P-I-N型锡铅钙钛矿太阳电池性能的限制因素及解决策略

王俪璇; 李仁杰; 刘辉; 王鹏阳; 石标; 赵颖; 张晓丹

doi:10.7498/aps.70.20201678

摘要

锡铅钙钛矿太阳电池已被证明可以用于全钙钛矿叠层太阳电池中, 作为窄带隙底电池进一步提高器件光电转换效率. 目前, P-I-N型锡铅钙钛矿太阳电池的最高效率为21.7%, 明显低于铅基钙钛矿太阳电池. 本文分析了限制其性能提高的主要因素, 并针对性地总结了近几年研究工作者们提出的有效解决策略, 主要包括: 1)通过添加富锡化合物、强还原剂或含大的有机阳离子的化合物以抑制Sn²⁺氧化, 减少锡铅钙钛矿材料p型掺杂程度, 降低电池开路电压损耗; 2)通过调控组分、改变钙钛矿薄膜制备方法、溶剂工程或添加含功能性基团的化合物以延缓锡铅钙钛矿薄膜结晶生长速率, 提高薄膜质量; 3)通过选用合适的电子传输层或空穴传输层, 减少能级失配对载流子传输的影响或避免载流子传输层的本身不稳定性对器件的影响. 最后, 本文展望了锡铅钙钛矿太阳电池的未来发展, 认为其不仅有望实现高效稳定的单结太阳电池, 而且还可以应用于高效全钙钛矿叠层太阳电池.

关键词:

Abstract

In order to break through the limit of Shockley-Queisser (SQ) radiation and further improve the efficiency of perovskite solar cells, tin-lead perovskite solar cells have widely and successfully been used as narrow-bandgap bottom cells in all-perovskite tandem solar cells. The highest efficiency of tin-lead perovskite solar cells has recently reached 21.7%, which, however, is still lower than that of lead-based perovskite solar cells. This article analyzes the main factors that limit the further improving of their performances, and summarizes the effective solutions proposed by researchers in recent years. The main points are as follows: 1) by adding tin-rich additives, strong reducing agents or compounds containing large organic cations, Sn²⁺ oxidation is inhibited and the p-doped degree of tin-lead perovskite and the open-circuit voltage loss are reduced; 2) through regulating the composition, changing the method of preparing the perovskite film, adding functional groups or solvent engineering, the crystallization rate of tin-lead perovskite film is delayed and the crystallization quality of the film is improved; 3) by selecting an appropriate electron transport layer or hole transport layer the influence of energy level mismatch on carrier transport or the instability of carrier transport layer on devices can be avoided. Finally, the future development of Sn-Pb perovskite solar cells is prospected. It is believed that the tin-lead perovskite solar cells can realize not only the high efficiency and stable single-junction solar cells, but also high efficiency perovskite-perovskite tandem solar cells.

Keywords:

作者及机构信息

1.
南开大学, 光电子薄膜器件与技术研究所, 太阳能转换中心, 天津　300350

2.
天津市光电子薄膜器件与技术重点实验室, 天津　300350

3.
薄膜光电子技术教育部工程研究中心, 天津　300350

4.
化学科学与工程协同创新中心, 天津　300072

5.
南开大学可再生能源转换与储存中心, 天津　300072

通信作者: 张晓丹, xdzhang@nankai.edu.cn

基金项目: 国家重点研发计划(批准号: 2018YFB1500103)、国家自然科学基金(批准号: 61674084)、高等学校学科创新引智计划(111 计划)(批准号: B16027)、天津市军民融合科技重大专项(批准号: 18ZXJMTG00220)和中央高校基本科研业务费(批准号: 63201171, 63201173)资助的课题

Authors and contacts

1.
Solar Energy Conversion Center, Institute of Photoelectronic Thin Film Devices and Technology, Nankai University, Tianjin 300350, China

2.
Key Laboratory of Photoelectronic Thin Film Devices and Technology of Tianjin, Tianjin 300350, China

3.
Engineering Research Center of Thin Film Photoelectronic Technology of Ministry of Education, Tianjin 300350, China

4.
Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072, China

5.
Renewable Energy Conversion and Storage Center, Nankai University, Tianjin 300072, China

Corresponding author: Zhang Xiao-Dan, xdzhang@nankai.edu.cn

Funds: Project supported by the National Research Program of China (Grant No. 2018YFB1500103), the National Natural Science Foundation of China (Grant No. 61674084), the 111 Project, China (Grant No. B16027), the Tianjin Civil Military Integration Project, China (Grant No. 18ZXJMTG00220), and the Fundamental Research Funds for the Central Universities, China (Grant Nos. 63201171, 63201173)

文章全文 : translate this paragraph

参考文献

[1]	Akihiro K, Kenjiro T, Yasuo S, Tsutomu M 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[2]	Best research-cell efficiencies https://www.nrel.gov/pv/cell-efficiency.html.
[3]	Shockley W, Queisser H J 1961 J. Appl. Phys. 32 510 Google Scholar
[4]	Xiao K, Lin R X, Han Q L, Hou Y, Qin Z Y, Nguyen H T, Wen J, Wei M Y, Yeddu V, Saidaminov M I, Gao Y, Luo X, Wang Y R, Gao H, Zhang C F, Xu J, Zhu J, Sargent E H, Tan H R 2020 Nat. Energy 5 870 Google Scholar
[5]	Ogomi Y, Morita A, Tsukamoto S, Saitho T, Fujikawa N, Shen Q, Toyoda T, Yoshino K, Pandey S S, Ma T L, Hayase S 2014 J. Phys. Chem. Lett. 5 1004 Google Scholar
[6]	Im J, Stoumpos C C, Jin H, Freeman A J, Kanatzidis M G 2015 J. Phys. Chem. Lett. 6 3503 Google Scholar
[7]	Eperon G E, Leijtens T, Bush K A, et al. 2016 Science 354 86 Google Scholar
[8]	Hao F, Stoumpos C C, Chang R P H, Kanatzidis M G 2014 J. Am. Chem. Soc. 136 8094 Google Scholar
[9]	Klug M T, Milot R L, Patel J B, Green T, Sansom H C, Farrar M D, Ramadan A J, Martani S, Wang Z P, Wenger B, Ball J M, Langshaw L, Petrozza A, Johnston M B, Herz L M, Snaith H J 2020 Energy Environ. Sci. 14 112
[10]	Gu S, Lin R X, Han Q L, Gao Y, Tan H R, Zhu J 2020 Adv. Mater. 32 1907392
[11]	Yao H H, Zhou F G, Li Z Z, Ci Z P, Ding L M, Jin Z W 2020 Adv. Sci. 7 1903540 Google Scholar
[12]	Zhu Z L, Chueh C C, Li N, Mao C Y, Jen A K Y 2018 Adv. Mater. 30 1703800 Google Scholar
[13]	Li J M, Cao H L, Jiao W B, Wang Q, Wei M D, Cantone I, Lü J, Abate A 2020 Nat. Commun. 11 310 Google Scholar
[14]	Tchounwou P B, Yedjou C G, Patlolla A K, Sutton D J 2012 Molecular, Clinical and Environmental Toxicology (Vol. 101) (Jackson: Springer, Basel.) p133
[15]	Nishimura K, Kamarudin M A, Hirotani D, Hamada K, Shen Q, Iikubo S, Minemoto T, Yoshino K, Hayase S 2020 Nano Energy 74 104858 Google Scholar
[16]	Leijtens T, Prasanna R, Parker A G, Toney M F, McGehee M D 2017 ACS Energy Lett. 2 2159 Google Scholar
[17]	Yan Y J, Pullerits T, Zheng K B, Liang Z Q 2020 ACS Energy Lett. 5 2052 Google Scholar
[18]	Lin R X, Xiao K, Qin Z Y, Han Q L, Zhang C F, Wei M Y, Saidaminov M I, Gao Y, Xu J, Xiao M, Li A D, Zhu J, Sargent E H, Tan H R 2019 Nat. Energy 4 864 Google Scholar
[19]	Ricciarelli D, Meggiolaro D, Ambrosio F, Angelis F D 2020 ACS Energy Lett. 5 2787 Google Scholar
[20]	Chung I, Song J H, Im J, Androulakis J, Malliakas C D, Li H, Freeman A J, Kenney J T, Kanatzidis M G 2012 J. Am. Chem. Soc. 134 8579 Google Scholar
[21]	Ma L, Hao F, Stoumpos C C, Phelan B T, Wasielewski M R, Kanatzidis M G 2016 J. Am. Chem. Soc 138 14750 Google Scholar
[22]	Yang Z B, Rajagopal A, Jen A K Y 2017 Adv. Mater. 29 1704418 Google Scholar
[23]	Noel N K, Stranks S D, Abate A, Wehrenfennig C, Guarnera S, Haghighirad A A, Sadhanala A, Eperon G E, Pathak S K, Johnston M B, Petrozza A, Herza L M, Snaith H J 2014 Energy Environ. Sci. 7 3061 Google Scholar
[24]	Wang J K, Datta K, Li J Y, Verheijen M A, Zhang D, Wienk M M, Janssen R A J 2020 Adv. Energy Mater. 10 2000566 Google Scholar
[25]	Hao F, Stoumpos C C, Guo P J, Zhou N J, Marks T J, Chang R P H, Kanatzidis M G 2015 J. Am. Chem. Soc. 137 11445 Google Scholar
[26]	Liao W Q, Zhao D W, Yu Y, Shrestha N, Ghimire K, Grice C R, Wang C L, Xiao Y Q, Cimaroli A J, Ellingson R J, Podraza N J, Zhu K, Xiong R G, Yan Y F 2016 J. Am. Chem. Soc. 138 12360 Google Scholar
[27]	Chi D, Huang S H, Zhang M Y, Mu S Q, Zhao Y, Chen Y, You J B 2018 Adv. Funct. Mater. 28 1804603 Google Scholar
[28]	Wang C L, Song Z N, Li C W, Zhao D W, Yan Y F 2019 Adv. Funct. Mater. 29 1808801 Google Scholar
[29]	Tavakoli M M, Zakeeruddin S M, Grätzel M, Fan Z Y 2018 Adv. Mater. 30 1705998 Google Scholar
[30]	Zhao D W, Chen C, Wang C L, Junda M M, Song Z N, Grice C R, Yu Y, Li C W, Subedi B, Podraza N J, Zhao X Z, Fang G J, Xiong R G, Zhu K, Yan Y F 2018 Nat. Energy 3 1093 Google Scholar
[31]	Kumar M H, Dharani S, Leong W L, Boix P P, Prabhakar R R, Baikie T, Shi C, Ding H, Ramesh R, Asta M, Graetzel M, Mhaisalkar S G, Mathews N 2014 Adv. Mater. 26 7122 Google Scholar
[32]	Xiao M, Gu S, Zhu P C, Tang M Y, Zhu W D, Lin R X, Chen C L, Xu W C, Yu T, Zhu J 2018 Adv. Opt. Mater. 6 1700615 Google Scholar
[33]	Gupta S, Cahen D, Hodes G 2018 J. Phys. Chem. C 122 13926 Google Scholar
[34]	Liao W Q, Zhao D W, Yu Y, Grice C R, Wang C L, Cimaroli A J, Schulz P, Meng W W, Zhu K, Xiong R G, Yan Y F 2016 Adv. Mater. 28 9333 Google Scholar
[35]	Lee S J, Shin S S, Kim Y C, Kim D, Ahn T K, Noh J H, Seo J, and Seok S I 2016 J. Am. Chem. Soc. 138 3974 Google Scholar
[36]	Zong Y X, Zhou Z M, Chen M, Padture N P. Zhou Y Y 2018 Adv. Energy Mater. 8 1800997 Google Scholar
[37]	Chung I, Lee B, He J Q, Chang R P H, Kanatzidis M G 2012 Nature 485 486 Google Scholar
[38]	Xu X B, Chueh C C, Yang Z B, Rajagopal A, Xu J Q, Jo S B, Jen A K Y 2017 Nano Energy 34 392 Google Scholar
[39]	Zhu Z L, Li N, Zhao D B, Wang L D, Jen A K Y 2019 Adv. Energy Mater. 9 1802774 Google Scholar
[40]	Saidaminov M I, Spanopoulos I, Abed J, Ke W J, Wicks J, Kanatzidis M G, and Sargent E H 2020 ACS Energy Lett. 5 1153 Google Scholar
[41]	Cao D H, Stoumpos C C, Farha O K, Hupp J T, Kanatzidis M G 2015 J. Am. Chem. Soc. 137 7843 Google Scholar
[42]	Wei M Y, Xiao K, Walters G, Lin R X, Zhao Y B, Saidaminov M I, Todorović P, Johnston A, Huang Z R, Chen H J, Li A D, Zhu J, Yang Z Y, Wang Y K, Proppe A H, Kelley S O, Hou Y, Voznyy O, Tan H R, Sargent E H 2020 Adv. Mater. 32 1907058 Google Scholar
[43]	Ramirez D, Schutt K, Wang Z P, Pearson A J, Ruggeri E, Snaith H J, Stranks S D, Jaramillo F 2018 ACS Energy Lett. 3 2246 Google Scholar
[44]	Li C H, Pan Y M, Hu J L, Qiu S D, Zhang C L, Yang Y Z, Chen S, Liu X H, Brabec C J, Nazeeruddin M K, Mai Y H, Guo F 2020 ACS Energy Lett. 5 1386 Google Scholar
[45]	Yang D W, Lv J, Zhao X G, Xu Q L, Fu Y H, Zhan Y Q, Zunger A, Zhang L J 2017 Chem. Mater. 29 524 Google Scholar
[46]	Green M A, Baillie A H, Snaith H J 2014 Nat. Photon. 8 506 Google Scholar
[47]	Bartel C J, Sutton C, Goldsmith B R, Ouyang R H, Musgrave C B, Ghiringhelli L M, Scheffler M 2019 Sci. Adv. 5 eaav0693 Google Scholar
[48]	Shi T T, Zhang H S, Meng W W, Teng Q, Liu M Y, Yang X B, Yan Y F, Yip H L, Zhao Y J 2017 J. Mater. Chem. A 5 15124 Google Scholar
[49]	Yang Z B, Rajagopal A, Chueh C C, Jo S B, Liu B, Zhao T, Jen A K Y 2016 Adv. Mater. 28 8990 Google Scholar
[50]	Lee J W, Kim D H, Kim H S, Seo S W, Cho S M, Park N G 2015 Adv. Energy Mater. 5 1501310 Google Scholar
[51]	Prasanna R, Leijtens T, Dunfield S P, Raiford J A, Wolf E J, Swifter S A, Werner J, Eperon G E, Paula C d, Palmstrom A F, Boyd C C, Hest M F A M, Bent S F, Teeter G, Berry J J, McGehee M D 2019 Nat. Energy 4 939 Google Scholar
[52]	Han Q L, Wei Y, Lin R X, Fang Z M, Xiao K, Luo X, Gu S, Zhu J, Ding L M, Tan H R 2019 Sci. Bull. 64 1399 Google Scholar
[53]	Li C W, Song Z N, Zhao D W, Xiao C X, Subedi B, Shrestha N, Junda M M, Wang C L, Jiang C S, Jassim M A, Ellingson R J, Podraza N J, Zhu K, Yan Y F 2018 Adv. Energy Mater. 9 1803135
[54]	Lian X M, Chen J H, Zhang Y Z, Qin M C, Li J, Tian S X, Yang W T, Lu X H, Wu G, Chen H Z 2019 Adv. Funct. Mater. 29 1807024 Google Scholar
[55]	Tong J H, Song Z N, Kim D H, Chen X H, Chen C, Palmstrom A F, Ndione P F, Reese M O, Dunfield S P, Reid O G, Liu J, Zhang F, Harvey S P, Li Z, Christensen S T, Teeter G, Zhao D W, Jassim M M A, Hest M F A M, Beard M C, Shaheen S E, Berry J J, Yan Y F, Zhu K 2019 Science 364 475 Google Scholar
[56]	Zhu H L, Xiao J Y, Mao J, Zhang H, Zhao Y, Choy W C H 2017 Adv. Funct. Mater. 27 1605469 Google Scholar
[57]	Konstantakou M, Stergiopoulos T 2017 J. Mater. Chem. A 5 11518 Google Scholar
[58]	Ke W J, Stoumpos C C, Kanatzidis M G 2018 Adv. Mater. 31 1803230 Google Scholar
[59]	Zhu L Z, Yuh B, Schoen S, Li X P, Aldighaithir M, Richardson B J, Alamera A, Yu Q M 2016 Nanoscale 8 7621 Google Scholar
[60]	Liu M Y, Chen Z M, Xue Q F, Cheung S H, So S K, Yip H L, Cao Y 2018 J. Mater. Chem. A 6 16347 Google Scholar
[61]	Nejand B A, Hossain I M, Jakoby M, Moghadamzadeh S, Abzieher T, Gharibzadeh S, Schwenzer J A, Nazari P, Schackmar F, Hauschild D, Weinhardt L, Lemmer U, Richards B S, Howard I A, Paetzold U W 2019 Adv. Energy Mater. 10 1902580 Google Scholar
[62]	Ball J M, Buizza L, Sansom H C, Farrar M D, Klug M T, Borchert J, Patel J, Herz L M, Johnston M B, Snaith H J 2019 ACS Energy Lett. 4 2748 Google Scholar
[63]	Wu Y Z, Islam A, Yang X D, Qin C J, Liu J, Zhang K, Peng W Q, Han L Y 2014 Energy Environ. Sci. 7 2934 Google Scholar
[64]	Liu C, Fan J D, Li H L, Zhang C L, Mai Y H 2016 Sci. Rep. 6 35705 Google Scholar
[65]	Liu C, Li W Z, Li H L, Zhang C L, Fan J D, Mai Y H 2017 Nanoscale 9 13967 Google Scholar
[66]	Zhou X Y, Zhang L Z, Wang X Z, Liu C, Chen S, Zhang M Q, Li X N, Yi W D, Xu B M 2020 Adv. Mater. 32 1908107 Google Scholar
[67]	Hu M Y, Chen M, Guo P J, Zhou H, Deng J J, Yao Y D, Jiang Y, Gong J, Dai Z H, Zhou Y X, Qian F, Chong X Y, Feng J, Schaller R D, Zhu K, Padture N P, Zhou Y Y 2020 Nat. Commun. 11 151 Google Scholar
[68]	Yang Z B, Yu Z H, Wei H T, Xiao X, Ni Z Y, Chen B, Deng Y H, Habisreutinger S N., Chen X H, Wang K, Zhao J J, Rudd P N, Berry J J, Beard M C, Huang J S 2019 Nat. Commun. 10 4498 Google Scholar
[69]	Kapil G, Ripolles T S., Hamada K, Ogomi Y, Bessho T, Kinoshita T, Chantana J, Yoshino K, Shen Q, Toyoda T, Minemoto T, Murakami T N, Segawa H, Hayase S 2018 Nano Lett. 18 3600 Google Scholar
[70]	Minemoto T, Matsui T, Takakura H, Hamakawa Y, Negami T, Hashimoto Y, Uenoyama T, Kitagawa M 2001 Sol. Energy Mater. Sol. Cells 67 83 Google Scholar
[71]	Zhou X Y, Hua M M, Liu C, Zhang L Z, Zhong X W, Li X N, Tian Y Q, Cheng C, Xu B M 2019 Nano Energy 63 103866 Google Scholar
[72]	Liu J W, Ozaki M, Yakumaru S, Handa T, Nishikubo R, Kanemitsu Y, Saeki A, Murata Y, Murdey R, Wakamiya A 2018 Angew. Chem 130 13405 Google Scholar
[73]	Li C W, Song Z N, Zhao D W, Xiao C X, Subedi B, Shrestha N, Junda M M, Wang C L, Jiang C S, Jassim M A, Ellingson R J, Podraza N J, Zhu K, Yan Y F 2019 Adv. Energy Mater. 9 1803135 Google Scholar
[74]	Jiang T M, Chen Z, Chen X, Liu T Y, Chen X Y, Sha W E I, Zhu H M, Yang Y 2020 Sol. RRL 4 1900467 Google Scholar
[75]	Yang Z B, Zhang X H, Yang W Y, Eperon G E, Ginger D S 2020 Chem. Mater. 32 2782 Google Scholar
[76]	Zhu Z L, Bai Y, Zhang T, Liu Z K, Long X, Wei Z H, Wang Z L, Zhang L X, Wang J N, Yan F, Yang S H 2014 Angew. Chem 53 12571
[77]	Jeng J Y, Chen K C, Chiang T Y, Lin P Y, Tsai T D, Chang Y C, Guo T F, Chen P, Wen T C, Hsu Y J 2014 Adv. Mater. 26 4107 Google Scholar
[78]	Garcia A, Welch G C, Ratcliff E L, Ginley D S, Bazan G C, Olson D C 2012 Adv. Mater. 24 5368 Google Scholar
[79]	Manders J R, Tsang S W, Hartel M J, Lai T H, Chen S, Amb C M, Reynolds J R, So F 2013 Adv. Funct. Mater. 23 2993 Google Scholar
[80]	Yu Z H, Yang Z B, Ni Z Y, Shao Y C, Chen B, Lin Y Z, Wei H T, Yu Z S J, Holman Z, Huang J S 2020 Nat. Energy 5 657 Google Scholar
[81]	Tang H Y, Shang Y Q, Zhou W J, Peng Z J, Ning Z J 2019 Sol. RRL 3 1800256 Google Scholar
[82]	Xu G Y, Bi P Q, Wang S H, Xue R M, Zhang J W, Chen H Y, Chen W J, Hao X T, Li Y W, Li Y F 2018 Adv. Funct. Mater. 28 1804427 Google Scholar
[83]	Ni Z Y, Bao C X, Liu Y, Jiang Q, Wu W Q, Chen S S, Dai X Z, Chen B, Hartweg B, Yu Z S, Holman Z, Huang J S 2020 Science 367 1352 Google Scholar
[84]	Chen Y H, Li N X, Wang L G, Li L, Xu Z Q, Jiao H Y, Liu P F, Zhu C, Zai H C, Sun M Z, Zou W, Zhang S, Xing G C, Liu X F, Wang J P, Li D D, Huang B L, Chen Q, Zhou H P 2019 Nat. Commun. 10 1112 Google Scholar

施引文献

图 1 提高P-I-N型锡铅钙钛矿太阳电池性能的解决策略

Fig. 1. Solutions to improve the performance of P-I-N type tin lead perovskite solar cells.

下载: 全尺寸图片幻灯片

图 2 钙钛矿材料的能带结构随着金属比例的变化而调整　(a) Ogomi等^[5]表征CH₃NH₃Sn_1–xPb_xI₃能带结构随金属比例的变化; (b) Eperon等^[7]通过Tauc plot、PL及第一性原理计算FASn_xPb_1–xI₃带隙随金属比例的变化趋势; (c) Hao等^[8]通过紫外吸收光谱表征CH₃NH₃Sn_1–xPb_xI₃的带隙变化

Fig. 2. The energy band of Sn-Pb perovskite changed with the metal ratios: (a) Ogomi et al.^[5] characterized the CH₃NH₃Sn_1–xPb_xI₃ energy band structure changed with the metal ratio; (b) Eperon et al.^[7] used the Tauc plot, PL and first-principles calculations to obtain the variable trend of HC(NH₂)₂Sn_xPb_1–xI₃(FASn_xPb_1–xI₃) band gap with metal proportions; (c) Hao et al.^[8] characterized the band gap changes of CH₃NH₃Sn_1–xPb_xI₃ by electronic absorption spectra.

下载: 全尺寸图片幻灯片

图 3 不同结构的Sn-Pb钙钛矿太阳电池器件效率进展图, 包括N-I-P型(绿色)和P-I-N型(红色)结构

Fig. 3. The efficiency progress diagram of Sn-Pb perovskite solar cells in different structures, including N-I-P (green) and P-I-N (red) structures.

下载: 全尺寸图片幻灯片

图 4 (a)不同SnF₂添加量的钙钛矿薄膜扫描电子显微镜(scanning electron microscope, SEM)扫描图^[34]; (b) Zhu等^[39]利用伽伐尼置换反应(GDR)制备MAPb_xSn_1–xI₃钙钛矿溶液的照片和示意图以及薄膜老化过程机制示意图; (c)由于前驱体溶液中存在Sn⁴⁺而在Sn-Pb钙钛矿中形成锡空位的示意图^[18]; (d) Wei等^[42]利用PEAI实现Sn-Pb钙钛矿表面钝化或膜内钝化的处理方法示意图; (e) Ramirez等^[43]引入叔丁胺离子n = 4和n = 5的Sn-Pb钙钛矿晶格示意图; (f) Li等^[44]引入4-氟苯乙基碘化铵(FPEAI)使(MAPbI₃)_0.75(FASnI₃)_0.25晶粒高度垂直排列的示意图及未使用与使用(FPEAI)的器件J-V曲线

Fig. 4. (a) SEM images of perovskite films with different SnF₂ additions^[34]; (b) photos and schematic diagrams of preparing MAPb_xSn_1–xI₃ precursor solution using GDR and the schematic diagram of film aging process^[39]; (c) the schematic diagram of tin vacancies formation in Sn-Pb perovskite due to the presence of Sn⁴⁺ in the precursor solution^[18]; (d) Wei et al. ^[42]used PEAI to achieve surface passivation or in-film passivation of Sn-Pb perovskit; (e) the schematic diagram of Sn-Pb perovskite lattice with n = 4 and n = 5 introduced by Ramirez et al.^[43]; (f) Li et al.^[44]introduced FPEAI to vertically arrange the (MAPbI₃)_0.75(FASnI₃)_0.25 grain height and the J-V curve of unused and used FPEAI devices.

下载: 全尺寸图片幻灯片

图 5 (a) AMX₃型钙钛矿材料常用元素组分及不同组分的材料性质^[45]; (b) FA⁺掺入对MA_1–yFA_yPb_0.75Sn_0.25I₃钙钛矿器件稳定性的影响^[49]; (c)由计算和实验所得的MASn_1–xPb_xI₃带隙随x的变化^[6]; (d)不同Sn-Pb比例的FA_0.66MA_0.34Pb_1–xSn_xI₃钙钛矿的XRD图谱^[24]; (e) Br含量分别为0, 6%和16%的Sn-Pb钙钛矿太阳电池的暗态J-V曲线^[53]; (f)未掺入Cl和掺入2.5% Cl对钙钛矿薄膜的SEM扫描图^[30]; (g)掺入不同比例(0, 15%, 25%, 40%)MASCN对薄膜钙钛矿薄膜的SEM顶部扫描图及横截面扫描图^[54]

Fig. 5. (a) The commonly used element compositions and their properties of AMX₃^[45]; (b) FA⁺-doping effects to the stability of MA_1–yFA_yPb_0.75Sn_0.25I₃ perovskite devices^[49]; (c) the band gap variation with x changes of MASn_1–xPb_xI₃ obtained from calculations and experiments^[6]; (d) XRD patterns of FA_0.66MA_0.34Pb_1–xSn_xI₃ perovskites with different Sn-Pb ratios^[24]; (e) dark J-V curves of Sn-Pb perovskite solar cells with Br concentrations of 0, 6% and 16% respectively^[53]; (f) SEM images of perovskite films without Cl and with 2.5% Cl^[30]; (g) the top and cross-section SEM images of perovskite films mixed with 0, 15%, 25%, 40% of MASCN^[54].

下载: 全尺寸图片幻灯片

图 6 (a)两步顺序沉积结合DMSO溶剂蒸气处理的方式制备MASn_0.1Pb_0.9I₃的过程示意图^[59]; (b)两步顺序沉积FA_0.66MA_0.34Pb_0.5Sn_0.5I₃的过程示意及原位吸收光谱图^[24]

Fig. 6. (a) The schematic diagram of the two-step sequential depositions combined with DMSO solvent vapor treatment method to prepare MASn_0.1Pb_0.9I₃ perovskite films^[59]; (b) the schematic diagram of the two-step sequential deposition process of FA_0.66MA_0.34Pb_0.5Sn_0.5I₃ and in-situ absorption spectra^[24].

下载: 全尺寸图片幻灯片

图 7 (a)真空辅助热退火结合一步溶液法制备的器件结构及原理示意图^[60]; (b)使用/不使用真空辅助热退火所制备的薄膜形貌顶部SEM图^[60]; (c)真空辅助生长(VAGC)方法的原理示意图及横截面SEM图像^[61]; (d)双源共蒸法制备FA_1–xCs_xSn_1–yPb_yI₃钙钛矿薄膜过程示意图及晶体结构示意图^[62]

Fig. 7. (a) Device architecture and schematic diagram that combined the vacuum-assisted thermal annealing process and one-step solution method^[60]; (b) the top SEM images of the film prepared with/without vacuum-assisted thermal annealing^[60]; (c) the schematic diagram and cross-section SEM image of the film prepared by VAGC method^[61]; (d) the schematic diagram and crystal structure of FA_1–xCs_xSn_1–yPb_yI₃ perovskite films prepared by dual-source co-evaporation method^[62].

下载: 全尺寸图片幻灯片

图 8 (a)不同DMSO/DMF溶剂比的Sn-Pb钙钛矿反应机理示意图^[56]; (b) MAPb_1–xSn_xI₃(0 ≤ x ≤ 1)薄膜的形成机理以及相应的晶体结构示意图^[64]; (c)在不同偏置电压下未掺杂及掺杂C₆₀的MAPb_0.75Sn_0.25I₃钙钛矿器件的本体复合寿命和表面复合寿命^[65]

Fig. 8. (a) The mechanism diagram of Sn-Pb perovskite reactions with different DMSO/DMF solvent ratio^[56]; (b) the formation mechanisms of MAPb_1–xSn_xI₃ (0 ≤ x ≤ 1) film and corresponding crystal structures^[64]; (c) bulk recombination life and surface recombination life of MAPb_0.75Sn_0.25I₃ perovskite devices with or without C₆₀-doped under different amplitude voltages^[65].

下载: 全尺寸图片幻灯片

图 9 (a)含GABr的FA_0.7MA_0.3Pb_0.7Sn_0.3I₃表面的电荷密度分布图(等电势为0.03 eÅ^–3)以及未添加与添加12%的GABr的钙钛矿SEM扫描图^[66]; (b)添加CdI₂的1.22 eV窄带隙钙钛矿与1.80 eV宽带隙钙钛矿叠层太阳电池的结构示意图和SEM横截面扫描图^[68]; (c) (4AMP)²⁺, 哌嗪离子和PEA⁺阳离子的结构式及用(4AMP)I₂, 碘化哌嗪和PEAI表面处理的CsPb_0.6Sn_0.4I₃钙钛矿太阳电池的J-V曲线^[67]

Fig. 9. (a) The charge density distribution on the FA_0.7MA_0.3Pb_0.7Sn_0.3I₃ surface containing GABr (the isopotential is 0.03 eÅ^–3) and the SEM images of the perovskite without and with 12% GABr^[66]; (b) structure diagram and cross-section SEM inage of 1.22 eV narrow-bandgap perovskite with CdI₂ added and 1.80 eV wide-bandgap perovskite tandem solar cell^[68]; (c) structure of(4AMP)²⁺, piperazine ion and PEA⁺ and J-V curves of CsPb_0.6Sn_0.4I₃ perovskite solar cell that absorber film surface treated with (4AMP)I₂, piperazine iodide and PEAI, respectively^[67].

下载: 全尺寸图片幻灯片

图 10 (a) Kapil等^[69]对比传统无PCBM层和带PCBM层的电荷提取和复合过程示意图, τ_r表示从FAMA到C₆₀的载流子注入时间; (b)添加DF-C₆₀形成的梯度异质结(GHJ)结构示意图^[72]; (c)在NiO_x及PEDOT:PSS上沉积钙钛矿膜的SEM顶部扫描图及截面扫描图^[27]; (d)使用BHJ PBDB-T:ITIC中间层形成的逐步升高的HOMO能级结构示意图^[82]; (e) S-乙酰硫代胆碱氯化物分子锚定在缺陷部位的示意图, 其中红色、黄色和蓝色符号分别代表S-乙酰硫代胆碱氯化物分子中的O原子、S原子和N原子^[71]

Fig. 10. (a) The diagram of Kapil et al^[69]. compared the traditional charge extraction and recombination process without and with PCBM, τ_r represents the carrier injection time from FAMA to C₆₀; (b) the schematic diagram of the gradient heterojunction (GHJ) with DF-C₆₀^[72]; (c) the top and cross-section SEM images of the perovskite films deposited on NiO_x and PEDOT:PSS^[27]; (d) the schematic diagram of the gradually increasing HOMO energy level structure formed by BHJ PBDB-T:ITIC intermediate layer^[82]; (e) the schematic diagram of the S-acetylthiocholine chloride molecule anchored at the defect sites, where the red, yellow and blue symbols represent the O atom, S atom and N atom in the acetylthiocholine chloride molecule, respectively^[71].

下载: 全尺寸图片幻灯片

表 A1 P-I-N型Sn-Pb钙钛矿太阳电池性能统计

Table A1. Statistics of P-I-N type tin-lead perovskite solar cells performance

Year	Perovskite	Device structure	Eg/eV	V_OC/V	J_SC/(mA·cm^–2)	FF/%	PCE/(%)	Ref.
2016	MA_0.5FA_0.5Pb_0.75Sn_0.25I₃	ITO/PEDOT:PSS/PVK/PCBM/Bis-C₆₀/Ag	1.33	0.78	23.03	79	14.19	[49]
2016	(FASnI₃)_0.6(MAPbI₃)_0.4	ITO/PEDOT:PSS/PVK/C₆₀/BCP/Ag	1.25	0.795	26.86	70.6	15.08	[26]
2017	MA_0.5FA_0.5Pb_0.5Sn_0.5I₃	ITO/PEDOT:PSS/PVK/PCBM/Bis-C₆₀/Ag	1.2	0.78	25.69	70	14.01	[38]
2017	MAPb_0.5Sn_0.5I₃	ITO/PEDOT:PSS/PVK-DF-C₆₀/ICBA/Bis-C₆₀/Ag	1.22	0.87	26.1	69	15.61	[72]
2018	(t-BUA)₂(FA_0.85Cs_0.15)_n–1 Pb_0.6Sn_0.4)_nI_3n+1	ITO/PEDOT:PSS/2 D-PVK/PCBM/BCP/Ag	1.24	0.70	24.2	63	10.6	[43]
2018	FA_0.6MA_0.4Sn_0.6Pb_0.4I₃	ITO/PFI-(PEDOT:PSS)/PVK/PCBM/BCP/Ag	1.22	0.784	27.22	74.36	15.85	[81]
2018	(FAPbI₃)_0.7(CsSnI₃)_0.3	ITO/PEDOT:PSS/PVK/C₆₀/BCP/Al	1.3	0.74	25.89	81.4	15.6	[36]
2018	(FASnI₃)_0.6(MAPbI₃)_0.34(MAPbBr₃)_0.06	ITO/PEDOT:PSS/PVK/C₆₀/BCP/Ag	1.272	0.888	28.72	74.6	19.03	[53]
2018	(FASnI₃)_0.6(MAPbI₃)_0.4	ITO/PEDOT:PSS/PVK/C₆₀/BCP/Ag	1.25	0.841	29.0	74.4	18.1	[30]
2018	FAPb_0.7Sn_0.3I₃	ITO/PEDOT:PSS/PVK/PEAI/PC₆₁BM/BCP/Ag	1.34	0.78	26.46	79	16.26	[54]
2018	FAPb_0.75Sn_0.25I₃	ITO/NiO_X/PVK/PC₆₀BM/BCP/Ag	1.36	0.81	28.23	75.4	17.25	[27]
2018	(FASnI₃)_0.6(MAPbI₃)_0.4	ITO/PEDOT:PSS/PBDBT:ITIC/PVK/C₆₀/BCP/Ag	1.25	0.86	27.92	75.1	18.03	[82]
2019	FA_0.8MA_0.2Sn_0.5Pb_0.5I₃	ITO/PEDOT:PSS/PVK/PCBM/BCP/Ag	1.27	0.81	30	75	18.2	[61]
2019	(FAPb_0.6Sn_0.4I₃)_0.85(MAPb_0.6Sn_0.4Br₃)_0.15	ITO/PEDOT:PSS/PVK/PCBM/BisC₆₀/Ag	1.28	0.87	26.45	79.1	18.21	[39]
2019	FA_0.7MA_0.3Pb_0.5Sn_0.5I₃	ITO/PEDOT:PSS/PVK/PC₆₀BM/BCP/Cu	1.22	0.831	31.4	80.8	21.1	[18]
2019	Cs_0.1MA_0.2FA_0.7Pb_0.5Sn_0.5I₃	ITO/NiO_X/PVK/C₆₀/BCP/Cu	1.2	0.771	31.1	73.3	17.6	[52]
2019	FA_0.75Cs_0.25Sn_0.4Pb_0.6I₃	ITO/PVK/C₆₀/BCP/Ag	1.25	0.72	32.59	69.8	16.4	[51]
2019	(FASnI₃)_0.6(MAPbI₃)_0.4	ITO/PEDOT:PSS/PVK/C₆₀/BCP/Ag	1.25	0.834	30.4	80.8	20.5	[55]
2019	Cs_0.1MA_0.2FA_0.7Sn_0.5Pb_0.5I₃	ITO/NiO_X/PVK/C₆₀/BCP/Cu	1.2	0.771	31.1	73.3	17.6	[52]
2020	(MAPbI₃)_0.75(FASnI₃)_0.25	ITO/PEDOT:PSS/PVK/BCP/Ag	1.33	0.79	28.42	78	17.51	[44]
2020	Cs_0.1MA_0.2FA_0.7Pb_0.5Sn_0.5I₃	ITO/PEDOT:PSS/PVK/PCBM/PEIE/Ag	1.25	0.81	30.3	78.9	19.4	[42]
2020	FA_0.83Cs_0.17Pb_0.7Sn_0.3I₃	ITO/PEDOT:PSS/PVK/PCBM/BCP/Ag	1.3	0.82	30.3	78.4	18.1	[9]
2020	FA_0.7MA_0.3Pb_0.7Sn_0.3I₃	ITO/PEDOT:PSS(EMIC)/PVK/S-acetylthiocholine chlorde/C₆₀/BCP/Ag	1.35	1.02	26.61	76	20.63	[66]
2020	FA_0.66MA_0.34Pb_0.5Sn_0.5I₃	ITO/PEDOT:PSS/PVK/C₆₀/BCP/Ag	1.23	0.78	27.8	73	15.8	[54]
2020	FA_0.5MA_0.45Cs_0.05Pb_0.5Sn_0.5I₃	ITO/PEDOT:PSS/PTAA/Cd-PVK/C₆₀/BCP/Cu	1.22	0.85	30.2	79	20.3	[68]
2020	FA_0.7MA_0.3Pb_0.5Sn_0.5I₃	ITO/PEDOT:PSS/PVK/C₆₀/BCP/Cu	1.24	0.85	31.6	80.8	21.7	[4]

下载: 导出CSV

map

[1]	Akihiro K, Kenjiro T, Yasuo S, Tsutomu M 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[2]	Best research-cell efficiencies https://www.nrel.gov/pv/cell-efficiency.html.
[3]	Shockley W, Queisser H J 1961 J. Appl. Phys. 32 510 Google Scholar
[4]	Xiao K, Lin R X, Han Q L, Hou Y, Qin Z Y, Nguyen H T, Wen J, Wei M Y, Yeddu V, Saidaminov M I, Gao Y, Luo X, Wang Y R, Gao H, Zhang C F, Xu J, Zhu J, Sargent E H, Tan H R 2020 Nat. Energy 5 870 Google Scholar
[5]	Ogomi Y, Morita A, Tsukamoto S, Saitho T, Fujikawa N, Shen Q, Toyoda T, Yoshino K, Pandey S S, Ma T L, Hayase S 2014 J. Phys. Chem. Lett. 5 1004 Google Scholar
[6]	Im J, Stoumpos C C, Jin H, Freeman A J, Kanatzidis M G 2015 J. Phys. Chem. Lett. 6 3503 Google Scholar
[7]	Eperon G E, Leijtens T, Bush K A, et al. 2016 Science 354 86 Google Scholar
[8]	Hao F, Stoumpos C C, Chang R P H, Kanatzidis M G 2014 J. Am. Chem. Soc. 136 8094 Google Scholar
[9]	Klug M T, Milot R L, Patel J B, Green T, Sansom H C, Farrar M D, Ramadan A J, Martani S, Wang Z P, Wenger B, Ball J M, Langshaw L, Petrozza A, Johnston M B, Herz L M, Snaith H J 2020 Energy Environ. Sci. 14 112
[10]	Gu S, Lin R X, Han Q L, Gao Y, Tan H R, Zhu J 2020 Adv. Mater. 32 1907392
[11]	Yao H H, Zhou F G, Li Z Z, Ci Z P, Ding L M, Jin Z W 2020 Adv. Sci. 7 1903540 Google Scholar
[12]	Zhu Z L, Chueh C C, Li N, Mao C Y, Jen A K Y 2018 Adv. Mater. 30 1703800 Google Scholar
[13]	Li J M, Cao H L, Jiao W B, Wang Q, Wei M D, Cantone I, Lü J, Abate A 2020 Nat. Commun. 11 310 Google Scholar
[14]	Tchounwou P B, Yedjou C G, Patlolla A K, Sutton D J 2012 Molecular, Clinical and Environmental Toxicology (Vol. 101) (Jackson: Springer, Basel.) p133
[15]	Nishimura K, Kamarudin M A, Hirotani D, Hamada K, Shen Q, Iikubo S, Minemoto T, Yoshino K, Hayase S 2020 Nano Energy 74 104858 Google Scholar
[16]	Leijtens T, Prasanna R, Parker A G, Toney M F, McGehee M D 2017 ACS Energy Lett. 2 2159 Google Scholar
[17]	Yan Y J, Pullerits T, Zheng K B, Liang Z Q 2020 ACS Energy Lett. 5 2052 Google Scholar
[18]	Lin R X, Xiao K, Qin Z Y, Han Q L, Zhang C F, Wei M Y, Saidaminov M I, Gao Y, Xu J, Xiao M, Li A D, Zhu J, Sargent E H, Tan H R 2019 Nat. Energy 4 864 Google Scholar
[19]	Ricciarelli D, Meggiolaro D, Ambrosio F, Angelis F D 2020 ACS Energy Lett. 5 2787 Google Scholar
[20]	Chung I, Song J H, Im J, Androulakis J, Malliakas C D, Li H, Freeman A J, Kenney J T, Kanatzidis M G 2012 J. Am. Chem. Soc. 134 8579 Google Scholar
[21]	Ma L, Hao F, Stoumpos C C, Phelan B T, Wasielewski M R, Kanatzidis M G 2016 J. Am. Chem. Soc 138 14750 Google Scholar
[22]	Yang Z B, Rajagopal A, Jen A K Y 2017 Adv. Mater. 29 1704418 Google Scholar
[23]	Noel N K, Stranks S D, Abate A, Wehrenfennig C, Guarnera S, Haghighirad A A, Sadhanala A, Eperon G E, Pathak S K, Johnston M B, Petrozza A, Herza L M, Snaith H J 2014 Energy Environ. Sci. 7 3061 Google Scholar
[24]	Wang J K, Datta K, Li J Y, Verheijen M A, Zhang D, Wienk M M, Janssen R A J 2020 Adv. Energy Mater. 10 2000566 Google Scholar
[25]	Hao F, Stoumpos C C, Guo P J, Zhou N J, Marks T J, Chang R P H, Kanatzidis M G 2015 J. Am. Chem. Soc. 137 11445 Google Scholar
[26]	Liao W Q, Zhao D W, Yu Y, Shrestha N, Ghimire K, Grice C R, Wang C L, Xiao Y Q, Cimaroli A J, Ellingson R J, Podraza N J, Zhu K, Xiong R G, Yan Y F 2016 J. Am. Chem. Soc. 138 12360 Google Scholar
[27]	Chi D, Huang S H, Zhang M Y, Mu S Q, Zhao Y, Chen Y, You J B 2018 Adv. Funct. Mater. 28 1804603 Google Scholar
[28]	Wang C L, Song Z N, Li C W, Zhao D W, Yan Y F 2019 Adv. Funct. Mater. 29 1808801 Google Scholar
[29]	Tavakoli M M, Zakeeruddin S M, Grätzel M, Fan Z Y 2018 Adv. Mater. 30 1705998 Google Scholar
[30]	Zhao D W, Chen C, Wang C L, Junda M M, Song Z N, Grice C R, Yu Y, Li C W, Subedi B, Podraza N J, Zhao X Z, Fang G J, Xiong R G, Zhu K, Yan Y F 2018 Nat. Energy 3 1093 Google Scholar
[31]	Kumar M H, Dharani S, Leong W L, Boix P P, Prabhakar R R, Baikie T, Shi C, Ding H, Ramesh R, Asta M, Graetzel M, Mhaisalkar S G, Mathews N 2014 Adv. Mater. 26 7122 Google Scholar
[32]	Xiao M, Gu S, Zhu P C, Tang M Y, Zhu W D, Lin R X, Chen C L, Xu W C, Yu T, Zhu J 2018 Adv. Opt. Mater. 6 1700615 Google Scholar
[33]	Gupta S, Cahen D, Hodes G 2018 J. Phys. Chem. C 122 13926 Google Scholar
[34]	Liao W Q, Zhao D W, Yu Y, Grice C R, Wang C L, Cimaroli A J, Schulz P, Meng W W, Zhu K, Xiong R G, Yan Y F 2016 Adv. Mater. 28 9333 Google Scholar
[35]	Lee S J, Shin S S, Kim Y C, Kim D, Ahn T K, Noh J H, Seo J, and Seok S I 2016 J. Am. Chem. Soc. 138 3974 Google Scholar
[36]	Zong Y X, Zhou Z M, Chen M, Padture N P. Zhou Y Y 2018 Adv. Energy Mater. 8 1800997 Google Scholar
[37]	Chung I, Lee B, He J Q, Chang R P H, Kanatzidis M G 2012 Nature 485 486 Google Scholar
[38]	Xu X B, Chueh C C, Yang Z B, Rajagopal A, Xu J Q, Jo S B, Jen A K Y 2017 Nano Energy 34 392 Google Scholar
[39]	Zhu Z L, Li N, Zhao D B, Wang L D, Jen A K Y 2019 Adv. Energy Mater. 9 1802774 Google Scholar
[40]	Saidaminov M I, Spanopoulos I, Abed J, Ke W J, Wicks J, Kanatzidis M G, and Sargent E H 2020 ACS Energy Lett. 5 1153 Google Scholar
[41]	Cao D H, Stoumpos C C, Farha O K, Hupp J T, Kanatzidis M G 2015 J. Am. Chem. Soc. 137 7843 Google Scholar
[42]	Wei M Y, Xiao K, Walters G, Lin R X, Zhao Y B, Saidaminov M I, Todorović P, Johnston A, Huang Z R, Chen H J, Li A D, Zhu J, Yang Z Y, Wang Y K, Proppe A H, Kelley S O, Hou Y, Voznyy O, Tan H R, Sargent E H 2020 Adv. Mater. 32 1907058 Google Scholar
[43]	Ramirez D, Schutt K, Wang Z P, Pearson A J, Ruggeri E, Snaith H J, Stranks S D, Jaramillo F 2018 ACS Energy Lett. 3 2246 Google Scholar
[44]	Li C H, Pan Y M, Hu J L, Qiu S D, Zhang C L, Yang Y Z, Chen S, Liu X H, Brabec C J, Nazeeruddin M K, Mai Y H, Guo F 2020 ACS Energy Lett. 5 1386 Google Scholar
[45]	Yang D W, Lv J, Zhao X G, Xu Q L, Fu Y H, Zhan Y Q, Zunger A, Zhang L J 2017 Chem. Mater. 29 524 Google Scholar
[46]	Green M A, Baillie A H, Snaith H J 2014 Nat. Photon. 8 506 Google Scholar
[47]	Bartel C J, Sutton C, Goldsmith B R, Ouyang R H, Musgrave C B, Ghiringhelli L M, Scheffler M 2019 Sci. Adv. 5 eaav0693 Google Scholar
[48]	Shi T T, Zhang H S, Meng W W, Teng Q, Liu M Y, Yang X B, Yan Y F, Yip H L, Zhao Y J 2017 J. Mater. Chem. A 5 15124 Google Scholar
[49]	Yang Z B, Rajagopal A, Chueh C C, Jo S B, Liu B, Zhao T, Jen A K Y 2016 Adv. Mater. 28 8990 Google Scholar
[50]	Lee J W, Kim D H, Kim H S, Seo S W, Cho S M, Park N G 2015 Adv. Energy Mater. 5 1501310 Google Scholar
[51]	Prasanna R, Leijtens T, Dunfield S P, Raiford J A, Wolf E J, Swifter S A, Werner J, Eperon G E, Paula C d, Palmstrom A F, Boyd C C, Hest M F A M, Bent S F, Teeter G, Berry J J, McGehee M D 2019 Nat. Energy 4 939 Google Scholar
[52]	Han Q L, Wei Y, Lin R X, Fang Z M, Xiao K, Luo X, Gu S, Zhu J, Ding L M, Tan H R 2019 Sci. Bull. 64 1399 Google Scholar
[53]	Li C W, Song Z N, Zhao D W, Xiao C X, Subedi B, Shrestha N, Junda M M, Wang C L, Jiang C S, Jassim M A, Ellingson R J, Podraza N J, Zhu K, Yan Y F 2018 Adv. Energy Mater. 9 1803135
[54]	Lian X M, Chen J H, Zhang Y Z, Qin M C, Li J, Tian S X, Yang W T, Lu X H, Wu G, Chen H Z 2019 Adv. Funct. Mater. 29 1807024 Google Scholar
[55]	Tong J H, Song Z N, Kim D H, Chen X H, Chen C, Palmstrom A F, Ndione P F, Reese M O, Dunfield S P, Reid O G, Liu J, Zhang F, Harvey S P, Li Z, Christensen S T, Teeter G, Zhao D W, Jassim M M A, Hest M F A M, Beard M C, Shaheen S E, Berry J J, Yan Y F, Zhu K 2019 Science 364 475 Google Scholar
[56]	Zhu H L, Xiao J Y, Mao J, Zhang H, Zhao Y, Choy W C H 2017 Adv. Funct. Mater. 27 1605469 Google Scholar
[57]	Konstantakou M, Stergiopoulos T 2017 J. Mater. Chem. A 5 11518 Google Scholar
[58]	Ke W J, Stoumpos C C, Kanatzidis M G 2018 Adv. Mater. 31 1803230 Google Scholar
[59]	Zhu L Z, Yuh B, Schoen S, Li X P, Aldighaithir M, Richardson B J, Alamera A, Yu Q M 2016 Nanoscale 8 7621 Google Scholar
[60]	Liu M Y, Chen Z M, Xue Q F, Cheung S H, So S K, Yip H L, Cao Y 2018 J. Mater. Chem. A 6 16347 Google Scholar
[61]	Nejand B A, Hossain I M, Jakoby M, Moghadamzadeh S, Abzieher T, Gharibzadeh S, Schwenzer J A, Nazari P, Schackmar F, Hauschild D, Weinhardt L, Lemmer U, Richards B S, Howard I A, Paetzold U W 2019 Adv. Energy Mater. 10 1902580 Google Scholar
[62]	Ball J M, Buizza L, Sansom H C, Farrar M D, Klug M T, Borchert J, Patel J, Herz L M, Johnston M B, Snaith H J 2019 ACS Energy Lett. 4 2748 Google Scholar
[63]	Wu Y Z, Islam A, Yang X D, Qin C J, Liu J, Zhang K, Peng W Q, Han L Y 2014 Energy Environ. Sci. 7 2934 Google Scholar
[64]	Liu C, Fan J D, Li H L, Zhang C L, Mai Y H 2016 Sci. Rep. 6 35705 Google Scholar
[65]	Liu C, Li W Z, Li H L, Zhang C L, Fan J D, Mai Y H 2017 Nanoscale 9 13967 Google Scholar
[66]	Zhou X Y, Zhang L Z, Wang X Z, Liu C, Chen S, Zhang M Q, Li X N, Yi W D, Xu B M 2020 Adv. Mater. 32 1908107 Google Scholar
[67]	Hu M Y, Chen M, Guo P J, Zhou H, Deng J J, Yao Y D, Jiang Y, Gong J, Dai Z H, Zhou Y X, Qian F, Chong X Y, Feng J, Schaller R D, Zhu K, Padture N P, Zhou Y Y 2020 Nat. Commun. 11 151 Google Scholar
[68]	Yang Z B, Yu Z H, Wei H T, Xiao X, Ni Z Y, Chen B, Deng Y H, Habisreutinger S N., Chen X H, Wang K, Zhao J J, Rudd P N, Berry J J, Beard M C, Huang J S 2019 Nat. Commun. 10 4498 Google Scholar
[69]	Kapil G, Ripolles T S., Hamada K, Ogomi Y, Bessho T, Kinoshita T, Chantana J, Yoshino K, Shen Q, Toyoda T, Minemoto T, Murakami T N, Segawa H, Hayase S 2018 Nano Lett. 18 3600 Google Scholar
[70]	Minemoto T, Matsui T, Takakura H, Hamakawa Y, Negami T, Hashimoto Y, Uenoyama T, Kitagawa M 2001 Sol. Energy Mater. Sol. Cells 67 83 Google Scholar
[71]	Zhou X Y, Hua M M, Liu C, Zhang L Z, Zhong X W, Li X N, Tian Y Q, Cheng C, Xu B M 2019 Nano Energy 63 103866 Google Scholar
[72]	Liu J W, Ozaki M, Yakumaru S, Handa T, Nishikubo R, Kanemitsu Y, Saeki A, Murata Y, Murdey R, Wakamiya A 2018 Angew. Chem 130 13405 Google Scholar
[73]	Li C W, Song Z N, Zhao D W, Xiao C X, Subedi B, Shrestha N, Junda M M, Wang C L, Jiang C S, Jassim M A, Ellingson R J, Podraza N J, Zhu K, Yan Y F 2019 Adv. Energy Mater. 9 1803135 Google Scholar
[74]	Jiang T M, Chen Z, Chen X, Liu T Y, Chen X Y, Sha W E I, Zhu H M, Yang Y 2020 Sol. RRL 4 1900467 Google Scholar
[75]	Yang Z B, Zhang X H, Yang W Y, Eperon G E, Ginger D S 2020 Chem. Mater. 32 2782 Google Scholar
[76]	Zhu Z L, Bai Y, Zhang T, Liu Z K, Long X, Wei Z H, Wang Z L, Zhang L X, Wang J N, Yan F, Yang S H 2014 Angew. Chem 53 12571
[77]	Jeng J Y, Chen K C, Chiang T Y, Lin P Y, Tsai T D, Chang Y C, Guo T F, Chen P, Wen T C, Hsu Y J 2014 Adv. Mater. 26 4107 Google Scholar
[78]	Garcia A, Welch G C, Ratcliff E L, Ginley D S, Bazan G C, Olson D C 2012 Adv. Mater. 24 5368 Google Scholar
[79]	Manders J R, Tsang S W, Hartel M J, Lai T H, Chen S, Amb C M, Reynolds J R, So F 2013 Adv. Funct. Mater. 23 2993 Google Scholar
[80]	Yu Z H, Yang Z B, Ni Z Y, Shao Y C, Chen B, Lin Y Z, Wei H T, Yu Z S J, Holman Z, Huang J S 2020 Nat. Energy 5 657 Google Scholar
[81]	Tang H Y, Shang Y Q, Zhou W J, Peng Z J, Ning Z J 2019 Sol. RRL 3 1800256 Google Scholar
[82]	Xu G Y, Bi P Q, Wang S H, Xue R M, Zhang J W, Chen H Y, Chen W J, Hao X T, Li Y W, Li Y F 2018 Adv. Funct. Mater. 28 1804427 Google Scholar
[83]	Ni Z Y, Bao C X, Liu Y, Jiang Q, Wu W Q, Chen S S, Dai X Z, Chen B, Hartweg B, Yu Z S, Holman Z, Huang J S 2020 Science 367 1352 Google Scholar
[84]	Chen Y H, Li N X, Wang L G, Li L, Xu Z Q, Jiao H Y, Liu P F, Zhu C, Zai H C, Sun M Z, Zou W, Zhang S, Xing G C, Liu X F, Wang J P, Li D D, Huang B L, Chen Q, Zhou H P 2019 Nat. Commun. 10 1112 Google Scholar

[1]	王桂强, 王东升, 毕佳宇, 常嘉润, 孟凡宁. 苯基硫脲调控CsPbIBr₂钙钛矿结晶及其光电性能. , 2023, 72(15): 158801. doi: 10.7498/aps.72.20230593
[2]	韩晓静, 杨静, 张佳莉, 刘冬雪, 石标, 王鹏阳, 赵颖, 张晓丹. 反应等离子体沉积二氧化锡电子传输层及其在钙钛矿太阳电池中的应用. , 2023, 72(17): 178401. doi: 10.7498/aps.72.20230693
[3]	孙雪, 黄锋, 刘桂雄, 苏子生. 纳米成核点辅助结晶对钙钛矿光电探测器性能的影响. , 2022, 71(17): 178102. doi: 10.7498/aps.71.20220189
[4]	梁琦, 杨孟骐, 张京阳, 王如志. PECVD法制备高结晶GaN薄膜及其光电响应性能. , 2022, 71(9): 097302. doi: 10.7498/aps.71.20211922
[5]	王佩佩, 张晨曦, 胡李纳, 李仕奇, 任炜桦, 郝玉英. 氧化镍在倒置平面钙钛矿太阳能电池中的应用进展. , 2021, 70(11): 118801. doi: 10.7498/aps.70.20201896
[6]	许青林, 项婷, 徐伟, 李婷, 吴小龑, 李巍, 邱学军, 陈平. 金纳米粒子修饰氧化铟锡阳极的高效率红光钙钛矿发光二极管. , 2021, 70(20): 207803. doi: 10.7498/aps.70.20210500
[7]	陈隆, 陈成克, 李晓, 胡晓君. 氧化对单颗粒层纳米金刚石薄膜硅空位发光和微结构的影响. , 2019, 68(16): 168101. doi: 10.7498/aps.68.20190422
[8]	李明阳, 张雷敏, 吕沙沙, 李正操. 离子辐照和氧化对IG-110核级石墨中的点缺陷的影响. , 2019, 68(12): 128102. doi: 10.7498/aps.68.20190371
[9]	赵国栋, 杨亚利, 任伟. 钙钛矿型氧化物非常规铁电研究进展. , 2018, 67(15): 157504. doi: 10.7498/aps.67.20180936
[10]	杨蒙生, 易泰民, 郑凤成, 唐永建, 张林, 杜凯, 李宁, 赵利平, 柯博, 邢丕峰. 沉积态铀薄膜表面氧化的X射线光电子能谱. , 2018, 67(2): 027301. doi: 10.7498/aps.67.20172055
[11]	王栋, 朱慧敏, 周忠敏, 王在伟, 吕思刘, 逄淑平, 崔光磊. 溶剂对钙钛矿薄膜形貌和结晶性的影响研究. , 2015, 64(3): 038403. doi: 10.7498/aps.64.038403
[12]	李晓娜, 郑月红, 李震, 王苗, 张坤, 董闯. 基于团簇模型设计的Cu-Cu12-[Mx/(12+x)Ni12/(12+x)]5 (M=Si, Cr, Cr+Fe) 合金抗高温氧化研究. , 2014, 63(2): 028102. doi: 10.7498/aps.63.028102
[13]	伊丁, 秦伟, 解士杰. 钙钛矿锰氧化物中的极化子研究. , 2012, 61(20): 207101. doi: 10.7498/aps.61.207101
[14]	胡美娇, 李成, 徐剑芳, 赖虹凯, 陈松岩. 循环氧化/退火制备GeOI薄膜材料及其性质研究. , 2011, 60(7): 078102. doi: 10.7498/aps.60.078102
[15]	向军, 王晓晖. Sm0.9Sr0.1AlO3-δ钙钛矿氧化物的固相反应合成和电学性能. , 2008, 57(7): 4417-4423. doi: 10.7498/aps.57.4417
[16]	谢自力, 张荣, 修向前, 刘斌, 朱顺明, 赵红, 濮林, 韩平, 江若琏, 施毅, 郑有炓. InN薄膜的氧化特性研究. , 2007, 56(2): 1032-1035. doi: 10.7498/aps.56.1032
[17]	李雅, 陈玲燕, 张哲, 吴永刚, 乔轶, 徐炜新. XPS研究Nd表面氧化物的生长过程. , 2001, 50(1): 79-82. doi: 10.7498/aps.50.79
[18]	姜勇, 李广, 曾祥勇, 杨应平, 袁松柳, 金嗣昭. 钙钛矿Mn基氧化物的电子顺磁共振行为的实验研究. , 2000, 49(9): 1846-1851. doi: 10.7498/aps.49.1846
[19]	杨广亮, 鲜于文旭, 千正男, 金汉民. 纳米晶类钙钛矿型锰氧化物导电性的高压研究. , 2000, 49(3): 553-556. doi: 10.7498/aps.49.553
[20]	连贵君, 李美亚, 康晋峰, 郭建东, 孙云峰, 熊光成. 钙钛矿结构氧化物薄膜的外延生长. , 1999, 48(10): 1917-1922. doi: 10.7498/aps.48.1917

计量

文章访问数: 11528
PDF下载量: 289
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板