Design and fabrication of GdHoErCoNiAl metallic glasses with excellent glass forming capability and magnetocaloric effects

Wang Zhuang; Jin Fan; Li Wei; Ruan Jia-Yi; Wang Long-Fei; Wu Xue-Lian; Zhang Yi-Kun; Yuan Chen-Chen

doi:10.7498/aps.73.20241132

Abstract

In this work, Gd_20+2xHo_20–xEr_20–xCo₂₀Ni₁₀Al₁₀ (x = 0, 5, 10) high-entropy metallic glasses (MGs) with a critical diameter of 2 mm are successfully designed and fabricated by substituting Gd, Ho and Er. The effects of type and content of rare-earth (RE) elements on the microstructure, thermodynamic behaviors, and magnetocaloric effect (MCE) are investigated systematically. The amorphous structures of the ribbons and as-cast rods are confirmed by X-ray diffraction (XRD) with Cu Kα radiation (2θ = 20°–80°). The atomic-scale ordered configurations are examined by using high-resolution transmission electron microscope (HRTEM). Thermal analysis is carried out on differential scanning calorimeter (DSC) with a heating rate of 20 K/min by using ribbons. The magnetic measurements are conducted by using magnetometer in a temperature range of 5–180 K. According to DSC traces, it is suggested that as Ho and Er are replaced by Gd, the thermal stability of MGs slightly decreases, for example, both glass transition temperature (T_g) and initial crystallization temperature (T_x) decrease gradually, meanwhile the liquidus temperature (T_l) increases, which results in a reduction of glass-forming ability criteria such as the reduced glass transition temperatures T_rg (T_rg = T_g/T_l), γ (γ = T_x/(T_g + T_l)), and γ_m (γ_m = (2T_x – T_g)/T_l), thermodynamically. The analyses based on XRD and HRTEM show that the degree of order in MGs decreases with Gd content increasing, which facilitates the glass formation. The magnetocaloric parameters such as Curie temperature (T_c), maximum magnetic entropy change ($ | {\Delta S_{\text{M}}^{{\text{pk}}}} | $) and relative cooling power (RCP) all increase gradually with the addition of Gd. The Gd₄₀Ho₁₀Er₁₀CoNiAl exhibits the best refrigeration performance in all studied systems, where the peak value of $ |{\Delta S}_{{\mathrm{M}}}| $ is 8.31 J/(kg·K) and RCP is 740.82 J/kg. The results indicate that MCEs of MGs including RCP, T_c and $ | {\Delta S_{\text{M}}^{{\text{pk}}}} | $, mainly depend on the de Gennes factor rather than the effective magnetic moment, while thermodynamic properties are more affected by the f-d hybridization effect. As the number of 4f electrons increases, the thermal stability increases with the degree f-d orbital hybridization increasing. In summary, the RE-based MG with high thermal stability and adjustable T_c can be achieved by the RE substitution via adjusting the number of 4f electrons.

Keywords:

rare-earth based high-entropy metallic glasses /
thermodynamic properties /
magnetocaloric effect /
glass forming ability

Authors and contacts

1.
School of Materials Science and Engineering, Southeast University, Nanjing 211189, China
2.
School of Materials and Environmental Engineering, Hangzhou Dianzi University, Hangzhou 310018, China
3.
School of Materials Science and Engineering, Anhui University of Technology, Ma'anshan 243032, China

Corresponding author: Yuan Chen-Chen, yuanchenchenneu@hotmail.com

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 52071078) and the “Zhishan” Scholars Programs of Southeast University, China (Grant No. 2242021R41158).

FullText HTML : translate this paragraph

Supplements

2024年24期217101补充材料.pdf

References

[1]	Gschneidner K A, Pecharsky V, Tsokol A 2005 Rep. Prog. Phys. 68 1479 Google Scholar
[2]	Uporov S, Ryltsev R, Bykov V, Uporova N, Estemirova S K, Chtchelkatchev N 2021 J. Alloys Compd. 854 157170 Google Scholar
[3]	Warburg E 1881 Ann. Der. Phys. 249 141 Google Scholar
[4]	Debye P 1926 Ann. Der. Phys. 386 1154 Google Scholar
[5]	Giauque W F 1927 J. Am. Chem. Soc. 49 1864 Google Scholar
[6]	Pecharsky V K, Gschneidner Jr K A 1997 Phys. Rev. Lett. 78 4494 Google Scholar
[7]	Pecharsky V K, Gschneidner Jr K A 1997 Appl. Phys. Lett. 70 3299 Google Scholar
[8]	Jia Y S, Zhao X Y, Liu X L, Li L W 2020 J. Alloys Compd. 813 152177 Google Scholar
[9]	Zhang Y K, Zhu J, Li S, Zhang B, Wang Y M, Wang J, Ren Z M 2022 J. Alloys Compd. 895 162633 Google Scholar
[10]	Wang Q, Pan L L, Tang B Z, Ding D, Xia L 2022 J. Non-Cryst. Solids 580 121394 Google Scholar
[11]	Luo Q, Zhao D Q, Pan M X, Wang W H 2007 Appl. Phys. Lett. 90 211903 Google Scholar
[12]	Lim X 2016 Nature 533 306 Google Scholar
[13]	Huo J T, Huo L S, Li J W, Men H, Wang X M, Inoue A, Chang C T, Wang J Q, Li R W 2015 J. Appl. Phys. 117 073902 Google Scholar
[14]	Huo J T, Huo L S, Men H, Wang X M, Inoue A, Wang J, Chang C T, Li R W 2015 Intermetallics 58 31 Google Scholar
[15]	Sheng W, Wang J Q, Wang G, Huo J T, Wang X, Li R W 2018 Intermetallics 96 79 Google Scholar
[16]	Li J W, Xue L, Yang W, Yuan C, Huo J T, Shen B 2018 Intermetallics 96 90 Google Scholar
[17]	Zhang Y K, Zhu J, Li S, Wang J, Ren Z M 2022 J. Mater. Sci. Technol. 102 66 Google Scholar
[18]	Li L W, Xu C, Yuan Y, Zhou S Q 2018 Materialia 3 74 Google Scholar
[19]	Yang Y, Chen Y, Yu P, Qian L J, Wu F F, Cui Y T, Wu Z M, Ding D, Xia L 2015 J. Nanosci. Nanotechnol. 15 3295 Google Scholar
[20]	Li L W, Xu C, Yuan Y, Zhou S Q 2018 Mater. Res. Lett. 6 413 Google Scholar
[21]	Dong Z Q, Wang Z J, Yin S H 2020 J. Magn. Magn. Mater. 514 167270 Google Scholar
[22]	Luo L, Shen H X, Bao Y, Yin H B, Jiang S D, Huang Y J, Guo S Y, Gao S, Xing D W, Li Z, Sun J F 2020 J. Magn. Magn. Mater. 507 166856 Google Scholar
[23]	Zhang Y K, Xu P, Zhu J, Yan S, Zhang J, Li L W 2023 Mater. Today Phys. 32 101031 Google Scholar
[24]	Zhang Y K, Zhu J, Hao Z, Hao W, Mo Z, Li L W 2023 Mater. Des. 229 111894 Google Scholar
[25]	Civan E, Sarlar K, Kucuk I 2017 Philos. Mag. 97 1464 Google Scholar
[26]	Johnson F, Shull R D 2006 J. Appl. Phys. 99 08K909 Google Scholar
[27]	Kucuk I, Sarlar K, Adam A, Civan E 2016 Philos. Mag. 96 3120 Google Scholar
[28]	Wu K N, Liu C, Li Q, Huo J T, Li M C, Chang C T, Sun Y F 2019 J. Magn. Magn. Mater. 489 165404 Google Scholar
[29]	Wang G F, Li H L, Zhao Z R, Zhang X F 2017 J. Alloys Compd. 692 793 Google Scholar
[30]	Lv Y B, Chen Q J, Huang Y L 2019 J. Rare Earth. 37 404 Google Scholar
[31]	Guo D, Moreno-Ramírez L M, Romero-Muñiz C, Zhang Y K, Law J Y, Franco V, Wang J, Ren Z M 2021 Sci. China Mater. 64 2846 Google Scholar
[32]	Xue L, Shao L L, Li Z, Han Z D, Zhang B S, Huo J T, Wang X M, Zhu S S, Qian B, Cheng J B, Shen B L 2022 J. Mater. Res. Technol. 18 5301 Google Scholar
[33]	Lindner N, Śniadecki Z, Kołodziej M, Grenèche J M, Marcin J, Škorvánek I, Idzikowski B 2022 J. Mater. Sci. 57 553 Google Scholar
[34]	Zheng Z G, Qiu Z G, Zeng D C 2019 Mater. Res. Express 6 096109 Google Scholar
[35]	Law J Y, Ramanujan R V, Franco V 2010 J. Alloys Compd. 508 14 Google Scholar
[36]	糜晓磊, 胡亮, 武博文, 龙强, 魏炳波 2024 73 097102 Google Scholar Mi X L, Hu L, Wu B W, Long Q, Wei B B 2024 Acta Phys. Sin. 73 097102 Google Scholar
[37]	Xue L, Shao L L, Luo Q, Shen B L 2019 J. Alloys Compd. 790 633 Google Scholar
[38]	Wei S J, Shen H X, Zhang L Y, Luo L, Tang X X, Sun J F, Li X Q 2024 Rare Metals 43 1234 Google Scholar
[39]	Lu S F, Ma L, Wang J, Du Y S, Li L W, Zhao J T, Rao G H 2021 J. Alloys Compd. 874 159918 Google Scholar
[40]	Yeh J W 2013 JOM 65 1759 Google Scholar
[41]	Ma E, Wu X L 2019 Nat. Commun. 10 5623 Google Scholar
[42]	Gu J L, Luan H W, Zhao S F, Bu H T, Si J J, Shao Y, Yao K F 2020 Mater. Sci. Eng. A 786 139417 Google Scholar
[43]	Xue L, Shao L L, Zhang B S, Li Z, Cheng J B, Shen B L 2024 J. Rare Earth. 42 129 Google Scholar
[44]	Pang C M, Yuan C C, Chen L, Xu H, Guo K, He J C, Li Y, Wei M S, Wang X M, Huo J T, Shen B L 2020 J. Non-Cryst. Solids 549 120354 Google Scholar
[45]	Pang C M, Chen L, Xu H, Guo W, Lv Z W, Huo J T, Cai M J, Shen B L, Wang X L, Yuan C C 2020 J. Alloys Compd. 827 154101 Google Scholar
[46]	Wang X, Tang B Z, Wang Q, Yu P, Ding D, Xia L 2020 J. Non-Cryst. Solids 544 120146 Google Scholar
[47]	Hao F, Lin H, Zhou C, Liu Y Z, Li J B 2011 Phys. Chem. Chem. Phys. 13 15918 Google Scholar
[48]	Wang Q, Liu C T, Yang Y, Liu J B, Dong Y D, Lu J 2014 Sci. Rep. 4 4648 Google Scholar
[49]	Imafuku M, Yaoita K, Sato S, Zhang W, Inoue A, Waseda Y 2001 Mater. Sci. Eng. A 304 660 Google Scholar
[50]	Wang W H 2009 Adv. Mater. 21 4524 Google Scholar
[51]	Yuan C C, Shen X, Cui J, Gu L, Yu R C, Xi X K 2012 Appl. Phys. Lett. 101 021902 Google Scholar
[52]	Liu Z H, Zhang Y K J, Liu E K, Liu G D, Ma X Q, Wu G H 2015 J. Phys. D Appl. Phys. 48 325001 Google Scholar
[53]	Yuan C C, Yang F, Xi X K, Shi C L, Holland-Moritz D, Li M Z, Hu F, Shen B L, Wang X L, Meyer A, Wang W H 2020 Mater. Today 32 26 Google Scholar
[54]	Jin F, Pang C M, Wang X M, Yuan C C 2023 J. Non-Cryst. Solids 600 121992 Google Scholar
[55]	Inoue A 2000 Acta Mater. 48 279 Google Scholar
[56]	Lu Z P, Tan H, Ng S C, Li Y 2000 Scr. Mater. 42 667 Google Scholar
[57]	Lu Z P, Liu C T 2002 Acta Mater. 50 3501 Google Scholar
[58]	Lu Z P, Liu C T 2003 Phys. Rev. Lett. 91 115505 Google Scholar
[59]	Du X H, Huang J C, Liu C T, Lu Z P 2007 J. Appl. Phys. 101 086108 Google Scholar
[60]	Zhang W, Jia F, Zhang X, Xie G, Inoue A 2010 Metall. Mater. Trans. A 41 1685 Google Scholar
[61]	Zhang Y K, Guo D, Wu B B, Wang H F, Guan R G, Li X, Ren Z M 2020 J. Appl. Phys. 127 033905 Google Scholar
[62]	Yin H, Wang J Q, Huang Y, Shen H X, Guo S, Fan H, Huo J T, Sun J 2023 J. Mater. Sci. Technol. 149 167 Google Scholar
[63]	Zhong H X, Li K, Zhang Q, Wang J, Meng F L, Wu Z J, Yan J M, Zhang X B 2016 NPG Asia Mater. 8 e308 Google Scholar
[64]	Franco V, Blázquez J, Conde A 2006 J. Appl. Phys. 89 222512 Google Scholar
[65]	Zhang H Y, Li R, Zhang L L, Zhang T 2014 J. Appl. Phys. 115 133903 Google Scholar
[66]	Yosida K 1957 Phys. Rev. 107 396 Google Scholar
[67]	Banerjee B 1964 Phys. Lett. 12 16 Google Scholar
[68]	Franco V, Conde A, Romero-Enrique J M, Blázquez J S 2008 J. Phys. Condens. Matter 20 285207 Google Scholar
[69]	Oesterreicher H, Parker F 1984 J. Appl. Phys. 55 4334 Google Scholar
[70]	Guo D, Zhang Y K, Geng S H, Xu H, Ren Z M, Wilde G 2018 J. Mater. Sci. 53 9816 Google Scholar
[71]	Zhang Y K, Li H D, Geng S H, Lu X G, Wilde G 2019 J. Alloys Compd. 770 849 Google Scholar
[72]	Dong Z Q, Yin S H 2020 J. Magn. Magn. Mater. 495 165888 Google Scholar
[73]	Huo J T, Zhao D Q, Bai H Y, Axinte E, Wang W H 2013 J. Non-Cryst. Solids 359 1 Google Scholar

Cited By

图 1 Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10)非晶合金条带(a)和铸棒(b)的XRD图谱

Figure 1. XRD patterns of Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10) ribbons (a) and rods (b).

DownLoad: Full-Size Img PowerPoint

图 2 Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10)非晶合金条带HRTEM图(a)—(c)及选区二维自相关处理图(d)—(f), 插图为选区电子衍射图

Figure 2. (a)−(c) HRTEM image of Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10) ribbons and (d)−(f) 2D auto-correlation processing image of selected area. The inset shows the selected area electron diffraction pattern.

DownLoad: Full-Size Img PowerPoint

图 3 (a) Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10) 非晶合金条带DSC图; (b) T_g和T_x与4f电子数的关系图

Figure 3. (a) DSC traces of Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10) ribbons; (b) T_g and T_x as a function of 4f electron number.

DownLoad: Full-Size Img PowerPoint

图 4 (a) Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10)非晶合金200 Oe外场场冷和零场冷磁化强度与温度关系图; (b) 200 Oe外场下的$ {1 {/ } {\chi \left( T \right)}} $随温度变化曲线; (c)场冷曲线求导图; (d) T_c与G因子的关系

Figure 4. (a) Temperature dependence of ZFC and FC magnetization curves (M-T) of Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10) under 200 Oe; (b) $ {1 {/ } {\chi \left( T \right)}} $ curves at H = 200 Oe; (c) dM/dT-T curves; (d) T_c as a function of G factor.

DownLoad: Full-Size Img PowerPoint

图 5 Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10)非晶合金不同温度下磁化强度与外场关系图(a)—(c)和Arrott图(d)—(f); 不同外场下的磁熵变与温度关系图(g)—(i)和$|\Delta S_{\text{M}}/ | {\Delta S_{\text{M}}^{{\text{pk}}}} |\text{-}\theta$图(j)—(l)

Figure 5. Isothermal magnetization curves (M-H ) (a)–(c) and Arrott plots (d)–(f); magnetic entropy changes as a function of temperature (|ΔS_M|-T ) (g)–(i) and $|\Delta S_{\text{M}}/ | {\Delta S_{\text{M}}^{{\text{pk}}}} |\text{-}\theta$ curves (j)–(l) for Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10).

DownLoad: Full-Size Img PowerPoint

图 6 Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10)非晶合金5 T外场下磁熵变与温度关系图, 插图为3种合金相对制冷量值

Figure 6. Magnetic entropy changes as a function of temperature (|ΔS_M|-T) of Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10) under an applied field of 5 T. The inset is RCP value.

DownLoad: Full-Size Img PowerPoint

图 7 Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10)非晶合金(a)峰值磁熵变和(b)相对制冷能力与外场关系图, 实线为指数函数拟合曲线

Figure 7. (a) Maximum magnetic entropy changes and (b) relative cooling power as a function of applied field ($ | {\Delta S_{\text{M}}^{{\text{pk}}}} | $/RCP-H ) for Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10). The solid lines are the exponential function fitting curves.

DownLoad: Full-Size Img PowerPoint

图 8 (a) T_c, (b) $ | {\Delta S_{\text{M}}^{{\text{pk}}}} | $和(c) RCP与G因子的关系

Figure 8. (a) T_c, (b) $ | {\Delta S_{\text{M}}^{{\text{pk}}}} | $, and (c) RCP as a function of G factor.

DownLoad: Full-Size Img PowerPoint

图 9 (a) T_g, (b) T_x和(c) ΔT_x与4f层电子数的关系

Figure 9. (a) T_g, (b) T_x, and (c) ΔT_x as a function of 4f electron number.

DownLoad: Full-Size Img PowerPoint

表 1 Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10)非晶合金热力学参数(R为气体常数)

Table 1. Thermodynamic parameters and GFA criteria of Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10).

Compositions	ΔS_conf	4f electron number	T_g/K	T_x/K	T_l/K	ΔT_x/K	T_rg	γ	γ_m
x = 0	1.748R	9.33	560.6	616.3	973.0	55.7	0.576	0.402	0.691
x = 5	1.713R	8.75	554.8	613.9	989.6	59.1	0.561	0.398	0.680
x = 10	1.609R	8.17	551.3	605.3	985.6	54.0	0.559	0.394	0.669

DownLoad: CSV

表 2 Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10)非晶合金的磁热参数

Table 2. Magnetocaloric parameters of Gd_20+2xHo_20–xEr_20–xCoNiAl (x = 0, 5, 10).

x	ΔS_conf	G-factor	T_c/K	θ/K	μ_eff/μ_B(实验)	μ_eff/μ_B(理论)	$ \| {\Delta S_{\text{M}}^{{\text{pk}}}} \| $/(J·kg^–1·K^–1)	δT_FWHM/K	RCP/(J·kg^–1)	n	N
0	1.748R	7.60	65	17.968	7.18	7.75	8.21	73.99	607.20	0.80	1.00
5	1.713R	9.64	67	77.788	6.68	7.45	8.28	80.43	665.67	0.78	1.00
10	1.609R	11.68	81	92.191	6.61	7.14	8.31	89.17	740.82	0.76	1.01

DownLoad: CSV

map

[1]	Gschneidner K A, Pecharsky V, Tsokol A 2005 Rep. Prog. Phys. 68 1479 Google Scholar
[2]	Uporov S, Ryltsev R, Bykov V, Uporova N, Estemirova S K, Chtchelkatchev N 2021 J. Alloys Compd. 854 157170 Google Scholar
[3]	Warburg E 1881 Ann. Der. Phys. 249 141 Google Scholar
[4]	Debye P 1926 Ann. Der. Phys. 386 1154 Google Scholar
[5]	Giauque W F 1927 J. Am. Chem. Soc. 49 1864 Google Scholar
[6]	Pecharsky V K, Gschneidner Jr K A 1997 Phys. Rev. Lett. 78 4494 Google Scholar
[7]	Pecharsky V K, Gschneidner Jr K A 1997 Appl. Phys. Lett. 70 3299 Google Scholar
[8]	Jia Y S, Zhao X Y, Liu X L, Li L W 2020 J. Alloys Compd. 813 152177 Google Scholar
[9]	Zhang Y K, Zhu J, Li S, Zhang B, Wang Y M, Wang J, Ren Z M 2022 J. Alloys Compd. 895 162633 Google Scholar
[10]	Wang Q, Pan L L, Tang B Z, Ding D, Xia L 2022 J. Non-Cryst. Solids 580 121394 Google Scholar
[11]	Luo Q, Zhao D Q, Pan M X, Wang W H 2007 Appl. Phys. Lett. 90 211903 Google Scholar
[12]	Lim X 2016 Nature 533 306 Google Scholar
[13]	Huo J T, Huo L S, Li J W, Men H, Wang X M, Inoue A, Chang C T, Wang J Q, Li R W 2015 J. Appl. Phys. 117 073902 Google Scholar
[14]	Huo J T, Huo L S, Men H, Wang X M, Inoue A, Wang J, Chang C T, Li R W 2015 Intermetallics 58 31 Google Scholar
[15]	Sheng W, Wang J Q, Wang G, Huo J T, Wang X, Li R W 2018 Intermetallics 96 79 Google Scholar
[16]	Li J W, Xue L, Yang W, Yuan C, Huo J T, Shen B 2018 Intermetallics 96 90 Google Scholar
[17]	Zhang Y K, Zhu J, Li S, Wang J, Ren Z M 2022 J. Mater. Sci. Technol. 102 66 Google Scholar
[18]	Li L W, Xu C, Yuan Y, Zhou S Q 2018 Materialia 3 74 Google Scholar
[19]	Yang Y, Chen Y, Yu P, Qian L J, Wu F F, Cui Y T, Wu Z M, Ding D, Xia L 2015 J. Nanosci. Nanotechnol. 15 3295 Google Scholar
[20]	Li L W, Xu C, Yuan Y, Zhou S Q 2018 Mater. Res. Lett. 6 413 Google Scholar
[21]	Dong Z Q, Wang Z J, Yin S H 2020 J. Magn. Magn. Mater. 514 167270 Google Scholar
[22]	Luo L, Shen H X, Bao Y, Yin H B, Jiang S D, Huang Y J, Guo S Y, Gao S, Xing D W, Li Z, Sun J F 2020 J. Magn. Magn. Mater. 507 166856 Google Scholar
[23]	Zhang Y K, Xu P, Zhu J, Yan S, Zhang J, Li L W 2023 Mater. Today Phys. 32 101031 Google Scholar
[24]	Zhang Y K, Zhu J, Hao Z, Hao W, Mo Z, Li L W 2023 Mater. Des. 229 111894 Google Scholar
[25]	Civan E, Sarlar K, Kucuk I 2017 Philos. Mag. 97 1464 Google Scholar
[26]	Johnson F, Shull R D 2006 J. Appl. Phys. 99 08K909 Google Scholar
[27]	Kucuk I, Sarlar K, Adam A, Civan E 2016 Philos. Mag. 96 3120 Google Scholar
[28]	Wu K N, Liu C, Li Q, Huo J T, Li M C, Chang C T, Sun Y F 2019 J. Magn. Magn. Mater. 489 165404 Google Scholar
[29]	Wang G F, Li H L, Zhao Z R, Zhang X F 2017 J. Alloys Compd. 692 793 Google Scholar
[30]	Lv Y B, Chen Q J, Huang Y L 2019 J. Rare Earth. 37 404 Google Scholar
[31]	Guo D, Moreno-Ramírez L M, Romero-Muñiz C, Zhang Y K, Law J Y, Franco V, Wang J, Ren Z M 2021 Sci. China Mater. 64 2846 Google Scholar
[32]	Xue L, Shao L L, Li Z, Han Z D, Zhang B S, Huo J T, Wang X M, Zhu S S, Qian B, Cheng J B, Shen B L 2022 J. Mater. Res. Technol. 18 5301 Google Scholar
[33]	Lindner N, Śniadecki Z, Kołodziej M, Grenèche J M, Marcin J, Škorvánek I, Idzikowski B 2022 J. Mater. Sci. 57 553 Google Scholar
[34]	Zheng Z G, Qiu Z G, Zeng D C 2019 Mater. Res. Express 6 096109 Google Scholar
[35]	Law J Y, Ramanujan R V, Franco V 2010 J. Alloys Compd. 508 14 Google Scholar
[36]	糜晓磊, 胡亮, 武博文, 龙强, 魏炳波 2024 73 097102 Google Scholar Mi X L, Hu L, Wu B W, Long Q, Wei B B 2024 Acta Phys. Sin. 73 097102 Google Scholar
[37]	Xue L, Shao L L, Luo Q, Shen B L 2019 J. Alloys Compd. 790 633 Google Scholar
[38]	Wei S J, Shen H X, Zhang L Y, Luo L, Tang X X, Sun J F, Li X Q 2024 Rare Metals 43 1234 Google Scholar
[39]	Lu S F, Ma L, Wang J, Du Y S, Li L W, Zhao J T, Rao G H 2021 J. Alloys Compd. 874 159918 Google Scholar
[40]	Yeh J W 2013 JOM 65 1759 Google Scholar
[41]	Ma E, Wu X L 2019 Nat. Commun. 10 5623 Google Scholar
[42]	Gu J L, Luan H W, Zhao S F, Bu H T, Si J J, Shao Y, Yao K F 2020 Mater. Sci. Eng. A 786 139417 Google Scholar
[43]	Xue L, Shao L L, Zhang B S, Li Z, Cheng J B, Shen B L 2024 J. Rare Earth. 42 129 Google Scholar
[44]	Pang C M, Yuan C C, Chen L, Xu H, Guo K, He J C, Li Y, Wei M S, Wang X M, Huo J T, Shen B L 2020 J. Non-Cryst. Solids 549 120354 Google Scholar
[45]	Pang C M, Chen L, Xu H, Guo W, Lv Z W, Huo J T, Cai M J, Shen B L, Wang X L, Yuan C C 2020 J. Alloys Compd. 827 154101 Google Scholar
[46]	Wang X, Tang B Z, Wang Q, Yu P, Ding D, Xia L 2020 J. Non-Cryst. Solids 544 120146 Google Scholar
[47]	Hao F, Lin H, Zhou C, Liu Y Z, Li J B 2011 Phys. Chem. Chem. Phys. 13 15918 Google Scholar
[48]	Wang Q, Liu C T, Yang Y, Liu J B, Dong Y D, Lu J 2014 Sci. Rep. 4 4648 Google Scholar
[49]	Imafuku M, Yaoita K, Sato S, Zhang W, Inoue A, Waseda Y 2001 Mater. Sci. Eng. A 304 660 Google Scholar
[50]	Wang W H 2009 Adv. Mater. 21 4524 Google Scholar
[51]	Yuan C C, Shen X, Cui J, Gu L, Yu R C, Xi X K 2012 Appl. Phys. Lett. 101 021902 Google Scholar
[52]	Liu Z H, Zhang Y K J, Liu E K, Liu G D, Ma X Q, Wu G H 2015 J. Phys. D Appl. Phys. 48 325001 Google Scholar
[53]	Yuan C C, Yang F, Xi X K, Shi C L, Holland-Moritz D, Li M Z, Hu F, Shen B L, Wang X L, Meyer A, Wang W H 2020 Mater. Today 32 26 Google Scholar
[54]	Jin F, Pang C M, Wang X M, Yuan C C 2023 J. Non-Cryst. Solids 600 121992 Google Scholar
[55]	Inoue A 2000 Acta Mater. 48 279 Google Scholar
[56]	Lu Z P, Tan H, Ng S C, Li Y 2000 Scr. Mater. 42 667 Google Scholar
[57]	Lu Z P, Liu C T 2002 Acta Mater. 50 3501 Google Scholar
[58]	Lu Z P, Liu C T 2003 Phys. Rev. Lett. 91 115505 Google Scholar
[59]	Du X H, Huang J C, Liu C T, Lu Z P 2007 J. Appl. Phys. 101 086108 Google Scholar
[60]	Zhang W, Jia F, Zhang X, Xie G, Inoue A 2010 Metall. Mater. Trans. A 41 1685 Google Scholar
[61]	Zhang Y K, Guo D, Wu B B, Wang H F, Guan R G, Li X, Ren Z M 2020 J. Appl. Phys. 127 033905 Google Scholar
[62]	Yin H, Wang J Q, Huang Y, Shen H X, Guo S, Fan H, Huo J T, Sun J 2023 J. Mater. Sci. Technol. 149 167 Google Scholar
[63]	Zhong H X, Li K, Zhang Q, Wang J, Meng F L, Wu Z J, Yan J M, Zhang X B 2016 NPG Asia Mater. 8 e308 Google Scholar
[64]	Franco V, Blázquez J, Conde A 2006 J. Appl. Phys. 89 222512 Google Scholar
[65]	Zhang H Y, Li R, Zhang L L, Zhang T 2014 J. Appl. Phys. 115 133903 Google Scholar
[66]	Yosida K 1957 Phys. Rev. 107 396 Google Scholar
[67]	Banerjee B 1964 Phys. Lett. 12 16 Google Scholar
[68]	Franco V, Conde A, Romero-Enrique J M, Blázquez J S 2008 J. Phys. Condens. Matter 20 285207 Google Scholar
[69]	Oesterreicher H, Parker F 1984 J. Appl. Phys. 55 4334 Google Scholar
[70]	Guo D, Zhang Y K, Geng S H, Xu H, Ren Z M, Wilde G 2018 J. Mater. Sci. 53 9816 Google Scholar
[71]	Zhang Y K, Li H D, Geng S H, Lu X G, Wilde G 2019 J. Alloys Compd. 770 849 Google Scholar
[72]	Dong Z Q, Yin S H 2020 J. Magn. Magn. Mater. 495 165888 Google Scholar
[73]	Huo J T, Zhao D Q, Bai H Y, Axinte E, Wang W H 2013 J. Non-Cryst. Solids 359 1 Google Scholar

[1]	Lin Yuan, Hu Feng-Xia, Shen Bao-Gen. Phase transition regulation, magnetocaloric effect, and abnormal thermal expansion. Acta Physica Sinica, 2023, 72(23): 237501. doi: 10.7498/aps.72.20231118
[2]	Sun Ji, Shen Peng-Fei, Shang Qi-Zhong, Zhang Peng-Yan, Liu Li, Li Ming-Rui, Hou Long, Li Wei-Huo. Effects of adding B element on amorphous forming ability, magnetic properties, and mechanical properties of FePBCCu alloy. Acta Physica Sinica, 2023, 72(2): 026101. doi: 10.7498/aps.72.20221553
[3]	Zhang Yan, Zong Shuo-Tong, Sun Zhi-Gang, Liu Hong-Xia, Chen Feng-Hua, Zhang Ke-Wei, Hu Ji-Fan, Zhao Tong-Yun, Shen Bao-Gen. Magnetic and anisotropic magnetocaloric effects of HoCoSi fast quenching ribbons. Acta Physica Sinica, 2022, 71(16): 167501. doi: 10.7498/aps.71.20220683
[4]	Peng Jia-Xin, Tang Ben-Zhen, Chen Qi-Xin, Li Dong-Mei, Guo Xiao-Long, Xia Lei, Yu Peng. Preparation and magnetocaloric properties of Gd₄₅Ni₃₀Al₁₅Co₁₀ amorphous alloy. Acta Physica Sinica, 2022, 71(2): 026102. doi: 10.7498/aps.70.20211530
[5]	Ma Shuang, Hao Wei-Ye, Wang Xu-Dong, Zhang Wei, Yao Man. Mechanism analysis of metalloid elements affecting amorphous forming ability and magnetic properties of Co-Y-B alloy. Acta Physica Sinica, 2022, 71(22): 228102. doi: 10.7498/aps.71.20220873
[6]	Yang Jing-Jie, Zhao Jin-Liang, Xu Lei, Zhang Hong-Guo, Yue Ming, Liu Dan-Min, Jiang Yi-Jian. Influences of interstitial atoms H, B and C on magnetic properties and magnetocaloric effect in LaFe11.5Al1.5 compound. Acta Physica Sinica, 2018, 67(7): 077501. doi: 10.7498/aps.67.20172250
[7]	Li Rui-Xuan, Zhang Yong. Entropy and glass formation. Acta Physica Sinica, 2017, 66(17): 177101. doi: 10.7498/aps.66.177101
[8]	Wu Yuan, Song Wen-Li, Zhou Jie, Cao Di, Wang Hui, Liu Xiong-Jun, Lü Zhao-Ping. Ductilization of bulk metallic glassy material and its mechanism. Acta Physica Sinica, 2017, 66(17): 176111. doi: 10.7498/aps.66.176111
[9]	Ke Hai-Bo, Pu Zhen, Zhang Pei, Zhang Peng-Guo, Xu Hong-Yang, Huang Huo-Gen, Liu Tian-Wei, Wang Ying-Min. Research progress in U-based amorphous alloys. Acta Physica Sinica, 2017, 66(17): 176104. doi: 10.7498/aps.66.176104
[10]	Huo Jun-Tao, Sheng Wei, Wang Jun-Qiang. Magnetocaloric effects and magnetic regenerator performances in metallic glasses. Acta Physica Sinica, 2017, 66(17): 176409. doi: 10.7498/aps.66.176409
[11]	Zheng Xin-Qi, Shen Jun, Hu Feng-Xia, Sun Ji-Rong, Shen Bao-Gen. Research progress in magnetocaloric effect materials. Acta Physica Sinica, 2016, 65(21): 217502. doi: 10.7498/aps.65.217502
[12]	Xiao Yu-Ling, He Ji-Zhou, Cheng Hai-Tao. Influence of the heat reservoir boundary on the performance of Brownian heat engine. Acta Physica Sinica, 2014, 63(20): 200501. doi: 10.7498/aps.63.200501
[13]	Wang Fang, Yuan Feng-Ying, Wang Jin-Zhi. Magnetic properties and magnetocaloric effect in Mn42Al50-xFe8+x alloys. Acta Physica Sinica, 2013, 62(16): 167501. doi: 10.7498/aps.62.167501
[14]	Zhang Ya-Nan, Wang You-Jun, Kong Ling-Ti, Li Jin-Fu. Influence of Y addition on the glass forming ability and soft magnetic properties of Fe-Si-B amorphous alloy. Acta Physica Sinica, 2012, 61(15): 157502. doi: 10.7498/aps.61.157502
[15]	Zhang Hao-Lei, Li Zhe, Qiao Yan-Fei, Cao Shi-Xun, Zhang Jin-Cang, Jing Chao. Martensitic transformation and magnetocaloric effect in Ni-Co-Mn-Sn Heusler alloy. Acta Physica Sinica, 2009, 58(11): 7857-7863. doi: 10.7498/aps.58.7857
[16]	Jing Chao, Chen Ji-Ping, Li Zhe, Cao Shi-Xun, Zhang Jin-Cang. Martensitic transformation and magnetocaloric effect in Ni50Mn35In15 Heusler alloy. Acta Physica Sinica, 2008, 57(7): 4450-4455. doi: 10.7498/aps.57.4450
[17]	Zhang Hui, Zhang Guo-Ying, Yang Shuang, Wu Di, Qi Ke-Zhen. Effects of additional element on the glass forming ability and corrosion resistance of bulk Zr-based amorphous alloys. Acta Physica Sinica, 2008, 57(12): 7822-7826. doi: 10.7498/aps.57.7822
[18]	Wang Zhen-Yu, Yang Yuan-Sheng, Tong Wen-Hui, Li Hui-Qiang, Hu Zhuang-Qi. A new model for calculating critical cooling rates of alloy systems based on viscosity calculation. Acta Physica Sinica, 2007, 56(3): 1543-1548. doi: 10.7498/aps.56.1543
[19]	Wang Zhen-Yu, Yang Yuan-Sheng, Tong Wen-Hui, Li Hui-Qiang, Hu Zhuang-Qi. A new model for calculating the critical cooling rate of bulk metallic glass under non-isothermal condition. Acta Physica Sinica, 2006, 55(4): 1953-1958. doi: 10.7498/aps.55.1953
[20]	CHEN WEI, ZHONG WEI, PAN CHENG, CHANG HONG, DU YOU-WEI. CURIE TEMPERATURE AND MAGNETOCALORIC EFFECT OF POLYCRYSTALLINE La0.8-xCa0.2MnO3. Acta Physica Sinica, 2001, 50(2): 319-323. doi: 10.7498/aps.50.319

2024年24期217101补充材料.pdf

Catalog

Vol. 73, Issue 21 - 2024-11-05

Metrics

Abstract views: 877
PDF Downloads: 14
Cited By: 0