硒化亚铜薄膜热电性能研究进展

杨亮亮; 秦源浩; 魏江涛; 宋培帅; 张明亮; 杨富华; 王晓东

doi:10.7498/aps.70.20201677

摘要

热电材料可以实现热能和电能的相互转换, 它是一种环境友好的功能性材料. 当前, 热电材料的热电转换效率低, 这严重制约了热电器件的大规模应用, 因此寻找更加优异热电性能的新材料或提高传统热电材料的热电性能成为热电研究的主题. 与块状材料相比, 薄膜具有二维的宏观性质和一维的纳米结构特性, 方便研究材料的物理机制与性能的关系, 还适用于制备可穿戴电子设备. 本文总结了Cu₂Se薄膜5种不同的制备方法, 包括电化学沉积、热蒸发、旋涂、溅射以及脉冲激光沉积. 另外, 结合典型事例, 总结了薄膜的表征手段, 并从Cu₂Se的电导率、塞贝克系数和热导率等参数出发, 讨论了各个参数对热电性能的影响机制. 最后介绍了Cu₂Se薄膜热电的热门应用方向.

关键词:

Abstract

Thermoelectric (TE) materials can directly realize the mutual conversion between heat and electricity, and it is an environmentally friendly functional material. At present, the thermoelectric conversion efficiencies of thermoelectric materials are low, which seriously restricts the large-scale application of thermoelectric devices. Therefore, finding new materials with better thermoelectric properties or improving the thermoelectric properties of traditional thermoelectric materials has become the subject of thermoelectric research. Thin film materials, compared with bulk materials, possess both the two-dimensional macroscopic properties and one-dimensional nanostructure characteristics, which makes it much easier to study the relationships between physical mechanisms and properties. Besides, thin film are also suitable for the preparation of wearable electronic devices. This article summarizes five different preparation methods of Cu₂Se thin films, i.e. electrochemical deposition, thermal evaporation, spin coating, sputtering, and pulsed laser deposition. In addition, combing with typical examples, the characterization methods of the film are summarized, and the influence mechanism of each parameter on the thermoelectric performance from electrical conductivity, Seebeck coefficient and thermal conductivity is discussed. Finally, the hot application direction of Cu₂Se thin film thermoelectrics is also introduced.

Keywords:

作者及机构信息

1.
中国科学院半导体研究所半导体集成技术工程研究中心, 北京　100083

2.
中国科学院大学微电子学院及材料与光电研究中心, 北京　100049

3.
北京量子信息科学研究院, 北京　100193

4.
北京市半导体微纳集成工程技术研究中心, 北京　100083

通信作者: 王晓东, xdwang@semi.ac.cn

基金项目: 国家重点研发计划(批准号: 2019YFB1503602, 2018YFB1107502)、中国科学院先导B项目(批准号: XDB43020500)和中国科学院科研仪器设备研制项目(批准号: GJJSTD20200006)资助的课题

Authors and contacts

1.
Engineering Research Center for Semiconductor Integrated Technology, Institute of Semiconductors, Chinese Academy of Sciences, Beijing 100083, China

2.
College of Microelectronics and Research Center of Materials and Optoelectronics, University of Chinese Academy of Sciences, Beijing 100049, China

3.
Beijing Institute of Quantum Information Science, Beijing 100193, China

4.
Beijing Semiconductor Micro/Nano Integrated Engineering Technology Research Center, Beijing 100083, China

Corresponding author: Wang Xiao-Dong, xdwang@semi.ac.cn

Funds: Project supported by the National Key Research and Development Program of China (Grant Nos. 2019YFB1503602, 2018YFB1107502), the Pilot B Program of the Chinese Academy of Sciences, China (Grant No. XDB43020500) and Development Program of Scientific Research Instruments and Equipment of the Chinese Academy of Sciences, China (Grant No. GJJSTD20200006)

文章全文 : translate this paragraph

参考文献

[1]	Lu P, Liu H, Yuan X, Xu F, Shi X, Zhao K, Qiu W, Zhang W, Chen L 2015 J. Mater. Chem. A 3 6901 Google Scholar
[2]	Hussain R A, Hussain I 2020 Solid State Sci. 100 106101 Google Scholar
[3]	Malekar V P, Gangawane S A, Fulari V J 2020 Mater. Today Proc. 23 202 Google Scholar
[4]	Sharma K, Sharma D K, Kumar V 2020 Optik 206 164376 Google Scholar
[5]	Li Y, Fan P, Zheng Z, Luo J, Liang G, Guo S 2016 J. Alloy. Compd. 658 880 Google Scholar
[6]	Wei J J, Yang L L, Ma Z, Song P S, Zhang M L, Ma J, Yang F H, Wang X D 2020 J. Mater. Sci. 55 12642 Google Scholar
[7]	Biswas K, He J, Blum I D, Wu C I, Hogan T P, Seidman D N, Dravid V P, Kanatzidis M G 2012 Nature 489 414 Google Scholar
[8]	Harman T C, Taylor P J, Walsh M P, LaForge B E 2002 Science 297 2229 Google Scholar
[9]	Pammi S V N, Jella V, Choi J S, Yoon S G 2017 J. Mater. Chem. C 5 763 Google Scholar
[10]	Lv Y, Chen J, Zheng R K, Shi X, Song J, Zhang T, Li X, Chen L 2015 Ceram. Int. 41 7439 Google Scholar
[11]	Ma Z, Liu Y, Deng L, Zhang M, Zhang S, Ma J, Song P, Liu Q, Ji A, Yang F, Wang X 2018 Nanomaterials 8 77 Google Scholar
[12]	Chen X, Dai W, Wu T, Luo W, Yang J, Jiang W, Wang L 2018 Coatings 8 244 Google Scholar
[13]	Hicks L D, Dresselhaus M S 1993 Phys. Rev. B Condens Matter 47 12727 Google Scholar
[14]	Dresselhaus M S, Dresselhaus G, Sun X, Zhang Z, Cronin S B, Koga T 1999 Phys. Solid State 41 679 Google Scholar
[15]	Venkatasubramanian R, Siivola E, Colpitts T, O'Quinn B J N 2001 Nature 413 597 Google Scholar
[16]	Zhou Y, Matsubara I, Shin W, Izu N, Murayama N 2004 J. Appl. Phys. 95 625 Google Scholar
[17]	Hochbaum A I, Chen R, Delgado R D, Liang W, Garnett E C, Najarian M, Majumdar A, Yang P 2008 Nature 451 163 Google Scholar
[18]	Zheng X J, Zhu L, Zhou Y H, Zhang Q 2005 Appl. Phys. Lett. 87 2229
[19]	Mehdizadeh D A, Zebarjadi M, He J, Tritt T M 2015 Mater. Sci. Eng. R 97 1 Google Scholar
[20]	Hinterleitner B, Knapp I, Poneder M, Shi Y, Müller H, Eguchi G, Eisenmenger S C, Stöger P M, Kakefuda Y, Kawamoto N, Guo Q, Baba T, Mori T, Ullah S, Chen X Q, Bauer E 2019 Nature 576 85 Google Scholar
[21]	Wang C, Xia K, Wang H, Liang X, Yin Z, Zhang Y 2019 Adv. Mater. 31 1801072 Google Scholar
[22]	Zhao W Y, Zhang Q J, Sun Z G, Zhu W T, Wei P, Fang W B, Tian Y, Nie X L, Li P 2019 J. Inorg. Mater. 34 6
[23]	Gahtori B, Bathula S, Tyagi K, Jayasimhadri M, Srivastava A K, Singh S, Budhani R C, Dhar A 2015 Nano Energy 13 36 Google Scholar
[24]	Zhao K, Liu K, Yue Z, Wang Y, Song Q, Li J, Guan M, Xu Q, Qiu P, Zhu H, Chen L, Shi X 2019 Adv. Mater. 190 3480
[25]	Byeon D, Sobota R, Delime Codrin K, Choi S, Hirata K, Adachi M, Kiyama M, Matsuura T, Yamamoto Y, Matsunami M, Takeuchi T 2019 Nat. Commun. 10 72 Google Scholar
[26]	Byeon D, Sobota R, Singh S, Ghodke S, Choi S, Kubo N, Adachi M, Yamamoto Y, Matsunami M, Takeuchi T 2020 J. Electron. Mater. 49 2855 Google Scholar
[27]	Chen H Y, Shi X, Chen L D, Chou P F 2019 J. Inorg. Mater. 34 1041
[28]	Kim J H, Oh S, Sohn W H, Rhyee J S, Park S D, Kang H, Ahn D 2015 Acta Mater. 100 32 Google Scholar
[29]	Tak J Y, Nam W H, Lee C, Kim S, Lim Y S, Ko K, Lee S, Seo W S, Cho H K, Shim J H, Park C H 2018 Chem. Mat. 30 3276 Google Scholar
[30]	Liu W, Shi X, Hong M, Yang L, Moshwan R, Chen Z G, Zou J 2018 J. Mater. Chem. C 6 13225
[31]	Sun Y, Xi L, Yang J, Wu L, Shi X, Chen L, Snyder J, Yang J, Zhang W 2017 J. Mater. Chem. A 5 5098 Google Scholar
[32]	Olvera A A, Moroz N A, Sahoo P, Ren P, Bailey T P, Page A A, Uher C, Poudeu P F P 2017 Energy & Environ. Sci. 10 1668
[33]	R. D. Heyding 1966 Can. J. Chem. 44 1233 Google Scholar
[34]	Namsani S, Auluck S, Singh J K 2017 Appl. Phys. Lett. 111 163903 Google Scholar
[35]	Eikeland E, Blichfeld A B, Borup K A, Zhao K, Overgaard J, Shi X, Chen L, Iversen B B 2017 Iucrj 4 476 Google Scholar
[36]	Bailey T P, Hui S, Xie H, Olvera A, Poudeu P F P, Tang X, Uher C 2016 J. Mater. Chem. A 4 17225 Google Scholar
[37]	Yang L, Chen Z G, Han G, Hong M, Zou Y, Zou J 2015 Nano Energy 16 367 Google Scholar
[38]	Kim H, Ballikaya S, Chi H, Ahn J P, Ahn K, Uher C, Kaviany M 2015 Acta Mater. 86 247 Google Scholar
[39]	Ballikaya S, Chi H, Salvador J R, Uher C 2013 J. Mater. Chem. A 1 12478 Google Scholar
[40]	Lin Z, Hollar C, Kang J S, Yin A, Wang Y, Shiu H Y, Huang Y, Hu Y, Zhang Y, Duan X 2017 Adv. Mater. 29 1606662 Google Scholar
[41]	Ghosh A, Kulsi C, Banerjee D, Mondal A 2016 Appl. Surf. Sci. 369 525 Google Scholar
[42]	Liu T C, Hu Y, Chang W B 2014 Mater. Sci. Eng. B 180 33 Google Scholar
[43]	Rajesh D, Chandrakanth R R, Sunandana 2013 J. Apple. Phys. 4 65
[44]	Mansour B A, Zawawi I K E L, Elsayed A H E, Hameed T A 2018 J. Alloy. Comp. 740 1125 Google Scholar
[45]	Emslie A G, Bonner F T, Peck L G 1958 J. Appl. Phys. 29 858 Google Scholar
[46]	王东, 刘红缨, 贺军辉, 刘林林 2012 影像科学与光化学 30 91 Google Scholar Wang D, Liu H Y, He J H, Liu L L, 2012 Imaging Sci. Photochem. 30 91 Google Scholar
[47]	Mitzi D B, Kosbar L L, Murray C E, Copel M, Afzali A 2004 Nature 428 299 Google Scholar
[48]	Mitzi D B, Copel M, Murray C E 2006 Adv. Mater. 18 2448 Google Scholar
[49]	Sheng J, Han K L, Hong T, Choi W H, Park J S 2018 J. Semicond. 39 011008 Google Scholar
[50]	Mihi A, Ocana M, Miguez H 2006 Adv. Mater. 18 2244 Google Scholar
[51]	Zhang T, Yao G, Pan T, Lu Q 2020 J. Semicond. 41 041602 Google Scholar
[52]	Lee H, Lee B P, Messersmith P B 2007 Nature 448 338 Google Scholar
[53]	Lee J H, Oh J Y, Kim D M 1999 J. Mater. Sci.-Mater. Med. 10 629 Google Scholar
[54]	Scimeca M R, Yang F, Zaia E, Chen N, Zhao P, Gordon M P, Forster J D, Liu Y S, Guo J, Urban J J, Sahu A 2019 ACS Appl. Energy Mater. 2 1517 Google Scholar
[55]	Day T W, Weldert K S, Zeier W G, Chen B R, Moffitt S L, Weis U, Jochum K P, Panthoefer M, Bedzyk M J, Snyder G J, Tremel W 2015 Chem. Mater. 27 7018 Google Scholar
[56]	Zeng Y, Liang G, Fan P, Xie Y, Fan B, Hu J, Zheng Z, Zhang X, Luo J, Zhang D 2017 J. Mater. Sci.-Mater. Electron. 28 13763 Google Scholar
[57]	Shen S, Zhu W, Deng Y, Zhao H, Peng Y, Wang C 2017 Appl. Surf. Sci. 414 197 Google Scholar
[58]	Kim H J, Kim K C, Choi W C, Kim J S, Kim Y H, Kim S I, Park C 2012 J. Nanosci. Nanotechnol. 12 3629 Google Scholar
[59]	Yuan D, Zhi Wei Z 2015 J. Inorg. Mater. 30 1 Google Scholar
[60]	Perez Taborda J A, Vera L, Caballero Calero O, Lopez E O, Romero J J, Stroppa D G, Briones F, Martin Gonzalez M 2017 Adv. Mater. Technol. 2 7
[61]	Lv Y H, Chen J K, Doebeli M, Li Y L, Shi X, Chen L D 2015 J. Inorg. Mater. 30 1115 Google Scholar
[62]	Yang L, Wei J, Ma Z, Song P, Ma J, Zhao Y, Huang Z, Zhang M, Yang F, Wang X 2019 Nanomaterials 9 12
[63]	Liu H, Yuan X, Lu P, Shi X, Xu F, He Y, Tang Y, Bai S, Zhang W, Chen L, Lin Y, Shi L, Lin H, Gao X, Zhang X, Chi H, Uher C 2013 Adv. Mater. 25 6607 Google Scholar
[64]	Hu Q, Zhu Z, Zhang Y, Li X J, Song H, Zhang Y 2018 J. Mater. Chem. A 6 23417 Google Scholar
[65]	Zhong B, Zhang Y, Li W, Chen Z, Cui J, Li W, Xie Y, Hao Q, He Q 2014 Appl. Phys. Lett. 105 123902 Google Scholar
[66]	Cui J, Liu X, Zhang X, Li Y, Deng Y 2011 J. Appl. Phys. 110 023708 Google Scholar
[67]	Boukai A I, Bunimovich Y, Tahir Kheli J, Yu J K, Goddard W A, 3 rd, Heath J R 2008 Nature 451 168 Google Scholar
[68]	Bhuse V M, Hankare P P, Garadkar K M, Khomane A S 2003 Mater. Chem. Phys. 80 82 Google Scholar
[69]	Pathan H M, Lokhande C D, Amalnerkar D P, Seth T 2003 Appl. Surf. Sci. 211 48 Google Scholar
[70]	Dhanam M, Manoj P K, Prabhu R R 2005 J. Cryst. Growth 280 425 Google Scholar
[71]	Hu Y, Afzaal M, Malik M A, O’Brien P 2006 J. Cryst. Growth 297 61 Google Scholar
[72]	Hiramatsu H, Koizumi I, Kim K B, Yanagi H, Kamiya T, Hirano M, Matsunami N, Hosono H 2008 J. Appl. Phys. 104 113723 Google Scholar
[73]	Yang M, Shen Z, Liu X, Wang W 2016 J. Electron. Mater. 45 1974 Google Scholar
[74]	Romero J J, Perez Taborda J A, Briones F, Martín González M S 2016 12^th European Conference on Thermoelectrics, Madrid, Spain, September 24–26, 2014
[75]	Liu K, Jing M, Zhang L, Li J, Shi L 2018 Integr. Ferroelectr. 189 71 Google Scholar
[76]	Forster J D, Lynch J J, Coates N E, Liu J, Jang H, Zaia E, Gordon M P, Szybowski M, Sahu A, Cahill D G, Urban J J 2017 Sci. Rep. 7 2765 Google Scholar
[77]	Lu Y, Ding Y, Qiu Y, Cai K, Yao Q, Song H, Tong L, He J, Chen L 2019 ACS Appl. Mater. Interfaces 11 12819 Google Scholar
[78]	邓元, 张义政, 王瑶, 高洪利 2014 航空学报 35 2733 Deng Y, Zhang Y Z, Wang Y, Gao H L 2014 Acta Aeronaut. Astronaut. Sin. 35 2733
[79]	Jin Q, Jiang S, Zhao Y, Wang D, Qiu J, Tang D M, Tan J, Sun D M, Hou P X, Chen X Q, Tai K, Gao N, Liu C, Cheng H M, Jiang X 2019 Nat. Mater. 18 62 Google Scholar
[80]	Bahk J H, Fang H, Yazawa K, Shakouri A 2015 J. Mater. Chem. C 3 10362 Google Scholar
[81]	Liu X, Long Y Z, Liao L, Duan X, Fan Z 2012 ACS Nano 6 1888 Google Scholar
[82]	Lu Y, Qiu Y, Jiang Q, Cai K, Du Y, Song H, Gao M, Huang C, He J, Hu D 2018 ACS Appl. Mater. Interfaces 10 42310 Google Scholar
[83]	Du Y, Shen S Z, Cai K, Casey P S 2012 Prog. Polym. Sci. 37 820 Google Scholar
[84]	Fan Z, Razavi H, Do J W, Moriwaki A, Ergen O, Chueh Y L, Leu P W, Ho J C, Takahashi T, Reichertz L A, Neale S, Yu K, Wu M, Ager J W, Javey A 2009 Nat. Mater. 8 648 Google Scholar
[85]	He Y, Wang X, Gao Y, Hou Y, Wan Q 2018 J. Semicond. 39 011005 Google Scholar
[86]	Lu Y, Qiu Y, Cai K, Ding Y, Wang M, Jiang C, Yao Q, Huang C, Chen L, He J 2020 Energy. Environ. Sci. 13 1240 Google Scholar
[87]	Zhao K, Blichfeld A B, Chen H, Song Q, Zhang T, Zhu C, Ren D, Hanus R, Qiu P, Iversen B B, Xu F, Snyder G J, Shi X, Chen L 2017 Chem. Mat. 29 6367 Google Scholar
[88]	Finefrock S W, Zhu X, Sun Y, Wu Y 2015 Nanoscale 7 5598 Google Scholar
[89]	Im H, Moon H G, Lee J S, Chung I Y, Kang T J, Kim Y H 2015 Nano Res. 7 443
[90]	Kim S J, Lee H E, Choi H, Kim Y, We J H, Shin J S, Lee K J, Cho B J 2016 ACS Nano 10 10851 Google Scholar

施引文献

图 1 Cu₂Se高温β相晶体结构^[34]　(a)在8c和32f间隙位置显示有铜原子的晶胞; (b)沿着立方[$1\bar{1} 0$]方向的晶体结构的投影平面表示

Fig. 1. Cu₂Se high temperature β- phase crystal structure^[34] (a) Unit cell where the 8c and 32f interstitial positions are shown with Cu atoms; (b) projected plane representation of the crystal structure along the cubic [$1\bar{1} 0$] direction.

下载: 全尺寸图片幻灯片

图 2 (a)电镀沉积生长机制示意图; (b) Cu₂Se薄膜的XRD图案; (c) Cu₂Se薄膜的场发射扫描电子显微镜(FESEM)图像; (d) ITO基板上Cu₂Se薄膜的AFM 3D图像^[41]

Fig. 2. (a) Schematic diagram of Galvanic Deposition mechanism; (b) XRD pattern of Cu₂Se thin film; (c) FESEM image of Cu₂Se thin film; (d) AFM 3D image of Cu₂Se film on ITO substrate^[41].

下载: 全尺寸图片幻灯片

图 3 (a)溶解在硫醇胺中的Cu_2–xSe溶液; (b) 旋涂和退火后, 玻璃上的Cu₂Se薄膜; (c) (d) Cu_2–xSe薄膜样品浸泡前的SEM图像; (d) Cu_2–xSe薄膜样品浸泡后的SEM图像; (e) 旋涂制备的Cu_2–xSe样品的XRD图谱^[54]

Fig. 3. (a) Cu_2–x Se solution dissolved in thiolamine; (b) after spin coating and annealing, the Cu₂Se film on the glass; (c) SEM image of Cu_2–xSe thin film sample before soaking; (d) SEM image of Cu_2–xSe thin film sample after soaking; (e) XRD pattern of Cu_2–xSe sample prepared by spin coating^[54].

下载: 全尺寸图片幻灯片

图 4 (a) Al₂O₃基板上沉积的Cu₂Se薄膜的照片; (b) 在573 K下退火的薄膜能量色散X射线光谱(EDS); (c) Al₂O₃基材上薄膜的横截面SEM分析; (d) 薄膜中纳米晶体的TEM分析, 其中虚线突出了晶界, 插图是TEM图像的相应FFT^[40]

Fig. 4. (a) Photograph of Cu₂Se thin film deposited on Al₂O₃ substrate; (b) energy dispersive X-ray spectroscopy (EDS) of thin film annealed at 573 K; (c) cross-sectional SEM analysis of thin film on Al₂O₃ substrate; (d) TEM analysis of nanocrystals in the thin film, the dotted line highlights the grain boundaries, the inset is the corresponding FFT of the TEM image.^[40]

下载: 全尺寸图片幻灯片

图 5 (a) 脉冲混合反应磁控溅射(PHRMS)沉积系统; (b) 从标称成分分别为Cu/Se = 1, 2, 2.4, 3.6, 5和9的薄膜上获得的掠入射同步辐射X射线衍射图^[60]

Fig. 5. (a) Pulse hybrid reactive magnetron sputtering (PHRMS) deposition system; (b) grazing incident synchrotron radiation X Ray diffraction pattern obtained from a film with a nominal composition of Cu/Se = 1, 2, 2.4, 3.6, 5 and 9^[60].

下载: 全尺寸图片幻灯片

图 6 具有不同铜/硒比的薄膜的SEM图像^[60]　(a) Cu/Se = 1; (b) Cu/Se = 2; (c) Cu/Se = 2.4; (d) Cu/Se = 3.6; (e) Cu/Se = 5; (f) Cu/Se = 9

Fig. 6. SEM images of films with different copper/selenium ratios^[60] (a) Cu/Se = 1; (b) Cu/Se = 2; (c) Cu/Se = 2.4; (d) Cu/Se = 3.6; (e) Cu/Se = 5; (f) Cu/Se = 9.

下载: 全尺寸图片幻灯片

图 7 (a)由各种Cu_2+xSe靶沉积的Cu_2–ySe膜中的XRD图案; (b) 根据布拉格定律计算的(001)面的晶面晶体间距(c); (c) Cu₂Se膜的截面HRTEM图像; (d) (e)不同Cu_2–xSe靶沉积的Cu_2–ySe膜的FESEM图像, (d) x = 0.1, (d) x = 0.3 ^[10]

Fig. 7. (a) XRD patterns in Cu_2–y Se films deposited from various Cu_2+x Se targets; (b) (001) plane crystal spacing (c) calculated according to Bragg's law; (c) HRTEM image of the cross-section of Cu₂Se film; (d)(e) FESEM images of Cu_2–ySe films deposited on different Cu_2–x Se targets, (d) x = 0.1, (e) x = 0.3 ^[10]

下载: 全尺寸图片幻灯片

图 8 (a)在不同温度下退火的Cu₂Se薄膜中的室温载流子浓度; (b)电导率对薄膜中载流子浓度的依赖性; (c)塞贝克系数对薄膜中载流子浓度的依赖性; (d) (e) 柔性塑料基板上Cu₂Se薄膜的热电性能; (f)沉积在聚酰亚胺基板上的薄膜的电导率σ, (g)塞贝克系数S, (h) 功率因数PF = σS² ^[40]

Fig. 8. (a) Room temperature carrier concentration in Cu₂Se thin films annealed at different temperatures; (b) dependence of conductivity on carrier concentration in thin films; (c) dependence of Seebeck coefficient on carrier concentration in film; (d)(e) thermoelectric properties of Cu₂Se film on flexible plastic substrate, (f) conductivity σ of the film deposited on polyimide substrate, (g) Seebeck coefficient S, (h) power factor PF = σS² ^[40].

下载: 全尺寸图片幻灯片

图 9 (a) Cu₂Se/PEDOT: PSS复合膜的输出电压与温度梯度的关系; (b) 在不同温差下的输出电压和功率与电流的关系; (c) 设备的数码照片; (d) 由于手臂和周围环境之间的温差而产生的4.5 mV电压的照片; (e) 将茶水倒入500 mL烧杯中直至液位到达设备下边缘时产生的15.4 mV电压的照片, d部分和e部分的插图是红外热像图^[77]

Fig. 9. (a) Cu₂Se/PEDOT: Relationship between the output voltage of the PSS composite film and the temperature gradient; (b) relationship between output voltage and power and current under different temperature differences; (c) digital photos of the device; (d) photo of the 4.5 mV voltage generated due to the temperature difference between the arm and the surrounding environment; (e) pour the tea water into a 500 mL beaker until the liquid level reaches the bottom edge of the device at 15.4 mV voltage, where Illustrations in the (d) and (e) parts are infrared thermal images^[77]

下载: 全尺寸图片幻灯片

表 1 近年来Cu₂Se薄膜热电性能研究进展

Table 1. Research progress of Cu₂Se thin film thermoelectric properties in recent years.

Methods	Film	Cu/Se	Crystallite size/mm	S/μV·K^–1	σ/ ×10³ S/m	κ/ W·(m·K)^–1	PF/ mW·(m·K²) ^–1	ZT	Ref.
Chemical deposition	600	1.8	38		18				[68]
	330	2.125			1				[69]
	403	1.96	37.039		17.8				[70]
	1700	1.81			8.13 × 10³				[71]
Pulsed laser deposition	40	1.7	< 10		450				[72]
	234			57	130		619		[10]
				60	10		350		[61]
Electrochemial deposition	90—100	1.92—1.89			0.14—0.22				[42]
		1.78	40—50	80	27	0.77	173	0.07	[41]
		2.191	34	56			130		[73]
Sputtering deposition		1—3	1000	10—100	100				[74]
		3—10	100	> 100	1
	48—131	1.777		37.3	1.4—4.9				[5]
	600—850	1—9	25—84	100	100	0.8 ± 0.1	110	0.4	[60]
Spin coating process			300—500		44.603				[75]
	62.6	1.9—1.995		200—250	25	0.62	653	0.34	[54]
	50—100			80	100	0.4—1.4		0.14	[76]
	55	1.79 ± 0.06	10			1.3—1.5	620		[40]
Simple mechanical pressing	10000—50000	1.743		14.3	557.82	0.79	111.84	0.04	[9]
Wet-chemical process	8000	1.98		50.8	104.7	0.25—0.3	270.3	0.3	[77]

下载: 导出CSV

map

[1]	Lu P, Liu H, Yuan X, Xu F, Shi X, Zhao K, Qiu W, Zhang W, Chen L 2015 J. Mater. Chem. A 3 6901 Google Scholar
[2]	Hussain R A, Hussain I 2020 Solid State Sci. 100 106101 Google Scholar
[3]	Malekar V P, Gangawane S A, Fulari V J 2020 Mater. Today Proc. 23 202 Google Scholar
[4]	Sharma K, Sharma D K, Kumar V 2020 Optik 206 164376 Google Scholar
[5]	Li Y, Fan P, Zheng Z, Luo J, Liang G, Guo S 2016 J. Alloy. Compd. 658 880 Google Scholar
[6]	Wei J J, Yang L L, Ma Z, Song P S, Zhang M L, Ma J, Yang F H, Wang X D 2020 J. Mater. Sci. 55 12642 Google Scholar
[7]	Biswas K, He J, Blum I D, Wu C I, Hogan T P, Seidman D N, Dravid V P, Kanatzidis M G 2012 Nature 489 414 Google Scholar
[8]	Harman T C, Taylor P J, Walsh M P, LaForge B E 2002 Science 297 2229 Google Scholar
[9]	Pammi S V N, Jella V, Choi J S, Yoon S G 2017 J. Mater. Chem. C 5 763 Google Scholar
[10]	Lv Y, Chen J, Zheng R K, Shi X, Song J, Zhang T, Li X, Chen L 2015 Ceram. Int. 41 7439 Google Scholar
[11]	Ma Z, Liu Y, Deng L, Zhang M, Zhang S, Ma J, Song P, Liu Q, Ji A, Yang F, Wang X 2018 Nanomaterials 8 77 Google Scholar
[12]	Chen X, Dai W, Wu T, Luo W, Yang J, Jiang W, Wang L 2018 Coatings 8 244 Google Scholar
[13]	Hicks L D, Dresselhaus M S 1993 Phys. Rev. B Condens Matter 47 12727 Google Scholar
[14]	Dresselhaus M S, Dresselhaus G, Sun X, Zhang Z, Cronin S B, Koga T 1999 Phys. Solid State 41 679 Google Scholar
[15]	Venkatasubramanian R, Siivola E, Colpitts T, O'Quinn B J N 2001 Nature 413 597 Google Scholar
[16]	Zhou Y, Matsubara I, Shin W, Izu N, Murayama N 2004 J. Appl. Phys. 95 625 Google Scholar
[17]	Hochbaum A I, Chen R, Delgado R D, Liang W, Garnett E C, Najarian M, Majumdar A, Yang P 2008 Nature 451 163 Google Scholar
[18]	Zheng X J, Zhu L, Zhou Y H, Zhang Q 2005 Appl. Phys. Lett. 87 2229
[19]	Mehdizadeh D A, Zebarjadi M, He J, Tritt T M 2015 Mater. Sci. Eng. R 97 1 Google Scholar
[20]	Hinterleitner B, Knapp I, Poneder M, Shi Y, Müller H, Eguchi G, Eisenmenger S C, Stöger P M, Kakefuda Y, Kawamoto N, Guo Q, Baba T, Mori T, Ullah S, Chen X Q, Bauer E 2019 Nature 576 85 Google Scholar
[21]	Wang C, Xia K, Wang H, Liang X, Yin Z, Zhang Y 2019 Adv. Mater. 31 1801072 Google Scholar
[22]	Zhao W Y, Zhang Q J, Sun Z G, Zhu W T, Wei P, Fang W B, Tian Y, Nie X L, Li P 2019 J. Inorg. Mater. 34 6
[23]	Gahtori B, Bathula S, Tyagi K, Jayasimhadri M, Srivastava A K, Singh S, Budhani R C, Dhar A 2015 Nano Energy 13 36 Google Scholar
[24]	Zhao K, Liu K, Yue Z, Wang Y, Song Q, Li J, Guan M, Xu Q, Qiu P, Zhu H, Chen L, Shi X 2019 Adv. Mater. 190 3480
[25]	Byeon D, Sobota R, Delime Codrin K, Choi S, Hirata K, Adachi M, Kiyama M, Matsuura T, Yamamoto Y, Matsunami M, Takeuchi T 2019 Nat. Commun. 10 72 Google Scholar
[26]	Byeon D, Sobota R, Singh S, Ghodke S, Choi S, Kubo N, Adachi M, Yamamoto Y, Matsunami M, Takeuchi T 2020 J. Electron. Mater. 49 2855 Google Scholar
[27]	Chen H Y, Shi X, Chen L D, Chou P F 2019 J. Inorg. Mater. 34 1041
[28]	Kim J H, Oh S, Sohn W H, Rhyee J S, Park S D, Kang H, Ahn D 2015 Acta Mater. 100 32 Google Scholar
[29]	Tak J Y, Nam W H, Lee C, Kim S, Lim Y S, Ko K, Lee S, Seo W S, Cho H K, Shim J H, Park C H 2018 Chem. Mat. 30 3276 Google Scholar
[30]	Liu W, Shi X, Hong M, Yang L, Moshwan R, Chen Z G, Zou J 2018 J. Mater. Chem. C 6 13225
[31]	Sun Y, Xi L, Yang J, Wu L, Shi X, Chen L, Snyder J, Yang J, Zhang W 2017 J. Mater. Chem. A 5 5098 Google Scholar
[32]	Olvera A A, Moroz N A, Sahoo P, Ren P, Bailey T P, Page A A, Uher C, Poudeu P F P 2017 Energy & Environ. Sci. 10 1668
[33]	R. D. Heyding 1966 Can. J. Chem. 44 1233 Google Scholar
[34]	Namsani S, Auluck S, Singh J K 2017 Appl. Phys. Lett. 111 163903 Google Scholar
[35]	Eikeland E, Blichfeld A B, Borup K A, Zhao K, Overgaard J, Shi X, Chen L, Iversen B B 2017 Iucrj 4 476 Google Scholar
[36]	Bailey T P, Hui S, Xie H, Olvera A, Poudeu P F P, Tang X, Uher C 2016 J. Mater. Chem. A 4 17225 Google Scholar
[37]	Yang L, Chen Z G, Han G, Hong M, Zou Y, Zou J 2015 Nano Energy 16 367 Google Scholar
[38]	Kim H, Ballikaya S, Chi H, Ahn J P, Ahn K, Uher C, Kaviany M 2015 Acta Mater. 86 247 Google Scholar
[39]	Ballikaya S, Chi H, Salvador J R, Uher C 2013 J. Mater. Chem. A 1 12478 Google Scholar
[40]	Lin Z, Hollar C, Kang J S, Yin A, Wang Y, Shiu H Y, Huang Y, Hu Y, Zhang Y, Duan X 2017 Adv. Mater. 29 1606662 Google Scholar
[41]	Ghosh A, Kulsi C, Banerjee D, Mondal A 2016 Appl. Surf. Sci. 369 525 Google Scholar
[42]	Liu T C, Hu Y, Chang W B 2014 Mater. Sci. Eng. B 180 33 Google Scholar
[43]	Rajesh D, Chandrakanth R R, Sunandana 2013 J. Apple. Phys. 4 65
[44]	Mansour B A, Zawawi I K E L, Elsayed A H E, Hameed T A 2018 J. Alloy. Comp. 740 1125 Google Scholar
[45]	Emslie A G, Bonner F T, Peck L G 1958 J. Appl. Phys. 29 858 Google Scholar
[46]	王东, 刘红缨, 贺军辉, 刘林林 2012 影像科学与光化学 30 91 Google Scholar Wang D, Liu H Y, He J H, Liu L L, 2012 Imaging Sci. Photochem. 30 91 Google Scholar
[47]	Mitzi D B, Kosbar L L, Murray C E, Copel M, Afzali A 2004 Nature 428 299 Google Scholar
[48]	Mitzi D B, Copel M, Murray C E 2006 Adv. Mater. 18 2448 Google Scholar
[49]	Sheng J, Han K L, Hong T, Choi W H, Park J S 2018 J. Semicond. 39 011008 Google Scholar
[50]	Mihi A, Ocana M, Miguez H 2006 Adv. Mater. 18 2244 Google Scholar
[51]	Zhang T, Yao G, Pan T, Lu Q 2020 J. Semicond. 41 041602 Google Scholar
[52]	Lee H, Lee B P, Messersmith P B 2007 Nature 448 338 Google Scholar
[53]	Lee J H, Oh J Y, Kim D M 1999 J. Mater. Sci.-Mater. Med. 10 629 Google Scholar
[54]	Scimeca M R, Yang F, Zaia E, Chen N, Zhao P, Gordon M P, Forster J D, Liu Y S, Guo J, Urban J J, Sahu A 2019 ACS Appl. Energy Mater. 2 1517 Google Scholar
[55]	Day T W, Weldert K S, Zeier W G, Chen B R, Moffitt S L, Weis U, Jochum K P, Panthoefer M, Bedzyk M J, Snyder G J, Tremel W 2015 Chem. Mater. 27 7018 Google Scholar
[56]	Zeng Y, Liang G, Fan P, Xie Y, Fan B, Hu J, Zheng Z, Zhang X, Luo J, Zhang D 2017 J. Mater. Sci.-Mater. Electron. 28 13763 Google Scholar
[57]	Shen S, Zhu W, Deng Y, Zhao H, Peng Y, Wang C 2017 Appl. Surf. Sci. 414 197 Google Scholar
[58]	Kim H J, Kim K C, Choi W C, Kim J S, Kim Y H, Kim S I, Park C 2012 J. Nanosci. Nanotechnol. 12 3629 Google Scholar
[59]	Yuan D, Zhi Wei Z 2015 J. Inorg. Mater. 30 1 Google Scholar
[60]	Perez Taborda J A, Vera L, Caballero Calero O, Lopez E O, Romero J J, Stroppa D G, Briones F, Martin Gonzalez M 2017 Adv. Mater. Technol. 2 7
[61]	Lv Y H, Chen J K, Doebeli M, Li Y L, Shi X, Chen L D 2015 J. Inorg. Mater. 30 1115 Google Scholar
[62]	Yang L, Wei J, Ma Z, Song P, Ma J, Zhao Y, Huang Z, Zhang M, Yang F, Wang X 2019 Nanomaterials 9 12
[63]	Liu H, Yuan X, Lu P, Shi X, Xu F, He Y, Tang Y, Bai S, Zhang W, Chen L, Lin Y, Shi L, Lin H, Gao X, Zhang X, Chi H, Uher C 2013 Adv. Mater. 25 6607 Google Scholar
[64]	Hu Q, Zhu Z, Zhang Y, Li X J, Song H, Zhang Y 2018 J. Mater. Chem. A 6 23417 Google Scholar
[65]	Zhong B, Zhang Y, Li W, Chen Z, Cui J, Li W, Xie Y, Hao Q, He Q 2014 Appl. Phys. Lett. 105 123902 Google Scholar
[66]	Cui J, Liu X, Zhang X, Li Y, Deng Y 2011 J. Appl. Phys. 110 023708 Google Scholar
[67]	Boukai A I, Bunimovich Y, Tahir Kheli J, Yu J K, Goddard W A, 3 rd, Heath J R 2008 Nature 451 168 Google Scholar
[68]	Bhuse V M, Hankare P P, Garadkar K M, Khomane A S 2003 Mater. Chem. Phys. 80 82 Google Scholar
[69]	Pathan H M, Lokhande C D, Amalnerkar D P, Seth T 2003 Appl. Surf. Sci. 211 48 Google Scholar
[70]	Dhanam M, Manoj P K, Prabhu R R 2005 J. Cryst. Growth 280 425 Google Scholar
[71]	Hu Y, Afzaal M, Malik M A, O’Brien P 2006 J. Cryst. Growth 297 61 Google Scholar
[72]	Hiramatsu H, Koizumi I, Kim K B, Yanagi H, Kamiya T, Hirano M, Matsunami N, Hosono H 2008 J. Appl. Phys. 104 113723 Google Scholar
[73]	Yang M, Shen Z, Liu X, Wang W 2016 J. Electron. Mater. 45 1974 Google Scholar
[74]	Romero J J, Perez Taborda J A, Briones F, Martín González M S 2016 12^th European Conference on Thermoelectrics, Madrid, Spain, September 24–26, 2014
[75]	Liu K, Jing M, Zhang L, Li J, Shi L 2018 Integr. Ferroelectr. 189 71 Google Scholar
[76]	Forster J D, Lynch J J, Coates N E, Liu J, Jang H, Zaia E, Gordon M P, Szybowski M, Sahu A, Cahill D G, Urban J J 2017 Sci. Rep. 7 2765 Google Scholar
[77]	Lu Y, Ding Y, Qiu Y, Cai K, Yao Q, Song H, Tong L, He J, Chen L 2019 ACS Appl. Mater. Interfaces 11 12819 Google Scholar
[78]	邓元, 张义政, 王瑶, 高洪利 2014 航空学报 35 2733 Deng Y, Zhang Y Z, Wang Y, Gao H L 2014 Acta Aeronaut. Astronaut. Sin. 35 2733
[79]	Jin Q, Jiang S, Zhao Y, Wang D, Qiu J, Tang D M, Tan J, Sun D M, Hou P X, Chen X Q, Tai K, Gao N, Liu C, Cheng H M, Jiang X 2019 Nat. Mater. 18 62 Google Scholar
[80]	Bahk J H, Fang H, Yazawa K, Shakouri A 2015 J. Mater. Chem. C 3 10362 Google Scholar
[81]	Liu X, Long Y Z, Liao L, Duan X, Fan Z 2012 ACS Nano 6 1888 Google Scholar
[82]	Lu Y, Qiu Y, Jiang Q, Cai K, Du Y, Song H, Gao M, Huang C, He J, Hu D 2018 ACS Appl. Mater. Interfaces 10 42310 Google Scholar
[83]	Du Y, Shen S Z, Cai K, Casey P S 2012 Prog. Polym. Sci. 37 820 Google Scholar
[84]	Fan Z, Razavi H, Do J W, Moriwaki A, Ergen O, Chueh Y L, Leu P W, Ho J C, Takahashi T, Reichertz L A, Neale S, Yu K, Wu M, Ager J W, Javey A 2009 Nat. Mater. 8 648 Google Scholar
[85]	He Y, Wang X, Gao Y, Hou Y, Wan Q 2018 J. Semicond. 39 011005 Google Scholar
[86]	Lu Y, Qiu Y, Cai K, Ding Y, Wang M, Jiang C, Yao Q, Huang C, Chen L, He J 2020 Energy. Environ. Sci. 13 1240 Google Scholar
[87]	Zhao K, Blichfeld A B, Chen H, Song Q, Zhang T, Zhu C, Ren D, Hanus R, Qiu P, Iversen B B, Xu F, Snyder G J, Shi X, Chen L 2017 Chem. Mat. 29 6367 Google Scholar
[88]	Finefrock S W, Zhu X, Sun Y, Wu Y 2015 Nanoscale 7 5598 Google Scholar
[89]	Im H, Moon H G, Lee J S, Chung I Y, Kang T J, Kim Y H 2015 Nano Res. 7 443
[90]	Kim S J, Lee H E, Choi H, Kim Y, We J H, Shin J S, Lee K J, Cho B J 2016 ACS Nano 10 10851 Google Scholar

[1]	杨士冠, 林鑫, 何俊松, 翟立军, 程林, 吕明豪, 刘虹霞, 张艳, 孙志刚. 并联模型研究双层热电薄膜热电性能. , 2023, 72(22): 228401. doi: 10.7498/aps.72.20231259
[2]	郑建军, 张丽萍. 单层Cu₂X(X=S,Se):具有低晶格热导率的优秀热电材料. , 2023, 0(0): 0-0. doi: 10.7498/aps.72.20220015
[3]	郑建军, 张丽萍. 单层Cu₂X的热电性质. , 2023, 72(8): 086301. doi: 10.7498/aps.72.20222015
[4]	马云鹏, 庄华鹭, 李敬锋, 李千. 应变增强Nb掺杂SrTiO₃薄膜热电性能. , 2023, 72(9): 096803. doi: 10.7498/aps.72.20222301
[5]	陈上峰, 孙乃坤, 张宪民, 王凯, 李武, 韩艳, 吴丽君, 岱钦. Mn₃As₂掺杂Cd₃As₂纳米结构的制备及热电性能. , 2022, 71(18): 187201. doi: 10.7498/aps.71.20220584
[6]	许静, 何梓民, 杨文龙, 吴荣, 赖晓芳, 简基康. 层状Bi_1–xSb_xSe纳米薄膜的制备及其热电性能研究. , 2022, 71(19): 197301. doi: 10.7498/aps.71.20220834
[7]	聂晓蕾, 余灏成, 朱婉婷, 桑夏晗, 魏平, 赵文俞. 石墨烯/Bi_0.5Sb_1.5Te₃柔性热电薄膜及其面内散热器件的设计制备与性能评价. , 2022, 71(15): 157301. doi: 10.7498/aps.71.20220358
[8]	陈赟斐, 魏锋, 王赫, 赵未昀, 邓元. 高性能Bi₂Te_3–xSe_x热电薄膜的可控生长. , 2021, 70(20): 207303. doi: 10.7498/aps.70.20211090
[9]	邹平, 吕丹, 徐桂英. 高压烧结制备Tb掺杂n型(Bi_1–xTb_x)₂(Te_0.9Se_0.1)₃合金及其微结构和热电性能. , 2020, 69(5): 057201. doi: 10.7498/aps.69.20191561
[10]	王娇, 刘少辉, 周梦, 郝好山. 抗坏血酸后处理化学气相法制备的聚3, 4-乙撑二氧噻吩薄膜及其热电性能. , 2020, 69(14): 147201. doi: 10.7498/aps.69.20200431
[11]	张华, 陈少平, 龙洋, 樊文浩, 王文先, 孟庆森. 微波低温制备Mg2Si0.4Sn0.6-yBiy热电材料的传输机理. , 2015, 64(24): 247302. doi: 10.7498/aps.64.247302
[12]	刘冉, 高琳洁, 李龙江, 翟胜军, 王江龙, 傅广生, 王淑芳. Ca2+掺杂对CdO多晶热电性能的影响. , 2015, 64(21): 218101. doi: 10.7498/aps.64.218101
[13]	霍凤萍, 吴荣归, 徐桂英, 牛四通. 热压制备(AgSbTe2)100-x-(GeTe)x合金的热电性能. , 2012, 61(8): 087202. doi: 10.7498/aps.61.087202
[14]	杜保立, 徐静静, 鄢永高, 唐新峰. 非化学计量比AgSbTe2+x化合物制备及热电性能. , 2011, 60(1): 018403. doi: 10.7498/aps.60.018403
[15]	范平, 蔡兆坤, 郑壮豪, 张东平, 蔡兴民, 陈天宝. Bi-Sb-Te基热电薄膜温差电池离子束溅射制备与表征. , 2011, 60(9): 098402. doi: 10.7498/aps.60.098402
[16]	范平, 郑壮豪, 梁广兴, 张东平, 蔡兴民. Sb2Te3热电薄膜的离子束溅射制备与表征. , 2010, 59(2): 1243-1247. doi: 10.7498/aps.59.1243
[17]	熊飞, 张辉, 李洪山, 张鹏翔, 蒋最敏. 退火氧压对YBa2Cu3O7-x薄膜中的激光感生热电电压效应的影响. , 2008, 57(8): 5237-5243. doi: 10.7498/aps.57.5237
[18]	陈晓阳, 徐象繁, 胡荣星, 任之, 许祝安, 曹光旱. LixNayCoO2的制备和热电性质. , 2007, 56(3): 1627-1631. doi: 10.7498/aps.56.1627
[19]	李金华, 袁宁一, 陈王丽华, 林成鲁. 用离子束增强沉积从V2O5粉末制备高热电阻温度系数VO_2薄膜. , 2002, 51(8): 1788-1792. doi: 10.7498/aps.51.1788
[20]	陈继述. 红外薄膜热电探测器分析. , 1974, 23(6): 51-58. doi: 10.7498/aps.23.51

计量

文章访问数: 10796
PDF下载量: 357
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板