Discovery of robust superconductivity against volume shrinkage

Guo Jing; Wu Qi; Sun Li-Ling

doi:10.7498/aps.72.20231341

Abstract

The superconducting transition temperature (T_c) of superconductor is related intimately to multiple degree of freedom of charge, spin, orbital and lattice. Many studies have indicated that pressure is an effective way to tune T_c though changing crystal structure and electronic structure. Here, we report a new progress made in the high-pressure studies – discovery of a new type of superconductors whose T_c is robust against large volume shrinkage under extremely high pressure, named RSAVS (robust superconductivity against volume shrinkage) superconductor. Such RSAVS behavior was observed initially in the high entropy alloys of (TaNb)_0.67(HfZrTi)_0.33 and (ScZrNbTa)_0.6(RhPd)_0.4, then in the widely-used NbTi alloy, Nb and Ta elements. Analysis shows that this type of superconductor possesses a body-centered cubic crystal structure and is composed of transition metal elements. The observed results not only present new research topics but also raise the question of what determines T_c of conventional or unconventional superconductors.

Keywords:

Authors and contacts

1.
Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China
2.
Center for High Pressure Science & Technology Advanced Research, Beijing 100094, China
3.
University of Chinese Academy of Sciences, Beijing 100190, China

Corresponding author: Sun Li-Ling, llsun@iphy.ac.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. U2032214, 12122414) and the National Basic Research Program of China (Grant Nos. 2022YFA1403900, 2021YFA1401800).

FullText HTML : translate this paragraph

References

[1]	Mao H K, Chen X J, Ding Y, Li B, Wang L 2018 Rev. Mod. Phys. 90 015007 Google Scholar
[2]	Chu C W, Gao L, Chen F, Huang Z J, Meng R L, Xue Y Y 1993 Nature 365 323 Google Scholar
[3]	Gao L, Xue Y Y, Chen F, Xiong Q, Meng R L, Ramirez D, Chu C W, Eggert J H, Mao H K 1994 Phys. Rev. B 50 4260 Google Scholar
[4]	Guo J, Zhou Y Z, Huang C, Cai S, Sheng Y T, Gu G D, Yang C L, Lin G C, Yang K, Li A G, Wu Q, Xiang T, Sun L L 2020 Nat. Phys. 16 295 Google Scholar
[5]	Chen X J, Struzhkin V V, Yu Y, Goncharov A F, Lin C T, Mao H K, Hemley R J 2010 Nature 466 950 Google Scholar
[6]	Zhou Y Z, Guo J, Cai S, Zhao J Y , Gu G D, Lin C T, Yan H T, Huang C, Yang C L, Long S J, Gong Y, Li Y C , Li X D , Wu Q, Hu J P , Zhou X J, Xiang T , Sun L L, 2022 Nat. Phys. 18 406 Google Scholar
[7]	Deng L, Zheng Y, Wu Z, Huyan S, Wu H C, Nie Y, Cho K, Chu C W 2019 Proc. Natl. Acad. Sci. U. S. A. 116 2004 Google Scholar
[8]	Sun L L, Chen X J, Guo J, Gao P W, Huang Q Z, Wang H D, Fang M H, Chen X L, Chen G F, Wu Q, Zhang C, Gu D C, Dong X L, Wang L, Yang K, Li A G, Dai X, Mao H K, Zhao Z X 2012 Nature 483 67 Google Scholar
[9]	Takahashi H, Igawa K, Arii K, Kamihara Y, Hirano M, Hosono H 2008 Nature 453 376 Google Scholar
[10]	Gao P W, Sun L L, Ni N, Guo J, Wu Q, Zhang C, Gu D C, Yang K, Li A G, Jiang S, Cava R J, Zhao Z X 2014 Adv. Mater. 26 2346 Google Scholar
[11]	Yamauchi T, Hirata Y, Ueda Y, Ohgushi K 2015 Phys. Rev. Lett. 115 246402 Google Scholar
[12]	Medvedev S, McQueen T M, Troyan I A, Palasyuk T, Eremets M I, Cava R J, Naghavi S, Casper F, Ksenofontov V, Wortmann G, Felser C 2009 Nat. Mater. 8 630 Google Scholar
[13]	Zhang C, Sun L L, Chen Z Y, Zhou X J, Wu Q, Yi W, Guo J, Dong X L, Zhao Z X 2011 Phys. Rev. B 83 140504(R Google Scholar
[14]	Cheng J G, Matsubayashi K, Wu W, Sun J P, Lin F K, Luo J L, Uwatoko Y 2015 Phys. Rev. Lett. 114 117001 Google Scholar
[15]	Hamlin J J 2015 Physica C 514 59 Google Scholar
[16]	Eiling A, Schilling J S 1981 J. Phys. F: Met. Phys. 11 623
[17]	Shimizu K 2015 Physica C 514 46 Google Scholar
[18]	Akahama Y, Kobayashi M, Kawamura H 1990 J. Phys. Soc. Jpn. 59 3843 Google Scholar
[19]	Ishizuka M, Iketani M, Endo S 2000 Phys. Rev. B 61 R3823 Google Scholar
[20]	Sakata M, Nakamoto Y, Shimizu K 2011 Phys. Rev. B 83 220512(R Google Scholar
[21]	Yabuuchi T, Matsuoka T, Nakamoto Y, Shimizu K 2006 J. Phys. Soc. Jpn. 75 083703 Google Scholar
[22]	Zhang C L, He X, Liu C, Li Z W, Lu K, Zhang S J, Feng S M, Wang X C, Peng Y, Long Y W, Yu R C, Wang L H, Prakapenk V, Chariton S, Li Q, Liu H Z, Chen C F , Jin C Q 2022 Nat. Commun. 13 5411 Google Scholar
[23]	Ying J J, Liu S Q, Lu Q, Wen X K, Gui Z G, Zhang Y Q, Wang X M, Sun J, Chen X H 2023 Phys. Rev. Lett. 130 256002 Google Scholar
[24]	Eremets M I, Struzhkin V V, Mao H K, Hemley R J 2001 Science 293 272 Google Scholar
[25]	Struzhkin V V, Hemley R J, Mao H K, Timofeev Y A 1997 Nature 390 382 Google Scholar
[26]	Sun L L, Matsuoka T, Tamari Y, Shimizu K, Tian J F, Tian Y, Zhang C D, Shen C M, Yi W, Gao H J, Li J Q, Dong X L, Zhao Z X 2009 Phys. Rev. B 79 140505(R Google Scholar
[27]	Shimizu K, Kimura T, FuromotoS, Takeda K, Kontani K, Onuki Y, Amaya K 2001 Nature 412 316 Google Scholar
[28]	Shimizu K, Ishikawa H, Takao D, Yagi T, Amaya K 2002 Nature 419 597 Google Scholar
[29]	Guo J, Wang H H, Rohr F, Yi W, Zhou Y Z, Wang Z, Cai S, Zhang S, Li X D, Li Y C, Liu J, Yang K, Li A G, Jiang S, Wu Q, Xiang T, Cava R J, Sun L L 2017 Phys. Rev. B 96 224513 Google Scholar
[30]	Shimizu K, Suhara K, Eremets M I, Amaya K 1998 Nature 393 767 Google Scholar
[31]	Sun H L, Huo M W, Hu X W, Li J Y, Han Y F, Tang L Y, Mao Z Q, Yang P T, Wang B S, Cheng J G, Yao D X, Zhang G M, Wang M 2023 Nature arXiv: 2305.09586
[32]	Yuan H Q, Grosche F M, Deppe M, Geibel C, Sparn G , Strglich F 2003 Science 302 2104 Google Scholar
[33]	Drozdov1 A P, Eremets1 M I, Troyan1 I A, Ksenofontov V, Shylin S I 2015 Nature 525 73 Google Scholar
[34]	Somayazulu M, Ahart M, Mishra A K, Geballe Z M, Baldini M, Meng Y, Struzhkin V V, Hemley R J 2019 Phy. Rev. Lett. 122 027001 Google Scholar
[35]	Drozdov A P, Kong P P, Minkov V S, Besedin S P, Kuzovnikov M A, Mozaffari S, Balicas L, Balakirev F F, Graf D E, Prakapenka V B, Greenberg E, Knyazev D A, Tkacz M, Eremets M I 2019 Nature 569 528 Google Scholar
[36]	Zhang L, Wang Y, Lü J , Ma Y 2017 Nat. Rev. Mater. 2 17005 Google Scholar
[37]	Li Z W, He X, Zhang C L, Wang X C, Zhang S J, Jia Y T, Feng S M, Lu K, Zhao J F, Zhang J, Min B S, Long Y W, Yu R C, Wang L H, Ye M Y, Zhang Z S, Prakapenka V, Chariton S, Ginsberg P A, Bass J, Yuan S H, Liu H Z , Jin C Q 2022 Nat. Commun. 13 2863 Google Scholar
[38]	Ma L, Wang K, Xie Y, Yang X, Wang Y Y, Zhou M, Liu H Y, Yu X H, Zhao Y S, Wang H B, Liu G T, Ma Y M 2022 Phys. Rev. Lett. 128 167001 Google Scholar
[39]	Kong P, Minkov V S, Kuzovnikov M A, Drozdov A P, Besedin S P, Mozaffari S, Balicas L, Balakirev F F, Prakapenka V B, Chariton S, Knyazev D A, Greenberg E, Eremets M I 2021 Nat. Commun. 12 5075 Google Scholar
[40]	Chen W, Semenok D V, Huang X, Shu H, Li X, Duan D, Cui T, Oganov A R 2021 Phys. Rev. Lett. 127 117001 Google Scholar
[41]	Guo J, Wang H H, Rohrc F von, Wang Z, Cai S, Zhou Y Z, Yang K, Li A G, Jiang S, Wu Q, Cava R J, Sun L L 2017 Proc. Natl. Acad. Sci. U. S. A. 114 13144 Google Scholar
[42]	Guo J, Lin G C, Cai S, Xi C Y, Zhang C J, Sun W S, Wang Q L, Yang K, Li A G, Wu Q, Zhang Y H, Xiang T, Cava R J, L L Sun 2019 Adv. Mater. 31 1807240 Google Scholar
[43]	Huang C, Guo J, Zhang J F, Stolze K, Cai S, Liu K, Weng H M, Lu Z Y, Wu Q, Xiang T, Cava R J, Sun L L 2020 Phys. Rev. Mater. 4 071801(R Google Scholar
[44]	Yeh J W, Chen S K, Lin S J, Gan G Y, Chin S T, Shun T T, Tsau S H, Chang S Y 2004 Adv. Eng. Mater. 6 299 Google Scholar
[45]	Ye Y F, Wang Q, Lu J, Liu C T, Yang Y 2016 Mater. Today 19 349 Google Scholar
[46]	Miracle D B, Senkov O N 2017 Acta Mater. 122 448 Google Scholar
[47]	Zhang W R, Liaw P K, Zhang Y 2018 Chin. Mater. 61 2 Google Scholar
[48]	George E P, Rabbe D, Ritchie R O 2019 Nat. Rev. Mater. 4 515 Google Scholar
[49]	Gludovatz B, Hohenwarter A, Thurston K V S, Bei H B, Wu Z G, George E P, Ritchie R O 2016 Nat. Commun. 7 10602 Google Scholar
[50]	Gludovatz B, Hohenwarter A, Catoor D, Chang E H, Geogre E P , Ritchie R O 2014 Science 345 1153 Google Scholar
[51]	Kou H, Lu J, Li Y 2014 Adv. Mater. 26 5518 Google Scholar
[52]	Zou Y, Ma H, Spolenak R 2015 Nat. Commun. 6 7748 Google Scholar
[53]	Koželj P, Vrtnik S, Jelen A, Jazbec S, Jagličić Z, Maiti S, Feuerbacher M, Steurer W, Dolinšek J 2014 Phys. Rev. Lett. 113 107001 Google Scholar
[54]	Sun L L, Cava R J 2019 Phys. Rev. Mater. 3 090301 Google Scholar
[55]	von Rohr F O, Cava R J 2018 Phys. Rev. Mater. 2 034801 Google Scholar
[56]	Vrtnik S, Koželj P, Meden A, Maiti S, Steurer W, Feuerbacher M, Dolinšek J 2017 J. Alloys Compd. 695 3530 Google Scholar
[57]	Yuan Y, Wu Y, Luo H, Wang Z, Liang X, Yang Z, Wang H, Liu X, Lu Z 2018 Front. Mater. 5 72 Google Scholar
[58]	Xia S, Lousada C M, Mao H, Maier A C, Korzhavyi P A, Sström R, Wang Y , Zhang Y 2018 Front. Mater. 5 26 Google Scholar
[59]	Stolze K, Cevallos F A, Kong T, Cava R J 2018 J. Mater. Chem. C 6 10441 Google Scholar
[60]	Wu K Y, Chen S K, Wu J M 2018 Nat. Sci. J. 10 110 Google Scholar
[61]	Scanlan R M, Malozemoff A P, Larbalestier D C 2004 Proc. IEEE 92 1639 Google Scholar
[62]	Parizh M, Lvovsky Y, Sumption M 2017 Supercond. Sci. Technol. 30 014007 Google Scholar
[63]	Liu J H, Cheng J S, Wang Q L 2013 IEEE Trans. Appl. Supercond. 23 4802606 Google Scholar
[64]	Zhang P X, Li J F, Guo Q, Zhu Y M, Yan K J, Wang R L, Zhang K L, Liu X H, Feng Y 2019 Titanium for Consumer Applications 15 279 Google Scholar
[65]	Banno N, Kobayashi K, Uchida A, Kitaguchi H 2021 J. Mater. Sci. 56 20197 Google Scholar
[66]	Struzhkin V V, Timofeev Y A, Hemley R J, Mao H K 1997 Phys. Rev. Lett. 79 4262 Google Scholar
[67]	Tonkov E Y, Ponyatovsky E 2004 Phase Transformations of Elements Under High Pressure (Boca Raton: CRC Press LLC) p237
[68]	Cynn H, Yoo C S 1999 Phys. Rev. B 59 8526 Google Scholar
[69]	Kenichi T, Singh A K 2006 Phys. Rev. B 73 224119 Google Scholar
[70]	Gao M C, Miracle D B, Maurice D, Yan X H, Zhang Y, Hawk J A 2018 J. Mater. Res. 33 3138 Google Scholar
[71]	Browne A J, Strong D P, Cava R J 2023 J. Solid State Chem. 321 123881 Google Scholar
[72]	Jung S G, Han Y, Kim J H, Hidayati R, Rhyee J S, Lee J M, Kang W N, Choi W S, Jeon H R, Suk J, Park T 2022 Nat. Commun. 13 3373 Google Scholar
[73]	Koblischka M R, Koblischka-Veneva A 2022 Metals 12 568 Google Scholar
[74]	Mgrdichian L 2018 A Material that Superconducts Continuously up to Extreme Pressures
[75]	Research Highlight: Super-squeezing can't crush this superconductor's powers 2017 Nature 552 150 Google Scholar
[76]	Lee C H, Iyo A, Eisaki H, Kito H, Fern, ez-Diaz M T, Ito T, Kihou K, Matsuhata H, Braden M, Yamada K 2008 J. Phys. Soc. Jpn. 77 083704 Google Scholar
[77]	Mizuguchi Y, Hara Y, Deguchi K, Tsuda S, Yamaguchi T, Takeda K, Kotegawa H, Tou H, Takano Y 2010 Supercond. Sci. Technol. 23 054013 Google Scholar
[78]	Zhang J F, Gao M, Liu K, Lu Z Y 2020 Phys. Rev. B 102 195140 Google Scholar
[79]	Liu X Q, Jiang P, Wang Y M, Li M T, Li N N, Zhang Q, Wang Y D, Li Y L, Yang W G 2022 Phys. Rev. B 105 224511 Google Scholar

Cited By

图 1 由电阻-温度曲线确定的超导转变温度与压力关系相图, 压力范围为0至190.6 GPa^[41]

Figure 1. Phase diagram of superconducting transition temperature vs. applied pressure up to 190.6 GPa for the HEA, combined with plots of the corresponding resistance vs. temperature ^[41].

DownLoad: Full-Size Img PowerPoint

图 2 (a) 高熵合金(ScZrNbTa)_0.6(RhPd)_0.4在2.9—71.8 GPa压力范围内的电阻随温度变化关系; (b) 较低温度范围的归一化电阻; (c) 3.9—80.1 GPa压力范围X射线粉末衍射图谱; (d), (e) 晶格参数和晶胞体积随压力的变化^[41]

Figure 2. (a) Temperature dependence of the resistance in the pressure range of 2.9–71.8 GPa; (b) normalized resistance at lower temperature, exhibiting sharp superconducting transitions with zero resistance and the continuous increase in T_c upon compression; (c) X-ray powder diffraction patterns collected in the pressure range of 3.9–80.1 GPa; (d), (e) pressure dependence of the lattice parameter and unit cell volume ^[41].

DownLoad: Full-Size Img PowerPoint

图 3 高压下NbTi合金结构信息　(a) 0.1—200.5 GPa压力范围内X射线粉末衍射图谱; (b), (c) 两轮独立测量获得的晶格参数和晶胞体积随压力的变化. 图(b)插图为NbTi超导体晶体结构示意图 ^[42]

Figure 3. Structure information for NbTi at high pressure: (a) X-ray powder diffraction patterns collected in the pressure range of 0.1–200.5 GPa; (b), (c) pressure dependence of the lattice parameter and unit cell volume for independent two runs. The inset of Figure (b) displays the schematic crystal structure of the NbTi superconductor ^[42].

DownLoad: Full-Size Img PowerPoint

图 4 Nb_0.44Ti_0.56的超导性在不同压力和磁场条件下的变化以及摩尔体积的压力依赖关系. 在压力与超导转变温度(T_c)关系图中, 彩色球代表来自不同轮实验的T_c值. 在磁场B(T)与T_c关系图中, 黑色、绿色和红色球代表在零磁场和外加磁场下获得的T_c值. 在压力与体积(–∆V = V_p – V₀, 其中V_p是在固定压力下的体积, V₀是环境压力下的体积)关系图中, 粉色和蓝色方块表示来自两轮独立实验的结果. 红色五角星号代表最高压力下的T_c值, 绿色五角星号表示1.8 K下的临界磁场和本研究的最大压力, 蓝色五角星号表示研究中所施加最高压力下的相对体积^[42]

Figure 4. Superconductivity of Nb_0.44Ti_0.56 under various pressure and magnetic field conditions, and the pressure dependence of its molar volume. In the panel of pressure versus superconducting transition temperature (T_c), the colored balls represent the T_c obtained from the different experimental runs. In the panel of magnetic field, B (T) versus T_c, the black, green, and red balls represent T_c obtained under zero and applied magnetic fields. In the panel of pressure versus volume (–ΔV = V_p – V₀, where V_p is the volume at fixed pressure and V₀ is the ambient-pressure volume), the pink and blue squares represent the results obtained from the two independent runs. The red star labels the T_c value at the record-high pressure, the green star marks the critical field at 1.8 K and the maximum pressure of this study, and the blue star refers to the relative volume at the highest pressure investigated. The top left panel displays that the maximum pressure of this study falls in that of outer core of the earth ^[42].

DownLoad: Full-Size Img PowerPoint

图 5 单质金属Nb和Ta的超导转变温度随压力的变化. 数据引自[41, 66, 67]

Figure 5. Pressure dependence of T_c for elemental Ta and Nb. The data were taken from Refs. [41, 66, 67] .

DownLoad: Full-Size Img PowerPoint

图 6 RSAVS超导体的超导转变温度随体积的变化　(a) (TaNb)_0.67(HfZrTi)_0.33和(ScZrNbTa)_0.6(RhPd)_0.4高熵合金、NbTi合金和单质金属Ta和Nb的超导转变温度(T_c)随体积的变化. 为了方便对不同材料进行比较, 采用相对体积变化率(–ΔV/V₀)作为变量. 图中的箭头表示RSAVS状态出现的临界压力(P_C). 对于(ScZrNbTa)_0.6(RhPd)_0.4超导体, P_C约为30 GPa(对应体积变化率–ΔV/V₀约为15.5%), 对于(TaNb)_0.67(HfZrTi)_0.33超导体, P_C为60 GPa(–ΔV/V₀ = 21.6%), 对于NbTi超导体, P_C为120 GPa(–ΔV/V₀ = 34.7%), 而对于单质Ta和Nb超导体, P_C为1 bar. P_E和P^*分别表示RSAVS态的结束压力和测量到RSAVS态的最高压力. (b) (TaNb)_0.67(HfZrTi)_0.33和(ScZrNbTa)_0.6(RhPd)_0.4高熵合金、NbTi合金以及单质Ta和Nb的晶体结构示意图, 均为体心立方结构^[43]

Figure 6. Superconductivity and crystal structure for the RSAVS superconductors. (a) The pressure-dependent change in the superconducting transition temperature (T_c) of the (TaNb)_0.67(HfZrTi)_0.33 and (ScZrNbTa)_0.6(RhPd)_0.4 high-entropy alloys, the NbTi alloy, and the elemental metals, Ta and Nb. In order to facilitate the comparison of the different materials, we use the volume shrinkage (–ΔV/V₀) as a variable. Arrows in the diagram indicate the critical pressure (P_C) where the RSAVS state emerges. P_C is about 30 GPa [the corresponding volume (–ΔV/V₀ ) change is about 15.5%] for the (ScZrNbTa)_0.6(RhPd)_0.4 superconductor, 60 GPa (–ΔV/V₀ = 21.6%) for the (TaNb)_0.67(HfZrTi)_0.33 superconductor, and 120 GPa (–ΔV/V₀= 34.7%) for the NbTi superconductor, while P_C is 1 bar for the elemental Ta and Nb superconductors. P_E and P^* represent the end pressure of the RSAVS state and the highest pressure measured for the RSAVS state, respectively. (b) Sketches for the lattice structure of the (TaNb)_0.67(HfZrTi)_0.33 and (ScZrNbTa)_0.6(RhPd)_0.4 high-entropy alloys, NbTi alloy, and elemental Ta and Nb, which all possess body-centered cubic structure ^[43]

DownLoad: Full-Size Img PowerPoint

map

[1]	Mao H K, Chen X J, Ding Y, Li B, Wang L 2018 Rev. Mod. Phys. 90 015007 Google Scholar
[2]	Chu C W, Gao L, Chen F, Huang Z J, Meng R L, Xue Y Y 1993 Nature 365 323 Google Scholar
[3]	Gao L, Xue Y Y, Chen F, Xiong Q, Meng R L, Ramirez D, Chu C W, Eggert J H, Mao H K 1994 Phys. Rev. B 50 4260 Google Scholar
[4]	Guo J, Zhou Y Z, Huang C, Cai S, Sheng Y T, Gu G D, Yang C L, Lin G C, Yang K, Li A G, Wu Q, Xiang T, Sun L L 2020 Nat. Phys. 16 295 Google Scholar
[5]	Chen X J, Struzhkin V V, Yu Y, Goncharov A F, Lin C T, Mao H K, Hemley R J 2010 Nature 466 950 Google Scholar
[6]	Zhou Y Z, Guo J, Cai S, Zhao J Y , Gu G D, Lin C T, Yan H T, Huang C, Yang C L, Long S J, Gong Y, Li Y C , Li X D , Wu Q, Hu J P , Zhou X J, Xiang T , Sun L L, 2022 Nat. Phys. 18 406 Google Scholar
[7]	Deng L, Zheng Y, Wu Z, Huyan S, Wu H C, Nie Y, Cho K, Chu C W 2019 Proc. Natl. Acad. Sci. U. S. A. 116 2004 Google Scholar
[8]	Sun L L, Chen X J, Guo J, Gao P W, Huang Q Z, Wang H D, Fang M H, Chen X L, Chen G F, Wu Q, Zhang C, Gu D C, Dong X L, Wang L, Yang K, Li A G, Dai X, Mao H K, Zhao Z X 2012 Nature 483 67 Google Scholar
[9]	Takahashi H, Igawa K, Arii K, Kamihara Y, Hirano M, Hosono H 2008 Nature 453 376 Google Scholar
[10]	Gao P W, Sun L L, Ni N, Guo J, Wu Q, Zhang C, Gu D C, Yang K, Li A G, Jiang S, Cava R J, Zhao Z X 2014 Adv. Mater. 26 2346 Google Scholar
[11]	Yamauchi T, Hirata Y, Ueda Y, Ohgushi K 2015 Phys. Rev. Lett. 115 246402 Google Scholar
[12]	Medvedev S, McQueen T M, Troyan I A, Palasyuk T, Eremets M I, Cava R J, Naghavi S, Casper F, Ksenofontov V, Wortmann G, Felser C 2009 Nat. Mater. 8 630 Google Scholar
[13]	Zhang C, Sun L L, Chen Z Y, Zhou X J, Wu Q, Yi W, Guo J, Dong X L, Zhao Z X 2011 Phys. Rev. B 83 140504(R Google Scholar
[14]	Cheng J G, Matsubayashi K, Wu W, Sun J P, Lin F K, Luo J L, Uwatoko Y 2015 Phys. Rev. Lett. 114 117001 Google Scholar
[15]	Hamlin J J 2015 Physica C 514 59 Google Scholar
[16]	Eiling A, Schilling J S 1981 J. Phys. F: Met. Phys. 11 623
[17]	Shimizu K 2015 Physica C 514 46 Google Scholar
[18]	Akahama Y, Kobayashi M, Kawamura H 1990 J. Phys. Soc. Jpn. 59 3843 Google Scholar
[19]	Ishizuka M, Iketani M, Endo S 2000 Phys. Rev. B 61 R3823 Google Scholar
[20]	Sakata M, Nakamoto Y, Shimizu K 2011 Phys. Rev. B 83 220512(R Google Scholar
[21]	Yabuuchi T, Matsuoka T, Nakamoto Y, Shimizu K 2006 J. Phys. Soc. Jpn. 75 083703 Google Scholar
[22]	Zhang C L, He X, Liu C, Li Z W, Lu K, Zhang S J, Feng S M, Wang X C, Peng Y, Long Y W, Yu R C, Wang L H, Prakapenk V, Chariton S, Li Q, Liu H Z, Chen C F , Jin C Q 2022 Nat. Commun. 13 5411 Google Scholar
[23]	Ying J J, Liu S Q, Lu Q, Wen X K, Gui Z G, Zhang Y Q, Wang X M, Sun J, Chen X H 2023 Phys. Rev. Lett. 130 256002 Google Scholar
[24]	Eremets M I, Struzhkin V V, Mao H K, Hemley R J 2001 Science 293 272 Google Scholar
[25]	Struzhkin V V, Hemley R J, Mao H K, Timofeev Y A 1997 Nature 390 382 Google Scholar
[26]	Sun L L, Matsuoka T, Tamari Y, Shimizu K, Tian J F, Tian Y, Zhang C D, Shen C M, Yi W, Gao H J, Li J Q, Dong X L, Zhao Z X 2009 Phys. Rev. B 79 140505(R Google Scholar
[27]	Shimizu K, Kimura T, FuromotoS, Takeda K, Kontani K, Onuki Y, Amaya K 2001 Nature 412 316 Google Scholar
[28]	Shimizu K, Ishikawa H, Takao D, Yagi T, Amaya K 2002 Nature 419 597 Google Scholar
[29]	Guo J, Wang H H, Rohr F, Yi W, Zhou Y Z, Wang Z, Cai S, Zhang S, Li X D, Li Y C, Liu J, Yang K, Li A G, Jiang S, Wu Q, Xiang T, Cava R J, Sun L L 2017 Phys. Rev. B 96 224513 Google Scholar
[30]	Shimizu K, Suhara K, Eremets M I, Amaya K 1998 Nature 393 767 Google Scholar
[31]	Sun H L, Huo M W, Hu X W, Li J Y, Han Y F, Tang L Y, Mao Z Q, Yang P T, Wang B S, Cheng J G, Yao D X, Zhang G M, Wang M 2023 Nature arXiv: 2305.09586
[32]	Yuan H Q, Grosche F M, Deppe M, Geibel C, Sparn G , Strglich F 2003 Science 302 2104 Google Scholar
[33]	Drozdov1 A P, Eremets1 M I, Troyan1 I A, Ksenofontov V, Shylin S I 2015 Nature 525 73 Google Scholar
[34]	Somayazulu M, Ahart M, Mishra A K, Geballe Z M, Baldini M, Meng Y, Struzhkin V V, Hemley R J 2019 Phy. Rev. Lett. 122 027001 Google Scholar
[35]	Drozdov A P, Kong P P, Minkov V S, Besedin S P, Kuzovnikov M A, Mozaffari S, Balicas L, Balakirev F F, Graf D E, Prakapenka V B, Greenberg E, Knyazev D A, Tkacz M, Eremets M I 2019 Nature 569 528 Google Scholar
[36]	Zhang L, Wang Y, Lü J , Ma Y 2017 Nat. Rev. Mater. 2 17005 Google Scholar
[37]	Li Z W, He X, Zhang C L, Wang X C, Zhang S J, Jia Y T, Feng S M, Lu K, Zhao J F, Zhang J, Min B S, Long Y W, Yu R C, Wang L H, Ye M Y, Zhang Z S, Prakapenka V, Chariton S, Ginsberg P A, Bass J, Yuan S H, Liu H Z , Jin C Q 2022 Nat. Commun. 13 2863 Google Scholar
[38]	Ma L, Wang K, Xie Y, Yang X, Wang Y Y, Zhou M, Liu H Y, Yu X H, Zhao Y S, Wang H B, Liu G T, Ma Y M 2022 Phys. Rev. Lett. 128 167001 Google Scholar
[39]	Kong P, Minkov V S, Kuzovnikov M A, Drozdov A P, Besedin S P, Mozaffari S, Balicas L, Balakirev F F, Prakapenka V B, Chariton S, Knyazev D A, Greenberg E, Eremets M I 2021 Nat. Commun. 12 5075 Google Scholar
[40]	Chen W, Semenok D V, Huang X, Shu H, Li X, Duan D, Cui T, Oganov A R 2021 Phys. Rev. Lett. 127 117001 Google Scholar
[41]	Guo J, Wang H H, Rohrc F von, Wang Z, Cai S, Zhou Y Z, Yang K, Li A G, Jiang S, Wu Q, Cava R J, Sun L L 2017 Proc. Natl. Acad. Sci. U. S. A. 114 13144 Google Scholar
[42]	Guo J, Lin G C, Cai S, Xi C Y, Zhang C J, Sun W S, Wang Q L, Yang K, Li A G, Wu Q, Zhang Y H, Xiang T, Cava R J, L L Sun 2019 Adv. Mater. 31 1807240 Google Scholar
[43]	Huang C, Guo J, Zhang J F, Stolze K, Cai S, Liu K, Weng H M, Lu Z Y, Wu Q, Xiang T, Cava R J, Sun L L 2020 Phys. Rev. Mater. 4 071801(R Google Scholar
[44]	Yeh J W, Chen S K, Lin S J, Gan G Y, Chin S T, Shun T T, Tsau S H, Chang S Y 2004 Adv. Eng. Mater. 6 299 Google Scholar
[45]	Ye Y F, Wang Q, Lu J, Liu C T, Yang Y 2016 Mater. Today 19 349 Google Scholar
[46]	Miracle D B, Senkov O N 2017 Acta Mater. 122 448 Google Scholar
[47]	Zhang W R, Liaw P K, Zhang Y 2018 Chin. Mater. 61 2 Google Scholar
[48]	George E P, Rabbe D, Ritchie R O 2019 Nat. Rev. Mater. 4 515 Google Scholar
[49]	Gludovatz B, Hohenwarter A, Thurston K V S, Bei H B, Wu Z G, George E P, Ritchie R O 2016 Nat. Commun. 7 10602 Google Scholar
[50]	Gludovatz B, Hohenwarter A, Catoor D, Chang E H, Geogre E P , Ritchie R O 2014 Science 345 1153 Google Scholar
[51]	Kou H, Lu J, Li Y 2014 Adv. Mater. 26 5518 Google Scholar
[52]	Zou Y, Ma H, Spolenak R 2015 Nat. Commun. 6 7748 Google Scholar
[53]	Koželj P, Vrtnik S, Jelen A, Jazbec S, Jagličić Z, Maiti S, Feuerbacher M, Steurer W, Dolinšek J 2014 Phys. Rev. Lett. 113 107001 Google Scholar
[54]	Sun L L, Cava R J 2019 Phys. Rev. Mater. 3 090301 Google Scholar
[55]	von Rohr F O, Cava R J 2018 Phys. Rev. Mater. 2 034801 Google Scholar
[56]	Vrtnik S, Koželj P, Meden A, Maiti S, Steurer W, Feuerbacher M, Dolinšek J 2017 J. Alloys Compd. 695 3530 Google Scholar
[57]	Yuan Y, Wu Y, Luo H, Wang Z, Liang X, Yang Z, Wang H, Liu X, Lu Z 2018 Front. Mater. 5 72 Google Scholar
[58]	Xia S, Lousada C M, Mao H, Maier A C, Korzhavyi P A, Sström R, Wang Y , Zhang Y 2018 Front. Mater. 5 26 Google Scholar
[59]	Stolze K, Cevallos F A, Kong T, Cava R J 2018 J. Mater. Chem. C 6 10441 Google Scholar
[60]	Wu K Y, Chen S K, Wu J M 2018 Nat. Sci. J. 10 110 Google Scholar
[61]	Scanlan R M, Malozemoff A P, Larbalestier D C 2004 Proc. IEEE 92 1639 Google Scholar
[62]	Parizh M, Lvovsky Y, Sumption M 2017 Supercond. Sci. Technol. 30 014007 Google Scholar
[63]	Liu J H, Cheng J S, Wang Q L 2013 IEEE Trans. Appl. Supercond. 23 4802606 Google Scholar
[64]	Zhang P X, Li J F, Guo Q, Zhu Y M, Yan K J, Wang R L, Zhang K L, Liu X H, Feng Y 2019 Titanium for Consumer Applications 15 279 Google Scholar
[65]	Banno N, Kobayashi K, Uchida A, Kitaguchi H 2021 J. Mater. Sci. 56 20197 Google Scholar
[66]	Struzhkin V V, Timofeev Y A, Hemley R J, Mao H K 1997 Phys. Rev. Lett. 79 4262 Google Scholar
[67]	Tonkov E Y, Ponyatovsky E 2004 Phase Transformations of Elements Under High Pressure (Boca Raton: CRC Press LLC) p237
[68]	Cynn H, Yoo C S 1999 Phys. Rev. B 59 8526 Google Scholar
[69]	Kenichi T, Singh A K 2006 Phys. Rev. B 73 224119 Google Scholar
[70]	Gao M C, Miracle D B, Maurice D, Yan X H, Zhang Y, Hawk J A 2018 J. Mater. Res. 33 3138 Google Scholar
[71]	Browne A J, Strong D P, Cava R J 2023 J. Solid State Chem. 321 123881 Google Scholar
[72]	Jung S G, Han Y, Kim J H, Hidayati R, Rhyee J S, Lee J M, Kang W N, Choi W S, Jeon H R, Suk J, Park T 2022 Nat. Commun. 13 3373 Google Scholar
[73]	Koblischka M R, Koblischka-Veneva A 2022 Metals 12 568 Google Scholar
[74]	Mgrdichian L 2018 A Material that Superconducts Continuously up to Extreme Pressures
[75]	Research Highlight: Super-squeezing can't crush this superconductor's powers 2017 Nature 552 150 Google Scholar
[76]	Lee C H, Iyo A, Eisaki H, Kito H, Fern, ez-Diaz M T, Ito T, Kihou K, Matsuhata H, Braden M, Yamada K 2008 J. Phys. Soc. Jpn. 77 083704 Google Scholar
[77]	Mizuguchi Y, Hara Y, Deguchi K, Tsuda S, Yamaguchi T, Takeda K, Kotegawa H, Tou H, Takano Y 2010 Supercond. Sci. Technol. 23 054013 Google Scholar
[78]	Zhang J F, Gao M, Liu K, Lu Z Y 2020 Phys. Rev. B 102 195140 Google Scholar
[79]	Liu X Q, Jiang P, Wang Y M, Li M T, Li N N, Zhang Q, Wang Y D, Li Y L, Yang W G 2022 Phys. Rev. B 105 224511 Google Scholar

[1]	Chen Bei, Deng Yong-He, Qi Qing-Hua, Gao Ming, Wen Da-Dong, Wang Xiao-Yun, Peng Ping. Analysis of icosahedral structure in rapidly solidified Pd₈₂Si₁₈ amorphous alloy under high pressure. Acta Physica Sinica, 2024, 73(2): 026101. doi: 10.7498/aps.73.20231101
[2]	Zhang Yi-Fan, Ren Wei, Wang Wei-Li, Ding Shu-Jian, Li Nan, Chang Liang, Zhou Qian. Machine learning combined with solid solution strengthening model for predicting hardness of high entropy alloys. Acta Physica Sinica, 2023, 72(18): 180701. doi: 10.7498/aps.72.20230646
[3]	Wen Peng, Tao Gang. Molecular dynamics study of the effect of temperature on the shock response and plastic deformation mechanism of CoCrFeMnNi high-entropy alloys. Acta Physica Sinica, 2023, 0(0): 0-0. doi: 10.7498/aps.72.20221621
[4]	Wang Kai-Le, Yang Wen-Kui, Shi Xin-Cheng, Hou Hua, Zhao Yu-Hong. Phase-field-method-studied mechanism of Cu-rich phase precipitation in Al_xCuMnNiFe high-entropy alloy. Acta Physica Sinica, 2023, 72(7): 076102. doi: 10.7498/aps.72.20222439
[5]	Wen Peng, Tao Gang. Molecular dynamics study of temperature effects on shock response and plastic deformation mechanism of CoCrFeMnNi high-entropy alloys. Acta Physica Sinica, 2022, 71(24): 246101. doi: 10.7498/aps.71.20221621
[6]	Shen Tian-Zhan, Song Hai-Yang, An Min-Rong. Effect of twin boundary on mechanical behavior of Cr₂₆Mn₂₀Fe₂₀Co₂₀Ni₁₄ high-entropy alloy by molecular dynamics simulation. Acta Physica Sinica, 2021, 70(18): 186201. doi: 10.7498/aps.70.20210324
[7]	Huang Wen-Jun, Qiao Jun-Wei, Chen Shun-Hua, Wang Xue-Jiao, Wu Yu-Cheng. Preparation, structures and properties of tungsten-containing refractory high entropy alloys. Acta Physica Sinica, 2021, 70(10): 106201. doi: 10.7498/aps.70.20201986
[8]	Ren Xian-Li, Zhang Wei-Wei, Wu Xiao-Yong, Wu Lu, Wang Yue-Xia. Prediction of short range order in high-entropy alloys and its effect on the electronic, magnetic and mechanical properties. Acta Physica Sinica, 2020, 69(4): 046102. doi: 10.7498/aps.69.20191671
[9]	Wang Yan, Cao Qian-Hui, Hu Cui-E, Zeng Zhao-Yi. First-principles calculations of high pressure phase transition of Ce-La-Th alloy. Acta Physica Sinica, 2019, 68(8): 086401. doi: 10.7498/aps.68.20182128
[10]	Guo Jing, Wu Qi, Sun Li-Ling. Pressure-induced phenomena and physics in iron-based superconductors. Acta Physica Sinica, 2018, 67(20): 207409. doi: 10.7498/aps.67.20181651
[11]	Yi Wei, Wu Qi, Sun Li-Ling. Superconductivities of pressurized iron pnictide superconductors. Acta Physica Sinica, 2017, 66(3): 037402. doi: 10.7498/aps.66.037402
[12]	Duan De-Fang, Ma Yan-Bin, Shao Zi-Ji, Xie Hui, Huang Xiao-Li, Liu Bing-Bing, Cui Tian. Structures and novel superconductivity of hydrogen-rich compounds under high pressures. Acta Physica Sinica, 2017, 66(3): 036102. doi: 10.7498/aps.66.036102
[13]	Zhu Guang-Zheng, Guo Lian-Bo, Hao Zhong-Qi, Li Chang-Mao, Shen Meng, Li Kuo-Hu, Li Xiang-You, Liu Jian-Guo, Zeng Xiao-Yan, Lu Yong-Feng. Detection of metal element in water using laser-induced breakdown spectroscopy assisted by nebulizer. Acta Physica Sinica, 2015, 64(2): 024212. doi: 10.7498/aps.64.024212
[14]	Wang Jin-Rong, Zhu Jun, Hao Yan-Jun, Ji Guang-Fu, Xiang Gang, Zou Yang-Chun. First-principles study of the structural, elastic and electronic properties of RhB under high pressure. Acta Physica Sinica, 2014, 63(18): 186401. doi: 10.7498/aps.63.186401
[15]	Zhang Pin-Liang, Gong Zi-Zheng, Ji Guang-Fu, Liu Song. First-principles study of high-pressure physical properties of α-Ti2Zr. Acta Physica Sinica, 2013, 62(4): 046202. doi: 10.7498/aps.62.046202
[16]	Chen Zhong-Jun. First principles study of the elastic, electronic and optical properties of MgS under pressure. Acta Physica Sinica, 2012, 61(17): 177104. doi: 10.7498/aps.61.177104
[17]	Ming Xing, Wang Xiao-Lan, Du Fei, Chen Gang, Wang Chun-Zhong, Yin Jian-Wu. Phase transition and properties of siderite FeCO3 under high pressure: an ab initio study. Acta Physica Sinica, 2012, 61(9): 097102. doi: 10.7498/aps.61.097102
[18]	Tang Jie, Yang Li-Rong, Wang Xiao-Jun, Zhang Lin, Wei Cheng-Fu, Chen Bo-Wei, Mei Yang. Effects of high pressure on microstructure and properties of bulk (PrNd)xAl0.6Nb0.5Cu0.15B1.05Fe97.7-x alloys. Acta Physica Sinica, 2012, 61(24): 240701. doi: 10.7498/aps.61.240701
[19]	Wang Hai-Yan, Liu Ri-Ping, Ma Ming-Zhen, Gao Ming, Yao Yu-Shu, Wang Wen-Kui. Solidification of FeSi2 alloy under high pressure. Acta Physica Sinica, 2004, 53(7): 2378-2383. doi: 10.7498/aps.53.2378
[20]	Chen Zhi-Qian, Zheng Ren-Rong. . Acta Physica Sinica, 2002, 51(7): 1604-1607. doi: 10.7498/aps.51.1604

Catalog

Vol. 72, Issue 23 - 2023-12-05

Metrics

Abstract views: 2821
PDF Downloads: 105
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板