Preparation and magnetocaloric properties of Gd45Ni30Al15Co10 amorphous alloy

Peng Jia-Xin; Tang Ben-Zhen; Chen Qi-Xin; Li Dong-Mei; Guo Xiao-Long; Xia Lei; Yu Peng

doi:10.7498/aps.70.20211530

Abstract

Materials with excellent magnetocaloric properties are a key factor for the application of magnetic refrigeration technology. In this work, an amorphous ribbon of quaternary Gd₄₅Ni₃₀Al₁₅Co₁₀ alloy is designed and prepared, and the magnetocaloric properties of the alloy are systematically studied. The introduction of Co can improve the thermal stability of the amorphous structure. The Curie temperature and effective magnetic moment of Gd₄₅Ni₃₀Al₁₅Co₁₀ amorphous ribbon are 80 K and 7.21 μ_B, respectively. At 10 K temperature, the saturation magnetization and the coercivity of the alloy reach 173 A·m²·kg^–1 and 0.8 kA·m^–1, respectively, which indicates excellent soft magnetic properties. At 5 T magnetic field, the peak value of magnetic entropy change and relative cooling capacity of Gd₄₅Ni₃₀Al₁₅Co₁₀ amorphous alloy are as high as 10.2 J·kg^–1·K^–1 and 918 J·kg^–1 respectively. The amorphous alloy has typical secondary magnetic phase transition characteristics, and the magnetic refrigeration can be realized in a wide temperature range. The Gd atomic content is less than 50% with low cost, which means that the alloy is an ideal magnetic refrigeration material.

Keywords:

Authors and contacts

1.
Chongqing Key Laboratory of Photo-Electric Functional Materials, College of Physics and Electronic Engineering, Chongqing Normal University, Chongqing 401331, China
2.
Institute of Materials, Shanghai University, Shanghai 200072, China

Corresponding author: Yu Peng, pengyu@cqnu.edu.cn

Funds: Project supported by the National Nature Science Foundation of China (Grant No. 52071043) and the Key Project of Science and Technology Research Program of Chongqing Education Commission of China (Grant No. KJZD-K201900501).

FullText HTML : translate this paragraph

References

[1]	Uporov S A, Ryltsev R E, Bykov V A, Uporova N S, Estemirova S K, Chtchelkatchev N M 2021 J. Alloys Compd. 854 157170 Google Scholar
[2]	Fang Y K, Lai C H, Hsieh C C, Zhao X G, Chang H W, Chang W C, Li W 2010 J. Appl. Phys. 107 09A901 Google Scholar
[3]	Yu P, Zhang J Z, Xia L 2017 J. Mater. Sci. 52 13948 Google Scholar
[4]	王永田, 刘宗德, 易军, 薛志勇 2012 61 056102 Google Scholar Wang Y T, Liu Z D, Yi J, Xue Z Y 2012 Acta Phys. Sin. 61 056102 Google Scholar
[5]	Warburg E 1881 Ann. Phys. 13 141
[6]	Zhao X G, Lai J H, Hsieh C C, Fang Y K, Chang W C, Zhang Z D 2011 J. Appl. Phys. 109 07A911 Google Scholar
[7]	Tang B Z, Liu X P, Li D M, Yu P, Xia L 2020 Chin. Phys. B 29 056401 Google Scholar
[8]	Huang L W, Tang B Z, Ding D, Wang X, Xia L 2019 J. Alloys Compd. 811 152003 Google Scholar
[9]	Pecharsky V K, Gschneidner Jr K A 1997 Phys. Rev. Lett. 78 4494 Google Scholar
[10]	Hu F X, Shen B G, Sun J R, Cheng Z H, Rao G H, Zhang X X 2001 Appl. Phys. Lett. 78 3675 Google Scholar
[11]	Tegus O, Brück E, Buschow K H J, De Boer F R 2002 Nature 415 150 Google Scholar
[12]	De Medeiros Jr L G, De Oliveira N A, Troper A 2010 J. Alloys Compd. 501 177 Google Scholar
[13]	Zhong X C, Tang P F, Gao B B, Min J X, Liu Z W, Zheng Z G, Zeng D C, Yu H Y, Qiu W Q 2013 Sci. China: Phys. Mech. Astron. 56 1096 Google Scholar
[14]	Tang B Z, Huang L W, Song M N, Ding D, Wang X, Xia L 2019 J. Non-Cryst. Solids 522 119589 Google Scholar
[15]	Yu P, Chen L S, Xia L 2018 J. Non-Cryst. Solids 493 82 Google Scholar
[16]	Zhong X C, Tang P F, Liu Z W, Zeng D C, Zheng Z G, Yu H Y, Qiu W Q, Zhang H, Ramanujan R V 2012 J. Appl. Phys. 111 07A919 Google Scholar
[17]	Ma Y F, Tang B Z, Xia L, Ding D 2016 Chin. Phys. Lett. 33 126101 Google Scholar
[18]	霍军涛, 盛威, 王军强 2017 66 176409 Google Scholar Huo J T, Sheng W, Wang J Q 2017 Acta Phys. Sin. 66 176409 Google Scholar
[19]	Wang X, Tang B Z, Wang Q, Yu P, Ding D, Xia L 2020 J. Non-Cryst. Solids 554 120146
[20]	Wang X, Wang Q, Tang B Z, Yu P, Xia L, Ding D 2021 J. Rare Earths 39 998 Google Scholar
[21]	Uporov S, Bykov V, Uporova N 2019 J. Non-Cryst. Solids 521 119506 Google Scholar
[22]	Song M N, Huang L W, Tang B Z, Ding D, Wang X, Xia L 2019 Intermetallics 115 106614 Google Scholar
[23]	Song M N, Huang L W, Tang B Z, Ding D, Zhou Q, Xia L 2020 Mod. Phys. Lett. B 34 2050050
[24]	Yuan F, Du J, Shen B L 2012 Appl. Phys. Lett. 101 032405 Google Scholar
[25]	Ma L Q, Inoue A 1999 Mater. Lett. 38 58 Google Scholar
[26]	Takeuchi A, Inoue A 2000 Mater. Trans. 41 1372 Google Scholar
[27]	Ding D, Tang M B, Xia L 2013 J. Alloys Compd. 581 828 Google Scholar
[28]	Banerjee S K 1964 Phys. Lett. 12 16
[29]	Zhang H Y, Ouyang J T, Ding D, Li H L, Wang J G, Li W H 2018 J. Alloys Compd. 769 186 Google Scholar
[30]	Shen J, Wu J F, Sun J R 2009 J. Appl. Phys. 106 083902 Google Scholar
[31]	Provenzano V, Shapiro A J, Shull R D 2004 Nature 429 853 Google Scholar
[32]	Feng J Q, Li F M, Wang G, Wang J Q, Huo J T 2020 J. Non-Cryst. Solids 536 120004 Google Scholar
[33]	Gao W L, Wang X J, Wang L J, Zhang Y K, Cui J Z 2018 J. Non-Cryst. Solids 484 36 Google Scholar
[34]	Zhang H Y, Li R, Zhang L L, Zhang T 2014 J. Appl. Phys. 115 133903 Google Scholar
[35]	Luo Q, Zhao D Q, Pan M X, Wang W H 2007 Appl. Phys. Lett. 90 211903 Google Scholar
[36]	Franco V, Blázquez J S, Conde A 2006 Appl. Phys. Lett. 89 222512 Google Scholar
[37]	Pecharsky V K, Gschneidner Jr K A 1999 J. Appl. Phys. 86 565 Google Scholar
[38]	Zhong X C, Tang P F, Liu Z W, Zeng D C, Zheng Z G, Yu H Y, Qiu W Q, Zou M 2011 J. Alloys Compd. 509 6889 Google Scholar
[39]	Yu P, Wu C, Cui Y T, Xia L 2016 Mater. Lett. 173 239 Google Scholar
[40]	Xia L, Tang M B, Chan K C, Dong Y D 2014 J. Appl. Phys. 115 223904 Google Scholar
[41]	Wu C, Ding D, Xia L 2016 Chin. Phys. Lett. 33 016102 Google Scholar
[42]	Belo J H, Amaral J S, Pereira A M, Amara V S, Araújo J P 2012 Appl. Phys. Lett. 100 242407 Google Scholar

Cited By

图 1 Gd₄₅Ni₃₀Al₁₅Co₁₀合金条带的XRD图像, 插图为合金条带的DSC曲线

Figure 1. XRD pattern of the Gd₄₅Ni₃₀Al₁₅Co₁₀ alloy ribbon, the inset shows DSC trance of the alloy ribbon.

DownLoad: Full-Size Img PowerPoint

图 2 (a) Gd₄₅Ni₃₀Al₁₅Co₁₀非晶合金在0.03 T外加磁场下的M-T曲线, 插图为(dM/dT)-T曲线; (b) Gd₄₅Ni₃₀Al₁₅Co₁₀非晶合金磁场强度/磁化强度的温度依赖(H/M-T)曲线

Figure 2. (a) The M-T curve of Gd₄₅Ni₃₀Al₁₅Co₁₀ amorphous ribbon under a field of 0.03 T, the inset shows (dM/dT)-T curve; (b) the H/M-T curve for the Gd₄₅Ni₃₀Al₁₅Co₁₀ amorphous ribbon.

DownLoad: Full-Size Img PowerPoint

图 3 Gd₄₅Ni₃₀Al₁₅Co₁₀非晶合金在5 T外加磁场下10 和160 K的磁滞回线, 插图为10 K温度下磁滞回线的放大部分

Figure 3. The hysteresis loops of Gd₄₅Ni₃₀Al₁₅Co₁₀ amorphous alloy at 10 and 160 K under a field of 5 T, the inset shows the enlarged part of magnetic hysteresis loop at 10 K.

DownLoad: Full-Size Img PowerPoint

图 4 (a) Gd₄₅Ni₃₀Al₁₅Co₁₀非晶条带在不同温度下的绝热M-H曲线; (b) 合金的Arrott曲线

Figure 4. (a) The adiabatic M-H curves of the Gd₄₅Ni₃₀Al₁₅Co₁₀ amorphous ribbon at different temperatures; (b) arrott curves of the amorphous ribbon.

DownLoad: Full-Size Img PowerPoint

图 5 (a) Gd₄₅Ni₃₀Al₁₅Co₁₀非晶条带在不同磁场下磁熵变的温度依赖关系; (b) ln($-\Delta S^{{\rm{peak}}} _{\rm{m}} $)与lnH的关系图, 插图为指数n随温度变化n-T曲线

Figure 5. (a) Temperature dependence of magnetic entropy changes (–ΔS_m) of the Gd₄₅Ni₃₀Al₁₅Co₁₀ amorphous ribbon under different magnetic field; (b) the ln($-\Delta S^{{\rm{peak}}} _{\rm{m}} $) vs. lnH plot of the amorphous ribbon, the inset shows the n-T curve of the amorphous ribbon.

DownLoad: Full-Size Img PowerPoint

表 1 Gd₅₅Ni₃₀Al₁₅和Gd₄₅Ni₃₀Al₁₅Co₁₀非晶条带的热力学参数

Table 1. Thermodynamics parameters of the Gd₅₅Ni₃₀Al₁₅ and Gd₄₅Ni₃₀Al₁₅Co₁₀ amorphous ribbons.

合金	T_g/K	T_x/K	∆T_x/K	T_m/K	T_l/K	γ
Gd₅₅Ni₃₀Al₁₅	576	620	44	911	962	0.40
Gd₄₅Ni₃₀Al₁₅Co₁₀	525	605	80	930	1231	0.35

DownLoad: CSV

表 2 Gd₄₅Ni₃₀Al₁₅Co₁₀和部分Gd基非晶态(A)、晶态(C)合金的T_c、5 T磁场下的$-\Delta S^{{\rm{peak}}} _{\rm{m}} $和RCP值

Table 2. T_c, $-\Delta S^{{\rm{peak}}} _{\rm{m}} $, and RCP under 5 T applied field of the Gd₄₅Ni₃₀Al₁₅Co₁₀ amorphous alloy and some other Gd-based amorphous and crystalline alloys.

合金	结构	T_c /K	$-\Delta S^{{\rm{peak}}} _{\rm{m}} $/ (J·kg^–1·K^–1)	RCP/ (J·kg^–1)	参考文献
Gd₄₅Ni₃₀Al₁₅Co₁₀	A	80	10.2	918	本文
Gd₆₅Ni₃₅	A	122	6.9	524	[38]
Gd₆₈Ni₃₂	A	124	8	583	[38]
Gd₇₁Ni₂₉	A	122	9	724	[38]
Gd₆₀Ni₃₇Co₃	A	135	10.42	860	[17]
Gd₃₄Ni₃₃Al₃₃	A	38	11.06	—	[20]
Gd₅₅Ni₁₅Al₃₀	A	70	6.12	606	[24]
Gd₅₅Ni₂₀Al₂₅	A	71	7.98	782	[24]
Gd₅₅Ni₂₅Al₂₀	A	75	8.49	806	[24]
Gd₅₅Ni₃₀Al₁₅	A	83	9.25	851	[24]
Gd₃₄Ni₂₂Co₁₁Al₃₃	A	54	9.91	—	[39]
Gd₅₅Al₂₀Co₂₀Ni₅	A	105	9.8	615	[40]
Gd₆₀Al₂₅(NiCo)₁₅	A	91	6.31	890	[21]
Gd	C	293	9.7	556	[30]
Gd₅Si₂Ge₂	C	276	18.6	305	[31]

DownLoad: CSV

map

[1]	Uporov S A, Ryltsev R E, Bykov V A, Uporova N S, Estemirova S K, Chtchelkatchev N M 2021 J. Alloys Compd. 854 157170 Google Scholar
[2]	Fang Y K, Lai C H, Hsieh C C, Zhao X G, Chang H W, Chang W C, Li W 2010 J. Appl. Phys. 107 09A901 Google Scholar
[3]	Yu P, Zhang J Z, Xia L 2017 J. Mater. Sci. 52 13948 Google Scholar
[4]	王永田, 刘宗德, 易军, 薛志勇 2012 61 056102 Google Scholar Wang Y T, Liu Z D, Yi J, Xue Z Y 2012 Acta Phys. Sin. 61 056102 Google Scholar
[5]	Warburg E 1881 Ann. Phys. 13 141
[6]	Zhao X G, Lai J H, Hsieh C C, Fang Y K, Chang W C, Zhang Z D 2011 J. Appl. Phys. 109 07A911 Google Scholar
[7]	Tang B Z, Liu X P, Li D M, Yu P, Xia L 2020 Chin. Phys. B 29 056401 Google Scholar
[8]	Huang L W, Tang B Z, Ding D, Wang X, Xia L 2019 J. Alloys Compd. 811 152003 Google Scholar
[9]	Pecharsky V K, Gschneidner Jr K A 1997 Phys. Rev. Lett. 78 4494 Google Scholar
[10]	Hu F X, Shen B G, Sun J R, Cheng Z H, Rao G H, Zhang X X 2001 Appl. Phys. Lett. 78 3675 Google Scholar
[11]	Tegus O, Brück E, Buschow K H J, De Boer F R 2002 Nature 415 150 Google Scholar
[12]	De Medeiros Jr L G, De Oliveira N A, Troper A 2010 J. Alloys Compd. 501 177 Google Scholar
[13]	Zhong X C, Tang P F, Gao B B, Min J X, Liu Z W, Zheng Z G, Zeng D C, Yu H Y, Qiu W Q 2013 Sci. China: Phys. Mech. Astron. 56 1096 Google Scholar
[14]	Tang B Z, Huang L W, Song M N, Ding D, Wang X, Xia L 2019 J. Non-Cryst. Solids 522 119589 Google Scholar
[15]	Yu P, Chen L S, Xia L 2018 J. Non-Cryst. Solids 493 82 Google Scholar
[16]	Zhong X C, Tang P F, Liu Z W, Zeng D C, Zheng Z G, Yu H Y, Qiu W Q, Zhang H, Ramanujan R V 2012 J. Appl. Phys. 111 07A919 Google Scholar
[17]	Ma Y F, Tang B Z, Xia L, Ding D 2016 Chin. Phys. Lett. 33 126101 Google Scholar
[18]	霍军涛, 盛威, 王军强 2017 66 176409 Google Scholar Huo J T, Sheng W, Wang J Q 2017 Acta Phys. Sin. 66 176409 Google Scholar
[19]	Wang X, Tang B Z, Wang Q, Yu P, Ding D, Xia L 2020 J. Non-Cryst. Solids 554 120146
[20]	Wang X, Wang Q, Tang B Z, Yu P, Xia L, Ding D 2021 J. Rare Earths 39 998 Google Scholar
[21]	Uporov S, Bykov V, Uporova N 2019 J. Non-Cryst. Solids 521 119506 Google Scholar
[22]	Song M N, Huang L W, Tang B Z, Ding D, Wang X, Xia L 2019 Intermetallics 115 106614 Google Scholar
[23]	Song M N, Huang L W, Tang B Z, Ding D, Zhou Q, Xia L 2020 Mod. Phys. Lett. B 34 2050050
[24]	Yuan F, Du J, Shen B L 2012 Appl. Phys. Lett. 101 032405 Google Scholar
[25]	Ma L Q, Inoue A 1999 Mater. Lett. 38 58 Google Scholar
[26]	Takeuchi A, Inoue A 2000 Mater. Trans. 41 1372 Google Scholar
[27]	Ding D, Tang M B, Xia L 2013 J. Alloys Compd. 581 828 Google Scholar
[28]	Banerjee S K 1964 Phys. Lett. 12 16
[29]	Zhang H Y, Ouyang J T, Ding D, Li H L, Wang J G, Li W H 2018 J. Alloys Compd. 769 186 Google Scholar
[30]	Shen J, Wu J F, Sun J R 2009 J. Appl. Phys. 106 083902 Google Scholar
[31]	Provenzano V, Shapiro A J, Shull R D 2004 Nature 429 853 Google Scholar
[32]	Feng J Q, Li F M, Wang G, Wang J Q, Huo J T 2020 J. Non-Cryst. Solids 536 120004 Google Scholar
[33]	Gao W L, Wang X J, Wang L J, Zhang Y K, Cui J Z 2018 J. Non-Cryst. Solids 484 36 Google Scholar
[34]	Zhang H Y, Li R, Zhang L L, Zhang T 2014 J. Appl. Phys. 115 133903 Google Scholar
[35]	Luo Q, Zhao D Q, Pan M X, Wang W H 2007 Appl. Phys. Lett. 90 211903 Google Scholar
[36]	Franco V, Blázquez J S, Conde A 2006 Appl. Phys. Lett. 89 222512 Google Scholar
[37]	Pecharsky V K, Gschneidner Jr K A 1999 J. Appl. Phys. 86 565 Google Scholar
[38]	Zhong X C, Tang P F, Liu Z W, Zeng D C, Zheng Z G, Yu H Y, Qiu W Q, Zou M 2011 J. Alloys Compd. 509 6889 Google Scholar
[39]	Yu P, Wu C, Cui Y T, Xia L 2016 Mater. Lett. 173 239 Google Scholar
[40]	Xia L, Tang M B, Chan K C, Dong Y D 2014 J. Appl. Phys. 115 223904 Google Scholar
[41]	Wu C, Ding D, Xia L 2016 Chin. Phys. Lett. 33 016102 Google Scholar
[42]	Belo J H, Amaral J S, Pereira A M, Amara V S, Araújo J P 2012 Appl. Phys. Lett. 100 242407 Google Scholar

[1]	Wang Zhuang, Jin Fan, Li Wei, Ruan Jia-Yi, Wang Long-Fei, Wu Xue-Lian, Zhang Yi-Kun, Yuan Chen-Chen. Design and fabrication of GdHoErCoNiAl metallic glasses with excellent glass forming capability and magnetocaloric effects. Acta Physica Sinica, 2024, 73(21): 217101. doi: 10.7498/aps.73.20241132
[2]	Lin Yuan, Hu Feng-Xia, Shen Bao-Gen. Phase transition regulation, magnetocaloric effect, and abnormal thermal expansion. Acta Physica Sinica, 2023, 72(23): 237501. doi: 10.7498/aps.72.20231118
[3]	Zhang Yan, Zong Shuo-Tong, Sun Zhi-Gang, Liu Hong-Xia, Chen Feng-Hua, Zhang Ke-Wei, Hu Ji-Fan, Zhao Tong-Yun, Shen Bao-Gen. Magnetic and anisotropic magnetocaloric effects of HoCoSi fast quenching ribbons. Acta Physica Sinica, 2022, 71(16): 167501. doi: 10.7498/aps.71.20220683
[4]	Zhang Peng, Piao Hong-Guang, Zhang Ying-De, Huang Jiao-Hong. Research progress of critical behaviors and magnetocaloric effects of perovskite manganites. Acta Physica Sinica, 2021, 70(15): 157501. doi: 10.7498/aps.70.20210097
[5]	Su Wen-Xia, Lu Hai-Ming, Zeng Zi-Rui, Zhang Yi-Fei, Liu Jian, Xu Kun, Wang Dun-Hui, Du You-Wei. High-throughput computation on relationship between composition and magnetic phase transition temperature of LaFe_11.5Si_1.5-based magnetic refrigeration materials. Acta Physica Sinica, 2021, 70(20): 207501. doi: 10.7498/aps.70.20211085
[6]	Yang Jing-Jie, Zhao Jin-Liang, Xu Lei, Zhang Hong-Guo, Yue Ming, Liu Dan-Min, Jiang Yi-Jian. Influences of interstitial atoms H, B and C on magnetic properties and magnetocaloric effect in LaFe11.5Al1.5 compound. Acta Physica Sinica, 2018, 67(7): 077501. doi: 10.7498/aps.67.20172250
[7]	Zhang Hu, Xing Cheng-Fen, Long Ke-Wen, Xiao Ya-Ning, Tao Kun, Wang Li-Chen, Long Yi. Linear dependence of magnetocaloric effect on magnetic field in Mn0.6Fe0.4NiSi0.5Ge0.5 and Ni50Mn34Co2Sn14 with first-order magnetostructural transformation. Acta Physica Sinica, 2018, 67(20): 207501. doi: 10.7498/aps.67.20180927
[8]	Hao Zhi-Hong, Wang Hai-Ying, Zhang Quan, Mo Zhao-Jun. Magnetic and magnetocaloric effects of Eu_0.9M_0.1TiO₃ (M=Ca, Sr, Ba, La, Ce, Sm) compounds. Acta Physica Sinica, 2018, 67(24): 247502. doi: 10.7498/aps.67.20181750
[9]	Sun Xiao-Dong, Xu Bao, Wu Hong-Ye, Cao Feng-Ze, Zhao Jian-Jun, Lu Yi. Magnetic entropy change and electrical transport properties of rare earth Tb doped manganites La4/3Sr5/3Mn2O7. Acta Physica Sinica, 2017, 66(15): 157501. doi: 10.7498/aps.66.157501
[10]	Huo Jun-Tao, Sheng Wei, Wang Jun-Qiang. Magnetocaloric effects and magnetic regenerator performances in metallic glasses. Acta Physica Sinica, 2017, 66(17): 176409. doi: 10.7498/aps.66.176409
[11]	Zheng Xin-Qi, Shen Jun, Hu Feng-Xia, Sun Ji-Rong, Shen Bao-Gen. Research progress in magnetocaloric effect materials. Acta Physica Sinica, 2016, 65(21): 217502. doi: 10.7498/aps.65.217502
[12]	Gao Xin-Qiang, Shen Jun, He Xiao-Nan, Tang Cheng-Chun, Dai Wei, Li Ke, Gong Mao-Qiong, Wu Jian-Feng. Numerical simulation of a hybrid magnetic refrigeration combined with high pressure Stirling regenerative refrigeration effect. Acta Physica Sinica, 2015, 64(21): 210201. doi: 10.7498/aps.64.210201
[13]	Wang Fang, Yuan Feng-Ying, Wang Jin-Zhi. Magnetic properties and magnetocaloric effect in Mn42Al50-xFe8+x alloys. Acta Physica Sinica, 2013, 62(16): 167501. doi: 10.7498/aps.62.167501
[14]	Cai Pei-Yang, Feng Shang-Shen, Chen Wei-Ping, Xue Shuang-Xi, Li Zhi-Gang, Zhou Ying, Wang Hai-Bo, Wang Gu-Ping. Magnetic entropy change and magnetic-field-induced strain in polycrystalline Ni47Mn32Ga21 alloy. Acta Physica Sinica, 2011, 60(10): 107501. doi: 10.7498/aps.60.107501
[15]	Zhang Hao-Lei, Li Zhe, Qiao Yan-Fei, Cao Shi-Xun, Zhang Jin-Cang, Jing Chao. Martensitic transformation and magnetocaloric effect in Ni-Co-Mn-Sn Heusler alloy. Acta Physica Sinica, 2009, 58(11): 7857-7863. doi: 10.7498/aps.58.7857
[16]	Bao Bing-Hao, Ren Nai-Fei, Wang Guo-Yu. The influence of anisotropic fields on stress-impedance effect in amorphous alloys. Acta Physica Sinica, 2008, 57(4): 2519-2523. doi: 10.7498/aps.57.2519
[17]	Jing Chao, Chen Ji-Ping, Li Zhe, Cao Shi-Xun, Zhang Jin-Cang. Martensitic transformation and magnetocaloric effect in Ni50Mn35In15 Heusler alloy. Acta Physica Sinica, 2008, 57(7): 4450-4455. doi: 10.7498/aps.57.4450
[18]	Zhao He-Yun, Kan Jia-De, Liu Qing-Ju, Liu Zuo-Quan. Novel physical effects in amorphous alloy crystallization induced by shock wave. Acta Physica Sinica, 2005, 54(4): 1711-1718. doi: 10.7498/aps.54.1711
[19]	Shen Jun, Li Yang-Xian, Hu Feng-Xia, Wang Guang-Jun, Zhang Shao-Ying. Magnetic properties and magnetic entropy change of Ce2Fe16Al near Curie temperature. Acta Physica Sinica, 2003, 52(5): 1250-1254. doi: 10.7498/aps.52.1250
[20]	CHEN WEI, ZHONG WEI, PAN CHENG, CHANG HONG, DU YOU-WEI. CURIE TEMPERATURE AND MAGNETOCALORIC EFFECT OF POLYCRYSTALLINE La0.8-xCa0.2MnO3. Acta Physica Sinica, 2001, 50(2): 319-323. doi: 10.7498/aps.50.319

Catalog

Vol. 71, Issue 2 - 2022-01-20

Metrics

Abstract views: 5171
PDF Downloads: 89
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板

Preparation and magnetocaloric properties of Gd₄₅Ni₃₀Al₁₅Co₁₀ amorphous alloy

Abstract

Authors and contacts

Corresponding author: Yu Peng, pengyu@cqnu.edu.cn

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Authors

Referees

About Journal

About

Search

Article

留言板