强磁场对金属离子掺杂CaTiO3结构和光学性能的影响

李强; 杨合; 薛向欣; 李清伟

doi:10.7498/aps.63.227803

摘要

研究了800 ℃条件下不同制备磁场强度(最高12 T)对CaTiO3 及其浸渍掺杂样品在结构和光学性能方面的影响. 研究表明: 样品吸光性能随浸渍掺杂的离子浓度的增大而提升, 且发生红移现象; 相同掺杂浓度下, 磁场下制备样品的吸光性能均较非磁场下制备的样品有所提高, 但不同磁场强度下所制备样品的吸光曲线彼此差异不大; 此外, 磁制备纯CaTiO3晶体粉末的X-射线衍射曲线峰左移, 紫外-可见漫反射光谱吸收截止波长增长, 这表明强磁场可使CaTiO3晶面间距和晶格常数增大、禁带宽度减小.

关键词:

CaTiO3 /
强磁场 /
掺杂

Abstract

In the paper, the changes of structures and optical properties of metal ions doped modified CaTiO3 prepared under different magnetic field intensities (up to 12 T) and 800 ℃ are studied. The results indicate that the photo absorption performances are enhanced with the ions doped concentration increasing and red shift occurs significantly. With the same doped concentration, the photo absorption performances of the samples prepared under magnetic field are improved compared with under no magnetic field, while there are little differences among the absorption curves of these samples prepared under different magnetic field intensities. Furthermore, it is observed that the X-ray diffraction curve peaks of pure CaTiO3 prepared under magnetic field are all left-shifted and cutoff wavelengths of UV-vis are augmented, which indicates that the interplanar spacing and lattice constant are increased while the band gap is narrowed.

Keywords:

CaTiO3 /
high magnetic field /
dopant

作者及机构信息

1.
东北大学材料与冶金学院, 冶金资源循环科学辽宁省重点实验室, 沈阳 110004;

2.
沈阳建筑大学理学院, 沈阳 110168

基金项目: 国家自然科学基金(批准号:51090384)和辽宁百千万人才工程(批准号:20139210C4)资助的课题.

Authors and contacts

1.
Liaoning Key Laboratory of Metallurgical Resources Recycling Science, School of Materials and Metallurgy, Northeastern University, Shenyang 110004, China;

2.
School of Science, Shenyang Jianzhu University, Shenyang 110168, China

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 51090384) and Liaoning Bai Qian Wan Latlennts Program, China (Grant No 20139210C4).

参考文献

[1]	Labhsetwar N, Doggali P, Rayalu S, Yadav R, Mistuhashi T, Haneda H 2012 Chin. J. Catal. 33 1611
[2]	Zhong W, Au C T, Du Y W 2013 Chin. Phys. B 22 057501
[3]	Shi J W, Guo L J 2012 Prog. Nat. Sci. Mater. Inter. 22 592
[4]	Xiang J, Guo Y T, Zhou G Z, Chu Y Q 2012 Acta Phys. Sin. 61 227201 (in Chinese) [向军, 郭银涛, 周广振, 褚艳秋 2012 61 227201]
[5]	Li Z L, An X Y, Cheng X L, Wang X M, Zhang H, Peng L P, Wu W D 2013 Chin. Phys. B 22 037104
[6]	Cai L G, Liu F M, Zhong W W 2010 Chin. Phys. B 19 097101
[7]	Zhang J, Tang S H, Liao L Y, Yu W F 2013 Chin. J. Catal. 34 1051
[8]	Fu X X, Sang L X, Wang J Z, Yang Q H, Sun Y H, Li Z Y, Zeng S L 2001 J. Tianjin Univ. 02 229 (in Chinese) [傅希贤, 桑丽霞, 王俊珍, 杨秋华, 孙艺环, 李增勇, 曾淑兰 2001 天津大学学报 02 229 ]
[9]	Cavalcante L S, Marques V S, Sczancoski J C, Escote MT, JoyaJ M R, Varela J A, Santos M R M C, Pizani P S, Longo E 2008 Chem. Engineer. J. 143 299
[10]	Lemański K, Deren P J 2014 J. Lumin. 145 661
[11]	Yang K, Wang C L, Li J C, Zhang C, Wu Q Z, Zhang Y F, Yin N, Liu X Y 2006 Chin. Phys. 15 1580
[12]	Shen J, Zhou J, Shi G Q, Yang W C, Liu H X, Chen W 2013 Acta Phys. Sin. 62 117702 (in Chinese) [沈杰, 周静, 石国强, 杨文才, 刘韩星, 陈文 2013 62 117702]
[13]	Zhang H J 2010 Ph. D. Dissertation (Harbin: Harbin Institute of Technology) (in Chinese) [张红杰 2010 博士学位论文 (哈尔滨: 哈尔滨工业大学)]
[14]	Fu Q, Li J L, He T, Yang G W 2013 J. Appl. Phys. 113 104303
[15]	Nishimoto S, Matsuda M, Miyake M 2006 Chem. Lett. 35 308
[16]	Ren S Y, Ren Z M, Ren W L, Cao G H 2009 Acta Phys. Sin. 58 5567 (in Chinese) [任树洋, 任忠鸣, 任维丽, 操光辉 2009 58 5567]
[17]	Du J, Luo Z Q, Li P P 2014 Chin. Phys. C 38 015102
[18]	Yang G, Wang L, Tian J L 2013 Chin. Phys. B 22 127350
[19]	Numoto N, Shimizu K I, Matsumoto K, Miki K, Kita A 2013 J. Cryst. Growth 367 53
[20]	Zheng A M, Huang S J, Wang Q, Zhang H L, Deng F, Liu S B 2013 Chin. J. Catal. 34 436
[21]	Gu H B, Guo J, Wei H G, Huang Y D, Zhao C Y, Li Y, Wu Q L, Haldolaarachchige N, Yong D P, Wei S Y 2013 Phys. Chem. Chem. Phys. 15 10866
[22]	Wang Z C, Karato S I 1995 Acta Geophys. Sin. 38 718 (in Chinese) [王子潮, 唐户俊一郎 1995 地球 38 718]
[23]	Gan H X, Liu T Y, Cheng Z J, Yang C X 2011 J. Synth. Cryst. 40 1022 (in Chinese) [甘海秀, 刘廷禹, 程志君, 杨晨星 2011 人工晶体学报 40 1022]
[24]	Wang G Y, Wang T J, Zhao X Q, Zhang H T 2005 Chin. J. Catal. 26 0138 (in Chinese) [王桂赟, 王廷吉, 赵新强, 张海涛 2005 催化学报 26 0138]

施引文献

[1]	Labhsetwar N, Doggali P, Rayalu S, Yadav R, Mistuhashi T, Haneda H 2012 Chin. J. Catal. 33 1611
[2]	Zhong W, Au C T, Du Y W 2013 Chin. Phys. B 22 057501
[3]	Shi J W, Guo L J 2012 Prog. Nat. Sci. Mater. Inter. 22 592
[4]	Xiang J, Guo Y T, Zhou G Z, Chu Y Q 2012 Acta Phys. Sin. 61 227201 (in Chinese) [向军, 郭银涛, 周广振, 褚艳秋 2012 61 227201]
[5]	Li Z L, An X Y, Cheng X L, Wang X M, Zhang H, Peng L P, Wu W D 2013 Chin. Phys. B 22 037104
[6]	Cai L G, Liu F M, Zhong W W 2010 Chin. Phys. B 19 097101
[7]	Zhang J, Tang S H, Liao L Y, Yu W F 2013 Chin. J. Catal. 34 1051
[8]	Fu X X, Sang L X, Wang J Z, Yang Q H, Sun Y H, Li Z Y, Zeng S L 2001 J. Tianjin Univ. 02 229 (in Chinese) [傅希贤, 桑丽霞, 王俊珍, 杨秋华, 孙艺环, 李增勇, 曾淑兰 2001 天津大学学报 02 229 ]
[9]	Cavalcante L S, Marques V S, Sczancoski J C, Escote MT, JoyaJ M R, Varela J A, Santos M R M C, Pizani P S, Longo E 2008 Chem. Engineer. J. 143 299
[10]	Lemański K, Deren P J 2014 J. Lumin. 145 661
[11]	Yang K, Wang C L, Li J C, Zhang C, Wu Q Z, Zhang Y F, Yin N, Liu X Y 2006 Chin. Phys. 15 1580
[12]	Shen J, Zhou J, Shi G Q, Yang W C, Liu H X, Chen W 2013 Acta Phys. Sin. 62 117702 (in Chinese) [沈杰, 周静, 石国强, 杨文才, 刘韩星, 陈文 2013 62 117702]
[13]	Zhang H J 2010 Ph. D. Dissertation (Harbin: Harbin Institute of Technology) (in Chinese) [张红杰 2010 博士学位论文 (哈尔滨: 哈尔滨工业大学)]
[14]	Fu Q, Li J L, He T, Yang G W 2013 J. Appl. Phys. 113 104303
[15]	Nishimoto S, Matsuda M, Miyake M 2006 Chem. Lett. 35 308
[16]	Ren S Y, Ren Z M, Ren W L, Cao G H 2009 Acta Phys. Sin. 58 5567 (in Chinese) [任树洋, 任忠鸣, 任维丽, 操光辉 2009 58 5567]
[17]	Du J, Luo Z Q, Li P P 2014 Chin. Phys. C 38 015102
[18]	Yang G, Wang L, Tian J L 2013 Chin. Phys. B 22 127350
[19]	Numoto N, Shimizu K I, Matsumoto K, Miki K, Kita A 2013 J. Cryst. Growth 367 53
[20]	Zheng A M, Huang S J, Wang Q, Zhang H L, Deng F, Liu S B 2013 Chin. J. Catal. 34 436
[21]	Gu H B, Guo J, Wei H G, Huang Y D, Zhao C Y, Li Y, Wu Q L, Haldolaarachchige N, Yong D P, Wei S Y 2013 Phys. Chem. Chem. Phys. 15 10866
[22]	Wang Z C, Karato S I 1995 Acta Geophys. Sin. 38 718 (in Chinese) [王子潮, 唐户俊一郎 1995 地球 38 718]
[23]	Gan H X, Liu T Y, Cheng Z J, Yang C X 2011 J. Synth. Cryst. 40 1022 (in Chinese) [甘海秀, 刘廷禹, 程志君, 杨晨星 2011 人工晶体学报 40 1022]
[24]	Wang G Y, Wang T J, Zhao X Q, Zhang H T 2005 Chin. J. Catal. 26 0138 (in Chinese) [王桂赟, 王廷吉, 赵新强, 张海涛 2005 催化学报 26 0138]

[1]	张冷, 张鹏展, 刘飞, 李方政, 罗毅, 侯纪伟, 吴孔平. 基于形变势理论的掺杂计算Sb₂Se₃空穴迁移率. , 2024, 73(4): 047101. doi: 10.7498/aps.73.20231406
[2]	颜俊, 王子毅, 曾若生, 邹炳锁. 零维Sb³⁺掺杂Rb₇Bi₃Cl₁₆金属卤化物的三重态自陷激子发射. , 2021, 70(24): 247801. doi: 10.7498/aps.70.20211024
[3]	张小娅, 宋佳讯, 王鑫豪, 王金斌, 钟向丽. In掺杂h-LuFeO₃光吸收及极化性能的第一性原理计算. , 2021, 70(3): 037101. doi: 10.7498/aps.70.20201287
[4]	翟顺成, 郭平, 郑继明, 赵普举, 索兵兵, 万云, . 第一性原理研究O和S掺杂的石墨相氮化碳(g-C3N4)6量子点电子结构和光吸收性质. , 2017, 66(18): 187102. doi: 10.7498/aps.66.187102
[5]	阮璐风, 王磊, 孙得彦. Sr掺杂对La1-xSrxMnO3/LaAlO3/SrTiO3界面电子结构的影响. , 2017, 66(18): 187301. doi: 10.7498/aps.66.187301
[6]	程超群, 李刚, 张文栋, 李朋伟, 胡杰, 桑胜波, 邓霄. B, P掺杂β-Si3N4的电子结构和光学性质研究. , 2015, 64(6): 067102. doi: 10.7498/aps.64.067102
[7]	廖建, 谢召起, 袁健美, 黄艳平, 毛宇亮. 3d过渡金属Co掺杂核壳结构硅纳米线的第一性原理研究. , 2014, 63(16): 163101. doi: 10.7498/aps.63.163101
[8]	杨双波. 温度与外磁场对Si均匀掺杂的GaAs量子阱电子态结构的影响. , 2014, 63(5): 057301. doi: 10.7498/aps.63.057301
[9]	曾思良, 倪飞飞, 何建锋, 邹士阳, 颜君. 强磁场中氢原子的能级结构. , 2011, 60(4): 043201. doi: 10.7498/aps.60.043201
[10]	郭熹, 王霞, 郑鹉, 唐为华. Eu掺杂TbMnO3多晶材料的介电性质. , 2010, 59(4): 2815-2819. doi: 10.7498/aps.59.2815
[11]	张云, 邵晓红, 王治强. 3C-SiC材料p型掺杂的第一性原理研究. , 2010, 59(8): 5652-5660. doi: 10.7498/aps.59.5652
[12]	赵安昆, 任忠鸣, 任树洋, 操光辉, 任维丽. 强磁场对真空蒸镀制取Te薄膜的影响. , 2009, 58(10): 7101-7107. doi: 10.7498/aps.58.7101
[13]	徐新发, 邵晓红. Y掺杂SrTiO3晶体材料的电子结构计算. , 2009, 58(3): 1908-1916. doi: 10.7498/aps.58.1908
[14]	任树洋, 任忠鸣, 任维丽, 操光辉. 3 T强磁场对真空蒸发Zn薄膜晶体结构的影响. , 2009, 58(8): 5567-5571. doi: 10.7498/aps.58.5567
[15]	庞雪君, 王强, 王春江, 王亚勤, 李亚彬, 赫冀成. 强磁场对铝合金中溶质组元分布状态的影响效果. , 2006, 55(10): 5129-5134. doi: 10.7498/aps.55.5129
[16]	王春江, 王强, 王亚勤, 黄剑, 赫冀成. 强磁场对Al-Si合金凝固组织中硅分布的影响. , 2006, 55(2): 648-654. doi: 10.7498/aps.55.648
[17]	张加宏, 马荣, 刘甦, 刘楣. 掺杂MgCNi3超导电性和磁性的第一性原理研究. , 2006, 55(9): 4816-4821. doi: 10.7498/aps.55.4816
[18]	林子扬, 项颖, 李涛. 掺杂对液晶磁场弗里德里克斯转变影响的探讨. , 2004, 53(4): 1166-1170. doi: 10.7498/aps.53.1166
[19]	巫翔, 秦善, 吴自玉, 董宇辉, 刘景, 李晓东. 钙钛矿CaTiO3的超高压结构研究. , 2004, 53(6): 1967-1971. doi: 10.7498/aps.53.1967
[20]	初宝进, 李国荣, 殷庆瑞, 张望重, 陈大任. 非化学计量和掺杂对(Na1/2Bi1/2)0.92Ba0.08TiO3陶瓷电性能的影响. , 2001, 50(10): 2012-2016. doi: 10.7498/aps.50.2012

计量

文章访问数: 6034
PDF下载量: 721
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板