Research progress of photonics devices on lithium-niobate-on-insulator thin films

Li Geng-Lin; Jia Yue-Chen; Chen Feng

doi:10.7498/aps.69.20200302

Abstract

Lithium niobate (LiNbO₃, LN) crystals have excellent electro-optical and nonlinear optical properties, and they have been regarded as one of the most promising materials for constructing the multifunctional photonic integrated systems. Due to the excellent optical properties of LN crystal, the emerging LN thin film technology has received great attention in the research of integrated photonics in recent years. With the help of advanced micro-nano fabrication technologies, many high-performance lithium niobate integrated photonic devices have been realized. Integrated photonic platform can incorporate high-density, multi-functional optical components, micro-nano photonics structures, and optical materials on a monolithic substrate, which can flexibly implement a variety of photonic functions. At the same time, it also provides a low-cost, small-size, and scalable solution for miniaturizing and integrating the free-space optical systems. Photonic chips based on LN have been widely used in fast electro-optic modulation, nonlinear optical frequency conversion and frequency comb generation. In particular, periodically poled lithium niobate (PPLN) based on quasi-phase matching has gradually become a mature integrated photonic platform and has been widely used in the field of nonlinear optics. As wafer bonding technology is matured, the lithium-niobate-on-insulator (LNOI) thin films made by the “smart-cut” process have been commercialized. The thickness of the LN film on a Si or SiO₂ substrate can reach several hundred nanometers, and good uniformity in film thickness at a larger size (3 inches) can be ensured. With the development of micro-nano fabrication technologies, the quality and functions of photonic devices on LNOI chips have been significantly improved in recent years, and research on integrated photonic devices based on LNOI has also been developed rapidly in recent years. In this article we briefly review the development of LNOI technology, introducing the applications of several advanced micro-nano fabrication techniques and summarizing their applications in the micro-/nano-fabrication of on-chip photonic devices based on LNOI wafers. In addition, in this article we also summarize the latest advances in the functionality of LNOI on-chip photonic devices and give a short prospective on their future applications in integrated photonics.

Keywords:

Authors and contacts

State Key Laboratory of Crystal Materials, School of Physics, Shandong University, Jinan 250100, China

Corresponding author: Jia Yue-Chen, yuechen.jia@sdu.edu.cn ; Chen Feng, drfchen@sdu.edu.cn

FullText HTML : translate this paragraph

References

[1]	Desiatov B, Shams A A, Zhang M, Wang C, Lončar M 2019 Optica 6 380 Google Scholar
[2]	He L Y, Zhang M, Shams A A, Zhu R R, Wang C, Lončar M 2019 Opt. Lett. 44 2314 Google Scholar
[3]	Nikogosyan D N 2005 Nonlinear Optical Crystals: A Complete Survey (New York: Springer Science + Business Media) pp35–53
[4]	Poberaj G, Hu H, Sohler W, Günter P 2012 Laser Photonics Rev. 6 488 Google Scholar
[5]	Boes A, Corcoran B, Chang L, Bowers J, Mitchell A 2018 Laser Photonics Rev. 12 1700256 Google Scholar
[6]	Stepanenko O, Quillier E, Tronche H, Baldi P, Micheli M D 2014 IEEE Photonics Technol. Lett. 26 1557 Google Scholar
[7]	Bruel M 1995 Electron. Lett. 31 1201 Google Scholar
[8]	Ramadan A T, Levy M, Osgood J R M 2000 Appl. Phys. Lett. 76 1407 Google Scholar
[9]	Roth R M, Djukic D, Lee Y S, Jr R M O, Bakhru S, Laulicht B, Dunn K, Bakhru H, Wu L Q, Huang M B 2006 Appl. Phys. Lett. 89 112906 Google Scholar
[10]	Rabiei P, Gunter P 2004 Appl. Phys. Lett. 85 4603 Google Scholar
[11]	Djukic D, Cerda P G, Roth R M, Jr R M O, Bakhru S, Bakhru H 2007 Appl. Phys. Lett. 90 171116 Google Scholar
[12]	Wang J, Zhu B W, Hao Z Z, Bo F, Wang X L, Gao F, Li Y G, Zhang G Q, Xu J J 2016 Opt. Express 24 21869 Google Scholar
[13]	Wang L, Wang C, Wang J, Bo F, Zhang M, Gong Q H, Lončar M, Xiao Y F 2018 Opt. Lett. 43 2917 Google Scholar
[14]	Liang H X, Luo R, He Y, Jiang H W, Lin Q 2017 Optica 4 1251 Google Scholar
[15]	Wang M, Xu Y X, Fang Z W, Liao Y, Wang P, Chu W, Qiao L L, Lin J T, Fang W, Cheng Y 2017 Opt. Express 25 124 Google Scholar
[16]	Fang Z W, Lin J T, Wang M, Liu Z M, Yao J P, Qiao L L, Cheng Y 2015 Opt. Express 23 27941 Google Scholar
[17]	Song J X, Lin J T, Tang J L, Liao Y, He F, Wang Z H, Qiao L L, Sugioka K, Cheng Y 2014 Opt. Express 22 14792 Google Scholar
[18]	Jia Y C, Chen F 2019 Chin. Opt. Lett. 17 012302 Google Scholar
[19]	Chen F, Vázquez de Aldana J R 2014 Laser Photonics Rev. 8 251 Google Scholar
[20]	Wu R B, Zhang J H, Yao N, Fang W, Qiao L L, Fang C, Lin J T, Cheng Y 2018 Opt. Lett. 43 4116 Google Scholar
[21]	Zheng Y L, Fang Z W, Liu S J, Cheng Y, Chen X F 2019 Phys. Rev. Lett. 122 253902 Google Scholar
[22]	Fang Z W, Xu Y X, Wang M, Qiao L L, Lin J T, Fang W, Cheng Y 2017 Sci. Rep. 7 45610 Google Scholar
[23]	Rao A, Fathpour S 2018 IEEE J. Sel. Top. Quantum Electron. 24 8200912 Google Scholar
[24]	Rao A, Fathpour S 2018 IEEE J. Sel. Top. Quantum Electron. 24 3400114 Google Scholar
[25]	Honardoost A, Gonzalez G F C, Khan S, Malinowski M, Rao A, Tremblay J E, Yadav A, Richardson K, Wu M C, Fathpour S 2018 IEEE Photonics J. 10 4500909 Google Scholar
[26]	Gonzalez G F C, Malinowski M, Honardoost A, Fathpour S 2019 Appl. Opt. 58 D1 Google Scholar
[27]	Rao A, Abdelsalam K, Sjaardema T, Honardoost A, Camacho G G F, Fathpour S 2019 Opt. Express 27 25920 Google Scholar
[28]	Wang T, Ng D K T, Ng S K, Toh Y T, Chee A K L, Chen G F R, Wang Q, Tan D T H 2015 Laser Photonics Rev. 9 498 Google Scholar
[29]	Honardoost A, Juneghani F A, Safian R, Fathpour S 2019 Opt. Express 27 6495 Google Scholar
[30]	Rao A, Chiles J, Khan S, Toroghi S, Malinowski M, Camacho G G F, Fathpour S 2017 Appl. Phys. Lett. 110 111109 Google Scholar
[31]	Rao A, Patil A, Chiles J, Malinowski M, Novak S, Richardson K, Rabiei P, Fathpour S 2015 Opt. Express 23 22746 Google Scholar
[32]	Luo R, He Y, Liang H X, Li M X, Lin Q 2018 Optica 5 1006 Google Scholar
[33]	He Y, Liang H X, Luo R, Li M X, Lin Q 2018 Opt. Express 26 16315 Google Scholar
[34]	Chen J Y, Sua Y M, Fan H, Huang Y P 2018 OSA Continuum 1 229 Google Scholar
[35]	Chen J Y, Sua Y M, Ma Z H, Tang C, Li Z, Huang Y P 2019 OSA Continuum 2 2914 Google Scholar
[36]	Reich M, Korte F, Fallnich C, Welling H, Tünnermann A 1998 Opt. Lett. 23 1817 Google Scholar
[37]	Wolf R, Breunig I, Zappe H, Buse K 2018 Opt. Express 26 19815 Google Scholar
[38]	Wang M, Wu R B, Lin J T, Zhang J H, Fang Z W, Chai Z F, Cheng Y 2019 Quantum Eng. 1 1 Google Scholar
[39]	Fang Z W, Haque S, Lin J T, Wu R B, Zhang J H, Wang M, Zhou J X, Rafa M, Tao L, Cheng Y 2019 Opt. Lett. 44 1214 Google Scholar
[40]	Luo R, Jiang H W, Liang H X, Chen Y P, Lin Q 2017 Opt. Lett. 42 1281 Google Scholar
[41]	Jiang H W, Luo R, Liang H X, Chen X F, Chen Y P, Lin Q 2017 Opt. Lett. 42 3267 Google Scholar
[42]	Zhang M, Wang C, Cheng R, Shams A A, Lončar M 2017 Optica 4 1536 Google Scholar
[43]	Fang Z W, Yao N, Wang M, Lin J T, Zhang J H, Wu R B, Qiao L L, Fang W, Lu T, Cheng Y 2017 Int. J. Optomechatronics 11 47 Google Scholar
[44]	Guarino A, Poberaj G, Rezzonico D, Riccardo D, Günter P 2007 Nat. Photonics 1 407 Google Scholar
[45]	Ren T, Zhang M, Wang C, Shao L B, Reimer C, Zhang Y, King O, Esman R, Cullen T, Lončar M 2019 IEEE Photonics Technol. Lett. 31 889 Google Scholar
[46]	Jin M W, Chen J Y, Sua Y M, Huang Y P 2019 Opt. Lett. 44 1265 Google Scholar
[47]	Wang C, Zhang M, Stern B, Lipson M, Lončar M 2018 Opt. Express 26 1547 Google Scholar
[48]	Wang C, Zhang M, Chen X, Bertrand M, Shams A A, Chandrasekhar S, Winzer P, Lončar M 2018 Nature 562 101 Google Scholar
[49]	He M B, Xu M Y, Ren Y X, Jian J, Ruan Z L, Xu Y S, Gao S Q, Sun S H, Wen X Q, Zhou L D, Liu L, Guo C J, Chen H, Yu S Y, Liu L, Cai X L 2019 Nat. Photonics 13 359 Google Scholar
[50]	Ahmed A N R, Nelan S, Shi S Y, Yao P, Mercante A, Prather D W 2020 Opt. Lett. 45 1112 Google Scholar
[51]	Thomaschewski M, Zenin V A, Wolff C, Bozhevolnyi S I 2020 Nat. Commun. 11 748 Google Scholar
[52]	Luo R, He Y, Liang H X, Li M X, Ling J W, Lin Q 2019 Phys. Rev. Appl. 11 034026 Google Scholar
[53]	Luo R, Jiang H W, Rogers S, Liang H X, He Y, Lin Q 2017 Opt. Express 25 24531 Google Scholar
[54]	Lin J T, Yao N, Hao Z Z, Zhang J h, Mao W B, Wang M, Chu W, Wu R B, Fang Z W, Qiao L L, Fang W, Bo F, Cheng Y 2019 Phys. Rev. Lett. 122 173903 Google Scholar
[55]	Liu S J, Zheng Y L, Fang Z W, Ye X N, Cheng Y, Chen X F 2019 Opt. Lett. 44 1456 Google Scholar
[56]	Ye X N, Liu S J, Chen Y P, Zheng Y L, Chen X F 2020 Opt. Lett. 45 523 Google Scholar
[57]	Wolf R, Jia Y C, Bonaus S, Werner C S, Herr S J, Breunig I, Buse K, Zappe H 2018 Optica 5 872 Google Scholar
[58]	Chen J Y, Ma Z H, Sua Y M, Li Z, Tang C, Huang Y P 2019 Optica 6 1244 Google Scholar
[59]	Lu J J, Surya J B, Liu X W, Bruch A W, Gong Z, Xu Y T, Tang H X 2019 Optica 6 1455 Google Scholar
[60]	Hao Z Z, Zhang L, Gao A, Mao W B, Lyu X D, Gao X M, Bo F, Gao F, Zhang G Q, Xu J J 2018 Sci. China, Ser. G 61 114211 Google Scholar
[61]	Hao Z Z, Zhang L, Mao W B, Gao A, Gao X M, Gao F, Bo F, Zhang G Q, Xu J J 2020 Photonics Res. 8 311 Google Scholar
[62]	Sua Y M, Chen J Y, Huang Y P 2018 Opt. Lett. 43 2965 Google Scholar
[63]	Niu Y F, Lin C, Liu X Y, Chen Y, Hu X P, Zhang Y, Cai X L, Gong Y X, Xie Z D, Zhu S N 2020 Appl. Phys. Lett. 116 Google Scholar
[64]	Zhang M, Buscaino B, Wang C, Shams A A, Reimer C, Zhu R R, Kahn J M, Lončar M 2019 Nature 568 373 Google Scholar
[65]	Wang C, Zhang M, Yu M J, Zhu R R, Hu H, Lončar M 2019 Nat. Commun. 10 1 Google Scholar
[66]	Yu M J, Desiatov B, Okawachi Y, Gaeta A L, Lončar M 2019 Opt. Lett. 44 1222 Google Scholar
[67]	Jiang W C, Lin Q 2016 Sci. Rep. 6 36920 Google Scholar
[68]	Cai L T, Mahmoud A, Khan M, Mahmoud M, Mukherjee T, Bain J, Piazza G 2019 Photonics Res. 7 1003 Google Scholar
[69]	Yao N, Zhou J X, Gao R H, Lin J T, Wang M, Cheng Y, Fang W, Tong L M 2020 Opt. Express 28 12416 Google Scholar
[70]	Mahmoud M, Ghosh S, Piazza G 2015 CLEO: Science and Innovations San Jose, USA, May 10–15, 2015 pSW41.7
[71]	Chen Z H, Peng R H, Wang Y w, Zhu H B, Hu H 2017 Opt. Mater. Express 7 4010 Google Scholar
[72]	Krasnokutska I, Chapman R J, Tambasco J L J, Peruzzo A 2019 Opt. Express 27 17681 Google Scholar
[73]	Khan M, Bain J A, Piazza G 2019 Opt. Lett. 44 4558 Google Scholar

Cited By

图 1 晶片直接键合制备单晶LN薄膜流程图

Figure 1. Flow chart of preparation of single crystal lithium niobate films by direct bonding of wafers.

DownLoad: Full-Size Img PowerPoint

图 2 使用飞秒激光微加工制备LN片上微盘谐振腔的过程　(a) 在LN样品表面沉积Cr; (b) 飞秒激光加工将微盘图形转移到Cr膜上; (c) CMP过程将微盘图形转移到LN薄膜上; (d) 湿法刻蚀去除Cr膜和SiO₂^[20]

Figure 2. Flow chart of fabricating LN microdisk using femtosecond laser micromachining: (a) Depositing metallic chromium on LN sample surface; (b) transferring microdisk graphics onto chrome layer by femtosecond laser micromachining; (c) transferring microdisk pattern onto LN film by CMP; (d) wet etching removes chromium film and SiO₂^[20].

DownLoad: Full-Size Img PowerPoint

图 3 PPLN薄膜片上脊形波导的制备流程　(a) 待加工的x切LN薄膜样品; (b) 沉积梳状金属极化电极; (c) 对金属电极施加极化电压; (d) 制作完成的PPLN脊形波导; (e) PPLN脊形波导俯视图, 深色部分为铁电畴反转区域; (f) 经过CMP或FIB技术处理之后的PPLN片上脊形波导侧壁^[35]

Figure 3. Preparation process of PPLN ridge waveguide: (a) The x-cut LN thin film sample to be processed; (b) deposition of comb-shaped metal polarized electrode; (c) application of polarization voltage to metal electrode; (d) the fabricated PPLN ridge waveguide; (e) top view of the PPLN ridge waveguide, the dark area is the domain inversion area; (f) PPLN ridge waveguide sidewall after CMP or FIB fabricating^[35].

DownLoad: Full-Size Img PowerPoint

图 4 (a) 抛光后的微环谐振腔的扫描电子显微镜(scanning electron microscope, SEM)着色图像(LN标记为黄色, SiO₂为灰色); (b)−(d) 不同抛光参数对最终抛光效果的影响^[37]

Figure 4. (a) A SEM coloring image of polished micro-ring resonator (LN is yellow; SiO₂ is gray); (b)−(d) influences of different polishing parameters on the final sidewall roughness^[37].

DownLoad: Full-Size Img PowerPoint

图 5 CMP技术制备LNOI片上光子学器件流程图　(a) 磁控溅射沉积Cr薄膜; (b) 飞秒激光微加工制备待加工图案; (c) CMP过程去除多余的LN; (d) 使用Cr腐蚀剂去除刻蚀掩模以及二次CMP过程; (e) CMP仪器示意图^[38]

Figure 5. Schematic of using CMP technology to prepare LNOI on-chip optics: (a) Depositing Cr film on LNOI by magnetron sputtering; (b) femtosecond laser processing defines the pattern to be processed; (c) CMP process to remove excess LN; (d) use Cr etchant to remove the etching mask and secondary CMP process; (e) schematic diagram of CMP instrument^[38].

DownLoad: Full-Size Img PowerPoint

图 6 (a), (b) LNOI片上电光调制器的SEM图像; (c) 赛道型电光调制器耦合区域的放大图; (d) 电极与光波导的放大图; (e) M-Z型电光调制器的透射光谱; (f)赛道型电光调制器的电光调制带宽(9 V, 1480−1580 nm)^[47]

Figure 6. (a), (b) SEM images of the LNOI modulator; (c) enlarged view of the coupling area of the track modulator; (d) enlarged view of the electrode and optical waveguide; (e) transmission spectrum of MZI modulator; (f) electro-optical bandwidth of racetrack modulator (9 V, 1480−1580 nm)^[47].

DownLoad: Full-Size Img PowerPoint

图 7 LNOI片上等离子体电光定向耦合器的SEM图像^[51]

Figure 7. False-colored SEM image of LNOI plasma electro-optic directional coupler^[51].

DownLoad: Full-Size Img PowerPoint

图 8 (a) 级联过程光谱, 其中抽运波长固定在1534.9 nm, 信号光波长分别位于1541.8 和1548.9 nm; (b) LN微盘中有效的FWM过程, FW闲频光功率依赖性和理论拟合, 信号光功率保持在5 mW^[55]

Figure 8. (a) Spectrum of the cascade process: the pump wavelength is fixed at 1534.9 nm, and the signal wavelength is at 1541.8 and 1548.9 nm. (b) Effective FWM process in LN microdisk, FW idler power dependence and theoretical fitting, the signal power is maintained at 5 mW^[55].

DownLoad: Full-Size Img PowerPoint

图 9 (a) LN微环谐振腔的显微照片, 黑线是蚀刻的光波导, 黄色区域是金电极; (b) 从微环谐振腔产生的EO频率梳的输出频谱, 左插图显示了几条梳齿的放大图, 梳齿之间的功率变化约为0.1 dB, 右插图显示了几个不同调制指数(β)的透射光谱^[64]

Figure 9. (a) Photograph of the LN microring resonator, the black line is an etched optical waveguide, and the yellow area is a gold electrode. (b) The output spectrum of the EO frequency comb generated from the micro-ring resonator. The left illustration shows an enlarged view of several comb teeth. The power variation between the comb teeth is about 0.1 dB. The right inset shows the transmission spectra of several different modulation indices (β)^[64].

DownLoad: Full-Size Img PowerPoint

图 10 (a), (b)宽带频率梳的产生, 即当抽运功率为300 mW且输入信号与(a) TM模和(b) TE模共振时, 产生的频率梳频谱; (c) LN片上纳米光子学回路的SEM图像^[65]

Figure 10. (a), (b) Generation of a broadband frequency comb: The frequency comb spectrum is generated when the pump power is 300 mW and the input signal resonates with the (a) TM mode and the (b) TE mode; (c) SEM image of nanophotonic circuit on LN film^[65].

DownLoad: Full-Size Img PowerPoint

图 11 (a) M-Z干涉仪型和(b) 谐振腔型声光调制器的显微镜照片; (c) 光波导的SEM图像; (d) IDT区域的SEM图像^[68]

Figure 11. (a) Micrograph of M-Z interferometer type and (b) resonator type acousto-optic modulator; (c) SEM image of the optical waveguide; (d) SEM image of the IDT region^[68].

DownLoad: Full-Size Img PowerPoint

图 12 (a) 锥形单模光纤的SEM图像^[69]; (b) 双层锥形模式转换器的SEM图像^[2]

Figure 12. (a) SEM image of single mode tapered fiber^[69]; (b) SEM image of bilayer tapered mode converter^[2].

DownLoad: Full-Size Img PowerPoint

表 1 不同加工手段制备的LN片上光子学器件的主要性能参数

Table 1. Main performance parameters of LN on-chip photonic devices fabricated by different fabrication techniques.

加工图案	微纳加工技术	尺寸	损耗(测量波长)	品质因子(测量波长/nm)
微盘^[13]	紫外光刻技术	d = 50 μm	—	1.5 × 10⁶ (1551.4)
微盘^[12]	紫外光刻技术	r = 50 μm	—	3.1 × 10⁵ (1550)
微盘^[40]	电子束曝光技术	r = 25 μm	—	2.9 × 10⁵ (1502)
微盘^[41]		r = 25 μm	—	2.69 × 10⁵ (1548.78)
微环^[1]		r = 100 μm	—	1.1 × 10⁷ (637)
微环^[42]		r = 80 μm	—	～10⁷ (1590)
光子晶体微腔^[14]		w = 750 nm	—	1.09 × 10⁵ (1452)
		h = 250 nm
		a = 600 nm
微盘^[21]	飞秒激光微加工	d = 29.92 μm	—	9.61 × 10⁶ (1547.8)
微盘^[20]		d = 140 μm	—	1.46 × 10⁷ (773.49)
双微盘^[43]		d = 29.92 μm	—	1.35 × 10⁵ (1528.5)
双微盘^[43]		g = 138 nm	—	1.35 × 10⁵ (1528.5)
脊形波导^[1]	电子束曝光技术	W = 480 nm	6 dB/m (635 nm)	—
脊形波导^[1]		H = 120 nm	6 dB/m (635 nm)	—
脊形波导^[42]		W = 2.4 μm	(2.7 ± 0.3) dB/m (1590 nm)	—
脊形波导^[42]		H = 0.25 μm	(2.7 ± 0.3) dB/m (1590 nm)	—
脊形波导^[29]	异质集成	W = 1.3 μm	0.1 dB/m (1550 nm)	—
脊形波导^[29]	异质集成	H = 0.5 μm	0.1 dB/m (1550 nm)	—
脊形波导^[37]	化学机械抛光	W = 4 μm	4 dB/m (1550 nm)	—
脊形波导^[37]	化学机械抛光	H = 3 μm	4 dB/m (1550 nm)	—

DownLoad: CSV

map

[1]	Desiatov B, Shams A A, Zhang M, Wang C, Lončar M 2019 Optica 6 380 Google Scholar
[2]	He L Y, Zhang M, Shams A A, Zhu R R, Wang C, Lončar M 2019 Opt. Lett. 44 2314 Google Scholar
[3]	Nikogosyan D N 2005 Nonlinear Optical Crystals: A Complete Survey (New York: Springer Science + Business Media) pp35–53
[4]	Poberaj G, Hu H, Sohler W, Günter P 2012 Laser Photonics Rev. 6 488 Google Scholar
[5]	Boes A, Corcoran B, Chang L, Bowers J, Mitchell A 2018 Laser Photonics Rev. 12 1700256 Google Scholar
[6]	Stepanenko O, Quillier E, Tronche H, Baldi P, Micheli M D 2014 IEEE Photonics Technol. Lett. 26 1557 Google Scholar
[7]	Bruel M 1995 Electron. Lett. 31 1201 Google Scholar
[8]	Ramadan A T, Levy M, Osgood J R M 2000 Appl. Phys. Lett. 76 1407 Google Scholar
[9]	Roth R M, Djukic D, Lee Y S, Jr R M O, Bakhru S, Laulicht B, Dunn K, Bakhru H, Wu L Q, Huang M B 2006 Appl. Phys. Lett. 89 112906 Google Scholar
[10]	Rabiei P, Gunter P 2004 Appl. Phys. Lett. 85 4603 Google Scholar
[11]	Djukic D, Cerda P G, Roth R M, Jr R M O, Bakhru S, Bakhru H 2007 Appl. Phys. Lett. 90 171116 Google Scholar
[12]	Wang J, Zhu B W, Hao Z Z, Bo F, Wang X L, Gao F, Li Y G, Zhang G Q, Xu J J 2016 Opt. Express 24 21869 Google Scholar
[13]	Wang L, Wang C, Wang J, Bo F, Zhang M, Gong Q H, Lončar M, Xiao Y F 2018 Opt. Lett. 43 2917 Google Scholar
[14]	Liang H X, Luo R, He Y, Jiang H W, Lin Q 2017 Optica 4 1251 Google Scholar
[15]	Wang M, Xu Y X, Fang Z W, Liao Y, Wang P, Chu W, Qiao L L, Lin J T, Fang W, Cheng Y 2017 Opt. Express 25 124 Google Scholar
[16]	Fang Z W, Lin J T, Wang M, Liu Z M, Yao J P, Qiao L L, Cheng Y 2015 Opt. Express 23 27941 Google Scholar
[17]	Song J X, Lin J T, Tang J L, Liao Y, He F, Wang Z H, Qiao L L, Sugioka K, Cheng Y 2014 Opt. Express 22 14792 Google Scholar
[18]	Jia Y C, Chen F 2019 Chin. Opt. Lett. 17 012302 Google Scholar
[19]	Chen F, Vázquez de Aldana J R 2014 Laser Photonics Rev. 8 251 Google Scholar
[20]	Wu R B, Zhang J H, Yao N, Fang W, Qiao L L, Fang C, Lin J T, Cheng Y 2018 Opt. Lett. 43 4116 Google Scholar
[21]	Zheng Y L, Fang Z W, Liu S J, Cheng Y, Chen X F 2019 Phys. Rev. Lett. 122 253902 Google Scholar
[22]	Fang Z W, Xu Y X, Wang M, Qiao L L, Lin J T, Fang W, Cheng Y 2017 Sci. Rep. 7 45610 Google Scholar
[23]	Rao A, Fathpour S 2018 IEEE J. Sel. Top. Quantum Electron. 24 8200912 Google Scholar
[24]	Rao A, Fathpour S 2018 IEEE J. Sel. Top. Quantum Electron. 24 3400114 Google Scholar
[25]	Honardoost A, Gonzalez G F C, Khan S, Malinowski M, Rao A, Tremblay J E, Yadav A, Richardson K, Wu M C, Fathpour S 2018 IEEE Photonics J. 10 4500909 Google Scholar
[26]	Gonzalez G F C, Malinowski M, Honardoost A, Fathpour S 2019 Appl. Opt. 58 D1 Google Scholar
[27]	Rao A, Abdelsalam K, Sjaardema T, Honardoost A, Camacho G G F, Fathpour S 2019 Opt. Express 27 25920 Google Scholar
[28]	Wang T, Ng D K T, Ng S K, Toh Y T, Chee A K L, Chen G F R, Wang Q, Tan D T H 2015 Laser Photonics Rev. 9 498 Google Scholar
[29]	Honardoost A, Juneghani F A, Safian R, Fathpour S 2019 Opt. Express 27 6495 Google Scholar
[30]	Rao A, Chiles J, Khan S, Toroghi S, Malinowski M, Camacho G G F, Fathpour S 2017 Appl. Phys. Lett. 110 111109 Google Scholar
[31]	Rao A, Patil A, Chiles J, Malinowski M, Novak S, Richardson K, Rabiei P, Fathpour S 2015 Opt. Express 23 22746 Google Scholar
[32]	Luo R, He Y, Liang H X, Li M X, Lin Q 2018 Optica 5 1006 Google Scholar
[33]	He Y, Liang H X, Luo R, Li M X, Lin Q 2018 Opt. Express 26 16315 Google Scholar
[34]	Chen J Y, Sua Y M, Fan H, Huang Y P 2018 OSA Continuum 1 229 Google Scholar
[35]	Chen J Y, Sua Y M, Ma Z H, Tang C, Li Z, Huang Y P 2019 OSA Continuum 2 2914 Google Scholar
[36]	Reich M, Korte F, Fallnich C, Welling H, Tünnermann A 1998 Opt. Lett. 23 1817 Google Scholar
[37]	Wolf R, Breunig I, Zappe H, Buse K 2018 Opt. Express 26 19815 Google Scholar
[38]	Wang M, Wu R B, Lin J T, Zhang J H, Fang Z W, Chai Z F, Cheng Y 2019 Quantum Eng. 1 1 Google Scholar
[39]	Fang Z W, Haque S, Lin J T, Wu R B, Zhang J H, Wang M, Zhou J X, Rafa M, Tao L, Cheng Y 2019 Opt. Lett. 44 1214 Google Scholar
[40]	Luo R, Jiang H W, Liang H X, Chen Y P, Lin Q 2017 Opt. Lett. 42 1281 Google Scholar
[41]	Jiang H W, Luo R, Liang H X, Chen X F, Chen Y P, Lin Q 2017 Opt. Lett. 42 3267 Google Scholar
[42]	Zhang M, Wang C, Cheng R, Shams A A, Lončar M 2017 Optica 4 1536 Google Scholar
[43]	Fang Z W, Yao N, Wang M, Lin J T, Zhang J H, Wu R B, Qiao L L, Fang W, Lu T, Cheng Y 2017 Int. J. Optomechatronics 11 47 Google Scholar
[44]	Guarino A, Poberaj G, Rezzonico D, Riccardo D, Günter P 2007 Nat. Photonics 1 407 Google Scholar
[45]	Ren T, Zhang M, Wang C, Shao L B, Reimer C, Zhang Y, King O, Esman R, Cullen T, Lončar M 2019 IEEE Photonics Technol. Lett. 31 889 Google Scholar
[46]	Jin M W, Chen J Y, Sua Y M, Huang Y P 2019 Opt. Lett. 44 1265 Google Scholar
[47]	Wang C, Zhang M, Stern B, Lipson M, Lončar M 2018 Opt. Express 26 1547 Google Scholar
[48]	Wang C, Zhang M, Chen X, Bertrand M, Shams A A, Chandrasekhar S, Winzer P, Lončar M 2018 Nature 562 101 Google Scholar
[49]	He M B, Xu M Y, Ren Y X, Jian J, Ruan Z L, Xu Y S, Gao S Q, Sun S H, Wen X Q, Zhou L D, Liu L, Guo C J, Chen H, Yu S Y, Liu L, Cai X L 2019 Nat. Photonics 13 359 Google Scholar
[50]	Ahmed A N R, Nelan S, Shi S Y, Yao P, Mercante A, Prather D W 2020 Opt. Lett. 45 1112 Google Scholar
[51]	Thomaschewski M, Zenin V A, Wolff C, Bozhevolnyi S I 2020 Nat. Commun. 11 748 Google Scholar
[52]	Luo R, He Y, Liang H X, Li M X, Ling J W, Lin Q 2019 Phys. Rev. Appl. 11 034026 Google Scholar
[53]	Luo R, Jiang H W, Rogers S, Liang H X, He Y, Lin Q 2017 Opt. Express 25 24531 Google Scholar
[54]	Lin J T, Yao N, Hao Z Z, Zhang J h, Mao W B, Wang M, Chu W, Wu R B, Fang Z W, Qiao L L, Fang W, Bo F, Cheng Y 2019 Phys. Rev. Lett. 122 173903 Google Scholar
[55]	Liu S J, Zheng Y L, Fang Z W, Ye X N, Cheng Y, Chen X F 2019 Opt. Lett. 44 1456 Google Scholar
[56]	Ye X N, Liu S J, Chen Y P, Zheng Y L, Chen X F 2020 Opt. Lett. 45 523 Google Scholar
[57]	Wolf R, Jia Y C, Bonaus S, Werner C S, Herr S J, Breunig I, Buse K, Zappe H 2018 Optica 5 872 Google Scholar
[58]	Chen J Y, Ma Z H, Sua Y M, Li Z, Tang C, Huang Y P 2019 Optica 6 1244 Google Scholar
[59]	Lu J J, Surya J B, Liu X W, Bruch A W, Gong Z, Xu Y T, Tang H X 2019 Optica 6 1455 Google Scholar
[60]	Hao Z Z, Zhang L, Gao A, Mao W B, Lyu X D, Gao X M, Bo F, Gao F, Zhang G Q, Xu J J 2018 Sci. China, Ser. G 61 114211 Google Scholar
[61]	Hao Z Z, Zhang L, Mao W B, Gao A, Gao X M, Gao F, Bo F, Zhang G Q, Xu J J 2020 Photonics Res. 8 311 Google Scholar
[62]	Sua Y M, Chen J Y, Huang Y P 2018 Opt. Lett. 43 2965 Google Scholar
[63]	Niu Y F, Lin C, Liu X Y, Chen Y, Hu X P, Zhang Y, Cai X L, Gong Y X, Xie Z D, Zhu S N 2020 Appl. Phys. Lett. 116 Google Scholar
[64]	Zhang M, Buscaino B, Wang C, Shams A A, Reimer C, Zhu R R, Kahn J M, Lončar M 2019 Nature 568 373 Google Scholar
[65]	Wang C, Zhang M, Yu M J, Zhu R R, Hu H, Lončar M 2019 Nat. Commun. 10 1 Google Scholar
[66]	Yu M J, Desiatov B, Okawachi Y, Gaeta A L, Lončar M 2019 Opt. Lett. 44 1222 Google Scholar
[67]	Jiang W C, Lin Q 2016 Sci. Rep. 6 36920 Google Scholar
[68]	Cai L T, Mahmoud A, Khan M, Mahmoud M, Mukherjee T, Bain J, Piazza G 2019 Photonics Res. 7 1003 Google Scholar
[69]	Yao N, Zhou J X, Gao R H, Lin J T, Wang M, Cheng Y, Fang W, Tong L M 2020 Opt. Express 28 12416 Google Scholar
[70]	Mahmoud M, Ghosh S, Piazza G 2015 CLEO: Science and Innovations San Jose, USA, May 10–15, 2015 pSW41.7
[71]	Chen Z H, Peng R H, Wang Y w, Zhu H B, Hu H 2017 Opt. Mater. Express 7 4010 Google Scholar
[72]	Krasnokutska I, Chapman R J, Tambasco J L J, Peruzzo A 2019 Opt. Express 27 17681 Google Scholar
[73]	Khan M, Bain J A, Piazza G 2019 Opt. Lett. 44 4558 Google Scholar

[1]	Gao Rong, Yang Ya-Nan, Zhan Chen-Yi, Zhang Zong-Zhen, Deng Yi, Wang Zi-Xiao, Liang Kun, Feng Su-Chun. Design of optical frequency comb based on dual frequency pumped normal dispersion silicon carbide microresonator. Acta Physica Sinica, 2024, 73(3): 034203. doi: 10.7498/aps.73.20231442
[2]	Liu Li-Qiang, Su Wei-Lun, Liu Jun-Ming, Zou Yu, Hong Li-Hong, Li Zhi-Yuan. Design and angular robustness test of chirped periodically poled lithium niobate crystal for 1064 nm second-harmonic generation experiment. Acta Physica Sinica, 2024, 73(17): 174204. doi: 10.7498/aps.73.20240778
[3]	Hu Sheng-Run, Ji Xue-Qiang, Wang Jin-Jin, Yan Jie-Yun, Zhang Tian-Yue, Li Pei-Gang. Ultralow switching threshold optical bistable devices based on epsilon-near-zero Ga₂O₃-SiC-Ag multilayer structures. Acta Physica Sinica, 2024, 73(5): 054201. doi: 10.7498/aps.73.20231534
[4]	Wu Bo, Wang Jue, Wang Wei, Zhou Guo-Fu. Research advances in nondegenerate two-photonabsorption and its applications. Acta Physica Sinica, 2023, 72(20): 204204. doi: 10.7498/aps.72.20230911
[5]	Xiong Xiao, Cao Qi-Tao, Xiao Yun-Feng. Thin-film lithium niobate photonic integrated devices: Advances and oppotunities. Acta Physica Sinica, 2023, 72(23): 234201. doi: 10.7498/aps.72.20231295
[6]	Li Ming-Zhou, Li Zhi-Yuan. Structure design and numerical simulation of chirped periodically polarized lithium niobate crystal for broadband mid-infrared laser generation. Acta Physica Sinica, 2022, 71(13): 134206. doi: 10.7498/aps.71.20220016
[7]	Xu Fan, Zhao Yan, Wu Yu-Hang, Wang Wen-Chi, Jin Xue-Ying. Stability and non-linear dynamic analysis of Kerr optical frequencycombs in dual-coupled microcavities with high-order dispersion. Acta Physica Sinica, 2022, 71(18): 184204. doi: 10.7498/aps.71.20220691
[8]	Li Hai-Peng, Zhou Jia-Sheng, Ji Wei, Yang Zi-Qiang, Ding Hui-Min, Zhang Zi-Tao, Shen Xiao-Peng, Han Kui. Effect of edge on nonlinear optical property of graphene quantum dots. Acta Physica Sinica, 2021, 70(5): 057801. doi: 10.7498/aps.70.20201643
[9]	Bai Rui-Xue, Yang Jue-Han, Wei Da-Hai, Wei Zhong-Ming. Research progress of low-dimensional semiconductor materials in field of nonlinear optics. Acta Physica Sinica, 2020, 69(18): 184211. doi: 10.7498/aps.69.20200206
[10]	Xu Xin, Jin Xue-Ying, Hu Xiao-Hong, Huang Xin-Ning. Spatiotemporal evolution and spectral character of second harmonic generation in optical microresonator. Acta Physica Sinica, 2020, 69(2): 024203. doi: 10.7498/aps.69.20191294
[11]	Li Xiao-Nan, Guan Guo-Rong, Liu Yi-Kun, Liang Hao-Wen, Zhang Ai-Qin, Zhou Jian-Ying. Fabrication and physical measurement accuracy of nanoscale standard samples for vector beams confocal laser scanning microscopy. Acta Physica Sinica, 2019, 68(14): 148102. doi: 10.7498/aps.68.20190252
[12]	Hou Guo-Hui, Luo Teng, Chen Bing-Ling, Liu Jie, Lin Zi-Yang, Chen Dan-Ni, Qu Jun-Le. Experimental study on two-photon fluorescence and coherent anti-Stokes Raman scattering microscopy. Acta Physica Sinica, 2017, 66(10): 104204. doi: 10.7498/aps.66.104204
[13]	Deng Jun-Hong, Li Gui-Xin. Nonlinear photonic metasurfaces. Acta Physica Sinica, 2017, 66(14): 147803. doi: 10.7498/aps.66.147803
[14]	Zhang Long, Han Hai-Nian, Hou Lei, Yu Zi-Jiao, Zhu Zheng, Jia Yu-Lei, Wei Zhi-Yi. Supercontinuum generation in photonic crystal fiber and tapered single-mode fiber. Acta Physica Sinica, 2014, 63(19): 194208. doi: 10.7498/aps.63.194208
[15]	Lu Jing-Jing, Feng Miao, Zhan Hong-Bing. Preparation of graghene oxide/chitosan composite films and investigations on their nonlinear optical limiting effect. Acta Physica Sinica, 2013, 62(1): 014204. doi: 10.7498/aps.62.014204
[16]	Liu Feng, Hu Xiao-Kun, Li Yan-Feng, Xing Qi-Rong, Hu Ming-Lie, Chai Lu, Wang Ching-Yue. GaP terahertz emitter with micro-pyramid anti-reflection layer. Acta Physica Sinica, 2012, 61(4): 040703. doi: 10.7498/aps.61.040703
[17]	Sun Bo, Liu Jin-Song, Ling Fu-Ri, Wang Ke-Jia, Zhu Da-Qing, Yao Jian-Quan. Investigation of the operation characteristics of terahertz-wave parametric oscillator based on LiTaO3. Acta Physica Sinica, 2009, 58(3): 1745-1751. doi: 10.7498/aps.58.1745
[18]	Yang Guang, Chen Zheng-Hao. Large optical nonlinearities in Ag-doped BaTiO3 nanocomposite films. Acta Physica Sinica, 2007, 56(2): 1182-1187. doi: 10.7498/aps.56.1182
[19]	Liang Xiao-Rui, Zhao Bo, Zhou Zhi-Hua. Ab initio study on the second-order nonlinear optical properties of some coumarin derivatives. Acta Physica Sinica, 2006, 55(2): 723-728. doi: 10.7498/aps.55.723
[20]	MA JIN-YI, QIU XI-JUN. INTERACTION BETWEEN AN ELECTRONIC SYSTEM AND MULTIPHOTONS IN A STRONG LASER FIELD. Acta Physica Sinica, 2001, 50(3): 416-421. doi: 10.7498/aps.50.416

Catalog

Vol. 69, Issue 15 - 2020-08-05

Metrics

Abstract views: 18984
PDF Downloads: 997
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板