Research progress of wide bandgap perovskite materials and solar cells

Cui Xing-Hua; Xu Qiao-Jing; Shi Biao; Hou Fu-Hua; Zhao Ying; Zhang Xiao-Dan

doi:10.7498/aps.69.20200822

Abstract

Organic-inorganic metal halide perovskites are a new type of photovoltaic material, they have attracted wide attention and made excellent progress in recent years. The power conversion efficiency of a single-junction perovskite solar cell has been increased to 25.2% just within a decade. Meanwhile, crystalline silicon solar cells account for nearly 90% of industrialized solar cells and have a maximum efficiency of 26.7%, approaching to their theoretical limit. It is more difficult to further improve the efficiency of single junction solar cells. It has been shown that multi-junction tandem solar cells prepared by stacking absorption layers with different bandgaps can better use sunlight, which is one of the most promising strategies to break the efficiency limitation of single-junction solar cells. Due to the bandgap tunability and low-temperature solution processability, perovskites stand out among many other materials for manufacturing multi-junction tandem solar cells. Wide bandgap perovskites with a bandgap of 1.63 eV or above have been combined with narrow band gap inorganic absorption layers such as silicon, copper indium gallium selenide, cadmium telluride or narrow bandgap perovskite to produce high efficiency tandem solar cells. In addition to the promoting of the efficiency improvement of solar cells, the wide bandgap perovskites have broad applications in photovoltaic building integration and photocatalytic fields. Therefore, it is very important to explore and develop high quality wide bandgap perovskite materials and solar cells. Unfortunately, the wide bandgap perovskites have several intrinsic weaknesses, including being more vulnerable to the migration of halogen ions under being illuminated, more defects, and greater possibility of energy level mismatching with the charge transport layers than the narrow bandgap counterparts, which limits the further development of the wide bandgap perovskite solar cells. In this review, the development status of wide bandgap perovskite solar cells is summarized and corresponding strategies for improving their performance are put forward. Furthermore, some personal views on the future development of wide bandgap perovskite solar cells are also presented here in this paper.

Keywords:

Authors and contacts

1.
Institute of Photoelectronic Thin Film Devices and Technology, Nankai University, Tianjin 300350, China
2.
Key Laboratory of Photoelectronic Thin Film Devices and Technology of Tianjin, Tianjin 300350, China
3.
Engineering Research Center of Thin Film Photoelectronic Technology, Ministry of Education, Tianjin 300350, China
4.
Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072, China
5.
Renewable Energy Conversion and Storage Center of Nankai University, Tianjin 300072, China

Corresponding author: Zhang Xiao-Dan, xdzhang@nankai.edu.cn

Funds: Project supported by the National Key Research and Development Program of China (Grant No. 2018YFB1500103), the National Natural Science Foundation of China (Grant No. 61674084), the Overseas Expertise Introduction Project for Discipline Innovation of Higher Education of China (Grant No. B16027), the Science and Technology Project of Tianjin, China (Grant No. 18ZXJMTG00220), and the Fundamental Research Fund for the Central Universities, China (Grant No. 63201171)

FullText HTML : translate this paragraph

References

[1]	Xing G C, Mathews N, Lim S S, Yantara N, Liu X F, Sabba D, Grätzel M, Mhaisalkar S, Sum T C 2014 Nat. Mater. 13 476 Google Scholar
[2]	Tan Z K, Moghaddam R S, Lai M L, Docampo P, Higler R, Deschler F, Price M, Sadhanala A, Pazos L M, Credgington D 2014 Nat. Nanotechnol. 9 687 Google Scholar
[3]	Dou L, Yang Y, You J B, Hong Z, Chang W H, Li G, Yang Y 2014 Nat. Commun. 5 5404 Google Scholar
[4]	Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[5]	Kim M, Kim G H, Lee T K, Choi I W, Choi H W, Jo Y, Yoon Y J, Kim J W, Lee J Y, Huh D, Lee H, Kwak S K, Kim J Y, Kim D S 2019 Joule 3 2179 Google Scholar
[6]	Jiang Q, Zhao Y, Zhang X W, Yang X L, Chen Y, Chu Z, Ye Q, Li X X, Yin Z G, You J B 2019 Nat. Photonics 13 460 Google Scholar
[7]	Wang P Y, Li R J, Chen B B, Hou F H, Zhang J, Zhao Y, Zhang X D 2020 Adv. Mater. 32 1905766 Google Scholar
[8]	Min H, Kim M, Lee S U, Kim H, Kim G, Choi K, Lee J Hee, Seok S I 2019 Science 366 749 Google Scholar
[9]	Yoo J J, Wieghold S, Sponseller M C, Chua M R, Bertram S N, Hartono N T P, Tresback J S, Hansen E C, Correa-Baena J P, Bulovic V 2019 Energy Environ. Sci. 12 2192 Google Scholar
[10]	Liu Y H, Akin S, Pan L F, Uchida R, Grätzel M 2019 Sci. Adv. 5 eaaw2543 Google Scholar
[11]	Zhu P C, Gu S, Luo X, Gao Y, Li S L, Zhu J, Tan H R 2019 Adv. Energy Mater. 10 1903083 Google Scholar
[12]	Zheng X P, Hou Y, Bao C X, Yin J, Yuan F L, Huang Z R, Song K P, Liu J K, Troughton J, Gasparini N, Zhou C, Lin Y B, Xue D J, Chen B, Johnston A K, Wei N N, Hedhili M N, Wei M, Alsalloum A Y, Maity P, Turedi B, Yang C, Baran D, Anthopoulos T D, Han Y, Lu Z H, Mohammed O F, Gao F, Sargent E H, Bakr O M 2020 Nat. Energy 5 131 Google Scholar
[13]	Shockley W, Queisser H J 1961 J. Appl. Phys. 32 510 Google Scholar
[14]	Beiley Z M, McGehee M D 2012 Energy Environ. Sci. 5 9173 Google Scholar
[15]	Mailoa J P, Bailie C D, Johlin E C, Hoke E T, Akey A J, Nguyen W H, McGehee M D, Buonassisi T 2015 Appl. Phys. Lett. 106 121105 Google Scholar
[16]	Albrecht S, Saliba M, Correa Baena J P, Lang F, Kegelmann L, Mews M, Steier L, Abate A, Rappich J, Korte L, Schlatmann R, Nazeeruddin M K, Hagfeldt A, Grätzel M, Rech B 2016 Energy Environ. Sci. 9 81 Google Scholar
[17]	Altazin S, Stepanova L, Werner J, Niesen B, Ballif C, Ruhstaller B 2018 Opt. Express 26 A579 Google Scholar
[18]	Fang Z M, Wang S Z, Yang S F, Ding L M 2018 Inorg. Chem. Front. 5 1690 Google Scholar
[19]	Hu W P, He X, Fang Z M, Lian W T, Shang Y B, Li X C, Zhou W R, Zhang M M, Chen T, Lu Y L, Zhang L J, Ding L M, Yang S F 2020 Nano Energy 68 104362 Google Scholar
[20]	Jia X, Ding L M 2018 Sci. China Mater. 62 54 Google Scholar
[21]	Zuo C T, Ding L M 2017 Angew. Chem. Int. Ed. 56 6528 Google Scholar
[22]	Chen B, Zheng X P, Bai Y, Padture N P, Huang J S 2017 Adv. Energy Mater. 7 1602400 Google Scholar
[23]	Hu J N, Cheng Q, Fan R D, Zhou H P 2017 Sol. RRL 1 1700045 Google Scholar
[24]	Lal N N, Dkhissi Y, Li W, Hou Q C, Cheng Y B, Bach U 2017 Adv. Energy Mater. 7 1602761 Google Scholar
[25]	Jošt M, Kegelmann L, Korte L, Albrecht S 2020 Adv. Energy Mater. 10 1904102 Google Scholar
[26]	Al-Ashouri A, Magomedov A, Roß M, et al. 2019 Energy Environ. Sci. 12 3356 Google Scholar
[27]	Kim D H, Muzzillo C P, Tong J, et al. 2019 Joule 3 1734 Google Scholar
[28]	Lin R, Xiao K, Qin Z Y, Han Q L, Zhang C F, Wei M Y, Saidaminov M I, Gao Y, Xu J, Xiao M, Li A D, Zhu J, Sargent E H, Tan H R 2019 Nat. Energy 4 864 Google Scholar
[29]	McMeekin D P, Mahesh S, Noel N K, Klug M T, Lim J, Warby J H, Ball J M, Herz L M, Johnston M B, Snaith H J 2019 Joule 3 387 Google Scholar
[30]	Xue Q F, Xia R X, Brabec C J, Yip H L 2018 Energy Environ. Sci. 11 1688 Google Scholar
[31]	Henemann A 2008 Renew. Energy Focus 9 14 Google Scholar
[32]	Shi B, Duan L R, Zhao Y, Luo J S, Zhang X D 2020 Adv. Mater. 32 1806474 Google Scholar
[33]	Park S, Chang W J, Lee C W, Park S, Ahn H Y, Nam K T 2016 Nat. Energy 2 16185 Google Scholar
[34]	陈为, 魏伟, 孙予罕 2017 中国科学: 化学 47 1251 Google Scholar Chen W, Wei W, Sun Y H 2017 Sci. China: Chem. 47 1251 Google Scholar
[35]	Hu M, Bi C, Yuan Y B, Bai Y, Huang J S 2016 Adv. Sci. 3 1500301 Google Scholar
[36]	Lin Y Z, Chen B, Zhao F W, Zheng X P, Deng Y H, Shao Y C, Fang Y J, Bai Y, Wang C R, Huang J S 2017 Adv. Mater. 29 1700607 Google Scholar
[37]	Bush K A, Frohna K, Prasanna R, Beal R E, Leijtens T, Swifter S A, McGehee M D 2018 ACS Energy Lett. 3 428 Google Scholar
[38]	Wang Z P, Lin Q Q, Chmiel F P, Sakai N, Herz L M, Snaith H J 2017 Nat. Energy 2 17135 Google Scholar
[39]	Chen C, Song Z N, Xiao C X, Zhao D W, Shrestha N, Li C W, Yang G, Yao F, Zheng X L, Ellingson R J, Jiang C S, Al-Jassim M, Zhu K, Fang G J, Yan Y F 2019 Nano Energy 61 141 Google Scholar
[40]	Chen B, Yu Z S, Liu K, Zheng X P, Liu Y, Shi J W, Spronk D, Rudd P N, Holman Z, Huang J S 2019 Joule 3 177 Google Scholar
[41]	Wang J, Zhang J, Zhou Y Z, Liu H B, Xue Q F, Li X S, Chueh C C, Yip L P, Zhu Z L, Jen A K Y 2020 Nat. Commun. 11 177 Google Scholar
[42]	Liu C, Yang Y Z, Zhang C L, Wu S H, Wei L Y, Guo F, Arumugam G M, Hu J L, Liu X Y, Lin J, Schropp R E L, Mai Y H 2020 Adv. Mater. 32 1907361 Google Scholar
[43]	Palmstrom A F, Eperon G E, Leijtens T, et al. 2019 Joule 3 2193 Google Scholar
[44]	Xu J X, Boyd C C, Yu Z J, et al. 2020 Science 367 1097 Google Scholar
[45]	Kim D, Jung H J, Park I J, Larson B W, Dunfield S P, Xiao C X, Kim J, Tong J H, Boonmongkolras P, Ji S G, Zhang F, Pae S R, Kim M, Kang S B, Dravid V, Berry J J, Kim J Y, Zhu K, Kim D H, Shin B 2020 Science 368 155 Google Scholar
[46]	Ye J Y, Tong J H, Hu J, et al. 2020 Sol. RRL 4 2000082 Google Scholar
[47]	Duong T, Wu Y L, Shen H P, et al. 2017 Adv. Energy Mater. 7 1700228 Google Scholar
[48]	Yang M J, Kim D H, Yu Y, Li Z, Reid O G, Song Z N, Zhao D W, Wang C L, Li L W, Meng Y, Guo T, Yan Y F, Zhu K 2018 Mater. Today Energy 7 232 Google Scholar
[49]	Zhou Y, Wang F, Cao Y, Wang J P, Fang H H, Loi M A, Zhao N, Wong C P 2017 Adv. Energy Mater. 7 1701048 Google Scholar
[50]	Yu Y, Wang C L, Grice C R, Shrestha N, Zhao D W, Liao W Q, Guan L, Awni R A, Meng W W, Cimaroli A J, Zhu K, Ellingson R J, Yan Y F 2017 ACS Energy Lett. 2 1177 Google Scholar
[51]	Zhou Y, Jia Y H, Fang H H, Loi M A, Xie F Y, Gong L, Qin M C, Lu X H, Wong C P, Zhao N 2018 Adv. Funct. Mater. 28 1803130 Google Scholar
[52]	Abdi-Jalebi M, Andaji-Garmaroudi Z, Cacovich S, et al. 2018 Nature 555 497 Google Scholar
[53]	Kim J, Saidaminov M I, Tan H R, et al. 2018 Adv. Mater. 30 1706275 Google Scholar
[54]	Duong T, Pham H, Kho T H, et al. 2019 Adv. Energy Mater. 10 1903553 Google Scholar
[55]	Tan H R, Che F L, Wei M Y, Zhao Y C, Saidaminov M I, Petar T, Danny B, Grant W, Tan F R, Zhuang T T 2018 Nat. Commun. 9 3100 Google Scholar
[56]	Saliba M, Matsui T, Domanski K, Seo J Y, Ummadisingu A, Zakeeruddin S M, Correa-Baena J P, Tress W R, Abate A, Hagfeldt A, Grätzel M 2016 Science 354 206 Google Scholar
[57]	McMeekin D P, Sadoughi G, Rehman W, Eperon G E, Saliba M, Hörantner M T, Haghighirad A, Sakai N, Korte L, Rech B, Johnston M B, Herz L M, Snaith H J 2016 Science 351 151 Google Scholar
[58]	Zhuang J, Mao P, Luan Y G, Yi X H, Tu Z Y, Zhang Y Y, Yi Y P, Wei Y Z, Chen N L, Lin T, Wang F Y, Li C, Wang J Z 2019 ACS Energy Lett. 4 2913 Google Scholar
[59]	Gharibzadeh S, Abdollahi Nejand B, Jakoby M, et al. 2019 Adv. Energy Mater. 9 1803699 Google Scholar
[60]	Wang P Y, Zhang X W, Zhou Y Q, Jiang Q, Ye Q F, Chu Z M, Li X X, Yang X L, Yin Z G, You J B 2018 Nat. Commun. 9 2225 Google Scholar
[61]	Zhang J, Bai D L, Jin Z W, Bian H, Wang K, Sun J, Wang Q, Liu S Z F 2018 Adv. Energy Mater. 8 1703246 Google Scholar
[62]	Wang Y, Dar M I, Ono L K, Zhang T Y, Kan M, Li Y W, Zhang L J, Wang X T, Yang Y G, Gao X Y, Qi Y B, Grätzel M, Zhao Y X 2019 Science 365 591 Google Scholar
[63]	Ye Q F, Zhao Y, Mu S Q, Ma F, Gao F, Chu Z M, Yin Z G, Gao P Q, Zhang X W, You J B 2019 Adv. Mater. 1 1905143 Google Scholar
[64]	Xiao Q, Tian J J, Xue Q F, Wang J, Xiong B J, Han M M, Li Z, Zhu Z L, Yip H L, Li Z 2019 Angew. Chem. Int. Ed. 58 17724 Google Scholar
[65]	Green M A, Ho-Baillie A, Snaith H J 2014 Nat. Photonics 8 506 Google Scholar
[66]	Kim H S, Im S H, Park N G 2014 J. Phys.Chem. C 118 5615 Google Scholar
[67]	Li Z, Yang M J, Park J S, Wei S H, Berry J, Zhu K 2015 Chem. Mater. 28 284 Google Scholar
[68]	Chang Y H, Park C H 2004 J. Korean Phys. Soc. 44 889
[69]	Anaya M, Correabaena J P, Lozano G L, Saliba M, Anguita P, Roose B, Abate A, Steiner U, Grätzel M, Calvo M 2016 J. Mater. Chem. A 4 11214 Google Scholar
[70]	Noh J H, Im S H, Heo J H, Mandal T N, Seok S I 2013 Nano Lett. 13 1764 Google Scholar
[71]	Eperon G E, Stranks S D, Menelaou C, Johnston M B, Herz L M, Snaith H J 2014 Energy Environ. Sci. 7 982 Google Scholar
[72]	Saliba M, Correa-Baena J P, Grätzel M, Hagfeldt A, Abate A 2017 Angew. Chem. Int. Ed. 57 2554 Google Scholar
[73]	Unger E L, Bowring A R, Tassone C J, Pool V L, Gold-Parker A, Cheacharoen R, Stone K H, Hoke E T, Toney M F, McGehee M D 2014 Chem. Mater. 26 7158 Google Scholar
[74]	Dong Q, Yuan Y B, Shao Y C, Fang Y J, Wang Q, Huang J S 2015 Energy Environ. Sci. 8 2464 Google Scholar
[75]	Lee B, Hwang T, Lee S, Shin B, Park B 2019 Sci. Rep. 9 4803 Google Scholar
[76]	Zhang C P, Li Z P, Liu J, Xin Y C, Shao Z P, Cui G, Pang S P 2018 ACS Energy Lett. 3 1801 Google Scholar
[77]	Ma T, Wang S W, Zhang Y W, Zhang K X, Yi L X 2020 J. Mater. Sci. 55 464 Google Scholar
[78]	Tong G, Ono L K, Qi Y B 2019 Energy Technol. 8 1900961 Google Scholar
[79]	Protesescu L, Yakunin S, Bodnarchuk M I, et al. 2015 Nano Lett. 15 3692 Google Scholar
[80]	Mehrabian M, Dalir S, Mahmoudi G, Miroslaw B, Safin D A 2019 Eur. J. Inorg. Chem. 2019 3699 Google Scholar
[81]	Leijtens T, Bush K A, Prasanna R, McGehee M D 2018 Nat. Energy 3 828 Google Scholar
[82]	Mahesh S, Ball J M, Oliver R D J, McMeekin D P, Nayak P K, Johnston M B, Snaith H J 2020 Energy Environ. Sci. 13 258 Google Scholar
[83]	Levine I, Vera O G, Kulbak M, Ceratti D-R, Rehermann C, Márquez J A, Levcenko S, Unold T, Hodes G, Balberg I, Cahen D, Dittrich T 2019 ACS Energy Lett. 4 1150 Google Scholar
[84]	Song Z, Chen C, Li C, Awni R A, Zhao D, Yan Y 2019 Semicond. Sci. Technol. 34 093001 Google Scholar
[85]	Hoke E T, Slotcavage D J, Dohner E R, Bowring A R, Karunadasa H I, McGehee M D 2015 Chem. Sci. 6 613 Google Scholar
[86]	Slotcavage D J, Karunadasa H I, McGehee M D 2016 ACS Energy Lett. 1 1199 Google Scholar
[87]	Yun J S, Seidel J, Kim J, Soufiani A M, Huang S, Lau J, Jeon N J, Seok S I, Green M A, Ho-Baillie A 2016 Adv. Energy Mater. 6 1600330 Google Scholar
[88]	Beal R E, Hagström N Z, Barrier J, Gold-Parker A, Prasanna R, Bush K A, Passarello D, Schelhas L T, Brüning K, Tassone C J, Steinrück H G, McGehee M D, Toney M F, Nogueira A F 2020 Matter 2 207 Google Scholar
[89]	Bischak C G, Hetherington C L, Wu H, Aloni S, Ogletree D F, Limmer D T, Ginsberg N S 2017 Nano Lett. 17 1028 Google Scholar
[90]	Brennan M C, Draguta S, Kamat P V, Kuno M 2017 ACS Energy Lett. 3 204 Google Scholar
[91]	Liu S, Guan Y J, Sheng Y S, Hu Y, Rong Y G, Mei A Y, Han H W 2020 Adv. Energy Mater. 10 1902492 Google Scholar
[92]	Gao F, Zhao Y, Zhang X W, You J B 2020 Adv. Energy Mater. 10 1902650 Google Scholar
[93]	Han J H, Luo S P, Yin X W, Zhou Y, Nan H, Li J B, Li X, Oron D, Shen H P, Lin H 2018 Small 14 1801016 Google Scholar
[94]	Bai S, Da P M, Li C, Wang Z P, Yuan Z C, Fu F, Kawecki M, Liu X J, Sakai N, Wang J T W, Huettner S, Buecheler S, Fahlman M, Gao F, Snaith H J 2019 Nature 571 245 Google Scholar
[95]	Bi D Q, Yi C Y, Luo J S, Décoppet J D, Zhang F, Zakeeruddin Shaik M, Li X, Hagfeldt A, Grätzel M 2016 Nat. Energy 1 16142 Google Scholar
[96]	Noel N K, Abate A, Stranks S D, Parrott E S, Burlakov V M, Goriely A, Snaith H J 2014 ACS Nano 8 9815 Google Scholar
[97]	Correa-Baena J B, Luo Y Q, Brenner T M, Snaider J, Sun S J, Li X Y, Jensen M A, Hartono N P T, Nienhaus L, Wieghold S, Poindexter J R, Wang S, Meng Y S, Wang T, Lai B, Holt M V, Cai Z H, Bawendi M G, Huang L B, Buonassisi T, Fenning D P 2019 Science 363 627 Google Scholar
[98]	Kieslich G, Sun S, Cheetham A K 2014 Chem. Sci. 12 4712 Google Scholar
[99]	Kubicki D, Prochowicz D, Hofstetter A, Saski M, Yadav P, Bi D, Pellet N, Lewiński J, Zakeeruddin S M, Grätzel M 2018 J. Mater. Chem. A 140 3345 Google Scholar
[100]	Jodlowski A D, Roldán-Carmona C, Grancini G, Salado M, Ralaiarisoa M, Ahmad S, Koch N, Camacho L, de Miguel G, Nazeeruddin M K 2017 Nat. Energy 2 972 Google Scholar
[101]	Chen H, Wei Q, Saidaminov M I, Wang F, Johnston A, Hou Y, Peng Z J, Xu K M, Zhou W J, Liu Z H, Qiao L, Wang X, Xu S W, Li J Y, Long R, Ke Y Q, Sargent E H, Ning Z J 2019 Adv. Mater. 31 e1903559 Google Scholar
[102]	Stoddard R J, Rajagopal A, Palmer R L, Braly I L, Jen A K Y, Hillhouse H W 2018 ACS Energy Lett. 3 1261 Google Scholar
[103]	Yu H, Wang F, Xie F Y, Li W W, Chen J, Zhao N 2014 Adv. Funct. Mater. 24 7102 Google Scholar
[104]	Chae J S, Dong Q F, Huang J S, Centrone A 2015 Nano Lett. 15 8114 Google Scholar
[105]	Gao C, Liu J, Liao C, Ye Q Y, Zhang Y Z, He X L, Guo X W, Mei J, Lau W 2015 RSC Adv. 5 26175 Google Scholar
[106]	Xie Y L, Yu H Y, Duan J S, Xu L, Hu B 2020 ACS Appl. Mater. Interfaces 12 11190 Google Scholar
[107]	Abate A, Saliba M, Hollman D J, Stranks S D, Wojciechowski K, Avolio R, Grancini G, Petrozza A, Snaith H J 2014 Nano Lett. 14 3247 Google Scholar
[108]	Heo D Y, Lee T H, Iwan A, Kavan L, Omatova M, Majkova E, Kamarás K, Jang H W, Kim S Y 2020 J. Power Sources 458 228067 Google Scholar
[109]	Tong J H, Song Z N, Kim D H, et al. 2019 Science 364 475 Google Scholar
[110]	Tang G, Yang C, Stroppa A, Fang D N, Hong J W 2017 J. Chem. Phys. 146 224702 Google Scholar
[111]	Ke W J, Xiao C X, Wang C L, et al. 2016 Adv. Mater. 28 5214 Google Scholar
[112]	Xu J X, Buin A, Ip A H, et al. 2015 Nat. Commun. 6 7081 Google Scholar
[113]	Liang P W, Chueh C C, Williams S T, Jen A K Y 2015 Adv. Energy Mater. 5 1402321 Google Scholar
[114]	Gatti T, Menna E, Meneghetti M, Maggini M, Petrozza A, Lamberti F 2017 Nano Energy 41 84 Google Scholar
[115]	Fang Y J, Bi C, Wang D, Huang J S 2017 ACS Energy Lett. 2 782 Google Scholar
[116]	Cui C H, Li Y W, Li Y F 2017 Adv. Energy Mater. 7 1601251 Google Scholar
[117]	Lee J W, Park N G 2019 Adv. Energy Mater. 10 1903249 Google Scholar
[118]	Lee J W, Kim H S, Park N G 2016 Acc. Chem. Res. 49 311 Google Scholar
[119]	Xue D J, Hou Y, Liu S C, Wei M, Chen B, Huang Z, Li Z, Sun B, Proppe A H, Dong Y, Saidaminov M I, Kelley S O, Hu J S, Sargent E H 2020 Nat. Commun. 11 1514 Google Scholar
[120]	Jan S, Robby P, Rolf B 2018 Sol. Energy Mater. Sol. Cells 187 39 Google Scholar
[121]	Luo D Y, Yang W Q, Wang Z P, et al. 2018 Science 360 1442 Google Scholar
[122]	Bu X N, Westbrook R J E, Lanzetta L, Ding D, Chotchuangchutchaval T, Aristidou N, Haque S A 2019 Sol. RRL 3 1800282 Google Scholar
[123]	Wang Q, Zheng X P, Deng Y H, Zhao J J, Chen Z L, Huang J S 2017 Joule 1 371 Google Scholar
[124]	Zheng X P, Chen B, Dai J, Fang Y J, Bai Y, Lin Y Z, Wei H T, Zeng X C, Huang J S 2017 Nat. Energy 2 17102 Google Scholar
[125]	Elgamel H E, Barnett A M, Rohatgi A, Chen Z, Vinckier C, Nijs J, Mertens R 1995 J. Appl. Phys. 78 3457 Google Scholar
[126]	Jaysankar M, Raul B A L, Bastos J, Burgess C, Weijtens C, Creatore M, Aernouts T, Kuang Y, Gehlhaar R, Hadipour A, Poortmans J 2018 ACS Energy Lett. 4 259 Google Scholar
[127]	Stolterfoht M, Caprioglio P, Wolff C M, et al. 2019 Energy Environ. Sci. 12 2778 Google Scholar
[128]	Bian H, Bai D L, Jin Z W, Wang K, Liang L, Wang H R, Zhang J R, Wang Q, Liu S Z F 2018 Joule 2 1500 Google Scholar
[129]	Zeng Q, Liu L, Xiao Z, Liu F Y, Hua Y, Yuan Y B, Ding L M 2019 Sci. Bull. 64 885 Google Scholar
[130]	Zhao D W, Ding L M 2020 Sci. Bull. 65 1144 Google Scholar
[131]	Zhao D W, Chen C, Wang C L, Junda M M, Song Z N, Grice C R, Yu Y, Li C W, Subedi B, Podraza N J, Zhao X Z, Fang G J, Xiong R G, Zhu K, Yan Y F 2018 Nat. Energy 3 1093 Google Scholar
[132]	Shen H P, Omelchenko S T, Jacobs D A, et al. 2018 Sci. Adv. 4 eaau9711 Google Scholar
[133]	Hou F H, Yan L L, Shi B, et al. 2019 ACS Appl. Energy Mater. 2 243 Google Scholar
[134]	Werner J, Weng C H, Walter A, Fesquet L, Seif J P, De Wolf S, Niesen B, Ballif C 2016 J. Phys. Chem. Lett. 7 161 Google Scholar
[135]	Sahli F, Kamino B A, Werner J, et al. 2018 Adv. Energy Mater. 8 1701609 Google Scholar
[136]	Fan R D, Z N, Zhang L, Yang R, Meng Y, Li L W, Guo T, Chen Y H, Xu Z Q, Zheng G H J, Huang Y, Li L, Qin L, Qiu X H, Chen Q, Zhou H P 2017 Sol. RRL 1 1700149 Google Scholar
[137]	Qiu Z W, Xu Z Q, Li N X, Zhou N, Chen Y H, Wan X X, Liu J L, Li N, Hao X T, Bi P Q, Chen Q, Cao B Q, Zhou H P 2018 Nano Energy 53 798 Google Scholar
[138]	Zhu S J, Y X, Ren Q S, et al. 2018 Nano Energy 45 280 Google Scholar
[139]	Zhu S J, Hou F H, Huang W, et al. 2018 Sol. RRL 2 1800176 Google Scholar
[140]	Hou F H, Han C, Isabella O, et al. 2019 Nano Energy 56 234 Google Scholar
[141]	Bush K A, Palmstrom A F, Yu Z J, et al. 2017 Nat. Energy 2 17009 Google Scholar
[142]	Bush K A, Manzoor S, Frohna K, Yu Z J, Raiford J A, Palmstrom A F, Wang H-P, Prasanna R, Bent S F, Holman Z C, McGehee M D 2018 ACS Energy Lett. 3 2173 Google Scholar
[143]	Marko Jošt, Köhnen E, Morales-Vilches A B, Lipovšek B, Jäger K, Macco B, Al-Ashouri A, Krč J, Korte L, Rech B, Schlatmann R, Topič M, Stannowski B, Albrecht S 2018 Energy Environ. Sci. 11 3511 Google Scholar
[144]	Sahli F, Werner J, Kamino B A, et al. 2018 Nat. Mater. 17 820 Google Scholar
[145]	Nogay G, Sahli F, Werner J, Monnard R, Boccard M, Despeisse M, Haug F J, Jeangros Q, Ingenito A, Ballif C 2019 ACS Energy Lett. 4 844 Google Scholar
[146]	Mazzarella L, Lin Y H, Kirner S, Morales-Vilches A B, Korte L, Albrecht S, Crossland E, Stannowski B, Case C, Snaith H J, Schlatmann R 2019 Adv. Energy Mater. 9 1803241 Google Scholar
[147]	Chen B, Yu Z J, Manzoor S, Wang S, Weigand W, Yu Z H, Yang G, Ni Z Y, Dai X Z, Holman Z C, Huang J S 2020 Joule 4 850 Google Scholar
[148]	Berhe T A, Su W N, Chen C H, Pan C J, Cheng J H, Chen H M, Tsai M C, Chen L Y, Dubale A A, Hwang B J 2016 Energy Environ. Sci. 9 323 Google Scholar
[149]	Li Z, Xiao C X, Yang Y, et al. 2017 Energy Environ. Sci. 10 1234 Google Scholar

Cited By

图 1 宽带隙钙钛矿太阳电池性能统计图(E_g ≥ 1.63 eV, PCE > 15%)　(a) V_OC与E_g之间的关系, 红色阴影部分表示的是qV_OC与E_g的比值小于0.75, 其中q表示单位电荷量; (b) PCE和E_g之间的关系

Figure 1. Performance statistics of WBG-PSCs (E_g ≥ 1.63 eV, PCE > 15%): (a) Relationship between V_OC and E_g. The red shaded part indicates that the ratio between qV_OC and E_g is less than 0.75, where q represents the unit charge; (b) relationship between PCE and E_g.

DownLoad: Full-Size Img PowerPoint

图 2 (a)钙钛矿结构; (b)不同钙钛矿所对应的容差因子图以及相应的晶体结构^[67]

Figure 2. (a) Structure of perovskite; (b) corresponding tolerance factor and crystal structure of different perovskites^[67].

DownLoad: Full-Size Img PowerPoint

图 3 (a) MAPb(Br_xI_1–x)₃的紫外可见吸收光谱、不同颜色钙钛矿薄膜照片以及带隙随Br含量变化的函数图^[70]; (b) FAPb(Br_1–yI_y)₃的紫外可见吸收光谱和光致发光(PL)光谱^[71]; (c) CsPb(Br_zI_1–z)₃的钙钛矿溶液和对应的光致发光(PL)谱^[79]

Figure 3. (a) UV-visible absorption spectra, photos of perovskite films with different colors, as well as functional graph between bandgap and bromine content of MAPb(Br_xI_1–x)₃^[70]; (b) UV-visible absorption spectra and photoluminescence (PL) spectra of FAPb(Br_1–yI_y)₃^[71]; (c) photos of CsPb(Br_zI_1–z)₃ solutions and corresponding PL spectra^[79].

DownLoad: Full-Size Img PowerPoint

图 4 (a)卤素离子在光照下发生迁移和团簇示意图^[90]; (b) MAPb(Br_0.4I_0.6)₃在光照下的光致发光(PL)光谱, 插图表示初始PL增长率的温度依赖性^[85]; (c)在约50 mW /cm²的条件下, MAPb(Br_0.4I_0.6)₃膜在白光浸泡5 min前(黑色线)、后(红色线)的XRD图谱, 将MAPb(Br_0.2I_0.8)₃膜(绿色虚线)和MAPb(Br_0.7I_0.3)₃膜(棕色虚线)的XRD图谱进行比较^[85]

Figure 4. (a) Schematic illustration of halogen ion migration and clusters under light^[90]; (b) photoluminescence (PL) spectra of MAPb(Br_0.4I_0.6)₃ under light. The illustration shows the temperature dependence of the initial PL growth rate^[85]; (c) the XRD pattern of MAPb(Br_0.4I_0.6)₃ film before (black) and after (red) white-light soaking for 5 min at about 50 mW/cm². XRD patterns of the MAPb(Br_0.2I_0.8)₃ film (dashed green) and the MAPb(Br_0.7I_0.3)₃ film (dashed brown) are included for comparison^[85].

DownLoad: Full-Size Img PowerPoint

图 5 (a) APbI₃钙钛矿的容差因子^[56]; (b) FACs基钙钛矿光稳定性明显提高^[57]; (c) Cs_xFA_1–xPb(Br_yI_1–y)₃材料中的带隙和V_OC 变化^[37]; (d) K⁺钝化作用示意图^[52]

Figure 5. (a) Tolerance factor of APbI₃^[56]; (b) FACs-based perovskite light stability was improved obviously^[57]; (c) changes of E_g and V_OC in the Cs_xFA_1–xPb(Br_yI_1–y)₃ compositions^[37]; (d) schematic of K⁺ passivation^[52].

DownLoad: Full-Size Img PowerPoint

图 6 (a) 3种阳离子的分子构型以及MA⁺空间旋转的示意图^[55]; (b) CsFA和CSMAFA钙钛矿太阳电池最佳J-V曲线和EQE曲线^[55]; (c) Cs⁺和GA⁺混合到钙钛矿晶格以及对带隙的调控曲线^[102]; (d) DMA⁺对钙钛矿带隙的调整^[43]

Figure 6. (a) The molecular configurations of the three cations and the rotation of MA⁺ in space^[55]; (b) J-V and EQE curves of the best-performing CsFA and CsMAFA PSCs^[55]; (c) Cs⁺ and GA⁺ are mixed into the perovskite lattice and the tuning curves of the E_g^[102]; (d) DMA⁺ adjusts the E_g of perovskite^[43].

DownLoad: Full-Size Img PowerPoint

图 7 基于MACl以及MAH₂PO₂添加剂的钙钛矿薄膜SEM图像^[40]

Figure 7. SEM images of perovskite films based on MACl and MAH₂PO₂ additives^[40].

DownLoad: Full-Size Img PowerPoint

图 8 三卤化物钙钛矿的光稳定性　(a), (b)对照组钙钛矿薄膜(Cs25Br20)经过10倍和100倍太阳光照20 min后的PL光谱, 箭头表示PL峰位随时间变化的方向; (c)对照组薄膜的光谱中心随时间的移动, 在更强光照下, 红移变得更加明显; (d), (e)三卤钙钛矿薄膜(Cs25Br20+Cl3)分别经过10倍和100倍太阳光照20 min后的PL光谱; (f)三卤钙钛矿薄膜的光谱中心随时间的移动, 在更强光照下, 蓝移变得更加明显^[44]

Figure 8. Light stability of triple-halide perovskite: (a), (b) PL spectra of control perovskite films (Cs25Br20) under 10-sun and 100-sun illumination for 20 min, respectively. Arrows indicate the direction of the PL shift over time; (c) the shift of the spectral centroids of control films over time. The red shift becomes more obvious under higher injection; (d), (e) PL spectra of triple-halide perovskites (Cs22Br15+Cl3) under 10-sun and 100-sun illumination for 20 min, respectively; (f) the shift of the spectral centroids of triple-halide perovskites over time. The blue shift becomes more obvious under higher injection^[44].

DownLoad: Full-Size Img PowerPoint

图 9 (a)硫氰酸铅添加剂和DMF溶剂辅助退火对钙钛矿薄膜性能的改善^[50]; (b), (c)阴离子工程的钙钛矿太阳电池的器件性能和光稳定性^[45]

Figure 9. (a) Performance improvement of perovskite film by adding Pb(SCN)₂ and DMF solvent assisted annealing^[50]; (b), (c) the device performance and stability of PSCs with anion engineering^[45].

DownLoad: Full-Size Img PowerPoint

图 10 (a)非加快反溶剂萃取(左)和加快反溶剂萃取(右)制备的钙钛矿薄膜SEM图像^[119]; (b)无尿素添加剂(左)和尿素添加剂(右)的700 nm厚钙钛矿薄膜SEM图像^[119]; (c)甲酰胺诱导直接形成钙钛矿相, 抑制非钙钛矿相的形成^[53]; (d)甲酰胺添加剂提高钙钛矿薄膜结晶质量(右)^[53]

Figure 10. (a) SEM images of perovskite films prepared using no-boosted solvent extraction (BSE) (left) and BSE (right) methods ^[119]; (b) SEM images of thick perovskite films without urea additives (left) and with urea additives (right) ^[119]; (c) formamide induces direct formation of perovskite phase and inhibits the formation of non-perovskite phase^[53]; (d) improvement of perovskite film crystallization quality by formamide additives (right)^[53].

DownLoad: Full-Size Img PowerPoint

图 11 (a) BA分子与钙钛矿薄膜表面作用示意图^[49]; (b)用BABr的异丙醇溶液处理钙钛矿薄膜表面形成二维钙钛矿薄层^[59]; (c)经过BABr溶液处理的钙钛矿太阳电池J-V曲线⁵⁹; (d) BABr溶液处理的钙钛矿太阳电池稳定功率输出曲线(SPCE)⁵⁹; (e)在连续照明(AM 1.5 G)下测量的最优电池的稳态开路电压(V_OC)⁵⁹; (f), (g)两种电池的开路电压和效率统计^[59]

Figure 11. (a) Schematic of the impact of BA modification on the perovskite film^[49]; (b) the perovskite film surface was treated with BABr solution to form a 2D perovskite thin layer^[59]; (c) J-V and (d) SPCE curve of PSC with and without BABr treatment^[59]; (e) steady-state V_OC of the best-performing PSC measured under continuous illumination (AM 1.5 G)^[59]; (f), (g) V_OC and PCE statistics of two kinds of PSCs^[59].

DownLoad: Full-Size Img PowerPoint

图 12 宽带隙钙钛矿、窄带隙钙钛矿和常用电荷传输层的能带图

Figure 12. Energy band schematic of wide bandgap perovskite, narrow bandgap perovskite, and commonly used charge transport layers.

DownLoad: Full-Size Img PowerPoint

图 13 (a) 2T叠层太阳电池的理论效率图^[81]; (b), (c) N-I-P型和P-I-N型2T钙钛矿/硅TSCs结构示意图(TCO: 透明导电氧化物, AR coating: 抗反射膜)

Figure 13. (a) Theoretical efficiency limit for 2T tandem solar cells; (b), (c) schematics of device structures for N-I-P and P-I-N 2T perovskite/silicon TSCs (TCO: Transparent Conductive Oxide. AR coating: Antireflective coating).

DownLoad: Full-Size Img PowerPoint

表 1 宽带隙钙钛矿太阳电池性能统计(E_g ≥ 1.63 eV, PCE > 15%)

Table 1. WBG-PSCs performance statistics (E_g ≥ 1.63 eV and PCE > 15%).

Type	Perovskite	E_g/eV	V_OC/V	qV_OC/E_g	J_SC/mA·cm^–2	FF/%	PCE/%	Ref.
p-i-n	MAPbI_2.5Br_0.5	1.72	1.060	0.61	18.30	78.2	16.60	[35]
p-i-n	(FA_0.83MA_0.17)_0.95Cs_0.05Pb(I_0.6Br_0.4)₃	1.71	1.210	0.71	19.70	77.5	18.50	[36]
p-i-n	FA_0.6Cs_0.4Pb(I_0.7Br_0.3)₃	1.75	1.170	0.67	17.50	80.0	16.30	[37]
p-i-n	FA_0.83MA_0.17Pb(I_0.6Br_0.4)₃	1.72	1.150	0.67	19.40	77.0	17.20	[38]
p-i-n	FA_0.8Cs_0.2Pb(I_0.7Br_0.3)₃	1.75	1.240	0.71	17.92	81.9	18.19	[39]
p-i-n	(FA_0.65MA_0.20Cs_0.15)Pb(I_0.8Br_0.2)₃	1.68	1.170	0.70	21.20	79.8	19.50	[27]
p-i-n	Cs_0.15(FA_0.83MA_0.17)_0.85Pb(I_0.8Br_0.2)₃	1.64	1.190	0.73	19.50	80.2	18.60	[40]
p-i-n	CsPbI₃	1.73	1.160	0.67	17.70	78.6	16.10	[41]
p-i-n	CsPbI₂Br	1.80	1.230	0.67	15.26	78.0	15.19	[42]
p-i-n	FA_0.6Cs_0.3DMA_0.1PbI_2.4Br_0.6	1.70	1.200	0.70	19.60	82.0	19.40	[43]
p-i-n	FA_0.75Cs_0.25Pb(I_0.8Br_0.2)₃	1.68	1.217	0.72	20.18	83.6	20.42	[44]
p-i-n	(FA_0.65MA0_.2Cs_0.15)Pb(I_0.8Br_0.2)₃	1.67	1.200	0.72	NA	NA	20.70	[45]
p-i-n	(FA_0.64MA_0.20Cs_0.15)Pb_0.99(I_0.79Br_0.2)₃	1.68	1.196	0.71	21.65	81.5	21.00	[46]
n-i-p	Rb_0.05(FA_0.75MA_0.15Cs_0.1)_0.95PbI₂Br	1.73	1.120	0.71	19.40	73.0	15.90	[47]
n-i-p	FA_0.83Cs_0.17Pb(I_0.6Br_0.4)₃	1.75	1.160	0.66	18.27	78.5	16.28	[48]
n-i-p	FA_0.85Cs_0.15Pb(I_0.73Br_0.27)₃	1.72	1.240	0.72	19.83	73.7	18.13	[49]
n-i-p	FA_0.8Cs_0.2Pb(I_0.7Br_0.3)₃	1.75	1.250	0.71	18.53	79.0	18.27	[50]
n-i-p	MAPb(Br_0.2I_0.8)₃	1.72	1.120	0.65	17.30	82.3	15.90	[51]
n-i-p	K_0.1(Cs_0.06FA_0.79MA_0.15)_0.9Pb(I_0.4Br_0.6)₃	1.78	1.230	0.69	17.90	79.0	17.50	[52]
n-i-p	FA_0.83Cs_0.17Pb(I_0.6Br_0.4)₃	1.75	1.230	0.70	18.34	79.0	17.80	[53]
n-i-p	Cs_0.17FA_0.83PbI_2.2Br_0.8	1.72	1.270	0.74	19.30	77.4	18.60	[54]
n-i-p	Cs_0.12MA_0.05FA_0.83Pb(I_0.6Br_0.4)₃	1.74	1.250	0.72	19.00	81.5	19.10	[55]
n-i-p	Rb₅(Cs₅MAFA)₉₅Pb(I_0.83Br_0.17)₃	1.63	1.240	0.76	22.80	81.0	21.60	[56]
n-i-p	FA_0.83Cs_0.17Pb(I_0.6Br_0.4)₃	1.74	1.200	0.70	19.40	75.1	17.00	[57]
n-i-p	FA_0.17Cs_0.83PbI_2.2Br_0.8	1.72	1.244	0.72	19.80	75.0	18.60	[51]
n-i-p	Cs_0.2FA_0.8Pb(I_0.75Br_0.25)₃	1.65	1.220	0.74	21.20	80.5	20.70	[55]
n-i-p	BA_0.09(FA_0.83 Cs_0.17)_0.91Pb(I_0.6Br_0.4)₃	1.72	1.180	0.69	19.80	73.0	17.30	[38]
n-i-p	FA_0.15Cs_0.85Pb(I_0.73Br_0.27)₃	1.72	1.240	0.72	19.83	73.7	18.10	[58]
n-i-p	FA_0.83Cs_0.17Pb(I_0.6Br_0.4)₃	1.72	1.310	0.76	19.30	78.0	19.50	[59]
n-i-p	Rb_0.05Cs_0.095 MA_0.1425 FA_0.7125PbI₂Br	1.72	1.205	0.70	18.00	78.9	17.10	[54]
n-i-p	CsPbI₃	1.73	1.080	0.62	18.41	79.32	15.71	[60]
n-i-p	CsPbI₂Br	1.80	1.230	0.68	16.79	77.81	16.07	[61]
n-i-p	β-CsPbI₃	1.68	1.110	0.66	20.23	82.0	18.40	[62]
n-i-p	CsPbI_3-xBr_x	1.77	1.234	0.69	18.30	82.5	18.64	[63]
n-i-p	CsPbI₂Br	1.80	1.270	0.71	15.40	79.0	15.50	[64]
注: NA表示文献中没有给出具体数值; FF表示填充因子.

DownLoad: CSV

表 2 钙钛矿中常用离子有效半径^[56,72]

Table 2. Effective radius of commonly used ions in perovskite^[56,72].

序号	钙钛矿中常用离子	有效半径R/pm
1	胍离子(GA⁺)	278
2	二甲胺离子(DMA⁺)	272
3	甲脒离子(FA⁺)	253
4	甲胺离子(MA⁺)	217
5	铯离子(Cs⁺)	167
6	铷离子(Rb⁺)	152
7	钾离子(K⁺)	138
8	钠离子(Na⁺)	102
9	铅离子(Pb²⁺)	119
10	锡离子(Sn²⁺)	112
11	碘离子(I^–)	220
12	溴离子(Br^–)	196
13	氯离子(Cl^–)	181

DownLoad: CSV

表 3 近年来典型的2T钙钛矿/硅TSCs的详细性能参数总结

Table 3. Summary of detailed performance of typical 2T perovskite/silicon TSCs in recent years.

Type	Perovskite	E_g/eV	V_OC/V	Jsc/mA·cm^–2	FF/%	PCE/%	Year	Area/cm²	Ref.
N-I-P	MAPbI₃	1.61	1.580	11.50	75.00	13.70	2015	1.00	[15]
	FA_0.83MA_0.17Pb(I_0.84Br_0.16)₃	1.63	1.785	14.00	79.50	19.90	2016	0.16	[133]
	MAPbI₃	1.60	1.692	15.80	79.90	21.40	2016	0.17	[134]
	MAPbI₃	1.60	1.701	16.10	70.10	19.20	2016	1.22	[134]
	Cs_0.19MA_0.81PbI₃	1.59	1.751	18.80	77.10	22.70	2018	0.25	[135]
	Cs_0.19MA_0.81PbI₃	1.59	1.779	16.50	74.10	21.70	2018	1.43	[135]
	Cs_0.19FA_0.81Pb(I_0.78Br_0.22)₃	1.63	1.769	16.50	65.40	19.10	2018	12.96	[135]
	MA_0.37FA_0.48Cs_0.15PbI_2.01Br_0.99	1.69	1.703	15.26	79.20	20.57	2017	0.03	[136]
	FA_0.5MA_0.38Cs_0.12PbI_2.04Br_0.96	1.69	1.655	16.50	81.10	22.22	2018	0.06	[137]
	FA_0.75MA_0.25 Pb(I_0.76B_0.24)₃	1.65	1.710	15.49	71.00	18.81	2018	0.13	[138]
	Cs_0.08FA_0.74MA_0.18Pb(I_0.88Br_0.12)₃	1.65	1.780	17.82	75.00	23.73	2018	0.13	[139]
	Cs_0.1(FA_0.75MA_0.25)_0.9Pb(I_0.78Br_0.22)₃	1.67	1.830	16.74	70.00	21.31	2019	0.13	[133]
	Cs _0.08FA_0.69MA_0.23Pb(I_0.78Br₂₂)₃	1.67	1.750	16.89	74.18	21.93	2019	0.13	[140]
	CsRbFAMAPbI_3-xBr_x	1.62	1.763	17.80	78.10	24.50	2018	1.00	[132]
P-I-N	Cs_0.17FA_0.83Pb(Br_0.17I_0.83)₃	1.63	1.650	18.10	79.00	23.60	2017	1.00	[141]
	FA _0.75Cs_0.25Pb(I_0.8Br_0.2)₃	1.68	1.770	18.40	77.00	25.00	2018	1.00	[142]
	Cs_0.05(MA_0.17FA_0.83)Pb_1.1(I_0.83Br_0.17)₃	1.60	1.760	18.50	78.50	25.50	2018	0.81	[143]
	Cs_xFA_1-xPb(I, Br)₃	1.60	1.788	19.50	73.10	25.20	2018	1.42	[144]
	Cs_xFA_1-x Pb(I, Br)₃	1.60	1.741	19.50	74.70	25.40	2018	1.42	[145]
	Cs_0.15(FA_0.83MA_0.17)_0.85Pb(I_0.8Br_0.2)₃	1.64	1.800	17.80	79.40	25.40	2018	0.49	[40]
	Cs_0.05(FA_0.83MA_0.17)_0.95Pb(I_0.82Br_0.18)₃	1.63	1.792	19.02	74.60	25.43	2019	1.00	[146]
	Cs_0.1MA_0.9Pb(I_0.9Br_0.1)₃	1.60	1.820	19.20	75.30	26.20	2020	NA	[147]
	Cs _0.25FA_0.75Pb(I_0.85Br_0.15Cl_0.05)₃	1.67	1.890	19.10	75.30	27.04	2020	1.00	[44]
	Cs_0.05MA_0.15FA_0.8Pb(I_0.75Br_0.25)₃	1.68	1.700	19.80	77.00	25.70	2020	0.83	[46]
	(FA_0.65MA_0.2Cs_0.15)Pb(I_0.8Br_0.2)₃	1.68	1.818	18.90	76.40	26.20	2020	1.00	[45]
注: NA表示文献中没有给出具体数值.

DownLoad: CSV

map

[1]	Xing G C, Mathews N, Lim S S, Yantara N, Liu X F, Sabba D, Grätzel M, Mhaisalkar S, Sum T C 2014 Nat. Mater. 13 476 Google Scholar
[2]	Tan Z K, Moghaddam R S, Lai M L, Docampo P, Higler R, Deschler F, Price M, Sadhanala A, Pazos L M, Credgington D 2014 Nat. Nanotechnol. 9 687 Google Scholar
[3]	Dou L, Yang Y, You J B, Hong Z, Chang W H, Li G, Yang Y 2014 Nat. Commun. 5 5404 Google Scholar
[4]	Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[5]	Kim M, Kim G H, Lee T K, Choi I W, Choi H W, Jo Y, Yoon Y J, Kim J W, Lee J Y, Huh D, Lee H, Kwak S K, Kim J Y, Kim D S 2019 Joule 3 2179 Google Scholar
[6]	Jiang Q, Zhao Y, Zhang X W, Yang X L, Chen Y, Chu Z, Ye Q, Li X X, Yin Z G, You J B 2019 Nat. Photonics 13 460 Google Scholar
[7]	Wang P Y, Li R J, Chen B B, Hou F H, Zhang J, Zhao Y, Zhang X D 2020 Adv. Mater. 32 1905766 Google Scholar
[8]	Min H, Kim M, Lee S U, Kim H, Kim G, Choi K, Lee J Hee, Seok S I 2019 Science 366 749 Google Scholar
[9]	Yoo J J, Wieghold S, Sponseller M C, Chua M R, Bertram S N, Hartono N T P, Tresback J S, Hansen E C, Correa-Baena J P, Bulovic V 2019 Energy Environ. Sci. 12 2192 Google Scholar
[10]	Liu Y H, Akin S, Pan L F, Uchida R, Grätzel M 2019 Sci. Adv. 5 eaaw2543 Google Scholar
[11]	Zhu P C, Gu S, Luo X, Gao Y, Li S L, Zhu J, Tan H R 2019 Adv. Energy Mater. 10 1903083 Google Scholar
[12]	Zheng X P, Hou Y, Bao C X, Yin J, Yuan F L, Huang Z R, Song K P, Liu J K, Troughton J, Gasparini N, Zhou C, Lin Y B, Xue D J, Chen B, Johnston A K, Wei N N, Hedhili M N, Wei M, Alsalloum A Y, Maity P, Turedi B, Yang C, Baran D, Anthopoulos T D, Han Y, Lu Z H, Mohammed O F, Gao F, Sargent E H, Bakr O M 2020 Nat. Energy 5 131 Google Scholar
[13]	Shockley W, Queisser H J 1961 J. Appl. Phys. 32 510 Google Scholar
[14]	Beiley Z M, McGehee M D 2012 Energy Environ. Sci. 5 9173 Google Scholar
[15]	Mailoa J P, Bailie C D, Johlin E C, Hoke E T, Akey A J, Nguyen W H, McGehee M D, Buonassisi T 2015 Appl. Phys. Lett. 106 121105 Google Scholar
[16]	Albrecht S, Saliba M, Correa Baena J P, Lang F, Kegelmann L, Mews M, Steier L, Abate A, Rappich J, Korte L, Schlatmann R, Nazeeruddin M K, Hagfeldt A, Grätzel M, Rech B 2016 Energy Environ. Sci. 9 81 Google Scholar
[17]	Altazin S, Stepanova L, Werner J, Niesen B, Ballif C, Ruhstaller B 2018 Opt. Express 26 A579 Google Scholar
[18]	Fang Z M, Wang S Z, Yang S F, Ding L M 2018 Inorg. Chem. Front. 5 1690 Google Scholar
[19]	Hu W P, He X, Fang Z M, Lian W T, Shang Y B, Li X C, Zhou W R, Zhang M M, Chen T, Lu Y L, Zhang L J, Ding L M, Yang S F 2020 Nano Energy 68 104362 Google Scholar
[20]	Jia X, Ding L M 2018 Sci. China Mater. 62 54 Google Scholar
[21]	Zuo C T, Ding L M 2017 Angew. Chem. Int. Ed. 56 6528 Google Scholar
[22]	Chen B, Zheng X P, Bai Y, Padture N P, Huang J S 2017 Adv. Energy Mater. 7 1602400 Google Scholar
[23]	Hu J N, Cheng Q, Fan R D, Zhou H P 2017 Sol. RRL 1 1700045 Google Scholar
[24]	Lal N N, Dkhissi Y, Li W, Hou Q C, Cheng Y B, Bach U 2017 Adv. Energy Mater. 7 1602761 Google Scholar
[25]	Jošt M, Kegelmann L, Korte L, Albrecht S 2020 Adv. Energy Mater. 10 1904102 Google Scholar
[26]	Al-Ashouri A, Magomedov A, Roß M, et al. 2019 Energy Environ. Sci. 12 3356 Google Scholar
[27]	Kim D H, Muzzillo C P, Tong J, et al. 2019 Joule 3 1734 Google Scholar
[28]	Lin R, Xiao K, Qin Z Y, Han Q L, Zhang C F, Wei M Y, Saidaminov M I, Gao Y, Xu J, Xiao M, Li A D, Zhu J, Sargent E H, Tan H R 2019 Nat. Energy 4 864 Google Scholar
[29]	McMeekin D P, Mahesh S, Noel N K, Klug M T, Lim J, Warby J H, Ball J M, Herz L M, Johnston M B, Snaith H J 2019 Joule 3 387 Google Scholar
[30]	Xue Q F, Xia R X, Brabec C J, Yip H L 2018 Energy Environ. Sci. 11 1688 Google Scholar
[31]	Henemann A 2008 Renew. Energy Focus 9 14 Google Scholar
[32]	Shi B, Duan L R, Zhao Y, Luo J S, Zhang X D 2020 Adv. Mater. 32 1806474 Google Scholar
[33]	Park S, Chang W J, Lee C W, Park S, Ahn H Y, Nam K T 2016 Nat. Energy 2 16185 Google Scholar
[34]	陈为, 魏伟, 孙予罕 2017 中国科学: 化学 47 1251 Google Scholar Chen W, Wei W, Sun Y H 2017 Sci. China: Chem. 47 1251 Google Scholar
[35]	Hu M, Bi C, Yuan Y B, Bai Y, Huang J S 2016 Adv. Sci. 3 1500301 Google Scholar
[36]	Lin Y Z, Chen B, Zhao F W, Zheng X P, Deng Y H, Shao Y C, Fang Y J, Bai Y, Wang C R, Huang J S 2017 Adv. Mater. 29 1700607 Google Scholar
[37]	Bush K A, Frohna K, Prasanna R, Beal R E, Leijtens T, Swifter S A, McGehee M D 2018 ACS Energy Lett. 3 428 Google Scholar
[38]	Wang Z P, Lin Q Q, Chmiel F P, Sakai N, Herz L M, Snaith H J 2017 Nat. Energy 2 17135 Google Scholar
[39]	Chen C, Song Z N, Xiao C X, Zhao D W, Shrestha N, Li C W, Yang G, Yao F, Zheng X L, Ellingson R J, Jiang C S, Al-Jassim M, Zhu K, Fang G J, Yan Y F 2019 Nano Energy 61 141 Google Scholar
[40]	Chen B, Yu Z S, Liu K, Zheng X P, Liu Y, Shi J W, Spronk D, Rudd P N, Holman Z, Huang J S 2019 Joule 3 177 Google Scholar
[41]	Wang J, Zhang J, Zhou Y Z, Liu H B, Xue Q F, Li X S, Chueh C C, Yip L P, Zhu Z L, Jen A K Y 2020 Nat. Commun. 11 177 Google Scholar
[42]	Liu C, Yang Y Z, Zhang C L, Wu S H, Wei L Y, Guo F, Arumugam G M, Hu J L, Liu X Y, Lin J, Schropp R E L, Mai Y H 2020 Adv. Mater. 32 1907361 Google Scholar
[43]	Palmstrom A F, Eperon G E, Leijtens T, et al. 2019 Joule 3 2193 Google Scholar
[44]	Xu J X, Boyd C C, Yu Z J, et al. 2020 Science 367 1097 Google Scholar
[45]	Kim D, Jung H J, Park I J, Larson B W, Dunfield S P, Xiao C X, Kim J, Tong J H, Boonmongkolras P, Ji S G, Zhang F, Pae S R, Kim M, Kang S B, Dravid V, Berry J J, Kim J Y, Zhu K, Kim D H, Shin B 2020 Science 368 155 Google Scholar
[46]	Ye J Y, Tong J H, Hu J, et al. 2020 Sol. RRL 4 2000082 Google Scholar
[47]	Duong T, Wu Y L, Shen H P, et al. 2017 Adv. Energy Mater. 7 1700228 Google Scholar
[48]	Yang M J, Kim D H, Yu Y, Li Z, Reid O G, Song Z N, Zhao D W, Wang C L, Li L W, Meng Y, Guo T, Yan Y F, Zhu K 2018 Mater. Today Energy 7 232 Google Scholar
[49]	Zhou Y, Wang F, Cao Y, Wang J P, Fang H H, Loi M A, Zhao N, Wong C P 2017 Adv. Energy Mater. 7 1701048 Google Scholar
[50]	Yu Y, Wang C L, Grice C R, Shrestha N, Zhao D W, Liao W Q, Guan L, Awni R A, Meng W W, Cimaroli A J, Zhu K, Ellingson R J, Yan Y F 2017 ACS Energy Lett. 2 1177 Google Scholar
[51]	Zhou Y, Jia Y H, Fang H H, Loi M A, Xie F Y, Gong L, Qin M C, Lu X H, Wong C P, Zhao N 2018 Adv. Funct. Mater. 28 1803130 Google Scholar
[52]	Abdi-Jalebi M, Andaji-Garmaroudi Z, Cacovich S, et al. 2018 Nature 555 497 Google Scholar
[53]	Kim J, Saidaminov M I, Tan H R, et al. 2018 Adv. Mater. 30 1706275 Google Scholar
[54]	Duong T, Pham H, Kho T H, et al. 2019 Adv. Energy Mater. 10 1903553 Google Scholar
[55]	Tan H R, Che F L, Wei M Y, Zhao Y C, Saidaminov M I, Petar T, Danny B, Grant W, Tan F R, Zhuang T T 2018 Nat. Commun. 9 3100 Google Scholar
[56]	Saliba M, Matsui T, Domanski K, Seo J Y, Ummadisingu A, Zakeeruddin S M, Correa-Baena J P, Tress W R, Abate A, Hagfeldt A, Grätzel M 2016 Science 354 206 Google Scholar
[57]	McMeekin D P, Sadoughi G, Rehman W, Eperon G E, Saliba M, Hörantner M T, Haghighirad A, Sakai N, Korte L, Rech B, Johnston M B, Herz L M, Snaith H J 2016 Science 351 151 Google Scholar
[58]	Zhuang J, Mao P, Luan Y G, Yi X H, Tu Z Y, Zhang Y Y, Yi Y P, Wei Y Z, Chen N L, Lin T, Wang F Y, Li C, Wang J Z 2019 ACS Energy Lett. 4 2913 Google Scholar
[59]	Gharibzadeh S, Abdollahi Nejand B, Jakoby M, et al. 2019 Adv. Energy Mater. 9 1803699 Google Scholar
[60]	Wang P Y, Zhang X W, Zhou Y Q, Jiang Q, Ye Q F, Chu Z M, Li X X, Yang X L, Yin Z G, You J B 2018 Nat. Commun. 9 2225 Google Scholar
[61]	Zhang J, Bai D L, Jin Z W, Bian H, Wang K, Sun J, Wang Q, Liu S Z F 2018 Adv. Energy Mater. 8 1703246 Google Scholar
[62]	Wang Y, Dar M I, Ono L K, Zhang T Y, Kan M, Li Y W, Zhang L J, Wang X T, Yang Y G, Gao X Y, Qi Y B, Grätzel M, Zhao Y X 2019 Science 365 591 Google Scholar
[63]	Ye Q F, Zhao Y, Mu S Q, Ma F, Gao F, Chu Z M, Yin Z G, Gao P Q, Zhang X W, You J B 2019 Adv. Mater. 1 1905143 Google Scholar
[64]	Xiao Q, Tian J J, Xue Q F, Wang J, Xiong B J, Han M M, Li Z, Zhu Z L, Yip H L, Li Z 2019 Angew. Chem. Int. Ed. 58 17724 Google Scholar
[65]	Green M A, Ho-Baillie A, Snaith H J 2014 Nat. Photonics 8 506 Google Scholar
[66]	Kim H S, Im S H, Park N G 2014 J. Phys.Chem. C 118 5615 Google Scholar
[67]	Li Z, Yang M J, Park J S, Wei S H, Berry J, Zhu K 2015 Chem. Mater. 28 284 Google Scholar
[68]	Chang Y H, Park C H 2004 J. Korean Phys. Soc. 44 889
[69]	Anaya M, Correabaena J P, Lozano G L, Saliba M, Anguita P, Roose B, Abate A, Steiner U, Grätzel M, Calvo M 2016 J. Mater. Chem. A 4 11214 Google Scholar
[70]	Noh J H, Im S H, Heo J H, Mandal T N, Seok S I 2013 Nano Lett. 13 1764 Google Scholar
[71]	Eperon G E, Stranks S D, Menelaou C, Johnston M B, Herz L M, Snaith H J 2014 Energy Environ. Sci. 7 982 Google Scholar
[72]	Saliba M, Correa-Baena J P, Grätzel M, Hagfeldt A, Abate A 2017 Angew. Chem. Int. Ed. 57 2554 Google Scholar
[73]	Unger E L, Bowring A R, Tassone C J, Pool V L, Gold-Parker A, Cheacharoen R, Stone K H, Hoke E T, Toney M F, McGehee M D 2014 Chem. Mater. 26 7158 Google Scholar
[74]	Dong Q, Yuan Y B, Shao Y C, Fang Y J, Wang Q, Huang J S 2015 Energy Environ. Sci. 8 2464 Google Scholar
[75]	Lee B, Hwang T, Lee S, Shin B, Park B 2019 Sci. Rep. 9 4803 Google Scholar
[76]	Zhang C P, Li Z P, Liu J, Xin Y C, Shao Z P, Cui G, Pang S P 2018 ACS Energy Lett. 3 1801 Google Scholar
[77]	Ma T, Wang S W, Zhang Y W, Zhang K X, Yi L X 2020 J. Mater. Sci. 55 464 Google Scholar
[78]	Tong G, Ono L K, Qi Y B 2019 Energy Technol. 8 1900961 Google Scholar
[79]	Protesescu L, Yakunin S, Bodnarchuk M I, et al. 2015 Nano Lett. 15 3692 Google Scholar
[80]	Mehrabian M, Dalir S, Mahmoudi G, Miroslaw B, Safin D A 2019 Eur. J. Inorg. Chem. 2019 3699 Google Scholar
[81]	Leijtens T, Bush K A, Prasanna R, McGehee M D 2018 Nat. Energy 3 828 Google Scholar
[82]	Mahesh S, Ball J M, Oliver R D J, McMeekin D P, Nayak P K, Johnston M B, Snaith H J 2020 Energy Environ. Sci. 13 258 Google Scholar
[83]	Levine I, Vera O G, Kulbak M, Ceratti D-R, Rehermann C, Márquez J A, Levcenko S, Unold T, Hodes G, Balberg I, Cahen D, Dittrich T 2019 ACS Energy Lett. 4 1150 Google Scholar
[84]	Song Z, Chen C, Li C, Awni R A, Zhao D, Yan Y 2019 Semicond. Sci. Technol. 34 093001 Google Scholar
[85]	Hoke E T, Slotcavage D J, Dohner E R, Bowring A R, Karunadasa H I, McGehee M D 2015 Chem. Sci. 6 613 Google Scholar
[86]	Slotcavage D J, Karunadasa H I, McGehee M D 2016 ACS Energy Lett. 1 1199 Google Scholar
[87]	Yun J S, Seidel J, Kim J, Soufiani A M, Huang S, Lau J, Jeon N J, Seok S I, Green M A, Ho-Baillie A 2016 Adv. Energy Mater. 6 1600330 Google Scholar
[88]	Beal R E, Hagström N Z, Barrier J, Gold-Parker A, Prasanna R, Bush K A, Passarello D, Schelhas L T, Brüning K, Tassone C J, Steinrück H G, McGehee M D, Toney M F, Nogueira A F 2020 Matter 2 207 Google Scholar
[89]	Bischak C G, Hetherington C L, Wu H, Aloni S, Ogletree D F, Limmer D T, Ginsberg N S 2017 Nano Lett. 17 1028 Google Scholar
[90]	Brennan M C, Draguta S, Kamat P V, Kuno M 2017 ACS Energy Lett. 3 204 Google Scholar
[91]	Liu S, Guan Y J, Sheng Y S, Hu Y, Rong Y G, Mei A Y, Han H W 2020 Adv. Energy Mater. 10 1902492 Google Scholar
[92]	Gao F, Zhao Y, Zhang X W, You J B 2020 Adv. Energy Mater. 10 1902650 Google Scholar
[93]	Han J H, Luo S P, Yin X W, Zhou Y, Nan H, Li J B, Li X, Oron D, Shen H P, Lin H 2018 Small 14 1801016 Google Scholar
[94]	Bai S, Da P M, Li C, Wang Z P, Yuan Z C, Fu F, Kawecki M, Liu X J, Sakai N, Wang J T W, Huettner S, Buecheler S, Fahlman M, Gao F, Snaith H J 2019 Nature 571 245 Google Scholar
[95]	Bi D Q, Yi C Y, Luo J S, Décoppet J D, Zhang F, Zakeeruddin Shaik M, Li X, Hagfeldt A, Grätzel M 2016 Nat. Energy 1 16142 Google Scholar
[96]	Noel N K, Abate A, Stranks S D, Parrott E S, Burlakov V M, Goriely A, Snaith H J 2014 ACS Nano 8 9815 Google Scholar
[97]	Correa-Baena J B, Luo Y Q, Brenner T M, Snaider J, Sun S J, Li X Y, Jensen M A, Hartono N P T, Nienhaus L, Wieghold S, Poindexter J R, Wang S, Meng Y S, Wang T, Lai B, Holt M V, Cai Z H, Bawendi M G, Huang L B, Buonassisi T, Fenning D P 2019 Science 363 627 Google Scholar
[98]	Kieslich G, Sun S, Cheetham A K 2014 Chem. Sci. 12 4712 Google Scholar
[99]	Kubicki D, Prochowicz D, Hofstetter A, Saski M, Yadav P, Bi D, Pellet N, Lewiński J, Zakeeruddin S M, Grätzel M 2018 J. Mater. Chem. A 140 3345 Google Scholar
[100]	Jodlowski A D, Roldán-Carmona C, Grancini G, Salado M, Ralaiarisoa M, Ahmad S, Koch N, Camacho L, de Miguel G, Nazeeruddin M K 2017 Nat. Energy 2 972 Google Scholar
[101]	Chen H, Wei Q, Saidaminov M I, Wang F, Johnston A, Hou Y, Peng Z J, Xu K M, Zhou W J, Liu Z H, Qiao L, Wang X, Xu S W, Li J Y, Long R, Ke Y Q, Sargent E H, Ning Z J 2019 Adv. Mater. 31 e1903559 Google Scholar
[102]	Stoddard R J, Rajagopal A, Palmer R L, Braly I L, Jen A K Y, Hillhouse H W 2018 ACS Energy Lett. 3 1261 Google Scholar
[103]	Yu H, Wang F, Xie F Y, Li W W, Chen J, Zhao N 2014 Adv. Funct. Mater. 24 7102 Google Scholar
[104]	Chae J S, Dong Q F, Huang J S, Centrone A 2015 Nano Lett. 15 8114 Google Scholar
[105]	Gao C, Liu J, Liao C, Ye Q Y, Zhang Y Z, He X L, Guo X W, Mei J, Lau W 2015 RSC Adv. 5 26175 Google Scholar
[106]	Xie Y L, Yu H Y, Duan J S, Xu L, Hu B 2020 ACS Appl. Mater. Interfaces 12 11190 Google Scholar
[107]	Abate A, Saliba M, Hollman D J, Stranks S D, Wojciechowski K, Avolio R, Grancini G, Petrozza A, Snaith H J 2014 Nano Lett. 14 3247 Google Scholar
[108]	Heo D Y, Lee T H, Iwan A, Kavan L, Omatova M, Majkova E, Kamarás K, Jang H W, Kim S Y 2020 J. Power Sources 458 228067 Google Scholar
[109]	Tong J H, Song Z N, Kim D H, et al. 2019 Science 364 475 Google Scholar
[110]	Tang G, Yang C, Stroppa A, Fang D N, Hong J W 2017 J. Chem. Phys. 146 224702 Google Scholar
[111]	Ke W J, Xiao C X, Wang C L, et al. 2016 Adv. Mater. 28 5214 Google Scholar
[112]	Xu J X, Buin A, Ip A H, et al. 2015 Nat. Commun. 6 7081 Google Scholar
[113]	Liang P W, Chueh C C, Williams S T, Jen A K Y 2015 Adv. Energy Mater. 5 1402321 Google Scholar
[114]	Gatti T, Menna E, Meneghetti M, Maggini M, Petrozza A, Lamberti F 2017 Nano Energy 41 84 Google Scholar
[115]	Fang Y J, Bi C, Wang D, Huang J S 2017 ACS Energy Lett. 2 782 Google Scholar
[116]	Cui C H, Li Y W, Li Y F 2017 Adv. Energy Mater. 7 1601251 Google Scholar
[117]	Lee J W, Park N G 2019 Adv. Energy Mater. 10 1903249 Google Scholar
[118]	Lee J W, Kim H S, Park N G 2016 Acc. Chem. Res. 49 311 Google Scholar
[119]	Xue D J, Hou Y, Liu S C, Wei M, Chen B, Huang Z, Li Z, Sun B, Proppe A H, Dong Y, Saidaminov M I, Kelley S O, Hu J S, Sargent E H 2020 Nat. Commun. 11 1514 Google Scholar
[120]	Jan S, Robby P, Rolf B 2018 Sol. Energy Mater. Sol. Cells 187 39 Google Scholar
[121]	Luo D Y, Yang W Q, Wang Z P, et al. 2018 Science 360 1442 Google Scholar
[122]	Bu X N, Westbrook R J E, Lanzetta L, Ding D, Chotchuangchutchaval T, Aristidou N, Haque S A 2019 Sol. RRL 3 1800282 Google Scholar
[123]	Wang Q, Zheng X P, Deng Y H, Zhao J J, Chen Z L, Huang J S 2017 Joule 1 371 Google Scholar
[124]	Zheng X P, Chen B, Dai J, Fang Y J, Bai Y, Lin Y Z, Wei H T, Zeng X C, Huang J S 2017 Nat. Energy 2 17102 Google Scholar
[125]	Elgamel H E, Barnett A M, Rohatgi A, Chen Z, Vinckier C, Nijs J, Mertens R 1995 J. Appl. Phys. 78 3457 Google Scholar
[126]	Jaysankar M, Raul B A L, Bastos J, Burgess C, Weijtens C, Creatore M, Aernouts T, Kuang Y, Gehlhaar R, Hadipour A, Poortmans J 2018 ACS Energy Lett. 4 259 Google Scholar
[127]	Stolterfoht M, Caprioglio P, Wolff C M, et al. 2019 Energy Environ. Sci. 12 2778 Google Scholar
[128]	Bian H, Bai D L, Jin Z W, Wang K, Liang L, Wang H R, Zhang J R, Wang Q, Liu S Z F 2018 Joule 2 1500 Google Scholar
[129]	Zeng Q, Liu L, Xiao Z, Liu F Y, Hua Y, Yuan Y B, Ding L M 2019 Sci. Bull. 64 885 Google Scholar
[130]	Zhao D W, Ding L M 2020 Sci. Bull. 65 1144 Google Scholar
[131]	Zhao D W, Chen C, Wang C L, Junda M M, Song Z N, Grice C R, Yu Y, Li C W, Subedi B, Podraza N J, Zhao X Z, Fang G J, Xiong R G, Zhu K, Yan Y F 2018 Nat. Energy 3 1093 Google Scholar
[132]	Shen H P, Omelchenko S T, Jacobs D A, et al. 2018 Sci. Adv. 4 eaau9711 Google Scholar
[133]	Hou F H, Yan L L, Shi B, et al. 2019 ACS Appl. Energy Mater. 2 243 Google Scholar
[134]	Werner J, Weng C H, Walter A, Fesquet L, Seif J P, De Wolf S, Niesen B, Ballif C 2016 J. Phys. Chem. Lett. 7 161 Google Scholar
[135]	Sahli F, Kamino B A, Werner J, et al. 2018 Adv. Energy Mater. 8 1701609 Google Scholar
[136]	Fan R D, Z N, Zhang L, Yang R, Meng Y, Li L W, Guo T, Chen Y H, Xu Z Q, Zheng G H J, Huang Y, Li L, Qin L, Qiu X H, Chen Q, Zhou H P 2017 Sol. RRL 1 1700149 Google Scholar
[137]	Qiu Z W, Xu Z Q, Li N X, Zhou N, Chen Y H, Wan X X, Liu J L, Li N, Hao X T, Bi P Q, Chen Q, Cao B Q, Zhou H P 2018 Nano Energy 53 798 Google Scholar
[138]	Zhu S J, Y X, Ren Q S, et al. 2018 Nano Energy 45 280 Google Scholar
[139]	Zhu S J, Hou F H, Huang W, et al. 2018 Sol. RRL 2 1800176 Google Scholar
[140]	Hou F H, Han C, Isabella O, et al. 2019 Nano Energy 56 234 Google Scholar
[141]	Bush K A, Palmstrom A F, Yu Z J, et al. 2017 Nat. Energy 2 17009 Google Scholar
[142]	Bush K A, Manzoor S, Frohna K, Yu Z J, Raiford J A, Palmstrom A F, Wang H-P, Prasanna R, Bent S F, Holman Z C, McGehee M D 2018 ACS Energy Lett. 3 2173 Google Scholar
[143]	Marko Jošt, Köhnen E, Morales-Vilches A B, Lipovšek B, Jäger K, Macco B, Al-Ashouri A, Krč J, Korte L, Rech B, Schlatmann R, Topič M, Stannowski B, Albrecht S 2018 Energy Environ. Sci. 11 3511 Google Scholar
[144]	Sahli F, Werner J, Kamino B A, et al. 2018 Nat. Mater. 17 820 Google Scholar
[145]	Nogay G, Sahli F, Werner J, Monnard R, Boccard M, Despeisse M, Haug F J, Jeangros Q, Ingenito A, Ballif C 2019 ACS Energy Lett. 4 844 Google Scholar
[146]	Mazzarella L, Lin Y H, Kirner S, Morales-Vilches A B, Korte L, Albrecht S, Crossland E, Stannowski B, Case C, Snaith H J, Schlatmann R 2019 Adv. Energy Mater. 9 1803241 Google Scholar
[147]	Chen B, Yu Z J, Manzoor S, Wang S, Weigand W, Yu Z H, Yang G, Ni Z Y, Dai X Z, Holman Z C, Huang J S 2020 Joule 4 850 Google Scholar
[148]	Berhe T A, Su W N, Chen C H, Pan C J, Cheng J H, Chen H M, Tsai M C, Chen L Y, Dubale A A, Hwang B J 2016 Energy Environ. Sci. 9 323 Google Scholar
[149]	Li Z, Xiao C X, Yang Y, et al. 2017 Energy Environ. Sci. 10 1234 Google Scholar

[1]	Wang Jing, Gao Shan, Duan Xiang-Mei, Yin Wan-Jian. Influence of defect in perovskite solar cell materials on device performance and stability. Acta Physica Sinica, 2024, 73(6): 063101. doi: 10.7498/aps.73.20231631
[2]	Xu Chang, Zheng Dexu, Dong Xinrui, Wu SaJian, Wu MingXing, Wang Kai, Liu Shengzhong(Frank). Research progress of perovskite-based triple-junction tandem solar cells. Acta Physica Sinica, 2024, 73(24): . doi: 10.7498/aps.73.20241187
[3]	Yang Jing, Han Xiao-Jing, Liu Dong-Xue, Shi Biao, Wang Peng-Yang, Xu Sheng-Zhi, Zhao Ying, Zhang Xiao-Dan. Preparation of wide-bandgap perovskite thin films by propylamine hydrochloride assisted gas quenching method. Acta Physica Sinica, 2024, 73(15): 158401. doi: 10.7498/aps.73.20240561
[4]	Wang Yue, Shao Bo-Huai, Chen Shuang-Long, Wang Chun-Jie, Gao Chun-Xiao. Effects of defects on electrical transport properties of anatase TiO₂ polycrystalline under high pressure: AC impedance measurement. Acta Physica Sinica, 2023, 72(12): 126401. doi: 10.7498/aps.72.20230020
[5]	Zhang Mei-Rong, Zhu Zeng-Wei, Yang Xiao-Qin, Yu Tong-Xu, Yu Xiao-Qi, Lu Di, Li Shun-Feng, Zhou Da-Yong, Yang Hui. Research progress of perovskite/crystalline silicon tandem solar cells with efficiency of over 30%. Acta Physica Sinica, 2023, 72(5): 058801. doi: 10.7498/aps.72.20222019
[6]	Cao Zhen, Hao Da-Peng, Tang Gang, Xun Zhi-Peng, Xia Hui. Influence of cluster shaped defects on fracture process of fiber bundle. Acta Physica Sinica, 2021, 70(20): 204602. doi: 10.7498/aps.70.20210310
[7]	Yin Yuan, Li Ling, Yin Wan-Jian. Theoretical and computational study on defects of solar cell materials. Acta Physica Sinica, 2020, 69(17): 177101. doi: 10.7498/aps.69.20200656
[8]	Wu Bu-Jun, Lin Dong-Xu, Li Zheng, Cheng Zhen-Ping, Li Xin, Chen Ke, Shi Ting-Ting, Xie Wei-Guang, Liu Peng-Yi. Optimization of grain size to achieve high-performance perovskite solar cells in vapor deposition. Acta Physica Sinica, 2019, 68(7): 078801. doi: 10.7498/aps.68.20182221
[9]	Liu Hao-Hua, Wang Shao-Hua, Li Bo-Bo, Li Hua-Lin. Defect induced asymmetric soliton transmission in the nonlinear circuit. Acta Physica Sinica, 2017, 66(10): 100502. doi: 10.7498/aps.66.100502
[10]	Zhang Xiu-Zhi, Wang Kai-Yue, Li Zhi-Hong, Zhu Yu-Mei, Tian Yu-Ming, Chai Yue-Sheng. Effect of nitrogen on the defect luminescence in diamond. Acta Physica Sinica, 2015, 64(24): 247802. doi: 10.7498/aps.64.247802
[11]	Zhang Ming-Lan, Yang Rui-Xia, Li Zhuo-Xin, Cao Xing-Zhong, Wang Bao-Yi, Wang Xiao-Hui. Study on proton irradiation induced defects in GaN thick film. Acta Physica Sinica, 2013, 62(11): 117103. doi: 10.7498/aps.62.117103
[12]	Wang Xin-Hua, Pang Lei, Chen Xiao-Juan, Yuan Ting-Ting, Luo Wei-Jun, Zheng Ying-Kui, Wei Ke, Liu Xin-Yu. Investigation on trap by the gate fringecapacitance in GaN HEMT. Acta Physica Sinica, 2011, 60(9): 097101. doi: 10.7498/aps.60.097101
[13]	Ning Li-Zhong, Qi Xin, Yu Li, Zhou Yang. Defect structures of Rayleigh-Benard travelling wave convection in binary fluid mixtures. Acta Physica Sinica, 2009, 58(4): 2528-2534. doi: 10.7498/aps.58.2528
[14]	Zhang Kai-Wang, Zhong Jian-Xin. Influence of defects on the melting and premelting of carbon nanotubes. Acta Physica Sinica, 2008, 57(6): 3679-3683. doi: 10.7498/aps.57.3679
[15]	Xia Zhi-Lin, Shao Jian-Da, Fan Zheng-Xiu. Effect of bulk inclusion in films on damage probability. Acta Physica Sinica, 2007, 56(1): 400-406. doi: 10.7498/aps.56.400
[16]	Chen Zhi-Quan, Kawasuso Atsuo. Vacancy-type defects induced by He-implantation in ZnO studied by a slow positron beam. Acta Physica Sinica, 2006, 55(8): 4353-4357. doi: 10.7498/aps.55.4353
[17]	Sun Xian-Kai, Lin Bi-Xia, Zhu Jun-Jie, Zhang Yang, Fu Zhu-Xi. Studies on the strain and its effect on defects in heteroepitaxial ZnO films prepared by LP-OCVD method. Acta Physica Sinica, 2005, 54(6): 2899-2903. doi: 10.7498/aps.54.2899
[18]	Chen Ming-Bo, Cui Rong-Qiang, Wang Liang-Xing, Zhang Zhong-Wei, Lu Jian-Feng, Chi Wei-Ying. p-n GaInP2/GaAs tandem solar cells. Acta Physica Sinica, 2004, 53(11): 3632-3636. doi: 10.7498/aps.53.3632*
[19]	Li Peng-Fei, Yan Xiao-Hong, Wang Ru-Zhi. . Acta Physica Sinica, 2002, 51(9): 2139-2143. doi: 10.7498/aps.51.2139
[20]	TANG XUE-FENG, GU MU, TONG HONG-YONG, LIANG LING, YAO MING-ZHEN, CHEN LING-YAN, LIAO JING-YING, SHEN BIN-FU, QU XIANG-DONG, YIN ZHI-WEN, XU WEI-XIN, WANG JING-C HENG. A STUDY ON La-DOPED PbWO4 SCINTILLATING CRYSTAL. Acta Physica Sinica, 2000, 49(10): 2007-2010. doi: 10.7498/aps.49.2007

Catalog

Vol. 69, Issue 20 - 2020-10-20

Metrics

Abstract views: 28094
PDF Downloads: 1226
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板