Quantum oscillation phenomena in low-dimensional superconductors

Bi Xiang-Yu Huang Jun-Wei Qin Feng Qiu Cai-Yu Yuan Hong-Tao

Citation:

Quantum oscillation phenomena in low-dimensional superconductors

Bi Xiang-Yu, Huang Jun-Wei, Qin Feng, Qiu Cai-Yu, Yuan Hong-Tao
PDF
HTML
Get Citation
  • Low-dimensional superconductor serves as an excellent platform for investigating emergent superconducting quantum oscillation phenomena. The low-dimensional natures of these materials, originating from the finite size which is comparable with the superconducting coherence length, indicate that the corresponding physical properties will be constrained by quantum confinement effects. Importantly, some of the frontiers and hot issues in low-dimensional superconductors, including the anomalous metal state during the superconductor-insulator transition, spin-triplet pairing mechanism in superconductors, thermal-excited and electrical current-excited vortex dynamics in superconductors, and the “charge-vortex duality” in quantum dot materials and superconducting nanowires, are strongly correlated with the superconducting quantum oscillation effects. In recent years, all the above-mentioned topics have achieved breakthroughs based on the studies of superconducting quantum oscillation effects in low-dimensional superconductors. Generally, the periodicity and amplitude of the oscillation can clearly demonstrate the relation between the geometric structure of superconductors and various superconducting mechanisms. In particular, superconducting quantum oscillation phenomena are always correlated with the quantization of magnetic fluxoids and their dynamics, the pairing mechanism of superconducting electrons, and the excitation and fluctuation of superconducting systems.In this review article, three types of typical superconducting quantum oscillation effects observed in low-dimensional superconductors will be discussed from the aspects of research methods, theoretical expectations, and experimental results. a) The Little-Parks effect is the superconducting version of the Aharonov-Bohm effect, whose phase, amplitude and period are all helpful in studying superconductivity: the phase reflects the pairing mechanism in superconductors, the amplitude can be used for investigating the anomalous metal state, and the period provides the information about the sample geometry. b) The vortex motion effect is excited by thermal fluctuation or electrical current, and the corresponding oscillation phenomena show distinct temperature-dependent amplitudes compared with the Little-Parks effect. c) The Weber blockade effect originates from the magnetic flux moving across the superconducting nanowire, and such an effect provides a unique nonmonotonic critical current $ {I}_{\mathrm{C}} $ under a magnetic field in $I\text{-}V$ characteristics. The prospects of the above-mentioned quantum oscillation effects of low-dimensional superconductors for applications are also discussed at the end of this review, including quantum computing, device physics and low-temperature physics.
      Corresponding author: Yuan Hong-Tao, htyuan@nju.edu.cn
    • Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 51861145201, 91750101, 21733001, 52072168).
    [1]

    Tinkham M 2004 Introduction to Superconductivity (2nd Ed.) (New York: Courier Corporation)

    [2]

    张裕恒 2009 超导物理 (第三版) (合肥: 中国科学技术大学出版社)

    Zhang Y H 2009 Physics of Superconductivity (3rd Ed.) (Hefei: University of Science and Technology of China Press) (in Chinese)

    [3]

    Ginzburg V L, Landau L D 1950 Zh. Eksp. Teor. Fiz. 20 1064

    [4]

    Berezinskii, V L 1972 Sov. Phys. JETP 34 610

    [5]

    Kosterlitz J M, Thouless D J 1973 J. Phys. C 6 1181Google Scholar

    [6]

    Cao Y, Fatemi V, Fang S, Watanabe K, Taniguchi T, Kaxiras E, Jarillo-Herrero P 2018 Nature 556 43Google Scholar

    [7]

    Park J M, Cao Y, Watanabe K, Taniguchi T, Jarillo-Herrero P 2021 Nature 590 249Google Scholar

    [8]

    Xing Y, Zhang H M, Fu H L, Liu H, Sun Y, Peng J P, Wang F, Lin X, Ma X C, Xue Q K, Wang J, Xie X C 2015 Science 350 542Google Scholar

    [9]

    Liu Y, Wang Z, Shan P, Tang Y, Liu C, Chen C, Xing Y, Wang Q, Liu H, Lin X, Xie X C, Wang J 2019 Nat. Commun. 10 3633Google Scholar

    [10]

    Liu Y, Qi S, Fang J, Sun J, Liu C, Liu Y, Qi J, Xing Y, Liu H, Lin X, Wang L, Xue Q K, Xie X C, Wang J 2021 Phys. Rev. Lett. 127 137001Google Scholar

    [11]

    Bert J A, Kalisky B, Bell C, Kim M, Hikita Y, Hwang H Y, Moler K A 2011 Nat. Phys. 7 767Google Scholar

    [12]

    Liu C, Yan X, Jin D, Ma Y, Hsiao H W, Lin Y, Bertz-Sullivan T M, Zhou X J, Pearson J, Fisher B, Jiang J A, Han W, Zuo J M, Wen J G, Fong D D, Sun J R, Zhou H, Bhattacharya A 2021 Science 371 716Google Scholar

    [13]

    Saito Y, Nakamura Y, Bahramy M S, Kohama Y, Ye J, Kasahara Y, Nakagawa Y, Onga M, Tokunaga M, Nojima T, Yanase Y, Iwasa Y 2016 Nat. Phys. 12 144Google Scholar

    [14]

    Xi X, Wang Z, Zhao W, Park J H, Law K T, Berger H, Forró L, Shan J, Mak K F 2016 Nat. Phys. 12 139Google Scholar

    [15]

    Sohn E, Xi X, He W Y, Jiang S, Wang Z, Kang K, Park J H, Berger H, Forró L, Law K T, Shan J, Mak K F 2018 Nat. Mat. 17 504Google Scholar

    [16]

    Cleuziou J P, Wernsdorfer W, Bouchiat V, Ondarçuhu T, Monthioux M 2006 Nat. Nanotechnol. 1 53Google Scholar

    [17]

    Qin F, Shi W, Ideue T, Yoshida M, Zak A, Tenne R, Kikitsu T, Inoue D, Hashizume D, Iwasa Y 2017 Nat. Commun. 8 14465Google Scholar

    [18]

    Morgan-Wall T 2015 Ph. D. Dissertation (Baltimore: Johns Hopkins University)

    [19]

    Cohen R W, Abeles B 1968 Phys. Rev. 168 444Google Scholar

    [20]

    Morgan-Wall T, Leith B, Hartman N, Rahman A, Marković N 2015 Phys. Rev. Lett. 114 077002Google Scholar

    [21]

    Perali A, Pieri P, Strinati G C 2004 Phys. Rev. Lett. 93 100404Google Scholar

    [22]

    Nakagawa Y, Kasahara Y, Nomoto T, Arita R, Nojima T, Iwasa Y 2021 Science 372 190Google Scholar

    [23]

    He Q L, Liu H, He M, Lai Y H, He H, Wang G, Law K T, Lortz R, Wang J, Sou I K 2014 Nat. Commun. 5 4247Google Scholar

    [24]

    Langer J S, Ambegaokar V 1967 Phys. Rev. 164 498Google Scholar

    [25]

    McCumber D E, Halperin B I 1970 Phys. Rev. B 1 1054Google Scholar

    [26]

    Rogachev A, Bollinger A T, Bezryadin A 2005 Phys. Rev. Lett. 94 017004Google Scholar

    [27]

    Youn S J, Fischer M H, Rhim S H, Sigrist M, Agterberg D F 2012 Phys. Rev. B 85 220505(RGoogle Scholar

    [28]

    Bauer E, Sigrist M (Eds.) 2012 Non-Centrosymmetric Superconductors: Introduction and Overview (Vol. 847) (London: Springer Science & Business Media)

    [29]

    Lu J M, Zheliuk O, Leermakers I, Yuan N F, Zeitler U, Law K T, Ye J T 2015 Science 350 1353Google Scholar

    [30]

    Mackenzie A P, Maeno Y 2003 Rev. Mod. Phys. 75 657Google Scholar

    [31]

    Xu Y, Sheng Y, Yang Y F 2019 Phys. Rev. Lett. 123 217002Google Scholar

    [32]

    de la Barrera S C, Sinko M R, Gopalan D P, Sivadas N, Seyler K L, Watanabe K, Taniguchi T, Tsen A W, Xu X D, Xiao D, Hunt B M 2018 Nat. Commun. 9 1427Google Scholar

    [33]

    Monthoux P, Lonzarich G G 1999 Phys. Rev. B 59 14598Google Scholar

    [34]

    Maier T, Jarrell M, Pruschke T, Keller J 2000 Phys. Rev. Lett. 85 1524Google Scholar

    [35]

    Maier T A, Jarrell M, Schulthess T C, Kent P R C, White J B 2005 Phys. Rev. Lett. 95 237001Google Scholar

    [36]

    Lee P A, Nagaosa N, Wen X G 2006 Rev. Mod. Phys. 78 17Google Scholar

    [37]

    Hashimoto M, Vishik I M, He R H, Devereaux T P, Shen Z X 2014 Nat. Phys. 10 483Google Scholar

    [38]

    Hashimoto M, Nowadnick E A, He R H, Vishik I M, Moritz B, He Y, Tanaka K, Moore R G, Lu D, Yoshida Y, Ishikado M, Sasagawa T, Fujita K, Ishida S, Uchida S, Eisaki H, Hussain Z, Devereaux T P, Shen Z X 2015 Nat. Mat. 14 37Google Scholar

    [39]

    Yang C, Liu Y, Wang Y, Feng L, He Q, Sun J, Tang Y, Wu C, Xiong J, Zhang W, Lin X, Yao H, Liu H, Fernandes G, Xu J, Valles J M Jr., Wang J, Li Y 2019 Science 366 1505Google Scholar

    [40]

    Dobrovolskiy O V, Vodolazov D Y, Porrati F, Sachser R, Bevz V M, Mikhailov M Y, Chumak A V, Huth M 2020 Nat. Commun. 11 3291Google Scholar

    [41]

    Schmid A, Hauger W 1973 J. Low Temp. Phys. 11 667Google Scholar

    [42]

    Blatter G, Feigel'man M V, Geshkenbein V B, Larkin A I, Vinokur V M 1994 Rev. Mod. Phys. 66 1125Google Scholar

    [43]

    Feigel’man M V, Vinokur V M 1990 Phys. Rev. B 41 8986Google Scholar

    [44]

    Little W A, Parks R D 1962 Phys. Rev. Lett. 9 9Google Scholar

    [45]

    Parks R D, Little W A 1964 Phys. Rev. 133 97Google Scholar

    [46]

    Moshchalkov V V, Gielen L, Strunk C, Jonckheere R, Qiu X, van Haesendincj C, Bruynseraede Y 1995 Nature 373 319Google Scholar

    [47]

    Qin F, Ideue T, Shi W, Zhang X X, Yoshida M, Zak A, Tenne R, Kikitsu T, Inoue D, Hashizume D, Iwasa Y 2018 Nano Lett. 18 6789Google Scholar

    [48]

    Kirtley J R, Tsuei C C, Kogan V G, Clem J R, Raffy H, Li Z Z 2003 Phys. Rev. B 68 214505Google Scholar

    [49]

    Sochnikov I, Shaulov A, Yeshurun Y, Logvenov G, Božović I 2010 Phys. Rev. B 82 094513Google Scholar

    [50]

    Berdiyorov G R, Milošević M V, Latimer M L, Xiao Z L, Kwok W K, Peeters F M 2012 Phys. Rev. Lett. 109 057004Google Scholar

    [51]

    Pekker D, Refael G, Goldbart P M 2011 Phys. Rev. Lett. 107 017002Google Scholar

    [52]

    Johansson A, Sambandamurthy G, Shahar D, Jacobson N, Tenne R 2005 Phys. Rev. Lett. 95 116805Google Scholar

    [53]

    Simoni G D, Paolucci F, Solinas P, Strambini E, Giazotto F 2018 Nat. Nanotechnol. 13 802Google Scholar

    [54]

    Geim A K, Grigorieva I V 2013 Nature 499 419Google Scholar

    [55]

    Novoselov K S, Mishchenko O A, Carvalho O A, Neto A C 2016 Science 353 461Google Scholar

    [56]

    Liu Y, Weiss N O, Duan X, Cheng H C, Huang Y, Duan X 2016 Nat. Rev. Mater. 1 16042Google Scholar

    [57]

    Yankowitz M, Chen S, Polshyn H, Zhang Y, Watanabe K, Taniguchi T, Graf D, Young A F, Dean C R 2019 Science 363 1059Google Scholar

    [58]

    Buzdin A I 2005 Rev. Mod. Phys. 77 935Google Scholar

    [59]

    Ryazanov V V, Oboznov V A, Rusanov A Y, Veretennikov A V, Golubov A A, Aarts J 2001 Phys. Rev. Lett. 86 2427Google Scholar

    [60]

    Kezilebieke S, Silveira O J, Huda M N, Vaňo V, Aapro M, Ganguli S C, Lahtinen J, Mansell R, van Dijken S, Foster A S, Liljeroth P 2021 Adv. Mat. 33 2006850Google Scholar

    [61]

    Wen H H 2021 Acta Phys. Sin. 70 017405Google Scholar

    [62]

    Bardeen J, Cooper L N, Schrieffer J R 1957 Phys. Rev. 108 1175Google Scholar

    [63]

    Pearl J 1964 Appl. Phys. Lett. 5 65Google Scholar

    [64]

    Doh Y J, van Dam J A, Roest A L, Bakker E P A M, Kouwenhoven L P, de Franceschi S 2005 Science 309 272Google Scholar

    [65]

    Paolucci F, de Simoni G, Strambini E, Solinas P, Giazotto F 2018 Nano Lett. 18 4195Google Scholar

    [66]

    Li Y, Xu X, Lee M H, Chu M W, Chien C L 2019 Science 366 238Google Scholar

    [67]

    Aharonov Y, Bohm D 1959 Phys. Rev. 115 485Google Scholar

    [68]

    Peshkin M, Tonomura A 1989 The Aharonov-Bohm Effect (Vol. 340) (Berlin: Springer)

    [69]

    Tinkham M 1964 Rev. Mod. Phys. 36 268Google Scholar

    [70]

    Barash Y S 2008 Phys. Rev. Lett. 100 177003Google Scholar

    [71]

    Juricic V, Herbut I F, Tesanovic Z 2008 Phys. Rev. Lett. 100 187006Google Scholar

    [72]

    Loder F, Kampf A P, Kopp T, Mannhart J, Schneider C W, Barash Y S 2008 Nat. Phys. 4 112Google Scholar

    [73]

    Berg E, Fradkin E, Kivelson S A 2009 Nat. Phys. 5 830Google Scholar

    [74]

    Geshkenbein V B, Larkin A I, Barone A 1987 Phys. Rev. B 36 235Google Scholar

    [75]

    Xu X, Li Y, Chien C L 2020 Phys. Rev. Lett. 124 167001Google Scholar

    [76]

    Qi X L, Zhang S C 2011 Rev. Mod. Phys. 83 1057Google Scholar

    [77]

    Clarke J, Wilhelm F K 2008 Nature 453 1031Google Scholar

    [78]

    Anderson P W 1984 Phys. Rev. B 30 4000Google Scholar

    [79]

    Gor’kov L P, Rashba E I 2001 Phys. Rev. Lett. 87 037004Google Scholar

    [80]

    Sun Z, Enayat M, Maldonado A, Lithgow C, Yelland E, Peets D C, Yaresko A, Schnyder A P, Wahl P 2015 Nat. Commun. 6 6633Google Scholar

    [81]

    Jo S, Costanzo D, Berger H, Morpurgo A F 2015 Nano Lett. 15 1197Google Scholar

    [82]

    Shi W, Ye J, Zhang Y, Suzuki R, Yoshida M, Miyazaki J, Inoue N, Saito Y, Iwasa Y 2015 Sci. Rep. 5 12534Google Scholar

    [83]

    Barnett R, Demler E, Kaxiras E 2005 Phys. Rev. B 71 035429Google Scholar

    [84]

    Dubi Y, Meir Y, Avishai Y 2007 Nature 449 876Google Scholar

    [85]

    Cha M C, Fisher M P, Girvin S M, Wallin M, Young A P 1991 Phys. Rev. B 44 6883Google Scholar

    [86]

    Zhang G, Zeleznik M, Vanacken J, May P W, Moshchalkov V V 2013 Phys. Rev. Lett. 110 077001Google Scholar

    [87]

    Sochnikov I, Shaulov A, Yeshurun Y, Logvenov G, Božović I 2010 Nat. Nanotechnol. 5 516Google Scholar

    [88]

    Halbritter J 1987 Appl. Phys. A 43 1Google Scholar

    [89]

    Abrikosov A A 1957 Sov. Phys. JETP 5 1174

    [90]

    Kleiner W H, Roth L M, Autler S H 1964 Phys. Rev. 133 1226Google Scholar

    [91]

    Josephson B D 1962 Phys. Lett. 1 251Google Scholar

    [92]

    Makhlin Y, Schön G, Shnirman A 2001 Rev. Mod. Phys. 73 357Google Scholar

    [93]

    Mehta M M, Dikin D A, Bark C W, Ryu S, Folkman C M, Eom C B, Chandrasekhar V 2012 Nat. Commun. 3 955Google Scholar

    [94]

    Lee D H, Fisher M P 1991 Int. J. Mod. Phys. B 5 2675Google Scholar

    [95]

    Grabert H, Devoret M H (Eds.) 1992 Single Charge Tunneling: Coulomb Blockade Phenomena in Nanostructures (Vol. 294) (New York: Springer Science & Business Media)

    [96]

    Orlando T P, Lloyd S, Levitov L S, Berggren K K, Feldman M J, Bocko M F, Mooij J E, Harmans C J P, van der Wal C H 2002 Physica C 372-376 194Google Scholar

    [97]

    Casalbuoni R, Nardulli G 2004 Rev. Mod. Phys. 76 263Google Scholar

  • 图 1  低维超导体的超导量子振荡效应分类(利特尔-帕克斯效应、磁通涡旋运动、韦伯阻塞效应)与对应的物理机制, 以及一些典型实例[17,20,39,49-51,53,66]

    Figure 1.  Superconducting quantum oscillation effects observed in low-dimensional superconductors. Three distinct effects, including the Little-Parks (LP) effect, vortex motion effect and Weber blockade effects, together with the physical mechanisms and typical experimental results, are presented [17,20,39,49-51,53,66].

    图 2  利特尔-帕克斯效应的实验观测方法 (a) 通过磁场-临界温度关系的实验观测方法, 其中外磁场垂直于样品平面, 且临界温度对零磁场下的临界温度作了归一化处理, 样品为超导铝纳米结构, 形状及尺寸如内置插图所示[46]; (b) 通过电阻-磁场关系的实验观测方法, 样品为超导WS2手性纳米管, 外磁场方向沿管径向, 如右下角示意图所示. 通过振荡周期推算出的纳米管有效直径$d=80\;\mathrm{n}\mathrm{m}$, 这与透射电子显微镜的表征结果相符[17]

    Figure 2.  Experimental observation of LP effect: (a) By determining the relation between the superconducting critical temperature and the applied magnetic field, the LP oscillation can be observed in the H-TC relation. The sample used for the observation is a superconducting Al nanostructure, whose shape and size are presented in the inset figure. Note that the applied magnetic field is perpendicular to the sample surface, and that the superconducting critical temperature has been normalized by the critical temperature under zero magnetic field[46]. (b) By determining the relation between the four-terminal resistance and the applied magnetic field, the LP oscillation can be found in the $ R\text{-}T $ relation near a zero magnetic field. The sample used for the observation is superconducting chiral nanotube WS2, and the orientation of the applied magnetic field is along the nanotube axis. The calculated effective diameter of the superconducting nanotube is $d=80\;\mathrm{n}\mathrm{m}$ based on the periodicity of the oscillation, which is consistent with the pictures taken by transmission electron microscope[17].

    图 3  常规超导体(s波配对)与自旋三重态超导配对机制对应的利特尔-帕克斯效应对比[66] (a) 常规超导体的温度(上图)、磁电阻(下图)随磁场变化的利特尔-帕克斯振荡示意图, 零磁通状态对应于临界温度$ {T}_{\mathrm{C}} $的极大值、磁电阻$ R $的极小值; (b) 自旋三重态配对的超导体的温度(上图)、磁电阻(下图)随磁场变化的利特尔-帕克斯振荡示意图, 零磁通状态对应于$ {T}_{\mathrm{C}} $的极小值和$ R $的极大值, 与(a)刚好相反; (c) 常规超导体Nb磁电阻的利特尔-帕克斯振荡效应, 与图(a)相符, 其中磁场强度对30.2 Oe (单个磁通线对应的磁场强度, 1 Oe = 103/(4π) A/m)进行了归一化处理; (d) 拓扑超导体β-Bi2Pd磁电阻的利特尔-帕克斯振荡, 上图为原始曲线, 下图为去掉多项式背景信号后的曲线, 其振荡现象与图(b)相符, 证实了其自旋三重态配对的物理机制

    Figure 3.  Comparison of the LP oscillation effect between conventional superconductor (s-wave pairing) and spin-triplet superconductor[66]: (a) Schematic diagram of the LP effect of a conventional superconductor reflected by the critical temperature (upper panel) and magnetoresistance (lower panel). Note that the zero magnetic field state is associated with the maximum of $ {T}_{\mathrm{C}} $ and the minimum of $ R $. (b) Schematic diagram of the LP effect of a spin-triplet superconductor reflected by critical temperature (upper panel) and magnetoresistance (lower panel). Herein, the zero magnetic field state is associated with the minimum of $ {T}_{\mathrm{C}} $ and the maximum of $ R $, which is directly opposed to (a). (c) LP oscillation observed from magnetoresistance for conventional superconductor Nb, which is in accordance with the lower panel of (a). The magnetic field is normalized by 30.2 Oe, which is associated with a single magnetic fluxoid quantum. (d) LP oscillation of topological superconductor β-Bi2Pd observed from magnetoresistance. The upper panel shows the original data, and the lower panel shows the signal of oscillation by subtracting the normal $ R\text{-}H $ relation. The LP oscillation is in good accordance with the lower panel of (b), directly confirming the nature of the spin-triplet pairing mechanism of β-Bi2Pd.

    图 4  $ \alpha $-BiPd超导环的利特尔-帕克斯振荡的分析[75] (a)零磁通对应于磁电阻极大的利特尔-帕克斯振荡原始曲线(上图, 标记为$ R $)及去掉多项式背景后的结果(下图, 标记为$ {\Delta }R $), 该振荡的行为与图3(b)相对应, 这样的超导环被称为“$ \mathrm{\pi } $”环; (b)零磁通对应于磁电阻极小的利特尔-帕克斯振荡, 这里直接展示的是去掉背景后的结果(标记为$ {\Delta }R $), 与图3(a)相对应, 这样的超导环被称为“0”环

    Figure 4.  Analysis of LP oscillation for the $ \alpha $-BiPd superconducting ring[75]: (a) LP effect where the maximum resistance corresponds to the zero magnetic flux. The upper panel shows the original data of $ R\text{-} H$ relation (the resistance is marked as “$ R $”, and the sample size is shown in the inset panel), and the lower panel shows the results after subtracting the normal magnetoresistance data (marked as “${\Delta }R $”). The characteristics of the oscillation corresponds to Fig. 3(b), and this kind of superconducting ring is named the “$ \mathrm{\pi } $” ring. (b) LP effect where the minimum of resistance corresponds to zero magnetic flux. The characteristics of the oscillation correspond to Fig. 3(a), and this kind of superconducting ring is named the “$ 0 $” ring.

    图 5  对手性超导WS2纳米管的临界温度与管径间的关系研究[47] (a) 管径不同的4根超导纳米管的利特尔-帕克斯振荡以及根据公式${\mu }_{0}{\Delta }H\cdot\mathrm{\pi }{D}^{2}/4={\varPhi }_{0}$计算出的管径D和超导临界温度$ {T}_{\mathrm{C}} $(标在每条曲线上方); (b) 4根WS2超导纳米管以及WS2薄膜的电阻-温度关系, 其中电阻值对正常态的电阻作了归一化处理; (c) 4根WS2超导纳米管以及WS2薄膜的超导临界温度-管径关系, 其中WS2薄膜的管径被认为是无穷大

    Figure 5.  Investigation of the relation between the diameter of superconducting chiral WS2 nanotubes and the critical temperature[47]: (a) LP oscillation for 4 superconducting nanotubes with different diameters (D). The values of D are obtained based on the formula ${\mu }_{0}{\Delta }H\cdot\pi {D}^{2}/4={\varPhi }_{0}$ and the corresponding $ {T}_{\mathrm{C}} $ of each nanotube is marked on top of each curve. (b) The $ R\text{-}H$ relations for 4 superconducting nanotubes (corresponding to the order number in (a)) and superconducting WS2 flakes. (c) The relation between superconducting critical temperatures and diameters of nanotubes, where the diameter for WS2 flake is considered to be infinite.

    图 6  对二维超导体的绝缘体-超导相变中反常金属态的研究[39] (a) 样品结构示意图, 样品由无定形氧化铝(标记为AAO)、钇钡铜氧超导体(标记为YBCO)和钛酸锶衬底(标记为STO)三层结构构成, 多孔结构是利用Ar+和CF${}_3^+ $离子刻蚀的结果; (b) 不同刻蚀时间下得到的SC, AM1, TS以及INS对应的4种典型电阻-温度关系; (c)—(e) 不同温度下超导态(c)、反常金属态(d)、绝缘态(e)的归一化电导变化量随外磁场的振荡关系, 这3种态对应的振荡表现出了相同的周期; (f) 超导态、反常金属态、绝缘态的磁电导振荡幅度与温度的关系

    Figure 6.  Investigation of anomalous metal state existing in the transition from insulator to superconductor[39]: (a) Schematic illustration of the sample structure, including the amorphous alumina (AAO), Y-Ba-Cu-O superconductor (YBCO) and SrTiO3 (STO) layers. The porous structure is obtained by ionic etching of Ar+ and CF${}_3^+ $, respectively. (b) The $ R\text{-}T $ relations for 4 typical states: SC, AM1, TS and INS. (c)–(e) The oscillation signals in the $ R\text{-}H $ relations observed from normalized electrical conductance for the superconducting state (c), anomalous metal state (d), and insulating state (e). Note that the abovementioned three states have identical periodicity. (f) Temperature dependence of the oscillation amplitude for the abovementioned three states.

    图 7  热激发的磁通涡旋运动导致的磁电阻振荡效应[87] (a)高温超导La1.84Sr0.16CuO4纳米结构的扫描电子显微镜照片, 该结构由两个互相嵌套、成角45°的正方形构成, 右上角的插图为电阻-温度关系以及据此定义的临界温度$ {T}_{\mathrm{C}} $; (b) 磁电阻的振荡现象, 其中磁电阻的振荡幅度用$ {\Delta }R $表示. 内置插图为振荡幅度$ {\Delta }R $与温度的关系(散点图), 该振幅远远大于利特尔-帕克斯效应的预测(断续线), 却与根据热激发的磁通涡旋的运动模型计算的结果(实线)相吻合; (c), (d) 对振荡曲线作傅里叶变换得到的幅度-磁通倒数关系. 其中(c), (d)分别对应于75 nm, 150 nm边长的小正方形. 变换后只能在$2 {e}/h$位置处看到一个尖锐的峰, 而理论预测的${e}/h$$4 {e}/h$峰并不显著(图中$4 {e}/h$位置的矮峰源于$2 {e}/h$的二倍频信号, 并不是本征性质的反映)

    Figure 7.  Oscillation signal observed in magnetoresistance induced by the thermally excited vortex motion effect[87]. (a) Scanning electron microscope (SEM) image of a high $ {T}_{\mathrm{C}} $ superconductor La1.84Sr0.16CuO4 nanostructure, formed by two sets of square patterns at an angle of 45° with each other. The inset figure at the upper right corner shows the $ R \text{-}T$ relation and the superconducting critical temperature $ {T}_{\mathrm{C}} $ defined in this study. (b) The oscillation phenomena of magnetoresistance, where the amplitude of oscillation is defined as $ {\Delta }R $. The inset figure shows the relation between $ {\Delta }R $ and temperature. Note that the amplitude of oscillation is much larger than the expectation based on LP oscillation (dashed line), but is in good accordance with the calculation results based on thermally excited vortex motion effect (solid line). (c), (d) The Fourier transformation results of the oscillation signals, where (c) and (d) are associated with side lengths of 75 nm (c) and 150 nm (d) in the nanostructure patterns, respectively. Only a sharp peak can be observed at the position of $ 2 {e}/h $, but the theory-prospected peaks at the positions of $ e/h $ and $ 4 {e}/h $ seem insignificant (note that the peak at $ 4 {e}/h $ in (c) is just the double-frequency signal of the $ 2 {e}/h $ peak, instead of the intrinsic properties of the sample).

    图 8  电流激发的磁通涡旋运动导致的磁电阻振荡效应[50] (a) 器件结构示意图. (b) Nb超导纳米结构的电阻-温度关系, 其临界温度在7.6 K左右. 左上角内置插图为磁电阻振幅的温度依赖关系. 右下角内置插图为器件的SEM照片. (c) 7.35—7.65 K范围内不同温度下的归一化磁电阻测试曲线, 温度间隔为0.05 K. 磁电阻的振荡周期并不对应整数个磁通涡旋(见上刻度线). (d), (e) 不同电流强度下时间平均自由能(d)和超导纳米结构两端电势差(e)的磁通依赖关系. 电势差的变化幅度随着电流强度的增大而增大. (f) 固定温度(7.42 K)、不同电流强度下的归一化磁电阻测试曲线. 在零磁场的超导态保持为零电阻的范围内(对应于电流强度在$20\;\mathrm{\mu }\mathrm{A}$以下), 磁电阻的振荡幅度随电流强度的增加而增大, 与(e)的预期相符

    Figure 8.  Magnetoresistance oscillation phenomena originating from the current-induced vortex motion effect[50]: (a) Schematic diagram of the superconducting Nb device structure. (b) The $ R \text{-}T$ relation of Nb device. The superconducting critical temperature is approximately 7.6 K. The inset figure in the upper left panel shows the temperature dependence of the oscillation amplitude. The lower right panel shows the SEM image of the device. (c) The normalized experimental magnetoresistance results at temperatures from 7.35 K to 7.65 K. The temperature interval is chosen to be 0.05 K. Note that the periodicity of oscillation does not correspond to integer numbers of magnetic flux quantum. (d), (e) Magnetic flux-dependence of the time-average free energy (d) and electrical potential difference (e) under different intensities of electrical current. The amplitude of oscillation increases with increasing electrical current in (e). (f) Normalized magnetoresistance signal at fixed temperature (7.42 K) with different electrical current. Within the range of $I < 20\;\mathrm{\mu }\mathrm{A}$, the amplitude of oscillation in magnetoresistance increases with increasing electrical current, which is in good accordance with (e) .

    图 9  韦伯阻塞效应与库仑阻塞效应[51] (a) 韦伯阻塞效应示意图, 其中灰色长方形为超导纳米线, 其中的黑色涡旋代表量子磁通涡旋. 纳米线两侧(绿色区域)分别构成涡旋的“源”和“漏”, 在外加电流的驱动下两端的涡旋发生横跨超导纳米线的运动(如图中黑色箭头所示), 磁通涡旋的进出会导致纳米线两端的电压发生变化, 即韦伯阻塞效应. (b) 量子点的库仑阻塞效应. 量子点(灰色)的两侧分别为电子的“源”和“漏”(绿色), 在外加电压的驱动下电子发生源-量子点-漏的运动(黑色箭头所示). 对比图(a)与图(b)可知二者之间是电荷-涡旋对偶性的典型体现, 韦伯阻塞效应中对超导纳米线施加的电流起到了库仑阻塞效应中源漏间电压$ {V}_{\mathrm{S}} $-$ {V}_{\mathrm{D}} $的作用.

    Figure 9.  Comparison between Weber blockade and Coulomb blockade[51]: (a) Schematic diagram of Weber blockade, where the gray rectangle represents superconducting nanowires, and the black vortex represents quantum magnetic flux. The two sides of the nanowire (green regions) are the “source” and “drain” of the vortex. The vortex can move across the superconducting nanowire (shown by the black arrows) driven by the applied voltage. The entrance and exit of magnetic flux will cause a difference in the electrical potential of the nanowire, and this effect is named “Weber blockade”. (b) Coulomb blockade effect of a quantum dot. The two sides (green region) of the quantum dot (gray region) are the “source” and “drain” of electrons, respectively. The electrons move from the source to the quantum dot and finally drain driven by the applied voltage (shown by the black arrows). By comparing (a) and (b), one can see that the two phenomena are appropriate paradigms of charge-vortex duality.

    图 10  韦伯阻塞效应的实验观测[20] (a) Al超导纳米线的扫描电子显微镜照片与测试几何示意图; (b) 恒定温度(250 mK)下磁场强度由90 mT增加到130 mT时的电流-电压曲线; (c) 根据图(b)的实验结果绘制的临界电流$ {I}_{\mathrm{C}} $与磁场的关系. 内置插图为曲线在磁感应强度在0.1—0.13 T范围内的局部放大. 标记为a, b, c的3个典型区域的临界电流-磁感应强度曲线的斜率标识在右侧表中; (d) 不同磁感应强度下体系所处的状态示意图, 随磁感应强度的变化共可以分为5个区域(以罗马数字标识), 每个区域里上面的图代表实空间中纳米线的状态示意图(蓝色区域对应于超导态, 红色区域对应于正常金属态, 中间颜色为过渡态), 下面的图为对应的临界电流-磁场关系

    Figure 10.  Experimental confirmation of Weber blockade[20]: (a) SEM image and characterization geometry of Al superconducting nanowires[20]. (b) The $ I\text{-}V $ characteristics of the nanowire at a fixed temperature (250 mK) with the magnetic field increasing from 90 mT to 130 mT. (c) $ {I}_{\mathrm{C}}\text{-}B$relation derived from experimental results in (b). The slopes in the $ {I}_{\mathrm{C}}\text{-}B $ relation for the regions marked by a, b and c in the enlarged figure are presented in the inset table. (d) The physical states of the system with different intensities of magnetic field. Five typical states (marked by Roman numerals) can be found with the variance of the magnetic field. The upper panel of each region indicates the physical states of nanowires in real space (blue and red colors represent superconducting and normal metal states, and other colors represent transition states). The lower panel shows the corresponding $ {I}_{\mathrm{C}}\text{-}B $ relation.

    图 11  金属性超导场效应管中的韦伯阻塞效应[53] (a)器件结构示意图, 其中器件衬底为含有氧化层的重掺杂p型Si, $ {V}_{\mathrm{b}} $$ {V}_{\mathrm{s}} $分别代表底栅级和侧栅级的电势. 超导纳米线(蓝色结构)的电输运行为采用标准四线法测试. (b) 超导场效应管的伪色扫描电子显微镜照片, 其中栅极和超导纳米结构分别采用蓝绿色和深蓝色标识. Ti超导纳米线的长、宽、厚分别为900 nm, 200 nm, 30 nm. (c) 未施加栅级电压时的电阻-温度关系(深蓝色曲线)与5 mK下的电阻-磁场关系(蓝绿色曲线). (d) 未施加栅级电压时的临界电流-磁场关系, 在磁感应强度为30—100 mT范围内表现出了明显的振荡行为(测试温度为5 mK), 且该行为在施加相反方向的外磁场时也可观测到, 与韦伯阻塞效应的预期较为一致

    Figure 11.  Weber blockade effect in the metallic superconducting field-effect transistors[53]: (a) Schematic diagram of the device structure, where the substrate is heavily-doped p-type Si, and $ {V}_{\mathrm{b}} $ ($ {V}_{\rm{s}} $) represents the electrical potential of the bottom (side) gate. (b) Pseudo color SEM image of a superconducting field-effect transistor. “Gate” and superconducting nanostructures are colored cyan and dark blue, respectively. The length, width and thickness of Ti superconducting nanowires are 900 nm, 200 nm and 30 nm, respectively. (c) The R-T relation (dark blue line) and R-B relation at 5 mK (cyan line) with zero bias voltage. (d) The ${I}_{\mathrm{C}}\text{-} B$ relation with zero bias voltage. Observable oscillation phenomena can be found when the absolute value of the applied magnetic field ranges from 30 mT to 100 mT (the temperature is set to 5 mK). Such phenomena are in accordance with the expectation of Weber blockade.

    表 1  低维超导体的超导量子振荡现象

    Table 1.  Superconducting quantum oscillation phenomena in low-dimensional superconductors.

    振荡类型物理机制材料体系反映的物理规律
    利特尔-帕克斯振荡磁通量子化二维复连通薄膜、准一维纳米管电子的配对机制、
    样品的几何形状
    磁通涡旋运动导致的振荡热激发/电流激发的涡旋运动二维复连通薄膜体系中的涨落现象
    韦伯阻塞效应磁通涡旋横跨超导纳米线运动一维纳米线电荷-涡旋对偶性
    DownLoad: CSV
    Baidu
  • [1]

    Tinkham M 2004 Introduction to Superconductivity (2nd Ed.) (New York: Courier Corporation)

    [2]

    张裕恒 2009 超导物理 (第三版) (合肥: 中国科学技术大学出版社)

    Zhang Y H 2009 Physics of Superconductivity (3rd Ed.) (Hefei: University of Science and Technology of China Press) (in Chinese)

    [3]

    Ginzburg V L, Landau L D 1950 Zh. Eksp. Teor. Fiz. 20 1064

    [4]

    Berezinskii, V L 1972 Sov. Phys. JETP 34 610

    [5]

    Kosterlitz J M, Thouless D J 1973 J. Phys. C 6 1181Google Scholar

    [6]

    Cao Y, Fatemi V, Fang S, Watanabe K, Taniguchi T, Kaxiras E, Jarillo-Herrero P 2018 Nature 556 43Google Scholar

    [7]

    Park J M, Cao Y, Watanabe K, Taniguchi T, Jarillo-Herrero P 2021 Nature 590 249Google Scholar

    [8]

    Xing Y, Zhang H M, Fu H L, Liu H, Sun Y, Peng J P, Wang F, Lin X, Ma X C, Xue Q K, Wang J, Xie X C 2015 Science 350 542Google Scholar

    [9]

    Liu Y, Wang Z, Shan P, Tang Y, Liu C, Chen C, Xing Y, Wang Q, Liu H, Lin X, Xie X C, Wang J 2019 Nat. Commun. 10 3633Google Scholar

    [10]

    Liu Y, Qi S, Fang J, Sun J, Liu C, Liu Y, Qi J, Xing Y, Liu H, Lin X, Wang L, Xue Q K, Xie X C, Wang J 2021 Phys. Rev. Lett. 127 137001Google Scholar

    [11]

    Bert J A, Kalisky B, Bell C, Kim M, Hikita Y, Hwang H Y, Moler K A 2011 Nat. Phys. 7 767Google Scholar

    [12]

    Liu C, Yan X, Jin D, Ma Y, Hsiao H W, Lin Y, Bertz-Sullivan T M, Zhou X J, Pearson J, Fisher B, Jiang J A, Han W, Zuo J M, Wen J G, Fong D D, Sun J R, Zhou H, Bhattacharya A 2021 Science 371 716Google Scholar

    [13]

    Saito Y, Nakamura Y, Bahramy M S, Kohama Y, Ye J, Kasahara Y, Nakagawa Y, Onga M, Tokunaga M, Nojima T, Yanase Y, Iwasa Y 2016 Nat. Phys. 12 144Google Scholar

    [14]

    Xi X, Wang Z, Zhao W, Park J H, Law K T, Berger H, Forró L, Shan J, Mak K F 2016 Nat. Phys. 12 139Google Scholar

    [15]

    Sohn E, Xi X, He W Y, Jiang S, Wang Z, Kang K, Park J H, Berger H, Forró L, Law K T, Shan J, Mak K F 2018 Nat. Mat. 17 504Google Scholar

    [16]

    Cleuziou J P, Wernsdorfer W, Bouchiat V, Ondarçuhu T, Monthioux M 2006 Nat. Nanotechnol. 1 53Google Scholar

    [17]

    Qin F, Shi W, Ideue T, Yoshida M, Zak A, Tenne R, Kikitsu T, Inoue D, Hashizume D, Iwasa Y 2017 Nat. Commun. 8 14465Google Scholar

    [18]

    Morgan-Wall T 2015 Ph. D. Dissertation (Baltimore: Johns Hopkins University)

    [19]

    Cohen R W, Abeles B 1968 Phys. Rev. 168 444Google Scholar

    [20]

    Morgan-Wall T, Leith B, Hartman N, Rahman A, Marković N 2015 Phys. Rev. Lett. 114 077002Google Scholar

    [21]

    Perali A, Pieri P, Strinati G C 2004 Phys. Rev. Lett. 93 100404Google Scholar

    [22]

    Nakagawa Y, Kasahara Y, Nomoto T, Arita R, Nojima T, Iwasa Y 2021 Science 372 190Google Scholar

    [23]

    He Q L, Liu H, He M, Lai Y H, He H, Wang G, Law K T, Lortz R, Wang J, Sou I K 2014 Nat. Commun. 5 4247Google Scholar

    [24]

    Langer J S, Ambegaokar V 1967 Phys. Rev. 164 498Google Scholar

    [25]

    McCumber D E, Halperin B I 1970 Phys. Rev. B 1 1054Google Scholar

    [26]

    Rogachev A, Bollinger A T, Bezryadin A 2005 Phys. Rev. Lett. 94 017004Google Scholar

    [27]

    Youn S J, Fischer M H, Rhim S H, Sigrist M, Agterberg D F 2012 Phys. Rev. B 85 220505(RGoogle Scholar

    [28]

    Bauer E, Sigrist M (Eds.) 2012 Non-Centrosymmetric Superconductors: Introduction and Overview (Vol. 847) (London: Springer Science & Business Media)

    [29]

    Lu J M, Zheliuk O, Leermakers I, Yuan N F, Zeitler U, Law K T, Ye J T 2015 Science 350 1353Google Scholar

    [30]

    Mackenzie A P, Maeno Y 2003 Rev. Mod. Phys. 75 657Google Scholar

    [31]

    Xu Y, Sheng Y, Yang Y F 2019 Phys. Rev. Lett. 123 217002Google Scholar

    [32]

    de la Barrera S C, Sinko M R, Gopalan D P, Sivadas N, Seyler K L, Watanabe K, Taniguchi T, Tsen A W, Xu X D, Xiao D, Hunt B M 2018 Nat. Commun. 9 1427Google Scholar

    [33]

    Monthoux P, Lonzarich G G 1999 Phys. Rev. B 59 14598Google Scholar

    [34]

    Maier T, Jarrell M, Pruschke T, Keller J 2000 Phys. Rev. Lett. 85 1524Google Scholar

    [35]

    Maier T A, Jarrell M, Schulthess T C, Kent P R C, White J B 2005 Phys. Rev. Lett. 95 237001Google Scholar

    [36]

    Lee P A, Nagaosa N, Wen X G 2006 Rev. Mod. Phys. 78 17Google Scholar

    [37]

    Hashimoto M, Vishik I M, He R H, Devereaux T P, Shen Z X 2014 Nat. Phys. 10 483Google Scholar

    [38]

    Hashimoto M, Nowadnick E A, He R H, Vishik I M, Moritz B, He Y, Tanaka K, Moore R G, Lu D, Yoshida Y, Ishikado M, Sasagawa T, Fujita K, Ishida S, Uchida S, Eisaki H, Hussain Z, Devereaux T P, Shen Z X 2015 Nat. Mat. 14 37Google Scholar

    [39]

    Yang C, Liu Y, Wang Y, Feng L, He Q, Sun J, Tang Y, Wu C, Xiong J, Zhang W, Lin X, Yao H, Liu H, Fernandes G, Xu J, Valles J M Jr., Wang J, Li Y 2019 Science 366 1505Google Scholar

    [40]

    Dobrovolskiy O V, Vodolazov D Y, Porrati F, Sachser R, Bevz V M, Mikhailov M Y, Chumak A V, Huth M 2020 Nat. Commun. 11 3291Google Scholar

    [41]

    Schmid A, Hauger W 1973 J. Low Temp. Phys. 11 667Google Scholar

    [42]

    Blatter G, Feigel'man M V, Geshkenbein V B, Larkin A I, Vinokur V M 1994 Rev. Mod. Phys. 66 1125Google Scholar

    [43]

    Feigel’man M V, Vinokur V M 1990 Phys. Rev. B 41 8986Google Scholar

    [44]

    Little W A, Parks R D 1962 Phys. Rev. Lett. 9 9Google Scholar

    [45]

    Parks R D, Little W A 1964 Phys. Rev. 133 97Google Scholar

    [46]

    Moshchalkov V V, Gielen L, Strunk C, Jonckheere R, Qiu X, van Haesendincj C, Bruynseraede Y 1995 Nature 373 319Google Scholar

    [47]

    Qin F, Ideue T, Shi W, Zhang X X, Yoshida M, Zak A, Tenne R, Kikitsu T, Inoue D, Hashizume D, Iwasa Y 2018 Nano Lett. 18 6789Google Scholar

    [48]

    Kirtley J R, Tsuei C C, Kogan V G, Clem J R, Raffy H, Li Z Z 2003 Phys. Rev. B 68 214505Google Scholar

    [49]

    Sochnikov I, Shaulov A, Yeshurun Y, Logvenov G, Božović I 2010 Phys. Rev. B 82 094513Google Scholar

    [50]

    Berdiyorov G R, Milošević M V, Latimer M L, Xiao Z L, Kwok W K, Peeters F M 2012 Phys. Rev. Lett. 109 057004Google Scholar

    [51]

    Pekker D, Refael G, Goldbart P M 2011 Phys. Rev. Lett. 107 017002Google Scholar

    [52]

    Johansson A, Sambandamurthy G, Shahar D, Jacobson N, Tenne R 2005 Phys. Rev. Lett. 95 116805Google Scholar

    [53]

    Simoni G D, Paolucci F, Solinas P, Strambini E, Giazotto F 2018 Nat. Nanotechnol. 13 802Google Scholar

    [54]

    Geim A K, Grigorieva I V 2013 Nature 499 419Google Scholar

    [55]

    Novoselov K S, Mishchenko O A, Carvalho O A, Neto A C 2016 Science 353 461Google Scholar

    [56]

    Liu Y, Weiss N O, Duan X, Cheng H C, Huang Y, Duan X 2016 Nat. Rev. Mater. 1 16042Google Scholar

    [57]

    Yankowitz M, Chen S, Polshyn H, Zhang Y, Watanabe K, Taniguchi T, Graf D, Young A F, Dean C R 2019 Science 363 1059Google Scholar

    [58]

    Buzdin A I 2005 Rev. Mod. Phys. 77 935Google Scholar

    [59]

    Ryazanov V V, Oboznov V A, Rusanov A Y, Veretennikov A V, Golubov A A, Aarts J 2001 Phys. Rev. Lett. 86 2427Google Scholar

    [60]

    Kezilebieke S, Silveira O J, Huda M N, Vaňo V, Aapro M, Ganguli S C, Lahtinen J, Mansell R, van Dijken S, Foster A S, Liljeroth P 2021 Adv. Mat. 33 2006850Google Scholar

    [61]

    Wen H H 2021 Acta Phys. Sin. 70 017405Google Scholar

    [62]

    Bardeen J, Cooper L N, Schrieffer J R 1957 Phys. Rev. 108 1175Google Scholar

    [63]

    Pearl J 1964 Appl. Phys. Lett. 5 65Google Scholar

    [64]

    Doh Y J, van Dam J A, Roest A L, Bakker E P A M, Kouwenhoven L P, de Franceschi S 2005 Science 309 272Google Scholar

    [65]

    Paolucci F, de Simoni G, Strambini E, Solinas P, Giazotto F 2018 Nano Lett. 18 4195Google Scholar

    [66]

    Li Y, Xu X, Lee M H, Chu M W, Chien C L 2019 Science 366 238Google Scholar

    [67]

    Aharonov Y, Bohm D 1959 Phys. Rev. 115 485Google Scholar

    [68]

    Peshkin M, Tonomura A 1989 The Aharonov-Bohm Effect (Vol. 340) (Berlin: Springer)

    [69]

    Tinkham M 1964 Rev. Mod. Phys. 36 268Google Scholar

    [70]

    Barash Y S 2008 Phys. Rev. Lett. 100 177003Google Scholar

    [71]

    Juricic V, Herbut I F, Tesanovic Z 2008 Phys. Rev. Lett. 100 187006Google Scholar

    [72]

    Loder F, Kampf A P, Kopp T, Mannhart J, Schneider C W, Barash Y S 2008 Nat. Phys. 4 112Google Scholar

    [73]

    Berg E, Fradkin E, Kivelson S A 2009 Nat. Phys. 5 830Google Scholar

    [74]

    Geshkenbein V B, Larkin A I, Barone A 1987 Phys. Rev. B 36 235Google Scholar

    [75]

    Xu X, Li Y, Chien C L 2020 Phys. Rev. Lett. 124 167001Google Scholar

    [76]

    Qi X L, Zhang S C 2011 Rev. Mod. Phys. 83 1057Google Scholar

    [77]

    Clarke J, Wilhelm F K 2008 Nature 453 1031Google Scholar

    [78]

    Anderson P W 1984 Phys. Rev. B 30 4000Google Scholar

    [79]

    Gor’kov L P, Rashba E I 2001 Phys. Rev. Lett. 87 037004Google Scholar

    [80]

    Sun Z, Enayat M, Maldonado A, Lithgow C, Yelland E, Peets D C, Yaresko A, Schnyder A P, Wahl P 2015 Nat. Commun. 6 6633Google Scholar

    [81]

    Jo S, Costanzo D, Berger H, Morpurgo A F 2015 Nano Lett. 15 1197Google Scholar

    [82]

    Shi W, Ye J, Zhang Y, Suzuki R, Yoshida M, Miyazaki J, Inoue N, Saito Y, Iwasa Y 2015 Sci. Rep. 5 12534Google Scholar

    [83]

    Barnett R, Demler E, Kaxiras E 2005 Phys. Rev. B 71 035429Google Scholar

    [84]

    Dubi Y, Meir Y, Avishai Y 2007 Nature 449 876Google Scholar

    [85]

    Cha M C, Fisher M P, Girvin S M, Wallin M, Young A P 1991 Phys. Rev. B 44 6883Google Scholar

    [86]

    Zhang G, Zeleznik M, Vanacken J, May P W, Moshchalkov V V 2013 Phys. Rev. Lett. 110 077001Google Scholar

    [87]

    Sochnikov I, Shaulov A, Yeshurun Y, Logvenov G, Božović I 2010 Nat. Nanotechnol. 5 516Google Scholar

    [88]

    Halbritter J 1987 Appl. Phys. A 43 1Google Scholar

    [89]

    Abrikosov A A 1957 Sov. Phys. JETP 5 1174

    [90]

    Kleiner W H, Roth L M, Autler S H 1964 Phys. Rev. 133 1226Google Scholar

    [91]

    Josephson B D 1962 Phys. Lett. 1 251Google Scholar

    [92]

    Makhlin Y, Schön G, Shnirman A 2001 Rev. Mod. Phys. 73 357Google Scholar

    [93]

    Mehta M M, Dikin D A, Bark C W, Ryu S, Folkman C M, Eom C B, Chandrasekhar V 2012 Nat. Commun. 3 955Google Scholar

    [94]

    Lee D H, Fisher M P 1991 Int. J. Mod. Phys. B 5 2675Google Scholar

    [95]

    Grabert H, Devoret M H (Eds.) 1992 Single Charge Tunneling: Coulomb Blockade Phenomena in Nanostructures (Vol. 294) (New York: Springer Science & Business Media)

    [96]

    Orlando T P, Lloyd S, Levitov L S, Berggren K K, Feldman M J, Bocko M F, Mooij J E, Harmans C J P, van der Wal C H 2002 Physica C 372-376 194Google Scholar

    [97]

    Casalbuoni R, Nardulli G 2004 Rev. Mod. Phys. 76 263Google Scholar

  • [1] Chen Chen, Liu Qin, Zhang Tong, Feng Dong-Lai. Vortex bound states and Majorana zero mode in electron-doped FeSe-based high-temperature superconductor. Acta Physica Sinica, 2021, 70(1): 017401. doi: 10.7498/aps.70.20201673
    [2] Wen Hai-Hu. Brief introduction to flux pinning and vortex dynamics in high temperature superconductors. Acta Physica Sinica, 2021, 70(1): 017405. doi: 10.7498/aps.70.20201881
    [3] Liang Chao, Zhang Jie, Zhao Ke, Yang Xin-Sheng, Zhao Yong. Superconducting and flux pinning properties of FeSexTe1–x topological superconductors. Acta Physica Sinica, 2020, 69(23): 237401. doi: 10.7498/aps.69.20201125
    [4] Li Yao-Yi, Jia Jin-Feng. Search for Majorana zero mode in the magnetic vortex of artificial topological superconductor. Acta Physica Sinica, 2019, 68(13): 137401. doi: 10.7498/aps.68.20181698
    [5] Gong Dong-Liang, Luo Hui-Qian. Antiferromagnetic order and spin dynamics in iron-based superconductors. Acta Physica Sinica, 2018, 67(20): 207407. doi: 10.7498/aps.67.20181543
    [6] Cao Ning, Long Yong-Bing, Zhang Zhi-Guo, Gao Li-Juan, Yuan Jie, Zhao Bo-Ru, Zhao Shi-Ping, Yang Qian-Sheng, Zhao Ji-Min, Fu Pan-Ming. Femtosecond time-resolved dynamics in electron-doped high-Tc superconductor La2-xCexCuO4. Acta Physica Sinica, 2008, 57(4): 2543-2547. doi: 10.7498/aps.57.2543
    [7] He Guo-Liang, He Yan-Wen, Zhao Zhi-Gang, Liu Mei. Two-step depinning and reentrant superconducting phase of moving vortex lattice in disordered superconductors. Acta Physica Sinica, 2006, 55(2): 839-843. doi: 10.7498/aps.55.839
    [8] Li Xiao-Wei. . Acta Physica Sinica, 2002, 51(8): 1821-1825. doi: 10.7498/aps.51.1821
    [9] Liu Xu-Dong, Wang Jin, Liu Mei, Xing Ding-Yu. . Acta Physica Sinica, 2002, 51(5): 1122-1127. doi: 10.7498/aps.51.1122
    [10] HU LI-FA, ZHOU LIAN, ZHANG PING-XIANG, WANG JIN-XING. MAGNETIZATION AND HYSTERESIS LOSSES OF HIGH-Tc SUPERCONDUCTOR. Acta Physica Sinica, 2001, 50(7): 1359-1365. doi: 10.7498/aps.50.1359
    [11] Feng Yong, Zhou Lian, Yang Wan-min, Zhang Cui-ping, Wang Jing-rong, Yu Ze-ming, Wu Xiao-zu. Flux Pinning in PMP Y-Gd-Ba-Cu-O Superconductors. Acta Physica Sinica, 2000, 49(1): 146-152. doi: 10.7498/aps.49.146
    [12] XU KE-XI. NON-EQUILIBRIUM RADIATION RESPONSE AND DECOUPLING OF VORTEX-ANTIVORTES PAIRS IN TWO-DIMENSIONAL HIGH-Tc SUPERCONDUCTORS. Acta Physica Sinica, 2000, 49(5): 989-996. doi: 10.7498/aps.49.989
    [13] QU HAI, ZHOU SHI-PING. VORTEX LATTICE IN A HIGH-Tc SUPERCONDUCTOR OF MIXED PAIRING SYMMETRY. Acta Physica Sinica, 1999, 48(2): 352-362. doi: 10.7498/aps.48.352
    [14] DU AN, WEI GUO-ZHU, NIE HUI-QUAN. ANTIFERROMAGNETIC THEORETICAL CALCULATION FOR HlGH-Tc SUPERCONDUCTORS. Acta Physica Sinica, 1992, 41(10): 1686-1693. doi: 10.7498/aps.41.1686
    [15] JIN JI-RONG, CHEN WU-MING, JIN XIN, ZHANG YI-TONG, LU MU, JI HE-LIN, LIU XIN-HU, YAO XI-XIAN, YI MIN-YU, HONG CANG-SHENG, WAN TAO-YU, FANG JUN-REN. IRRADIATION EFFECT WITH SLOW NEUTRONS OF LOW FLUENCE ON Bi-BASED SUPERCONDUCTORS. Acta Physica Sinica, 1992, 41(5): 846-850. doi: 10.7498/aps.41.846
    [16] JIN XIN, ZHANG YI-TONG, LU MU, ZHANG CHANG-GUI, YAN YONG, YU YANG, SHEN JIAN-CANG, YAO XI-XIAN. MAGNETIC FLUX PINNING AND CREEP IN (BiPb)-Sr-Ca-Cu-O 2223 PHASE HIGH-Tc SUPERCONDUCTOR. Acta Physica Sinica, 1991, 40(4): 630-633. doi: 10.7498/aps.40.630
    [17] ZHANG FENG-YING, HUANG SUN-LI, CAO XIAO-WEN. FLUX CREEP IN HIGH Tc YBa2Cu3Oy BULK SUPERCONDUCTOR. Acta Physica Sinica, 1990, 39(5): 830-835. doi: 10.7498/aps.39.830
    [18] XIE XUE-GANG, CHEN SHI-GANG, HONG CHAO-SHENG. HYDRODYNAMIC EQUATION FOR A SUPERCONDUCTOR. Acta Physica Sinica, 1990, 39(4): 632-638. doi: 10.7498/aps.39.632
    [19] CAI XUE-YU, YIN DAO-LE. ON THE PROXIMITY EFFECT OF SUPERCONDUCTING MULTILAYER FILMS. Acta Physica Sinica, 1981, 30(5): 700-704. doi: 10.7498/aps.30.700
    [20] . Acta Physica Sinica, 1965, 21(3): 683-685. doi: 10.7498/aps.21.683
Metrics
  • Abstract views:  8889
  • PDF Downloads:  488
  • Cited By: 0
Publishing process
  • Received Date:  11 December 2021
  • Accepted Date:  31 December 2021
  • Available Online:  28 February 2022
  • Published Online:  20 June 2022

/

返回文章
返回
Baidu
map