Research progress of polymer based dielectrics for high-temperature capacitor energy storage

Dong Jiu-Feng; Deng Xing-Lei; Niu Yu-Juan; Pan Zi-Zhao; Wang Hong

doi:10.7498/aps.69.20201006

Abstract

Dielectric capacitors are widely used in modern electronic systems and power systems because of their advantages of fast charge discharge speed and high-power density. Nowadays, the new products related to renewable energy, such as hybrid electric vehicles, grid connected photovoltaic power generation and wind turbines, downhole oil, gas exploration, etc., put forward higher requirements for the energy storage capabilities of dielectric capacitors in elevated-temperature. In this review, the research progress of the polymer-based dielectrics for high-temperature capacitor energy storage in recent years is systematically reviewed to offer benefits for further study. Firstly, the physical mechanism of energy storage of dielectric materials is introduced, and several conduction mechanisms of dielectric materials are summarized and analyzed; then, several strategies to improve the high-temperature energy storage performance of polymer dielectrics are presented, including the nanocomposite modification and design of layer-structured polymer composites, and the molecular structure design and chemical crosslinking treatment of dielectric polymer. Finally the scientific and technological problems in the application of dielectric polymer and their nanocomposites for high-temperature capacitor energy storage are discussed, and a possible research direction in the future is prospected.

Keywords:

Authors and contacts

1.
Department of Materials Science and Engineering, Southern University of Science and Technology, Shenzhen 518055, China
2.
School of Electronic and Information Engineering, Xi’an Jiaotong University, Xi’an 710049, China

Corresponding author: Wang Hong, wangh6@sustech.edu.cn

Funds: Project supported by the Science and Technology Program of Shenzhen, China (Grant Nos. KQTD20180411143514543, JCYJ20180504165831308), the Key Area R&D Program of Guangdong Province, China (Grant No. 2020B010176001), and the DRC Project of Shenzhen, China (Grant No. [2018]1433)

FullText HTML : translate this paragraph

References

[1]	Pan H, Li F, Liu Y, Zhang Q H, Wang M, Lan S, Zheng Y P, Ma J, Gu L, Shen Y, Yu P, Zhang S J, Chen L Q, Lin Y H, Nan C W 2019 Science 365 578 Google Scholar
[2]	Lin X R, Salari M, Arava L M R, Ajayan P M, Grinstaff M W 2016 Chem. Soc. Rev. 45 5848 Google Scholar
[3]	Luo H, Zhou X F, Ellingford C, Zhang Y, Chen S, Zhou K C, Zhang D, Bowen C B, Wan C Y 2019 Chem. Soc. Rev. 48 4424 Google Scholar
[4]	Huang X Y, Sun B, Zhu Y K, Li S T, Jiang P K 2019 Prog. Mater. Sci. 100 187 Google Scholar
[5]	Yuan Q B, Yao F Z, Cheng S D, Wang L X, Wang Y F, Mi S B, Wang Q, Wang X H, Wang H 2020 Adv. Funct. Mater. 30 2000191 Google Scholar
[6]	Li Q, Zhang G Z, Liu F H, Han K, Gadiniski M R, Xiong C X, Wang Q 2015 Energy Environ. Sci. 8 922 Google Scholar
[7]	Li Q, Yao F Z, Liu Y, Zhang G Z, Wang H, Wang Q 2018 Ann. Rev. Mater. Res. 48 219 Google Scholar
[8]	Watson J, Castro G 2012 Analog Dialogue 46 1
[9]	Tan D, Zhang L, Chen Q, Irwin P 2014 J. Electron. Mater. 43 4569 Google Scholar
[10]	Johnson R W, Evans J L, Jacobsen P, Thompson J R, Christopher M 2004 IEEE Trans. Electron. Packag. Manuf. 27 164 Google Scholar
[11]	Barshaw E J, White J, Chait M J, Cornette J B, Bustamante J, Folli F, Biltchick D, Borelli G, Pocco G, Rabuffi M 2007 IEEE Trans. Magn. 43 223 Google Scholar
[12]	李吉超, 王春雷, 钟维烈, 薛旭艳, 王渊旭 2002 51 776 Google Scholar Li J C, Wang C L, Zhong W L, Xue X Y, Wang Y X 2002 Acta Phys. Sin. 51 776 Google Scholar
[13]	Gadinski M R, Han K, Li Q, Zhang G, Reainthippayasakul W, Wang Q 2014 ACS Appl. Mater. Interfaces 6 18981 Google Scholar
[14]	Chu B, Zhou X, Ren K, Neese B, Lin M, Wang Q, Bauer F, Zhang Q M 2006 Science 313 334 Google Scholar
[15]	Zhou X, Zhao X, Suo Z, Zou C, Runt J, Liu S, Zhang S, Zhang Q M 2009 Appl. Phys. Lett. 94 143 Google Scholar
[16]	Li Q, Chen L, Gadinski M R, Zhang S H, Zhang G Z, Li H U, Iagodkine E, Haque A, Chen L Q, Jackson T N, Wang Q 2015 Nature 523 576 Google Scholar
[17]	Prajapati P, Thakui V K, Gupta R 2016 Chem. Rev. 116 4260 Google Scholar
[18]	Zhou L, Jiang Y F 2019 Mater. Sci. Technol. 36 1 Google Scholar
[19]	Yao Z H, Song Z, Hao H, Yu Z Y, Cao M H, Zhang S J, Lanagan M T, Liu H X 2017 Adv. Mater. 29 1601727 Google Scholar
[20]	Palneedi H, Peddigari M, Hwang G T, Jeong D Y, Ryu J 2018 Adv. Funct. Mater. 28 1803665 Google Scholar
[21]	Kojima K, Takai Y, Ieda M 1986 J. Appl. Phys. 59 2655 Google Scholar
[22]	Chiu F C 2014 Adv. Mater. Sci. Eng. 2014 1 Google Scholar
[23]	Akram S, Yang Y, Zhong X, Bhutta S, Wu G N, Castellon J, Zhou K 2017 IEEE Trans. Dielectr. Electr. Insul. 24 3505 Google Scholar
[24]	Liu A, Zhu H H, Sun H B, Xu Y, Noh Y Y 2018 Adv. Mater. 30 1706364 Google Scholar
[25]	Vecchio M A, Meddeb A B, Lanagan M T, Ounaies Z, Shallenberger J R 2018 J. Appl. Phys. 124 114102 Google Scholar
[26]	Sawa A 2008 Mater. Today 11 28 Google Scholar
[27]	Angle R L, Talley H E 1978 IEEE Trans. Electron Devices 25 1277 Google Scholar
[28]	Chiu F C, Lee C Y, Pan T M 2009 J. Appl. Phys. 105 074103 Google Scholar
[29]	Calvet L, Wheeler R, Reed M 2002 Appl. Phys. Lett. 80 1761 Google Scholar
[30]	Chiu F C 2006 J. Appl. Phys. 100 114102 Google Scholar
[31]	Shen Z H, Wang J J, Jiang J Y, Huang S X, Lin Y H, Nan C W, Chen L Q, Shen Y 2019 Nat. Commun. 10 1843 Google Scholar
[32]	Laghari J R, Sarjeant W J 1992 IEEE Trans. Power Electron. 7 251 Google Scholar
[33]	Shen Z H, Wang J J, Lin Y H, Nan C W, Chen L Q, Shen Y 2018 Adv. Mater. 30 1704380 Google Scholar
[34]	Chi Q G, Gao Z Y, Zhang T D, Zhang C H, Zhang Y, Chen Q G, Wang X, Lei Q Q 2019 ACS Sustainable Chem. Eng. 7 748 Google Scholar
[35]	Tong H, Fu J, Ahmad A, Fan T, Hou Y D, Xu J 2019 Macromol. Mater. Eng. 304 1800709 Google Scholar
[36]	James J C 1986 Polym. Compos. 7 158 Google Scholar
[37]	Ho J S, Greenbaum S G 2018 ACS Appl. Mater. Interfaces 10 29189 Google Scholar
[38]	Mannodi-Kanakkithodi A, Treich G M, Huan T D, Ma R, Tefferi M, Cao Y, Sotzing G A, Ramprasad R 2016 Adv. Mater. 28 6277 Google Scholar
[39]	Klein R J, Barber P, Chance W M, Loye H C Z 2012 IEEE Trans. Dielectr. Electr. Insul. 19 1234 Google Scholar
[40]	Diaham S, Saysouk F, Locatelli M L, Lebey T 2016 IEEE Trans. Dielectr. Electr. Insul. 23 2795 Google Scholar
[41]	Chi Q G, Dong J F, Zhang C H, Wong C P, Wang X, Lei Q Q 2016 J. Mater. Chem. C 4 8179 Google Scholar
[42]	Wang S, Huang X Y, Wang G Y, Wang Y, He J L, Jiang P K 2015 J. Phys. Chem. C 119 25307 Google Scholar
[43]	冯奇, 李梦凯, 唐海通, 王晓东, 高忠民, 孟繁玲 2016 65 188101 Google Scholar Feng Q, Li M K, Tang H T, Wang X D, Gao Z M, Meng F L 2016 Acta Phys. Sin. 65 188101 Google Scholar
[44]	Pan Z B, Yao L M, Ge G L, Shen B, Zhai J W 2018 J. Mater. Chem. A 6 14614 Google Scholar
[45]	Zou K L, Dan Y, Yu Y X, Zhang Y, Zhang Q F, Lu Y M, Huang H T, Zhang X, He Y B 2019 J. Mater. Chem. A 7 13473 Google Scholar
[46]	Feng Y, Zhou Y H, Zhang T D, Zhang C H, Zhang Y Q, Zhang Y, Chen Q G, Chi Q G 2020 Energy Storage Mater. 25 180 Google Scholar
[47]	Yu K, Wang H, Zhou Y C, Bai Y Y, Niu Y J 2013 J. Appl. Phys. 113 034105 Google Scholar
[48]	Yu K, Niu Y J, Xiang F, Zhou Y C, Bai Y Y, Wang H 2013 J. Appl. Phys. 114 174107 Google Scholar
[49]	Wu Y H, Zha J W, Yao Z Q, Sun F, Li R K Y, Dang Z M 2015 RSC Adv. 9 44749 Google Scholar
[50]	Huang X Y, Jiang P K 2015 Adv. Mater. 27 546 Google Scholar
[51]	Hu P H, Sun W D, Fan M Z, et al. 2018 Appl. Surf. Sci. 458 743 Google Scholar
[52]	Sun W D, Lu X J, Jiang J Y, Zhang X, Hu P H, Li M, Lin Y H, Nan C W, Shen Y 2017 J. Appl. Phys. 121 244101 Google Scholar
[53]	Shen Z H, Wang J J, Jiang J Y, Lin Y H, Nan C W, Chen L Q, Shen Y 2018 Adv. Energy Mater. 8 1800509 Google Scholar
[54]	Zhu Y K, Zhu Y J, Huang X Y, Chen J, Li Q, He J L, Jiang P K 2019 Adv. Energy Mater. 9 1901826 Google Scholar
[55]	Li Y S, Zhou Y, Zhu Y J, Cheng S, Yuan C, Hu J, He J L, Li Q 2020 J. Mater. Chem. A 8 6576 Google Scholar
[56]	Wu L Y, Wu K, Liu D Y, Huang R, Huo J L, Chen F, Fu Q 2018 J. Mater. Chem. A 6 7573 Google Scholar
[57]	Wu L Y, Wu K, Lei C X, Liu D Y, Du R N, Chen F, Fu Q 2019 J. Mater. Chem. A 7 7664 Google Scholar
[58]	Liu F H, Li Q, Li Z Y, Liu Y, Dong L J, Xiong C X, Wang Q 2017 Compos. Sci. Technol. 142 139 Google Scholar
[59]	Ai D, Li H, Zhou Y, et al. 2020 Adv. Energy Mater. 10 1903881 Google Scholar
[60]	Li H, Ai D, Ren L L, Yao B, Han Z B, Shen Z H, Wang J J, Chen L Q, Wang Q 2019 Adv. Mater. 31 1900875 Google Scholar
[61]	Li H, Ren L L, Ai D, Han Z B, Liu Y, Yao B, Wang Q 2020 InfoMat. 2 389 Google Scholar
[62]	Thakur Y, Zhang T, Iacob C, Yang T N, Bernholc J, Chen L Q, Runt J, Zhang Q M 2017 Nanoscale 9 10992 Google Scholar
[63]	Chadband W G 1992 IEE Rev. 38 404 Google Scholar
[64]	Zhang T, Chen X, Thakur Y, Lu B, Zhang Q Y, Runt J, Zhang Q M 2020 Sci. Adv. 6 6622 Google Scholar
[65]	Thakur Y, Lean M H, Zhang Q M 2017 Appl. Phys. Lett. 110 122905 Google Scholar
[66]	Bouharrasa F E, Raihane M, Ameduri B 2020 Prog. Mater. Sci. 113 100670 Google Scholar
[67]	Niu Y J, Xiang F, Wang Y F, Chen J, Wang H 2018 Phys. Chem. Chem. Phys. 20 6598 Google Scholar
[68]	Niu Y J, Wang H 2019 ACS Appl. Nano Mater. 2 627 Google Scholar
[69]	Zhang X, Li B W, Dong L J, Liu H X, Chen W, Shen Y, Nan C W 2018 Adv. Mater. Interfaces 5 1800096 Google Scholar
[70]	Pan Z B, Yao L M, Zhai J W, Yao X, Chen H 2018 Adv. Mater. 30 1705662 Google Scholar
[71]	Rahimabady M, Mirshekarloo M S, Yao K, Lu L 2013 Phys. Chem. Chem. Phys. 15 16242 Google Scholar
[72]	Liu S, Xue S X, Shen B, Zhai J W 2015 Appl. Phys. Lett. 107 032907 Google Scholar
[73]	Choudhury A 2012 Polym. Int. 61 696 Google Scholar
[74]	Luo H, Zhang D, Jiang C, Yuan X, Chen C, Zhou K C 2015 ACS Appl. Mater. Interfaces 7 8061 Google Scholar
[75]	Liu J, Shen Z H, Xu W H, Zhang Y, Qian X S, Jiang Z H, Zhang Y H 2020 Small 2000714 Google Scholar
[76]	Xu W H, Liu J, Chen T W, Jiang X Y, Qian X S, Zhang Y, Jiang Z H, Zhang Y H 2019 Small 15 1901582 Google Scholar
[77]	Zhou Y, Yuan C, Wang S J, Zhu Y J, Cheng S, Yang X, Yang Y, Hu J, He J L, Li Q 2020 Energy Storage Mater. 28 255 Google Scholar
[78]	Wang Y F, Cui J, Yuan Q B, Niu Y J, Bai Y Y, Wang H 2015 Adv. Mater. 27 6658 Google Scholar
[79]	Wang Y F, Wang L X, Yuan Q B, et al. 2018 Nano Energy 44 364 Google Scholar
[80]	Chen J, Wang Y F, Yuan Q B, Xu X W, Niu Y J, Wang Q, Wang H 2018 Nano Energy 54 288 Google Scholar
[81]	Jiang J Y, Shen Z H, Qian J, Dan Z, Guo M, He Y, Lin Y H, Nan C W, Chen L Q, Shen Y 2019 Nano Energy 62 220 Google Scholar
[82]	Chen J, Wang Y F, Xu X W, Yuan Q B, Niu Y J, Wang Q, Wang H 2019 J. Mater. Chem. A 7 3729 Google Scholar
[83]	Wang Y F, Chen J. Li Y, Niu Y J, Wang Q, Wang H 2019 J. Mater. Chem. A 7 2965 Google Scholar
[84]	Chen X Y, Tseng J K, Treufeld I, Mackey M, Schuele D E, Li R P, Fukuto M, Baer E, Zhu L 2017 J. Mater. Chem. C 5 10417 Google Scholar
[85]	Li Z P, Chen X Y, Zhang C, Baer E, Langhe D, Ponting Ml, Brubaker M, Hosking T, Li R P, Fukuto M, Zhu L 2019 ACS Appl. Polym. Mater. 1 867 Google Scholar
[86]	Tewari P, Rajagopalan R, Furman E, Lanagan M T 2010 Langmuir 26 18817 Google Scholar
[87]	Hu P H, Shen Y, Guan Y H, Zhang X H, Lin Y H, Zhang Q M, Nan C W 2014 Adv. Funct. Mater. 24 3172 Google Scholar
[88]	Pan Z B, Liu B H, Zhai J W, Yao L M, Yang K, Shen B 2017 Nano Energy 40 587 Google Scholar
[89]	Tseng J K, Tang S, Zhou Z, Mackey M, Carr J M, Mu R, Flandin L, Schuele D E, Baer E, Zhu L 2014 Polymer 55 8 Google Scholar
[90]	Mackey M, Hiltner A, Baer E, Flandin L, Wolak M A, Shirk J S 2009 J. Phys. D: Appl. Phys. 42 175304 Google Scholar
[91]	Li Q, Liu F H, Yang T N, Gadinski M R, Zhang G Z, Chen L Q, Wang Q 2016 Proc. Natl. Acad. Sci. U.S.A. 113 9995 Google Scholar
[92]	Azizi A, Gadinski M R, Li Q, AlSaud M A, Wang J J, Wang Y, Wang B, Liu F H, Chen L Q, Alem N, Wang Q 2017 Adv. Mater. 29 1701864 Google Scholar
[93]	Zhou Y, Li Q, Dang B, Yang Y, Shao T, Li H, Hu J, Zeng R, He J L, Wang Q 2018 Adv. Mater. 30 1805672 Google Scholar
[94]	Bonardd S, Moreno-Serna V, Kortaberria G, Díaz D D, Leiva A, Saldías C 2019 Polymer 11 317 Google Scholar
[95]	Peng X W, Wu Q, Jiang S H, Hanif M, Chen S L, Hou H Q 2014 J. Appl. Polym. Sci. 131 40828 Google Scholar
[96]	Zhuang Y B, Seong J G, Lee Y M 2019 Prog. Polym. Sci. 92 35 Google Scholar
[97]	Kao K C 2004 Dielectric Phenomena in Solids (San Diego: Academic Press) p573
[98]	Wang Y, Zhou X, Lin M R, Zhang Q M 2009 Appl. Phys. Lett. 94 154 Google Scholar
[99]	Cheng Z X, Lin M R, Wu S, Thakur Y, Zhou Y, Jeong D Y, Shen Q D, Zhang Q M 2015 Appl. Phys. Lett. 106 202902 Google Scholar
[100]	Wu S, Li W P, Lin M R, Burlingame Q, Chen Q, Payzant A, Xiao K, Zhang Q M 2013 Adv. Mater. 25 1734 Google Scholar
[101]	Qiao Y L, Islam M S, Yin X D, Han K, Yan Y, Zhang J Y, Wang Q, Ploehn H J, Tang C B 2015 Polymer 72 428 Google Scholar
[102]	Yuan X P, Matsuyama Y, Chung T C M 2010 Macromolecules 43 4011 Google Scholar
[103]	Misra M, Agarwal M, Sinkovits D W, Kumar S K, Wang C C, Pilania G, Ramprasad R, Weiss R A, Yuan X P, Mike Chung T C 2014 Macromolecules 47 1122 Google Scholar
[104]	Zhang M, Zhang L, Zhu M, Wang Y G, Li N W, Zhang Z J, Chen Q, An L N, Lin Y H, Nan C W 2016 J. Mater. Chem. A 4 4797 Google Scholar
[105]	Chou Y H, Yen H J, Tsai C L, Lee W Y, Liou G S, Chen W C 2013 J. Mater. Chem. C 1 3235 Google Scholar
[106]	Treufeld I, Wang D H, Kurish B A, Tan L S 2014 J. Mater. Chem. A 2 20683 Google Scholar
[107]	Zhang Z B, Wang D H, Litt M H, Tan L S, Zhu L 2018 Angew. Chem. Int. Ed. 130 1547 Google Scholar
[108]	Zhang Z B, Zheng J F, Premasiri K, Kwok M H, Li Q, Li R P, Zhang S B, Litt M H, Gao X P A, Zhu L 2020 Mater. Horiz. 7 592 Google Scholar
[109]	Yang R Q, Wei R B, Li K, Tong L F, Jia K, Liu X B 2016 Sci. Rep. 6 36434 Google Scholar
[110]	Yang J, Yang X L, Zou Y K, Zhan Y Q, Zhao R, Liu X B 2012 J. Appl. Polym. Sci. 126 1129 Google Scholar
[111]	Hanley T L, Burford R P, Fleming R J, Barber K W 2003 IEEE Electr. Insul. Mag. 19 13 Google Scholar
[112]	Zhou Q, Ma J, Dong S, Li X, Cui G 2019 Adv. Mater. 31 1902029 Google Scholar
[113]	Khanchaitit P, Han K, Gadinski M R, Li Q, Wang Q 2013 Nat. Commun. 4 2845 Google Scholar
[114]	Meereboer N L, Terzić I, van der Steeg P, Portale G, Loos K 2019 J. Mater. Chem. A 7 2795 Google Scholar
[115]	Chen X Z, Li Z W, Cheng Z X, Zhang J Z, Shen Q D, Ge H X, Li H T 2011 Macromol. Rapid Commun. 32 94 Google Scholar
[116]	Tan S, Hu X, Ding S, Zhang Z, Li H, Yang L 2013 J. Mater. Chem. A 1 10353 Google Scholar
[117]	Li H, Gadinski M R, Huang Y Q, et al. 2020 Energy Environ. Sci. 13 1279 Google Scholar
[118]	Chen S Y, Meng G D, Kong B, Xiao B, Wang Z D, Jing Z, Gao Y S, Wu G L, Wang H, Cheng Y H 2020 Chem. Eng. J. 387 123662 Google Scholar
[119]	Wang Y X, Huang X Y, Li T, Wang Z W, Li L Q, Gu X J, Jiang P K 2017 J. Mater. Chem. A 5 20737 Google Scholar
[120]	Hung C C, Wu H C, Chiu Y C, Tung S H, Chen W C 2016 J. Polym. Sci. Polym. Chem. 54 3224 Google Scholar

Cited By

图 1 介电电容器、电化学电容器与电池的能量密度和功率密度的对比图

Figure 1. Comparison of power density and energy density capabilities of dielectric capacitors, electrochemical capacitors, and batteries.

DownLoad: Full-Size Img PowerPoint

图 2 (a) 两个金属电极之间的电介质电容器示意图; (b) 电介质材料的电位移-电场强度关系曲线

Figure 2. (a) Schematic diagram of dielectric capacitor between two metal electrodes; (b) electric displacement-electric field (D-E) hysteresis loop of a dielectric material.

DownLoad: Full-Size Img PowerPoint

图 3 各种电导机制的示意图

Figure 3. Schematic diagrams of various conduction mechanisms.

DownLoad: Full-Size Img PowerPoint

图 4 (a) PI-STO纳米复合膜制备的电容器示意图; 当电场强度为200 kV/mm, 400 K温度条件下工作时, 由(b) 纯PI, (c) 垂直纳米纤维, (d) 垂直纳米片, (e) 随机纳米颗粒, (f) 平行纳米纤维, (g) 平行纳米片填充的纳米复合薄膜制备的不同电容器的稳态温度分布; (h) 薄膜电容器内的最大温度T_max与热导率κ_z和电导率σ_z的函数关系图; (i) 6种情况下, 最大温度T_max(红色条)、击穿强度劣化因子β (蓝色条)和介电损耗tanδ (黑色条)的性能比较^[53]

Figure 4. (a) Schematic illustration of a real capacitor made by winding the PI-STO nanocomposite film. When working under an applied electric field of 200 kV/mm and a surrounding temperature of 400 K, the steady-state temperature distributions in different capacitors made by film nanocomposites filled by (b) pure polymer, (c) vertical nanofibers, (d) vertical nanosheets, (e) random nanoparticles, (f) parallel nanofibers, and (g) parallel nanosheets. (h) Maximal temperature T_max inside the film capacitor as function of the thermal conductivity component κ_z and electrical conductivity component σ_z. (i) Comparisons of the maximal temperature T_max (red bar), breakdown strength deterioration factor β (blue bar), and dielectric loss tanδ (black bar) among six circumstances^[53].

DownLoad: Full-Size Img PowerPoint

图 5 (a) 在25 ℃和1 kHz下, PI纳米复合材料的介电常数和损耗随填料含量的变化; PI和PI纳米复合材料在150 ℃下的(b) Weibull击穿强度和(c)储能性能; (d) 150 ℃下, 模拟电流密度分布随Al₂O₃, HfO₂和TiO₂填料含量和外加电场的变化^[59]

Figure 5. (a) Dielectric constant and loss of the PI nanocomposites as a function of filler content at 25 ℃ and 1 kHz; (b) Weibull breakdown strength and (c) energy density performance of PI and the PI nanocomposites measured at 150 ℃; (d) simulated current density distribution as a function of Al₂O₃, HfO₂, and TiO₂ filler content and the applied electric field at 150 ℃^[59].

DownLoad: Full-Size Img PowerPoint

图 6 (a) 蜘蛛丝和蜘蛛丝的显微结构; (b) BN-BCB@DPAES复合材料的工艺图^[76]

Figure 6. (a) Spider silk and the hierarchical microscopic structure of the spider silk; (b) schematic of preparation process of BN-BCB@DPAES films^[76].

DownLoad: Full-Size Img PowerPoint

图 7 (a) Roll-to-roll PECVD示意图; (b) 聚合物表层沉积SiO₂的断面扫描电子显微镜图; (c) 聚合物表层沉积SiO₂的断面能量色散X射线图谱; (d) 在120 ℃下, BOPP薄膜表层沉积180 nm 厚度的SiO₂前后的储能密度和储能效率对比; (e) 在150 ℃下, 储能效率大于90%时, 各种电介质聚合物薄膜表层沉积SiO₂前后的最大放电能量密度^[93]

Figure 7. (a) Schematic of the roll-to-roll PECVD; (b) cross-sectional scanning electron microscope image of the coating layer on polymer film; (c) element concentration from energy dispersive X-ray spectroscopy scanned across the coating layer deposited on polymer film; (d) charge-discharge efficiency and discharged energy density of BOPP and BOPP-SiO₂ films with 180 nm coating layer on each side of the polymer measured at 120 ℃; (e) maximum discharged energy density of the various dielectric films before and after coating achieved at above 90% charge-discharge efficiency measured at 150 ℃^[93].

DownLoad: Full-Size Img PowerPoint

图 8 (a) 芳香族聚脲、聚硫脲和聚芳醚脲的结构式; (b)砜基化聚苯醚和砜基化自具微孔聚合物的结构式

Figure 8. (a) Chemical structures of ArPU, ArPTU and PEEU; (b) chemical structures of SO₂-PPO₂₅, and SO₂-PIM.

DownLoad: Full-Size Img PowerPoint

map

[1]	Pan H, Li F, Liu Y, Zhang Q H, Wang M, Lan S, Zheng Y P, Ma J, Gu L, Shen Y, Yu P, Zhang S J, Chen L Q, Lin Y H, Nan C W 2019 Science 365 578 Google Scholar
[2]	Lin X R, Salari M, Arava L M R, Ajayan P M, Grinstaff M W 2016 Chem. Soc. Rev. 45 5848 Google Scholar
[3]	Luo H, Zhou X F, Ellingford C, Zhang Y, Chen S, Zhou K C, Zhang D, Bowen C B, Wan C Y 2019 Chem. Soc. Rev. 48 4424 Google Scholar
[4]	Huang X Y, Sun B, Zhu Y K, Li S T, Jiang P K 2019 Prog. Mater. Sci. 100 187 Google Scholar
[5]	Yuan Q B, Yao F Z, Cheng S D, Wang L X, Wang Y F, Mi S B, Wang Q, Wang X H, Wang H 2020 Adv. Funct. Mater. 30 2000191 Google Scholar
[6]	Li Q, Zhang G Z, Liu F H, Han K, Gadiniski M R, Xiong C X, Wang Q 2015 Energy Environ. Sci. 8 922 Google Scholar
[7]	Li Q, Yao F Z, Liu Y, Zhang G Z, Wang H, Wang Q 2018 Ann. Rev. Mater. Res. 48 219 Google Scholar
[8]	Watson J, Castro G 2012 Analog Dialogue 46 1
[9]	Tan D, Zhang L, Chen Q, Irwin P 2014 J. Electron. Mater. 43 4569 Google Scholar
[10]	Johnson R W, Evans J L, Jacobsen P, Thompson J R, Christopher M 2004 IEEE Trans. Electron. Packag. Manuf. 27 164 Google Scholar
[11]	Barshaw E J, White J, Chait M J, Cornette J B, Bustamante J, Folli F, Biltchick D, Borelli G, Pocco G, Rabuffi M 2007 IEEE Trans. Magn. 43 223 Google Scholar
[12]	李吉超, 王春雷, 钟维烈, 薛旭艳, 王渊旭 2002 51 776 Google Scholar Li J C, Wang C L, Zhong W L, Xue X Y, Wang Y X 2002 Acta Phys. Sin. 51 776 Google Scholar
[13]	Gadinski M R, Han K, Li Q, Zhang G, Reainthippayasakul W, Wang Q 2014 ACS Appl. Mater. Interfaces 6 18981 Google Scholar
[14]	Chu B, Zhou X, Ren K, Neese B, Lin M, Wang Q, Bauer F, Zhang Q M 2006 Science 313 334 Google Scholar
[15]	Zhou X, Zhao X, Suo Z, Zou C, Runt J, Liu S, Zhang S, Zhang Q M 2009 Appl. Phys. Lett. 94 143 Google Scholar
[16]	Li Q, Chen L, Gadinski M R, Zhang S H, Zhang G Z, Li H U, Iagodkine E, Haque A, Chen L Q, Jackson T N, Wang Q 2015 Nature 523 576 Google Scholar
[17]	Prajapati P, Thakui V K, Gupta R 2016 Chem. Rev. 116 4260 Google Scholar
[18]	Zhou L, Jiang Y F 2019 Mater. Sci. Technol. 36 1 Google Scholar
[19]	Yao Z H, Song Z, Hao H, Yu Z Y, Cao M H, Zhang S J, Lanagan M T, Liu H X 2017 Adv. Mater. 29 1601727 Google Scholar
[20]	Palneedi H, Peddigari M, Hwang G T, Jeong D Y, Ryu J 2018 Adv. Funct. Mater. 28 1803665 Google Scholar
[21]	Kojima K, Takai Y, Ieda M 1986 J. Appl. Phys. 59 2655 Google Scholar
[22]	Chiu F C 2014 Adv. Mater. Sci. Eng. 2014 1 Google Scholar
[23]	Akram S, Yang Y, Zhong X, Bhutta S, Wu G N, Castellon J, Zhou K 2017 IEEE Trans. Dielectr. Electr. Insul. 24 3505 Google Scholar
[24]	Liu A, Zhu H H, Sun H B, Xu Y, Noh Y Y 2018 Adv. Mater. 30 1706364 Google Scholar
[25]	Vecchio M A, Meddeb A B, Lanagan M T, Ounaies Z, Shallenberger J R 2018 J. Appl. Phys. 124 114102 Google Scholar
[26]	Sawa A 2008 Mater. Today 11 28 Google Scholar
[27]	Angle R L, Talley H E 1978 IEEE Trans. Electron Devices 25 1277 Google Scholar
[28]	Chiu F C, Lee C Y, Pan T M 2009 J. Appl. Phys. 105 074103 Google Scholar
[29]	Calvet L, Wheeler R, Reed M 2002 Appl. Phys. Lett. 80 1761 Google Scholar
[30]	Chiu F C 2006 J. Appl. Phys. 100 114102 Google Scholar
[31]	Shen Z H, Wang J J, Jiang J Y, Huang S X, Lin Y H, Nan C W, Chen L Q, Shen Y 2019 Nat. Commun. 10 1843 Google Scholar
[32]	Laghari J R, Sarjeant W J 1992 IEEE Trans. Power Electron. 7 251 Google Scholar
[33]	Shen Z H, Wang J J, Lin Y H, Nan C W, Chen L Q, Shen Y 2018 Adv. Mater. 30 1704380 Google Scholar
[34]	Chi Q G, Gao Z Y, Zhang T D, Zhang C H, Zhang Y, Chen Q G, Wang X, Lei Q Q 2019 ACS Sustainable Chem. Eng. 7 748 Google Scholar
[35]	Tong H, Fu J, Ahmad A, Fan T, Hou Y D, Xu J 2019 Macromol. Mater. Eng. 304 1800709 Google Scholar
[36]	James J C 1986 Polym. Compos. 7 158 Google Scholar
[37]	Ho J S, Greenbaum S G 2018 ACS Appl. Mater. Interfaces 10 29189 Google Scholar
[38]	Mannodi-Kanakkithodi A, Treich G M, Huan T D, Ma R, Tefferi M, Cao Y, Sotzing G A, Ramprasad R 2016 Adv. Mater. 28 6277 Google Scholar
[39]	Klein R J, Barber P, Chance W M, Loye H C Z 2012 IEEE Trans. Dielectr. Electr. Insul. 19 1234 Google Scholar
[40]	Diaham S, Saysouk F, Locatelli M L, Lebey T 2016 IEEE Trans. Dielectr. Electr. Insul. 23 2795 Google Scholar
[41]	Chi Q G, Dong J F, Zhang C H, Wong C P, Wang X, Lei Q Q 2016 J. Mater. Chem. C 4 8179 Google Scholar
[42]	Wang S, Huang X Y, Wang G Y, Wang Y, He J L, Jiang P K 2015 J. Phys. Chem. C 119 25307 Google Scholar
[43]	冯奇, 李梦凯, 唐海通, 王晓东, 高忠民, 孟繁玲 2016 65 188101 Google Scholar Feng Q, Li M K, Tang H T, Wang X D, Gao Z M, Meng F L 2016 Acta Phys. Sin. 65 188101 Google Scholar
[44]	Pan Z B, Yao L M, Ge G L, Shen B, Zhai J W 2018 J. Mater. Chem. A 6 14614 Google Scholar
[45]	Zou K L, Dan Y, Yu Y X, Zhang Y, Zhang Q F, Lu Y M, Huang H T, Zhang X, He Y B 2019 J. Mater. Chem. A 7 13473 Google Scholar
[46]	Feng Y, Zhou Y H, Zhang T D, Zhang C H, Zhang Y Q, Zhang Y, Chen Q G, Chi Q G 2020 Energy Storage Mater. 25 180 Google Scholar
[47]	Yu K, Wang H, Zhou Y C, Bai Y Y, Niu Y J 2013 J. Appl. Phys. 113 034105 Google Scholar
[48]	Yu K, Niu Y J, Xiang F, Zhou Y C, Bai Y Y, Wang H 2013 J. Appl. Phys. 114 174107 Google Scholar
[49]	Wu Y H, Zha J W, Yao Z Q, Sun F, Li R K Y, Dang Z M 2015 RSC Adv. 9 44749 Google Scholar
[50]	Huang X Y, Jiang P K 2015 Adv. Mater. 27 546 Google Scholar
[51]	Hu P H, Sun W D, Fan M Z, et al. 2018 Appl. Surf. Sci. 458 743 Google Scholar
[52]	Sun W D, Lu X J, Jiang J Y, Zhang X, Hu P H, Li M, Lin Y H, Nan C W, Shen Y 2017 J. Appl. Phys. 121 244101 Google Scholar
[53]	Shen Z H, Wang J J, Jiang J Y, Lin Y H, Nan C W, Chen L Q, Shen Y 2018 Adv. Energy Mater. 8 1800509 Google Scholar
[54]	Zhu Y K, Zhu Y J, Huang X Y, Chen J, Li Q, He J L, Jiang P K 2019 Adv. Energy Mater. 9 1901826 Google Scholar
[55]	Li Y S, Zhou Y, Zhu Y J, Cheng S, Yuan C, Hu J, He J L, Li Q 2020 J. Mater. Chem. A 8 6576 Google Scholar
[56]	Wu L Y, Wu K, Liu D Y, Huang R, Huo J L, Chen F, Fu Q 2018 J. Mater. Chem. A 6 7573 Google Scholar
[57]	Wu L Y, Wu K, Lei C X, Liu D Y, Du R N, Chen F, Fu Q 2019 J. Mater. Chem. A 7 7664 Google Scholar
[58]	Liu F H, Li Q, Li Z Y, Liu Y, Dong L J, Xiong C X, Wang Q 2017 Compos. Sci. Technol. 142 139 Google Scholar
[59]	Ai D, Li H, Zhou Y, et al. 2020 Adv. Energy Mater. 10 1903881 Google Scholar
[60]	Li H, Ai D, Ren L L, Yao B, Han Z B, Shen Z H, Wang J J, Chen L Q, Wang Q 2019 Adv. Mater. 31 1900875 Google Scholar
[61]	Li H, Ren L L, Ai D, Han Z B, Liu Y, Yao B, Wang Q 2020 InfoMat. 2 389 Google Scholar
[62]	Thakur Y, Zhang T, Iacob C, Yang T N, Bernholc J, Chen L Q, Runt J, Zhang Q M 2017 Nanoscale 9 10992 Google Scholar
[63]	Chadband W G 1992 IEE Rev. 38 404 Google Scholar
[64]	Zhang T, Chen X, Thakur Y, Lu B, Zhang Q Y, Runt J, Zhang Q M 2020 Sci. Adv. 6 6622 Google Scholar
[65]	Thakur Y, Lean M H, Zhang Q M 2017 Appl. Phys. Lett. 110 122905 Google Scholar
[66]	Bouharrasa F E, Raihane M, Ameduri B 2020 Prog. Mater. Sci. 113 100670 Google Scholar
[67]	Niu Y J, Xiang F, Wang Y F, Chen J, Wang H 2018 Phys. Chem. Chem. Phys. 20 6598 Google Scholar
[68]	Niu Y J, Wang H 2019 ACS Appl. Nano Mater. 2 627 Google Scholar
[69]	Zhang X, Li B W, Dong L J, Liu H X, Chen W, Shen Y, Nan C W 2018 Adv. Mater. Interfaces 5 1800096 Google Scholar
[70]	Pan Z B, Yao L M, Zhai J W, Yao X, Chen H 2018 Adv. Mater. 30 1705662 Google Scholar
[71]	Rahimabady M, Mirshekarloo M S, Yao K, Lu L 2013 Phys. Chem. Chem. Phys. 15 16242 Google Scholar
[72]	Liu S, Xue S X, Shen B, Zhai J W 2015 Appl. Phys. Lett. 107 032907 Google Scholar
[73]	Choudhury A 2012 Polym. Int. 61 696 Google Scholar
[74]	Luo H, Zhang D, Jiang C, Yuan X, Chen C, Zhou K C 2015 ACS Appl. Mater. Interfaces 7 8061 Google Scholar
[75]	Liu J, Shen Z H, Xu W H, Zhang Y, Qian X S, Jiang Z H, Zhang Y H 2020 Small 2000714 Google Scholar
[76]	Xu W H, Liu J, Chen T W, Jiang X Y, Qian X S, Zhang Y, Jiang Z H, Zhang Y H 2019 Small 15 1901582 Google Scholar
[77]	Zhou Y, Yuan C, Wang S J, Zhu Y J, Cheng S, Yang X, Yang Y, Hu J, He J L, Li Q 2020 Energy Storage Mater. 28 255 Google Scholar
[78]	Wang Y F, Cui J, Yuan Q B, Niu Y J, Bai Y Y, Wang H 2015 Adv. Mater. 27 6658 Google Scholar
[79]	Wang Y F, Wang L X, Yuan Q B, et al. 2018 Nano Energy 44 364 Google Scholar
[80]	Chen J, Wang Y F, Yuan Q B, Xu X W, Niu Y J, Wang Q, Wang H 2018 Nano Energy 54 288 Google Scholar
[81]	Jiang J Y, Shen Z H, Qian J, Dan Z, Guo M, He Y, Lin Y H, Nan C W, Chen L Q, Shen Y 2019 Nano Energy 62 220 Google Scholar
[82]	Chen J, Wang Y F, Xu X W, Yuan Q B, Niu Y J, Wang Q, Wang H 2019 J. Mater. Chem. A 7 3729 Google Scholar
[83]	Wang Y F, Chen J. Li Y, Niu Y J, Wang Q, Wang H 2019 J. Mater. Chem. A 7 2965 Google Scholar
[84]	Chen X Y, Tseng J K, Treufeld I, Mackey M, Schuele D E, Li R P, Fukuto M, Baer E, Zhu L 2017 J. Mater. Chem. C 5 10417 Google Scholar
[85]	Li Z P, Chen X Y, Zhang C, Baer E, Langhe D, Ponting Ml, Brubaker M, Hosking T, Li R P, Fukuto M, Zhu L 2019 ACS Appl. Polym. Mater. 1 867 Google Scholar
[86]	Tewari P, Rajagopalan R, Furman E, Lanagan M T 2010 Langmuir 26 18817 Google Scholar
[87]	Hu P H, Shen Y, Guan Y H, Zhang X H, Lin Y H, Zhang Q M, Nan C W 2014 Adv. Funct. Mater. 24 3172 Google Scholar
[88]	Pan Z B, Liu B H, Zhai J W, Yao L M, Yang K, Shen B 2017 Nano Energy 40 587 Google Scholar
[89]	Tseng J K, Tang S, Zhou Z, Mackey M, Carr J M, Mu R, Flandin L, Schuele D E, Baer E, Zhu L 2014 Polymer 55 8 Google Scholar
[90]	Mackey M, Hiltner A, Baer E, Flandin L, Wolak M A, Shirk J S 2009 J. Phys. D: Appl. Phys. 42 175304 Google Scholar
[91]	Li Q, Liu F H, Yang T N, Gadinski M R, Zhang G Z, Chen L Q, Wang Q 2016 Proc. Natl. Acad. Sci. U.S.A. 113 9995 Google Scholar
[92]	Azizi A, Gadinski M R, Li Q, AlSaud M A, Wang J J, Wang Y, Wang B, Liu F H, Chen L Q, Alem N, Wang Q 2017 Adv. Mater. 29 1701864 Google Scholar
[93]	Zhou Y, Li Q, Dang B, Yang Y, Shao T, Li H, Hu J, Zeng R, He J L, Wang Q 2018 Adv. Mater. 30 1805672 Google Scholar
[94]	Bonardd S, Moreno-Serna V, Kortaberria G, Díaz D D, Leiva A, Saldías C 2019 Polymer 11 317 Google Scholar
[95]	Peng X W, Wu Q, Jiang S H, Hanif M, Chen S L, Hou H Q 2014 J. Appl. Polym. Sci. 131 40828 Google Scholar
[96]	Zhuang Y B, Seong J G, Lee Y M 2019 Prog. Polym. Sci. 92 35 Google Scholar
[97]	Kao K C 2004 Dielectric Phenomena in Solids (San Diego: Academic Press) p573
[98]	Wang Y, Zhou X, Lin M R, Zhang Q M 2009 Appl. Phys. Lett. 94 154 Google Scholar
[99]	Cheng Z X, Lin M R, Wu S, Thakur Y, Zhou Y, Jeong D Y, Shen Q D, Zhang Q M 2015 Appl. Phys. Lett. 106 202902 Google Scholar
[100]	Wu S, Li W P, Lin M R, Burlingame Q, Chen Q, Payzant A, Xiao K, Zhang Q M 2013 Adv. Mater. 25 1734 Google Scholar
[101]	Qiao Y L, Islam M S, Yin X D, Han K, Yan Y, Zhang J Y, Wang Q, Ploehn H J, Tang C B 2015 Polymer 72 428 Google Scholar
[102]	Yuan X P, Matsuyama Y, Chung T C M 2010 Macromolecules 43 4011 Google Scholar
[103]	Misra M, Agarwal M, Sinkovits D W, Kumar S K, Wang C C, Pilania G, Ramprasad R, Weiss R A, Yuan X P, Mike Chung T C 2014 Macromolecules 47 1122 Google Scholar
[104]	Zhang M, Zhang L, Zhu M, Wang Y G, Li N W, Zhang Z J, Chen Q, An L N, Lin Y H, Nan C W 2016 J. Mater. Chem. A 4 4797 Google Scholar
[105]	Chou Y H, Yen H J, Tsai C L, Lee W Y, Liou G S, Chen W C 2013 J. Mater. Chem. C 1 3235 Google Scholar
[106]	Treufeld I, Wang D H, Kurish B A, Tan L S 2014 J. Mater. Chem. A 2 20683 Google Scholar
[107]	Zhang Z B, Wang D H, Litt M H, Tan L S, Zhu L 2018 Angew. Chem. Int. Ed. 130 1547 Google Scholar
[108]	Zhang Z B, Zheng J F, Premasiri K, Kwok M H, Li Q, Li R P, Zhang S B, Litt M H, Gao X P A, Zhu L 2020 Mater. Horiz. 7 592 Google Scholar
[109]	Yang R Q, Wei R B, Li K, Tong L F, Jia K, Liu X B 2016 Sci. Rep. 6 36434 Google Scholar
[110]	Yang J, Yang X L, Zou Y K, Zhan Y Q, Zhao R, Liu X B 2012 J. Appl. Polym. Sci. 126 1129 Google Scholar
[111]	Hanley T L, Burford R P, Fleming R J, Barber K W 2003 IEEE Electr. Insul. Mag. 19 13 Google Scholar
[112]	Zhou Q, Ma J, Dong S, Li X, Cui G 2019 Adv. Mater. 31 1902029 Google Scholar
[113]	Khanchaitit P, Han K, Gadinski M R, Li Q, Wang Q 2013 Nat. Commun. 4 2845 Google Scholar
[114]	Meereboer N L, Terzić I, van der Steeg P, Portale G, Loos K 2019 J. Mater. Chem. A 7 2795 Google Scholar
[115]	Chen X Z, Li Z W, Cheng Z X, Zhang J Z, Shen Q D, Ge H X, Li H T 2011 Macromol. Rapid Commun. 32 94 Google Scholar
[116]	Tan S, Hu X, Ding S, Zhang Z, Li H, Yang L 2013 J. Mater. Chem. A 1 10353 Google Scholar
[117]	Li H, Gadinski M R, Huang Y Q, et al. 2020 Energy Environ. Sci. 13 1279 Google Scholar
[118]	Chen S Y, Meng G D, Kong B, Xiao B, Wang Z D, Jing Z, Gao Y S, Wu G L, Wang H, Cheng Y H 2020 Chem. Eng. J. 387 123662 Google Scholar
[119]	Wang Y X, Huang X Y, Li T, Wang Z W, Li L Q, Gu X J, Jiang P K 2017 J. Mater. Chem. A 5 20737 Google Scholar
[120]	Hung C C, Wu H C, Chiu Y C, Tung S H, Chen W C 2016 J. Polym. Sci. Polym. Chem. 54 3224 Google Scholar

[1]	Chen Yu-Peng, Shi Lu-Lin, Wang Yu-Yu, Cheng Rui, Yang Jie, Chen Liang-Wen, Fan Wei-Li, Dong Jun-Yu. Internal structural changes in crystals induced by GeV heavy ion beam irradiation of LiF. Acta Physica Sinica, 2024, 73(15): 156401. doi: 10.7498/aps.73.20240717
[2]	Wang Wei, Li Jin-Yang, Mao Guo-Pei, Yang Yan, Gao Zhi-Qiang, Ma Cong, Zhong Xiang-Yu, Shi Qing. Optical fiber high-temperature pressure sensor with weak temperature sensitivity. Acta Physica Sinica, 2024, 73(1): 014208. doi: 10.7498/aps.73.20231155
[3]	Zhuo Jun-Tian, Lin Ming-Hao, Zhang Qi-Yan, Huang Shuang-Wu. Design, fabrication, and high-temperature dielectric energy storage performance of thermoplastic polyimide/aluminum oxide sandwich-structured flexible dielectric films. Acta Physica Sinica, 2024, 73(17): 177701. doi: 10.7498/aps.73.20240838
[4]	Zhang Mao-Lin, Ma Wan-Yu, Wang Lei, Liu Zeng, Yang Li-Li, Li Shan, Tang Wei-Hua, Guo Yu-Feng. Investigation of high-temperature performance of WO₃/β-Ga₂O₃ heterojunction deep-ultraviolet photodetectors. Acta Physica Sinica, 2023, 72(16): 160201. doi: 10.7498/aps.72.20230638
[5]	Pan Peng-Hui, Ji Peng-Fei, Lin Gen, Dong Xi-Ming, Zhao Jin-Hui. Theoretical and experimental research of femtosecond laser processing fused silica. Acta Physica Sinica, 2022, 71(24): 247901. doi: 10.7498/aps.71.20221496
[6]	Li Ming-Zhu, Cai Xiao-Wu, Zeng Chuan-Bin, Li Xiao-Jing, Li Duo-Li, Ni Tao, Wang Juan-Juan, Han Zheng-Sheng, Zhao Fa-Zhan. Effect of high-temperature on holding characteristics in MOSFET ESD protecting device. Acta Physica Sinica, 2022, 71(12): 128501. doi: 10.7498/aps.71.20220172
[7]	Li Zhi-Qiang, Tan Xiao-Yu, Duan Xin-Lei, Zhang Jing-Yi, Yang Jia-Yue. Deep learning molecular dynamics simulation on microwave high-temperature dielectric function of silicon nitride. Acta Physica Sinica, 2022, 71(24): 247803. doi: 10.7498/aps.71.20221002
[8]	Wang Yan-Bin, Liu Qian, Wang Yong, Dai Bo, Wei Xian-Hua. Effects of electrode materials and bias polarities on breakdown behaviors of oxide dielectrics and their mechanisms. Acta Physica Sinica, 2021, 70(8): 087302. doi: 10.7498/aps.70.20201262
[9]	Shen Zhong-Hui, Jiang Yan-Da, Li Bao-Wen, Zhang Xin. Reseach progress of ferroelectric polymer nanocomposites with high energy storage density. Acta Physica Sinica, 2020, 69(21): 217706. doi: 10.7498/aps.69.20201209
[10]	Song Ting, Sun Xiao-Wei, Wei Xiao-Ping, Ouyang Yu-Hua, Zhang Chun-Lin, Guo Peng, Zhao Wei. High-pressure structure prediction and high-temperature structural stability of periclase. Acta Physica Sinica, 2019, 68(12): 126201. doi: 10.7498/aps.68.20190204
[11]	Zhang Xing, Zhang Yi, Zhang Jian-Wei, Zhang Jian, Zhong Chu-Yu, Huang You-Wen, Ning Yong-Qiang, Gu Si-Hong, Wang Li-Jun. 894 nm high temperature operating vertical-cavity surface-emitting laser and its application in Cs chip-scale atomic-clock system. Acta Physica Sinica, 2016, 65(13): 134204. doi: 10.7498/aps.65.134204
[12]	Gao Ying-Jun, Qin He-Lin, Zhou Wen-Quan, Deng Qian-Qian, Luo Zhi-Rong, Huang Chuang-Gao. Phase field crystal simulation of grain boundary annihilation under strain strain at high temperature. Acta Physica Sinica, 2015, 64(10): 106105. doi: 10.7498/aps.64.106105
[13]	Han Yong, Long Xin-Ping, Guo Xiang-Li. Prediction of methane PVT relations at high temperatures by a simplified virial equation of state. Acta Physica Sinica, 2014, 63(15): 150505. doi: 10.7498/aps.63.150505
[14]	Song Yun-Fei, Yu Guo-Yang, Yin He-Dong, Zhang Ming-Fu, Liu Yu-Qiang, Yang Yan-Qiang. Temperature dependence of elastic modulus of single crystal sapphire investigated by laser ultrasonic. Acta Physica Sinica, 2012, 61(6): 064211. doi: 10.7498/aps.61.064211
[15]	Bi Xue-Song, Zhu Liang, Yang Fu-Long. Mechanism of current injection in the process of wire electrical explosion. Acta Physica Sinica, 2012, 61(7): 078105. doi: 10.7498/aps.61.078105
[16]	Fan Zhen-Jun, Geng Xue-Wen, Kong Wen-Jie, Jin Yi-Rong. Measurement of anisotropy thermopower of decagonal AlCuCo quasicrystal. Acta Physica Sinica, 2009, 58(10): 7119-7123. doi: 10.7498/aps.58.7119
[17]	Song Xiao-Shu, Cheng Xin-Lu, Yang Xiang-Dong, Linghu Rong-Feng. Line intensities of 3000—0200 and 1001—0110 transition bands of 14N216O at high temperature. Acta Physica Sinica, 2007, 56(8): 4428-4434. doi: 10.7498/aps.56.4428
[18]	Li Gong-Ping, Zhang Mei-Ling. Energetics and structures of high-temperature copper cluster studied by Monte Carlo method. Acta Physica Sinica, 2005, 54(6): 2873-2876. doi: 10.7498/aps.54.2873
[19]	Li Ling, Li Bo-Zang. The energy density in a one-dimensional cavity with two moving boundaries. Acta Physica Sinica, 2003, 52(11): 2762-2767. doi: 10.7498/aps.52.2762
[20]	TANG LI-JIA, CAI XI-JIE, LIN ZUN-QI. CONTROL OF PULSE SHAPE IN “SHENGGUANG II” MAIN AMPLIFERS. Acta Physica Sinica, 2001, 50(6): 1075-1079. doi: 10.7498/aps.50.1075

Catalog

Vol. 69, Issue 21 - 2020-11-05

Metrics

Abstract views: 19053
PDF Downloads: 779
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板