尺寸依赖的CoCrFeNiMn晶体/非晶双相高熵合金塑性变形机制的分子动力学模拟

安敏荣; 李思澜; 宿梦嘉; 邓琼; 宋海洋

doi:10.7498/aps.71.20221368

摘要

晶体/非晶双相高熵合金是近年来研究人员提出的获得高强高韧高熵合金的有效策略, 其塑性变形机制和组成相的尺寸密切相关. 本文采用分子动力学模拟方法研究了组成相尺寸对CoCrFeNiMn晶体/非晶双相高熵合金塑性变形机制的影响. 研究表明, 非晶相尺寸对双相高熵合金的力学行为和塑性变形机制有显著影响. 对于非晶相厚度较小的样品, 塑性变形是位错滑移和面心立方向六方密排结构的相变主导的, 尤其是在非晶厚度为1 nm的样品中观察到了孪晶和位错锁; 非晶相厚度适中时, 双相高熵合金主要通过晶体相中位错滑移、面心立方向六方密排结构的相变和非晶相的剪切带增殖来实现塑性变形; 非晶相厚度较大时, 双相高熵合金的塑性变形则由非晶相中均匀剪切带的形成主导. 此外, 非晶相厚度的增加对位错的形核和发射有延迟作用, 并且, 晶体/非晶双相结构中的非晶相有稳定晶粒的作用. 本文的研究结果对于设计和制备高性能的高熵合金具有一定的科学价值和指导意义.

关键词:

Abstract

Recently proposed crystalline/amorphous dual-phase high-entropy alloy is an effective strategy to obtain high-entropy, high-strength and high-toughness alloys. And the relative plastic deformation mechanism is dependent on the size of component phases. The effect of component phase size on the plastic deformation mechanism of CoCrFeNiMn crystalline/amorphous dual-phase high-entropy alloy is investigated by molecular dynamics simulation. The results indicate that the size of amorphous phase has a significant effect on the mechanical behavior and plastic deformation mechanism of high entropy alloy. For the sample with small thickness of amorphous phase, the plastic deformation is dominated by dislocation slip and phase transformation of face-centered-cubic structure to hexagonal-close-packed structure. Especially, the deformation twins and Lomer-Cottrell locks are observed in the sample with amorphous layer spacing of 1 nm. When the thickness of the amorphous layer is moderate, the plastic deformation of the dual-phase high-entropy alloy is realized mainly through the dislocation slip, phase transformation of face-centered-cubic structure to hexagonal-close-packed structure in crystalline part and shear band multiplication in amorphous part. If the amorphous layer spacing is larger, the plastic deformation of the high-entropy alloy is dominated by the formation of uniform shear bands in the amorphous phase. In addition, the amorphous phase in the dual-phase high-entropy alloy structure can stabilize the crystalline grains. The results of this study can provide a guidance for designing and preparing high entropy alloy with high performance.

Keywords:

crystalline/amorphous dual-phase high entropy alloy /
size effect /
deformation mechanism /
molecular dynamics simulation

作者及机构信息

1.
西安石油大学新能源学院, 西安　710065

2.
西安石油大学材料科学与工程学院, 西安　710065

3.
西北工业大学航空学院, 西安　710072

通信作者: 邓琼, dengqiong24@nwpu.edu.cn ; 宋海洋, hysong@xsyu.edu.cn

基金项目: 国家自然科学基金(批准号: 12072286)和陕西省自然科学基金 (批准号: 2021JZ-53)资助的课题.

Authors and contacts

1.
College of New Energy, Xi’an Shiyou University, Xi’an 710065, China

2.
College of Materials Science and Engineering, Xi’an Shiyou University, Xi’an 710065, China

3.
School of Aeronautics, Northwestern Polytechnical University, Xi’an 710072, China

Corresponding author: Deng Qiong, dengqiong24@nwpu.edu.cn ; Song Hai-Yang, hysong@xsyu.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 12072286) and the Natural Science Foundation of Shanxi Province, China (Grant No. 2021JZ-53).

文章全文 : translate this paragraph

参考文献

[1]	Yeh J W, Chen S K, Lin S J, Gan J Y, Chin T S, Shun T T, Tsau C H, Chang S Y 2004 Adv. Eng. Mater. 6 299 Google Scholar
[2]	王浩玉, 农智升, 王继杰, 朱景川 2019 68 036101 Google Scholar Wang H Y, Nong Z S, Wang J J, Zhu J C 2019 Acta Phys. Sin. 68 036101 Google Scholar
[3]	George E P, Raabe D, Ritchie R O 2019 Nat. Rev. Mater. 4 515 Google Scholar
[4]	Zhang W, Ma Z, Li C, Guo C, Liu D, Zhao H, Ren L 2022 J. Mater. Sci. Technol. 114 102 Google Scholar
[5]	Zhang X, Divinski S V, Grabowski B 2022 Acta Mater. 227 117677 Google Scholar
[6]	张勇, 陈明彪, 杨潇 2020 先进高熵合金技术 (北京: 化学工业出版社) 第76—123页 Zhang Y, Chen M B, Yang X 2020 Advanced High Entropy Alloy Technology (Beijing: Chemical Industry Press) pp76–123 (in Chinese)
[7]	李建国, 黄瑞瑞, 张倩, 李晓雁 2020 力学学报 52 42 Google Scholar Li J G, Huang R R, Zhang Q, Li X Y 2020 Chin. J. Theor. App. Mech. 52 42 Google Scholar
[8]	Ye Y F, Wang Q, Lu J, Liu C T, Yang Y 2016 Mater. Today 19 349 Google Scholar
[9]	黄文军, 乔珺威, 陈顺华, 王雪姣, 吴玉程 2021 70 106201 Google Scholar Huang W J, Qiao J W, Chen S H, Wang X J, Wu Y C 2021 Acta Phys. Sin. 70 106201 Google Scholar
[10]	Wu G, Balachandran S, Gault B, Xia W, Liu C, Rao Z, We Y, Liu S, Lu J, Herbig M, Lu W, Dehm G, Li Z, Raabe D 2020 Adv. Mater. 32 2002619 Google Scholar
[11]	Gludovatz B, Hohenwarter A, Catoor D, Chang E H, George E P, Ritchie R O 2014 Science 345 1153 Google Scholar
[12]	Huang H L, Wu Y, He J Y, Wang H, Liu X, An K, Wu W, Lu Z 2017 Adv. Mater. 29 1701678 Google Scholar
[13]	Chen L B, Wei R, Tang K, Zhang J, Jiang F, He L, Sun J 2018 Mater. Sci. Eng., A 716 150 Google Scholar
[14]	Yasuda H Y, Miyamoto H, Cho K, Nagase T 2017 Mater. Lett. 199 120 Google Scholar
[15]	Lei Z, Liu X, Wu Y, Wang H, Jiang S, Wang S, Hui X, Wu Y, Gault B, Kontis P, Raabe D, Gu L, Zhang Q, Chen H, Wang H, Liu J, An K, Zeng Q, Nieh T, Lu Z 2018 Nature 563 546 Google Scholar
[16]	Sha Z D, Teng Y, Poh L H, Pei Q X, Xing G C, Gao H J 2019 Acta Mater. 169 147 Google Scholar
[17]	Qiao J C, Wang Q, Pelletier J M, Kato H, Casalini R, Crespo D, Pineda E, Yao Y, Yang Y 2019 Prog. Mater. Sci. 104 250 Google Scholar
[18]	汪卫华 2013 物理学进展 33 177 Wang W H 2013 Prog. Phys. 33 177
[19]	吴渊, 宋温丽, 周捷, 曹迪, 王辉, 刘雄军, 吕昭平 2017 66 176111 Google Scholar Wu Y, Song W L, Zhou J, Cao D, Wang H, Liu X J, Lü Z P 2017 Acta Phys. Sin. 66 176111 Google Scholar
[20]	Wang Y, Li J, Hamza A V, Barbee T W 2007 Proc. Natl. Acad. Sci. U. S. A. 104 11155 Google Scholar
[21]	Xiao L L, Zheng Z Q, Guo S W, Huang P, Wang F 2020 Mater. Des. 194 108895 Google Scholar
[22]	Xiao L, Zheng Z, Huang P, Wang F 2022 Scr. Mater. 210 114454 Google Scholar
[23]	Jiang L, Bai Z T, Powers M, Fan Y, Zhang W, George E P, Misra A 2022 Mater. Sci. Eng., A 848 143144 Google Scholar
[24]	Li J, Chen H, Feng H, Fang Q, Liu Y, Liu F, Wu H, Liaw P K 2020 J. Mater. Sci. Technol. 54 14 Google Scholar
[25]	Zhou X Y, Wu H H, Zhu J H, Li B, Wu Y 2021 Compos. Commun. 24 100658 Google Scholar
[26]	吕昭平, 雷智锋, 黄海龙, 刘少飞, 张凡, 段大波, 曹培培, 吴渊, 刘雄军, 王辉 2018 金属学报 54 1553 Google Scholar Lü Z P, Lei Z F, Huang H L, Liu S F, Zhang F, Duan D B, Cao P P, Wu Y, Liu X J, Wang H 2018 Acta Metall. Sin. 54 1553 Google Scholar
[27]	陈晶晶, 邱小林, 李柯, 周丹, 袁军军 2022 71 199601 Google Scholar Chen J J, Qiu X L, Li K, Zhou D, Yuan J J 2022 Acta Phys. Sin. 71 199601 Google Scholar
[28]	申天展, 宋海洋, 安敏荣 2021 70 186201 Google Scholar Shen T Z, Song H Y, An M R 2021 Acta Phys. Sin. 70 186201 Google Scholar
[29]	Plimpton S 1995 J. Comput. Phys. 117 1 Google Scholar
[30]	Cao A J, Wei Y G 2007 J. Appl. Phys. 102 083511 Google Scholar
[31]	Yamakov V, Wolf D, Salazar M, Phillpot S R, Gleiter H 2001 Acta Mater. 49 2713 Google Scholar
[32]	Su M J, Deng Q, An M R, Liu L T, Chen L Y 2021 J. Alloys Compd. 868 159282 Google Scholar
[33]	Choi W M, Jo Y H, Sohn S S, Lee S, Lee B J 2018 NPJ Comput. Mater. 4 1 Google Scholar
[34]	Stukowski A 2010 Modell. Simul. Mater. Sci. Eng. 18 015012 Google Scholar
[35]	Faken D, Jónsson H 1994 Comput. Mater. Sci. 2 279 Google Scholar
[36]	Li J, Fang Q H, Liu B, Liu Y 2018 Acta Mater. 147 35 Google Scholar
[37]	Sha Z D, Wong W H, Pei Q X, Branicio P S, Liu Z S, Wang T J, Guo T F, Gao H J 2017 J. Mech. Phys. Solids 104 84 Google Scholar
[38]	Song H Y, Li S, An M R, Deng Q, Li Y L 2018 Comput. Mater. Sci. 150 42 Google Scholar
[39]	Qi Y M, Zhao M, Feng M L 2021 J. Alloys Compd. 851 156923 Google Scholar
[40]	Fang Q H, Chen Y, Li J, Jiang C, Liu B, Liu Y, Liaw P K 2019 Int. J. Plast. 114 161 Google Scholar
[41]	Xu X D, Liu P, Tang Z, Hirata A, Song S X, Nieh T G, Liaw P K, Liu C T, Chen M W 2018 Acta Mater. 144 107 Google Scholar
[42]	Jiang K, Ren T F, Shan G B, Ye T, Chen L Y, Wang C X, Zhao F, Li J G, Suo T 2020 Mater. Sci. Eng., A 797 140125 Google Scholar
[43]	Chowdhury P, Canadinc D, Sehitoglu H 2017 Mater. Sci. Eng. R:Rep. 122 1 Google Scholar

施引文献

图 1 CoCrFeNiMn晶体/非晶双相高熵合金模型　(a) 初始构型; (b) 经公共近邻分析得到的原子结构图

Fig. 1. Schematic of CoCrFeNiMn crystalline/amorphous dual-phase high-entropy alloy: (a) The initial configuration; (b) atomic configuration identified by the common neighbor analysis method.

下载: 全尺寸图片幻灯片

图 2 不同非晶相厚度的CoCrFeNiMn晶体/非晶双相高熵合金的拉伸力学性能　(a) 应力-应变曲线; (b) 杨氏模量; (c) 峰值应力和平均流动应力

Fig. 2. Tensile properties of dual-phase CoCrFeNiMn crystalline/amorphous high-entropy alloys with different amorphous layer spacing: (a) Stress-strain curves; (b) Young’s modulus; (c) peak stress and average flow stress.

下载: 全尺寸图片幻灯片

图 3 多晶CoCrFeNiMn高熵合金在不同拉伸应变时的原子结构演变图　(a) ε = 0.033; (b) ε = 0.045; (c) ε = 0.057; (d) ε = 0.089; (e) ε = 0.111; (f) ε = 0.200

Fig. 3. Atomic configuration evolutions of polycrystalline CoCrFeNiMn high-entropy alloy: (a) ε = 0.033; (b) ε = 0.045; (c) ε = 0.057; (d) ε = 0.089; (e) ε = 0.111; (f) ε = 0.200.

下载: 全尺寸图片幻灯片

图 4 不同非晶厚度的双相HEAs在不同拉伸应变时的原子结构演变图　(a) h = 1 nm; (b) h = 5 nm; (c) h = 11 nm. 图4(a1)中圆圈代表了位错发射点, 图4(a2)中圆圈代表孪晶, 图4(a3)中圆圈代表位错锁, 图4(b1)中圆圈代表剪切带的雏形

Fig. 4. Atomic configuration evolutions of the CoCrFeNiMn crystalline/amorphous dual-phase high-entropy alloys with different amorphous layer spacing: (a) h = 1 nm; (b) h = 5 nm; (c) h = 11 nm. The emission site of the dislocation, the deformation twin and the Lomer-Cottrell locks are depicted by the circles in Fig. 4(a1), Fig. 4(a2) and Fig. 4(a3), respectively. The circle in Fig. 4(b1) represents the embryo of the shear band.

下载: 全尺寸图片幻灯片

图 5 不同非晶厚度的双相HEAs在拉伸过程中的不同结构原子比例变化图, 其中(a) h = 1 nm, (b) h =5 nm, (c) h =11 nm; (d) FCC相转变为HCP相的原子分数

Fig. 5. Atomic fraction evolutions of different structures of the CoCrFeNiMn crystalline/amorphous dual-phase high-entropy alloys with different amorphous layer spacing: (a) h = 1 nm; (b) h = 5 nm; (c) h = 11 nm. (d) Atomic fraction evolution of FCC structure transformation to HCP structure with h = 1, 5 and 11 nm.

下载: 全尺寸图片幻灯片

图 6 不同非晶厚度的双相HEAs中剪切带的形成过程图　(a) h = 1 nm; (b) h = 5 nm; (c) h = 11 nm

Fig. 6. Formation process of the shear band in CoCrFeNiMn crystalline/amorphous dual-phase high-entropy alloys with different amorphous layer spacing: (a) h = 1 nm; (b) h = 5 nm; (c) h = 11 nm.

下载: 全尺寸图片幻灯片

图 7 晶体相中的变形机理细节图　(a) 形变孪晶细节图; (b) 图4(a3)中Lomer-Cottrell位错锁的放大图; (c) 实验中观察到的Shockley 部分位错相互作用形成Lomer-Cottrell位错锁^[42]

Fig. 7. Details of the plastic deformation mechanism in crystalline structure: (a) Detail of the deformation twins; (b) zoomed up snapshot of the Lomer-Cottrell locks of Fig. 4(a3); (c) the Lomer-Cottrell lock formed by the reaction of two Shockley partial dislocations in the experiment^[42].

下载: 全尺寸图片幻灯片

图 8 位错滑移辅助下的FCC-HCP转变机制图　(a) FCC结构示意图; (b) HCP结构示意图; (c) FCC→HCP相变示意图

Fig. 8. Schematic illustration of FCC-to-HCP transformation mechanism as assisted by dislocation glide: (a) Schematic illustration of FCC structure; (b) schematic illustration of HCP structure; (c) FCC-to-HCP transformation mechanism.

下载: 全尺寸图片幻灯片

map

[1]	Yeh J W, Chen S K, Lin S J, Gan J Y, Chin T S, Shun T T, Tsau C H, Chang S Y 2004 Adv. Eng. Mater. 6 299 Google Scholar
[2]	王浩玉, 农智升, 王继杰, 朱景川 2019 68 036101 Google Scholar Wang H Y, Nong Z S, Wang J J, Zhu J C 2019 Acta Phys. Sin. 68 036101 Google Scholar
[3]	George E P, Raabe D, Ritchie R O 2019 Nat. Rev. Mater. 4 515 Google Scholar
[4]	Zhang W, Ma Z, Li C, Guo C, Liu D, Zhao H, Ren L 2022 J. Mater. Sci. Technol. 114 102 Google Scholar
[5]	Zhang X, Divinski S V, Grabowski B 2022 Acta Mater. 227 117677 Google Scholar
[6]	张勇, 陈明彪, 杨潇 2020 先进高熵合金技术 (北京: 化学工业出版社) 第76—123页 Zhang Y, Chen M B, Yang X 2020 Advanced High Entropy Alloy Technology (Beijing: Chemical Industry Press) pp76–123 (in Chinese)
[7]	李建国, 黄瑞瑞, 张倩, 李晓雁 2020 力学学报 52 42 Google Scholar Li J G, Huang R R, Zhang Q, Li X Y 2020 Chin. J. Theor. App. Mech. 52 42 Google Scholar
[8]	Ye Y F, Wang Q, Lu J, Liu C T, Yang Y 2016 Mater. Today 19 349 Google Scholar
[9]	黄文军, 乔珺威, 陈顺华, 王雪姣, 吴玉程 2021 70 106201 Google Scholar Huang W J, Qiao J W, Chen S H, Wang X J, Wu Y C 2021 Acta Phys. Sin. 70 106201 Google Scholar
[10]	Wu G, Balachandran S, Gault B, Xia W, Liu C, Rao Z, We Y, Liu S, Lu J, Herbig M, Lu W, Dehm G, Li Z, Raabe D 2020 Adv. Mater. 32 2002619 Google Scholar
[11]	Gludovatz B, Hohenwarter A, Catoor D, Chang E H, George E P, Ritchie R O 2014 Science 345 1153 Google Scholar
[12]	Huang H L, Wu Y, He J Y, Wang H, Liu X, An K, Wu W, Lu Z 2017 Adv. Mater. 29 1701678 Google Scholar
[13]	Chen L B, Wei R, Tang K, Zhang J, Jiang F, He L, Sun J 2018 Mater. Sci. Eng., A 716 150 Google Scholar
[14]	Yasuda H Y, Miyamoto H, Cho K, Nagase T 2017 Mater. Lett. 199 120 Google Scholar
[15]	Lei Z, Liu X, Wu Y, Wang H, Jiang S, Wang S, Hui X, Wu Y, Gault B, Kontis P, Raabe D, Gu L, Zhang Q, Chen H, Wang H, Liu J, An K, Zeng Q, Nieh T, Lu Z 2018 Nature 563 546 Google Scholar
[16]	Sha Z D, Teng Y, Poh L H, Pei Q X, Xing G C, Gao H J 2019 Acta Mater. 169 147 Google Scholar
[17]	Qiao J C, Wang Q, Pelletier J M, Kato H, Casalini R, Crespo D, Pineda E, Yao Y, Yang Y 2019 Prog. Mater. Sci. 104 250 Google Scholar
[18]	汪卫华 2013 物理学进展 33 177 Wang W H 2013 Prog. Phys. 33 177
[19]	吴渊, 宋温丽, 周捷, 曹迪, 王辉, 刘雄军, 吕昭平 2017 66 176111 Google Scholar Wu Y, Song W L, Zhou J, Cao D, Wang H, Liu X J, Lü Z P 2017 Acta Phys. Sin. 66 176111 Google Scholar
[20]	Wang Y, Li J, Hamza A V, Barbee T W 2007 Proc. Natl. Acad. Sci. U. S. A. 104 11155 Google Scholar
[21]	Xiao L L, Zheng Z Q, Guo S W, Huang P, Wang F 2020 Mater. Des. 194 108895 Google Scholar
[22]	Xiao L, Zheng Z, Huang P, Wang F 2022 Scr. Mater. 210 114454 Google Scholar
[23]	Jiang L, Bai Z T, Powers M, Fan Y, Zhang W, George E P, Misra A 2022 Mater. Sci. Eng., A 848 143144 Google Scholar
[24]	Li J, Chen H, Feng H, Fang Q, Liu Y, Liu F, Wu H, Liaw P K 2020 J. Mater. Sci. Technol. 54 14 Google Scholar
[25]	Zhou X Y, Wu H H, Zhu J H, Li B, Wu Y 2021 Compos. Commun. 24 100658 Google Scholar
[26]	吕昭平, 雷智锋, 黄海龙, 刘少飞, 张凡, 段大波, 曹培培, 吴渊, 刘雄军, 王辉 2018 金属学报 54 1553 Google Scholar Lü Z P, Lei Z F, Huang H L, Liu S F, Zhang F, Duan D B, Cao P P, Wu Y, Liu X J, Wang H 2018 Acta Metall. Sin. 54 1553 Google Scholar
[27]	陈晶晶, 邱小林, 李柯, 周丹, 袁军军 2022 71 199601 Google Scholar Chen J J, Qiu X L, Li K, Zhou D, Yuan J J 2022 Acta Phys. Sin. 71 199601 Google Scholar
[28]	申天展, 宋海洋, 安敏荣 2021 70 186201 Google Scholar Shen T Z, Song H Y, An M R 2021 Acta Phys. Sin. 70 186201 Google Scholar
[29]	Plimpton S 1995 J. Comput. Phys. 117 1 Google Scholar
[30]	Cao A J, Wei Y G 2007 J. Appl. Phys. 102 083511 Google Scholar
[31]	Yamakov V, Wolf D, Salazar M, Phillpot S R, Gleiter H 2001 Acta Mater. 49 2713 Google Scholar
[32]	Su M J, Deng Q, An M R, Liu L T, Chen L Y 2021 J. Alloys Compd. 868 159282 Google Scholar
[33]	Choi W M, Jo Y H, Sohn S S, Lee S, Lee B J 2018 NPJ Comput. Mater. 4 1 Google Scholar
[34]	Stukowski A 2010 Modell. Simul. Mater. Sci. Eng. 18 015012 Google Scholar
[35]	Faken D, Jónsson H 1994 Comput. Mater. Sci. 2 279 Google Scholar
[36]	Li J, Fang Q H, Liu B, Liu Y 2018 Acta Mater. 147 35 Google Scholar
[37]	Sha Z D, Wong W H, Pei Q X, Branicio P S, Liu Z S, Wang T J, Guo T F, Gao H J 2017 J. Mech. Phys. Solids 104 84 Google Scholar
[38]	Song H Y, Li S, An M R, Deng Q, Li Y L 2018 Comput. Mater. Sci. 150 42 Google Scholar
[39]	Qi Y M, Zhao M, Feng M L 2021 J. Alloys Compd. 851 156923 Google Scholar
[40]	Fang Q H, Chen Y, Li J, Jiang C, Liu B, Liu Y, Liaw P K 2019 Int. J. Plast. 114 161 Google Scholar
[41]	Xu X D, Liu P, Tang Z, Hirata A, Song S X, Nieh T G, Liaw P K, Liu C T, Chen M W 2018 Acta Mater. 144 107 Google Scholar
[42]	Jiang K, Ren T F, Shan G B, Ye T, Chen L Y, Wang C X, Zhao F, Li J G, Suo T 2020 Mater. Sci. Eng., A 797 140125 Google Scholar
[43]	Chowdhury P, Canadinc D, Sehitoglu H 2017 Mater. Sci. Eng. R:Rep. 122 1 Google Scholar

[1]	袁用开, 陈茜, 高廷红, 梁永超, 谢泉, 田泽安, 郑权, 陆飞. GaAs晶体在不同应变下生长过程的分子动力学模拟. , 2023, 72(13): 136801. doi: 10.7498/aps.72.20221860
[2]	张博佳, 安敏荣, 胡腾, 韩腊. 镁中位错和非晶作用机制的分子动力学模拟. , 2022, 71(14): 143101. doi: 10.7498/aps.71.20212318
[3]	韦国翠, 田泽安. 不同尺寸Cu₆₄Zr₃₆纳米液滴的快速凝固过程分子动力学模拟. , 2021, 70(24): 246401. doi: 10.7498/aps.70.20211235
[4]	申天展, 宋海洋, 安敏荣. 孪晶界对Cr₂₆Mn₂₀Fe₂₀Co₂₀Ni₁₄高熵合金力学行为影响的分子动力学模拟. , 2021, 70(18): 186201. doi: 10.7498/aps.70.20210324
[5]	韦昭召, 马骁, 柯常波, 张新平. Fe合金FCC-BCC原子尺度台阶型马氏体相界面迁移行为的分子动力学模拟研究. , 2020, 69(13): 136102. doi: 10.7498/aps.69.20191903
[6]	周边, 杨亮. 分子动力学模拟冷却速率对非晶合金结构与变形行为的影响. , 2020, 69(11): 116101. doi: 10.7498/aps.69.20191781
[7]	李君, 刘立胜, 徐爽, 张金咏. 单轴压缩下Ti₃B₄的力学、电学性能及变形机制的第一性原理研究. , 2020, 69(4): 043102. doi: 10.7498/aps.69.20191194
[8]	覃业宏, 唐超, 张春小, 孟利军, 钟建新. 硅晶体表面石墨烯褶皱形貌的分子动力学模拟研究. , 2015, 64(1): 016804. doi: 10.7498/aps.64.016804
[9]	阳喜元, 全军. 金属纳米线弹性性能的尺寸效应及其内在机理的模拟研究. , 2015, 64(11): 116201. doi: 10.7498/aps.64.116201
[10]	齐玉, 曲昌荣, 王丽, 方腾. Fe50Cu50合金熔体相分离过程的分子动力学模拟. , 2014, 63(4): 046401. doi: 10.7498/aps.63.46401
[11]	谷卓, 班士良. 纤锌矿结构ZnO/MgxZn1-xO量子阱中带间光吸收的尺寸效应和三元混晶效应. , 2014, 63(10): 107301. doi: 10.7498/aps.63.107301
[12]	陈青, 孙民华. 分子动力学模拟尺寸对纳米Cu颗粒等温晶化过程的影响. , 2013, 62(3): 036101. doi: 10.7498/aps.62.036101
[13]	陈青, 王淑英, 孙民华. 纳米Cu颗粒等温晶化过程的分子动力学模拟研究. , 2012, 61(14): 146101. doi: 10.7498/aps.61.146101
[14]	刘永利, 赵星, 张宗宁, 张林, 王绍青, 叶恒强. TiAl/Ti3Al体系剪切变形的分子动力学研究. , 2009, 58(13): 246-S253. doi: 10.7498/aps.58.246
[15]	张然, 何军, 彭增辉, 宣丽. 向列相液晶nCB(4-n-alkyl-4′-cyanobiphenyls, n=5—8)的旋转黏度及其奇偶效应的分子动力学模拟. , 2009, 58(8): 5560-5566. doi: 10.7498/aps.58.5560
[16]	陈育祥, 谢国锋, 马颖, 周益春. BaTiO3晶体结构及弹性的分子动力学模拟. , 2009, 58(6): 4085-4089. doi: 10.7498/aps.58.4085
[17]	赵九洲, 刘俊, 赵毅, 胡壮麒. 压力对非晶铜形成影响的分子动力学模拟. , 2007, 56(1): 443-445. doi: 10.7498/aps.56.443
[18]	杨弘, 陈民. 深过冷液态Ni2TiAl合金热物理性质的分子动力学模拟. , 2006, 55(5): 2418-2421. doi: 10.7498/aps.55.2418
[19]	吴国强, 孔宪仁, 孙兆伟, 王亚辉. 氩晶体薄膜法向热导率的分子动力学模拟. , 2006, 55(1): 1-5. doi: 10.7498/aps.55.1
[20]	艾树涛, 蔡元贞. 与相变潜热有关的铁电-顺电相界动力学及其尺寸效应. , 2006, 55(7): 3721-3724. doi: 10.7498/aps.55.3721

计量

文章访问数: 5397
PDF下载量: 187
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板

尺寸依赖的CoCrFeNiMn晶体/非晶双相高熵合金塑性变形机制的分子动力学模拟