铝纳米晶的正电子湮没研究

李裕; 罗江山; 王柱; 杨蒙生; 邢丕峰; 易勇; 雷海乐

doi:10.7498/aps.63.247803

摘要

采用自悬浮定向流-真空热压法, 在不同压强下制得铝纳米晶材料, 并利用X射线衍射(XRD)和正电子湮没寿命谱(PALS)分析手段对铝纳米晶的结构和微观缺陷进行表征. XRD分析表明: 所制备的铝纳米晶的晶粒度为48 nm. PALS分析表明: 铝纳米晶的微观缺陷主要为类空位以及空位团, 而微孔洞很少; 短寿命τ1, 中间寿命τ2以及其对应的强度I1, I2随压强变化而呈现阶段性变化; 压制压强(P)低于0.39 GPa时制得的纳米晶空位团随压强的增加而逐渐转变为类空位; 0.39 GPa ≤ P≤ 0.72 GPa 时, 各类缺陷发生消除; P≥ 0.72 GPa时, 各类缺陷进一步发生消除. 随压强的提高, 铝纳米晶的密度增加, 其显微硬度也明显增高.

关键词:

Abstract

Aluminum nanoparticles with an average diameter of about 48 nm are compressed in a cemented-carbide mold under different pressures to produce nanocrystalline aluminum by the hot-pressing technology in a high vacuum condition. The X-ray diffraction and the positron annihilation lifetime spectroscopy (PALS) are used to characterize the microscopic structures of nanocrystalline aluminum. The PALS experimental results indicate that there are three types of defects in nanocrystalline aluminum, i.e., vacancy-like defects, vacancy clusters, and microvoids, which are corresponding to three lifetime components of positrons. The pressure for compaction has a great influence on the positron annihilating behavior. The vacancy clusters transform into the vacancy-like defects with increasing the pressure when it is below 0.39 GPa. The three types of defects tend to be rapidly eliminated in a pressure range from 0.39 GPa to 0.72 GPa. When pressure is above 0.72 GPa, the defects are further eliminated in nanocrystalline aluminum. The density and microhardness of nanocrystalline aluminum increase significantly with increasing the pressure for compaction.

Keywords:

作者及机构信息

1.
中国工程物理研究院激光聚变研究中心, 绵阳 621900;

2.
西南科技大学材料科学与工程学院, 绵阳 621010;

3.
武汉大学物理科学与技术学院, 武汉 430070

Authors and contacts

1.
Research Center of Laser Fusion, China Academy of Engineering Physics, Mianyang 621900, China;

2.
Institute of Science and Engineering, Southwest University of Science and Technology, Mianyang 621010, China;

3.
College of Physics Science and Technology, Wuhan University, Wuhan 430070, China

参考文献

[1]	Gleiter H 1989 Prog. Mater. Sci. 33 223
[2]	Schaefer H E, Wrschum R 1987 Phys. Lett. A 119 370
[3]	Qin X Y, Zhu J S, Zhou X Y, Wu X J 1994 Phys. Lett. A 193 335
[4]	Zeng X C 2012 M. S. Thesis ( Wuhan: Huazhong University of Science and Technology) (in Chinese) [曾小川 2012 硕士学位论文 (武汉: 华中科技大学)]
[5]	Schaefer H E, Wrschum R, Birringer R, Gleiter H 1988 Phys. Rev. B 38 9545
[6]	Qin X Y, Zhu J S, Zhang L D, Zhou X Y 1998 J. Phys. Cond. Matter 10 3075
[7]	Chu G, Luo J S, Liu W, Tang Y J, Lei H L, Yang S Y 2006 High Power Laser and Particle Beams 18 160 (in Chinese) [楚广, 罗江山, 刘伟, 唐永建, 雷海乐, 杨世源 2006 强激光与粒子束 18 160]
[8]	Zhang T, Qiu C, Zhang H J, Dai Y Q, Chen Z Q, Zhang H L, Lei H L 2010 J. Wuhan Univ. (Natural Science Edition) 6 3 (in Chinese) [章婷, 邱诚, 张宏俊, 戴益群, 陈志权, 张洪亮, 雷海乐 2010 武汉大学学报 (理学版) 6 3]
[9]	Zhou K, Li H, Pang J B, Wang Z 2012 Physica B 407 1219
[10]	Wrschum R, Scheytt M, Schaefer H E 1987 Phys. Stat. Solid. A 102 119
[11]	Qi N, Wang Y W, Wang D, Wang D D, Chen Z Q 2011 Acta Phys. Sin. 60 107805 (in Chinese) [祁宁, 王元为, 王栋, 王丹丹, 陈志权 2011 60 107805]
[12]	Zhou K, Li H, Wang Z 2013 Chin. Phys. Lett. 30 057804
[13]	Chen Z Y, Chen Z Q, Pan R K, Wang S J 2013 Chin. Phys. Lett. 30 027804
[14]	Fluss M J, Smedskjaer L C, Chason M K, Legnini D G, Siegel R W 1978 Phys. Rev. B 17 3444
[15]	Soininen E, Huomo H, Huttunen P A, Mäkinen J, Vehanen A, Hautojärvi P 1990 Phys. Rev. B 41 6227
[16]	Puska M J, Nieminen R M 1983 J. Phys. F 13 333
[17]	Li D X, Ping D H, Ye H Q, Qin X Y, Wu X J 1993 Mater. Lett. 18 29
[18]	Čížek J, Procházka I, Cieslar M, Kužel R, Kuriplach J, Chmelík F, Islamgaliev R K 2002 Phys. Rev. B 65 094106
[19]	Mascher P, Dannefaer S, Kerr D 1989 Phys. Rev. B 40 11764
[20]	Dupasquier A, Mills Jr A P 1995 Positron Spectroscopy of Solids (Amsterdam: IOS Press) pp505-522
[21]	Niemine R M, Laakkonen J 1979 Appl. Phys. 20 181

施引文献

[1]	Gleiter H 1989 Prog. Mater. Sci. 33 223
[2]	Schaefer H E, Wrschum R 1987 Phys. Lett. A 119 370
[3]	Qin X Y, Zhu J S, Zhou X Y, Wu X J 1994 Phys. Lett. A 193 335
[4]	Zeng X C 2012 M. S. Thesis ( Wuhan: Huazhong University of Science and Technology) (in Chinese) [曾小川 2012 硕士学位论文 (武汉: 华中科技大学)]
[5]	Schaefer H E, Wrschum R, Birringer R, Gleiter H 1988 Phys. Rev. B 38 9545
[6]	Qin X Y, Zhu J S, Zhang L D, Zhou X Y 1998 J. Phys. Cond. Matter 10 3075
[7]	Chu G, Luo J S, Liu W, Tang Y J, Lei H L, Yang S Y 2006 High Power Laser and Particle Beams 18 160 (in Chinese) [楚广, 罗江山, 刘伟, 唐永建, 雷海乐, 杨世源 2006 强激光与粒子束 18 160]
[8]	Zhang T, Qiu C, Zhang H J, Dai Y Q, Chen Z Q, Zhang H L, Lei H L 2010 J. Wuhan Univ. (Natural Science Edition) 6 3 (in Chinese) [章婷, 邱诚, 张宏俊, 戴益群, 陈志权, 张洪亮, 雷海乐 2010 武汉大学学报 (理学版) 6 3]
[9]	Zhou K, Li H, Pang J B, Wang Z 2012 Physica B 407 1219
[10]	Wrschum R, Scheytt M, Schaefer H E 1987 Phys. Stat. Solid. A 102 119
[11]	Qi N, Wang Y W, Wang D, Wang D D, Chen Z Q 2011 Acta Phys. Sin. 60 107805 (in Chinese) [祁宁, 王元为, 王栋, 王丹丹, 陈志权 2011 60 107805]
[12]	Zhou K, Li H, Wang Z 2013 Chin. Phys. Lett. 30 057804
[13]	Chen Z Y, Chen Z Q, Pan R K, Wang S J 2013 Chin. Phys. Lett. 30 027804
[14]	Fluss M J, Smedskjaer L C, Chason M K, Legnini D G, Siegel R W 1978 Phys. Rev. B 17 3444
[15]	Soininen E, Huomo H, Huttunen P A, Mäkinen J, Vehanen A, Hautojärvi P 1990 Phys. Rev. B 41 6227
[16]	Puska M J, Nieminen R M 1983 J. Phys. F 13 333
[17]	Li D X, Ping D H, Ye H Q, Qin X Y, Wu X J 1993 Mater. Lett. 18 29
[18]	Čížek J, Procházka I, Cieslar M, Kužel R, Kuriplach J, Chmelík F, Islamgaliev R K 2002 Phys. Rev. B 65 094106
[19]	Mascher P, Dannefaer S, Kerr D 1989 Phys. Rev. B 40 11764
[20]	Dupasquier A, Mills Jr A P 1995 Positron Spectroscopy of Solids (Amsterdam: IOS Press) pp505-522
[21]	Niemine R M, Laakkonen J 1979 Appl. Phys. 20 181

[1]	王荣, 杨静, 张涛, 于润升, 董俊才, 张鹏, 曹兴忠, 王宝义, 尹昊. 聚乙烯亚胺改性介孔氧化硅载体孔结构的调控机理. , 2023, 72(16): 168104. doi: 10.7498/aps.72.20230675
[2]	尹昊, 宋通, 彭雄刚, 张鹏, 于润升, 陈喆, 曹兴忠, 王宝义. 聚乙烯亚胺改性介孔二氧化硅SBA-15微观结构的小角X射线散射及正电子湮没谱学研究. , 2023, 72(11): 114101. doi: 10.7498/aps.72.20230265
[3]	孙丽俊, 代飞, 罗江山, 易勇, 杨蒙生, 张继成, 黎军, 雷海乐. 铝纳米晶的低温导电特性研究. , 2016, 65(13): 137303. doi: 10.7498/aps.65.137303
[4]	贺慧芳, 陈志权. 用正电子湮没研究纳米碲化铋的缺陷及其对热导率的影响. , 2015, 64(20): 207804. doi: 10.7498/aps.64.207804
[5]	许红霞, 郝颖萍, 韩荣典, 翁惠民, 杜淮江, 叶邦角. 纳米Fe3 O4 颗粒的正电子湮没谱学研究. , 2011, 60(6): 067803. doi: 10.7498/aps.60.067803
[6]	祁宁, 王元为, 王栋, 王丹丹, 陈志权. Co掺杂纳米ZnO微结构的正电子湮没研究. , 2011, 60(10): 107805. doi: 10.7498/aps.60.107805
[7]	王君君, 龚静, 宫振丽, 闫晓丽, 高舒, 王波. 聚合物纳米复合电解质(PEO)8-ZnO-LiClO4微结构及电导率研究. , 2011, 60(12): 127803. doi: 10.7498/aps.60.127803
[8]	张洪亮, 雷海乐, 唐永建, 罗江山, 李恺, 邓晓臣. 纳米结构Cu固体材料的低温热容性能研究. , 2010, 59(1): 471-475. doi: 10.7498/aps.59.471
[9]	张宏俊, 王栋, 陈志权, 王少阶, 徐友明, 罗锡辉. MoO3/Al2O3催化剂中Mo分散的正电子研究. , 2008, 57(11): 7333-7337. doi: 10.7498/aps.57.7333
[10]	魏强, 刘海, 何世禹, 郝小鹏, 魏龙. 质子辐照铝膜反射镜的慢正电子湮没研究. , 2006, 55(10): 5525-5530. doi: 10.7498/aps.55.5525
[11]	叶崇志, 廖晶莹, 杨培志, 谢建军, 罗澜, 曹顿华. F, Y双掺钨酸铅晶体的发光性能和微观缺陷. , 2006, 55(4): 1947-1952. doi: 10.7498/aps.55.1947
[12]	梁　玲, 顾　牡, 段　勇, 马晓辉, 刘峰松, 吴湘惠, 邱隆清, 陈铭南, 廖晶莹, 沈定中, 张　昕, 宫　波, 薛炫萍, 徐炜新, 王景成. +3价离子掺杂钨酸铅晶体发光性能和微观缺陷的研究. , 2004, 53(2): 543-549. doi: 10.7498/aps.53.543
[13]	唐永建, 韦建军, 李朝阳, 吴卫东, 王朝阳. 自悬浮定向流纳米金属粉末制备的理论模拟. , 2003, 52(9): 2331-2336. doi: 10.7498/aps.52.2331
[14]	汤学峰, 顾牡, 童宏勇, 梁玲, 姚明珍, 陈玲燕, 廖晶莹, 沈炳浮, 曲向东, 殷之文, 徐炜新, 王景成. 掺镧PbWO4闪烁晶体的缺陷研究. , 2000, 49(10): 2007-2010. doi: 10.7498/aps.49.2007
[15]	王小刚, 张宏. 铝中氢-空位复合体的正电子湮没特性. , 1992, 41(4): 633-639. doi: 10.7498/aps.41.633
[16]	. 用正电子湮没寿命谱研究凝聚态甲烷的温度关系. , 1990, 39(7): 106-111. doi: 10.7498/aps.39.106
[17]	苏昉, 郁伟中, 戴道扬, 赵宗源. 非晶离子导体B2O3-0.7Li2O-0.7LiCl-xAl2O3晶化过程的正电子湮没寿命谱和扫描电子显微镜研究. , 1985, 34(5): 622-627. doi: 10.7498/aps.34.622
[18]	何元金, 曹必松. 正电子湮没寿命谱的傅里叶变换分析法. , 1984, 33(12): 1745-1752. doi: 10.7498/aps.33.1745
[19]	曹玔, 王蕴玉, 熊兴民, 熊良钺, 姜健. 用正电子湮没技术研究形变铁的恢复. , 1982, 31(1): 126-131. doi: 10.7498/aps.31.126
[20]	王蕴玉, 张天保, 唐孝威. 正电子在铝中湮没γ射线能量的精密测量. , 1982, 31(7): 945-947. doi: 10.7498/aps.31.945

计量

文章访问数: 5785
PDF下载量: 357
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板