压-电-化学耦合增强策略及机理研究进展

贾艳敏; 王晓星; 张祺昌; 武峥

doi:10.7498/aps.72.20222078

摘要

压电材料能够收集环境中存在的微小的机械能, 具有将机械信号转换为电信号的强大能力. 利用压电材料的压电效应与电化学氧化还原效应二者的耦合可以实现压-电-化学耦合. 近年来, 压-电-化学耦合在收集清洁能源和处理废水保护环境方面受到国内外研究人员的广泛关注. 本文综述了增强压-电-化学耦合的策略, 从构建异质结、负载贵金属、构筑相界、混合碳或石墨烯和调控缺陷方面出发进行了总结梳理. 从电子的运输和转移、材料相变和氧空位的角度解释不同策略中的物理机理, 并对研究前景进行了展望.

关键词:

Abstract

Piezoelectric materials can harvest tiny mechanical energy existing in the environment, and have strong ability to convert mechanical signals into electrical signals. Piezo-electro-chemical coupling can be realized via combining piezoelectric effect of piezoelectric materials with electrochemical redox effect. In recent years, piezo-electro-chemical coupling has attracted a lot of attention from researchers in harvesting vibration energy to treat dye wastewater. The piezoelectric catalyst material dispersed in solution is deformed by ultrasonic vibrations. Owing to the piezoelectric effect and spontaneous polarization effects, positive and negative charges are generated at both ends of the catalyst, which can further react with dissolved oxygen and hydroxide ions in the solution to generate superoxide and hydroxyl radicals (·${}{\rm{O}}_2^- $ and ·OH) for decomposing organic dyes. However, ordinary piezoelectric catalytic materials are often difficult to meet people's pursuit of efficient treatment of organic dyes. Researchers have conducted a lot of researches on piezo-electro-chemical coupling, mainly focusing on the following two aspects: 1) the modification of piezoelectric catalysts to achieve extended carrier lifetime, accelerate carrier separation and high piezoelectric coefficients, and 2) the combination of piezo-electro-chemical coupling with photocatalysis to suppress photogenerated carrier compounding to obtain high synergistic catalytic performance. In this work, the following five strategies to enhance the piezo-electro-chemical coupling via modifying piezoelectric catalyst materials are introduced. The heterojunction structure is constructed to promote the separation of electron-hole pairs. The precious metal is coated on the surface of the catalyst to accelerate the transport and transfer of electrons. The catalyst composition is regulated and controlled to obtain an increased piezoelectric coefficient at the phase boundary. Carbon or graphene are mixed in the catalyst to accelerate the electron transfer on the surface of piezoelectric material. The number of active sites increases through introducing defects into the catalyst to increase the concentration of carriers. The physical mechanisms of five different strategies are described from the perspectives of electron transport and transfer, phase transition, and oxygen vacancies. In addition, the prospects for piezo-electro-chemical coupling in energy and biomedical applications such as hydrogen production, carbon dioxide reduction, tumor therapy and tooth whitening are presented.

Keywords:

作者及机构信息

1.
西安邮电大学理学院, 西安　710121

2.
西安工程大学环境与化学工程学院, 西安　710048

通信作者: 贾艳敏, jiayanmin@xupt.edu.cn ; 武峥, wuzheng@xpu.edu.cn

基金项目: 国家自然科学基金(批准号: 22179108)资助的课题.

Authors and contacts

1.
School of Science, Xi’an University of Posts and Telecommunications, Xi’an 710121, China

2.
School of Environmental and Chemical Engineering, Xi’an Polytechnic University, Xi’an, 710048, China

Corresponding author: Jia Yan-Min, jiayanmin@xupt.edu.cn ; Wu Zheng, wuzheng@xpu.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 22179108).

文章全文 : translate this paragraph

参考文献

[1]	Dai X Q, Chen L, Li Z Y, Li X, Wang J F, Hu X, Zhao L H, Jia Y M, Sun S X, Wu Y, He Y M 2021 J. Colloid Interface Sci. 603 220 Google Scholar
[2]	Zhang W H, Wang X J, Zhang Y C, Bochove B, Mäkilä E, Seppälä J, Xu W Y, Willför S, Xu C L 2020 Sep. Purif. Technol. 242 116523 Google Scholar
[3]	Oliveira L V, Bennici S, Josien L, Limousy L, Bizeto M A, Camilo F F 2020 Carbohydr. Polym. 230 115621 Google Scholar
[4]	Wang S S, Wu Z, Chen J, Ma J P, Ying J S, Cui S C, Yu S G, Hu Y M, Zhao J H, Jia Y M 2019 Ceram. Int. 45 11703 Google Scholar
[5]	Muraro P C L, Mortari S R, Vizzotto B S, Chuy G, Dos Santos C, Brum L F W, da Silva W L 2020 Sci. Rep. 10 1 Google Scholar
[6]	Roy J S, Dugas G, Morency S, Messaddeq Y 2020 Physica E:Low Dimens. Syst. Nanostruct. 120 114114 Google Scholar
[7]	Van Tran C, La D D, Hoai P N T, Ninh H D, Hong P N T, Vu T H T, Nadda A K, Nguyen X C, Nguyen D D, Ngo H H 2021 J. Hazard. Mater. 420 126636 Google Scholar
[8]	李冬冬, 王丽莉 2012 61 034212 Google Scholar Li D D, Wang L L 2012 Acta Phys. Sin. 61 034212 Google Scholar
[9]	Wu W, Yin X, Dai B Y, Kou J H, Ni Y, Lu C H 2020 Appl. Surf. Sci. 517 146119 Google Scholar
[10]	Lei H, Zhang H H, Zou Y, Dong X P, Jia Y M, Wang F F 2019 J. Alloys Compd. 809 151840 Google Scholar
[11]	佟建波, 黄茜, 张晓丹, 张存善, 赵颖 2012 61 047801 Google Scholar Tong J B, Huang Q, Zhang X D, Zhang C S, Zhao Y 2012 Acta Phys. Sin. 61 047801 Google Scholar
[12]	Moghaddas S, Elahi B, Javanbakht V, 2020 J. Alloys Compd. 821 153519 Google Scholar
[13]	赵娟, 胡慧芳, 曾亚萍, 程彩萍 2013 62 158104 Google Scholar Zhao J, Hu H F, Zeng Y P, Cheng C P 2013 Acta Phys. Sin. 62 158104 Google Scholar
[14]	Cha B J, Woo T G, Han S W, Saqlain S, Seo H O, Cho H K, Jee Y K, Kim Y D 2018 Catalysts 8 500 Google Scholar
[15]	Ni M, Leung M, Leung D, Sumathy K 2007 Renew. Sust. Energ. Rev. 11 401 Google Scholar
[16]	Xu X L, Xiao L B, Jia Y M, Hong Y T, Ma J P, Wu Z 2018 J. Electron. Mater. 47 536 Google Scholar
[17]	Ma J P, Chen L, Wu Z, Chen J, Jia Y M, Hu Y M 2019 Ceram. Int. 45 11934 Google Scholar
[18]	Yu D F, Liu Z H, Zhang J M, Li S, Zhao Z C, Zhu L F, Liu W S, Lin Y H, Liu H, Zhang Z T 2019 Nano Energy 58 695 Google Scholar
[19]	Ma J P, Wu Z, Luo W S, Zheng Y Q, Jia Y M, Wang L, Huang H T 2018 Ceram. Int. 44 21835 Google Scholar
[20]	李宗宝, 王霞, 樊帅伟 2014 63 157102 Google Scholar Li Z B, Wang X, Fan S W 2014 Acta Phys. Sin. 63 157102 Google Scholar
[21]	You H L, Ma X X, Wu Z, Fei L F, Chen X Q, Yang J, Liu Y S, Jia Y M, Li H M, Wang F F, Huang H T 2018 Nano Energy 52 351 Google Scholar
[22]	Wu Y L, Ma Y L, Zheng H Y, Ramakrishna S 2021 Materials & Design 211 110164 Google Scholar
[23]	Hooper T E, Roscow J I, Mathieson A, Khanbareh H, Goetzee-Barral A J, Bell A J 2021 J. Eur. Ceram. Soc. 41 6115 Google Scholar
[24]	Hong K S, Xu H F, Konishi H, Li X C 2010 J. Phys. Chem. Lett. 1 997 Google Scholar
[25]	Feng Z Y, Tan O K, Zhu W G, Jia Y M, Luo H S 2008 Appl. Phys. Lett. 92 142910 Google Scholar
[26]	李飞, 张树君, 徐卓 2020 69 217703 Google Scholar Li F, Zhang S J, Xu Z 2020 Acta Phys. Sin. 69 217703 Google Scholar
[27]	Hong K S, Xu H F, Konishi H, Li X C 2012 J. Phys. Chem. C 116 13045 Google Scholar
[28]	孙奇薇, 薛国梁, 周学凡, 罗行, 周科朝, 张斗 2021 中国有色金属学报 31 17 Google Scholar Sun Q W, Xue G L, Zhou X F, Luo H, Zhou K C, Zhang D 2021 T. Nonferr. Metal. Soc. 31 17 Google Scholar
[29]	洪元婷, 马江平, 武峥, 应静诗, 尤慧琳, 贾艳敏 2018 67 107702 Google Scholar Hong Y T, Ma J P, Wu Z, Ying S J, You H L, Jia Y M 2018 Acta Phys. Sin. 67 107702 Google Scholar
[30]	Fu D, Endo M, Taniguchi H, Taniyama T, Itoh M 2007 Appl. Phys. Lett. 90 252907
[31]	Tu S C, Guo Y X, Zhang Y H, Hu C, Zhang T R, Ma T Y, Huang H W 2020 Adv. Funct. Mater. 30 2005158 Google Scholar
[32]	Wang M Y, Wang B, Huang F, Lin Z Q 2019 Angew. Chem. , Int. Ed. 58 7526 Google Scholar
[33]	Pan L, Sun S C, Chen Y, Wang P H, Wang J Y, Zhang X W, Zou J J, Wang Z L 2020 Adv. Energy Mater. 10 2000214 Google Scholar
[34]	Wang X D, Rohrer G S, Li H X, 2018 MRS Bull. 43 946 Google Scholar
[35]	Liang Z, Yan C F, Rtimi S, Bandara J, 2019 Appl. Catal. B-environ. 241 256 Google Scholar
[36]	Liu W, Wang M L, Xu C X, Chen S F 2012 Chem. Eng. J. 209 386 Google Scholar
[37]	Yan Y X, Yang H, Yi Z, Xian T, Li R S, Wang X X 2019 Desalin. Water Treat. 170 349 Google Scholar
[38]	Wang L K, Wang J F, Ye C Y, Wang K Q, Zhao C R, Wu Y, He Y M 2021 Ultrason. Sonochem. 80 105813 Google Scholar
[39]	Zheng Y Q, Jia Y M, Li H M, Wu Z, Dong X P 2020 J Mater. Sci. 55 14787 Google Scholar
[40]	Li L, She X J, Yi J J, Pan L, Xia K X, Wei W, Zhu X W, Chen Z G, Xu H, Li H M 2019 Appl. Surf. Sci. 469 933 Google Scholar
[41]	Xing P X, Zhang W Q, Chen L, Dai X Q, Zhang J L, Zhao L H, He Y M 2020 Sustain. Energy Fuels 4 1112 Google Scholar
[42]	Jakob M, Levanon H, Kamat P V 2003 Nano Lett. 3 353 Google Scholar
[43]	Subramanian V, Wolf E E, Kamat P V 2003 J. Phys. Chem. B 107 7479 Google Scholar
[44]	Lin E Z, Wu J, Qin N, Yuan B W, Bao D H 2018 Catal. Sci. Technol. 8 4788 Google Scholar
[45]	Li Z Y, Zhang Q L, Wang L K, Yang J Y, Wu Y, He Y M 2021 Ultrason. Sonochem. 78 105729 Google Scholar
[46]	Lin E Z, Kang Z H, Wu J, Huang R, Qin N, Bao D H 2021 Appl. Catal. B 285 119823 Google Scholar
[47]	Zhao T L, Bokov A A, Wu J, Wang H, Wang C M, Yu Y, Wang C L, Zeng K Y, Ye Z G, Dong, S X 2019 Adv. Funct. Mater. 29 1807920 Google Scholar
[48]	Zhang A, Liu Z Y, Xie B, Lu J S, Guo K, Ke S M, Shu L L, Fan H Q 2020 Appl. Catal. B 279 119353 Google Scholar
[49]	Yuan B W, Wu J, Qin N, Lin E Z, Kang Z H, Bao D H 2019 Appl. Mater. Today 17 183 Google Scholar
[50]	Wu J G, Wu T 2020 ACS Appl. Mater. 12 52231 Google Scholar
[51]	Pham Thi T P, Yan Z, Nick G, Hamideh K, Nguyen Phuc H D, Xuefan Z, Dou Z, Kechao Z, Steve D, Chris B 2020 iScience 23 101095 Google Scholar
[52]	Kapat K, Shubhra Q T, Zhou M, Leeuwenburgh S 2020 Adv. Funct. Mater. 30 1909045 Google Scholar
[53]	Dawson J A, Sinclair D C, Harding J H, Freeman C L 2014 Chem. Mater. 26 6104
[54]	Reaney I, Colla E, Setter N 1994 Jpn. J. Appl. Phys. 33 3984 Google Scholar
[55]	Wu J, Qin N, Lin E Z, Kang Z H, Bao D H 2021 Mater. Today Energy 21 100732 Google Scholar
[56]	Chen L, Jia Y M, Zhao J H, Ma J P, Wu Z, Yuan G L, Cui X Z 2021 J. Colloid Interface Sci. 586 758 Google Scholar
[57]	Li X, Lin H M, Chen X, Niu H, Zhang T, Liu J Y, Qu F Y 2015 New J. Chem. 39 7863 Google Scholar
[58]	Yao W, Shen C, Lu Y 2013 Compos. Sci. Technol. 87 8 Google Scholar
[59]	Hou T, Cao F, Li M L, Wang J L, Lv L L 2020 J. Environ. Sci. Eng. 8 84 Google Scholar
[60]	Kumar M, Singh G, Vaish R 2021 Mater. Adv 2 4093 Google Scholar
[61]	Bai S L, Sun L X, Sun J H, Han J Y, Zhang K W, Li Q Q, Luo R X, Li D Q, Chen A 2021 J. Colloid Interface Sci. 587 183 Google Scholar
[62]	Zhao Z C, Wei L Y, Li S, Zhu L F, Su Y P, Liu Y, Bu Y B, Lin Y H, Liu W S, Zhang Z T 2020 J. Mater. Chem. A 8 16238 Google Scholar
[63]	Prakash J, Prasad U, Alexander R, Bahadur J, Dasgupta K, Kannan A N M 2019 Langmuir 35 14492 Google Scholar
[64]	Miao Y, Tian W R, Han J, Li N J, Chen D Y, Xu Q F, Lu J M 2022 Nano Energy 100 107473 Google Scholar
[65]	Zhou X F, Shen B, Zhai J W, Hedin N 2021 Adv. Funct. Mater. 31 2009594 Google Scholar
[66]	Guan J F, Jia Y M, Chang T, Ruan L J, Xu T S, Zhang Z, Yuan G L, Wu Z, Zhu G Q 2022 Sep. Purif. Technol. 286 120450 Google Scholar
[67]	Ji M, Kim J H, Ryu C H, Lee Y I 2022 Nano Energy 95 106993 Google Scholar
[68]	Fu C, Wu T, Sun G W, Yin G F, Wang C, Ran G X, Song Q J 2023 Appl. Catal. B 323 122196 Google Scholar
[69]	Khanbabaee B, Mehner E, Richter C, Hanzig J, Zschornak M, Pietsch U, St¨ocker H, Leisegang T, Meyer D C, Gorfman S 2016 Appl. Phys. Lett. 109 222901 Google Scholar
[70]	Kang Z H, Lin E Z, Qin N, Wu J, Yuan B W, Bao D H 2021 Environ. Sci. :Nano 8 1376 Google Scholar
[71]	Zhang D F, Su C H, Li H, Pu X P, Geng Y L 2020 J. Phys. Chem. Solids 139 109326 Google Scholar
[72]	Zhao Q, Xiao H Y, Geng H F, Zheng Z P, Wang J S, Wang F F, Guo Y P 2021 Nano Energy 85 106028 Google Scholar
[73]	Sun X X, Li R C, Yang Z W, Zhang N, Wu C, Li J H, Chen Y L, Chen Q, Zhang J, Yan H J, Lv X, Wu J G 2022 Appl. Catal. B 313 121471 Google Scholar
[74]	Li J H, Wei X W, Sun X X, Li R C, Wu C, Liao J Y, Zhang T, Wu J G 2022 ACS Appl. Mater. Inter. 14 46765 Google Scholar
[75]	Liu Z, Wen X R, Wang Y, Jia Y M, Wang F F, Yuan G L, Wang Y J 2022 Adv. Mater. Technol. 7 2101484 Google Scholar
[76]	Ruan L J, Jia Y M, Guan J F, Xue B, Huang S H, Wang Z H, Fu Y H, Wu Z 2022 J. Clean. Prod. 345 131060 Google Scholar
[77]	Wang S Y, Gao Y Y, Miao S, Liu T F, Mu L C, Li R G, Li R G, Fan F T, Li C 2017 J. Am. Chem. Soc. 139 11771 Google Scholar
[78]	Chen S, Zhu P, Mao L J, Wu W C, Lin H, Xu D L, Lu X Y, Shi J L 2023 Adv. Mater. 2208256
[79]	Wang Y, Wen X R, Jia Y M, Huang M, Wang F F, Zhang X H, Bai Y Y, Yuan G L, Wang Y J 2020 Nat. Commun. 11 1328 Google Scholar

施引文献

图 1 增强压-电-化学耦合5种策略, 异质结、贵金属负载、相界、缺陷、混合碳或石墨烯

Fig. 1. Five strategies to enhance piezo-electro-chemical coupling, including heterojunction, coating precious metal, phase boundary, defects, mixing carbon or graphene.

下载: 全尺寸图片幻灯片

图 2 BTO/CN异质结压-电-化学耦合的机理图^[39]

Fig. 2. Mechanism diagram for the piezo-electro-chemical coupling of BTO/CN heterostructures ^[39].

下载: 全尺寸图片幻灯片

图 3 异质结材料不同含量助剂对染料的降解率的影响　(a) CoO_x/BiFeO₃异质结^[38]; (b) BTO/CN异质结^[39]

Fig. 3. Effect of different content of cocatalyst in heterojunction materials on dye decomposition ratio: (a) CoO_x/BiFeO₃ heterostructure^[38]; (b) BTO/CN heterostructure^[39].

下载: 全尺寸图片幻灯片

图 4 Ag负载的BTO压-电-化学耦合的机理图^[44]

Fig. 4. Mechanism diagram for the piezo-electro-chemical coupling of Ag-coated BTO^[44].

下载: 全尺寸图片幻灯片

图 5 不同Ag含量的BTO-Ag降解RhB染料的反应速率常数k值对比^[44]

Fig. 5. Comparison of reaction rate constant k of RhB dye decomposition by BTO-Ag with different Ag content^[44].

下载: 全尺寸图片幻灯片

图 6 通过调控组分, 构建两相共存区^[48]

Fig. 6. Schematic diagram of constructing two-phase coexistence zone through regulating components^[48].

下载: 全尺寸图片幻灯片

图 7 不同Sr含量的Ba_1–xSr_xTiO₃ 降解MO染料^[55]

Fig. 7. Decomposition of MO dye by Ba_1–xSr_xTiO₃ with different Sr content^[55].

下载: 全尺寸图片幻灯片

图 8 不同C含量对BaTiO₃降解RhB染料的影响^[56]

Fig. 8. Effects of RhB dye decomposition by BaTiO₃ with different C content^[56].

下载: 全尺寸图片幻灯片

图 9 BaTiO₃/C的压-电-化学耦合示意图^[56]

Fig. 9. Mechanism diagram for the piezo-electro-chemical coupling of BaTiO₃/C^[56].

下载: 全尺寸图片幻灯片

图 10 Graphene/BiVO₄的压-电-化学耦合示意图^[60]

Fig. 10. Mechanism diagram for the piezo-electro-chemical coupling of graphene/BiVO₄^[60].

下载: 全尺寸图片幻灯片

图 11 CNC 在热处理前后对RhB染料的降解率^[66]

Fig. 11. Decomposition ratio of RhB dye by CNC before and after heat treatment^[66]

下载: 全尺寸图片幻灯片

表 1 不同策略对有机染料降解结果汇总

Table 1. Summary of decomposition results of organic dyes via different strategies.

策略	复合材料	助剂	增强前的降解率D 或反应速率常数k	增强后的降解率D 或反应速率常数k
构建异质结	CoO_x/BiFeO₃	CoO(光沉积时间为3 h)	D = 50.76%	D = 81.2% ^[38]
构建异质结	BaTiO₃/g-C₃N₄	g-C₃N₄(质量分数为15%)	D = 57%	D = 82% ^[39]
负载贵金属	BaTiO₃-Ag	Ag(质量分数为2.09%)	D = 15%	D = 84% ^[44]
负载贵金属	Ag/PbBiO₂I	Ag(质量分数为0.2%)	k = 0.0024 min^–1	k = 0.0165 min^–1^[45]
构筑相界	(1–x)Na_0.5K_0.5NbO₃-xLiNbO₃	Li (x = 0.006)	D = 53%	D = 91% ^[48]
	(1–x)(Pb_0.9625Sm_0.025) (Mg_1/3Nb_2/3)O₃-xPbTiO₃	PbTiO₃(x = 0.29)		k = 0.0453 min^–1^[49]
	Ba_1–xSr_xTiO₃	Sr(x = 0.20)	k = 0.005 min^–1	k = 0.025 min^–1^[51]
	0.96(K_0.48Na_0.52)Nb_0.955Sb_0.045O₃-0.04(Bi_0.5Na_0.5)ZrO₃	0.04(Bi_0.5Na_0.5)ZrO₃	k = 0.043 min^–1	k = 0.091 min^–1^[73]
	0.82 Ba(Ti_0.89Sn_0.11)O₃-0.18(Ba_0.7Ca_0.3)TiO₃	0.18(Ba_0.7Ca_0.3)TiO₃	k = 0.0706 min^–1	k = 0.0094 min^–1^[74]
混合碳	BaTiO₃/C	C(质量分数为2%)	D = 48.4%	D = 75.5% ^[56]
混合石墨烯	BaTiO₃@Graphene	Graphene(质量比为2∶1)	k = 0.002 min^–1	k = 0.028 min^–1^[59]
混合石墨烯	Graphene/BiVO₄	Graphene(质量分数为2%)	D = 19%	D = 81% ^[60]
调控缺陷	BaTiO_3–x		k = 0.0084 min^–1	k = 0.0101 min^–1^[67]
	C₃N_5–x-O		D = 73.5%	D = 99%^[68]
	CNC		D = 34.58%	D = 96.65% ^[66]

下载: 导出CSV

map

[1]	Dai X Q, Chen L, Li Z Y, Li X, Wang J F, Hu X, Zhao L H, Jia Y M, Sun S X, Wu Y, He Y M 2021 J. Colloid Interface Sci. 603 220 Google Scholar
[2]	Zhang W H, Wang X J, Zhang Y C, Bochove B, Mäkilä E, Seppälä J, Xu W Y, Willför S, Xu C L 2020 Sep. Purif. Technol. 242 116523 Google Scholar
[3]	Oliveira L V, Bennici S, Josien L, Limousy L, Bizeto M A, Camilo F F 2020 Carbohydr. Polym. 230 115621 Google Scholar
[4]	Wang S S, Wu Z, Chen J, Ma J P, Ying J S, Cui S C, Yu S G, Hu Y M, Zhao J H, Jia Y M 2019 Ceram. Int. 45 11703 Google Scholar
[5]	Muraro P C L, Mortari S R, Vizzotto B S, Chuy G, Dos Santos C, Brum L F W, da Silva W L 2020 Sci. Rep. 10 1 Google Scholar
[6]	Roy J S, Dugas G, Morency S, Messaddeq Y 2020 Physica E:Low Dimens. Syst. Nanostruct. 120 114114 Google Scholar
[7]	Van Tran C, La D D, Hoai P N T, Ninh H D, Hong P N T, Vu T H T, Nadda A K, Nguyen X C, Nguyen D D, Ngo H H 2021 J. Hazard. Mater. 420 126636 Google Scholar
[8]	李冬冬, 王丽莉 2012 61 034212 Google Scholar Li D D, Wang L L 2012 Acta Phys. Sin. 61 034212 Google Scholar
[9]	Wu W, Yin X, Dai B Y, Kou J H, Ni Y, Lu C H 2020 Appl. Surf. Sci. 517 146119 Google Scholar
[10]	Lei H, Zhang H H, Zou Y, Dong X P, Jia Y M, Wang F F 2019 J. Alloys Compd. 809 151840 Google Scholar
[11]	佟建波, 黄茜, 张晓丹, 张存善, 赵颖 2012 61 047801 Google Scholar Tong J B, Huang Q, Zhang X D, Zhang C S, Zhao Y 2012 Acta Phys. Sin. 61 047801 Google Scholar
[12]	Moghaddas S, Elahi B, Javanbakht V, 2020 J. Alloys Compd. 821 153519 Google Scholar
[13]	赵娟, 胡慧芳, 曾亚萍, 程彩萍 2013 62 158104 Google Scholar Zhao J, Hu H F, Zeng Y P, Cheng C P 2013 Acta Phys. Sin. 62 158104 Google Scholar
[14]	Cha B J, Woo T G, Han S W, Saqlain S, Seo H O, Cho H K, Jee Y K, Kim Y D 2018 Catalysts 8 500 Google Scholar
[15]	Ni M, Leung M, Leung D, Sumathy K 2007 Renew. Sust. Energ. Rev. 11 401 Google Scholar
[16]	Xu X L, Xiao L B, Jia Y M, Hong Y T, Ma J P, Wu Z 2018 J. Electron. Mater. 47 536 Google Scholar
[17]	Ma J P, Chen L, Wu Z, Chen J, Jia Y M, Hu Y M 2019 Ceram. Int. 45 11934 Google Scholar
[18]	Yu D F, Liu Z H, Zhang J M, Li S, Zhao Z C, Zhu L F, Liu W S, Lin Y H, Liu H, Zhang Z T 2019 Nano Energy 58 695 Google Scholar
[19]	Ma J P, Wu Z, Luo W S, Zheng Y Q, Jia Y M, Wang L, Huang H T 2018 Ceram. Int. 44 21835 Google Scholar
[20]	李宗宝, 王霞, 樊帅伟 2014 63 157102 Google Scholar Li Z B, Wang X, Fan S W 2014 Acta Phys. Sin. 63 157102 Google Scholar
[21]	You H L, Ma X X, Wu Z, Fei L F, Chen X Q, Yang J, Liu Y S, Jia Y M, Li H M, Wang F F, Huang H T 2018 Nano Energy 52 351 Google Scholar
[22]	Wu Y L, Ma Y L, Zheng H Y, Ramakrishna S 2021 Materials & Design 211 110164 Google Scholar
[23]	Hooper T E, Roscow J I, Mathieson A, Khanbareh H, Goetzee-Barral A J, Bell A J 2021 J. Eur. Ceram. Soc. 41 6115 Google Scholar
[24]	Hong K S, Xu H F, Konishi H, Li X C 2010 J. Phys. Chem. Lett. 1 997 Google Scholar
[25]	Feng Z Y, Tan O K, Zhu W G, Jia Y M, Luo H S 2008 Appl. Phys. Lett. 92 142910 Google Scholar
[26]	李飞, 张树君, 徐卓 2020 69 217703 Google Scholar Li F, Zhang S J, Xu Z 2020 Acta Phys. Sin. 69 217703 Google Scholar
[27]	Hong K S, Xu H F, Konishi H, Li X C 2012 J. Phys. Chem. C 116 13045 Google Scholar
[28]	孙奇薇, 薛国梁, 周学凡, 罗行, 周科朝, 张斗 2021 中国有色金属学报 31 17 Google Scholar Sun Q W, Xue G L, Zhou X F, Luo H, Zhou K C, Zhang D 2021 T. Nonferr. Metal. Soc. 31 17 Google Scholar
[29]	洪元婷, 马江平, 武峥, 应静诗, 尤慧琳, 贾艳敏 2018 67 107702 Google Scholar Hong Y T, Ma J P, Wu Z, Ying S J, You H L, Jia Y M 2018 Acta Phys. Sin. 67 107702 Google Scholar
[30]	Fu D, Endo M, Taniguchi H, Taniyama T, Itoh M 2007 Appl. Phys. Lett. 90 252907
[31]	Tu S C, Guo Y X, Zhang Y H, Hu C, Zhang T R, Ma T Y, Huang H W 2020 Adv. Funct. Mater. 30 2005158 Google Scholar
[32]	Wang M Y, Wang B, Huang F, Lin Z Q 2019 Angew. Chem. , Int. Ed. 58 7526 Google Scholar
[33]	Pan L, Sun S C, Chen Y, Wang P H, Wang J Y, Zhang X W, Zou J J, Wang Z L 2020 Adv. Energy Mater. 10 2000214 Google Scholar
[34]	Wang X D, Rohrer G S, Li H X, 2018 MRS Bull. 43 946 Google Scholar
[35]	Liang Z, Yan C F, Rtimi S, Bandara J, 2019 Appl. Catal. B-environ. 241 256 Google Scholar
[36]	Liu W, Wang M L, Xu C X, Chen S F 2012 Chem. Eng. J. 209 386 Google Scholar
[37]	Yan Y X, Yang H, Yi Z, Xian T, Li R S, Wang X X 2019 Desalin. Water Treat. 170 349 Google Scholar
[38]	Wang L K, Wang J F, Ye C Y, Wang K Q, Zhao C R, Wu Y, He Y M 2021 Ultrason. Sonochem. 80 105813 Google Scholar
[39]	Zheng Y Q, Jia Y M, Li H M, Wu Z, Dong X P 2020 J Mater. Sci. 55 14787 Google Scholar
[40]	Li L, She X J, Yi J J, Pan L, Xia K X, Wei W, Zhu X W, Chen Z G, Xu H, Li H M 2019 Appl. Surf. Sci. 469 933 Google Scholar
[41]	Xing P X, Zhang W Q, Chen L, Dai X Q, Zhang J L, Zhao L H, He Y M 2020 Sustain. Energy Fuels 4 1112 Google Scholar
[42]	Jakob M, Levanon H, Kamat P V 2003 Nano Lett. 3 353 Google Scholar
[43]	Subramanian V, Wolf E E, Kamat P V 2003 J. Phys. Chem. B 107 7479 Google Scholar
[44]	Lin E Z, Wu J, Qin N, Yuan B W, Bao D H 2018 Catal. Sci. Technol. 8 4788 Google Scholar
[45]	Li Z Y, Zhang Q L, Wang L K, Yang J Y, Wu Y, He Y M 2021 Ultrason. Sonochem. 78 105729 Google Scholar
[46]	Lin E Z, Kang Z H, Wu J, Huang R, Qin N, Bao D H 2021 Appl. Catal. B 285 119823 Google Scholar
[47]	Zhao T L, Bokov A A, Wu J, Wang H, Wang C M, Yu Y, Wang C L, Zeng K Y, Ye Z G, Dong, S X 2019 Adv. Funct. Mater. 29 1807920 Google Scholar
[48]	Zhang A, Liu Z Y, Xie B, Lu J S, Guo K, Ke S M, Shu L L, Fan H Q 2020 Appl. Catal. B 279 119353 Google Scholar
[49]	Yuan B W, Wu J, Qin N, Lin E Z, Kang Z H, Bao D H 2019 Appl. Mater. Today 17 183 Google Scholar
[50]	Wu J G, Wu T 2020 ACS Appl. Mater. 12 52231 Google Scholar
[51]	Pham Thi T P, Yan Z, Nick G, Hamideh K, Nguyen Phuc H D, Xuefan Z, Dou Z, Kechao Z, Steve D, Chris B 2020 iScience 23 101095 Google Scholar
[52]	Kapat K, Shubhra Q T, Zhou M, Leeuwenburgh S 2020 Adv. Funct. Mater. 30 1909045 Google Scholar
[53]	Dawson J A, Sinclair D C, Harding J H, Freeman C L 2014 Chem. Mater. 26 6104
[54]	Reaney I, Colla E, Setter N 1994 Jpn. J. Appl. Phys. 33 3984 Google Scholar
[55]	Wu J, Qin N, Lin E Z, Kang Z H, Bao D H 2021 Mater. Today Energy 21 100732 Google Scholar
[56]	Chen L, Jia Y M, Zhao J H, Ma J P, Wu Z, Yuan G L, Cui X Z 2021 J. Colloid Interface Sci. 586 758 Google Scholar
[57]	Li X, Lin H M, Chen X, Niu H, Zhang T, Liu J Y, Qu F Y 2015 New J. Chem. 39 7863 Google Scholar
[58]	Yao W, Shen C, Lu Y 2013 Compos. Sci. Technol. 87 8 Google Scholar
[59]	Hou T, Cao F, Li M L, Wang J L, Lv L L 2020 J. Environ. Sci. Eng. 8 84 Google Scholar
[60]	Kumar M, Singh G, Vaish R 2021 Mater. Adv 2 4093 Google Scholar
[61]	Bai S L, Sun L X, Sun J H, Han J Y, Zhang K W, Li Q Q, Luo R X, Li D Q, Chen A 2021 J. Colloid Interface Sci. 587 183 Google Scholar
[62]	Zhao Z C, Wei L Y, Li S, Zhu L F, Su Y P, Liu Y, Bu Y B, Lin Y H, Liu W S, Zhang Z T 2020 J. Mater. Chem. A 8 16238 Google Scholar
[63]	Prakash J, Prasad U, Alexander R, Bahadur J, Dasgupta K, Kannan A N M 2019 Langmuir 35 14492 Google Scholar
[64]	Miao Y, Tian W R, Han J, Li N J, Chen D Y, Xu Q F, Lu J M 2022 Nano Energy 100 107473 Google Scholar
[65]	Zhou X F, Shen B, Zhai J W, Hedin N 2021 Adv. Funct. Mater. 31 2009594 Google Scholar
[66]	Guan J F, Jia Y M, Chang T, Ruan L J, Xu T S, Zhang Z, Yuan G L, Wu Z, Zhu G Q 2022 Sep. Purif. Technol. 286 120450 Google Scholar
[67]	Ji M, Kim J H, Ryu C H, Lee Y I 2022 Nano Energy 95 106993 Google Scholar
[68]	Fu C, Wu T, Sun G W, Yin G F, Wang C, Ran G X, Song Q J 2023 Appl. Catal. B 323 122196 Google Scholar
[69]	Khanbabaee B, Mehner E, Richter C, Hanzig J, Zschornak M, Pietsch U, St¨ocker H, Leisegang T, Meyer D C, Gorfman S 2016 Appl. Phys. Lett. 109 222901 Google Scholar
[70]	Kang Z H, Lin E Z, Qin N, Wu J, Yuan B W, Bao D H 2021 Environ. Sci. :Nano 8 1376 Google Scholar
[71]	Zhang D F, Su C H, Li H, Pu X P, Geng Y L 2020 J. Phys. Chem. Solids 139 109326 Google Scholar
[72]	Zhao Q, Xiao H Y, Geng H F, Zheng Z P, Wang J S, Wang F F, Guo Y P 2021 Nano Energy 85 106028 Google Scholar
[73]	Sun X X, Li R C, Yang Z W, Zhang N, Wu C, Li J H, Chen Y L, Chen Q, Zhang J, Yan H J, Lv X, Wu J G 2022 Appl. Catal. B 313 121471 Google Scholar
[74]	Li J H, Wei X W, Sun X X, Li R C, Wu C, Liao J Y, Zhang T, Wu J G 2022 ACS Appl. Mater. Inter. 14 46765 Google Scholar
[75]	Liu Z, Wen X R, Wang Y, Jia Y M, Wang F F, Yuan G L, Wang Y J 2022 Adv. Mater. Technol. 7 2101484 Google Scholar
[76]	Ruan L J, Jia Y M, Guan J F, Xue B, Huang S H, Wang Z H, Fu Y H, Wu Z 2022 J. Clean. Prod. 345 131060 Google Scholar
[77]	Wang S Y, Gao Y Y, Miao S, Liu T F, Mu L C, Li R G, Li R G, Fan F T, Li C 2017 J. Am. Chem. Soc. 139 11771 Google Scholar
[78]	Chen S, Zhu P, Mao L J, Wu W C, Lin H, Xu D L, Lu X Y, Shi J L 2023 Adv. Mater. 2208256
[79]	Wang Y, Wen X R, Jia Y M, Huang M, Wang F F, Zhang X H, Bai Y Y, Yuan G L, Wang Y J 2020 Nat. Commun. 11 1328 Google Scholar

[1]	王盼, 宗易昕, 文宏玉, 夏建白, 魏钟鸣. 二维Janus原子晶体的电子性质. , 2021, 70(2): 026801. doi: 10.7498/aps.70.20201406
[2]	崔勇, 吴明, 宋晓, 黄玉平, 贾琦, 陶云飞, 王琛. 小型低频发射天线的研究进展. , 2020, 69(20): 208401. doi: 10.7498/aps.69.20200792
[3]	姚宽明, 姚靖仪, 海照, 李登峰, 解兆谦, 于欣格. 用于触觉感知的自供能可拉伸压电橡胶皮肤电子器件. , 2020, 69(17): 178701. doi: 10.7498/aps.69.20200664
[4]	魏晓薇, 陶红, 赵纯林, 吴家刚. 高性能铌酸钾钠基无铅陶瓷的压电和电卡性能. , 2020, 69(21): 217705. doi: 10.7498/aps.69.20200540
[5]	李飞, 张树君, 徐卓. 压电效应—百岁铁电的守护者. , 2020, 69(21): 217703. doi: 10.7498/aps.69.20200980
[6]	邓长发, 燕少安, 王冬, 彭金峰, 郑学军. 基于导电原子力显微镜的单根GaN纳米带光调控力电耦合性能. , 2019, 68(23): 237304. doi: 10.7498/aps.68.20191097
[7]	贺子厚, 赵静波, 姚宏, 蒋娟娜, 陈鑫. 基于压电材料的薄膜声学超材料隔声性能研究. , 2019, 68(13): 134302. doi: 10.7498/aps.68.20190245
[8]	李林利, 薛春霞. 压电材料双曲壳热弹耦合作用下的混沌运动. , 2019, 68(1): 010501. doi: 10.7498/aps.68.20181714
[9]	吴金根, 高翔宇, 陈建国, 王春明, 张树君, 董蜀湘. 高温压电材料、器件与应用. , 2018, 67(20): 207701. doi: 10.7498/aps.67.20181091
[10]	朱振业. 无铅四方相钙钛矿短周期超晶格压电效应机理研究. , 2018, 67(7): 077701. doi: 10.7498/aps.67.20172710
[11]	廖涛, 孙小伟, 宋婷, 田俊红, 康太凤, 孙伟彬. 新型二维压电声子晶体板带隙可调性研究. , 2018, 67(21): 214208. doi: 10.7498/aps.67.20180611
[12]	周勇, 李纯健, 潘昱融. 磁致伸缩/压电层叠复合材料磁电效应分析. , 2018, 67(7): 077702. doi: 10.7498/aps.67.20172307
[13]	洪元婷, 马江平, 武峥, 应静诗, 尤慧琳, 贾艳敏. AgNbO3压电纳米材料压-电-化学耦合研究. , 2018, 67(10): 107702. doi: 10.7498/aps.67.20180287
[14]	汤立国. 压电材料全矩阵材料常数超声谐振谱反演技术中的变温模式识别. , 2017, 66(2): 027703. doi: 10.7498/aps.66.027703
[15]	张添乐, 黄曦, 郑凯, 张欣梧, 王宇杰, 武丽明, 张晓青, 郑洁, 朱彪. 极化电压对聚丙烯压电驻极体膜压电性能的影响. , 2014, 63(15): 157703. doi: 10.7498/aps.63.157703
[16]	张欣梧, 张晓青. 聚丙烯压电驻极体膜的压电和声学性能研究. , 2013, 62(16): 167702. doi: 10.7498/aps.62.167702
[17]	陈蕾, 李平, 文玉梅, 王东. 高磁导率材料FeCuNbSiB对超磁致伸缩/压电层合材料磁电性能的影响. , 2011, 60(6): 067501. doi: 10.7498/aps.60.067501
[18]	卞雷祥, 文玉梅, 李平. 磁致伸缩/压电叠层复合材料磁-机-电耦合系数分析. , 2009, 58(6): 4205-4213. doi: 10.7498/aps.58.4205
[19]	范军峰, 张宁. Tb1－xDyxFe2－y-Fe掺杂BaTiO3多层膜中的磁电耦合. , 2007, 56(10): 6056-6060. doi: 10.7498/aps.56.6056
[20]	陈钢进, 夏钟福. 多孔聚四氟乙烯/氟代乙烯丙烯共聚物复合驻极体材料的压电效应研究. , 2004, 53(8): 2715-2719. doi: 10.7498/aps.53.2715

计量

文章访问数: 6290
PDF下载量: 203
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板