang Z, Liao K, Wu R, Zhu C, Xie H G, Zha C Y, Yin Y, Jiang X H, Qin S C, Wang W, Ouyang G, Qin T S, Wang L, Huang W 2020 Appl. Surf. Sci. 523 146371 Google Scholar
[9]	Zong X R, Hu H M, Ouyang G, Wang J W, Shi R, Zhang L, Zeng Q S, Zhu C, Chen S H, Cheng C, Wang B, Zhang H, Liu Z, Huang W, Wang T H, Wang L, Chen X L 2020 Light-Sci. Appl. 9 114 Google Scholar
[10]	Chen X L, Zhou Z S, Deng B C, Wu Z F, Xia F N, Cao Y, Zhang L, Huang W, Wang N, Wang L 2019 Nano Today 27 99 Google Scholar
[11]	Gatensby R, McEvoy N, Lee K, Hallam T, Berner N C, Rezvani E, Winters S, O'Brien M, Duesberg G S 2014 Appl. Surf. Sci. 297 139 Google Scholar
[12]	Ou Z W, Wang T, Tang J B, Zong X R, Wang W, Guo Q B, Xu Y H, Zhu C, Wang L, Huang W, Xu H X 2020 Adv. Opt. Mater. 8 2000201 Google Scholar
[13]	Voevodin A A, Waite A R, Bultman J E, Hu J J, Muratore C 2015 Surf. Coat. Technol. 280 260 Google Scholar
[14]	Reinwald M, Wurstbauer U, Doppe M, Kipferl W, Wagenhuber K, Tranitz H P, Weiss D, Wegscheider W 2005 J. Cryst. Growth 278 690 Google Scholar
[15]	Nazmul A M, Banshchikov A G, Shimizu H, Tanaka M 2001 J. Cryst. Growth 227 874 Google Scholar
[16]	Kobune M, Furotani R, Fujita S, Kikuchi K, Kikuchi T, Fujisawa H, Shimizu M, Fukumuro N 2016 Jpn. J. Appl. Phys. 55 10ta01 Google Scholar
[17]	Paek W B, Kim J, Lim S H 2004 Phys. Status Solidi B 241 1521 Google Scholar
[18]	Redjdal N, Salah H, Hauet T, Menari H, Cherif S M, Gabouze N, Azzaz M 2014 Thin Solid Films 552 164 Google Scholar
[19]	Bhuvaneswari P V, Ramamurthi K, Babu R R, Babu S M 2015 Appl. Phys. A 120 1113 Google Scholar
[20]	Mohamed R B, Nasina M R, Shaik K, Narayananellore S K, Kuppan M 2014 J. Supercond. Novel. Magn. 27 2147 Google Scholar
[21]	Awana G, Cox C, Venkat G, Morrison K, Zhou Z X, Backes D 2020 Mater. Res. Express 7 106406 Google Scholar
[22]	Farrell I L, Hyndman A R, Reeves R J, Williams G V M, Granville S 2017 Thin Solid Films 625 24 Google Scholar
[23]	Miao Y P, Huang Y H, Fang Q L, Yang Z, Xu K W, Ma F, Chu P K 2016 J. Mater. Sci. 51 9514 Google Scholar
[24]	Kaloni T P 2014 J. Phys. Chem. C 118 25200 Google Scholar
[25]	Mao Y L, Guo G, Yuan J M, Zhong J X 2019 Appl. Surf. Sci. 464 236 Google Scholar
[26]	Ersan F, Arkin H, Akturk E 2017 RSC Adv. 7 37815 Google Scholar
[27]	Roldan R, Goerbig M O, Fuchs J N 2010 Semicond. Sci. Technol. 25 034005 Google Scholar
[28]	Romero-Muniz C, Pou P, Perez R 2020 Carbon 159 102 Google Scholar
[29]	Mermin N D, Wagner H 1966 Phys. Rev. Lett. 17 1133 Google Scholar
[30]	Gong C, Li L, Li Z L, Ji H W, Stern A, Xia Y, Cao T, Bao W, Wang C Z, Wang Y A, Qiu Z Q, Cava R J, Louie S G, Xia J, Zhang X 2017 Nature 546 265 Google Scholar
[31]	Huang B, Clark G, Navarro-Moratalla E, Klein D R, Cheng R, Seyler K L, Zhong D, Schmidgall E, McGuire M A, Cobden D H, Yao W, Xiao D, Jarillo-Herrero P, Xu X D 2017 Nature 546 270 Google Scholar
[32]	Deng Y J, Yu Y J, Song Y C, Zhang J Z, Wang N Z, Sun Z Y, Yi Y F, Wu Y Z, Wu S W, Zhu J Y, Wang J, Chen X H, Zhang Y B 2018 Nature 563 94 Google Scholar
[33]	Meena S, Anudeep K 2020 J. Supercond. Novel. Magn. 33 1447 Google Scholar
[34]	Sheng H H, Zhu Y J, Bai D M, Wu X S, Wang J L 2020 Nanotechnology 31 315713 Google Scholar
[35]	Yang J J, Wang J, Liu Q, Xu R, Sun Y L, Li Z P, Gao F M, Xia M R 2020 J. Magn. Magn. Mater. 502 851 Google Scholar
[36]	Serri M, Cucinotta G, Poggini L, Serrano G, Sainctavit P, Strychalska-Nowak J, Politano A, Bonaccorso F, Caneschi A, Cava R J, Sessoli R, Ottaviano L, Klimczuk T, Pellegrini V, Mannini M 2020 Adv. Mater. 32 2000566 Google Scholar
[37]	Yang J T, Zhou Y, Guo Q L, Dedkov Y, Voloshina E 2020 RSC Adv. 10 851 Google Scholar
[38]	Kargar F, Coleman E A, Ghosh S, Lee J, Gomez M J, Liu Y H, Magana A S, Barani Z, Mohammadzadeh A, Debnath B, Wilson R B, Lake R K, Balandin A A 2020 ACS Nano 14 2424 Google Scholar
[39]	Wildes A R, Lancon D, Chan M K, Weickert F, Harrison N, Simonet V, Zhitomirsky M E, Gvozdikova M V, Ziman T, Ronnow H M 2020 Phys. Rev. B 101 024415 Google Scholar
[40]	Sun Y, Luo X 2019 Phys. Status Solidi B 256 1900052 Google Scholar
[41]	Ito N, Kikkawa T, Barker J, Hirobe D, Shiomi Y, Saitoh E 2019 Phys. Rev. B 100 060402 Google Scholar
[42]	Kang S, Kang S, Yu J 2019 J. Electron. Mater. 48 1441 Google Scholar
[43]	Xu C S, Feng J S, Xiang H J, Bellaiche L 2018 Npj Comput. Mater. 4 57 Google Scholar
[44]	Liu H T, Bao L H, Zhou Z, Che B Y, Zhang R Z, Bian C, Ma R S, Wu L M, Yang H F, Li J J, Gu C Z, Shen C M, Du S X, Gao H J 2019 Nano Lett. 19 4551 Google Scholar
[45]	Zheng G L, Xie W Q, Albarakati S, Algarni M, Tan C, Wang Y H, Peng J Y, Partridge J, Farrar L, Yi J B, Xiong Y M, Tian M L, Zhao Y J, Wang L 2020 Phys. Rev. Lett. 125 047202 Google Scholar
[46]	Zhu R, Zhang W, Shen W, Wong P K J, Wang Q X, Liang Q J, Tian Z, Zhai Y, Qiu C W, Wee A T S 2020 Nano Lett. 20 5030 Google Scholar
[47]	Deng Y J, Yu Y J, Shi M Z, Guo Z X, Xu Z H, Wang J, Chen X H, Zhang Y B 2020 Science 367 895 Google Scholar
[48]	Miao N H, Xu B, Zhu L G, Zhou J, Sun Z M 2018 J. Am. Chem. Soc. 140 2417 Google Scholar
[49]	Cortie D L, Causer G L, Rule K C, Fritzsche H, Kreuzpaintner W, Klose F 2020 Adv. Funct. Mater. 30 1901414 Google Scholar
[50]	Li H, Ruan S C, Zeng Y J 2019 Adv. Mater. 31 1900065 Google Scholar
[51]	Jiang S W, Li L Z, Wang Z F, Mak K F, Shan J 2018 Nat. Nanotechnol. 13 549 Google Scholar
[52]	Li X X, Wu X J, Yang J L 2014 J. Am. Chem. Soc. 136 11065 Google Scholar
[53]	Lv P, Li Y L, Wang J F 2020 Phys. Chem. Chem. Phys. 22 11266 Google Scholar
[54]	Wang X Z, Du K Z, Liu Y Y F, Hu P, Zhang J, Zhang Q, Owen M H S, Lu X, Gan C K, Sengupta P, Kloc C, Xiong Q H 2016 2 D Mater. 3 031009 Google Scholar
[55]	Xie Q Y, Wu M, Chen L M, Bai G, Zou W Q, Wang W, He L 2019 Chin. Phys. B 28 056102 Google Scholar
[56]	McGuire M A, Dixit H, Cooper V R, Sales B C 2015 Chem. Mater. 27 4165 Google Scholar
[57]	McGuire M A, Clark G, Santosh K C, Chance W M, Jellison G E, Cooper V R, Xu X D, Sales B C 2017 Phys. Rev. Mater. 1 014001 Google Scholar
[58]	Abramchuk M, Jaszewski S, Metz K R, Osterhoudt G B, Wang Y P, Burch K S, Tafti F 2018 Adv. Mater. 30 085401 Google Scholar
[59]	Song T C, Cai X H, Tu M W Y, Zhang X O, Huang B V, Wilson N P, Seyler K L, Zhu L, Taniguchi T, Watanabe K, McGuire M A, Cobden D H, Xiao D, Yao W, Xu X D 2018 Science 360 1214 Google Scholar
[60]	Jiang P H, Wang C, Chen D C, Zhong Z C, Yuan Z, Lu Z Y, Ji W 2019 Phys. Rev. B 99 144401 Google Scholar
[61]	Chen W O, Sun Z Y, Wang Z J, Gu L H, Xu X D, Wu S W, Gao C L 2019 Science 366 983 Google Scholar
[62]	Zhang Y J, Wu X H, Lyu B B, Wu M H, Zhao S X, Chen J Y, Jia M Y, Zhang C S, Wang L, Wang X W, Chen Y Z, Mei J W, Taniguchi T, Watanabe K, Yan H G, Liu Q H, Huang L, Zhao Y, Huang M Y 2020 Nano Lett. 20 729 Google Scholar
[63]	Seyler K L, Zhong D, Huang B, Linpeng X Y, Wilson N P, Taniguchi T, Watanabe K, Yao W, Xiao D, McGuire M A, Fu K M C, Xu X D 2018 Nano Lett. 18 3823 Google Scholar
[64]	Zhang J Y, Zhao B, Zhou T, Xue Y, Ma C L, Yang Z Q 2018 Phys. Rev. B 97 085401 Google Scholar
[65]	Plumb K W, Clancy J P, Sandilands L J, Shankar V V, Hu Y F, Burch K S, Kee H Y, Kim Y J 2014 Phys. Rev. B 90 041112 Google Scholar
[66]	Kim H S, Shankar V V, Catuneanu A, Kee H Y 2015 Phys. Rev. B 91 241110 Google Scholar
[67]	Zhou Y G, Lu H F, Zu X T, Gao F 2016 Sci. Rep. 6 19407 Google Scholar
[68]	He J J, Ma S Y, Lyu P B, Nachtigall P 2016 J. Mater. Chem. C 4 2518 Google Scholar
[69]	Kong T, Stolze K, Timmons E I, Tao J, Ni D R, Guo S, Yang Z, Prozorov R, Cava R J 2019 Adv. Mater. 31 1808074 Google Scholar
[70]	Son S, Coak M J, Lee N, Kim J, Kim T Y, Hamidov H, Cho H, Liu C, Jarvis D M, Brown P A C, Kim J H, Park C H, Khomskii D I, Saxena S S, Park J G 2019 Phys. Rev. B 99 041402 Google Scholar
[71]	Tian S J, Zhang J F, Li C H, Ying T P, Li S Y, Zhang X, Liu K, Lei H C 2019 J. Am. Chem. Soc. 141 5326 Google Scholar
[72]	Kong T, Guo S, Ni D R, Cava R J 2019 Phys. Rev. Mater. 3 084419 Google Scholar
[73]	Prayitno T B, Ishii F 2019 J. Phys. Soc. Jpn. 88 104705 Google Scholar
[74]	Yan Z P, Li N N, Wang L Y, Yu Z H, Li M T, Zhang J B, Li X D, Yang K, Gao G Y, Wang L 2020 J. Phys. Chem. C 124 23317 Google Scholar
[75]	Feng Y L, Wu X M, Hu L, Gao G Y 2020 J. Mater. Chem. C 8 14353 Google Scholar
[76]	Zhu Y Y, Li H L, Chen T, Liu D S, Zhou Q H 2020 Vacuum 182 109694 Google Scholar
[77]	Teng S K, Mao X J, Liu Z, Liu Y, Xu X T, Li L Y, Xie X J, Fan S S, Zhou G X, Li J, Li J 2020 New J. Phys. 22 103061 Google Scholar
[78]	Han H C, Zheng H L, Wang Q S, Yan Y 2020 Phys. Chem. Chem. Phys. 22 26917 Google Scholar
[79]	Liu H N, Wang X S, Wu J X, Chen Y S, Wan J, Wen R, Yang J B, Liu Y, Song Z G, Xie L M 2020 ACS Nano 14 10544 Google Scholar
[80]	Bernasconi M, Marra G L, Benedek G, Miglio L, Balkanski M, Scagliotti M, Julien C, Jouanne M 1988 Phys. Rev. B 38 12089 Google Scholar
[81]	Susner M A, Chyasnavichyus M, McGuire M A, Ganesh P, Maksymovych P 2017 Adv. Mater. 29 1602852 Google Scholar
[82]	Lancon D, Ewings R A, Guidi T, Formisano F, Wildes A R 2018 Phys. Rev. B 98 134414 Google Scholar
[83]	Joy P A, Vasudevan S 1992 Phys. Rev. B 46 5425 Google Scholar
[84]	Wildes A R, Simonet V, Ressouche E, Ballou R, McIntyre G J 2017 J. Phys.-Condens. Mater. 29 056102 Google Scholar
[85]	Gusmeao R, Sofer Z, Pumera M 2019 Adv. Funct. Mater. 29 1805975 Google Scholar
[86]	Vaclavkova D, Delhomme A, Faugeras C, Potemski M, Bogucki A, Suffczynski J, Kossacki P, Wildes A R, Gremaud B, Saul A 2020 2D Mater. 7 035030 Google Scholar
[87]	Kuo C T, Neumann M, Balamurugan K, Park H J, Kang S, Shiu H W, Kang J H, Hong B H, Han M, Noh T W, Park J G 2016 Sci. Rep. 6 20904 Google Scholar
[88]	Du K Z, Wang X Z, Liu Y, Hu P, Utama M I B, Gan C K, Xiong Q H, Kloc C 2016 ACS Nano 10 1738 Google Scholar
[89]	Lee J U, Lee S, Ryoo J H, Kang S, Kim T Y, Kim P, Park C H, Park J G, Cheong H 2016 Nano Lett. 16 7433 Google Scholar
[90]	Xing W Y, Qiu L Y, Wang X R, Yao Y Y, Ma Y, Cai R R, Jia S, Xie X C, Han W 2019 Phys. Rev. X 9 011026 Google Scholar
[91]	Xie Q Y, Liu Y, Wu M, Lu H Y, Wang W, He L, Wu X S 2019 Mater. Lett. 246 60 Google Scholar
[92]	Carteaux V, Moussa F, Spiesser M 1995 Europhys. Lett. 29 251 Google Scholar
[93]	Zhuang H L L, Xie Y, Kent P R C, Ganesh P 2015 Phys. Rev. B 92 035407 Google Scholar
[94]	Wang Z, Zhang T Y, Ding M, Dong B J, Li Y X, Chen M L, Li X X, Huang J Q, Wang H W, Zhao X T, Li Y, Li D, Jia C K, Sun L D, Guo H H, Ye Y, Sun D M, Chen Y S, Yang T, Zhang J, Ono S P, Han Z, Zhang Z D 2018 Nat. Nanotechnol. 13 554 Google Scholar
[95]	Li Y F, Wang W, Guo W, Gu C Y, Sun H Y, He L, Zhou J, Gu Z B, Nie Y F, Pan X Q 2018 Phys. Rev. B 98 125127 Google Scholar
[96]	Zhang J X, Cai X C, Xia W, Liang A J, Huang J W, Wang C W, Yang L X, Yuan H T, Chen Y L, Zhang S L, Guo Y F, Liu Z K, Liu G 2019 Phys. Rev. Lett. 123 047203 Google Scholar
[97]	Lohmann M, Su T, Niu B, Hou Y S, Alghamdi M, Aldosary M, Xing W Y, Zhong J N, Jia S, Han W, Wu R Q, Cui Y T, Shi J 2019 Nano Lett. 19 2397 Google Scholar
[98]	Ostwal V, Shen T T, Appenzeller J 2020 Adv. Mater. 32 1906021 Google Scholar
[99]	Lin M W, Zhuang H L L, Yan J Q, Ward T Z, Puretzky A A, Rouleau C M, Gai Z, Liang L B, Meunier V, Sumpter B G, Ganesh P, Kent P R C, Geohegan D B, Mandrus D G, Xiao K 2016 J. Mater. Chem. C 4 315 Google Scholar
[100]	Gonzalez-Herrero H, Gomez-Rodriguez J M, Mallet P, Moaied M, Palacios J J, Salgado C, Ugeda M M, Veuillen J Y, Yndurain F, Brihuega I 2016 Science 352 437 Google Scholar
[101]	Nair R R, Sepioni M, Tsai I L, Lehtinen O, Keinonen J, Krasheninnikov A V, Thomson T, Geim A K, Grigorieva I V 2012 Nat. Phys. 8 199 Google Scholar
[102]	Avsar A, Tan J Y, Taychatanapat T, Balakrishnan J, Koon G K W, Yeo Y, Lahiri J, Carvalho A, Rodin A S, O'Farrell E C T, Eda G, Neto A H C, Ozyilmaz B 2014 Nat. Commun. 5 4875 Google Scholar
[103]	Gao D Q, Xue Q X, Mao X Z, Wang W X, Xu Q, Xue D S 2013 J. Mater. Chem. C 1 5909 Google Scholar
[104]	Ma Y D, Dai Y, Guo M, Niu C W, Zhu Y T, Huang B B 2012 ACS Nano 6 1695 Google Scholar
[105]	Arnold F, Stan R M, Mahatha S K, Lund H E, Curcio D, Dendzik M, Bana H, Travaglia E, Bignardi L, Lacovig P, Lizzit D, Li Z S, Bianchi M, Miwa J A, Bremholm M, Lizzit S, Hofmann P, Sanders C E 2018 2D Mater. 5 045009 Google Scholar
[106]	Yu W, Li J, Herng T S, Wang Z S, Zhao X X, Chi X, Fu W, Abdelwahab I, Zhou J, Dan J D, Chen Z X, Chen Z, Li Z J, Lu J, Pennycook S J, Feng Y P, Ding J, Loh K P 2019 Adv. Mater. 31 1903779 Google Scholar
[107]	Chua R, Yang J, He X Y, Yu X J, Yu W, Bussolotti F, Wong P K J, Loh K P, Breese M B H, Goh K E J, Huang Y L, Wee A T S 2020 Adv. Mater. 32 2000693 Google Scholar
[108]	Liu H T, Xue Y Z, Sho J A, Guzman R A, Zhan P P, Zhou Z, He Y G, Bian C, Wu L M, Ma R S, Chen J C, Yan J H, Yang H T, Shen C M, Zhou W, Bao L H, Gao H J 2019 Nano Lett. 19 8572 Google Scholar
[109]	May A F, Calder S, Cantoni C, Cao H B, McGuire M A 2016 Phys. Rev. B 93 014411 Google Scholar
[110]	Zhuang H L L, Kent P R C, Hennig R G 2016 Phys. Rev. B 93 134407 Google Scholar
[111]	Tan C, Lee J, Jung S G, Park T, Albarakati S, Partridge J, Field M R, McCulloch D G, Wang L, Lee C 2018 Nat. Commun. 9 1554 Google Scholar
[112]	Seo J, Kim D Y, An E S, Kim K, Kim G Y, Hwang S Y, Kim D W, Jang B G, Kim H, Eom G, Seo S Y, Stania R, Muntwiler M, Lee J, Watanabe K, Taniguchi T, Jo Y J, Lee J, Min B I, Jo M H, Yeom H W, Choi S Y, Shim J H, Kim J S 2020 Sci. Adv. 6 eaay8912 Google Scholar
[113]	Duong D L, Yun S J, Lee Y H 2017 ACS Nano 11 11803 Google Scholar
[114]	May A F, Ovchinnikov D, Zheng Q, Hermann R, Calder S, Huang B, Fei Z Y, Liu Y H, Xu X D, McGuire M A 2019 ACS Nano 13 4436 Google Scholar
[115]	Li Z X, Xia W, Su H, Yu Z H, Fu Y P, Chen L M, Wang X, Yu N, Zou Z Q, Guo Y F 2020 Sci. Rep. 10 15345 Google Scholar
[116]	Li J H, Li Y, Du S Q, Wang Z, Gu B L, Zhang S C, He K, Duan W H, Xu Y 2019 Sci. Adv. 5 eaaw5685 Google Scholar
[117]	Zhang D Q, Shi M J, Zhu T S, Xing D Y, Zhang H J, Wang J 2019 Phys. Rev. Lett. 122 206401 Google Scholar
[118]	Ge J, Liu Y Z, Li J H, Li H, Luo T C, Wu Y, Xu Y, Wang J 2020 Natl. Sci. Rev. 7 1280 Google Scholar
[119]	Hu C W, Gordon K N, Liu P F, Liu J Y, Zhou X Q, Hao P P, Narayan D, Emmanouilidou E, Sun H Y, Liu Y T, Brawer H, Ramirez A P, Ding L, Cao H B, Liu Q H, Dessau D, Ni N 2020 Nat. Commun. 11 97 Google Scholar
[120]	Aliev Z S, Amiraslanov I R, Nasonova D I, Shevelkov A V, Abdullayev N A, Jahangirli Z A, Orujlu E N, Otrokov M M, Mamedov N T, Babanly M B, Chulkov E V 2019 J. Alloys Compd. 789 443 Google Scholar
[121]	Hu C W, Ding L, Gordon K N, Ghosh B, Tien H J, Li H X, Linn A G, Lien S W, Huang C Y, Mackey S, Liu J Y, Reddy P V S, Singh B, Agarwal A, Bansil A, Song M, Li D S, Xu S Y, Lin H, Cao H B, Chang T R, Dessau D, Ni N 2020 Sci. Adv. 6 eaba4275 Google Scholar
[122]	Jiang Z, Wang P, Xing J P, Jiang X, Zhao J J 2018 ACS Appl. Mater. Interfaces 10 39032 Google Scholar
[123]	Zhang T L, Wang Y M, Li H X, Zhong F, Shi J, Wu M H, Sun Z Y, Shen W F, Wei B, Hu W D, Liu X F, Huang L, Hu C G, Wang Z C, Jiang C B, Yang S X, Zhang Q M, Qu Z 2019 ACS Nano 13 11353 Google Scholar
[124]	Yan S N, Wang P F, Wang C Y, Xu T, Li Z, Cao T J, Chen M Y, Pan C, Cheng B, Sun L T, Liang S J, Miao F 2019 Sci. China Inform. Sci. 62 220407 Google Scholar
[125]	Qing X M, Li H, Zhong C G, Zhou P X, Dong Z C, Liu J M 2020 Phys. Chem. Chem. Phys. 22 17255 Google Scholar
[126]	Ferrenti A M, Klemenz S, Lei S M, Song X Y, Ganter P, Lotsch B V, Schoop L M 2020 Inorg. Chem. 59 1176 Google Scholar
[127]	Li W, Yang Z Y, Hou Y L, Gao S 2020 Prog. Chem. 32 1437 Google Scholar
[128]	Lu H Y, Wang W, Liu Y, Chen L M, Xie Q Y, Yin H D, Cheng G F, He L 2020 Appl. Surf. Sci. 504 144405 Google Scholar
[129]	Yu J X, Li J, Zhang W F, Chang H X 2015 Chem. Sci. 6 6705 Google Scholar
[130]	Li J, Zhao B, Chen P, Wu R, Li B, Xia Q, Guo G, Luo J, Zang K, Zhang Z, Ma H, Sun G, Duan X, Duan X F 2018 Adv. Mater. 30 e1801043 Google Scholar
[131]	Zhang Y, Chu J W, Yin L, Shifa T A, Cheng Z Z, Cheng R Q, Wang F, Wen Y, Zhan X Y, Wang Z X, He J 2019 Adv. Mater. 31 1900056 Google Scholar
[132]	Yuan J T, Balk A, Guo H, Fang Q Y, Patel S, Zhao X H, Terlier T, Natelson D, Crooker S, Lou J 2019 Nano Lett. 19 3777 Google Scholar
[133]	Kang L X, Ye C, Zhao X X, Zhou X Y, Hu J X, Li Q, Liu D, Das C M, Yang J F, Hu D Y, Chen J Q, Cao X, Zhang Y, Xu M Z, Di J, Tian D, Song P, Kutty G, Zeng Q S, Fu Q D, Deng Y, Zhou J D, Ariando A, Miao F, Hong G, Huang Y Z, Pennycook S J, Yong K T, Ji W, Wang X R S, Liu Z 2020 Nat. Commun. 11 3729 Google Scholar
[134]	Yang P F, Zou X L, Zhang Z P, Hong M, Shi J P, Chen S L, Shu J P, Zhao L Y, Jiang S L, Zhou X B, Huan Y H, Xie C Y, Gao P, Chen Q, Zhang Q, Liu Z F, Zhang Y F 2018 Nat. Commun. 9 979 Google Scholar
[135]	Cui F F, Zhao X X, Xu J J, Tang B, Shang Q Y, Shi J P, Huan Y H, Liao J H, Chen Q, Hou Y L, Zhang Q, Pennycook S J, Zhang Y F 2020 Adv. Mater. 32 1905896 Google Scholar
[136]	Dangol R, Dai Z F, Chaturvedi A, Zheng Y, Zhang Y, Dinh K N, Li B, Zong Y, Yan Q Y 2018 Nanoscale 10 4890 Google Scholar
[137]	Liu L, Yao T, Tan X G, Liu Q H, Wang Z Q, Shen D C, Sun Z H, Wei S Q, Xie Y 2012 Small 8 3752 Google Scholar
[138]	Feng J, Sun X, Wu C Z, Peng L L, Lin C W, Hu S L, Yang J L, Xie Y 2011 J. Am. Chem. Soc. 133 17832 Google Scholar
[139]	Yang H, Wang F, Zhang H S, Guo L H, Hu L Y, Wang L F, Xue D J, Xu X H 2020 J. Am. Chem. Soc. 142 4438 Google Scholar
[140]	Yang Z Y, Zhang H H, Xu J J, Ma R Z, Sasaki T, Zeng Y J, Ruan S C, Hou Y L 2020 Natl. Sci. Rev. 7 841 Google Scholar
[141]	De Siena M C, Creutz S E, Regan A, Malinowski P, Jiang Q N, Kluherz K T, Zhu G M, Lin Z, De Yoreo J J, Xu X D, Chu J H, Gamelin D R 2020 Nano Lett. 20 2100 Google Scholar
[142]	Liu S S, Yuan X, Zhou Y C, Sheng Y, Huang C, Zhang E Z, Ling J W, Liu Y W, Wang W Y, Zhang C, Zou J, Wang K Y, Xiu F X 2017 Npj 2D Mater. Appl. 1 1 Google Scholar
[143]	Liu Z L, Wu X, Shao Y, Qi J, Cao Y, Huang L, Liu C, Wang J O, Zheng Q, Zhu Z L, Ibrahim K, Wang Y L, Gao H J 2018 Sci. Bull. 63 419 Google Scholar
[144]	Liu Z L, Lei B, Zhu Z L, Tao L, Qi J, Bao D L, Wu X, Huang L, Zhang Y Y, Lin X, Wang Y L, Du S X, Pantelides S T, Gao H J 2019 Nano Lett. 19 4897 Google Scholar
[145]	Gong Y, Guo J W, Li J H, Zhu K J, Liao M H, Liu X Z, Zhang Q H, Gu L, Tang L, Feng X, Zhang D, Li W, Song C L, Wang L L, Yu P, Chen X, Wang Y Y, Yao H, Duan W H, Xu Y, Zhang S C, Ma X C, Xue Q K, He K 2019 Chin. Phys. Lett. 36 089901 Google Scholar
[146]	Wen Y, Liu Z H, Zhang Y, Xia C X, Zhai B X, Zhang X H, Zhai G H, Shen C, He P, Cheng R Q, Yin L, Yao Y Y, Sendeku M G, Wang Z X, Ye X B, Liu C S, Jiang C, Shan C X, Long Y W, He J 2020 Nano Lett. 20 3130 Google Scholar
[147]	Kimura A, Matsuno J, Okabayashi J, Fujimori A, Shishidou T, Kulatov E, Kanomata T 2001 Phys. Rev. B 63 224420 Google Scholar
[148]	Fei Z Y, Huang B, Malinowski P, Wang W B, Song T C, Sanchez J, Yao W, Xiao D, Zhu X Y, May A F, Wu W D, Cobden D H, Chu J H, Xu X D 2018 Nat. Mater. 17 778 Google Scholar
[149]	Pathak S, Sharma M 2014 J. Appl. Phys. 115 043906 Google Scholar
[150]	Zhang G P, Hubner W, Lefkidis G, Bai Y H, George T F 2009 Nat. Phys. 5 499 Google Scholar
[151]	Su J W, Wang M S, Liu G H, Li H Q, Han J B, Zhai T Y 2020 Adv. Sci. 7 2001722 Google Scholar
[152]	Liu B, Liu S S, Yang L, Chen Z D, Zhang E Z, Li Z H, Wu J, Ruan X Z, Xiu F X, Liu W Q, He L, Zhang R, Xu Y B 2020 Phys. Rev. Lett. 125 267205 Google Scholar
[153]	Cai L, Yu C L, Liu L Y, Xia W, Zhou H A, Zhao L, Dong Y Q, Xu T, Wang Z D, Guo Y F, Zhao Y G, Zhang J S, Yang L Y, Yang L X, Jiang W J 2020 Appl. Phys. Lett. 117 192401 Google Scholar
[154]	Gibson G A, Schultz S 1993 J. Appl. Phys. 73 4516 Google Scholar
[155]	Niu B, Su T, Francisco B A, Ghosh S, Kargar F, Huang X, Lohmann M, Li J X, Xu Y D, Taniguchi T, Watanabe K, Wu D, Balandin A, Shi J, Cui Y T 2020 Nano Lett. 20 553 Google Scholar
[156]	Bonilla M, Kolekar S, Ma Y J, Diaz H C, Kalappattil V, Das R, Eggers T, Gutierrez H R, Phan M H, Batzill M 2018 Nat. Nanotechnol. 13 289 Google Scholar
[157]	Zhou X H, Brzostowski B, Durajski A P, Liu M Z, Xiang J, Jiang T R, Wang Z Q, Chen S W, Li P G, Zhong Z H, Drzewinski A, Jarosik M W, Szczesniak R, Lai T S, Guo D H, Zhong D Y 2020 J. Phys. Chem. C 124 9416 Google Scholar
[158]	Tian Y, Gray M J, Ji H W, Cava R J, Burch K S 2016 2 D Mater. 3 025035 Google Scholar
[159]	Zhang X D, Xie Y 2013 Chem. Soc. Rev. 42 8187 Google Scholar
[160]	Heron J T, Trassin M, Ashraf K, Gajek M, He Q, Yang S Y, Nikonov D E, Chu Y H, Salahuddin S, Ramesh R 2011 Phys. Rev. Lett. 107 217202 Google Scholar
[161]	Cao T, Li Z L, Louie S G 2015 Phys. Rev. Lett. 114 236602 Google Scholar
[162]	Li X X, Yang J L 2014 J. Mater. Chem. C 2 7071 Google Scholar
[163]	Pan H 2014 Sci. Rep. 4 7524 Google Scholar
[164]	Li T X, Jiang S W, Sivadas N, Wang Z F, Xu Y, Weber D, Goldberger J E, Watanabe K, Taniguchi T, Fennie C J, Mak K F, Shan J 2019 Nat. Mater. 18 1303 Google Scholar
[165]	Song T C, Fei Z Y, Yankowitz M, Lin Z, Jiang Q N, Hwangbo K, Zhang Q, Sun B S, Taniguchi T, Watanabe K, McGuire M A, Graf D, Cao T, Chu J H, Cobden D H, Dean C R, Xiao D, Xu X D 2019 Nat. Mater. 18 1298 Google Scholar
[166]	Wang Y, Wang C, Liang S J, Ma Z C, Xu K, Liu X W, Zhang L L, Admasu A S, Cheong S W, Wang L Z, Chen M Y, Liu Z L, Cheng B, Ji W, Miao F 2020 Adv. Mater. 32 2004533 Google Scholar
[167]	Zhang W, Zhang L, Wong P K J, Yuan J R, Vinai G, Torelli P, van der Laan G, Feng Y P, Wee A T S 2019 ACS Nano 13 8997 Google Scholar
[168]	Zhang L M,Huang X Y, Dai H W, Wang M S, Cheng H, Tong L, Li Z, Han X T, Wang X, Ye L, Han J B 2020 Adv. Mater. 32 2002032 Google Scholar
[169]	Cao Y, Fatemi V, Demir A, Fang S, Tomarken S L, Luo J Y, Sanchez-Yamagishi J D, Watanabe K, Taniguchi T, Kaxiras E, Ashoori R C, Jarillo-Herrero P 2018 Nature 556 80 Google Scholar
[170]	Cao Y, Fatemi V, Fang S, Watanabe K, Taniguchi T, Kaxiras E, Jarillo-Herrero P 2018 Nature 556 43 Google Scholar
[171]	Jiang T, Liu H R, Huang D, Zhang S, Li Y G, Gong X G, Shen Y R, Liu W T, Wu S W 2014 Nat. Nanotechnol. 9 825 Google Scholar
[172]	Alegria L D, Ji H, Yao N, Clarke J J, Cava R J, Petta J R 2014 Appl. Phys. Lett. 105 053512 Google Scholar
[173]	Zhong D, Seyler K L, Linpeng X Y, Cheng R, Sivadas N, Huang B, Schmidgall E, Taniguchi T, Watanabe K, McGuire M A, Yao W, Xiao D, Fu K M C, Xu X D 2017 Sci. Adv. 3 e1603113 Google Scholar

[1]	Jiang Long-Xing, Li Qing-Chao, Zhang Xu, Li Jing-Feng, Zhang Jing, Chen Zu-Xin, Zeng Min, Wu Hao. Spintronic devices based on topological and two-dimensional materials. Acta Physica Sinica, 2024, 73(1): 017505. doi: 10.7498/aps.73.20231166
[2]	Xiong Yi-Nong, Wu Chuang-Wen, Ren Chuan-Tong, Meng De-Quan, Chen Shi-Wei, Liang Shi-Heng. Research progress of spin orbit torque of two-dimensional magnetic materials. Acta Physica Sinica, 2024, 73(1): 017502. doi: 10.7498/aps.73.20231244
[3]	Fan Xiao-Zheng, Li Yi-Lian, Wu Yi, Chen Jun-Cai, Xu Guo-Liang, An Yi-Peng. Magnetism and spin transport properties of two-dimensional magnetic semiconductor kagome lattice Nb₃Cl₈ monolayer. Acta Physica Sinica, 2023, 72(24): 247503. doi: 10.7498/aps.72.20231163
[4]	Yu Ze-Hao, Zhang Li-Fa, Wu Jing, Zhao Yun-Shan. Recent progress of 2-dimensional layered thermoelectric materials. Acta Physica Sinica, 2023, 72(5): 057301. doi: 10.7498/aps.72.20222095
[5]	Li Ce, Yang Dong-Liang, Sun Lin-Feng. Research progress of neuromorphic devices based on two-dimensional layered materials. Acta Physica Sinica, 2022, 71(21): 218504. doi: 10.7498/aps.71.20221424
[6]	Liu Nan-Shu, Wang Cong, Ji Wei. Recent research advances in two-dimensional magnetic materials. Acta Physica Sinica, 2022, 71(12): 127504. doi: 10.7498/aps.71.20220301
[7]	Liu Yu-Ting, He Wen-Yu, Liu Jun-Wei, Shao Qi-Ming. Berry curvature-induced emerging magnetic response in two-dimensional materials. Acta Physica Sinica, 2021, 70(12): 127303. doi: 10.7498/aps.70.20202132
[8]	Liao Jun-Yi, Wu Juan-Xia, Dang Chun-He, Xie Li-Ming. Methods of transferring two-dimensional materials. Acta Physica Sinica, 2021, 70(2): 028201. doi: 10.7498/aps.70.20201425
[9]	He Cong-Li, Xu Hong-Jun, Tang Jian, Wang Xiao, Wei Jin-Wu, Shen Shi-Peng, Chen Qing-Qiang, Shao Qi-Ming, Yu Guo-Qiang, Zhang Guang-Yu, Wang Shou-Guo. Research progress of spin-orbit torques based on two-dimensional materials. Acta Physica Sinica, 2021, 70(12): 127501. doi: 10.7498/aps.70.20210004
[10]	Wang Hai-Yu, Liu Ying-Jie, Xun Lu-Lu, Li Jing, Yang Qing, Tian Qi-Yun, Nie Tian-Xiao, Zhao Wei-Sheng. Research progress of preparation of large-scale two-dimensional magnetic materials and manipulation of Curie temperature. Acta Physica Sinica, 2021, 70(12): 127301. doi: 10.7498/aps.70.20210223
[11]	Xiao Han, Mi Meng-Juan, Wang Yi-Lin. Recent development in two-dimensional magnetic materials and multi-field control of magnetism. Acta Physica Sinica, 2021, 70(12): 127503. doi: 10.7498/aps.70.20202204
[12]	Wang Hui, Xu Meng, Zheng Ren-Kui. Research progress and device applications of multifunctional materials based on two-dimensional film/ferroelectrics heterostructures. Acta Physica Sinica, 2020, 69(1): 017301. doi: 10.7498/aps.69.20191486
[13]	Xu Yi-Quan, Wang Cong. All-optical devices based on two-dimensional materials. Acta Physica Sinica, 2020, 69(18): 184216. doi: 10.7498/aps.69.20200654
[14]	Wu Xiang-Shui, Tang Wen-Ting, Xu Xiang-Fan. Recent progresses of thermal conduction in two-dimensional materials. Acta Physica Sinica, 2020, 69(19): 196602. doi: 10.7498/aps.69.20200709
[15]	Xu Hong, Yuan Zheng-Yi, Huang Tong-Fei, Wang Xiao, Chen Zheng-Xian, Wei Jin, Zhang Xiang, Huang Yuan. Inspiration of wrinkles in layered material for the mechanism study of several geological activities. Acta Physica Sinica, 2020, 69(2): 026101. doi: 10.7498/aps.69.20190122
[16]	Wang Peng-Cheng, Cao Yi, Xie Hong-Guang, Yin Yao, Wang Wei, Wang Ze-Ying, Ma Xin-Chen, Wang Lin, Huang Wei. Magnetic properties of layered chiral topological magnetic material Cr_1/3NbS₂. Acta Physica Sinica, 2020, 69(11): 117501. doi: 10.7498/aps.69.20200007
[17]	Shi Ruo-Yu, Wang Lin-Feng, Gao Lei, Song Ai-Sheng, Liu Yan-Min, Hu Yuan-Zhong, Ma Tian-Bao. Quantitative calculation of atomic-scale frictional behavior of two-dimensional material based on sliding potential energy surface. Acta Physica Sinica, 2017, 66(19): 196802. doi: 10.7498/aps.66.196802
[18]	Li Zhu-Song, Steven Zhu. Continuum modeling of thermal transport in superlattices and layered materials for new energy matierlas. Acta Physica Sinica, 2016, 65(11): 116802. doi: 10.7498/aps.65.116802
[19]	Zhang Xin-Wei, Hua Zheng-He, Jiang Yu-Wen, Yang Shao-Guang. Progress in sol-gel autocombustion synthesis of metals and alloys. Acta Physica Sinica, 2015, 64(9): 098101. doi: 10.7498/aps.64.098101
[20]	Zhou Zhuo-Hui, Liu Xiao-Lai, Huang Da-Qing, Kang Fei-Yu. Design and preparation of a low frequency absorber based on hollowed-out cross-shaped meta-material structure. Acta Physica Sinica, 2014, 63(18): 184101. doi: 10.7498/aps.63.184101

Catalog

Vol. 70, Issue 12 - 2021-06-20

Metrics

Abstract views: 25873
PDF Downloads: 2204
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板