氧化镍在倒置平面钙钛矿太阳能电池中的应用进展

王佩佩; 张晨曦; 胡李纳; 李仕奇; 任炜桦; 郝玉英

doi:10.7498/aps.70.20201896

摘要

近年来有机-无机杂化钙钛矿太阳能电池(perovskite solar cells, PSCs)因具有光电转换效率高、制备工艺简单等优点而受到广泛关注. 空穴传输层(hole transport layer, HTL)的选择及其优化对器件的性能至关重要. 氧化镍(NiO_x) HTL具有化学稳定性好、空穴迁移率高、制备方法简单等特点, 在PSCs中得到了广泛应用. 本综述从NiO_x HTL在平面PSCs中的应用入手, 系统介绍了通过掺杂和表面修饰法实现对NiO_x HTL薄膜的结构和光电性能的改性, 并从能级匹配、空穴迁移率及结晶性等多个角度详细评述了NiO_x改性对PSCs光电转换效率、填充因子、开路电压、短路电流和稳定性的影响规律, 最后对于NiO_x平面PSCs的未来进行了展望.

关键词:

Abstract

In recent years, organic-inorganic hybrid perovskite solar cells (PSCs) have attracted wide attention due to their high photoelectric conversion efficiency and simple preparation process. Hole transport layer (HTL) is one of the most critical components in PSCs. As a kind of inorganic HTL material, nickel oxide (NiO_x) has been widely used in perovskite solar cells because of its excellent advantages, such as outstanding chemical stability, high carrier mobility, simple methods for its preparation, etc. In this paper, the applications of NiO_x HTL in planar PSCs are systematically summarized from the aspects of the improvment of its structure and photoelectric properties by doping and interface modification. The reasons for affecting the device performances, i.e. fill factor, open-circuit voltage, short-circuit current, photoelectric conversion efficiency, and stability are emphatically analyzed from several aspects, such as energy level matching, hole mobility and crystallinity. In addition, the future development directions of the planar PSCs are prospected.

Keywords:

作者及机构信息

太原理工大学物理与光电工程学院, 新型传感与智能控制教育部重点实验室, 太原　030024

通信作者: 张晨曦, zhangchenxi@tyut.edu.cn ; 郝玉英, haoyuying@tyut.edu.cn

基金项目: 国家自然科学基金(批准号: 62074108)、国家自然科学基金委员会-山西省煤基低炭联合基金(批准号: U1710115)、山西省科学技术重大专项(批准号: 20201101012)、山西省科技创新培育团队建设项目(批准号: 201805D131012-3)和山西省自然科学基金(批准号: 201901D211114)资助的课题

Authors and contacts

College of Physics and Optoelectronics, Key Lab of Advanced Transducers and Intelligent Control System, Taiyuan University of Technology, Taiyuan 030024, China

Corresponding author: Zhang Chen-Xi, zhangchenxi@tyut.edu.cn ; Hao Yu-Ying, haoyuying@tyut.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 62074108), the Joint Foundation of National Natural Science Foundation of China and Shanxi Coal-Based Low-Carbon Nurturing Project (Grant No. U1710115), the Major Special Projects of Shanxi Province in Science and Technology, China (Grant No. 20201101012), the Platform and Base Special Project of Shanxi, China (Grant No. 201805D131012-3), and the Natural Science Foundation of Shanxi Province, China (Grant No. 201901D211114)

文章全文 : translate this paragraph

参考文献

[1]	Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 60 Google Scholar
[2]	Lee M, Teuscher J, Miyasaka T, Murakami T, Snaith H 2012 Science 338 643 Google Scholar
[3]	Zhou H, Chen Q, Li G, Luo S, Song T, Duan H, Hong Z, You J, Liu Y, Yang Y 2014 Science 345 542 Google Scholar
[4]	Best Research-Cell Effciency Chart from NREL https://www.nrel.gov/pv/cell-efficiency.html
[5]	Kim Y, Jung E H, Kim G, Kim D, Kim B J, Seo J 2018 Adv. Energy Mater. 8 1801668 Google Scholar
[6]	Wang M, Wang H, Li W, Hu X, Sun K, Zang Z 2019 J. Mater. Chem. A 7 26421 Google Scholar
[7]	Jeng J Y, Chen K C, Chiang T Y, Lin P Y, Tsai T D, Chang Y C, Guo T F, Chen P, Wen T C, Hsu Y J 2014 Adv. Mater. 26 4107 Google Scholar
[8]	Seo J, Park S, Kim Y C, Jeon N J, Noh J H, Yoon S C, Seok S I 2014 Energy Environ. Sci. 7 2642 Google Scholar
[9]	Lyu M, Chen J, Park N G 2019 J. Solid State Chem. 269 367 Google Scholar
[10]	Chowdhury T H, Akhtaruzzaman M, Kayesh M E, Kaneko R, Noda T, Lee J J, Islam A 2018 Sol. Energy 171 652 Google Scholar
[11]	Sepalage G A, Meyer S, Pascoe A, Scully A D, Huang F, Bach U, Cheng Y B, Spiccia L 2015 Adv. Funct. Mater. 25 5650 Google Scholar
[12]	Chen W, Deng L, Dai S, Wang X, Tian C, Zhan X, Xie S, Huang R, Zheng L 2015 J. Mater. Chem. A 3 19353 Google Scholar
[13]	Zuo C, Ding L 2015 Small 11 5528 Google Scholar
[14]	Yu W, Li F, Wang H, Alarousu E, Chen Y, Lin B, Wang L, Hedhili M N, Li Y, Wu K, Wang X, Mohammed O F, Wu T 2016 Nanoscale 8 6173 Google Scholar
[15]	Yang Y, Chen H, Zheng X, Meng X, Zhang T, Hu C, Bai Y, Xiao S, Yang S 2017 Nano Energy 42 322 Google Scholar
[16]	Islam M B, Yanagida M, Shirai Y, Nabetani Y, Miyano K 2017 ACS Omega 2 2291 Google Scholar
[17]	Ru P, Bi E, Zhang Y, Wang Y, Kong W, Sha Y, Tang W, Zhang P, Wu Y, Chen W, Yang X, Chen H, Han L 2020 Adv. Energy Mater. 10 1903487 Google Scholar
[18]	Yin X, Guo Y, Xie H, Que W, Kong L B 2019 Solar RRL 3 1900001 Google Scholar
[19]	Zheng X, Song Z, Chen Z, Bista S S, Gui P, Shrestha N, Chen C, Li C, Yin X, Awni R A, Lei H, Tao C, Ellingson R J, Yan Y, Fang G 2020 J. Mater. Chem. C 8 1972 Google Scholar
[20]	Xu L, Chen X, Jin J, Liu W, Dong B, Bai X, Song H, Reiss P 2019 Nano Energy 63 103860 Google Scholar
[21]	Kim H S, Jang I H, Ahn N, Choi M, Guerrero A, Bisquert J, Park N G 2015 J. Phys. Chem. Lett. 6 4633 Google Scholar
[22]	Yin X, Que M, Xing Y, Que W 2015 J. Mater. Chem. A 3 24495 Google Scholar
[23]	Wang Y, Mahmoudi T, Rho W Y, Yang H Y, Seo S, Bhat K S, Ahmad R, Hahn Y B 2017 Nano Energy 40 408 Google Scholar
[24]	Sajid S, Elseman A M, Huang H, Ji J, Dou S, Jiang H, Liu X, Wei D, Cui P, Li M 2018 Nano Energy 51 408 Google Scholar
[25]	Yan X, Zheng J, Zheng L, Lin G, Lin H, Chen G, Du B, Zhang F 2018 Mater. Res. Bull. 103 150 Google Scholar
[26]	Corani A, Li M H, Shen P S, Chen P, Guo T F, El Nahhas A, Zheng K, Yartsev A, Sundstrom V, Jr Ponseca C S 2016 J. Phys. Chem. Lett. 7 1096 Google Scholar
[27]	Scheideler W J, Rolston N, Zhao O, Zhang J, Dauskardt R H 2019 Adv. Energy Mater. 9 1803600 Google Scholar
[28]	Seo Y H, Cho I H, Na S I 2019 J. Alloys Compd. 797 1018 Google Scholar
[29]	Kaneko R, Kanda H, Sugawa K, Otsuki J, Islam A, Nazeeruddin M K 2019 Solar RRL 3 1900172 Google Scholar
[30]	Park I J, Kang G, Park M A, Kim J S, Seo S W, Kim D H, Zhu K, Park T, Kim J Y 2017 Chem. Sus. Chem. 10 2660 Google Scholar
[31]	Kim J H, Liang P W, Williams S T, Cho N, Chueh C C, Glaz M S, Ginger D S, Jen A K 2015 Adv. Mater. 27 695 Google Scholar
[32]	Jung J W, Chueh C C, Jen A K 2015 Adv. Mater. 27 7874 Google Scholar
[33]	Huang A, Lei L, Chen Y, Yu Y, Zhou Y, Liu Y, Yang S, Bao S, Li R, Jin P 2018 Sol. Energy Mater. Sol. Cells 182 128 Google Scholar
[34]	Wei Y, Yao K, Wang X, Jiang Y, Liu X, Zhou N, Li F 2018 Appl. Surf. Sci. 427 782 Google Scholar
[35]	Lee P H, Li B T, Lee C F, Huang Z H, Huang Y C, Su W F 2020 Sol. Energy Mater. Sol. Cells 208 110352 Google Scholar
[36]	Qiu Z, Gong H, Zheng G, Yuan S, Zhang H, Zhu X, Zhou H, Cao B 2017 J. Mater. Chem. C 5 7084 Google Scholar
[37]	Chen W, Liu F Z, Feng X Y, Djurišić A B, Chan W K, He Z B 2017 Adv. Energy Mater. 7 1700722 Google Scholar
[38]	Ge B, Qiao H, Lin Z, Zhou Z, Chen A, Yang S, Hou Y, Yang H 2019 Sol. RRL 3 1900192 Google Scholar
[39]	Hu Z, Chen D, Yang P, Yang L, Qin L, Huang Y, Zhao X 2018 Appl. Surf. Sci. 441 258 Google Scholar
[40]	Wang S, Zhang B, Feng D, Lin Z, Zhang J, Hao Y, Fan X, Chang J 2019 J. Mater. Chem. C 7 9270 Google Scholar
[41]	Chen W, Zhou Y, Wang L, Wu Y, Tu B, Yu B, Liu F, Tam H W, Wang G, Djurisic A B, Huang L, He Z 2018 Adv. Mater. 30 1800515 Google Scholar
[42]	Chen W, Wu Y, Fan J, Djurišić A-B, Liu F, Tam H W, Ng A, Surya C, Chan W K, Wang D, He Z 2018 Adv. Energy Mater. 8 1870091 Google Scholar
[43]	Wang Z, Rong X, Wang L, Wang W, Lin H, Li X 2020 ACS Appl. Mater. & Interfaces 12 8342 Google Scholar
[44]	Li G, Jiang Y, Deng S, Tam A, Xu P, Wong M, Kwok H S 2017 Adv. Sci. 4 1700463 Google Scholar
[45]	Chen W, Wu Y, Yue Y, Liu J, Zhang W, Yang X, Chen H, Bi E, Ashraful I, Michael G, Han L 2015 Science 350 944 Google Scholar
[46]	Niu Q L, Deng Y, Cui D, Lv H, Duan X, Li Z, Liu Z, Zeng W, Xia R, Tan W, Min Y 2019 J. Mater. Sci. 54 14134 Google Scholar
[47]	He J, Xiang Y, Zhang F, Lian J, Hu R, Zeng P, Song J, Qu J 2018 Nano Energy 45 471 Google Scholar
[48]	Zhang J, Luo H, Xie W, Lin X, Hou X, Zhou J, Huang S, Ou-Yang W, Sun Z, Chen X 2018 Nanoscale 10 5617 Google Scholar
[49]	Li Z, Jo B H, Hwang S J, Kim T H, Somasundaram S, Kamaraj E, Bang J, Ahn T K, Park S, Park H J 2019 Adv. Sci. 6 1802163 Google Scholar
[50]	Wang S, Zhu Y, Wang C, Ma R 2020 Org. Electron. 78 105627 Google Scholar
[51]	Chen W, Zhou Y, Chen G, Wu Y, Tu B, Liu F Z, Huang L, Ng A M C, Djurišić A B, He Z 2019 Adv. Energy Mater. 9 1970068 Google Scholar
[52]	Wang T, Cheng Z, Zhou Y, Liu H, Shen W 2019 J. Mater. Chem. A 7 21730 Google Scholar
[53]	Zhao J, Tavakoli R, Tavakoli M-M 2019 Chem. Commun 55 9196 Google Scholar
[54]	Wang T, Xie M, Abbasi S, Cheng Z, Liu H, Shen W 2020 J. Power Sources 448 227584 Google Scholar
[55]	Wang Q, Chueh C C, Zhao T, Cheng J, Eslamian M, Choy W C H, Jen A K 2017 Chem. Sus. Chem. 10 3794 Google Scholar
[56]	Du Y, Xin C, Huang W, Shi B, Ding Y, Wei C, Zhao Y, Li Y, Zhang X 2018 ACS Sustain. Chem. Eng. 6 16806 Google Scholar
[57]	Zhai Z, Huang X, Xu M, Yuan J, Peng J, Ma W 2013 Adv. Energy Mater. 3 1614 Google Scholar
[58]	Sun Y, Chen W, Wu Y, He Z, Zhang S, Chen S 2019 Nanoscale 11 1021 Google Scholar
[59]	Wang T, Ding D, Zheng H, Wang X, Wang J, Liu H, Shen W 2019 Solar RRL 3 1900045 Google Scholar

施引文献

图 1 钙钛矿太阳电池结构示意图

Fig. 1. Schematic diagram of PSCs.

下载: 全尺寸图片幻灯片

图 2 NiO的立方晶体结构

Fig. 2. NiO cubic crystal structure

下载: 全尺寸图片幻灯片

图 3 (a) NiO_x和Cu:NiO_x薄膜的紫外光电子能谱^[33]; (b) 基于NiO_x或Cs: NiO_x单空穴器件的J-V曲线, 器件结构为FTO/ NiO_x 或 Cs:NiO_x/MoO₃/Ag^[37]; (c) 不同HTLs的PSCs能级图; (d) 倒置平面PSCs的结构^[38]; (e) F6TCNNQ掺杂分子的化学结构及其与NiO_x的能级排列^[41]; (f) NiO_x与TCNQ, F2TCNQ, F4TCNQ和F2HCNQ的电荷转移和能级分布示意图^[17]

Fig. 3. (a) Ultraviolet photoelectron spectra of NiO_x and Cu:NiO_x films^[33]; (b) J-V curves of hole only devices with NiO_x or Cs:NiO_x hole extraction layers, the device structure is FTO/ NiO_x or Cs:NiO_x/MoO₃/Ag^[37]; (c) energy-level diagram of the various layers in the PSCs exhibiting the transfer of photoinduced holes; (d) structural illustration of the inverted planar PSCs^[38]; (e) band alignment of NiO_x and molecular dopants of F6TCNNQ and the chemical structure^[41]; (f) schematic of charge transfer and energy level distribution of NiO_x, TCNQ, F2TCNQ, F4TCNQ, and F2HCNQ^[17].

下载: 全尺寸图片幻灯片

图 4 (a) 钙钛矿前驱体在NiO_x薄膜以及甘油处理后NiO_x膜上的接触角^[46]; (b) 三种氨基酸的三维分子模型^[47]; (c) NiO_x和NiO_x/FDA 薄膜上钙钛矿层的SEM图像; (d) NiO_x和NiO_x/FDA 薄膜上钙钛矿层的X射线衍射图^[48]; (e) 基于TPV实验计算的具有不同HTLs器件的载流子复合寿命与光强度关系图^[49]; (f) 在10 kHz下KCl修饰前后NiO_x基PSCs的Mott-Schottky图, 以及基于TPV实验计算的KCl修饰前后NiO_x基PSCs的陷阱态密度谱^[51]

Fig. 4. (a) Contact angles of the solvents of perovskite precursor solution on NiO_x: pristine film and with glycerol treatment^[46]; (b) molecular 3D models and formula of three amino acids^[47]; (c) SEM images of the perovskite layer on NiO_x and NiO_x/FDA films; (d) XRD patterns of the perovskite layer on NiO_x and NiO_x/FDA films^[48]; (e) recombination lifetime versus light intensity plots of complete cells having various HTLs, calculated by TPV experiments^[49]; (f) Mott–Schottky plots for the CsFAMA perovskite PSCs with pristine and KCl-modified NiO_x HTLs at 10 kHz and trap density of states (DOS) spectra for CsFAMA perovskite PSCs with pristine and KCl-modified NiO_x HTLs^[51]

下载: 全尺寸图片幻灯片

表 1 基于掺杂NiO_x薄膜的PSCs的性能

Table 1. Performances of the PSCs based on doped NiO_x films.

器件结构	电压 V_oc/V	电流 J_sc/(mA·cm^–2)	填充因子FF	光电转换效率PCE/%	掺杂/方法	文献
ITO/F2HCNQ:NiO_x/PMMA/CsMAFA/PCBM/BCP/Ag	1.14	23.44	0.83	22.13	F2HCNQ:NiO_x spin-coating	[17]
ITO/F6TCNNQ:NiO_x/CsFAMA/ PCBM/ZrAcac/Ag	1.12	23.18	0.80	20.86	F6TCNNQ/Spin coating	[41]
ITO/Cu:NiO_x/CH₃NH₃PbI₃/C₆₀/BCP/Ag	1.12	22.28	0.81	20.26	Cu:NiO_x NPs/Spin coating	[42]
ITO/Li:Co NiO_x/MA_1yFA_yPbI_3xCl_x/ PCBM/BCP/Ag	1.09	23.80	0.78	20.10	Li:Co/Spin-coating	[40]
ITO/Sr:NiO_x/CH₃NH₃PbI₃/C₆₀/BCP/Ag	1.14	22.66	0.76	19.49	Sr:NiO/Spin-coating	[38]
ITO/NiO_x:AGQDs/CsFAMA/PCBM/BCP/Ag	1.05	22.30	0.83	19.40	NiO_x:AGQDs/Spin-coating	[43]
FTO/Cs:NiO_x/MAPbI₃/PCBM/ZrAcac/Ag	1.12	21.77	0.79	19.35	Cs/Spin coating sol	[37]
ITO/NiMgO/CH₃NH₃PbI₃/PCBM/ZnMgO/Al	1.08	21.30	0.80	18.50	Mg/Sputtering	[44]
FTO/NIR-Co:NiO_x/MAPbI₃/PC₆₁BM/PEI/Ag	1.09	20.46	0.80	17.77	Co/Spin-coating	[35]
FTO/NiMgLiO/MAPbI₃/PCBM/Ti(Nb)O_x/Ag	1.07	20.21	0.75	16.20	Li-Mg/Spray pyrolysis	[45]

下载: 导出CSV

表 2 基于改性NiO_x薄膜的PSCs的性能

Table 2. Performances of the PSCs based on modified NiO_x films

器件结构	电压 V_oc/V	电流 J_sc/(mA·cm^–2)	填充因子FF	光电转换效率PCE/%	改性/方法	文献
ITO/NiO_x/KCl/CsFAMA/PCBM/ZrAcac/Ag	1.15	22.89	0.80	20.96	KCl or NaCl/ Spin-coating	[51]
ITO/NiO_x/PFN-P2/CsFAMA/C₆₀/BCP/Ag	1.13	23.33	0.78	20.50	PFN-P2	[53]
FTO/NiO_x/SDBS/CH₃NH₃PbI₃/ PCBM/BCP/Ag	1.12	22.94	0.78	20.15	SDBS/Spin-coating	[54]
ITO/NiO_x/NH₄F/CH₃NH₃PbI₃/C₆₀/BCP/Ag	1.09	22.45	0.77	18.94	NH₄F/Spin-coating	[50]
ITO/NiO_x/TPI-6MEO/MAPbI₃/ PCBM/BCP/Ag	0.98	23.31	0.81	18.42	TPI-6MEO/ Spin-coating	[49]
ITO/NiO_x/SAM/Perovskite/ PCBM/Bis-C₆₀/Ag	1.11	21.70	0.76	18.40	Benzoic acid modification	[55]
ITO/NiO_x/FDA/CH₃NH₃PbI₃/PCBM/AgAl	1.04	22.55	0.76	17.87	FDA modification	[48]
FTO/NiO_x/PTAA/FA_1–xMA_xPb (I_3–yBr_y)/PCBM/Au	1.06	21.54	0.75	17.10	PTAA/Sol–gel	[56]

下载: 导出CSV

map

[1]	Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 60 Google Scholar
[2]	Lee M, Teuscher J, Miyasaka T, Murakami T, Snaith H 2012 Science 338 643 Google Scholar
[3]	Zhou H, Chen Q, Li G, Luo S, Song T, Duan H, Hong Z, You J, Liu Y, Yang Y 2014 Science 345 542 Google Scholar
[4]	Best Research-Cell Effciency Chart from NREL https://www.nrel.gov/pv/cell-efficiency.html
[5]	Kim Y, Jung E H, Kim G, Kim D, Kim B J, Seo J 2018 Adv. Energy Mater. 8 1801668 Google Scholar
[6]	Wang M, Wang H, Li W, Hu X, Sun K, Zang Z 2019 J. Mater. Chem. A 7 26421 Google Scholar
[7]	Jeng J Y, Chen K C, Chiang T Y, Lin P Y, Tsai T D, Chang Y C, Guo T F, Chen P, Wen T C, Hsu Y J 2014 Adv. Mater. 26 4107 Google Scholar
[8]	Seo J, Park S, Kim Y C, Jeon N J, Noh J H, Yoon S C, Seok S I 2014 Energy Environ. Sci. 7 2642 Google Scholar
[9]	Lyu M, Chen J, Park N G 2019 J. Solid State Chem. 269 367 Google Scholar
[10]	Chowdhury T H, Akhtaruzzaman M, Kayesh M E, Kaneko R, Noda T, Lee J J, Islam A 2018 Sol. Energy 171 652 Google Scholar
[11]	Sepalage G A, Meyer S, Pascoe A, Scully A D, Huang F, Bach U, Cheng Y B, Spiccia L 2015 Adv. Funct. Mater. 25 5650 Google Scholar
[12]	Chen W, Deng L, Dai S, Wang X, Tian C, Zhan X, Xie S, Huang R, Zheng L 2015 J. Mater. Chem. A 3 19353 Google Scholar
[13]	Zuo C, Ding L 2015 Small 11 5528 Google Scholar
[14]	Yu W, Li F, Wang H, Alarousu E, Chen Y, Lin B, Wang L, Hedhili M N, Li Y, Wu K, Wang X, Mohammed O F, Wu T 2016 Nanoscale 8 6173 Google Scholar
[15]	Yang Y, Chen H, Zheng X, Meng X, Zhang T, Hu C, Bai Y, Xiao S, Yang S 2017 Nano Energy 42 322 Google Scholar
[16]	Islam M B, Yanagida M, Shirai Y, Nabetani Y, Miyano K 2017 ACS Omega 2 2291 Google Scholar
[17]	Ru P, Bi E, Zhang Y, Wang Y, Kong W, Sha Y, Tang W, Zhang P, Wu Y, Chen W, Yang X, Chen H, Han L 2020 Adv. Energy Mater. 10 1903487 Google Scholar
[18]	Yin X, Guo Y, Xie H, Que W, Kong L B 2019 Solar RRL 3 1900001 Google Scholar
[19]	Zheng X, Song Z, Chen Z, Bista S S, Gui P, Shrestha N, Chen C, Li C, Yin X, Awni R A, Lei H, Tao C, Ellingson R J, Yan Y, Fang G 2020 J. Mater. Chem. C 8 1972 Google Scholar
[20]	Xu L, Chen X, Jin J, Liu W, Dong B, Bai X, Song H, Reiss P 2019 Nano Energy 63 103860 Google Scholar
[21]	Kim H S, Jang I H, Ahn N, Choi M, Guerrero A, Bisquert J, Park N G 2015 J. Phys. Chem. Lett. 6 4633 Google Scholar
[22]	Yin X, Que M, Xing Y, Que W 2015 J. Mater. Chem. A 3 24495 Google Scholar
[23]	Wang Y, Mahmoudi T, Rho W Y, Yang H Y, Seo S, Bhat K S, Ahmad R, Hahn Y B 2017 Nano Energy 40 408 Google Scholar
[24]	Sajid S, Elseman A M, Huang H, Ji J, Dou S, Jiang H, Liu X, Wei D, Cui P, Li M 2018 Nano Energy 51 408 Google Scholar
[25]	Yan X, Zheng J, Zheng L, Lin G, Lin H, Chen G, Du B, Zhang F 2018 Mater. Res. Bull. 103 150 Google Scholar
[26]	Corani A, Li M H, Shen P S, Chen P, Guo T F, El Nahhas A, Zheng K, Yartsev A, Sundstrom V, Jr Ponseca C S 2016 J. Phys. Chem. Lett. 7 1096 Google Scholar
[27]	Scheideler W J, Rolston N, Zhao O, Zhang J, Dauskardt R H 2019 Adv. Energy Mater. 9 1803600 Google Scholar
[28]	Seo Y H, Cho I H, Na S I 2019 J. Alloys Compd. 797 1018 Google Scholar
[29]	Kaneko R, Kanda H, Sugawa K, Otsuki J, Islam A, Nazeeruddin M K 2019 Solar RRL 3 1900172 Google Scholar
[30]	Park I J, Kang G, Park M A, Kim J S, Seo S W, Kim D H, Zhu K, Park T, Kim J Y 2017 Chem. Sus. Chem. 10 2660 Google Scholar
[31]	Kim J H, Liang P W, Williams S T, Cho N, Chueh C C, Glaz M S, Ginger D S, Jen A K 2015 Adv. Mater. 27 695 Google Scholar
[32]	Jung J W, Chueh C C, Jen A K 2015 Adv. Mater. 27 7874 Google Scholar
[33]	Huang A, Lei L, Chen Y, Yu Y, Zhou Y, Liu Y, Yang S, Bao S, Li R, Jin P 2018 Sol. Energy Mater. Sol. Cells 182 128 Google Scholar
[34]	Wei Y, Yao K, Wang X, Jiang Y, Liu X, Zhou N, Li F 2018 Appl. Surf. Sci. 427 782 Google Scholar
[35]	Lee P H, Li B T, Lee C F, Huang Z H, Huang Y C, Su W F 2020 Sol. Energy Mater. Sol. Cells 208 110352 Google Scholar
[36]	Qiu Z, Gong H, Zheng G, Yuan S, Zhang H, Zhu X, Zhou H, Cao B 2017 J. Mater. Chem. C 5 7084 Google Scholar
[37]	Chen W, Liu F Z, Feng X Y, Djurišić A B, Chan W K, He Z B 2017 Adv. Energy Mater. 7 1700722 Google Scholar
[38]	Ge B, Qiao H, Lin Z, Zhou Z, Chen A, Yang S, Hou Y, Yang H 2019 Sol. RRL 3 1900192 Google Scholar
[39]	Hu Z, Chen D, Yang P, Yang L, Qin L, Huang Y, Zhao X 2018 Appl. Surf. Sci. 441 258 Google Scholar
[40]	Wang S, Zhang B, Feng D, Lin Z, Zhang J, Hao Y, Fan X, Chang J 2019 J. Mater. Chem. C 7 9270 Google Scholar
[41]	Chen W, Zhou Y, Wang L, Wu Y, Tu B, Yu B, Liu F, Tam H W, Wang G, Djurisic A B, Huang L, He Z 2018 Adv. Mater. 30 1800515 Google Scholar
[42]	Chen W, Wu Y, Fan J, Djurišić A-B, Liu F, Tam H W, Ng A, Surya C, Chan W K, Wang D, He Z 2018 Adv. Energy Mater. 8 1870091 Google Scholar
[43]	Wang Z, Rong X, Wang L, Wang W, Lin H, Li X 2020 ACS Appl. Mater. & Interfaces 12 8342 Google Scholar
[44]	Li G, Jiang Y, Deng S, Tam A, Xu P, Wong M, Kwok H S 2017 Adv. Sci. 4 1700463 Google Scholar
[45]	Chen W, Wu Y, Yue Y, Liu J, Zhang W, Yang X, Chen H, Bi E, Ashraful I, Michael G, Han L 2015 Science 350 944 Google Scholar
[46]	Niu Q L, Deng Y, Cui D, Lv H, Duan X, Li Z, Liu Z, Zeng W, Xia R, Tan W, Min Y 2019 J. Mater. Sci. 54 14134 Google Scholar
[47]	He J, Xiang Y, Zhang F, Lian J, Hu R, Zeng P, Song J, Qu J 2018 Nano Energy 45 471 Google Scholar
[48]	Zhang J, Luo H, Xie W, Lin X, Hou X, Zhou J, Huang S, Ou-Yang W, Sun Z, Chen X 2018 Nanoscale 10 5617 Google Scholar
[49]	Li Z, Jo B H, Hwang S J, Kim T H, Somasundaram S, Kamaraj E, Bang J, Ahn T K, Park S, Park H J 2019 Adv. Sci. 6 1802163 Google Scholar
[50]	Wang S, Zhu Y, Wang C, Ma R 2020 Org. Electron. 78 105627 Google Scholar
[51]	Chen W, Zhou Y, Chen G, Wu Y, Tu B, Liu F Z, Huang L, Ng A M C, Djurišić A B, He Z 2019 Adv. Energy Mater. 9 1970068 Google Scholar
[52]	Wang T, Cheng Z, Zhou Y, Liu H, Shen W 2019 J. Mater. Chem. A 7 21730 Google Scholar
[53]	Zhao J, Tavakoli R, Tavakoli M-M 2019 Chem. Commun 55 9196 Google Scholar
[54]	Wang T, Xie M, Abbasi S, Cheng Z, Liu H, Shen W 2020 J. Power Sources 448 227584 Google Scholar
[55]	Wang Q, Chueh C C, Zhao T, Cheng J, Eslamian M, Choy W C H, Jen A K 2017 Chem. Sus. Chem. 10 3794 Google Scholar
[56]	Du Y, Xin C, Huang W, Shi B, Ding Y, Wei C, Zhao Y, Li Y, Zhang X 2018 ACS Sustain. Chem. Eng. 6 16806 Google Scholar
[57]	Zhai Z, Huang X, Xu M, Yuan J, Peng J, Ma W 2013 Adv. Energy Mater. 3 1614 Google Scholar
[58]	Sun Y, Chen W, Wu Y, He Z, Zhang S, Chen S 2019 Nanoscale 11 1021 Google Scholar
[59]	Wang T, Ding D, Zheng H, Wang X, Wang J, Liu H, Shen W 2019 Solar RRL 3 1900045 Google Scholar

[1]	王辉, 郑德旭, 姜箫, 曹越先, 杜敏永, 王开, 刘生忠, 张春福. 基于协同钝化策略制备高性能柔性钙钛矿太阳能电池. , 2024, 73(7): 078401. doi: 10.7498/aps.73.20231846
[2]	徐洁, 冯泽华, 刘冰野, 朱欣怡, 代锦飞, 董化, 吴朝新. 聚合物内封装层辅助空气中钙钛矿模组器件制备及其光电特性. , 2023, 72(24): 248802. doi: 10.7498/aps.72.20231055
[3]	尉渊, 邢若飞, 杜慧恬, 周倩, 范继辉, 庞智勇, 韩圣浩. 通过pH值精细调控氧化镍纳米颗粒粒度提升反式钙钛矿太阳能电池性能. , 2023, 72(1): 018101. doi: 10.7498/aps.72.20221640
[4]	王成麟, 张左林, 朱云飞, 赵雪帆, 宋宏伟, 陈聪. 钙钛矿太阳能电池中缺陷及其钝化策略研究进展. , 2022, 71(16): 166801. doi: 10.7498/aps.71.20220359
[5]	孙盟杰, 何志群, 郑毅帆, 邵宇川. EDTA/SnO₂双层复合电子传输层在钙钛矿电池中的应用. , 2022, 71(13): 137201. doi: 10.7498/aps.71.20220074
[6]	王桂强, 毕佳宇, 刘洁琼, 雷苗, 张伟. 醋酸纤维素提高CsPbIBr₂无机钙钛矿薄膜质量及其太阳能电池光电性能. , 2022, 71(1): 018802. doi: 10.7498/aps.71.20211074
[7]	罗媛, 朱从潭, 马书鹏, 朱刘, 郭学益, 杨英. 低温制备SnO₂电子传输层用于钙钛矿太阳能电池. , 2022, 71(11): 118801. doi: 10.7498/aps.71.20211930
[8]	周玚, 任信钢, 闫业强, 任昊, 杜红梅, 蔡雪原, 黄志祥. 基于双层电子传输层钙钛矿太阳能电池的物理机制. , 2022, 71(20): 208802. doi: 10.7498/aps.71.20220725
[9]	颜佳豪, 陈思璇, 杨建斌, 董敬敬. 吸收层离子掺杂提高有机无机杂化钙钛矿太阳能电池效率及稳定性. , 2021, 70(20): 206801. doi: 10.7498/aps.70.20210836
[10]	姬超, 梁春军, 由芳田, 何志群. 界面修饰对有机-无机杂化钙钛矿太阳能电池性能的影响. , 2021, 70(2): 028402. doi: 10.7498/aps.70.20201222
[11]	吴家龙, 窦永江, 张建凤, 王浩然, 杨绪勇. 溶液法制备的金属掺杂氧化镍空穴注入层在钙钛矿发光二极管上的应用. , 2020, 69(1): 018101. doi: 10.7498/aps.69.20191269
[12]	张晨, 张海玉, 郝会颖, 董敬敬, 邢杰, 刘昊, 石磊, 仲婷婷, 唐坤鹏, 徐翔. 氧化锌纳米棒形貌控制及其在钙钛矿太阳能电池中作为电子传输层的应用. , 2020, 69(17): 178101. doi: 10.7498/aps.69.20200555
[13]	李晓果, 张欣, 施则骄, 张海娟, 朱成军, 詹义强. n-i-p结构钙钛矿太阳能电池界面钝化的研究进展. , 2019, 68(15): 158803. doi: 10.7498/aps.68.20190468
[14]	范伟利, 杨宗林, 张振雲, 齐俊杰. 高效无空穴传输层碳基钙钛矿太阳能电池的制备与性能研究. , 2018, 67(22): 228801. doi: 10.7498/aps.67.20181457
[15]	刘毅, 徐征, 赵谡玲, 乔泊, 李杨, 秦梓伦, 朱友勤. 双添加剂处理电子传输层富勒烯衍生物[6，6]-苯基-C61丁酸甲酯对钙钛矿太阳能电池性能的影响. , 2017, 66(11): 118801. doi: 10.7498/aps.66.118801
[16]	肖迪, 王东明, 李珣, 李强, 沈凯, 王德钊, 吴玲玲, 王德亮. 基于氧化镍背接触缓冲层碲化镉薄膜太阳电池的研究. , 2017, 66(11): 117301. doi: 10.7498/aps.66.117301
[17]	柴磊, 钟敏. 钙钛矿太阳能电池近期进展. , 2016, 65(23): 237902. doi: 10.7498/aps.65.237902
[18]	黄林泉, 周玲玉, 于为, 杨栋, 张坚, 李灿. 石墨烯衍生物作为有机太阳能电池界面材料的研究进展. , 2015, 64(3): 038103. doi: 10.7498/aps.64.038103
[19]	丁雄傑, 倪露, 马圣博, 马英壮, 肖立新, 陈志坚. 钙钛矿太阳能电池中电子传输材料的研究进展. , 2015, 64(3): 038802. doi: 10.7498/aps.64.038802
[20]	宋志浩, 王世荣, 肖殷, 李祥高. 新型空穴传输材料在钙钛矿太阳能电池中的研究进展. , 2015, 64(3): 033301. doi: 10.7498/aps.64.033301

计量

文章访问数: 16180
PDF下载量: 707
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板