The self-assembly behavior of polymer/nanorods hybrid system under oscillation field

Wang Kang-Ying; Ma Cai-Yuan; Yu Hui-Min; Zhang Hai-Tao; Cen Jian-Yong; Wang Ying-Ying; Pan Jun-Xing; Zhang Jin-Jun

doi:10.7498/aps.72.20222207

Abstract

The self-assembly behavior of diblock copolymer/homopolymer/nanorods hybrid system under oscillation field is performed by using Cell Dynamics Scheme (CDS) and Brownian Dynamics (BD). The effects of the amplitude and frequency of the oscillation field on the formation and evolution of the mixture morphology are investigated systematically. It is found that the oscillation field plays an important role in the formation and transformation of the ordered structure. With the frequency increasing, the orientation of the lamellar structure transforms from parallel to the field direction to random angle and then to perpendicular to the field direction. Compared with the pure rod system, the addition of polymers has a combing effect. Under high amplitude and low frequency ($ {\rm{\omega }}\leqslant 0.01 $) of the oscillation field, the arrangement of nanorods transforms from vertical to horizontal. However, under high amplitude and high frequency ($ \omega > 0.01 $), the nanorods change from vertical/horizontal hybrid arrangement to vertical arrangement. The evolution of domain size and orientation angle of nanorods under oscillation field are further analysed. The results provide a new method and reference for fabricating and regulating the ordered structure of polymer nanocomposites.

Keywords:

Authors and contacts

School of Physics and Information Engineering, Shanxi Normal University, Taiyuan 030031, China

Corresponding author: Pan Jun-Xing, panjx@sxnu.edu.cn ; Zhang Jin-Jun, zhangjinjun@sxnu.edu.cn

Funds: Projects supported by the Applied Basic Research Plan of Shanxi Province, China (Grant Nos. 2021030212345, 20210302123337), the Graduate Education Innovation Program of Shanxi Province, China (Grant No. 2021Y489), and the National Undergraduate Innovation and Entrepreneurship Program (Grant No.20220297).

FullText HTML : translate this paragraph

References

[1]	Seul M, Andelman D 1995 Science 267 476 Google Scholar
[2]	Tanaka H 1993 Phys. Rev. Lett. 70 2770 Google Scholar
[3]	Marencic A P, Adamson D H, Chaikin P M, Register R A 2010 Phys. Rev. E 81 011503 Google Scholar
[4]	Wu S 2009 Phys. Rev. E 79 031803 Google Scholar
[5]	Croll A B, Shi A C, Dalnoki-Veress K 2009 Phys. Rev. E 80 051803 Google Scholar
[6]	Hosoi A E, Kogan D, Devereaux C E, Bernoff A J, Baker S M 2005 Phys. Rev. Lett. 95 037801 Google Scholar
[7]	Lopes W A 2002 Phys. Rev. E 65 031606 Google Scholar
[8]	Leibler L 1980 Macromolecules 13 1602 Google Scholar
[9]	Kletenik-Edelman O, Ploshnik E, Salant A, Shenhar R, Banin U, Rabani E 2008 Phys. Chem. C 112 4498 Google Scholar
[10]	Keblinski P, Kumar S K, Maritan A, Koplik J, Banavar J R 1996 Phys. Rev. Lett. 76 1106 Google Scholar
[11]	Harrison C, Adamson D H, Cheng Z, Sebastian J M, Sethuraman S, Huse D A, Chaikin P M 2000 Science 290 1558 Google Scholar
[12]	Matsuyama A, Evans R M L, Cates M E 2000 Phys. Rev. E 61 2977 Google Scholar
[13]	Yamaguchi D, Hashimoto T 2001 Macromolecules 34 6495 Google Scholar
[14]	Angelescu D E, Waller J H, Register R A, Chaikin P M 2005 Adv. Mater 17 1878 Google Scholar
[15]	Komura S, Kodama H 1997 Phys. Rev. E 55 1722 Google Scholar
[16]	Roan J R, Shakhnovich E I 1999 Phys. Rev. E 59 2109 Google Scholar
[17]	Ginzburg V V 2005 Macromolecules 38 2362 Google Scholar
[18]	He G, Ginzburg V V, Balazs A C 2006 J. Polym. Sci. B 44 2389 Google Scholar
[19]	Lee J Y, Thompson R B, Jasnow D, Balazs A C 2002 Macromolecules 35 4855 Google Scholar
[20]	Osipov M A, Gorkunov M V 2016 Eur. Phys. J. E. 39 1 Google Scholar
[21]	Osipov M A, Gorkunov M V, Kudryavtsev, Y V 2017 Mol. Cryst. Liq. Cryst. 647 405 Google Scholar
[22]	Osipov M A, Gorkunov M V, Berezkin A V, Kudryavtsev Y V 2018 Phys. Rev. E 97 042706 Google Scholar
[23]	Diaz J, Pinna M, Zvelindovsky A, Pagonabarraga I 2019 Soft Matter 15 6400 Google Scholar
[24]	Diaz J, Pinna M, Zvelindovsky A V, Pagonabarraga I 2019 Macromolecules 52 8285 Google Scholar
[25]	Diaz J, Pinna M, Zvelindovsky A V, Pagonabarraga I, Shenhar R 2020 Macromolecules 53 3234 Google Scholar
[26]	Ye X, Shi T, Lu Z, Zhang C, Sun Z, An L 2005 Macromolecules 38 8853 Google Scholar
[27]	Ma J W, Li X, Tang P, Yang Y 2007 J. Phys. Chem. B 111 1552 Google Scholar
[28]	Guo Y Q, Pan J X, Sun M N, Zhang J J 2017 J. Chem. Phys. 146 024902 Google Scholar
[29]	Guo Y Q 2021 Chin. Phys. B 30 048301 Google Scholar
[30]	Sun M, Zhang J J, Wang B, Wu H S, Pan J 2011 Phys. Rev. E 84 011802 Google Scholar
[31]	Sun M N, Zhang J J, Pan J X, Wang B F, Wu, H S 2016 Nano 11 1650008 Google Scholar
[32]	Pan J X, Zhang J J, Wang B F, Wu H S, Sun M N 2013 Chin. Phys. B 22 026401 Google Scholar
[33]	Thorkelsson K, Mastroianni A J, Ercius P, Xu T 2012 Aps. March Meeting 12 498 Google Scholar
[34]	Thorkelsson K, Nelson J H, Alivisatos A P, Xu T 2013 ACS 13 4908 Google Scholar
[35]	Thorkelsson K, Bronstein N, Xu T 2016 Macromolecules 49 6669 Google Scholar
[36]	Ma Y Q 2000 Phys. Rev. E 62 8207 Google Scholar
[37]	Zhu Y J, Ma Y Q 2003 Phys. Rev. E 67 041503 Google Scholar
[38]	Olszowka V, Hund M, Kuntermann V, Scherdel S, Tsarkova L, Bker A, Krausch G 2006 Soft Matter 2 1089 Google Scholar
[39]	Wang Q, Nealey P F, de Pablo J J 2003 Macromolecules 36 1731 Google Scholar
[40]	Ginzburg V V, Gibbons C, Qiu F, Peng G, Balazs A C 2000 Macromolecules 33 6140 Google Scholar
[41]	Choi S H, Lodge T P, Bates F S 2010 Phys. Rev. Lett. 104 047802 Google Scholar
[42]	Huang F, Addas K, Ward A, Flynn N T, Velasco E, Hagan M F, Fraden S 2009 Phys. Rev. Lett. 102 108302 Google Scholar
[43]	Chen Z R, Kornfield J A, Smith S D, Grothaus J T, Satkowski M M 1997 Science 277 1248 Google Scholar
[44]	Mullin T 2000 Phys. Rev. Lett. 84 4741 Google Scholar
[45]	Wu M W, Register R A, Chaikin P M 2006 Phys. Rev. E 74 040801 Google Scholar
[46]	Morozov A N, van Saarloos W 2005 Phys. Rev. Lett. 95 024501 Google Scholar
[47]	Hong K M, Noolandi J 1983 Macromolecules 16 1083 Google Scholar
[48]	Morozov A N, Fraaije J G E M 2002 Phys. Rev. E 65 031803 Google Scholar
[49]	Zvelindovsky A V, Sevink G J A, Fraaije J G E M 2000 Phys. Rev. E 62 R3063 Google Scholar
[50]	Koizumi S, Hasegawa H, Hashimoto T 1994 Macromolecules 27 6532 Google Scholar
[51]	Ginzburg V V, Qiu F, Paniconi M, Peng G, Jasnow D, Balazs A C 1999 Phys. Rev. Lett. 82 4026 Google Scholar
[52]	Qiu F, Ginzburg V V, Paniconi M, Peng G, Jasnow D, Balazs A C 1999 Langmuir 15 4952 Google Scholar
[53]	Buxton G A, Balazs A C 2004 Mol. Simulat. 30 249 Google Scholar
[54]	Balazs A C, Ginzburg V V, Qiu F, Peng G, Jasnow D 2000 J. Phys. Chem. B 104 3411 Google Scholar
[55]	Ginzburg V V, Peng G, Qiu F, Jasnow D, Balazs, A C 1999 Phys. Rev. E 60 4352 Google Scholar
[56]	Zhang J J, Jin G, Ma Y 2005 Phys. Rev. E 71 051803 Google Scholar
[57]	Zhang J J, Jin G, Ma Y 2005 Eur. Phys. J. E 18 359 Google Scholar
[58]	Ito A 1998 Phys. Rev. E 58 6158 Google Scholar
[59]	Liu B, Tong C, Yang Y 2001 J. Phys. Chem. B 105 10091 Google Scholar
[60]	Tong C, Yang Y 2002 J. Chem. Phys. 116 1519 Google Scholar
[61]	Oono Y, Bahiana M 1988 Phys. Rev. Lett. 61 1109 Google Scholar
[62]	Bates F S, Fredrickson G H 1990 Annu. Rev. Phys. Chem. 41 525 Google Scholar
[63]	Chakrabarti A, Gunton J D 1993 Phys. Rev. E 47 R792 Google Scholar
[64]	Schmittmann B, Zia R K P 1998 Phys. Rep. 301 45 Google Scholar
[65]	Schmittmann B 1990 Phys. B 4 2269 Google Scholar
[66]	Oono Y, Puri S 1987 Phys. Rev. Lett. 58 836 Google Scholar
[67]	Oono Y, Puri S 1988 Phys. Rev. A 38 434 Google Scholar
[68]	Puri S, Oono Y 1988 Phys. Rev. A 38 1542 Google Scholar
[69]	Shinozaki A, Oono Y 1992 Phys. Rev. A 45 R2161 Google Scholar
[70]	Geng X B, Pan J X, Zhang J J, Sun M N, Cen J Y 2018 Chin. Phys. B 27 058102 Google Scholar
[71]	Shinozaki A, Oono Y 1993 Phys. Rev. E 48 2622 Google Scholar

Cited By

图 1 在$ t=5\times {10}^{6} $时, 随着振荡场频率改变, AB/C/ NRs混合体系自组装形貌图　(a)斜层状纳米线结构$(\gamma = $$ 0, \omega =0$); (b)平行结构($ \gamma =0.05, \omega =0.0005) $; (c)过渡结构($ \gamma =0.05, \omega =0.005 $); (d) (e)斜层结构($\gamma =0.05, $$ \omega =0.01$); (f)垂直结构($\gamma = $$ 0.05, \omega =0.05$). 其中, $ \gamma $代表振荡场的振幅, $ \omega $代表振荡场的频率. 红色代表A嵌段, 蓝色代表B嵌段, 黄色代表C单体, 黑色代表纳米棒

Figure 1. The self-assembly topography of AB/C/NRs hybrid system at $ {\rm{t}}=5\times {10}^{6} $ as the frequency of the oscillating field changes: (a) Slanted layered nanowire structure ($\gamma $$ =0, \omega =0$); (b) parallel structure ($ \gamma =0.05, \omega =0.0005 $); (c) transition structure ($\gamma = $$ 0.05, \omega =0.005$); (d) (e) inclined layer structure ($ \gamma =0.05, \omega =0.01 $); (f) vertical structure ($ \gamma =0.05, \omega =0.05 $). Where, $ \gamma $ represents the amplitude of the oscillation field and $ \omega $ represents the frequency of the oscillation field. Red represents block A, blue represents block B, yellow represents monomer C, and black represents nanorods.

DownLoad: Full-Size Img PowerPoint

图 2 振荡场作用下, AB/C/NRs混合体系相结构形貌图随振幅和频率变化的二维相图, 其中, 红色方块代表斜层结构, 蓝色圆圈代表平行结构, 绿色三角代表垂直结构, 紫色菱形代表过渡结构

Figure 2. Two-dimensional phase diagram of phase structure morphology of AB/C/NRs hybrid system with amplitude and frequency variation under oscillating field, where red square represents oblique layer structure, blue circle represents parallel structure, green triangle represents vertical structure, and purple diamond represents transition structure.

DownLoad: Full-Size Img PowerPoint

图 3 在不同频率下, 均聚物C发生畴生长尺寸随时间演化的双对数图　(a)沿x轴方向的畴尺寸图$ {R}_{x}\left(t\right) $; (b)沿y轴方向的畴尺寸图$ {R}_{y}\left(t\right) $. 其中, 黑色线: 平行结构($\omega $$ =0.0005$), 红色线: 过渡结构($ \omega =0.005 $); 蓝色线: 斜层结构($ \omega =0.01 $); 绿色线: 垂直结构($ \omega =0.05 $). $ \omega $代表振荡场的频率

Figure 3. Double logarithmic graph of domain growth size vs. time evolution of homopolymer C at different frequencies. (a) Domain size map $ {R}_{x}\left(t\right) $ along the x-axis; (b) domain size $ {R}_{y}\left(t\right) $ along the y-axis. Among them, the black line: parallel structure ($\omega = $$ 0.0005$), the red line: transition structure ($ \omega =0.005 $); blue line: oblique layer structure ($\omega = $$ 0.01$); green line: vertical structure ($\omega = $$ 0.05$). Omega represents the frequency of the oscillating field.

DownLoad: Full-Size Img PowerPoint

图 4 在不同振荡场强度下, 纳米棒取向角平均值随时间的变化图. 其中, 黑色线: 平行结构($\omega = 0.0005$), 红色线: 过渡结构($\omega = $$ 0.005$); 蓝色线: 斜层结构($ \omega =0.01 $); 绿色线: 垂直结构($ \omega =0.05 $). $ \omega $代表振荡场的频率

Figure 4. Variation of the mean orientation Angle of nanorods with time under different oscillating field intensities. Among them, the black line: parallel structure ($ \omega =0.0005 $), the red line: transition structure ($ \omega =0.005 $); blue line: oblique layer structure ($\omega = $$ 0.01$); green line: vertical structure ($ \omega =0.05 $). Omega represents the frequency of the oscillating field.

DownLoad: Full-Size Img PowerPoint

图 5 振荡场作用下, AB/C/NRs混合体系畴结构随时间演化的形貌图　(a) $t=10000$; (b)$ t=20000 $; (c)$t= $$ 100000$; (d)$t= $$ 1000000$; (e)$ t=2000000 $; (f)$ t=5000000 $. 其中, $L=11, {N}{L}=123, $$ \gamma =0.05, \omega =0.0005$

Figure 5. Morphology diagram of domain structure evolution of AB/C/NRs hybrid system with time under oscillating field: (a)$t= $$ 10000$; (b)$ t=20000 $; (c)$ t=100000 $; (d)$ t=1000000 $; (e)$ t=2000000 $; (f) $ t=5000000 $. Among them, $ L=11 $, ${N}{L}=123 $, $ \gamma =0.05 $, $ \omega =0.0005 $.

DownLoad: Full-Size Img PowerPoint

map

[1]	Seul M, Andelman D 1995 Science 267 476 Google Scholar
[2]	Tanaka H 1993 Phys. Rev. Lett. 70 2770 Google Scholar
[3]	Marencic A P, Adamson D H, Chaikin P M, Register R A 2010 Phys. Rev. E 81 011503 Google Scholar
[4]	Wu S 2009 Phys. Rev. E 79 031803 Google Scholar
[5]	Croll A B, Shi A C, Dalnoki-Veress K 2009 Phys. Rev. E 80 051803 Google Scholar
[6]	Hosoi A E, Kogan D, Devereaux C E, Bernoff A J, Baker S M 2005 Phys. Rev. Lett. 95 037801 Google Scholar
[7]	Lopes W A 2002 Phys. Rev. E 65 031606 Google Scholar
[8]	Leibler L 1980 Macromolecules 13 1602 Google Scholar
[9]	Kletenik-Edelman O, Ploshnik E, Salant A, Shenhar R, Banin U, Rabani E 2008 Phys. Chem. C 112 4498 Google Scholar
[10]	Keblinski P, Kumar S K, Maritan A, Koplik J, Banavar J R 1996 Phys. Rev. Lett. 76 1106 Google Scholar
[11]	Harrison C, Adamson D H, Cheng Z, Sebastian J M, Sethuraman S, Huse D A, Chaikin P M 2000 Science 290 1558 Google Scholar
[12]	Matsuyama A, Evans R M L, Cates M E 2000 Phys. Rev. E 61 2977 Google Scholar
[13]	Yamaguchi D, Hashimoto T 2001 Macromolecules 34 6495 Google Scholar
[14]	Angelescu D E, Waller J H, Register R A, Chaikin P M 2005 Adv. Mater 17 1878 Google Scholar
[15]	Komura S, Kodama H 1997 Phys. Rev. E 55 1722 Google Scholar
[16]	Roan J R, Shakhnovich E I 1999 Phys. Rev. E 59 2109 Google Scholar
[17]	Ginzburg V V 2005 Macromolecules 38 2362 Google Scholar
[18]	He G, Ginzburg V V, Balazs A C 2006 J. Polym. Sci. B 44 2389 Google Scholar
[19]	Lee J Y, Thompson R B, Jasnow D, Balazs A C 2002 Macromolecules 35 4855 Google Scholar
[20]	Osipov M A, Gorkunov M V 2016 Eur. Phys. J. E. 39 1 Google Scholar
[21]	Osipov M A, Gorkunov M V, Kudryavtsev, Y V 2017 Mol. Cryst. Liq. Cryst. 647 405 Google Scholar
[22]	Osipov M A, Gorkunov M V, Berezkin A V, Kudryavtsev Y V 2018 Phys. Rev. E 97 042706 Google Scholar
[23]	Diaz J, Pinna M, Zvelindovsky A, Pagonabarraga I 2019 Soft Matter 15 6400 Google Scholar
[24]	Diaz J, Pinna M, Zvelindovsky A V, Pagonabarraga I 2019 Macromolecules 52 8285 Google Scholar
[25]	Diaz J, Pinna M, Zvelindovsky A V, Pagonabarraga I, Shenhar R 2020 Macromolecules 53 3234 Google Scholar
[26]	Ye X, Shi T, Lu Z, Zhang C, Sun Z, An L 2005 Macromolecules 38 8853 Google Scholar
[27]	Ma J W, Li X, Tang P, Yang Y 2007 J. Phys. Chem. B 111 1552 Google Scholar
[28]	Guo Y Q, Pan J X, Sun M N, Zhang J J 2017 J. Chem. Phys. 146 024902 Google Scholar
[29]	Guo Y Q 2021 Chin. Phys. B 30 048301 Google Scholar
[30]	Sun M, Zhang J J, Wang B, Wu H S, Pan J 2011 Phys. Rev. E 84 011802 Google Scholar
[31]	Sun M N, Zhang J J, Pan J X, Wang B F, Wu, H S 2016 Nano 11 1650008 Google Scholar
[32]	Pan J X, Zhang J J, Wang B F, Wu H S, Sun M N 2013 Chin. Phys. B 22 026401 Google Scholar
[33]	Thorkelsson K, Mastroianni A J, Ercius P, Xu T 2012 Aps. March Meeting 12 498 Google Scholar
[34]	Thorkelsson K, Nelson J H, Alivisatos A P, Xu T 2013 ACS 13 4908 Google Scholar
[35]	Thorkelsson K, Bronstein N, Xu T 2016 Macromolecules 49 6669 Google Scholar
[36]	Ma Y Q 2000 Phys. Rev. E 62 8207 Google Scholar
[37]	Zhu Y J, Ma Y Q 2003 Phys. Rev. E 67 041503 Google Scholar
[38]	Olszowka V, Hund M, Kuntermann V, Scherdel S, Tsarkova L, Bker A, Krausch G 2006 Soft Matter 2 1089 Google Scholar
[39]	Wang Q, Nealey P F, de Pablo J J 2003 Macromolecules 36 1731 Google Scholar
[40]	Ginzburg V V, Gibbons C, Qiu F, Peng G, Balazs A C 2000 Macromolecules 33 6140 Google Scholar
[41]	Choi S H, Lodge T P, Bates F S 2010 Phys. Rev. Lett. 104 047802 Google Scholar
[42]	Huang F, Addas K, Ward A, Flynn N T, Velasco E, Hagan M F, Fraden S 2009 Phys. Rev. Lett. 102 108302 Google Scholar
[43]	Chen Z R, Kornfield J A, Smith S D, Grothaus J T, Satkowski M M 1997 Science 277 1248 Google Scholar
[44]	Mullin T 2000 Phys. Rev. Lett. 84 4741 Google Scholar
[45]	Wu M W, Register R A, Chaikin P M 2006 Phys. Rev. E 74 040801 Google Scholar
[46]	Morozov A N, van Saarloos W 2005 Phys. Rev. Lett. 95 024501 Google Scholar
[47]	Hong K M, Noolandi J 1983 Macromolecules 16 1083 Google Scholar
[48]	Morozov A N, Fraaije J G E M 2002 Phys. Rev. E 65 031803 Google Scholar
[49]	Zvelindovsky A V, Sevink G J A, Fraaije J G E M 2000 Phys. Rev. E 62 R3063 Google Scholar
[50]	Koizumi S, Hasegawa H, Hashimoto T 1994 Macromolecules 27 6532 Google Scholar
[51]	Ginzburg V V, Qiu F, Paniconi M, Peng G, Jasnow D, Balazs A C 1999 Phys. Rev. Lett. 82 4026 Google Scholar
[52]	Qiu F, Ginzburg V V, Paniconi M, Peng G, Jasnow D, Balazs A C 1999 Langmuir 15 4952 Google Scholar
[53]	Buxton G A, Balazs A C 2004 Mol. Simulat. 30 249 Google Scholar
[54]	Balazs A C, Ginzburg V V, Qiu F, Peng G, Jasnow D 2000 J. Phys. Chem. B 104 3411 Google Scholar
[55]	Ginzburg V V, Peng G, Qiu F, Jasnow D, Balazs, A C 1999 Phys. Rev. E 60 4352 Google Scholar
[56]	Zhang J J, Jin G, Ma Y 2005 Phys. Rev. E 71 051803 Google Scholar
[57]	Zhang J J, Jin G, Ma Y 2005 Eur. Phys. J. E 18 359 Google Scholar
[58]	Ito A 1998 Phys. Rev. E 58 6158 Google Scholar
[59]	Liu B, Tong C, Yang Y 2001 J. Phys. Chem. B 105 10091 Google Scholar
[60]	Tong C, Yang Y 2002 J. Chem. Phys. 116 1519 Google Scholar
[61]	Oono Y, Bahiana M 1988 Phys. Rev. Lett. 61 1109 Google Scholar
[62]	Bates F S, Fredrickson G H 1990 Annu. Rev. Phys. Chem. 41 525 Google Scholar
[63]	Chakrabarti A, Gunton J D 1993 Phys. Rev. E 47 R792 Google Scholar
[64]	Schmittmann B, Zia R K P 1998 Phys. Rep. 301 45 Google Scholar
[65]	Schmittmann B 1990 Phys. B 4 2269 Google Scholar
[66]	Oono Y, Puri S 1987 Phys. Rev. Lett. 58 836 Google Scholar
[67]	Oono Y, Puri S 1988 Phys. Rev. A 38 434 Google Scholar
[68]	Puri S, Oono Y 1988 Phys. Rev. A 38 1542 Google Scholar
[69]	Shinozaki A, Oono Y 1992 Phys. Rev. A 45 R2161 Google Scholar
[70]	Geng X B, Pan J X, Zhang J J, Sun M N, Cen J Y 2018 Chin. Phys. B 27 058102 Google Scholar
[71]	Shinozaki A, Oono Y 1993 Phys. Rev. E 48 2622 Google Scholar

[1]	Zhao Xian-Tuo, Xu Lin-Lin, Tian Yue, Jiao An-Xin, Ma Hui, Zhang Meng-Ya, Cui Qing-Qiang. Self-assembled CuS porous grade sub-nanoflowers as efficient nano-adsorbents for adsorption/self-deposition characteristics research. Acta Physica Sinica, 2021, 70(22): 226101. doi: 10.7498/aps.70.20211152
[2]	Li Ai-Yun, Zhang Xing-Fang, Liu Feng-Shou, Yan Xin, Liang Lan-Ju. Fano resonances in symmetric gold nanorod trimers. Acta Physica Sinica, 2019, 68(19): 197801. doi: 10.7498/aps.68.20190978
[3]	Wang Wen-Jing, Li Chong, Zhang Mao-Mao, Gao Kun. Dynamical study of ultrafast exciton migration in coujugated polymers driven by nonuniform field. Acta Physica Sinica, 2019, 68(17): 177201. doi: 10.7498/aps.68.20190432
[4]	Yan Da-Dong, Zhang Xing-Hua. Recent development on the theory of polymer crystallization. Acta Physica Sinica, 2016, 65(18): 188201. doi: 10.7498/aps.65.188201
[5]	Hua Yun-Feng, Zhang Dong, Zhang Lin-Xi. Ordered structures of nanorods induced by the helixes of semiflexible polymer chains. Acta Physica Sinica, 2015, 64(8): 088201. doi: 10.7498/aps.64.088201
[6]	Cui Hong-Fei, Li Kai, Yang Chen-Guang, He Shu-Li. Magnetic properties of (Fe1-xCox)3BO5 nanorods. Acta Physica Sinica, 2015, 64(5): 057501. doi: 10.7498/aps.64.057501
[7]	Yu Sen-Jiang. Atomic force microscopy studies on self-organized wrinkles in constrained metallic films deposited on silicone oil substrates. Acta Physica Sinica, 2014, 63(11): 116801. doi: 10.7498/aps.63.116801
[8]	Liu Jia, Xu Ling-Ling, Zhang Hai-Lin, Lü Wei, Zhu Lin, Gao Hong, Zhang Xi-Tian. One-step hydrothermal process for self-assembly of zinc oxide nanorods array on Al-doped ZnO nanoplate surface. Acta Physica Sinica, 2012, 61(2): 027802. doi: 10.7498/aps.61.027802
[9]	Zhang Bao-Hua, Guo Fu-Qiang, Sun Yi, Wang Jun-Jun, Li Yan-Qing, Zhi Li-Li. Solvothermal recrystallized synthesis of one-dimensional CdS nanorods self-assembled from nanoparticles. Acta Physica Sinica, 2012, 61(13): 138101. doi: 10.7498/aps.61.138101
[10]	Yan Yue, Zhao Su-Ling, Xu Zheng, Gong Wei, Wang Da-Wei. Effect of 3,4,9,10-perylenetetracarboxylic dianhydride on the performance of ZnO nanorods/polymer hybrid solar cell. Acta Physica Sinica, 2011, 60(8): 088803. doi: 10.7498/aps.60.088803
[11]	Shao Zheng-Zheng, Wang Xiao-Feng, Zhang Xue-Ao, Chang Sheng-Li. Piezoelectric discharge characteristic of ZnO nanorod studied with atomic force microscopy. Acta Physica Sinica, 2010, 59(1): 550-554. doi: 10.7498/aps.59.550
[12]	Shi Jing, Gao Kun, Lei Jie, Xie Shi-Jie. A real space study on the conducting polymer with a ground-state nondegenerate structure. Acta Physica Sinica, 2009, 58(1): 459-464. doi: 10.7498/aps.58.459
[13]	Jin Hua, An Li-Nan, Bu Fan-Liang, Li Li-Hua, Wang Rong, Yang Wei-You, Zhang Li-Gong. Study of ultraviolet photoluminescence from SiC nanorods. Acta Physica Sinica, 2009, 58(4): 2594-2598. doi: 10.7498/aps.58.2594
[14]	Wang Hao, Zeng Gu-Cheng, Liao Chang-Jun, Cai Ji-Ye, Zheng Shu-Wen, Fan Guang-Han, Chen Yong, Liu Song-Hao. Study on the metamorphosis of InP self-organized islands grown on GaxxIn1-x1-xP buffer layers. Acta Physica Sinica, 2005, 54(4): 1726-1730. doi: 10.7498/aps.54.1726
[15]	Xia A-Gen, Yang Bo, Jin Jin-Sheng, Zhang Yi-Wen, Tang Fan, Ye Gao-Xiang. Ordered structures and self-organized phenomena in Au films deposited on silicone oil surfaces. Acta Physica Sinica, 2005, 54(1): 302-306. doi: 10.7498/aps.54.302
[16]	Wang Yi-Ping, Chen Jian-Ping, Li Xin-Wan, Zhou Jun-He, Shen Hao, Shi Chang-Hai, Zhang Xiao-Hong, Hong Jian-Xun, Ye Ai-Lun. Fast tunable electro-optic polymer waveguide gratings. Acta Physica Sinica, 2005, 54(10): 4782-4788. doi: 10.7498/aps.54.4782
[17]	Yang Hai-Tao, Shen Cheng-Min, Du Shi-Xuan, Su Yi-Kun, Wang Yan-Guo, Wang Yu-Ping, Gao Hong-Jun. Ordered arrays and magnetic properties of cobalt nanoparticles. Acta Physica Sinica, 2003, 52(12): 3114-3119. doi: 10.7498/aps.52.3114
[18]	Shen Cheng-Min, Su Yi-Kun, Yang Hai-Tao, Yang Tian-Zhong, Wang Yu-Ping, Gao Hong-Jun. Self-assembled two-dimensional structure of magnetic cobalt nanocrystals. Acta Physica Sinica, 2003, 52(2): 483-486. doi: 10.7498/aps.52.483
[19]	Cao Wan-Qiang, Li Jing-De. . Acta Physica Sinica, 2002, 51(7): 1634-1638. doi: 10.7498/aps.51.1634
[20]	Wu Heng-An, Ni Xiang-Gui, Wang Yu, Wang Xiu-Xi. . Acta Physica Sinica, 2002, 51(7): 1412-1415. doi: 10.7498/aps.51.1412

Catalog

Vol. 72, Issue 7 - 2023-04-05

Metrics

Abstract views: 3180
PDF Downloads: 84
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板