全固态金属锂电池负极界面问题及解决策略

余启鹏; 刘琦; 王自强; 李宝华

doi:10.7498/aps.69.20201218

摘要

全固态金属锂电池有望提高当前商用锂离子电池的安全性及能量密度, 被广泛认为是下一代电池的重要研发方向. 其中的负极-电解质界面与电池性能紧密相连. 本文将该界面存在的问题划分为静态及动态两方面, 静态问题包括化学不稳定及物理接触差, 体现在电池循环前的巨大阻抗, 动态问题包括枝晶生长及孔洞形成, 体现在电池循环过程性能的快速衰退. 本文就静态及动态问题的起因及其解决策略进行分析, 并对高性能全固态金属锂电池的设计策略作出展望.

关键词:

Abstract

The developing of all-solid-state lithium-metal batteries promises to improve safety and energy density. The challenges in the anode|electrolyte interface are crucial and divided into static and dynamic issues in this review. The static issues are mainly shown as the huge resistances appearing in the assembled batteries, while the dynamic issues are reflected in the rapid deterioration of cycling performance. The static issues are mainly due to the poor chemical stability and interfacial contact, while dendrite growth and void formation are contained in the dynamic issues. Solving dynamic issues on the basis of static issues can conduce to the construction of stable all-solid-state lithium-metal batteries.

Keywords:

作者及机构信息

1.
清华大学深圳国际研究生院, 深圳动力电池安全研究重点实验室, 深圳　518055

2.
清华大学材料学院, 北京　100084

3.
麻省理工学院材料科学与工程系, 剑桥　02139, 美国

通信作者: 李宝华, libh@mail.sz.tsinghua.edu.cn

基金项目: 国家自然科学基金(批准号: 51872157)、广东省珠江人才计划地方创新科研团队项目基金(批准号: 2017BT01N111)、深圳市工信局科技基金(批准号: 20170428145209110)和深圳市科创委科技计划(批准号: JCYJ20170817161753629, JCYJ20170412170911187)资助的课题

Authors and contacts

1.
Shenzhen Key Laboratory on Power Battery Safety Research, Tsinghua Shenzhen International Graduate School, Tsinghua University, Shenzhen 518055, China

2.
School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China

3.
Department of Materials Science and Engineering, Massachusetts Institute of Technology, Cambridge, Massachusetts 02139, United States

Corresponding author: Li Bao-Hua, libh@mail.sz.tsinghua.edu.cn

Funds: Project supported by the National Nature Science Foundation of China (Grant No. 51872157), the Department of Science and Technology of Guangdong Province, China (Grant No. 2017BT01N111), Bureau of Industrial and Information Technology of Shenzhen, China (Grant No. 20170428145209110) and the Science and Technology Innovation Committee of Shenzhen, China (Grants Nos. JCYJ20170817161753629, JCYJ20170412170911187)

文章全文 : translate this paragraph

参考文献

[1]	王朔, 周格, 禹习谦, 李泓 2017 储能科学与技术 6 810 Google Scholar Wang S, Zhou G, Yu X Q, Li H 2017 Energ. Stor. Sci. Technol. 6 810 Google Scholar
[2]	缪平, 姚桢, 刘庆华, 王保国 2020 储能科学与技术 9 670 Liao P, Yao Z, Liu Q H, Wang B G 2020 Energ. Stor. Sci. Technol. 9 670
[3]	王其钰, 王朔, 张杰男, 郑杰允, 禹习谦, 李泓 2017 储能科学与技术 6 1008 Google Scholar Wang Q Y, Wang S, Zhang J N, Zheng J Y, Yu X Q, Li H 2017 Energ. Stor. Sci. Technol. 6 1008 Google Scholar
[4]	王其钰, 王朔, 周格, 张杰男, 郑杰允, 禹习谦, 李泓 2018 67 128501 Google Scholar Wang Q Y, Wang S, Zhou G, Zhang J N, Zheng J Y, Yu X Q, Li H 2018 Acta Phys. Sin. 67 128501 Google Scholar
[5]	肖睿娟, 李泓, 陈立泉 2018 67 128801 Google Scholar Xiao R J, Li H, Chen L Q 2018 Acta Phys. Sin. 67 128801 Google Scholar
[6]	樊亚平, 晏莉琴, 简德超, 吕桃林, 俞梦, 王振宇, 张全生, 解晶莹 2019 储能科学与技术 8 1040 Fan Y P, Yan L Q, Jian D C, Lv T L, Yu M, Wang Z Y, Zhang Q S, Xie J Y 2019 Energ. Stor. Sci. Technol. 8 1040
[7]	陈晓霞, 刘凯, 王保国 2020 储能科学与技术 9 583 Chen X X, Liu K, Wang B G 2020 Energ. Stor. Sci. Technol. 9 583
[8]	Li M, Lu J, Chen Z, Amine K 2018 Adv. Mater. 30 1800561 Google Scholar
[9]	高静, 任文锋, 陈剑 2017 储能科学与技术 6 557 Google Scholar Gao J, Ren W F, Chen J 2017 Energ. Stor. Sci. Technol. 6 557 Google Scholar
[10]	石凯, 安德成, 贺艳兵, 李宝华, 康飞宇 2017 储能科学与技术 6 479 Google Scholar Shi K, An D C, He Y B, Li B H, Kang F Y 2017 Energ. Stor. Sci. Technol. 6 479 Google Scholar
[11]	张涛, 张晓平, 温兆银 2016 储能科学与技术 5 702 Google Scholar Zhang T, Zhang X P, Wen Z Y 2016 Energ. Stor. Sci. Technol. 5 702 Google Scholar
[12]	吴娇杨, 刘品, 胡勇胜, 李泓 2016 储能科学与技术 5 443 Wu J Y, Liu P, Hu Y S, Li H 2016 Energ. Stor. Sci. Technol. 5 443
[13]	Cheng X B, Zhang R, Zhao C Z, Zhang Q 2017 Chem. Rev. 117 10403 Google Scholar
[14]	罗飞, 褚赓, 黄杰, 孙洋, 李泓 2014 储能科学与技术 3 146 Google Scholar Luo F, Chu G, Huang J, Song Y, Li H 2014 Energ. Stor. Sci. Technol. 3 146 Google Scholar
[15]	李杨, 丁飞, 桑林, 钟海, 刘兴江 2016 储能科学与技术 5 615 Google Scholar Li Y, Ding F, Sang L, Zhong H, Liu X J 2016 Energ. Stor. Sci. Technol. 5 615 Google Scholar
[16]	孙滢智, 黄佳琦, 张学强, 张强 2017 储能科学与技术 6 464 Google Scholar Sun Y Z, Huang J Q, Zhang X Q, Zhang Q 2017 Energ. Stor. Sci. Technol. 6 464 Google Scholar
[17]	吴敬华, 姚霞银 2020 储能科学与技术 9 501 Wu J H, Yao X Y 2020 Stor. Sci. Technol. 9 501
[18]	杨建锋, 李林艳, 吴振岳, 王开学 2019 储能科学与技术 8 829 Yang J F, Li L Y, Wu Z Y, Wang K X 2019 Energ. Stor. Sci. Technol. 8 829
[19]	张永龙, 夏会玲, 林久, 陈少杰, 许晓雄 2018 储能科学与技术 7 994 Google Scholar Zhang Y L, Xia H L, Lin J, Chen S J, Xu X X 2018 Energ. Stor. Sci. Technol. 7 994 Google Scholar
[20]	许晓雄, 李泓 2018 储能科学与技术 7 1 Google Scholar Xu X, Li H 2018 Energ. Stor. Sci. Technol. 7 1 Google Scholar
[21]	吴勇民, 吴晓萌, 朱蕾, 徐碇皓, 田文生, 汤卫平 2016 储能科学与技术 5 678 Google Scholar Wu Y M, Wu X M, Zhu L, Xu D H, Tian W S, Tang W P 2016 Energ. Stor. Sci. Technol. 5 678 Google Scholar
[22]	夏求应, 孙硕, 徐璟, 昝峰, 岳继礼, 夏晖 2018 储能科学与技术 7 565 Google Scholar Xia Q, Sun S, Xu J, Zan F, Yue J L, Xia H 2018 Energ. Stor. Sci. Technol. 7 565 Google Scholar
[23]	Zhao Q, Stalin S, Zhao C Z, Archer L A 2020 Nat. Rev. Mater. 5 229 Google Scholar
[24]	李泓 2018 储能科学与技术 7 188 Li H 2018 Energ. Stor. Sci. Technol. 7 188
[25]	Schlenker R, Stepien D, Koch P, Hupfer T, Indris S, Roling B, Miss V, Fuchs A, Wilhelmi M, Ehrenberg H 2020 ACS Appl. Mater. Interfaces 12 20012 Google Scholar
[26]	Porz L, Swamy T, Sheldon B W, Rettenwander D, Frömling T, Thaman H L, Berendts S, Uecker R, Carter W C, Chiang Y M 2017 Adv. Energy Mater. 7 1701003 Google Scholar
[27]	Hartmann P, Leichtweiss T, Busche M R, Schneider M, Reich M, Sann J, Adelhelm P, Janek J 2013 J. Phys. Chem. C 117 21064 Google Scholar
[28]	Wang C, Gong Y, Liu B, Fu K, Yao Y, Hitz E, Li Y, Dai J, Xu S, Luo W 2017 Nano Lett. 17 565 Google Scholar
[29]	Lee Y G, Fujiki S, Jung C, Suzuki N, Yashiro N, Omoda R, Ko D S, Shiratsuchi T, Sugimoto T, Ryu S 2020 Nat. Energy 5 299 Google Scholar
[30]	Hatzell K B, Chen X C, Cobb C L, Dasgupta N P, Dixit M B, Marbella L E, McDowell M T, Mukherjee P P, Verma A, Viswanathan V 2020 ACS Energy Lett. 5 922 Google Scholar
[31]	Albertus P, Babinec S, Litzelman S, Newman A 2018 Nat. Energy 3 16 Google Scholar
[32]	Xu L, Tang S, Cheng Y, Wang K, Liang J, Liu C, Cao Y C, Wei F, Mai L 2018 Joule 2 1991 Google Scholar
[33]	张强, 姚霞银, 张洪周, 张联齐, 许晓雄 2016 储能科学与技术 5 659 Google Scholar Zhang Q, Yao X Y, Zhang H Z, Zhang L Q, Xu X X 2016 Energ. Stor. Sci. Technol. 5 659 Google Scholar
[34]	Xiao Y, Wang Y, Bo S H, Kim J C, Miara L J, Ceder G 2010 Nat. Rev. Mater. 5 105
[35]	Famprikis T, Canepa P, Dawson J A, Islam M S, Masquelier C 2019 Nat. Mater. 18 1278 Google Scholar
[36]	Lewis J A, Tippens J, Cortes F J Q, McDowell M T 2019 Trends in Chem. 1 845 Google Scholar
[37]	Wang P, Qu W, Song W L, Chen H, Chen R, Fang D 2019 Adv. Funct. Mater. 29 1900950
[38]	Liu H, Cheng X B, Huang J Q, Yuan H, Lu Y, Yan C, Zhu G L, Xu R, Zhao C Z, Hou L P 2020 ACS Energy Lett. 5 833 Google Scholar
[39]	黄晓, 吴林斌, 黄祯, 林久, 许晓雄 2020 储能科学与技术 9 479 Huang X, Wu L B, Huang Z, Lin J, Xu X X 2020 Energ. Stor. Sci. Technol. 9 479
[40]	孙兴伟, 王龙龙, 姜丰, 马君, 周新红, 崔光磊 2019 储能科学与技术 8 1024 Sun X W, Wang L L, Jiang F, Ma J, Zhou X H, Cui G L 2019 Energ. Stor. Sci. Technol. 8 1024
[41]	Wang C, Zhang H, Li J, Chai J, Dong S, Cui G 2018 J. Power Sources 397 157 Google Scholar
[42]	Wenzel S, Leichtweiss T, Krüger D, Sann J, Janek J 2015 Solid State Ionics 278 98 Google Scholar
[43]	Alpen U 1979 J. Solid State Chem. 29 379 Google Scholar
[44]	Chung H, Kang B 2017 Chem. Mater. 29 8611 Google Scholar
[45]	Wenzel S, Weber D A, Leichtweiss T, Busche M R, Sann J, Janek J 2016 Solid State Ionics 286 24 Google Scholar
[46]	Wenzel S, Randau S, Leichtweiß T, Weber D A, Sann J, Zeier W G, Janek J 2016 Chem. Mater. 28 2400 Google Scholar
[47]	Ma C, Cheng Y, Yin K, Luo J, Sharafi A, Sakamoto J, Li J, More K L, Dudney N J, Chi M 2016 Nano Lett. 16 7030 Google Scholar
[48]	Rettenwander D, Wagner R, Reyer A, Bonta M, Cheng L, Doeff M M, Limbeck A, Wilkening M, Amthauer G 2018 J. Phys. Chem. C 122 3780
[49]	Kato A, Kowada H, Deguchi M, Hotehama C, Hayashi A, Tatsumisago M 2018 Solid State Ionics 322 1 Google Scholar
[50]	Wood K N, Steirer K X, Hafner S E, et al. 2018 Nat. Commun. 9 1 Google Scholar
[51]	Wenzel S, Sedlmaier S J, Dietrich C, Zeier W G, Janek J 2018 Solid State Ionics 318 102 Google Scholar
[52]	Schwöbel A, Hausbrand R, Jaegermann W 2015 Solid State Ionics 273 51 Google Scholar
[53]	Wolfenstine J, Rangasamy E, Allen J L, Sakamoto J 2012 J. Power Sources 208 193 Google Scholar
[54]	Zhang X, Xiang Q, Tang S, Wang A, Liu X, Luo J 2020 Nano Lett. 20 2871 Google Scholar
[55]	Fu K K, Gong Y, Liu B, Zhu Y, Xu S, Yao Y, Luo W, Wang C, Lacey S D, Dai J 2017 Sci. Adv. 3 e1601659 Google Scholar
[56]	Eustathopoulos N, Voytovych R 2016 J. Mater. Sci. 51 425 Google Scholar
[57]	Rangasamy E, Sahu G, Keum J K, Rondinone A J, Dudney N J, Liang C 2014 J. Mater. Chem. A 2 4111 Google Scholar
[58]	Liu Z, Fu W, Payzant E A, Yu X, Wu Z, Dudney N J, Kiggans J, Hong K, Rondinone A J, Liang C 2013 J. Am. Chem. Soc. 135 975 Google Scholar
[59]	Ishiguro K, Nakata Y, Matsui M, Uechi I, Takeda Y, Yamamoto O, Imanishi N 2013 J. Electrochem. Soc. 160 A1690 Google Scholar
[60]	Ishiguro K, Nemori H, Sunahiro S, Nakata Y, Sudo R, Matsui M, Takeda Y, Yamamoto O, Imanishi N 2014 J. Electrochem. Soc. 161 A668 Google Scholar
[61]	Wan Z, Lei D, Yang W, Liu C, Shi K, Hao X, Shen L, Lv W, Li B, Yang Q H 2019 Adv. Funct. Mater. 29 1805301 Google Scholar
[62]	Han X, Gong Y, Fu K K, He X, Hitz G T, Dai J, Pearse A, Liu B, Wang H, Rubloff G 2017 Nat. Mater. 16 572 Google Scholar
[63]	El Shinawi H, Janek J 2013 J. Power Sources 225 13 Google Scholar
[64]	Thangadurai V, Weppner W 2005 Adv. Funct. Mater. 15 107 Google Scholar
[65]	Buschmann H, Berendts S, Mogwitz B, Janek J 2012 J. Power Sources 206 236 Google Scholar
[66]	Cheng L, Crumlin E J, Chen W, Qiao R, Hou H, Lux S F, Zorba V, Russo R, Kostecki R, Liu Z 2014 Phys. Chem. Chem. Phys. 16 18294 Google Scholar
[67]	Duan H, Chen W P, Fan M, Wang W P, Yu L, Tan S J, Chen X, Zhang Q, Xin S, Wan L J 2020 Angew. Chem. 59 1491 Google Scholar
[68]	Cheng L, Liu M, Mehta A, Xin H, Lin F, Persson K, Chen G, Crumlin E J, Doeff M 2018 ACS Appl. Energy Materials 1 7244 Google Scholar
[69]	Huo H, Chen Y, Zhao N, Lin X, Luo J, Yang X, Liu Y, Guo X, Sun X 2019 Nano Energy 61 119 Google Scholar
[70]	Tian H K, Xu B, Qi Y 2018 J. Power Sources 392 79 Google Scholar
[71]	Luo W, Gong Y, Zhu Y, Li Y, Yao Y, Zhang Y, Fu K, Pastel G, Lin C F, Mo Y 2017 Adv. Mater. 29 1606042 Google Scholar
[72]	Luo W, Gong Y, Zhu Y, Fu K K, Dai J, Lacey S D, Wang C, Liu B, Han X, Mo Y 2016 J. Am. Chem. Soc. 138 12258 Google Scholar
[73]	Hasegawa S, Imanishi N, Zhang T, Xie J, Hirano A, Takeda Y, Yamamoto O 2009 J. Power Sources 189 371 Google Scholar
[74]	Yu Q, Han D, Lu Q, He Y B, Li S, Liu Q, Han C, Kang F, Li B 2019 ACS Appl. Mater. Interfaces 11 9911 Google Scholar
[75]	Sakuma M, Suzuki K, Hirayama M, Kanno R 2016 Solid State Ionics 285 101 Google Scholar
[76]	Ogawa M, Kanda R, Yoshida K, Uemura T, Harada K 2012 J. Power Sources 205 487 Google Scholar
[77]	Nagao M, Hayashi A, Tatsumisago M 2012 Electrochem. 80 734 Google Scholar
[78]	Lin D, Liu Y, Cui Y 2017 Nat. Nanotechnol. 12 194 Google Scholar
[79]	Takeda Y, Yamamoto O, Imanishi N 2016 Electrochem. 84 210 Google Scholar
[80]	张建军, 董甜甜, 杨金凤, 张敏, 崔光磊 2018 储能科学与技术 7 861 Google Scholar Zhang J J, Dong T T, Yang J F, Zhang M, Cui G L 2018 Energ. Stor. Sci. Technol. 7 861 Google Scholar
[81]	Dollé M, Sannier L, Beaudoin B, Trentin M, Tarascon J M 2002 Electrochem. and Solid State Lett. 5 A286 Google Scholar
[82]	Maslyn J A, Loo W S, McEntush K D, Oh H J, Harry K J, Parkinson D Y, Balsara N P 2018 J. Phys. Chem. C 122 26797 Google Scholar
[83]	Monroe C, Newman J 2004 J. Electrochem. Soc. 151 A880 Google Scholar
[84]	Monroe C, Newman J 2005 J. Electrochem. Soc. 152 A396 Google Scholar
[85]	Samsonov G V 2012 Handbook of the Physicochemical Properties of the Elements (Berlin: Springer Science & Business Media) p394
[86]	Schauser N S, Harry K J, Parkinson D Y, Watanabe H, Balsara N P 2014 J. Electrochem. Soc. 162 A398
[87]	Stone G, Mullin S, Teran A, Hallinan D, Minor A, Hexemer A, Balsara N 2012 J. Electrochem. Soc. 159 A222 Google Scholar
[88]	Harry K J, Hallinan D T, Parkinson D Y, MacDowell A A, Balsara N P 2014 Nat. Mater. 13 69 Google Scholar
[89]	Harry K J, Higa K, Srinivasan V, Balsara N P 2016 J. Electrochem. Soc. 163 A2216 Google Scholar
[90]	Golozar M, Hovington P, Paolella A, Bessette S P, Lagacé M, Bouchard P, Demers H, Gauvin R, Zaghib K 2018 Nano Lett. 18 7583 Google Scholar
[91]	Brissot C, Rosso M, Chazalviel J N, Lascaud S 1999 J. Power Sources 81 925
[92]	Kerman K, Luntz A, Viswanathan V, Chiang Y M, Chen Z 2017 J. Electrochem. Soc. 164 A1731 Google Scholar
[93]	Janek J, Zeier W G 2016 Nature Energy 1 1
[94]	周洪, 魏凤, 吴永庆 2020 储能科学与技术 9 1001 Zhou H, Wei F, Wu Y Q 2020 Energ. Stor. Sci. Technol. 9 1001
[95]	Garcia Mendez R, Mizuno F, Zhang R, Arthur T S, Sakamoto J 2017 Electrochim. Acta 237 144 Google Scholar
[96]	Han F, Yue J, Zhu X, Wang C 2018 Adv. Energy Mater. 8 1703644 Google Scholar
[97]	Nagao M, Hayashi A, Tatsumisago M, Kanetsuku T, Tsuda T, Kuwabata S 2013 Phys. Chem. Chem. Phys. 15 18600 Google Scholar
[98]	Aguesse F, Manalastas W, Buannic L, Lopez del Amo J M, Singh G, Llordés A, Kilner J 2017 ACS Appl. Mater. Interfaces 9 3808 Google Scholar
[99]	Cheng L, Chen W, Kunz M, Persson K, Tamura N, Chen G, Doeff M 2015 ACS Appl. Mater. Interfaces 7 2073 Google Scholar
[100]	Ren Y, Shen Y, Lin Y, Nan C W 2015 Electrochem. Commun. 57 27 Google Scholar
[101]	Cheng E J, Sharafi A, Sakamoto J 2017 Electrochim. Acta 223 85 Google Scholar
[102]	Sharafi A, Meyer H M, Nanda J, Wolfenstine J, Sakamoto J 2016 J. Power Sources 302 135 Google Scholar
[103]	Swamy T, Park R, Sheldon B W, Rettenwander D, Porz L, Berendts S, Uecker R, Carter W C, Chiang Y M 2018 J. Electrochem. Soc. 165 A3648 Google Scholar
[104]	Qian J, Henderson W A, Xu W, Bhattacharya P, Engelhard M, Borodin O, Zhang J G 2015 Nat. Commun. 6 1
[105]	Choudhury S, Archer L A 2016 Adv. Electron. Mater. 2 1500246 Google Scholar
[106]	Han F, Westover A S, Yue J, Fan X, Wang F, Chi M, Leonard D N, Dudney N J, Wang H, Wang C 2019 Nat. Energy 4 187 Google Scholar
[107]	Ahmad Z, Viswanathan V 2017 Phys. Rev. Lett. 119 056003 Google Scholar
[108]	Raj R, Wolfenstine J 2017 J. Power Sources 343 119 Google Scholar
[109]	Manalastas W, Rikarte J, Chater R J, Brugge R, Aguadero A, Buannic L, Llordés A, Aguesse F, Kilner J 2019 J. Power Sources 412 287 Google Scholar
[110]	Wang C, Gong Y, Dai J, Zhang L, Xie H, Pastel G, Liu B, Wachsman E, Wang H, Hu L 2017 J. Am. Chem. Soc. 139 14257 Google Scholar
[111]	Seitzman N, Guthrey H, Sulas D B, Platt H A, Al Jassim M, Pylypenko S 2018 J. Electrochem. Soc. 165 A3732 Google Scholar
[112]	Marbella L E, Zekoll S, Kasemchainan J, Emge S P, Bruce P G, Grey C P 2019 Chem. Mater. 31 2762 Google Scholar
[113]	Schmidt R D, Sakamoto J 2016 J. Power Sources 324 126 Google Scholar
[114]	Kim S, Jung C, Kim H, Thomas Alyea K E, Yoon G, Kim B, Badding M E, Song Z, Chang J, Kim J, Im D, Kang K 2020 Adv. Energy Mater. 10 1903993 Google Scholar
[115]	Kazyak E, Garcia Mendez R, LePage W S, Sharafi A, Davis A L, Sanchez A J, Chen K H, Haslam C, Sakamoto J, Dasgupta N P 2020 Matter 2 1025 Google Scholar
[116]	Koshikawa H, Matsuda S, Kamiya K, Miyayama M, Kubo Y, Uosaki K, Hashimoto K, Nakanishi S 2018 J. Power Sources 376 147 Google Scholar
[117]	Kasemchainan J, Zekoll S, Spencer Jolly D, Ning Z, Hartley G O, Marrow J, Bruce P G 2019 Nat. Mater. 18 1105 Google Scholar
[118]	Yu S, Schmidt R D, Garcia Mendez R, Herbert E, Dudney N J, Wolfenstine J B, Sakamoto J, Siegel D J 2016 Chem. Mater. 28 197 Google Scholar
[119]	Iriyama Y, Kako T, Yada C, Abe T, Ogumi Z 2005 Solid State Ionics 176 2371 Google Scholar
[120]	Sharafi A, Kazyak E, Davis A L, Yu S, Thompson T, Siegel D J, Dasgupta N P, Sakamoto J 2017 Chem. Mater. 29 7961 Google Scholar
[121]	Chen Y T, Jena A, Pang W K, Peterson V K, Sheu H S, Chang H, Liu R S 2017 J. Phys. Chem. C 121 15565 Google Scholar
[122]	Han F, Zhu Y, He X, Mo Y, Wang C 2016 Adv. Energy Mater. 6 1501590 Google Scholar
[123]	Doyle M, Fuller T F, Newman J 1994 Electrochim. Acta 39 2073 Google Scholar
[124]	Liu S, Imanishi N, Zhang T, Hirano A, Takeda Y, Yamamoto O, Yang J 2010 J. Power Sources 195 6847 Google Scholar
[125]	Liu S, Imanishi N, Zhang T, Hirano A, Takeda Y, Yamamoto O, Yang J 2010 J. Electrochem. Soc. 157 A1092 Google Scholar
[126]	Zhang X, Wang S, Xue C, Xin C, Lin Y, Shen Y, Li L, Nan C W 2019 Adv. Mater. 31 e1806082 Google Scholar
[127]	Frenck L, Maslyn J A, Loo W S, Parkinson D Y, Balsara N P 2019 ACS Appl. Mater. Interfaces 11 47878 Google Scholar
[128]	Fu J, Yu P, Zhang N, Ren G, Zheng S, Huang W, Long X, Li H, Liu X 2019 Energy & Environ. Sci. 12 1404
[129]	Shao Y, Wang H, Gong Z, Wang D, Zheng B, Zhu J, Lu Y, Hu Y S, Guo X, Li H 2018 ACS Energy Lett. 3 1212 Google Scholar
[130]	Song Y, Yang L, Zhao W, Wang Z, Zhao Y, Wang Z, Zhao Q, Liu H, Pan F 2019 Adv. Energy Mater. 9 1900671 Google Scholar
[131]	Maslyn J A, Frenck L, Loo W S, Parkinson D Y, Balsara N P 2019 ACS Appl. Energy Mater. 2 8197 Google Scholar
[132]	Hiratani M, Miyauchi K, Kudo T 1988 Solid State Ionics 28 1406
[133]	Okita K, Ikeda K i, Sano H, Iriyama Y, Sakaebe H 2011 J. Power Sources 196 2135 Google Scholar
[134]	Krauskopf T, Mogwitz B, Rosenbach C, Zeier W G, Janek J 2019 Adv. Energy Mater. 9 1902568 Google Scholar
[135]	Zhou W, Wang S, Li Y, Xin S, Manthiram A, Goodenough J B 2016 J. Am. Chem. Soc. 138 9385 Google Scholar
[136]	Mai W, Yu Q, Han C, Kang F, Li B 2020 Adv. Funct. Mater. 190991 2
[137]	Liu Q, Zhou D, Shanmukaraj D, Li P, Kang F, Li B, Armand M, Wang G 2020 ACS Energy Lett. 5 1456 Google Scholar
[138]	Li Q, Yi T, Wang X, Pan H, Quan B, Liang T, Guo X, Yu X, Wang H, Huang X 2019 Nano Energy 63 103895 Google Scholar
[139]	Xu S, McOwen D W, Wang C, Zhang L, Luo W, Chen C, Li Y, Gong Y, Dai J, Kuang Y 2018 Nano Lett. 18 3926 Google Scholar
[140]	Liu B, Zhang L, Xu S, McOwen D W, Gong Y, Yang C, Pastel G R, Xie H, Fu K, Dai J 2018 Energy Stor. Mater. 14 376 Google Scholar
[141]	Chen Y, Wang Z, Li X, Yao X, Wang C, Li Y, Xue W, Yu D, Kim S Y, Yang F 2020 Nature 578 251 Google Scholar
[142]	Herring C 1950 J. Appl. Phys. 21 437 Google Scholar
[143]	Frost H J, Ashby M F 1982 Deformation Mechanism Maps: The Plasticity and Creep of Metals and Ceramics (Oxford: Pergamon press) p11
[144]	Sun J, He L, Lo Y C, Xu T, Bi H, Sun L, Zhang Z, Mao S X, Li J 2014 Nat. Mater. 13 1007 Google Scholar
[145]	Tu K N 2007 Solder Joint Technology (Vol. 117) (Berlin: Springer) pp153−181
[146]	Tian L, Li J, Sun J, Ma E, Shan Z W 2013 Sci. Rep. 3 2113 Google Scholar
[147]	Mali M, Roos J, Sonderegger M, Brinkmann D, Heitjans P 1988 J. of Phys. F: Metal Phys. 18 403 Google Scholar
[148]	He Y, Lu C, Liu S, Zheng W, Luo J 2019 Adv. Energy Mater. 9 1901810 Google Scholar
[149]	Kamaya N, Homma K, Yamakawa Y, Hirayama M, Kanno R, Yonemura M, Kamiyama T, Kato Y, Hama S, Kawamoto K 2011 Nat. Mater. 10 682 Google Scholar

施引文献

图 1 全固态金属锂电池中金属锂负极-固态电解质界面的静态问题及动态问题示意图^[25-28]

Fig. 1. Schema of static and dynamic challenges of anode|electrolyte interface in all-solid-state lithium-metal batteries^[25-28].

下载: 全尺寸图片幻灯片

图 2 石榴石型LLZO固态电解质-金属锂界面的扫描电子显微镜(SEM)图像^[54]

Fig. 2. Scanning electron microscope (SEM) image of cross-section garnet-type Li₇La₃Zr₂O₁₂ (LLZO)|lithium metal interface^[54].

下载: 全尺寸图片幻灯片

图 3 NH₄F处理表面污染物转化为LiF包覆层示意图^[67]

Fig. 3. Schematic illustration showing the conversion from contaminated Li_6.4La₃Zr_1.4Ta_0.6O₁₂ (LLZTO) to LiF-coated LLZTO by NH₄F treatment, and the surface stability against air exposure and hostless evolution of Li metal^[67].

下载: 全尺寸图片幻灯片

图 4 金属锂负极-固态电解质界面表征的研究历史^[30]

Fig. 4. Timeline of imaging and characterization of Li-metal anode|solid electrolyte interfaces^[30].

下载: 全尺寸图片幻灯片

图 5 三种不同金属锂不规则沉积空隙型的　(a) X射线断层扫描图, (b) 三维重构图, (c)生长机理示意图; 球状型的 (d) X射线断层扫描图, (e) 三维重构图, (f) 生长机理示意图; 非球型的 (g) X射线断层扫描图, (h) 三维重构图, (i) 生长机理示意图^[82]

Fig. 5. Three different irregular deposition of lithium metal: (a) X-ray tomography, (b) three-dimensional reconstruction, (c) schematic diagram of growth mechanism of void type; (d) X-ray tomography, (e) three-dimensional reconstruction, (f) schematic diagram of growth mechanism of globule type; (g) X-ray tomography, (h) three-dimensional reconstruction, (i) schematic diagram of growth mechanism of protruding nonglobular type^[82].

下载: 全尺寸图片幻灯片

图 6 不同阶段锂枝晶生长的局部电流密度分布图　(a) 0−8.27 C/cm²; (b) 8.27−6.53 C/cm²; (c) 16.53−35.82 C/cm²; (d) 35.82−54.72 C/cm²^[89]

Fig. 6. Mapping of local current density for different stages during the growth of lithium globule: (a) 0−8.27 C/cm²; (b) 8.27−16.53 C/cm²; (c) 16.53−35.82 C/cm²; (d) 35.82−54.72 C/cm²^[89].

下载: 全尺寸图片幻灯片

图 7 (a) 金属锂负极边缘上针状枝晶的SEM图; (b) 聚焦离子束(FIB)打磨后针状枝晶的SEM图; (c) (d) 纳米操纵器推动针状锂枝晶后弯折的SEM图; (e) (f) 纳米操纵器在金属锂表面刮擦的SEM图^[90]

Fig. 7. SEM images showing (a) dendrite on the edge of the anode; (b) milled dendrite using focused ion beam (FIB) showing hollow morphology; (c) the nanomanipulator shown by red circle before scratching the dendrite; (d) the nanomanipulator after scratching the dendrite showing the bent in the nanomanipulator; (e) the nanomanipulator before scratching metallic Li sheet; and (f) the nanomanipulator after scratching metallic Li sheet showing the accumulation of Li on the tip.

下载: 全尺寸图片幻灯片

图 8 (a)锂枝晶在固态电解质中的简化示意图, 其中枝晶顶部的箭头表示来自金属锂的施加压力, 沿着侧面的箭头表示由于沿该界面的摩擦而产生的剪切力; (b) 锂沉积过电势及裂纹拓展应力与缺陷尺寸的关系^[26]

Fig. 8. (a) Simplified schematic of a Li filament in a solid electrolyte matrix; (b) Inverse square root dependence of Li plating overpotential and crack-extension stress (σ_{0, max}) on defect size. Curves for glassy LPS and LLZTO are shown^[26].

下载: 全尺寸图片幻灯片

图 9 金属锂在含有缺陷的LLZO表面沉积行为示意图^[114]

Fig. 9. Schematic descriptions of uneven lithium-ion flux induced by surface morphological fluctuations and the corresponding inhomogeneous lithium deposition^[114].

下载: 全尺寸图片幻灯片

图 10 金属锂在含有金界面层的LLZO表面沉积行为示意图^[114]

Fig. 10. Schematic description of lithium redistribution through the gold layer and lithium nucleation. ^[114].

下载: 全尺寸图片幻灯片

图 11 (a) LLCZN及 (b) LLCZN@LAO的金属锂对称电池的极化曲线; (c) 稳态电流与施加电压的关系图(插图: 电流与施加施加电压的时间关系图); (d)锂枝晶在电解质内部生长及抑制枝晶生长的示意图^[130]

Fig. 11. Lithium platting/stripping performance of (a) LLCZN and (b) LLCZN@LAO in Li symmetric cells at different current densities; (c) values of I_s for LLCZN and LLCZN@LAO with different applied external voltages; chronoamperometry results of LLCZN and LLCZN@LAO with an applied external voltage of 1 V (inset); (d) schematic illustrations of Li formation within LLCZN and how to suppress it through surface coating ^[130].

下载: 全尺寸图片幻灯片

图 12 (a)“电化学过滤”法示意图; (b)“电化学过滤”法对应的电化学曲线; (c) 处理前的X射线断层扫描图; (d)和(e)“电化学过滤”法处理后的X射线断层扫描图^[131]

Fig. 12. (a) Schematic of the electrochemical filtering treatment; (b) Current density and voltage of one electrochemical filtering treatment over time; (c) Slice through a reconstructed volume of a symmetric cell after 14 conditioning cycles. No inhomogeneities were observed at the interfaces, (d) (e) Slices through a reconstructed volume of the symmetric cell in (c) after an electrochemical filtering treatment ^[131].

下载: 全尺寸图片幻灯片

图 13 基于LAGP高性能金属锂电池中自愈合界面的设计与构造: Li |LAGP| LMO电池在不同界面修饰层作用下循环过程中的界面演变行为示意图　(a) 无界面修饰层; (b) 凝胶电解质修饰层; (c) 自愈合界面修饰层^[135]

Fig. 13. Design and fabrication of the SHE Janus interfaces for high-performance LAGP-based lithium metal batteries. (a)−(c) Schematic illustrations of the interfacial evolution in Li|LAGP|LMO batteries without interface layers and with GPEs and SHEs as Janus interface layers during cycling, respectively^[135].

下载: 全尺寸图片幻灯片

图 14 (a)原始金属锂电极和石榴石型固态电解质在剥离/沉积过程相互作用示意图; (b)金属锂-PDMS复合电极和石榴石型固态电解质在剥离/沉积过程相互作用示意图^[54]

Fig. 14. Schematic illustration of the (a) pristine lithium foil with garnet-type electrolyte; (b) stress self-adapted interface by using compressible PDMS/Li metal anode^[54].

下载: 全尺寸图片幻灯片

图 15 (a)基于MIEC三维管状集流体的金属锂负极结构示意图; (b)金属锂在碳基小管内以单晶形式沉积的TEM图; (c)碳基小管在沉积金属锂前后的高分辨TEM图^[141]

Fig. 15. (a)Schematic process of creep-enabled Li deposition/stripping in an MIEC tubular matrix, where Coble creep dominates via interfacial diffusion along the MIEC/Li_bcc incoherent interface; (b) TEM images of the Li metal deposition inside the carbon tubule as a single crystal; (c) high-resolution TEM imaging of a tubule before plating ^[141].

下载: 全尺寸图片幻灯片

表 1 不同界面问题解决策略的优劣比较

Table 1. Comparison of advantages and disadvantages of different interfacial strategies.

界面问题	解决策略	优点	不足	参考文献
静态问题	加热	易实现、对聚合物电解质效果显著	对疏锂的无机固态电解质无效、无法解决化学稳定性差问题	[61,62]
	加压	易实现、效果显著	仅在装配前加压不能解决动态问题、电池运行加压实用性低、无法解决化学稳定性差问题	[57—60]
	掺杂	对无机固态电解质有效、能一定程度解决化学稳定性差问题	易降低离子电导率	[63—65]
	电解质纯化	有望促使金属锂均匀沉积	无法避免杂质再次形成	[66,68—70]
	NH₄F预处理	避免污染物再次形成、有望抑制锂枝晶	需防范HF污染	[67]
	界面修饰	能同时解决两种静态问题	薄膜制备工艺成本高、生产效率较低	[28,55,62,71—74]
	锂合金负极	能同时解决两种静态问题、对动态问题也有帮助	降低负极比能量密度	[75—77,132—134]
动态问题	聚合物电解质改性	综合提高固态电解质的离子电导率、机械强度等	影响因素较多且效果相对有限	[86,124—127]
	引入反应界面层	结合界面层与锂合金负极的优点	薄膜制备工艺成本高、生产效率低	[28,55,62,71,72, 114,128,129]
	晶粒表面包覆	降低固态电解质电子电导率抑制枝晶生长	热处理时需要避免元素扩散	[130]
	金属锂负极纯化	有效避免金属锂的不均匀沉积及剥离	亟需开发大规模、低成本的生产方法	[131]
	聚合物复合界面	有效解决静态问题及消除体积变化所带来的应力	引入额外的界面阻碍电荷转移、制备超薄的聚合物界面层难度大	[135,136]
	弹性集流体	可逆地储存及释放应力	降低金属负极的电子电导率	[54]
	三维结构	为金属锂沉积预留体积	大规模制备具挑战	[138—141]

下载: 导出CSV

map

[1]	王朔, 周格, 禹习谦, 李泓 2017 储能科学与技术 6 810 Google Scholar Wang S, Zhou G, Yu X Q, Li H 2017 Energ. Stor. Sci. Technol. 6 810 Google Scholar
[2]	缪平, 姚桢, 刘庆华, 王保国 2020 储能科学与技术 9 670 Liao P, Yao Z, Liu Q H, Wang B G 2020 Energ. Stor. Sci. Technol. 9 670
[3]	王其钰, 王朔, 张杰男, 郑杰允, 禹习谦, 李泓 2017 储能科学与技术 6 1008 Google Scholar Wang Q Y, Wang S, Zhang J N, Zheng J Y, Yu X Q, Li H 2017 Energ. Stor. Sci. Technol. 6 1008 Google Scholar
[4]	王其钰, 王朔, 周格, 张杰男, 郑杰允, 禹习谦, 李泓 2018 67 128501 Google Scholar Wang Q Y, Wang S, Zhou G, Zhang J N, Zheng J Y, Yu X Q, Li H 2018 Acta Phys. Sin. 67 128501 Google Scholar
[5]	肖睿娟, 李泓, 陈立泉 2018 67 128801 Google Scholar Xiao R J, Li H, Chen L Q 2018 Acta Phys. Sin. 67 128801 Google Scholar
[6]	樊亚平, 晏莉琴, 简德超, 吕桃林, 俞梦, 王振宇, 张全生, 解晶莹 2019 储能科学与技术 8 1040 Fan Y P, Yan L Q, Jian D C, Lv T L, Yu M, Wang Z Y, Zhang Q S, Xie J Y 2019 Energ. Stor. Sci. Technol. 8 1040
[7]	陈晓霞, 刘凯, 王保国 2020 储能科学与技术 9 583 Chen X X, Liu K, Wang B G 2020 Energ. Stor. Sci. Technol. 9 583
[8]	Li M, Lu J, Chen Z, Amine K 2018 Adv. Mater. 30 1800561 Google Scholar
[9]	高静, 任文锋, 陈剑 2017 储能科学与技术 6 557 Google Scholar Gao J, Ren W F, Chen J 2017 Energ. Stor. Sci. Technol. 6 557 Google Scholar
[10]	石凯, 安德成, 贺艳兵, 李宝华, 康飞宇 2017 储能科学与技术 6 479 Google Scholar Shi K, An D C, He Y B, Li B H, Kang F Y 2017 Energ. Stor. Sci. Technol. 6 479 Google Scholar
[11]	张涛, 张晓平, 温兆银 2016 储能科学与技术 5 702 Google Scholar Zhang T, Zhang X P, Wen Z Y 2016 Energ. Stor. Sci. Technol. 5 702 Google Scholar
[12]	吴娇杨, 刘品, 胡勇胜, 李泓 2016 储能科学与技术 5 443 Wu J Y, Liu P, Hu Y S, Li H 2016 Energ. Stor. Sci. Technol. 5 443
[13]	Cheng X B, Zhang R, Zhao C Z, Zhang Q 2017 Chem. Rev. 117 10403 Google Scholar
[14]	罗飞, 褚赓, 黄杰, 孙洋, 李泓 2014 储能科学与技术 3 146 Google Scholar Luo F, Chu G, Huang J, Song Y, Li H 2014 Energ. Stor. Sci. Technol. 3 146 Google Scholar
[15]	李杨, 丁飞, 桑林, 钟海, 刘兴江 2016 储能科学与技术 5 615 Google Scholar Li Y, Ding F, Sang L, Zhong H, Liu X J 2016 Energ. Stor. Sci. Technol. 5 615 Google Scholar
[16]	孙滢智, 黄佳琦, 张学强, 张强 2017 储能科学与技术 6 464 Google Scholar Sun Y Z, Huang J Q, Zhang X Q, Zhang Q 2017 Energ. Stor. Sci. Technol. 6 464 Google Scholar
[17]	吴敬华, 姚霞银 2020 储能科学与技术 9 501 Wu J H, Yao X Y 2020 Stor. Sci. Technol. 9 501
[18]	杨建锋, 李林艳, 吴振岳, 王开学 2019 储能科学与技术 8 829 Yang J F, Li L Y, Wu Z Y, Wang K X 2019 Energ. Stor. Sci. Technol. 8 829
[19]	张永龙, 夏会玲, 林久, 陈少杰, 许晓雄 2018 储能科学与技术 7 994 Google Scholar Zhang Y L, Xia H L, Lin J, Chen S J, Xu X X 2018 Energ. Stor. Sci. Technol. 7 994 Google Scholar
[20]	许晓雄, 李泓 2018 储能科学与技术 7 1 Google Scholar Xu X, Li H 2018 Energ. Stor. Sci. Technol. 7 1 Google Scholar
[21]	吴勇民, 吴晓萌, 朱蕾, 徐碇皓, 田文生, 汤卫平 2016 储能科学与技术 5 678 Google Scholar Wu Y M, Wu X M, Zhu L, Xu D H, Tian W S, Tang W P 2016 Energ. Stor. Sci. Technol. 5 678 Google Scholar
[22]	夏求应, 孙硕, 徐璟, 昝峰, 岳继礼, 夏晖 2018 储能科学与技术 7 565 Google Scholar Xia Q, Sun S, Xu J, Zan F, Yue J L, Xia H 2018 Energ. Stor. Sci. Technol. 7 565 Google Scholar
[23]	Zhao Q, Stalin S, Zhao C Z, Archer L A 2020 Nat. Rev. Mater. 5 229 Google Scholar
[24]	李泓 2018 储能科学与技术 7 188 Li H 2018 Energ. Stor. Sci. Technol. 7 188
[25]	Schlenker R, Stepien D, Koch P, Hupfer T, Indris S, Roling B, Miss V, Fuchs A, Wilhelmi M, Ehrenberg H 2020 ACS Appl. Mater. Interfaces 12 20012 Google Scholar
[26]	Porz L, Swamy T, Sheldon B W, Rettenwander D, Frömling T, Thaman H L, Berendts S, Uecker R, Carter W C, Chiang Y M 2017 Adv. Energy Mater. 7 1701003 Google Scholar
[27]	Hartmann P, Leichtweiss T, Busche M R, Schneider M, Reich M, Sann J, Adelhelm P, Janek J 2013 J. Phys. Chem. C 117 21064 Google Scholar
[28]	Wang C, Gong Y, Liu B, Fu K, Yao Y, Hitz E, Li Y, Dai J, Xu S, Luo W 2017 Nano Lett. 17 565 Google Scholar
[29]	Lee Y G, Fujiki S, Jung C, Suzuki N, Yashiro N, Omoda R, Ko D S, Shiratsuchi T, Sugimoto T, Ryu S 2020 Nat. Energy 5 299 Google Scholar
[30]	Hatzell K B, Chen X C, Cobb C L, Dasgupta N P, Dixit M B, Marbella L E, McDowell M T, Mukherjee P P, Verma A, Viswanathan V 2020 ACS Energy Lett. 5 922 Google Scholar
[31]	Albertus P, Babinec S, Litzelman S, Newman A 2018 Nat. Energy 3 16 Google Scholar
[32]	Xu L, Tang S, Cheng Y, Wang K, Liang J, Liu C, Cao Y C, Wei F, Mai L 2018 Joule 2 1991 Google Scholar
[33]	张强, 姚霞银, 张洪周, 张联齐, 许晓雄 2016 储能科学与技术 5 659 Google Scholar Zhang Q, Yao X Y, Zhang H Z, Zhang L Q, Xu X X 2016 Energ. Stor. Sci. Technol. 5 659 Google Scholar
[34]	Xiao Y, Wang Y, Bo S H, Kim J C, Miara L J, Ceder G 2010 Nat. Rev. Mater. 5 105
[35]	Famprikis T, Canepa P, Dawson J A, Islam M S, Masquelier C 2019 Nat. Mater. 18 1278 Google Scholar
[36]	Lewis J A, Tippens J, Cortes F J Q, McDowell M T 2019 Trends in Chem. 1 845 Google Scholar
[37]	Wang P, Qu W, Song W L, Chen H, Chen R, Fang D 2019 Adv. Funct. Mater. 29 1900950
[38]	Liu H, Cheng X B, Huang J Q, Yuan H, Lu Y, Yan C, Zhu G L, Xu R, Zhao C Z, Hou L P 2020 ACS Energy Lett. 5 833 Google Scholar
[39]	黄晓, 吴林斌, 黄祯, 林久, 许晓雄 2020 储能科学与技术 9 479 Huang X, Wu L B, Huang Z, Lin J, Xu X X 2020 Energ. Stor. Sci. Technol. 9 479
[40]	孙兴伟, 王龙龙, 姜丰, 马君, 周新红, 崔光磊 2019 储能科学与技术 8 1024 Sun X W, Wang L L, Jiang F, Ma J, Zhou X H, Cui G L 2019 Energ. Stor. Sci. Technol. 8 1024
[41]	Wang C, Zhang H, Li J, Chai J, Dong S, Cui G 2018 J. Power Sources 397 157 Google Scholar
[42]	Wenzel S, Leichtweiss T, Krüger D, Sann J, Janek J 2015 Solid State Ionics 278 98 Google Scholar
[43]	Alpen U 1979 J. Solid State Chem. 29 379 Google Scholar
[44]	Chung H, Kang B 2017 Chem. Mater. 29 8611 Google Scholar
[45]	Wenzel S, Weber D A, Leichtweiss T, Busche M R, Sann J, Janek J 2016 Solid State Ionics 286 24 Google Scholar
[46]	Wenzel S, Randau S, Leichtweiß T, Weber D A, Sann J, Zeier W G, Janek J 2016 Chem. Mater. 28 2400 Google Scholar
[47]	Ma C, Cheng Y, Yin K, Luo J, Sharafi A, Sakamoto J, Li J, More K L, Dudney N J, Chi M 2016 Nano Lett. 16 7030 Google Scholar
[48]	Rettenwander D, Wagner R, Reyer A, Bonta M, Cheng L, Doeff M M, Limbeck A, Wilkening M, Amthauer G 2018 J. Phys. Chem. C 122 3780
[49]	Kato A, Kowada H, Deguchi M, Hotehama C, Hayashi A, Tatsumisago M 2018 Solid State Ionics 322 1 Google Scholar
[50]	Wood K N, Steirer K X, Hafner S E, et al. 2018 Nat. Commun. 9 1 Google Scholar
[51]	Wenzel S, Sedlmaier S J, Dietrich C, Zeier W G, Janek J 2018 Solid State Ionics 318 102 Google Scholar
[52]	Schwöbel A, Hausbrand R, Jaegermann W 2015 Solid State Ionics 273 51 Google Scholar
[53]	Wolfenstine J, Rangasamy E, Allen J L, Sakamoto J 2012 J. Power Sources 208 193 Google Scholar
[54]	Zhang X, Xiang Q, Tang S, Wang A, Liu X, Luo J 2020 Nano Lett. 20 2871 Google Scholar
[55]	Fu K K, Gong Y, Liu B, Zhu Y, Xu S, Yao Y, Luo W, Wang C, Lacey S D, Dai J 2017 Sci. Adv. 3 e1601659 Google Scholar
[56]	Eustathopoulos N, Voytovych R 2016 J. Mater. Sci. 51 425 Google Scholar
[57]	Rangasamy E, Sahu G, Keum J K, Rondinone A J, Dudney N J, Liang C 2014 J. Mater. Chem. A 2 4111 Google Scholar
[58]	Liu Z, Fu W, Payzant E A, Yu X, Wu Z, Dudney N J, Kiggans J, Hong K, Rondinone A J, Liang C 2013 J. Am. Chem. Soc. 135 975 Google Scholar
[59]	Ishiguro K, Nakata Y, Matsui M, Uechi I, Takeda Y, Yamamoto O, Imanishi N 2013 J. Electrochem. Soc. 160 A1690 Google Scholar
[60]	Ishiguro K, Nemori H, Sunahiro S, Nakata Y, Sudo R, Matsui M, Takeda Y, Yamamoto O, Imanishi N 2014 J. Electrochem. Soc. 161 A668 Google Scholar
[61]	Wan Z, Lei D, Yang W, Liu C, Shi K, Hao X, Shen L, Lv W, Li B, Yang Q H 2019 Adv. Funct. Mater. 29 1805301 Google Scholar
[62]	Han X, Gong Y, Fu K K, He X, Hitz G T, Dai J, Pearse A, Liu B, Wang H, Rubloff G 2017 Nat. Mater. 16 572 Google Scholar
[63]	El Shinawi H, Janek J 2013 J. Power Sources 225 13 Google Scholar
[64]	Thangadurai V, Weppner W 2005 Adv. Funct. Mater. 15 107 Google Scholar
[65]	Buschmann H, Berendts S, Mogwitz B, Janek J 2012 J. Power Sources 206 236 Google Scholar
[66]	Cheng L, Crumlin E J, Chen W, Qiao R, Hou H, Lux S F, Zorba V, Russo R, Kostecki R, Liu Z 2014 Phys. Chem. Chem. Phys. 16 18294 Google Scholar
[67]	Duan H, Chen W P, Fan M, Wang W P, Yu L, Tan S J, Chen X, Zhang Q, Xin S, Wan L J 2020 Angew. Chem. 59 1491 Google Scholar
[68]	Cheng L, Liu M, Mehta A, Xin H, Lin F, Persson K, Chen G, Crumlin E J, Doeff M 2018 ACS Appl. Energy Materials 1 7244 Google Scholar
[69]	Huo H, Chen Y, Zhao N, Lin X, Luo J, Yang X, Liu Y, Guo X, Sun X 2019 Nano Energy 61 119 Google Scholar
[70]	Tian H K, Xu B, Qi Y 2018 J. Power Sources 392 79 Google Scholar
[71]	Luo W, Gong Y, Zhu Y, Li Y, Yao Y, Zhang Y, Fu K, Pastel G, Lin C F, Mo Y 2017 Adv. Mater. 29 1606042 Google Scholar
[72]	Luo W, Gong Y, Zhu Y, Fu K K, Dai J, Lacey S D, Wang C, Liu B, Han X, Mo Y 2016 J. Am. Chem. Soc. 138 12258 Google Scholar
[73]	Hasegawa S, Imanishi N, Zhang T, Xie J, Hirano A, Takeda Y, Yamamoto O 2009 J. Power Sources 189 371 Google Scholar
[74]	Yu Q, Han D, Lu Q, He Y B, Li S, Liu Q, Han C, Kang F, Li B 2019 ACS Appl. Mater. Interfaces 11 9911 Google Scholar
[75]	Sakuma M, Suzuki K, Hirayama M, Kanno R 2016 Solid State Ionics 285 101 Google Scholar
[76]	Ogawa M, Kanda R, Yoshida K, Uemura T, Harada K 2012 J. Power Sources 205 487 Google Scholar
[77]	Nagao M, Hayashi A, Tatsumisago M 2012 Electrochem. 80 734 Google Scholar
[78]	Lin D, Liu Y, Cui Y 2017 Nat. Nanotechnol. 12 194 Google Scholar
[79]	Takeda Y, Yamamoto O, Imanishi N 2016 Electrochem. 84 210 Google Scholar
[80]	张建军, 董甜甜, 杨金凤, 张敏, 崔光磊 2018 储能科学与技术 7 861 Google Scholar Zhang J J, Dong T T, Yang J F, Zhang M, Cui G L 2018 Energ. Stor. Sci. Technol. 7 861 Google Scholar
[81]	Dollé M, Sannier L, Beaudoin B, Trentin M, Tarascon J M 2002 Electrochem. and Solid State Lett. 5 A286 Google Scholar
[82]	Maslyn J A, Loo W S, McEntush K D, Oh H J, Harry K J, Parkinson D Y, Balsara N P 2018 J. Phys. Chem. C 122 26797 Google Scholar
[83]	Monroe C, Newman J 2004 J. Electrochem. Soc. 151 A880 Google Scholar
[84]	Monroe C, Newman J 2005 J. Electrochem. Soc. 152 A396 Google Scholar
[85]	Samsonov G V 2012 Handbook of the Physicochemical Properties of the Elements (Berlin: Springer Science & Business Media) p394
[86]	Schauser N S, Harry K J, Parkinson D Y, Watanabe H, Balsara N P 2014 J. Electrochem. Soc. 162 A398
[87]	Stone G, Mullin S, Teran A, Hallinan D, Minor A, Hexemer A, Balsara N 2012 J. Electrochem. Soc. 159 A222 Google Scholar
[88]	Harry K J, Hallinan D T, Parkinson D Y, MacDowell A A, Balsara N P 2014 Nat. Mater. 13 69 Google Scholar
[89]	Harry K J, Higa K, Srinivasan V, Balsara N P 2016 J. Electrochem. Soc. 163 A2216 Google Scholar
[90]	Golozar M, Hovington P, Paolella A, Bessette S P, Lagacé M, Bouchard P, Demers H, Gauvin R, Zaghib K 2018 Nano Lett. 18 7583 Google Scholar
[91]	Brissot C, Rosso M, Chazalviel J N, Lascaud S 1999 J. Power Sources 81 925
[92]	Kerman K, Luntz A, Viswanathan V, Chiang Y M, Chen Z 2017 J. Electrochem. Soc. 164 A1731 Google Scholar
[93]	Janek J, Zeier W G 2016 Nature Energy 1 1
[94]	周洪, 魏凤, 吴永庆 2020 储能科学与技术 9 1001 Zhou H, Wei F, Wu Y Q 2020 Energ. Stor. Sci. Technol. 9 1001
[95]	Garcia Mendez R, Mizuno F, Zhang R, Arthur T S, Sakamoto J 2017 Electrochim. Acta 237 144 Google Scholar
[96]	Han F, Yue J, Zhu X, Wang C 2018 Adv. Energy Mater. 8 1703644 Google Scholar
[97]	Nagao M, Hayashi A, Tatsumisago M, Kanetsuku T, Tsuda T, Kuwabata S 2013 Phys. Chem. Chem. Phys. 15 18600 Google Scholar
[98]	Aguesse F, Manalastas W, Buannic L, Lopez del Amo J M, Singh G, Llordés A, Kilner J 2017 ACS Appl. Mater. Interfaces 9 3808 Google Scholar
[99]	Cheng L, Chen W, Kunz M, Persson K, Tamura N, Chen G, Doeff M 2015 ACS Appl. Mater. Interfaces 7 2073 Google Scholar
[100]	Ren Y, Shen Y, Lin Y, Nan C W 2015 Electrochem. Commun. 57 27 Google Scholar
[101]	Cheng E J, Sharafi A, Sakamoto J 2017 Electrochim. Acta 223 85 Google Scholar
[102]	Sharafi A, Meyer H M, Nanda J, Wolfenstine J, Sakamoto J 2016 J. Power Sources 302 135 Google Scholar
[103]	Swamy T, Park R, Sheldon B W, Rettenwander D, Porz L, Berendts S, Uecker R, Carter W C, Chiang Y M 2018 J. Electrochem. Soc. 165 A3648 Google Scholar
[104]	Qian J, Henderson W A, Xu W, Bhattacharya P, Engelhard M, Borodin O, Zhang J G 2015 Nat. Commun. 6 1
[105]	Choudhury S, Archer L A 2016 Adv. Electron. Mater. 2 1500246 Google Scholar
[106]	Han F, Westover A S, Yue J, Fan X, Wang F, Chi M, Leonard D N, Dudney N J, Wang H, Wang C 2019 Nat. Energy 4 187 Google Scholar
[107]	Ahmad Z, Viswanathan V 2017 Phys. Rev. Lett. 119 056003 Google Scholar
[108]	Raj R, Wolfenstine J 2017 J. Power Sources 343 119 Google Scholar
[109]	Manalastas W, Rikarte J, Chater R J, Brugge R, Aguadero A, Buannic L, Llordés A, Aguesse F, Kilner J 2019 J. Power Sources 412 287 Google Scholar
[110]	Wang C, Gong Y, Dai J, Zhang L, Xie H, Pastel G, Liu B, Wachsman E, Wang H, Hu L 2017 J. Am. Chem. Soc. 139 14257 Google Scholar
[111]	Seitzman N, Guthrey H, Sulas D B, Platt H A, Al Jassim M, Pylypenko S 2018 J. Electrochem. Soc. 165 A3732 Google Scholar
[112]	Marbella L E, Zekoll S, Kasemchainan J, Emge S P, Bruce P G, Grey C P 2019 Chem. Mater. 31 2762 Google Scholar
[113]	Schmidt R D, Sakamoto J 2016 J. Power Sources 324 126 Google Scholar
[114]	Kim S, Jung C, Kim H, Thomas Alyea K E, Yoon G, Kim B, Badding M E, Song Z, Chang J, Kim J, Im D, Kang K 2020 Adv. Energy Mater. 10 1903993 Google Scholar
[115]	Kazyak E, Garcia Mendez R, LePage W S, Sharafi A, Davis A L, Sanchez A J, Chen K H, Haslam C, Sakamoto J, Dasgupta N P 2020 Matter 2 1025 Google Scholar
[116]	Koshikawa H, Matsuda S, Kamiya K, Miyayama M, Kubo Y, Uosaki K, Hashimoto K, Nakanishi S 2018 J. Power Sources 376 147 Google Scholar
[117]	Kasemchainan J, Zekoll S, Spencer Jolly D, Ning Z, Hartley G O, Marrow J, Bruce P G 2019 Nat. Mater. 18 1105 Google Scholar
[118]	Yu S, Schmidt R D, Garcia Mendez R, Herbert E, Dudney N J, Wolfenstine J B, Sakamoto J, Siegel D J 2016 Chem. Mater. 28 197 Google Scholar
[119]	Iriyama Y, Kako T, Yada C, Abe T, Ogumi Z 2005 Solid State Ionics 176 2371 Google Scholar
[120]	Sharafi A, Kazyak E, Davis A L, Yu S, Thompson T, Siegel D J, Dasgupta N P, Sakamoto J 2017 Chem. Mater. 29 7961 Google Scholar
[121]	Chen Y T, Jena A, Pang W K, Peterson V K, Sheu H S, Chang H, Liu R S 2017 J. Phys. Chem. C 121 15565 Google Scholar
[122]	Han F, Zhu Y, He X, Mo Y, Wang C 2016 Adv. Energy Mater. 6 1501590 Google Scholar
[123]	Doyle M, Fuller T F, Newman J 1994 Electrochim. Acta 39 2073 Google Scholar
[124]	Liu S, Imanishi N, Zhang T, Hirano A, Takeda Y, Yamamoto O, Yang J 2010 J. Power Sources 195 6847 Google Scholar
[125]	Liu S, Imanishi N, Zhang T, Hirano A, Takeda Y, Yamamoto O, Yang J 2010 J. Electrochem. Soc. 157 A1092 Google Scholar
[126]	Zhang X, Wang S, Xue C, Xin C, Lin Y, Shen Y, Li L, Nan C W 2019 Adv. Mater. 31 e1806082 Google Scholar
[127]	Frenck L, Maslyn J A, Loo W S, Parkinson D Y, Balsara N P 2019 ACS Appl. Mater. Interfaces 11 47878 Google Scholar
[128]	Fu J, Yu P, Zhang N, Ren G, Zheng S, Huang W, Long X, Li H, Liu X 2019 Energy & Environ. Sci. 12 1404
[129]	Shao Y, Wang H, Gong Z, Wang D, Zheng B, Zhu J, Lu Y, Hu Y S, Guo X, Li H 2018 ACS Energy Lett. 3 1212 Google Scholar
[130]	Song Y, Yang L, Zhao W, Wang Z, Zhao Y, Wang Z, Zhao Q, Liu H, Pan F 2019 Adv. Energy Mater. 9 1900671 Google Scholar
[131]	Maslyn J A, Frenck L, Loo W S, Parkinson D Y, Balsara N P 2019 ACS Appl. Energy Mater. 2 8197 Google Scholar
[132]	Hiratani M, Miyauchi K, Kudo T 1988 Solid State Ionics 28 1406
[133]	Okita K, Ikeda K i, Sano H, Iriyama Y, Sakaebe H 2011 J. Power Sources 196 2135 Google Scholar
[134]	Krauskopf T, Mogwitz B, Rosenbach C, Zeier W G, Janek J 2019 Adv. Energy Mater. 9 1902568 Google Scholar
[135]	Zhou W, Wang S, Li Y, Xin S, Manthiram A, Goodenough J B 2016 J. Am. Chem. Soc. 138 9385 Google Scholar
[136]	Mai W, Yu Q, Han C, Kang F, Li B 2020 Adv. Funct. Mater. 190991 2
[137]	Liu Q, Zhou D, Shanmukaraj D, Li P, Kang F, Li B, Armand M, Wang G 2020 ACS Energy Lett. 5 1456 Google Scholar
[138]	Li Q, Yi T, Wang X, Pan H, Quan B, Liang T, Guo X, Yu X, Wang H, Huang X 2019 Nano Energy 63 103895 Google Scholar
[139]	Xu S, McOwen D W, Wang C, Zhang L, Luo W, Chen C, Li Y, Gong Y, Dai J, Kuang Y 2018 Nano Lett. 18 3926 Google Scholar
[140]	Liu B, Zhang L, Xu S, McOwen D W, Gong Y, Yang C, Pastel G R, Xie H, Fu K, Dai J 2018 Energy Stor. Mater. 14 376 Google Scholar
[141]	Chen Y, Wang Z, Li X, Yao X, Wang C, Li Y, Xue W, Yu D, Kim S Y, Yang F 2020 Nature 578 251 Google Scholar
[142]	Herring C 1950 J. Appl. Phys. 21 437 Google Scholar
[143]	Frost H J, Ashby M F 1982 Deformation Mechanism Maps: The Plasticity and Creep of Metals and Ceramics (Oxford: Pergamon press) p11
[144]	Sun J, He L, Lo Y C, Xu T, Bi H, Sun L, Zhang Z, Mao S X, Li J 2014 Nat. Mater. 13 1007 Google Scholar
[145]	Tu K N 2007 Solder Joint Technology (Vol. 117) (Berlin: Springer) pp153−181
[146]	Tian L, Li J, Sun J, Ma E, Shan Z W 2013 Sci. Rep. 3 2113 Google Scholar
[147]	Mali M, Roos J, Sonderegger M, Brinkmann D, Heitjans P 1988 J. of Phys. F: Metal Phys. 18 403 Google Scholar
[148]	He Y, Lu C, Liu S, Zheng W, Luo J 2019 Adv. Energy Mater. 9 1901810 Google Scholar
[149]	Kamaya N, Homma K, Yamakawa Y, Hirayama M, Kanno R, Yonemura M, Kamiyama T, Kato Y, Hama S, Kawamoto K 2011 Nat. Mater. 10 682 Google Scholar

[1]	任清勇, 王建立, 李昺, 马杰, 童欣. 复杂晶格动力学与能源材料的中子散射研究. , 2025, 74(1): . doi: 10.7498/aps.74.20241178
[2]	李梅, 钟淑英, 胡军平, 孙宝珍, 徐波. 固态电解质Li_1+xAl_xTi_2–x (PO₄)₃中 Li⁺的迁移特性. , 2024, 73(13): 138201. doi: 10.7498/aps.73.20240044
[3]	华彪, 孙宝珍, 王靖轩, 石晶, 徐波. Li含量对Li_3xLa_(2/3)–x†_(1/3)–2xTiO₃固态电解质表面稳定性、电子结构及Li离子输运性质的影响. , 2023, 72(2): 028201. doi: 10.7498/aps.72.20221808
[4]	杨源, 胡乃方, 金永成, 马君, 崔光磊. 富锂正极材料在全固态锂电池中的研究进展. , 2023, 72(11): 118801. doi: 10.7498/aps.72.20230258
[5]	耿晓彬, 李顶根, 徐波. 固态电解质电池锂枝晶生长机械应力-热力学相场模拟研究. , 2023, 72(22): 220201. doi: 10.7498/aps.72.20230824
[6]	何兵, 练宇翔, 吴木生, 罗文崴, 杨慎博, 欧阳楚英. 阳离子调控对卤化物固态电解质性能的改善. , 2022, 71(20): 208201. doi: 10.7498/aps.71.20221050
[7]	游逸玮, 崔建文, 张小锋, 郑锋, 吴顺情, 朱梓忠. 锂磷氧氮(LiPON)固态电解质与Li负极界面特性. , 2021, 70(13): 136801. doi: 10.7498/aps.70.20202214
[8]	张念, 任国玺, 章辉, 周櫈, 刘啸嵩. 石榴石型固态电解质表界面问题及优化的研究进展. , 2020, 69(22): 228806. doi: 10.7498/aps.69.20201533
[9]	冯吴亮, 王飞, 周星, 吉晓, 韩福东, 王春生. 固态电解质与电极界面的稳定性. , 2020, 69(22): 228206. doi: 10.7498/aps.69.20201554
[10]	王鑫萌, 石鹏, 张学强, 陈爱兵, 张强. 实用化条件下金属锂负极失效的研究. , 2020, 69(22): 228501. doi: 10.7498/aps.69.20200906
[11]	赵宁, 穆爽, 郭向欣. 石榴石型固态锂电池中的物理问题. , 2020, 69(22): 228804. doi: 10.7498/aps.69.20201191
[12]	刘玉龙, 辛明杨, 丛丽娜, 谢海明. 聚氧乙烯基聚合物固态电池的界面研究进展. , 2020, 69(22): 228202. doi: 10.7498/aps.69.20201588
[13]	彭林峰, 曾子琪, 孙玉龙, 贾欢欢, 谢佳. 富钠反钙钛矿型固态电解质的简易合成与电化学性能. , 2020, 69(22): 228201. doi: 10.7498/aps.69.20201227
[14]	张桥保, 龚正良, 杨勇. 硫化物固态电解质材料界面及其表征的研究进展. , 2020, 69(22): 228803. doi: 10.7498/aps.69.20201581
[15]	曹文卓, 李泉, 王胜彬, 李文俊, 李泓. 金属锂在固态电池中的沉积机理、策略及表征. , 2020, 69(22): 228204. doi: 10.7498/aps.69.20201293
[16]	陈棋, 尚学府, 张鹏, 徐鹏, 王淼, 今西誠之. 流延法制备高锂离子电导Li1.4Al0.4Ti1.6(PO4)3固态电解质及其环氧树脂改性. , 2017, 66(18): 188201. doi: 10.7498/aps.66.188201
[17]	郭立强, 陶剑, 温娟, 程广贵, 袁宁一, 丁建宁. 玉米淀粉固态电解质质子\电子杂化突触晶体管. , 2017, 66(16): 168501. doi: 10.7498/aps.66.168501
[18]	郭立强, 温娟, 程广贵, 袁宁一, 丁建宁. 基于KH550-GO固态电解质中电容耦合作用的双侧栅IZO薄膜晶体管. , 2016, 65(17): 178501. doi: 10.7498/aps.65.178501
[19]	郭文昊, 肖惠, 门传玲. SiO2固态电解质中的质子特性对氧化物双电层薄膜晶体管性能的影响. , 2015, 64(7): 077302. doi: 10.7498/aps.64.077302
[20]	俞文海, 丁屹. 固体电解质与电极之间界面的分数维模型及其频率响应. , 1989, 38(10): 1621-1627. doi: 10.7498/aps.38.1621

计量

文章访问数: 18351
PDF下载量: 702
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板