辐照对掺Er硅酸盐玻璃吸收和发光特性的影响

盛于邦; 杨旅云; 栾怀训; 刘自军; 李进延; 戴能利

doi:10.7498/aps.61.116301

摘要

用传统的高温熔融法熔制了一系列掺Er硅酸盐玻璃, 并测试了这些样品经5 kGy 射线辐照前后紫外至近红外的吸收和荧光光谱. 实验结果表明, 辐致暗化效应使得玻璃材料中形成了大量色心, 导致在400 nm附近出现强吸收带, 其尾端延伸至近红外区. 辐照产生的新能带增加了基质与Er3+ 特定能级(如2H11/2, 4S3/2及4F9/2等) 之间的能量传递, 从而使辐照后的样品荧光寿命减小, 且在相同激发条件下荧光强度下降. 室温下辐照样品在荧光测试过程中出现了漂白现象.

关键词:

Abstract

A series of Er-doped silicate glasses is prepared by a conventional melting method under normal processing conditions, and the effects of gamma-ray radiation on absorption and emission properties of all samples are investigated. The radiation-induced darkening causes a strong broad optical absorption band that has a maximum around 400 nm and extends to the near infrared region. The point defects generated in the silicate matrix by irradiation around the Er3+ ion favor the activation of non-radiative relaxation channels thus modifying the photoluminescence quantum efficiency from specific excited levels, such as those emitting at 520 and 650 nm. Photobleaching effects are observed in Er-doped silicate glasses pumped by 980 nm LD at room temperature.

Keywords:

作者及机构信息

1.
华中科技大学光电子科学与工程学院, 武汉光电国家实验室(筹), 武汉 430074

基金项目: 国家高技术研究发展计划(批准号: 2011AA030201)资助的课题.

Authors and contacts

1.
College of Optoelectronic Science and Engineering, Huazhong University of Science and Technology, Wuhan National Laboratory for Optoelectronics, Wuhan 430074, China

Funds: Project supported by the National High Technology Research and Development Program of China (Grant No. 2011AA030201).

参考文献

[1]	Miniscalco W J 1991 J. Lightwave Tech. 9 234
[2]	Zotov K V, Likhachev M E, Tomashuk A L, Bubnov M M, Yashkov M V, Guryanov A N 2007 Quantum Electron. 37 946
[3]	Fox B P, Simmons-Potter K, Thomes W J, Kliner D 2010 IEEE Trans. Nucl. Sci. 57 1618
[4]	Wilson K, Enoch M 2000 IEEE Commun. Mag. 38 134
[5]	Ma J, Li M, Tan L, Zhou Y, Yu S, Ran Q 2009 Opt. Express 17 15571
[6]	Wysocki P F, Digonnet M J F, Kim B Y, Shaw H J 1994 J. Lightwave Tech. 12 550
[7]	Lewis R, Sikora E, Wright J V, West R H, Dowling S 1992 Electron. Lett. 28 1589
[8]	Williams G M, Putnam M A, Askins C G, Gingerich M E, Friebele E J 1992 Electron. Lett. 28 1816
[9]	Fukuda C, Chigusa Y, Kashiwada T, Onishi M, Kanamori H, Okamoto S 1994 Electron. Lett. 30 1342
[10]	Xiao Z Y, Wang T Y, Luo W Y, Wang Z H 2008 Acta Phys. Sin. 57 2273 (in Chinese) [肖中银, 王廷云, 罗文芸, 王子华 2008 57 2273]
[11]	Henschel H, Kohn O, Schmidt H U, Kirchof J, Unger S 1998 IEEE Trans. Nucl. Sci. 45 1552
[12]	Caussanel M, Gilard O, Sotom M, Signoret P, Gasiot J 2005 Electron. Lett. 41 168
[13]	Tortech B, Ouerdane Y, Girard S, Meunier J P, Boukenter A, Robin T, Cadier B, Crochet P 2009 J. Non-Cryst. Solids 355 1085
[14]	Raghavachari K, Ricci D, Pacchioni G 2002 J. Chem. Phys. 116 825
[15]	Skuja L, Hirano M, Hosono H, Kajihara K 2005 Phys. Status Solidi C 2 15
[16]	Jiang X W, Qiu J R 2001 Acta Phys. Sin. 50 871 (in Chinese) [姜雄伟, 邱建荣 2001 50 871]
[17]	Xiao Z Y, Luo W Y, Wang T Y 2007 Acta Phys. Sin. 56 2731 (in Chinese) [肖中银, 罗文芸, 王廷云 2007 56 2731]
[18]	Griscom D L 1991 J. Ceram. Soc. Japan 99 923
[19]	Raghavachari K, Pacchioni G 2001 J. Chem. Phys. 114 4657
[20]	Girard S, Baggio J, Bisutti J 2006 IEEE Trans. Nucl. Sci. 53 3750
[21]	Dai S X, Xu T F, Nie Q H, Shen X, Zhang J J, Hu L L 2006 Acta Phys. Sin. 55 1479 (in Chinese) [戴世勋, 徐铁峰, 聂秋华, 沈祥, 张军杰, 胡丽丽 2006 55 1479]
[22]	Zhao L J, Sun L D, Xu J J, Zhang G Y 2001 Acta Phys. Sin. 50 63 (in Chinese) [赵丽娟, 孙聆东, 许京军, 张光寅 2001 50 63]
[23]	Han Y L, Xiao W, Yi X S, Zhang Y C 2008 Infrared Laser Eng. 37 128 (in Chinese) [韩艳玲, 肖文, 伊小素, 张运春 2008 红外与激光工程 37 128]

施引文献

[1]	Miniscalco W J 1991 J. Lightwave Tech. 9 234
[2]	Zotov K V, Likhachev M E, Tomashuk A L, Bubnov M M, Yashkov M V, Guryanov A N 2007 Quantum Electron. 37 946
[3]	Fox B P, Simmons-Potter K, Thomes W J, Kliner D 2010 IEEE Trans. Nucl. Sci. 57 1618
[4]	Wilson K, Enoch M 2000 IEEE Commun. Mag. 38 134
[5]	Ma J, Li M, Tan L, Zhou Y, Yu S, Ran Q 2009 Opt. Express 17 15571
[6]	Wysocki P F, Digonnet M J F, Kim B Y, Shaw H J 1994 J. Lightwave Tech. 12 550
[7]	Lewis R, Sikora E, Wright J V, West R H, Dowling S 1992 Electron. Lett. 28 1589
[8]	Williams G M, Putnam M A, Askins C G, Gingerich M E, Friebele E J 1992 Electron. Lett. 28 1816
[9]	Fukuda C, Chigusa Y, Kashiwada T, Onishi M, Kanamori H, Okamoto S 1994 Electron. Lett. 30 1342
[10]	Xiao Z Y, Wang T Y, Luo W Y, Wang Z H 2008 Acta Phys. Sin. 57 2273 (in Chinese) [肖中银, 王廷云, 罗文芸, 王子华 2008 57 2273]
[11]	Henschel H, Kohn O, Schmidt H U, Kirchof J, Unger S 1998 IEEE Trans. Nucl. Sci. 45 1552
[12]	Caussanel M, Gilard O, Sotom M, Signoret P, Gasiot J 2005 Electron. Lett. 41 168
[13]	Tortech B, Ouerdane Y, Girard S, Meunier J P, Boukenter A, Robin T, Cadier B, Crochet P 2009 J. Non-Cryst. Solids 355 1085
[14]	Raghavachari K, Ricci D, Pacchioni G 2002 J. Chem. Phys. 116 825
[15]	Skuja L, Hirano M, Hosono H, Kajihara K 2005 Phys. Status Solidi C 2 15
[16]	Jiang X W, Qiu J R 2001 Acta Phys. Sin. 50 871 (in Chinese) [姜雄伟, 邱建荣 2001 50 871]
[17]	Xiao Z Y, Luo W Y, Wang T Y 2007 Acta Phys. Sin. 56 2731 (in Chinese) [肖中银, 罗文芸, 王廷云 2007 56 2731]
[18]	Griscom D L 1991 J. Ceram. Soc. Japan 99 923
[19]	Raghavachari K, Pacchioni G 2001 J. Chem. Phys. 114 4657
[20]	Girard S, Baggio J, Bisutti J 2006 IEEE Trans. Nucl. Sci. 53 3750
[21]	Dai S X, Xu T F, Nie Q H, Shen X, Zhang J J, Hu L L 2006 Acta Phys. Sin. 55 1479 (in Chinese) [戴世勋, 徐铁峰, 聂秋华, 沈祥, 张军杰, 胡丽丽 2006 55 1479]
[22]	Zhao L J, Sun L D, Xu J J, Zhang G Y 2001 Acta Phys. Sin. 50 63 (in Chinese) [赵丽娟, 孙聆东, 许京军, 张光寅 2001 50 63]
[23]	Han Y L, Xiao W, Yi X S, Zhang Y C 2008 Infrared Laser Eng. 37 128 (in Chinese) [韩艳玲, 肖文, 伊小素, 张运春 2008 红外与激光工程 37 128]

[1]	程大钊, 刘彩艳, 张超然, 屈佳辉, 张静. 中子辐照奥氏体不锈钢晶内/晶间孔隙形貌演化的相场模拟. , 2024, 73(22): 224601. doi: 10.7498/aps.73.20241353
[2]	曹涧秋, 周尚德, 刘鹏飞, 黄值河, 王泽锋, 司磊, 陈金宝. 辐照效应对于掺镱光纤放大器模式不稳定阈值影响的理论研究. , 2024, 73(20): 204202. doi: 10.7498/aps.73.20240816
[3]	李奋飞, 周晓燕, 张魁宝, 石兆华, 陈进湛, 叶鑫, 吴卫东, 李波. 中子辐照对掺镱光纤材料光学特性的影响. , 2021, 70(19): 190201. doi: 10.7498/aps.70.20210083
[4]	张强强, 胡建勇, 景明勇, 李斌, 秦成兵, 李耀, 肖连团, 贾锁堂. 单光子调制频谱用于量子点荧光寿命动力学的研究. , 2019, 68(1): 017803. doi: 10.7498/aps.68.20181797
[5]	乔志星, 秦成兵, 贺文君, 弓亚妮, 张晓荣, 张国峰, 陈瑞云, 高岩, 肖连团, 贾锁堂. 通过光致还原调制氧化石墨烯寿命并用于微纳图形制备. , 2018, 67(6): 066802. doi: 10.7498/aps.67.20172331
[6]	黄宏琪, 赵楠, 陈瑰, 廖雷, 刘自军, 彭景刚, 戴能利. γ射线辐照对掺Yb光纤材料性能的影响. , 2014, 63(20): 200201. doi: 10.7498/aps.63.200201
[7]	张明兰, 杨瑞霞, 李卓昕, 曹兴忠, 王宝义, 王晓晖. GaN厚膜中的质子辐照诱生缺陷研究. , 2013, 62(11): 117103. doi: 10.7498/aps.62.117103
[8]	沈应龙, 唐春梅, 盛秋春, 刘双, 李文涛, 王龙飞, 陈丹平. 铈铕共掺高钆氧化物玻璃的发光性能及能量传递效应. , 2013, 62(11): 117803. doi: 10.7498/aps.62.117803
[9]	万文博, 华灯鑫, 乐静, 刘美霞, 曹宁. 激光诱导叶绿素荧光寿命的测量及其特性分析. , 2013, 62(19): 190601. doi: 10.7498/aps.62.190601
[10]	卢喜瑞, 崔春龙, 张东, 陈梦君, 杨岩凯. 锆英石的抗γ射线辐照能力和Rietveld结构精修. , 2011, 60(7): 078901. doi: 10.7498/aps.60.078901
[11]	肖志强, 李蕾蕾, 张波, 徐静, 陈正才. 基于SOI技术的单层多晶EEPROM和SONOS EEPROM抗总剂量辐照特性研究. , 2011, 60(2): 028502. doi: 10.7498/aps.60.028502
[12]	李蕾蕾, 于宗光, 肖志强, 周昕杰. SOI SONOS EEPROM 总剂量辐照阈值退化机理研究. , 2011, 60(9): 098502. doi: 10.7498/aps.60.098502
[13]	喻军, 周朋, 赵衡煜, 吴锋, 夏海平, 苏良碧, 徐军. γ射线辐照诱导Bi:α-BaB2O4单晶近红外宽带发光的研究. , 2010, 59(5): 3538-3541. doi: 10.7498/aps.59.3538
[14]	彭绍泉, 杜磊, 庄奕琪, 包军林, 何亮, 陈伟华. 基于辐照前1/f噪声的金属-氧化物-半导体场效应晶体管辐照退化模型. , 2008, 57(8): 5205-5211. doi: 10.7498/aps.57.5205
[15]	丁君, 杨秋红, 唐在峰, 徐军, 苏良碧. Er3+/Yb3+共掺的氧化镧钇透明陶瓷的光谱性能研究. , 2007, 56(4): 2207-2211. doi: 10.7498/aps.56.2207
[16]	刘立新, 屈军乐, 林子扬, 陈丹妮, 许改霞, 胡涛, 郭宝平, 牛憨笨. 双光子激发时间分辨荧光光谱测量技术. , 2006, 55(12): 6281-6286. doi: 10.7498/aps.55.6281
[17]	林子扬, 付哲, 刘立新, 胡涛, 屈军乐, 郭宝平, 牛憨笨. 双光子阵列点激发同时多维荧光信息的处理. , 2006, 55(12): 6701-6707. doi: 10.7498/aps.55.6701
[18]	王雪俊, 夏海平. Bi离子掺杂GeO2-Al2O3-M(M=Na2O，BaO，Y2O3)玻璃的光学性质. , 2006, 55(10): 5263-5267. doi: 10.7498/aps.55.5263
[19]	苗壮, 李善锋, 张庆瑜. Y共掺对掺Er硅酸盐玻璃光致荧光及荧光寿命的影响. , 2006, 55(8): 4321-4326. doi: 10.7498/aps.55.4321
[20]	张可言. 金属材料在中强度激光辐照下的相变速度研究. , 2004, 53(6): 1815-1819. doi: 10.7498/aps.53.1815

计量

文章访问数: 6954
PDF下载量: 720
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板