Be1-xMgxO合金的能带特性与相结构稳定性研究

郑树文; 范广涵; 李述体; 张涛; 苏晨

doi:10.7498/aps.61.237101

摘要

采用基于密度泛函理论的平面波赝势方法, 对纤锌矿和岩盐矿结构Be1-xMgxO合金的晶格常数、能带特性和形成能进行计算, 分析了不同Mg组分下不同结构的Be1-xMgxO合金晶格常数和能带差异. 结果表明: 随着Mg组分的增大, 纤锌矿和岩盐矿Be1-xMgxO合金的晶格常数都线性增加, 但它们的能隙都逐渐减小. 对于相同Mg组分的Be1-xMgxO合金, 岩盐矿结构的能隙要大于纤锌矿结构. 当Mg组分为0.89时, Be1-xMgxO合金由纤锌矿相转变为岩盐矿相. 为了使理论值与实验值相一致, 对Be1-xMgxO合金的能隙计算值进行修正, 得到纤锌矿和岩盐矿Be1-xMgxO合金的能隙弯曲系数b值分别为3.451 eV和4.96 eV. 对纤锌矿BeO-MgO-ZnO三元合金的能隙和弯曲系数与晶格常数关系做了分析.

关键词:

Abstract

The lattice constants, energy band properties and phase stabilities of wurtzite (WZ) and rocksalt (RS) Be1-xMgxO alloys are investigated by the plan-wave pseudopotential method in the generalized gradient approximation based on the density functional theory. The theoretical results show that the lattice constants of WZ and RS Be1-xMgxO alloys increase and their bandgaps decrease as the content x of Mg increases from 0 to 1. For the same Mg content values, the bandgap of RS Be1-xMgxO alloy is greater than that of WZ Be1-xMgxO alloy. The WZ phase will transit to the RS phase when the Mg content is about 0.89. In order to obtain the theoretical values in accordance with the experimental results, the bandgaps of WZ and RS Be1-xMgxO alloys are corrected and the values of bandgap bowing parameter b are 3.451 eV and 4.96 eV for WZ Be1-xMgxO and RS Be1-xMgxO respectively. The reason of large band gap bowing parameter b is attributed to a large difference in ionic radius between Be and Mg. Besides, the relations among energy bandgap, bowing parameter and lattice constant of wurtzite BeO-ZnO-CdO ternary alloy are analyzed.

Keywords:

作者及机构信息

1.
华南师范大学光电子材料与技术研究所, 广州 510631

基金项目: 国家自然科学基金(批准号: 61176043)、广东省战略性新兴产业专项资金(批准号: 2010A081002005, 2011A081301003, 2012A080304016) 和广东省教育部产学研结合项目资金(批准号: 2010B090400192)资助的课题.

Authors and contacts

1.
Institute of Opto-electronic Materials and Technology, South China Normal University, Guangzhou 510631, China

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 61176043), the Special Funds for Provincial Strategic and Emerging Industries Projects of Guangdong, China (Grant Nos. 2010A081002005, 2011A081301003, 2012A080304016), Combination of the Ministry of Education Project in Guangdong Province, China (Grant No. 2010B090400192).

参考文献

[1]	Bagnall D M, Chen Y F, Zhu Z, Yao T, Koyama S, Shen M Y, Goto T 1997 Appl. Phys. Lett. 70 2230
[2]	Ryu Y R, Zhu S, Look D C, Wrobel J M, Jeong H M, White H W 2000 J. Cryst. Growth 216 330
[3]	Ryu Y R, Lee T S, White H W 2003 Appl. Phys. Lett. 83 87
[4]	Park W I, Yi G C, Jang H M 2001 Appl. Phys. Lett. 79 2022
[5]	Ohtomo A, Kawasaki M, Koida T, Masubuchi K, Koinuma H 1998 Appl. Phys. Lett. 72 2466
[6]	Ryu Y R, Lee T S, Lubguban J A, Corman A B, White H W, Leem J H, Han M S, Park Y S, Youn C J, Kim W J 2006 Appl. Phys. Lett. 88 052103
[7]	Kim W J, Leem T H, Han M S, Park I M, Ryu Y R, Lee T S 2006 J. Appl. Phys. 99 096104
[8]	Jin X L, Lou S Y, Kong D G, Li Y C, Du Z L 2006 Acta Phys. Sin. 55 4809 (in Chinese) [靳锡联, 娄世云, 孔德国, 李蕴才, 杜祖亮 2006 55 4809]
[9]	Chen X H, Kang J Y 2008 Semicond. Sci. Technol. 23 025008
[10]	Ding S F, Fan G H, Li S T, Chen K, Xiao B 2007 Physical B 394 127
[11]	Shi L B, Li R B, Cheng S, Li M B 2009 Acta Phys. Sin. 58 6446 (in Chinese) [史力斌, 李容兵, 成爽, 李明标 2009 58 6446]
[12]	Shi H L, Duan Y 2008 Eur. Phys. J. B 66 439
[13]	Kim W J, Leem T H, Han M S, Park I M, Ryu Y R, Lee T S 2006 J. Appl. Phys. 99 096104
[14]	Zhu Y Z, Chen G D, Ye H, Walsh A, Moon C Y, Wei S H 2008 Phys. Rev. B 77 245209
[15]	Hohenberg P, Kohn W 1964 Phys. Rev. B 136 864
[16]	Huang H C, Gilmer G H, de la Rubia T D 1998 J. Appl. Phys. 84 3636
[17]	Perdew J P, Chevary J A, Vosko S H, Jackson K A, Pederson M R, Singh D J, Fiolhais C 1992 Phys. Rev. B 46 6671
[18]	Vanderbilt D 1990 Phys. Rev. B 41 7892
[19]	Monkhorst H J, Pack J D 1977 Phys. Rev. B 16 1748
[20]	Fischer T H, Almlof J 1992 J. Phys. Chem. 96 9768
[21]	Amrani B, Rashid A, El Haj H F 2007 Computational Materials Science 40 66
[22]	Vegard L 1921 Z. Phys. 5 17
[23]	Fan X F, Sun H D, Shen Z X, Kuo J L, Lu Y M 2008 J. Phys: Condens. Matter 20 235221
[24]	Zhang Y, Shao X H, Wang C Q 2010 Acta Phys. Sin. 59 5652 (in Chinese) [张云, 邵晓红, 王治强 2010 59 5652]
[25]	Massidda S, Resta R, Posternak M, Baldereschi A 1995 Phys. Rev. B 52 16977
[26]	Anisimov V I, Aryasetiawan F, Lichtenstein A I 1997 J. Phys: Condens. Matter 9 767
[27]	Tang X, Lu H F, Zhao J J, Zhang Q Y 2010 J. Phys. Chem. Solids 71 336
[28]	Wang Z J, Li S C, Wang L Y, Liu Z 2009 Chin. Phys. B 18 2992
[29]	Xu X F, Shao X H 2009 Acta Phys. Sin. 58 1908 (in Chinese) [徐新发, 邵晓红 2009 58 1908]
[30]	de Paiva R, Alves J L A, Nogueira R A, de Oliveira C, Alves H W L, Scolfaro L M R, Leite J R 2002 Mater. Sci. Eng. B 93 2

施引文献

[1]	Bagnall D M, Chen Y F, Zhu Z, Yao T, Koyama S, Shen M Y, Goto T 1997 Appl. Phys. Lett. 70 2230
[2]	Ryu Y R, Zhu S, Look D C, Wrobel J M, Jeong H M, White H W 2000 J. Cryst. Growth 216 330
[3]	Ryu Y R, Lee T S, White H W 2003 Appl. Phys. Lett. 83 87
[4]	Park W I, Yi G C, Jang H M 2001 Appl. Phys. Lett. 79 2022
[5]	Ohtomo A, Kawasaki M, Koida T, Masubuchi K, Koinuma H 1998 Appl. Phys. Lett. 72 2466
[6]	Ryu Y R, Lee T S, Lubguban J A, Corman A B, White H W, Leem J H, Han M S, Park Y S, Youn C J, Kim W J 2006 Appl. Phys. Lett. 88 052103
[7]	Kim W J, Leem T H, Han M S, Park I M, Ryu Y R, Lee T S 2006 J. Appl. Phys. 99 096104
[8]	Jin X L, Lou S Y, Kong D G, Li Y C, Du Z L 2006 Acta Phys. Sin. 55 4809 (in Chinese) [靳锡联, 娄世云, 孔德国, 李蕴才, 杜祖亮 2006 55 4809]
[9]	Chen X H, Kang J Y 2008 Semicond. Sci. Technol. 23 025008
[10]	Ding S F, Fan G H, Li S T, Chen K, Xiao B 2007 Physical B 394 127
[11]	Shi L B, Li R B, Cheng S, Li M B 2009 Acta Phys. Sin. 58 6446 (in Chinese) [史力斌, 李容兵, 成爽, 李明标 2009 58 6446]
[12]	Shi H L, Duan Y 2008 Eur. Phys. J. B 66 439
[13]	Kim W J, Leem T H, Han M S, Park I M, Ryu Y R, Lee T S 2006 J. Appl. Phys. 99 096104
[14]	Zhu Y Z, Chen G D, Ye H, Walsh A, Moon C Y, Wei S H 2008 Phys. Rev. B 77 245209
[15]	Hohenberg P, Kohn W 1964 Phys. Rev. B 136 864
[16]	Huang H C, Gilmer G H, de la Rubia T D 1998 J. Appl. Phys. 84 3636
[17]	Perdew J P, Chevary J A, Vosko S H, Jackson K A, Pederson M R, Singh D J, Fiolhais C 1992 Phys. Rev. B 46 6671
[18]	Vanderbilt D 1990 Phys. Rev. B 41 7892
[19]	Monkhorst H J, Pack J D 1977 Phys. Rev. B 16 1748
[20]	Fischer T H, Almlof J 1992 J. Phys. Chem. 96 9768
[21]	Amrani B, Rashid A, El Haj H F 2007 Computational Materials Science 40 66
[22]	Vegard L 1921 Z. Phys. 5 17
[23]	Fan X F, Sun H D, Shen Z X, Kuo J L, Lu Y M 2008 J. Phys: Condens. Matter 20 235221
[24]	Zhang Y, Shao X H, Wang C Q 2010 Acta Phys. Sin. 59 5652 (in Chinese) [张云, 邵晓红, 王治强 2010 59 5652]
[25]	Massidda S, Resta R, Posternak M, Baldereschi A 1995 Phys. Rev. B 52 16977
[26]	Anisimov V I, Aryasetiawan F, Lichtenstein A I 1997 J. Phys: Condens. Matter 9 767
[27]	Tang X, Lu H F, Zhao J J, Zhang Q Y 2010 J. Phys. Chem. Solids 71 336
[28]	Wang Z J, Li S C, Wang L Y, Liu Z 2009 Chin. Phys. B 18 2992
[29]	Xu X F, Shao X H 2009 Acta Phys. Sin. 58 1908 (in Chinese) [徐新发, 邵晓红 2009 58 1908]
[30]	de Paiva R, Alves J L A, Nogueira R A, de Oliveira C, Alves H W L, Scolfaro L M R, Leite J R 2002 Mater. Sci. Eng. B 93 2

[1]	陈暾, 崔节超, 李敏, 陈文, 孙志鹏, 付宝勤, 侯氢. 合金元素Sn, Nb对锆合金腐蚀氧化膜相稳定性影响的第一性原理研究. , 2024, 73(15): 157101. doi: 10.7498/aps.73.20240602
[2]	周金萍, 李春梅, 姜博, 黄仁忠. Co和Ni过量影响Co₂NiGa合金晶体结构及相稳定性的第一性原理研究. , 2023, 72(15): 156301. doi: 10.7498/aps.72.20230626
[3]	王明军, 李春福, 文平, 张凤春, 王垚, 刘恩佐. Cr,Mo,Ni在-Fe(C)中的键合性质及对相结构稳定性的影响. , 2016, 65(3): 037101. doi: 10.7498/aps.65.037101
[4]	马振宁, 蒋敏, 王磊. Mg-Y-Zn合金三元金属间化合物的电子结构及其相稳定性的第一性原理研究. , 2015, 64(18): 187102. doi: 10.7498/aps.64.187102
[5]	代广珍, 蒋先伟, 徐太龙, 刘琦, 陈军宁, 代月花. 密度泛函理论研究氧空位对HfO2晶格结构和电学特性影响. , 2015, 64(3): 033101. doi: 10.7498/aps.64.033101
[6]	余本海, 陈东. 用密度泛函理论研究氮化硅新相的电子结构、光学性质和相变. , 2014, 63(4): 047101. doi: 10.7498/aps.63.047101
[7]	吕瑾, 杨丽君, 王艳芳, 马文瑾. Al2Sn（n=210）团簇结构特征和稳定性的密度泛函理论研究. , 2014, 63(16): 163601. doi: 10.7498/aps.63.163601
[8]	张蓓, 保安, 陈楚, 张军. ConCm(n=15; m=1,2)团簇的密度泛函理论研究. , 2012, 61(15): 153601. doi: 10.7498/aps.61.153601
[9]	郑树文, 范广涵, 何苗, 姚光锐, 陈峻, 贺龙飞. 纤锌矿BeO掺Cd的电子结构与能带特性研究. , 2012, 61(17): 177102. doi: 10.7498/aps.61.177102
[10]	郑树文, 范广涵, 章勇, 何苗, 李述体, 张涛. Be和Ca掺杂纤锌矿ZnO的晶格常数与能带特性研究. , 2012, 61(22): 227101. doi: 10.7498/aps.61.227101
[11]	陈跃云, 侯春菊, 孔祥山, 刘长松, 王先平, 方前锋. 氧离子导体La2Mo2-xMxO9(M=Cr,W)的理论研究. , 2011, 60(4): 046603. doi: 10.7498/aps.60.046603
[12]	张秀荣, 吴礼清, 康张李, 唐会帅. OsnN0,±(n=1—6)团簇几何结构与稳定性的理论研究. , 2011, 60(5): 053601. doi: 10.7498/aps.60.053601
[13]	孙路石, 张安超, 向军, 郭培红, 刘志超, 苏胜. 密度泛函理论研究Hg与Auqn(n=1—6, q=0,+1,-1) 团簇的相互作用. , 2011, 60(7): 073103. doi: 10.7498/aps.60.073103
[14]	徐文武, 宋晓艳, 李尔东, 魏君, 李凌梅. 纳米尺度下Sm-Co合金体系中相组成与相稳定性的研究. , 2009, 58(5): 3280-3286. doi: 10.7498/aps.58.3280
[15]	李喜波, 王红艳, 罗江山, 吴卫东, 唐永建. 密度泛函理论研究ScnO(n=1—9)团簇的结构、稳定性与电子性质. , 2009, 58(9): 6134-6140. doi: 10.7498/aps.58.6134
[16]	陈玉红, 康龙, 张材荣, 罗永春, 蒲忠胜. (Li3N)n(n=1—5)团簇结构与性质的密度泛函研究. , 2008, 57(7): 4174-4181. doi: 10.7498/aps.57.4174
[17]	陈玉红, 康龙, 张材荣, 罗永春, 元丽华, 李延龙. (Ca3N2)n(n=1—4)团簇结构与性质的密度泛函理论研究. , 2008, 57(10): 6265-6270. doi: 10.7498/aps.57.6265
[18]	李喜波, 罗江山, 郭云东, 吴卫东, 王红艳, 唐永建. 密度泛函理论研究Scn，Yn和Lan(n=2—10)团簇的稳定性、电子性质和磁性. , 2008, 57(8): 4857-4865. doi: 10.7498/aps.57.4857
[19]	陈玉红, 康龙, 张材荣, 罗永春, 马军. ［Mg(NH2)2］n(n=1—5)团簇的密度泛函理论研究. , 2008, 57(8): 4866-4874. doi: 10.7498/aps.57.4866
[20]	陈玉红, 张材荣, 马军. MgmBn(m=1,2;n=1—4)团簇结构与性质的密度泛函理论研究. , 2006, 55(1): 171-178. doi: 10.7498/aps.55.171

计量

文章访问数: 8266
PDF下载量: 653
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板