溶液法制备全无机钙钛矿太阳能电池的研究进展

王基铭; 陈科; 谢伟广; 时婷婷; 刘彭义; 郑毅帆; 朱瑞

doi:10.7498/aps.68.20190355

摘要

太阳能光伏技术, 能实现太阳能与电能的高效转换, 是实现人类文明可持续发展的关键绿色能源技术. 其中, 有机无机杂化钙钛矿太阳能电池具有优异的光电特性、低廉的制备成本、高效的转换效率, 已成为该领域的研究前沿. 虽然有机无机杂化钙钛矿太阳能电池的光电转换效率已约高达24%, 但其体系中的有机物组分易受环境中的光、热、潮等因素影响而分解, 致使器件稳定性存在严重的缺陷, 极大地限制了钙钛矿太阳能电池的产业化进程. 因此, 如何制备高效稳定的钙钛矿太阳能电池, 是目前该领域的研究热点与难点, 而发展具有更高环境稳定性的全无机钙钛矿太阳能电池具有重要意义. 本文回顾了近年来全无机钙钛矿太阳能电池领域的研究成果, 重点审视了钙钛矿薄膜的湿法制备工艺, 并探讨了器件在光热稳定性方面的改善, 为进一步推动钙钛矿太阳能电池的实用化进程提供可行性参考.

关键词:

Abstract

Photovoltaic technology, which can converse solar illumination into electricity, is crucial to the sustainable development of human civilization. Among them, the organic-inorganic hybrid perovskite solar cell (OIPSC) has become a research front due to its excellent photoelectric characteristics, low production cost and high power conversion efficiency (PCE). Although the PCE of OIPSC has exceeded 24%, the organic components in the perovskite system are sensitive to the decomposion caused by either being exposed to light or heated in high temperature environment. The stability defects have greatly limited the commercialization of perovskite solar cells. Therefore, it is urgent to improve the stability of perovskite solar cells, especially to solve the material decomposition problem. All-inorganic perovskite photovoltaic material, composed of all-inorganic elements, exhibits excellent heat and moisture resistance. Therefore, the development of all-inorganic perovskite solar cells is of great significance for solving the current stability problems in perovskite photovoltaics. In this work, we review the recent research progress of all-inorganic perovskite solar cells, discuss the solution approaches to processing all-inorganic perovskite films, and explore the enhancement of device stability. Our work provides a guideline for further promoting the device stability and PCE.

Keywords:

作者及机构信息

1.
暨南大学物理学系, 广州市真空薄膜技术与新能源材料重点实验室, 广东省真空薄膜技术与新能源材料工程技术中心, 思源实验室, 广州　510632

2.
北京大学, 人工微结构与介观物理国家重点实验室, 北京　100871

3.
山西大学, 极端光学协同创新中心, 太原　030006

通信作者: 刘彭义, tlpy@jnu.edu.cn ; 郑毅帆, yifan.zheng@pku.edu.cn ;

基金项目: 国家自然科学基金(批准号: 11804117, 61674070)、中央高校基本科研业务费专项资金(暨南大学科研培育与创新基金)(批准号: 21618313)、广东省科技攻关计划(批准号: 2017B09090701)和博士后创新人才支持计划(批准号: 8206200013)资助的课题.

Authors and contacts

1.
Siyuan Laboratory, Guangzhou Key Laboratory of Vacuum Coating Technologies and New Energy Materials, Guangdong Provincial Engineering Technology Research Center of Vacuum Coating Technologies and New Energy Materials, Department of Physics, Jinan University, Guangzhou 510632, China

2.
State Key Laboratory For Artificial Microstructure and Mesoscopic Physics, Peking University, Beijing 100871, China

3.
Collaboration Innovation Center of Extreme Optics, Shanxi University, Taiyuan 030006, China

Corresponding author: Liu Peng-Yi, tlpy@jnu.edu.cn ; Zheng Yi-Fan, yifan.zheng@pku.edu.cn ;

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 11804117, 61674070), the Fundamental Research Funds for the Central Universities, China (Grant No. 21618313), the Key Science and Technology Program of Guangdong Province, China (Grant No. 2017B09090701), and the China Postdoctoral Innovation Talent Foundation (Grant No. 8206200013).

文章全文 : translate this paragraph

参考文献

[1]	范伟利, 杨宗林, 张振雲, 齐俊杰 2018 67 228801 Google Scholar Fan W L, Yang Z L, Zhang Z Y, Qi J J 2018 Acta Phys. Sin. 67 228801 Google Scholar
[2]	Hu Q, Zhao L, Wu J, Gao K, Luo D, Jiang Y, Zhang Z, Zhu C, Schaible E, Hexemer A, Wang C, Liu Y, Zhang W, Grätzel M, Liu F, Russell T P, Zhu R, Gong Q 2017 Nat. Commun. 8 15688 Google Scholar
[3]	Luo D, Yang W, Wang Z, Sadhanala A, Hu Q, Su R, Shivanna R, Trindade G F, Watts J F, Xu Z, Liu T, Chen K, Ye F, Wu P, Zhao L, Wu J, Tu Y, Zhang Y, Yang X, Zhang W, Friend R H, Gong Q, Snaith H J, Zhu R 2018 Science 360 1442 Google Scholar
[4]	Chen K, Hu Q, Liu T, Zhao L, Luo D, Wu J, Zhang Y, Zhang W, Liu F, Russell T P, Zhu R, Gong Q 2016 Adv. Mater. 28 10718 Google Scholar
[5]	Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[6]	Kim H S, Lee C R, Im J H, Lee K B, Moehl T, Marchioro A, Moon S J, Humphry-Baker R, Yum J H, Moser J E, Gratzel M, Park N G 2012 Sci. Rep. 2 591 Google Scholar
[7]	NREL 2019 Best Research-Cell Efficiencies https://www.nrel.gov/pv/cell-efficiency.html [2019-03-12]
[8]	Chung I, Lee B, He J, Chang R P H, Kanatzidis M G 2012 Nature 485 486 Google Scholar
[9]	Chen Z, Wang J J, Ren Y, Yu C, Shum K 2012 Appl. Phys. Lett. 101 093901 Google Scholar
[10]	Zeng Q, Zhang X, Liu C, Feng T, Chen Z, Zhang W, Zheng W, Zhang H, Yang B 2019 Sol. RRL 3 1800239
[11]	Cui P, Wei D, Ji J, Song D, Li Y, Liu X, Huang J, Wang T, You J, Li M 2017 Sol. RRL 1 1600027 Google Scholar
[12]	Ahn N, Kwak K, Jang M S, Yoon H, Lee B Y, Lee J K, Pikhitsa P V, Byun J, Choi M 2016 Nat. Commun. 7 13422 Google Scholar
[13]	Park N G, Grätzel M, Miyasaka T, Zhu K, Emery K 2016 Nat. Energy 1 16152 Google Scholar
[14]	张翱陈, 闫君, 张春秀 2018 67 106701 Google Scholar Zhao A, Chen Y L, Yan J, Zhang C X 2018 Acta Phys. Sin. 67 106701 Google Scholar
[15]	Akbulatov A F, Luchkin S Y, Frolova L A, Dremova N N, Gerasimov K L, Zhidkov I S, Anokhin D V, Kurmaev E Z, Stevenson K J, Troshin P A 2017 J. Phys. Chem. Lett. 8 1211 Google Scholar
[16]	Xiao C, Li Z, Guthrey H, Moseley J, Yang Y, Wozny S, Moutinho H, To B, Berry J J, Gorman B, Yan Y, Zhu K, Al-Jassim M 2015 J. Phys. Chem. C 119 26904 Google Scholar
[17]	Liang J, Liu J, Jin Z 2017 Sol. RRL 1 1700086 Google Scholar
[18]	Zhou W, Zhao Y, Zhou X, Fu R, Li Q, Zhao Y, Liu K, Yu D, Zhao Q 2017 J. Phys. Chem. Lett. 8 4122 Google Scholar
[19]	Unger E L, Hoke E T, Bailie C D, Nguyen W H, Bowring A R, Heumüller T, Christoforo M G, McGehee M D 2014 Energy Environ. Sci. 7 3690 Google Scholar
[20]	Tress W, Marinova N, Moehl T, Zakeeruddin S M, Nazeeruddin M K, Grätzel M 2015 Energy Environ. Sci. 8 995 Google Scholar
[21]	Lau C F J, Zhang M, Deng X, Zheng J, Bing J, Ma Q, Kim J, Hu L, Green M A, Huang S, Ho-Baillie A 2017 ACS Energy Lett. 2 2319 Google Scholar
[22]	Lu C, Li H, Kolodziejski K, Dun C, Huang W, Carroll D, Geyer S M 2018 Nano Res. 11 762
[23]	Swarnkar A, Marshall A R, Sanehira E M, Chernomordik B D, Moore D T, Christians J A, Chakrabarti T, Luther J M 2016 Science 354 92 Google Scholar
[24]	Huang H, Chen B, Wang Z, Hung T F, Susha A S, Zhong H, Rogach A L 2016 Chem. Sci. 7 5699 Google Scholar
[25]	De Roo J, Ibanez M, Geiregat P, Nedelcu G, Walravens W, Maes J, Martins J C, van Driessche I, Kovalenko M V, Hens Z 2016 ACS Nano 10 2071 Google Scholar
[26]	Eperon G E, Paternò G M, Sutton R J, Zampetti A, Haghighirad A A, Cacialli F, Snaith H J 2015 J. Mater. Chem. A 3 19688 Google Scholar
[27]	Wang Y, Zhang T, Kan M, Zhao Y 2018 J. Am. Chem. Soc. 140 12345 Google Scholar
[28]	Lu M, Zhang X, Bai X, Wu H, Shen X, Zhang Y, Zhang W, Zheng W, Song H, Yu W W, Rogach A L 2018 ACS Energy Lett. 3 1571 Google Scholar
[29]	Fu L, Zhang Y, Chang B, Li B, Zhou S, Zhang L, Yin L 2018 J. Mater. Chem. A 6 13263 Google Scholar
[30]	Stoddard R J, Rajagopal A, Palmer R L, Braly I L, Jen A K Y, Hillhouse H W 2018 ACS Energy Lett. 3 1261 Google Scholar
[31]	Travis W, Glover E N K, Bronstein H, Scanlon D O, Palgrave R G 2016 Chem. Sci. 7 4548 Google Scholar
[32]	Luo P, Zhou Y, Zhou S, Lu Y, Xu C, Xia W, Sun L 2018 Chem. Eng. J. 343 146 Google Scholar
[33]	Zhang L, Li B, Yuan J, Wang M, Shen T, Huang F, Wen W, Cao G, Tian J 2018 J. Phys. Chem. Lett. 9 3646 Google Scholar
[34]	Li X, Yu D, Cao F, Gu Y, Wei Y, Wu Y, Song J, Zeng H 2016 Adv. Funct. Mater. 26 5903 Google Scholar
[35]	García de Arquer F P, Armin A, Meredith P, Sargent E H 2017 Nat. Rev. Mater. 2 16100 Google Scholar
[36]	Voznyy O, Sutherland B R, Ip A H, Zhitomirsky D, Sargent E H 2017 Nat. Rev. Mater. 2 17026 Google Scholar
[37]	Xiang S, Fu Z, Li W, Wei Y, Liu J, Liu H, Zhu L, Zhang R, Chen H 2018 ACS Energy Lett. 3 1824 Google Scholar
[38]	Liang J, Wang C, Zhao P, Lu Z, Ma Y, Xu Z, Wang Y, Zhu H, Hu Y, Zhu G, Ma L, Chen T, Tie Z, Liu J, Jin Z 2017 Nanoscale 9 11841 Google Scholar
[39]	Luo P, Xia W, Zhou S, Sun L, Cheng J, Xu C, Lu Y 2016 J. Phys. Chem. Lett. 7 3603 Google Scholar
[40]	Ramadan A J, Rochford L A, Fearn S, Snaith H J 2017 J. Phys. Chem. Lett. 8 4172 Google Scholar
[41]	Correa Baena J P, Steier L, Tress W, Saliba M, Neutzner S, Matsui T, Giordano F, Jacobsson T J, Srimath Kandada A R, Zakeeruddin S M, Petrozza A, Abate A, Nazeeruddin M K, Grätzel M, Hagfeldt A 2015 Energy Environ. Sci. 8 2928 Google Scholar
[42]	Wang P, Zhang X, Zhou Y, Jiang Q, Ye Q, Chu Z, Li X, Yang X, Yin Z, You J 2018 Nat. Commun. 9 2225 Google Scholar
[43]	Yu B, Zhang H, Wu J, Li Y, Li H, Li Y, Shi J, Wu H, Li D, Luo Y, Meng Q 2018 J. Mater. Chem. A 6 19810 Google Scholar
[44]	Zhu W, Zhang Q, Zhang C, Zhang Z, Chen D, Lin Z, Chang J, Zhang J, Hao Y 2018 ACS Appl. Energy Mater. 1 4991 Google Scholar
[45]	Liu C, Li W, Chen J, Fan J, Mai Y, Schropp R E I 2017 Nano Energy 41 75 Google Scholar
[46]	Ma Q, Huang S, Wen X, Green M A, Ho-Baillie A W Y 2016 Adv. Energy Mater. 6 1502202 Google Scholar
[47]	Sutton R J, Eperon G E, Miranda L, Parrott E S, Kamino B A, Patel J B, Hörantner M T, Johnston M B, Haghighirad A A, Moore D T, Snaith H J 2016 Adv. Energy Mater. 6 1502458 Google Scholar
[48]	Duan J, Zhao Y, He B, Tang Q 2018 Angew. Chem. Int. Ed. Engl. 57 3787 Google Scholar
[49]	Hoffman J B, Zaiats G, Wappes I, Kamat P V 2017 Chem. Mat. 29 9767 Google Scholar
[50]	Liu X, Tan X, Liu Z, Ye H, Sun B, Shi T, Tang Z, Liao G 2019 Nano Energy 56 184 Google Scholar
[51]	Zhao Y, Duan J, Yuan H, Wang Y, Yang X, He B, Tang Q 2019 Sol. RRL 3 1800284 Google Scholar
[52]	Lee B, Krenselewski A, Baik S I, Seidman D N, Chang R P H 2017 Sustain. Energy Fuels 1 710 Google Scholar
[53]	Song L, Wang W, Körstgens V, González D M, Yao Y, Minar N K, Feckl J M, Peters K, Bein T, Fattakhova-Rohlfing D, Santoro G, Roth S V, Müller-Buschbaum P 2016 Adv. Funct. Mater. 26 1498 Google Scholar
[54]	Su B, Caller-Guzman H A, Korstgens V, Rui Y, Yao Y, Saxena N, Santoro G, Roth S V, Muller-Buschbaum P 2017 ACS Appl. Mater. Inter. 9 43724 Google Scholar
[55]	Heo J H, Lee M H, Jang M H, Im S H 2016 J. Mater. Chem. A 4 17636 Google Scholar
[56]	Zheng Y, Kong J, Huang D, Shi W, McMillon-Brown L, Katz H E, Yu J, Taylor A D 2018 Nanoscale 10 11342 Google Scholar
[57]	Cheng J, Hu R, Meng X, Li Y, Yan X, Yang X, Liao X, Li L, Pei Q, Chong K B 2018 Sol. RRL 2 1800064 Google Scholar
[58]	Cheng J, Hu R, Wang Q, Zhang C, Xie Z, Long Z, Yang X, Li L 2015 Int. J. Photoenergy 2015 201472
[59]	Lau C F J, Deng X, Ma Q, Zheng J, Yun J S, Green M A, Huang S, Ho-Baillie A W Y 2016 ACS Energy Lett. 1 573 Google Scholar
[60]	Ruan W, Hu Y, Qiu T, Bai F, Zhang S, Xu F 2019 J. Phys. Chem. Solids 127 258 Google Scholar
[61]	Zhou H, Fan L, He G, Yuan C, Wang Y, Shi S, Sui N, Chen B, Zhang Y, Yao Q, Zhao J, Zhang X, Yin J 2018 RSC Adv. 8 29089 Google Scholar
[62]	Yang Z, Wang M, Li J, Dou J, Qiu H, Shao J 2018 ACS Appl. Mater. Inter. 10 26387 Google Scholar
[63]	Liao H, Guo S, Cao S, Wang L, Gao F, Yang Z, Zheng J, Yang W 2018 Adv. Opt. Mater. 6 1800346 Google Scholar
[64]	Wang Y, Zhu Y, Huang J, Cai J, Zhu J, Yang X, Shen J, Jiang H, Li C 2016 J. Phys. Chem. Lett. 7 4253 Google Scholar
[65]	Li Y, Duan J, Yuan H, Zhao Y, He B, Tang Q 2018 Sol. RRL 2 1800164 Google Scholar
[66]	Nam J K, Chai S U, Cha W, Choi Y J, Kim W, Jung M S, Kwon J, Kim D, Park J H 2017 Nano Lett. 17 2028 Google Scholar
[67]	Bu T, Liu X, Zhou Y, Yi J, Huang X, Luo L, Xiao J, Ku Z, Peng Y, Huang F, Cheng Y B, Zhong J 2017 Energy Environ. Sci. 10 2509 Google Scholar
[68]	Lee J H, Bristowe N C, Lee J H, Lee S H, Bristowe P D, Cheetham A K, Jang H M 2016 Chem. Mat. 28 4259 Google Scholar
[69]	Son D Y, Kim S G, Seo J Y, Lee S H, Shin H, Lee D, Park N G 2018 J. Am. Chem. Soc. 140 1358 Google Scholar
[70]	Krieg F, Ochsenbein S T, Yakunin S, Ten Brinck S, Aellen P, Suess A, Clerc B, Guggisberg D, Nazarenko O, Shynkarenko Y, Kumar S, Shih C J, Infante I, Kovalenko M V 2018 ACS Energy Lett. 3 641 Google Scholar
[71]	Yang D, Li X, Zeng H 2018 Adv. Mater. Inter. 5 1701662 Google Scholar
[72]	Kumar M H, Dharani S, Leong W L, Boix P P, Prabhakar R R, Baikie T, Shi C, Ding H, Ramesh R, Asta M, Graetzel M, Mhaisalkar S G, Mathews N 2014 Adv. Mater. 26 7122 Google Scholar
[73]	Xiang S, Li W, Wei Y, Liu J, Liu H, Zhu L, Chen H 2018 Nanoscale 10 9996 Google Scholar
[74]	Zhao S, Yamamoto K, Iikubo S, Hayase S, Ma T 2018 J. Phys. Chem. Solids 117 117 Google Scholar
[75]	Akkerman Q A, Meggiolaro D, Dang Z, de Angelis F, Manna L 2017 ACS Energy Lett. 2 2183 Google Scholar
[76]	Greul E, Petrus Michiel L, Binek A, Docampo P, Bein T 2017 J. Mater. Chem. A 5 19972 Google Scholar
[77]	Bian H, Bai D, Jin Z, Wang K, Liang L, Wang H, Zhang J, Wang Q, Liu S 2018 Joule 2 1500 Google Scholar
[78]	Lau C F J, Deng X, Zheng J, Kim J, Zhang Z, Zhang M, Bing J, Wilkinson B, Hu L, Patterson R, Huang S, Ho-Baillie A 2018 J. Mater. Chem. A 6 5580 Google Scholar
[79]	Yang R X, Skelton J M, da Silva E L, Frost J M, Walsh A 2017 J. Phys. Chem. Lett. 8 4720 Google Scholar
[80]	Ju M G, Dai J, Ma L, Zeng X C 2017 J. Am. Chem. Soc. 139 8038 Google Scholar
[81]	Noel N K, Stranks S D, Abate A, Wehrenfennig C, Guarnera S, Haghighirad A A, Sadhanala A, Eperon G E, Pathak S K, Johnston M B, Petrozza A, Herz L M, Snaith H J 2014 Energy Environ. Sci. 7 3061 Google Scholar
[82]	Hao F, Stoumpos C C, Chang R P, Kanatzidis M G 2014 J. Am. Chem. Soc. 136 8094 Google Scholar
[83]	Swarnkar A, Mir W J, Nag A 2018 ACS Energy Lett. 3 286 Google Scholar
[84]	Sabba D, Mulmudi H K, Prabhakar R R, Krishnamoorthy T, Baikie T, Boix P P, Mhaisalkar S, Mathews N 2015 J. Phys. Chem. C 119 1763 Google Scholar
[85]	Bai D, Zhang J, Jin Z, Bian H, Wang K, Wang H, Liang L, Wang Q, Liu S F 2018 ACS Energy Lett. 3 970 Google Scholar
[86]	Liang J, Liu Z, Qiu L, Hawash Z, Meng L, Wu Z, Jiang Y, Ono L K, Qi Y 2018 Adv. Energy Mater. 8 1800504 Google Scholar
[87]	Hu Y, Zhang S, Shu T, Qiu T, Bai F, Ruan W, Xu F 2018 J. Mater. Chem. A 6 20365 Google Scholar
[88]	Ge S, Wang Y, Xiang Z, Cui Y 2018 ACS Appl. Mater. Inter. 10 24620 Google Scholar
[89]	Jena A K, Kulkarni A, Sanehira Y, Ikegami M, Miyasaka T 2018 Chem. Mat. 31 6668
[90]	Duan J, Zhao Y, Yang X, Wang Y, He B, Tang Q 2018 Adv. Energy Mater. 8 1802346 Google Scholar
[91]	Liu C, Li W, Li H, Wang H, Zhang C, Yang Y, Gao X, Xue Q, Yip H L, Fan J, Schropp R E I, Mai Y 2019 Adv. Energy Mater. 9 1803572 Google Scholar
[92]	Liang J, Zhao P, Wang C, Wang Y, Hu Y, Zhu G, Ma L, Liu J, Jin Z 2017 J. Am. Chem. Soc. 139 14009 Google Scholar
[93]	Protesescu L, Yakunin S, Bodnarchuk M I, Krieg F, Caputo R, Hendon C H, Yang R X, Walsh A, Kovalenko M V 2015 Nano Lett. 15 3692 Google Scholar
[94]	Dastidar S, Egger D A, Tan L Z, Cromer S B, Dillon A D, Liu S, Kronik L, Rappe A M, Fafarman A T 2016 Nano Lett. 16 3563 Google Scholar
[95]	Diroll B T, Nedelcu G, Kovalenko M V, Schaller R D 2017 Adv. Funct. Mater. 27 1606750 Google Scholar
[96]	Mondal N, De A, Samanta A 2018 J. Phys. Chem. Lett. 9 3673 Google Scholar
[97]	Han G, Hadi H D, Bruno A, Kulkarni S A, Koh T M, Wong L H, Soci C, Mathews N, Zhang S, Mhaisalkar S G 2018 J. Phys. Chem. C 122 13884 Google Scholar
[98]	Zheng Y, Shi W, Kong J, Huang D, Katz H E, Yu J, Taylor A D 2017 Small Methods 1 1700244 Google Scholar
[99]	Jeong B, Han H, Choi Y J, Cho S H, Kim E H, Lee S W, Kim J S, Park C, Kim D, Park C 2018 Adv. Funct. Mater. 28 1706401 Google Scholar
[100]	Li B, Zhang Y, Fu L, Yu T, Zhou S, Zhang L, Yin L 2018 Nat. Commun. 9 1076 Google Scholar
[101]	Ding X, Chen H, Wu Y, Ma S, Dai S, Yang S, Zhu J 2018 J. Mater. Chem. A 6 18258 Google Scholar
[102]	Ke Y, Wang N, Kong D, Cao Y, He Y, Zhu L, Wang Y, Xue C, Peng Q, Gao F, Huang W, Wang J 2019 J. Phys. Chem. Lett. 10 380 Google Scholar
[103]	Zhang F, Kim D H, Zhu K 2018 Curr. Opin. Electr. 11 105
[104]	Heo D Y, Han S M, Woo N S, Kim Y J, Kim T Y, Luo Z, Kim S Y 2018 J. Phys. Chem. C 122 15903 Google Scholar
[105]	Zhao B, Jin S, Huang S, Liu N, Ma J Y, Xue D J, Han Q, Ding J, Ge Q Q, Feng Y, Hu J S 2018 J. Am. Chem. Soc. 140 11716 Google Scholar
[106]	Huang Y, Yin W J, He Y 2018 J. Phys. Chem. C 122 1345
[107]	Jiang Y, Yuan J, Ni Y, Yang J, Wang Y, Jiu T, Yuan M, Chen J 2018 Joule 2 1356 Google Scholar
[108]	Lin D, Zhang T, Wang J, Long M, Xie F, Chen J, Wu B, Shi T, Yan K, Xie W, Liu P, Xu J 2019 Nano Energy 59 619 Google Scholar
[109]	Nedelcu G, Protesescu L, Yakunin S, Bodnarchuk M I, Grotevent M J, Kovalenko M V 2015 Nano Lett. 15 5635 Google Scholar
[110]	Sanehira E M, Marshall A R, Christians J A, Harvey S P, Ciesielski P N, Wheeler L M, Schulz P, Lin L Y, Beard M C, Luther J M 2017 Sci. Adv. 3 eaao4204 Google Scholar
[111]	Zou C, Xi Y, Huang C Y, Keeler E G, Feng T, Zhu S, Pozzo L D, Lin L Y 2018 Adv. Opt. Mater. 6 1800324 Google Scholar
[112]	Yuan J, Ling X, Yang D, Li F, Zhou S, Shi J, Qian Y, Hu J, Sun Y, Yang Y, Gao X, Duhm S, Zhang Q, Ma W 2018 Joule 2 2450 Google Scholar
[113]	Wang Q, Jin Z, Chen D, Bai D, Bian H, Sun J, Zhu G, Wang G, Liu S F 2018 Adv. Energy Mater. 8 1800007 Google Scholar
[114]	Akkerman Q A, Gandini M, Di Stasio F, Rastogi P, Palazon F, Bertoni G, Ball J M, Prato M, Petrozza A, Manna L 2016 Nat. Energy 2 16194
[115]	Liao J Y, He J W, Xu H, Kuang D B, Su C Y 2012 J. Mater. Chem. 22 7910 Google Scholar
[116]	Wu W Q, Huang F, Chen D, Cheng Y B, Caruso R A 2015 Adv. Funct. Mater. 25 3264 Google Scholar
[117]	Xu Y F, Wu W Q, Rao H S, Chen H Y, Kuang D B, Su C Y 2015 Nano Energy 11 621 Google Scholar
[118]	Zhang D, Eaton S W, Yu Y, Dou L, Yang P 2015 J. Am. Chem. Soc. 137 9230 Google Scholar
[119]	Im J H, Luo J, Franckevičius M, Pellet N, Gao P, Moehl T, Zakeeruddin S M, Nazeeruddin M K, Grätzel M, Park N G 2015 Nano Lett. 15 2120 Google Scholar
[120]	Chen Z, Dong L, Tang H, Yu Y, Ye L, Zang J 2019 CrystEngComm 21 1389 Google Scholar
[121]	Chen G, Feng J, Gao H, Zhao Y, Pi Y, Jiang X, Wu Y, Jiang L 2019 Adv. Funct. Mater. 29 1808741 Google Scholar
[122]	Waleed A, Tavakoli M M, Gu L, Hussain S, Zhang D, Poddar S, Wang Z, Zhang R, Fan Z 2017 Nano Lett. 17 4951 Google Scholar
[123]	Chen K, Wu P, Yang W, Su R, Luo D, Yang X, Tu Y, Zhu R, Gong Q 2018 Nano Energy 49 411 Google Scholar
[124]	Zhang T, Dar M I, Li G, Xu F, Guo N, Grätzel M, Zhao Y 2017 Sci. Adv. 3 e1700841 Google Scholar
[125]	Song J, Xu L, Li J, Xue J, Dong Y, Li X, Zeng H 2016 Adv. Mater. 28 4861 Google Scholar
[126]	Li X, Yu D, Chen J, Wang Y, Cao F, Wei Y, Wu Y, Wang L, Zhu Y, Sun Z, Ji J, Shen Y, Sun H, Zeng H 2017 ACS Nano 11 2015 Google Scholar
[127]	Liao J F, Rao H S, Chen B X, Kuang D B, Su C Y 2017 J. Mater. Chem. A 5 2066 Google Scholar
[128]	Li F, Pei Y, Xiao F, Zeng T, Yang Z, Xu J, Sun J, Peng B, Liu M 2018 Nanoscale 10 6318 Google Scholar
[129]	Wang Y, Zhang T, Kan M, Li Y, Wang T, Zhao Y 2018 Joule 2 2065 Google Scholar
[130]	Zhang S, Yi C, Wang N, Sun Y, Zou W, Wei Y, Cao Y, Miao Y, Li R, Yin Y, Zhao N, Wang J, Huang W 2017 Adv. Mater. 29 1606600 Google Scholar
[131]	Chuang C H, Brown P R, Bulovic V, Bawendi M G 2014 Nat. Mater. 13 796 Google Scholar
[132]	Wang S, Sakurai T, Wen W, Qi Y 2018 Adv. Mater. Inter. 5 1800260 Google Scholar
[133]	Zhang J, Bai D, Jin Z, Bian H, Wang K, Sun J, Wang Q, Liu S F 2018 Adv. Energy Mater. 8 1703246 Google Scholar
[134]	Hirotsu S, Harada J, Iizumi M, Gesi K 1974 J. Phys. Soc. Jpn. 37 1393 Google Scholar
[135]	Luchkin S Y, Akbulatov A F, Frolova L A, Tsarev S A, Troshin P A, Stevenson K J 2017 Sol. Energy Mater. Sol. Cells 171 205 Google Scholar
[136]	Beal R E, Slotcavage D J, Leijtens T, Bowring A R, Belisle R A, Nguyen W H, Burkhard G F, Hoke E T, McGehee M D 2016 J. Phys. Chem. Lett. 7 746 Google Scholar
[137]	Klein-Kedem N, Cahen D, Hodes G 2016 Acc. Chem. Res. 49 347 Google Scholar
[138]	An R, Zhang F, Zou X, Tang Y, Liang M, Oshchapovskyy I, Liu Y, Honarfar A, Zhong Y, Li C, Geng H, Chen J, Canton S E, Pullerits T, Zheng K 2018 ACS Appl. Mater. Inter. 10 39222 Google Scholar
[139]	Malinkiewicz O, Yella A, Lee Y H, Espallargas G M, Graetzel M, Nazeeruddin M K, Bolink H J 2014 Nat. Photon. 8 128
[140]	Chen C Y, Lin H Y, Chiang K M, Tsai W L, Huang Y C, Tsao C S, Lin H W 2017 Adv. Mater. 29 1605290 Google Scholar
[141]	Chen C W, Kang H W, Hsiao S Y, Yang P F, Chiang K M, Lin H W 2014 Adv. Mater. 26 6647 Google Scholar
[142]	Frolova L A, Anokhin D V, Piryazev A A, Luchkin S Y, Dremova N N, Stevenson K J, Troshin P A 2017 J. Phys. Chem. Lett. 8 67 Google Scholar
[143]	Burwig T, Franzel W, Pistor P 2018 J. Phys. Chem. Lett. 9 4808 Google Scholar
[144]	Hu Y, Wang Q, Shi YL, Li M, Zhang L, Wang Z K, Liao LS 2017 J. Mater. Chem. C 5 8144 Google Scholar
[145]	Yonezawa K, Yamamoto K, Shahiduzzaman M, Furumoto Y, Hamada K, Ripolles T S, Karakawa M, Kuwabara T, Takahashi K, Hayase S, Taima T 2017 Jpn. J. Appl. Phys. 56 04CS11
[146]	Shahiduzzaman M, Yonezawa K, Yamamoto K, Ripolles T S, Karakawa M, Kuwabara T, Takahashi K, Hayase S, Taima T 2017 ACS Omega 2 4464 Google Scholar
[147]	Chen M, Ju M G, Carl A D, Zong Y, Grimm R L, Gu J, Zeng X C, Zhou Y, Padture N P 2018 Joule 2 558 Google Scholar
[148]	Moghe D, Wang L, Traverse C J, Redoute A, Sponseller M, Brown P R, Bulović V, Lunt R R 2016 Nano Energy 28 469 Google Scholar
[149]	Hu Y, Bai F, Liu X, Ji Q, Miao X, Qiu T, Zhang S 2017 ACS Energy Lett. 2 2219 Google Scholar
[150]	Wang Q, Zheng X, Deng Y, Zhao J, Chen Z, Huang J 2017 Joule 1 371 Google Scholar
[151]	Chang X, Li W, Zhu L, Liu H, Geng H, Xiang S, Liu J, Chen H 2016 ACS Appl. Mater. Inter. 8 33649 Google Scholar
[152]	Duan J, Dou D, Zhao Y, Wang Y, Yang X, Yuan H, He B, Tang Q 2018 Mater. Today Energy 10 146 Google Scholar
[153]	Gong J, Guo P, Benjamin S E, Van Patten P G, Schaller R D, Xu T 2018 J. Energy Chem. 27 1017 Google Scholar
[154]	Zheng G, Zhu C, Ma J, Zhang X, Tang G, Li R, Chen Y, Li L, Hu J, Hong J, Chen Q, Gao X, Zhou H 2018 Nat. Commun. 9 2793 Google Scholar
[155]	Zhou Y, Zhao Y 2019 Energy Environ. Sci. 12 1495 Google Scholar
[156]	Zhu C, Niu X, Fu Y, Li N, Hu C, Chen Y, He X, Na G, Liu P, Zai H, Ge Y, Lu Y, Ke X, Bai Y, Yang S, Chen P, Li Y, Sui M, Zhang L, Zhou H, Chen Q 2019 Nat. Commun. 10 815 Google Scholar
[157]	Ju M G, Chen M, Zhou Y, Garces H F, Dai J, Ma L, Padture N P, Zeng X C 2018 ACS Energy Lett. 3 297 Google Scholar
[158]	Huang L Y, Lambrecht W R L 2016 Phys. Rev. B 93 195211 Google Scholar
[159]	Ahmad W, Khan J, Niu G, Tang J 2017 Sol. RRL 1 1700048 Google Scholar
[160]	Wei S, Yang Y, Kang X, Wang L, Huang L, Pan D 2017 Inorg. Chem. 56 2596 Google Scholar
[161]	Shojaei F, Yin W J 2018 J. Phys. Chem. C 122 15214 Google Scholar
[162]	Huang J, Xiang S, Yu J, Li C Z 2019 Energy Environ. Sci. 12 929 Google Scholar
[163]	Dong S, Liu Y, Hong Z, Yao E, Sun P, Meng L, Lin Y, Huang J, Li G, Yang Y 2017 Nano Lett. 17 5140 Google Scholar
[164]	Gao K, Zhu Z, Xu B, Jo S B, Kan Y, Peng X, Jen A K 2017 Adv. Mater. 29 1703980 Google Scholar
[165]	Leijtens T, Bush K A, Prasanna R, McGehee M D 2018 Nat. Energy 3 828 Google Scholar

施引文献

图 1 立方晶格钙钛矿结构ABX₃

Fig. 1. Cubic perovskite structures of ABX₃.

下载: 全尺寸图片幻灯片

图 2 (a)一步成膜法制备CsPbI₃粉末及薄膜^[38]; (b)多步成膜法制备CsPbBr₃^[49]; (c)喷涂^[62]; (d)一步静电纺丝工艺^[63]

Fig. 2. Schematic illustration of (a) the one-step solution-phase synthesis and powders and thin film fabrication of CsPbI₃^[38], (b) the multi-step fabrication process of the cesium lead bromide films^[49]; (c) spray-coated^[62]; (d) one-step electrospinning technique^[63].

下载: 全尺寸图片幻灯片

图 3 (a) CsPbBr₃, Cs_0.98Li_0.02PbBr₃, Cs_0.94Na_0.06PbBr₃, Cs_0.92K_0.08PbBr₃和Cs_0.91Rb_0.09PbBr₃薄膜的表面扫描电子显微镜(SEM)图像和不同碱金属阳离子掺杂全无机PSCs的伏安特性曲线^[65]. (b) 各种金属离子对Pb²⁺的部分取代(掺杂或合金化), 改善正交CsPbBr₃的热稳定性, 使α-CsPbI₃稳定化^[83]. 下图显示了Sn基全无机钙钛矿中随Br^–浓度变化的带隙变化曲线图: 从左到右为CsSnI₃, CsSnI₂Br, CsSnIBr₂和CsSnBr₃^[84]. (c) 在FTO / c-TiO₂/m-TiO₂基底上制备的不同镧系元素掺杂的钙钛矿薄膜的SEM图像: CsPbBr₃, Yb³⁺-CsPbBr₃, Er³⁺-CsPbBr₃, Ho³⁺-CsPbBr₃, Tb³⁺-CsPbBr₃, Sm³⁺-CsPbBr₃^[90]; (d)纯CsPbI₃和CsPbI_3–xCl_x的化学烧结薄膜的紫外-可见吸收光谱和Abs及PL (右侧, 吸收(细线)和光致发光(粗线))图谱^[94,95]; (e) CsPbI₃通过PEO进行相稳定的机制和薄膜制备流程^[99]

Fig. 3. (a) Scanning electron microscope (SEM) images of the CsPbBr₃, Cs_0.98Li_0.02PbBr₃, Cs_0.94Na_0.06PbBr₃, Cs_0.92K_0.08PbBr₃, and Cs_0.91Rb_0.09PbBr₃ films and J-V curves of different alkali metal cations doped PSCs under air mass 1.5 global^[65]. (b) Schematic representation showing partial substitution (doping or alloying) of Pb²⁺ by various metal ions, which can lead to stabilization of α-CsPbI₃ at room temperature and improved thermal stability of orthorhombic CsPbBr₃^[83]. The graphic is about band gap variation with respect to Br⁻ concentration in the Sn based all-inorganic perovskite: CsSnI₃, CsSnI₂Br, CsSnIBr₂ and CsSnBr₃ from left to right^[84]. (c) The top SEM images of as-prepared perovskite films with different Lanthanide-doping on FTO/c-TiO₂/m-TiO₂ substrates CsPbBr₃, Yb³⁺-CsPbBr₃, Er³⁺-CsPbBr₃, Ho³⁺-CsPbBr₃, Tb³⁺-CsPbBr₃, Sm³⁺-CsPbBr₃^[90]. (d) UV-vis absorbance spectra of chemically sintered thin films of pure CsPbI₃ and CsPbI_3−xCl_x, absorption spectra (thin lines) and photoluminescence (PL) spectra (thick lines) of CsPbX₃ samples^[94,95]. (e) PEO added in precursor colloidal solution to improve the stability of perovskite film and the fabrication process of CsPbI₃^[99].

下载: 全尺寸图片幻灯片

图 4 (a) α-CsPbI₃ QDs PCSs的结构和基于μGR/ CsPbI₃薄膜的PSCs的电荷传输过程和稳定机制的示意图^[113]; (b) 基于CsPbI₃钙钛矿纳米线的光电探测器装置的能带图, 其中铝和氧化铟锡(indium tin oxides, ITO)作为电极, 基于CsPbI₃钙钛矿纳米线的器件的示意图, 具有面积为0.0314 cm²的ITO的顶部圆形电极^[122]; (c) 合成2D超薄CsPbBr₃纳米片高倍放大SEM图像^[125]; (d) 分级界面的太阳能电池的结构示意图和SEM图像^[133]

Fig. 4. (a) Architecture of the completed α-CsPbI₃ device and the charge transport process and stabilization mechanism for the μGR/CsPbI₃ film based PSCs^[113]; (b) band diagram for CsPbI₃ perovskite nanowires (NWs)-based photodetector device and CsPbI₃ perovskite NWs based device with top circular electorode^[122]; (c) 2D-CsPbBr₃ nanosheets high-magnification SEM images^[125]; (d) schematic structures of devices without and with a graded interface and SEM images of CsPbBrI₂ film, CsPbBrI₂ NSs/CsPbBrI₂ film, CsPbBrI₂ QDs/CsPbBrI₂ film, and CsPbBrI₂ QDs/CsPbBrI₂ NSs/CsPbBrI₂ film^[133].

下载: 全尺寸图片幻灯片

图 5 (a) KPFM测量非老化和热老化的CsPbBr₃振幅, 晶界上的形貌和功函数信号^[135]; (b) CsPbI₃在5 kV, 1 nA和点1, 2和3的CL光谱下的SEM图像^[16]; (c)在光照射前后比较CsPbBr₃和MAPbBr₃之间的SEM图像的示意图^[15]; (d) CsPbI₃钙钛矿薄膜上的梯度Br掺杂和PTA有机阳离子表面钝化的示意图^[27]

Fig. 5. (a) KPFM measurement on the non-aged and thermally aged CsPbBr₃ amplitude, cross-sections of topography and work function signals over the grain boundary^[135]; (b) SEM image of CsPbI₃ under 5 kV, 1 nA, and CL spectra of points 1, 2 and 3 ^[16]; (c) schematic comparing SEM images between the CsPbBr₃ and MAPbBr₃ before and after illumination^[15]; (d) gradient Br doping and PTA organic cation surface passivation on CsPbI₃ perovskite thin film^[27].

下载: 全尺寸图片幻灯片

表 1 溶液法及其他方法全无机PSCs性能

Table 1. Performance of all inorganic perovskite solar cells fabricated by solution or other process.

电池结构	制备方法	V_OC/V	J_sc/mA·cm^–2	FF/%	PCE/%	参考文献
FTO/PEDOT:PSS/CsPbI₃/PCBM/Al	溶液法	~0.9	3		1.7	[26]
FTO/c-TiO₂/CsPbI₃/Spiro-OMeTAD/Au	溶液法	0.8	12		2.9	[26]
FTO/c-TiO₂/m-TiO₂/CsPbI₃/Spiro-OMeTAD/Au	溶液法	~0.6	8		1.3	[26]
FTO/c-TiO₂/CsPbI₃/CuI/Au	溶液法	0.89	16.02	56.59	8.07	[149]
FTO/c-TiO₂/CsPb_0.96Bi_0.04I₃/CuI/Au	溶液法	0.97	18.76	72.59	13.21	[149]
FTO/TiO₂/CsPbI₃/Spiro-OMeTAD/Ag	溶液法	0.66	11.92	52.47	4.13	[39]
FTO/c-TiO₂/CsPbI₃/Carbon	溶液法	0.67	14.31	48	4.65	[38]
FTO/c-TiO₂/m-TiO₂/CsPbI₃/Carbon	溶液法	0.58	13.74	44	3.48	[38]
FTO/TiO₂/AX-coatedCsPbI₃-QDs/Spiro-OMeTAD/MoO_x/Al	溶液法	1.16	15.24	76.63	13.43	[110]
FTO/TiO₂/CsPbI₃ QDs/Spiro-OMeTAD/MoO_x/Al	溶液法	1.23	13.47	65	10.77	[23]
MgF₂/FTO/c-TiO₂/m-TiO₂/CsPb_0.95Ca_0.05I₃/P3HT/Au	溶液法	0.95	17.9	80	13.5	[78]
ITO/PTAA/zwitterion-CsPb(I_0.98Cl_0.02)₃/PCBM/C₆₀/BCP/Al	溶液法	1.09	14.9	70	11.4	[150]
ITO/TiO₂/CsPbBr₃/Carbon	溶液法	0.64	5.3	64	3.9	[151]
FTO/TiO₂/CsPbI₂Br-0.02MnCl₂/PCBM/Ag	溶液法	1.172	14.37	80	13.47	[85]
FTO/TiO₂/CsPbI₂Br/PTAA/Au	溶液法	1.177	14.25	80.2	13.45	[77]
FTO/TiO₂/CsPbI₃ QDs/PTAA/Au	溶液法	1.192	11.75	78.3	10.97	[77]
FTO/c-TiO₂/CsPbI₃-0.05DETAI₃/P3HT/Au	溶液法	1.06	12.21	61	7.89	[101]
FTO/TiO₂/quasi-2D Cs_0.9PEA_0.1PbI₃/Spiro-OMeTAD/Au	溶液法	0.838	10.96	62	5.7	[128]
FTO/NiO_x/InCl₃:CsPbI₂Br/ZnO@C₆₀/Ag	溶液法	1.15	15.1	78	13.57	[91]
FTO/NiO_x/CsPbI₂Br/ZnO@C₆₀/Ag	溶液法	1.1	15.1	78	12.92	[91]
FTO/TiO₂/CsPbI₃/Carbon	溶液法	0.79	18.5	65	9.5	[37]
FTO/TiO₂/CsPbI₃ QDs/PTB7/MoO_x/Ag	溶液法	1.27	12.39	80	12.55	[112]
FTO/c-TiO₂/BA₂CsPb₂I₇/Spiro-OMeTAD/Au	溶液法	0.957	8.88	57	4.84	[127]
FTO/TiO₂/CsPb_0.995Mn_0.005I_1.01Br_1.99/Carbon	溶液法	0.99	13.15	57	7.36	[86]
FTO/bl-TiO₂/2 wt% Sn-TiO₂/Cs₂SnI₄Br₂/solid state Cs₂SnI₆ based HTM/LPAH	溶液法	0.563	6.22	57.7	2.025	[52]
FTO/TiO₂/CsPbI₂Br/CsPbI₃ QDs/PTAA/Au	溶液法	1.204	15.25	78.7	14.45	[77]
FTO/c-TiO₂/m-TiO₂/CsPbBr₃/MoS₂ QDs/Carbon	喷涂法	1.307	6.55	79.4	6.80	[152]
FTO/c-TiO₂/m-TiO₂/CsPbIBr₂/Spiro-OMeTAD/Au	喷涂法	1.121	7.9	70	6.2	[59]
FTO/SnO₂ QDs/CsPbBr₃/carbon	溶液法	1.572	7.68	75	9.15	[50]
ITO/PEDOT:PSS/CsPbBr₃/PCBM/Ag	溶液法	0.982	5.9	73.7	4.5	[135]
FTO/m-TiO₂/CsPbBr₃/CsBi_2/3Br₃/carbon	溶液法	1.594	7.75	80.9	10.0	[50]
FTO/SnO₂ QDs/CsPbBr₃/CsSnBr₃ QDs/carbon	溶液法	1.610	7.8	84.4	10.6	[50]
FTO/m-TiO₂/Cs₂AgBiBr₆/Spiro-MeOTAD/Ag	溶液法	0.98	3.93	63	2.43	[76]
FTO/TiO₂/PTABrCsPbI₃/Spiro-MeOTAD/Ag	溶液法	1.104	19.15	68.5	17.06	[27]
FTO/TiO₂/CsPbI₃/Spiro-MeOTAD/Ag	溶液法	1.051	18.89	68.5	13.61	[27]
PET/ITO/TiO₂/CsPb_0.96Bi_0.04I₃/Spiro-OMeTAD/Au	溶液-气相辅助法	1.05	15.11	72.32	11.47	[87]
ITO/TiO₂/CsPbI₃/P3HT/Au	气相法	1.063	13.8	71.6	10.5	[142]
ITO/TiO₂/CsPbI₃/Au	气相法	0.959	8.7	56	4.7	[46]
ITO/C₆₀/CsPbI₂Br/TAPC/MoO₃/Ag	气相法	1.15	15.2	67	11.7	[140]
FTO/TiO₂/CsPbI₃/P3HT/Ag	气相法	0.79	12..06	72	6.79	[146]

下载: 导出CSV

map

[1]	范伟利, 杨宗林, 张振雲, 齐俊杰 2018 67 228801 Google Scholar Fan W L, Yang Z L, Zhang Z Y, Qi J J 2018 Acta Phys. Sin. 67 228801 Google Scholar
[2]	Hu Q, Zhao L, Wu J, Gao K, Luo D, Jiang Y, Zhang Z, Zhu C, Schaible E, Hexemer A, Wang C, Liu Y, Zhang W, Grätzel M, Liu F, Russell T P, Zhu R, Gong Q 2017 Nat. Commun. 8 15688 Google Scholar
[3]	Luo D, Yang W, Wang Z, Sadhanala A, Hu Q, Su R, Shivanna R, Trindade G F, Watts J F, Xu Z, Liu T, Chen K, Ye F, Wu P, Zhao L, Wu J, Tu Y, Zhang Y, Yang X, Zhang W, Friend R H, Gong Q, Snaith H J, Zhu R 2018 Science 360 1442 Google Scholar
[4]	Chen K, Hu Q, Liu T, Zhao L, Luo D, Wu J, Zhang Y, Zhang W, Liu F, Russell T P, Zhu R, Gong Q 2016 Adv. Mater. 28 10718 Google Scholar
[5]	Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[6]	Kim H S, Lee C R, Im J H, Lee K B, Moehl T, Marchioro A, Moon S J, Humphry-Baker R, Yum J H, Moser J E, Gratzel M, Park N G 2012 Sci. Rep. 2 591 Google Scholar
[7]	NREL 2019 Best Research-Cell Efficiencies https://www.nrel.gov/pv/cell-efficiency.html [2019-03-12]
[8]	Chung I, Lee B, He J, Chang R P H, Kanatzidis M G 2012 Nature 485 486 Google Scholar
[9]	Chen Z, Wang J J, Ren Y, Yu C, Shum K 2012 Appl. Phys. Lett. 101 093901 Google Scholar
[10]	Zeng Q, Zhang X, Liu C, Feng T, Chen Z, Zhang W, Zheng W, Zhang H, Yang B 2019 Sol. RRL 3 1800239
[11]	Cui P, Wei D, Ji J, Song D, Li Y, Liu X, Huang J, Wang T, You J, Li M 2017 Sol. RRL 1 1600027 Google Scholar
[12]	Ahn N, Kwak K, Jang M S, Yoon H, Lee B Y, Lee J K, Pikhitsa P V, Byun J, Choi M 2016 Nat. Commun. 7 13422 Google Scholar
[13]	Park N G, Grätzel M, Miyasaka T, Zhu K, Emery K 2016 Nat. Energy 1 16152 Google Scholar
[14]	张翱陈, 闫君, 张春秀 2018 67 106701 Google Scholar Zhao A, Chen Y L, Yan J, Zhang C X 2018 Acta Phys. Sin. 67 106701 Google Scholar
[15]	Akbulatov A F, Luchkin S Y, Frolova L A, Dremova N N, Gerasimov K L, Zhidkov I S, Anokhin D V, Kurmaev E Z, Stevenson K J, Troshin P A 2017 J. Phys. Chem. Lett. 8 1211 Google Scholar
[16]	Xiao C, Li Z, Guthrey H, Moseley J, Yang Y, Wozny S, Moutinho H, To B, Berry J J, Gorman B, Yan Y, Zhu K, Al-Jassim M 2015 J. Phys. Chem. C 119 26904 Google Scholar
[17]	Liang J, Liu J, Jin Z 2017 Sol. RRL 1 1700086 Google Scholar
[18]	Zhou W, Zhao Y, Zhou X, Fu R, Li Q, Zhao Y, Liu K, Yu D, Zhao Q 2017 J. Phys. Chem. Lett. 8 4122 Google Scholar
[19]	Unger E L, Hoke E T, Bailie C D, Nguyen W H, Bowring A R, Heumüller T, Christoforo M G, McGehee M D 2014 Energy Environ. Sci. 7 3690 Google Scholar
[20]	Tress W, Marinova N, Moehl T, Zakeeruddin S M, Nazeeruddin M K, Grätzel M 2015 Energy Environ. Sci. 8 995 Google Scholar
[21]	Lau C F J, Zhang M, Deng X, Zheng J, Bing J, Ma Q, Kim J, Hu L, Green M A, Huang S, Ho-Baillie A 2017 ACS Energy Lett. 2 2319 Google Scholar
[22]	Lu C, Li H, Kolodziejski K, Dun C, Huang W, Carroll D, Geyer S M 2018 Nano Res. 11 762
[23]	Swarnkar A, Marshall A R, Sanehira E M, Chernomordik B D, Moore D T, Christians J A, Chakrabarti T, Luther J M 2016 Science 354 92 Google Scholar
[24]	Huang H, Chen B, Wang Z, Hung T F, Susha A S, Zhong H, Rogach A L 2016 Chem. Sci. 7 5699 Google Scholar
[25]	De Roo J, Ibanez M, Geiregat P, Nedelcu G, Walravens W, Maes J, Martins J C, van Driessche I, Kovalenko M V, Hens Z 2016 ACS Nano 10 2071 Google Scholar
[26]	Eperon G E, Paternò G M, Sutton R J, Zampetti A, Haghighirad A A, Cacialli F, Snaith H J 2015 J. Mater. Chem. A 3 19688 Google Scholar
[27]	Wang Y, Zhang T, Kan M, Zhao Y 2018 J. Am. Chem. Soc. 140 12345 Google Scholar
[28]	Lu M, Zhang X, Bai X, Wu H, Shen X, Zhang Y, Zhang W, Zheng W, Song H, Yu W W, Rogach A L 2018 ACS Energy Lett. 3 1571 Google Scholar
[29]	Fu L, Zhang Y, Chang B, Li B, Zhou S, Zhang L, Yin L 2018 J. Mater. Chem. A 6 13263 Google Scholar
[30]	Stoddard R J, Rajagopal A, Palmer R L, Braly I L, Jen A K Y, Hillhouse H W 2018 ACS Energy Lett. 3 1261 Google Scholar
[31]	Travis W, Glover E N K, Bronstein H, Scanlon D O, Palgrave R G 2016 Chem. Sci. 7 4548 Google Scholar
[32]	Luo P, Zhou Y, Zhou S, Lu Y, Xu C, Xia W, Sun L 2018 Chem. Eng. J. 343 146 Google Scholar
[33]	Zhang L, Li B, Yuan J, Wang M, Shen T, Huang F, Wen W, Cao G, Tian J 2018 J. Phys. Chem. Lett. 9 3646 Google Scholar
[34]	Li X, Yu D, Cao F, Gu Y, Wei Y, Wu Y, Song J, Zeng H 2016 Adv. Funct. Mater. 26 5903 Google Scholar
[35]	García de Arquer F P, Armin A, Meredith P, Sargent E H 2017 Nat. Rev. Mater. 2 16100 Google Scholar
[36]	Voznyy O, Sutherland B R, Ip A H, Zhitomirsky D, Sargent E H 2017 Nat. Rev. Mater. 2 17026 Google Scholar
[37]	Xiang S, Fu Z, Li W, Wei Y, Liu J, Liu H, Zhu L, Zhang R, Chen H 2018 ACS Energy Lett. 3 1824 Google Scholar
[38]	Liang J, Wang C, Zhao P, Lu Z, Ma Y, Xu Z, Wang Y, Zhu H, Hu Y, Zhu G, Ma L, Chen T, Tie Z, Liu J, Jin Z 2017 Nanoscale 9 11841 Google Scholar
[39]	Luo P, Xia W, Zhou S, Sun L, Cheng J, Xu C, Lu Y 2016 J. Phys. Chem. Lett. 7 3603 Google Scholar
[40]	Ramadan A J, Rochford L A, Fearn S, Snaith H J 2017 J. Phys. Chem. Lett. 8 4172 Google Scholar
[41]	Correa Baena J P, Steier L, Tress W, Saliba M, Neutzner S, Matsui T, Giordano F, Jacobsson T J, Srimath Kandada A R, Zakeeruddin S M, Petrozza A, Abate A, Nazeeruddin M K, Grätzel M, Hagfeldt A 2015 Energy Environ. Sci. 8 2928 Google Scholar
[42]	Wang P, Zhang X, Zhou Y, Jiang Q, Ye Q, Chu Z, Li X, Yang X, Yin Z, You J 2018 Nat. Commun. 9 2225 Google Scholar
[43]	Yu B, Zhang H, Wu J, Li Y, Li H, Li Y, Shi J, Wu H, Li D, Luo Y, Meng Q 2018 J. Mater. Chem. A 6 19810 Google Scholar
[44]	Zhu W, Zhang Q, Zhang C, Zhang Z, Chen D, Lin Z, Chang J, Zhang J, Hao Y 2018 ACS Appl. Energy Mater. 1 4991 Google Scholar
[45]	Liu C, Li W, Chen J, Fan J, Mai Y, Schropp R E I 2017 Nano Energy 41 75 Google Scholar
[46]	Ma Q, Huang S, Wen X, Green M A, Ho-Baillie A W Y 2016 Adv. Energy Mater. 6 1502202 Google Scholar
[47]	Sutton R J, Eperon G E, Miranda L, Parrott E S, Kamino B A, Patel J B, Hörantner M T, Johnston M B, Haghighirad A A, Moore D T, Snaith H J 2016 Adv. Energy Mater. 6 1502458 Google Scholar
[48]	Duan J, Zhao Y, He B, Tang Q 2018 Angew. Chem. Int. Ed. Engl. 57 3787 Google Scholar
[49]	Hoffman J B, Zaiats G, Wappes I, Kamat P V 2017 Chem. Mat. 29 9767 Google Scholar
[50]	Liu X, Tan X, Liu Z, Ye H, Sun B, Shi T, Tang Z, Liao G 2019 Nano Energy 56 184 Google Scholar
[51]	Zhao Y, Duan J, Yuan H, Wang Y, Yang X, He B, Tang Q 2019 Sol. RRL 3 1800284 Google Scholar
[52]	Lee B, Krenselewski A, Baik S I, Seidman D N, Chang R P H 2017 Sustain. Energy Fuels 1 710 Google Scholar
[53]	Song L, Wang W, Körstgens V, González D M, Yao Y, Minar N K, Feckl J M, Peters K, Bein T, Fattakhova-Rohlfing D, Santoro G, Roth S V, Müller-Buschbaum P 2016 Adv. Funct. Mater. 26 1498 Google Scholar
[54]	Su B, Caller-Guzman H A, Korstgens V, Rui Y, Yao Y, Saxena N, Santoro G, Roth S V, Muller-Buschbaum P 2017 ACS Appl. Mater. Inter. 9 43724 Google Scholar
[55]	Heo J H, Lee M H, Jang M H, Im S H 2016 J. Mater. Chem. A 4 17636 Google Scholar
[56]	Zheng Y, Kong J, Huang D, Shi W, McMillon-Brown L, Katz H E, Yu J, Taylor A D 2018 Nanoscale 10 11342 Google Scholar
[57]	Cheng J, Hu R, Meng X, Li Y, Yan X, Yang X, Liao X, Li L, Pei Q, Chong K B 2018 Sol. RRL 2 1800064 Google Scholar
[58]	Cheng J, Hu R, Wang Q, Zhang C, Xie Z, Long Z, Yang X, Li L 2015 Int. J. Photoenergy 2015 201472
[59]	Lau C F J, Deng X, Ma Q, Zheng J, Yun J S, Green M A, Huang S, Ho-Baillie A W Y 2016 ACS Energy Lett. 1 573 Google Scholar
[60]	Ruan W, Hu Y, Qiu T, Bai F, Zhang S, Xu F 2019 J. Phys. Chem. Solids 127 258 Google Scholar
[61]	Zhou H, Fan L, He G, Yuan C, Wang Y, Shi S, Sui N, Chen B, Zhang Y, Yao Q, Zhao J, Zhang X, Yin J 2018 RSC Adv. 8 29089 Google Scholar
[62]	Yang Z, Wang M, Li J, Dou J, Qiu H, Shao J 2018 ACS Appl. Mater. Inter. 10 26387 Google Scholar
[63]	Liao H, Guo S, Cao S, Wang L, Gao F, Yang Z, Zheng J, Yang W 2018 Adv. Opt. Mater. 6 1800346 Google Scholar
[64]	Wang Y, Zhu Y, Huang J, Cai J, Zhu J, Yang X, Shen J, Jiang H, Li C 2016 J. Phys. Chem. Lett. 7 4253 Google Scholar
[65]	Li Y, Duan J, Yuan H, Zhao Y, He B, Tang Q 2018 Sol. RRL 2 1800164 Google Scholar
[66]	Nam J K, Chai S U, Cha W, Choi Y J, Kim W, Jung M S, Kwon J, Kim D, Park J H 2017 Nano Lett. 17 2028 Google Scholar
[67]	Bu T, Liu X, Zhou Y, Yi J, Huang X, Luo L, Xiao J, Ku Z, Peng Y, Huang F, Cheng Y B, Zhong J 2017 Energy Environ. Sci. 10 2509 Google Scholar
[68]	Lee J H, Bristowe N C, Lee J H, Lee S H, Bristowe P D, Cheetham A K, Jang H M 2016 Chem. Mat. 28 4259 Google Scholar
[69]	Son D Y, Kim S G, Seo J Y, Lee S H, Shin H, Lee D, Park N G 2018 J. Am. Chem. Soc. 140 1358 Google Scholar
[70]	Krieg F, Ochsenbein S T, Yakunin S, Ten Brinck S, Aellen P, Suess A, Clerc B, Guggisberg D, Nazarenko O, Shynkarenko Y, Kumar S, Shih C J, Infante I, Kovalenko M V 2018 ACS Energy Lett. 3 641 Google Scholar
[71]	Yang D, Li X, Zeng H 2018 Adv. Mater. Inter. 5 1701662 Google Scholar
[72]	Kumar M H, Dharani S, Leong W L, Boix P P, Prabhakar R R, Baikie T, Shi C, Ding H, Ramesh R, Asta M, Graetzel M, Mhaisalkar S G, Mathews N 2014 Adv. Mater. 26 7122 Google Scholar
[73]	Xiang S, Li W, Wei Y, Liu J, Liu H, Zhu L, Chen H 2018 Nanoscale 10 9996 Google Scholar
[74]	Zhao S, Yamamoto K, Iikubo S, Hayase S, Ma T 2018 J. Phys. Chem. Solids 117 117 Google Scholar
[75]	Akkerman Q A, Meggiolaro D, Dang Z, de Angelis F, Manna L 2017 ACS Energy Lett. 2 2183 Google Scholar
[76]	Greul E, Petrus Michiel L, Binek A, Docampo P, Bein T 2017 J. Mater. Chem. A 5 19972 Google Scholar
[77]	Bian H, Bai D, Jin Z, Wang K, Liang L, Wang H, Zhang J, Wang Q, Liu S 2018 Joule 2 1500 Google Scholar
[78]	Lau C F J, Deng X, Zheng J, Kim J, Zhang Z, Zhang M, Bing J, Wilkinson B, Hu L, Patterson R, Huang S, Ho-Baillie A 2018 J. Mater. Chem. A 6 5580 Google Scholar
[79]	Yang R X, Skelton J M, da Silva E L, Frost J M, Walsh A 2017 J. Phys. Chem. Lett. 8 4720 Google Scholar
[80]	Ju M G, Dai J, Ma L, Zeng X C 2017 J. Am. Chem. Soc. 139 8038 Google Scholar
[81]	Noel N K, Stranks S D, Abate A, Wehrenfennig C, Guarnera S, Haghighirad A A, Sadhanala A, Eperon G E, Pathak S K, Johnston M B, Petrozza A, Herz L M, Snaith H J 2014 Energy Environ. Sci. 7 3061 Google Scholar
[82]	Hao F, Stoumpos C C, Chang R P, Kanatzidis M G 2014 J. Am. Chem. Soc. 136 8094 Google Scholar
[83]	Swarnkar A, Mir W J, Nag A 2018 ACS Energy Lett. 3 286 Google Scholar
[84]	Sabba D, Mulmudi H K, Prabhakar R R, Krishnamoorthy T, Baikie T, Boix P P, Mhaisalkar S, Mathews N 2015 J. Phys. Chem. C 119 1763 Google Scholar
[85]	Bai D, Zhang J, Jin Z, Bian H, Wang K, Wang H, Liang L, Wang Q, Liu S F 2018 ACS Energy Lett. 3 970 Google Scholar
[86]	Liang J, Liu Z, Qiu L, Hawash Z, Meng L, Wu Z, Jiang Y, Ono L K, Qi Y 2018 Adv. Energy Mater. 8 1800504 Google Scholar
[87]	Hu Y, Zhang S, Shu T, Qiu T, Bai F, Ruan W, Xu F 2018 J. Mater. Chem. A 6 20365 Google Scholar
[88]	Ge S, Wang Y, Xiang Z, Cui Y 2018 ACS Appl. Mater. Inter. 10 24620 Google Scholar
[89]	Jena A K, Kulkarni A, Sanehira Y, Ikegami M, Miyasaka T 2018 Chem. Mat. 31 6668
[90]	Duan J, Zhao Y, Yang X, Wang Y, He B, Tang Q 2018 Adv. Energy Mater. 8 1802346 Google Scholar
[91]	Liu C, Li W, Li H, Wang H, Zhang C, Yang Y, Gao X, Xue Q, Yip H L, Fan J, Schropp R E I, Mai Y 2019 Adv. Energy Mater. 9 1803572 Google Scholar
[92]	Liang J, Zhao P, Wang C, Wang Y, Hu Y, Zhu G, Ma L, Liu J, Jin Z 2017 J. Am. Chem. Soc. 139 14009 Google Scholar
[93]	Protesescu L, Yakunin S, Bodnarchuk M I, Krieg F, Caputo R, Hendon C H, Yang R X, Walsh A, Kovalenko M V 2015 Nano Lett. 15 3692 Google Scholar
[94]	Dastidar S, Egger D A, Tan L Z, Cromer S B, Dillon A D, Liu S, Kronik L, Rappe A M, Fafarman A T 2016 Nano Lett. 16 3563 Google Scholar
[95]	Diroll B T, Nedelcu G, Kovalenko M V, Schaller R D 2017 Adv. Funct. Mater. 27 1606750 Google Scholar
[96]	Mondal N, De A, Samanta A 2018 J. Phys. Chem. Lett. 9 3673 Google Scholar
[97]	Han G, Hadi H D, Bruno A, Kulkarni S A, Koh T M, Wong L H, Soci C, Mathews N, Zhang S, Mhaisalkar S G 2018 J. Phys. Chem. C 122 13884 Google Scholar
[98]	Zheng Y, Shi W, Kong J, Huang D, Katz H E, Yu J, Taylor A D 2017 Small Methods 1 1700244 Google Scholar
[99]	Jeong B, Han H, Choi Y J, Cho S H, Kim E H, Lee S W, Kim J S, Park C, Kim D, Park C 2018 Adv. Funct. Mater. 28 1706401 Google Scholar
[100]	Li B, Zhang Y, Fu L, Yu T, Zhou S, Zhang L, Yin L 2018 Nat. Commun. 9 1076 Google Scholar
[101]	Ding X, Chen H, Wu Y, Ma S, Dai S, Yang S, Zhu J 2018 J. Mater. Chem. A 6 18258 Google Scholar
[102]	Ke Y, Wang N, Kong D, Cao Y, He Y, Zhu L, Wang Y, Xue C, Peng Q, Gao F, Huang W, Wang J 2019 J. Phys. Chem. Lett. 10 380 Google Scholar
[103]	Zhang F, Kim D H, Zhu K 2018 Curr. Opin. Electr. 11 105
[104]	Heo D Y, Han S M, Woo N S, Kim Y J, Kim T Y, Luo Z, Kim S Y 2018 J. Phys. Chem. C 122 15903 Google Scholar
[105]	Zhao B, Jin S, Huang S, Liu N, Ma J Y, Xue D J, Han Q, Ding J, Ge Q Q, Feng Y, Hu J S 2018 J. Am. Chem. Soc. 140 11716 Google Scholar
[106]	Huang Y, Yin W J, He Y 2018 J. Phys. Chem. C 122 1345
[107]	Jiang Y, Yuan J, Ni Y, Yang J, Wang Y, Jiu T, Yuan M, Chen J 2018 Joule 2 1356 Google Scholar
[108]	Lin D, Zhang T, Wang J, Long M, Xie F, Chen J, Wu B, Shi T, Yan K, Xie W, Liu P, Xu J 2019 Nano Energy 59 619 Google Scholar
[109]	Nedelcu G, Protesescu L, Yakunin S, Bodnarchuk M I, Grotevent M J, Kovalenko M V 2015 Nano Lett. 15 5635 Google Scholar
[110]	Sanehira E M, Marshall A R, Christians J A, Harvey S P, Ciesielski P N, Wheeler L M, Schulz P, Lin L Y, Beard M C, Luther J M 2017 Sci. Adv. 3 eaao4204 Google Scholar
[111]	Zou C, Xi Y, Huang C Y, Keeler E G, Feng T, Zhu S, Pozzo L D, Lin L Y 2018 Adv. Opt. Mater. 6 1800324 Google Scholar
[112]	Yuan J, Ling X, Yang D, Li F, Zhou S, Shi J, Qian Y, Hu J, Sun Y, Yang Y, Gao X, Duhm S, Zhang Q, Ma W 2018 Joule 2 2450 Google Scholar
[113]	Wang Q, Jin Z, Chen D, Bai D, Bian H, Sun J, Zhu G, Wang G, Liu S F 2018 Adv. Energy Mater. 8 1800007 Google Scholar
[114]	Akkerman Q A, Gandini M, Di Stasio F, Rastogi P, Palazon F, Bertoni G, Ball J M, Prato M, Petrozza A, Manna L 2016 Nat. Energy 2 16194
[115]	Liao J Y, He J W, Xu H, Kuang D B, Su C Y 2012 J. Mater. Chem. 22 7910 Google Scholar
[116]	Wu W Q, Huang F, Chen D, Cheng Y B, Caruso R A 2015 Adv. Funct. Mater. 25 3264 Google Scholar
[117]	Xu Y F, Wu W Q, Rao H S, Chen H Y, Kuang D B, Su C Y 2015 Nano Energy 11 621 Google Scholar
[118]	Zhang D, Eaton S W, Yu Y, Dou L, Yang P 2015 J. Am. Chem. Soc. 137 9230 Google Scholar
[119]	Im J H, Luo J, Franckevičius M, Pellet N, Gao P, Moehl T, Zakeeruddin S M, Nazeeruddin M K, Grätzel M, Park N G 2015 Nano Lett. 15 2120 Google Scholar
[120]	Chen Z, Dong L, Tang H, Yu Y, Ye L, Zang J 2019 CrystEngComm 21 1389 Google Scholar
[121]	Chen G, Feng J, Gao H, Zhao Y, Pi Y, Jiang X, Wu Y, Jiang L 2019 Adv. Funct. Mater. 29 1808741 Google Scholar
[122]	Waleed A, Tavakoli M M, Gu L, Hussain S, Zhang D, Poddar S, Wang Z, Zhang R, Fan Z 2017 Nano Lett. 17 4951 Google Scholar
[123]	Chen K, Wu P, Yang W, Su R, Luo D, Yang X, Tu Y, Zhu R, Gong Q 2018 Nano Energy 49 411 Google Scholar
[124]	Zhang T, Dar M I, Li G, Xu F, Guo N, Grätzel M, Zhao Y 2017 Sci. Adv. 3 e1700841 Google Scholar
[125]	Song J, Xu L, Li J, Xue J, Dong Y, Li X, Zeng H 2016 Adv. Mater. 28 4861 Google Scholar
[126]	Li X, Yu D, Chen J, Wang Y, Cao F, Wei Y, Wu Y, Wang L, Zhu Y, Sun Z, Ji J, Shen Y, Sun H, Zeng H 2017 ACS Nano 11 2015 Google Scholar
[127]	Liao J F, Rao H S, Chen B X, Kuang D B, Su C Y 2017 J. Mater. Chem. A 5 2066 Google Scholar
[128]	Li F, Pei Y, Xiao F, Zeng T, Yang Z, Xu J, Sun J, Peng B, Liu M 2018 Nanoscale 10 6318 Google Scholar
[129]	Wang Y, Zhang T, Kan M, Li Y, Wang T, Zhao Y 2018 Joule 2 2065 Google Scholar
[130]	Zhang S, Yi C, Wang N, Sun Y, Zou W, Wei Y, Cao Y, Miao Y, Li R, Yin Y, Zhao N, Wang J, Huang W 2017 Adv. Mater. 29 1606600 Google Scholar
[131]	Chuang C H, Brown P R, Bulovic V, Bawendi M G 2014 Nat. Mater. 13 796 Google Scholar
[132]	Wang S, Sakurai T, Wen W, Qi Y 2018 Adv. Mater. Inter. 5 1800260 Google Scholar
[133]	Zhang J, Bai D, Jin Z, Bian H, Wang K, Sun J, Wang Q, Liu S F 2018 Adv. Energy Mater. 8 1703246 Google Scholar
[134]	Hirotsu S, Harada J, Iizumi M, Gesi K 1974 J. Phys. Soc. Jpn. 37 1393 Google Scholar
[135]	Luchkin S Y, Akbulatov A F, Frolova L A, Tsarev S A, Troshin P A, Stevenson K J 2017 Sol. Energy Mater. Sol. Cells 171 205 Google Scholar
[136]	Beal R E, Slotcavage D J, Leijtens T, Bowring A R, Belisle R A, Nguyen W H, Burkhard G F, Hoke E T, McGehee M D 2016 J. Phys. Chem. Lett. 7 746 Google Scholar
[137]	Klein-Kedem N, Cahen D, Hodes G 2016 Acc. Chem. Res. 49 347 Google Scholar
[138]	An R, Zhang F, Zou X, Tang Y, Liang M, Oshchapovskyy I, Liu Y, Honarfar A, Zhong Y, Li C, Geng H, Chen J, Canton S E, Pullerits T, Zheng K 2018 ACS Appl. Mater. Inter. 10 39222 Google Scholar
[139]	Malinkiewicz O, Yella A, Lee Y H, Espallargas G M, Graetzel M, Nazeeruddin M K, Bolink H J 2014 Nat. Photon. 8 128
[140]	Chen C Y, Lin H Y, Chiang K M, Tsai W L, Huang Y C, Tsao C S, Lin H W 2017 Adv. Mater. 29 1605290 Google Scholar
[141]	Chen C W, Kang H W, Hsiao S Y, Yang P F, Chiang K M, Lin H W 2014 Adv. Mater. 26 6647 Google Scholar
[142]	Frolova L A, Anokhin D V, Piryazev A A, Luchkin S Y, Dremova N N, Stevenson K J, Troshin P A 2017 J. Phys. Chem. Lett. 8 67 Google Scholar
[143]	Burwig T, Franzel W, Pistor P 2018 J. Phys. Chem. Lett. 9 4808 Google Scholar
[144]	Hu Y, Wang Q, Shi YL, Li M, Zhang L, Wang Z K, Liao LS 2017 J. Mater. Chem. C 5 8144 Google Scholar
[145]	Yonezawa K, Yamamoto K, Shahiduzzaman M, Furumoto Y, Hamada K, Ripolles T S, Karakawa M, Kuwabara T, Takahashi K, Hayase S, Taima T 2017 Jpn. J. Appl. Phys. 56 04CS11
[146]	Shahiduzzaman M, Yonezawa K, Yamamoto K, Ripolles T S, Karakawa M, Kuwabara T, Takahashi K, Hayase S, Taima T 2017 ACS Omega 2 4464 Google Scholar
[147]	Chen M, Ju M G, Carl A D, Zong Y, Grimm R L, Gu J, Zeng X C, Zhou Y, Padture N P 2018 Joule 2 558 Google Scholar
[148]	Moghe D, Wang L, Traverse C J, Redoute A, Sponseller M, Brown P R, Bulović V, Lunt R R 2016 Nano Energy 28 469 Google Scholar
[149]	Hu Y, Bai F, Liu X, Ji Q, Miao X, Qiu T, Zhang S 2017 ACS Energy Lett. 2 2219 Google Scholar
[150]	Wang Q, Zheng X, Deng Y, Zhao J, Chen Z, Huang J 2017 Joule 1 371 Google Scholar
[151]	Chang X, Li W, Zhu L, Liu H, Geng H, Xiang S, Liu J, Chen H 2016 ACS Appl. Mater. Inter. 8 33649 Google Scholar
[152]	Duan J, Dou D, Zhao Y, Wang Y, Yang X, Yuan H, He B, Tang Q 2018 Mater. Today Energy 10 146 Google Scholar
[153]	Gong J, Guo P, Benjamin S E, Van Patten P G, Schaller R D, Xu T 2018 J. Energy Chem. 27 1017 Google Scholar
[154]	Zheng G, Zhu C, Ma J, Zhang X, Tang G, Li R, Chen Y, Li L, Hu J, Hong J, Chen Q, Gao X, Zhou H 2018 Nat. Commun. 9 2793 Google Scholar
[155]	Zhou Y, Zhao Y 2019 Energy Environ. Sci. 12 1495 Google Scholar
[156]	Zhu C, Niu X, Fu Y, Li N, Hu C, Chen Y, He X, Na G, Liu P, Zai H, Ge Y, Lu Y, Ke X, Bai Y, Yang S, Chen P, Li Y, Sui M, Zhang L, Zhou H, Chen Q 2019 Nat. Commun. 10 815 Google Scholar
[157]	Ju M G, Chen M, Zhou Y, Garces H F, Dai J, Ma L, Padture N P, Zeng X C 2018 ACS Energy Lett. 3 297 Google Scholar
[158]	Huang L Y, Lambrecht W R L 2016 Phys. Rev. B 93 195211 Google Scholar
[159]	Ahmad W, Khan J, Niu G, Tang J 2017 Sol. RRL 1 1700048 Google Scholar
[160]	Wei S, Yang Y, Kang X, Wang L, Huang L, Pan D 2017 Inorg. Chem. 56 2596 Google Scholar
[161]	Shojaei F, Yin W J 2018 J. Phys. Chem. C 122 15214 Google Scholar
[162]	Huang J, Xiang S, Yu J, Li C Z 2019 Energy Environ. Sci. 12 929 Google Scholar
[163]	Dong S, Liu Y, Hong Z, Yao E, Sun P, Meng L, Lin Y, Huang J, Li G, Yang Y 2017 Nano Lett. 17 5140 Google Scholar
[164]	Gao K, Zhu Z, Xu B, Jo S B, Kan Y, Peng X, Jen A K 2017 Adv. Mater. 29 1703980 Google Scholar
[165]	Leijtens T, Bush K A, Prasanna R, McGehee M D 2018 Nat. Energy 3 828 Google Scholar

[1]	张雪, KimBokyung, LeeHyeonju, ParkJaehoon. 低温快速制备基于溶液工艺的高性能氧化铟薄膜及晶体管. , 2024, 73(9): 096802. doi: 10.7498/aps.73.20240082
[2]	隽珽, 邢家赫, 曾凡聪, 郑鑫, 徐琳. 基于SnO₂:DPEPO混合电子传输层的钙钛矿太阳能电池性能研究. , 2024, 73(19): 198401. doi: 10.7498/aps.73.20240827
[3]	仲婷婷, 郝会颖. 基于大气环境下全无机钙钛矿薄膜及碳基太阳能电池的组分调控和添加剂工程. , 2024, 73(23): 238101. doi: 10.7498/aps.73.20241439
[4]	刘恒, 李晔, 杜梦超, 仇鹏, 何荧峰, 宋祎萌, 卫会云, 朱晓丽, 田丰, 彭铭曾, 郑新和. AlGaN合金的原子层沉积及其在量子点敏化太阳能电池的应用. , 2023, 72(13): 137701. doi: 10.7498/aps.72.20230113
[5]	荆斌, 徐萌, 彭聪, 陈龙龙, 张建华, 李喜峰. 高负偏光照稳定性的溶液法像素级IZTO TFT. , 2022, 71(13): 138502. doi: 10.7498/aps.71.20220154
[6]	张翱, 张春秀, 张春梅, 田益民, 闫君, 孟涛. CH₃NH₃多聚体的形成对有机-无机杂化钙钛矿太阳能电池性能的影响. , 2021, 70(16): 168801. doi: 10.7498/aps.70.20210353
[7]	李家森, 梁春军, 姬超, 宫宏康, 宋奇, 张慧敏, 刘宁. 在空穴传输层聚(3-己基噻吩)中添加1, 8-二碘辛烷改善碳基钙钛矿太阳能电池的性能. , 2021, 70(19): 198403. doi: 10.7498/aps.70.20210586
[8]	于鹏, 曹盛, 曾若生, 邹炳锁, 赵家龙. 金属离子掺杂提高全无机钙钛矿纳米晶发光性质的研究进展. , 2020, 69(18): 187801. doi: 10.7498/aps.69.20200795
[9]	王继飞, 林东旭, 袁永波. 有机金属卤化物钙钛矿中的离子迁移现象及其研究进展. , 2019, 68(15): 158801. doi: 10.7498/aps.68.20190853
[10]	付鹏飞, 虞丹妮, 彭子健, 龚晋慷, 宁志军. 扭曲二维结构钝化的钙钛矿太阳能电池. , 2019, 68(15): 158802. doi: 10.7498/aps.68.20190306
[11]	夏俊民, 梁超, 邢贵川. 喷墨打印钙钛矿太阳能电池研究进展与展望. , 2019, 68(15): 158807. doi: 10.7498/aps.68.20190302
[12]	张世玉, 喻志农, 程锦, 吴德龙, 栗旭阳, 薛唯. 退火温度和Ga含量对溶液法制备InGaZnO薄膜晶体管性能的影响. , 2016, 65(12): 128502. doi: 10.7498/aps.65.128502
[13]	夏祥, 刘喜哲. CH3NH3I在制备CH3NH3PbI(3-x)Clx钙钛矿太阳能电池中的作用. , 2015, 64(3): 038104. doi: 10.7498/aps.64.038104
[14]	袁怀亮, 李俊鹏, 王鸣魁. 有机无机杂化固态太阳能电池的研究进展. , 2015, 64(3): 038405. doi: 10.7498/aps.64.038405
[15]	张丹霏, 郑灵灵, 马英壮, 王树峰, 卞祖强, 黄春辉, 龚旗煌, 肖立新. 影响杂化钙钛矿太阳能电池稳定性的因素探讨. , 2015, 64(3): 038803. doi: 10.7498/aps.64.038803
[16]	丁美斌, 娄朝刚, 王琦龙, 孙强. GaAs量子阱太阳能电池量子效率的研究. , 2014, 63(19): 198502. doi: 10.7498/aps.63.198502
[17]	柯少颖, 王茺, 潘涛, 何鹏, 杨杰, 杨宇. 渐变带隙氢化非晶硅锗薄膜太阳能电池的优化设计. , 2014, 63(2): 028802. doi: 10.7498/aps.63.028802
[18]	王海啸, 郑新和, 吴渊渊, 甘兴源, 王乃明, 杨辉. 1 eV吸收带边GaInAs/GaNAs超晶格太阳能电池的阱层设计. , 2013, 62(21): 218801. doi: 10.7498/aps.62.218801
[19]	罗翀, 孟志国, 王烁, 熊绍珍. 溶液法铝诱导晶化制备多晶硅薄膜. , 2009, 58(9): 6560-6565. doi: 10.7498/aps.58.6560
[20]	郝会颖, 孔光临, 曾湘波, 许颖, 刁宏伟, 廖显伯. 非晶/微晶相变域硅薄膜及其太阳能电池. , 2005, 54(7): 3327-3331. doi: 10.7498/aps.54.3327

计量

文章访问数: 30504
PDF下载量: 737
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板