磁场退火对Co基熔体抽拉丝巨磁阻抗效应的影响

张树玲; 孙剑飞; 邢大伟

doi:10.7498/aps.59.2068

摘要

对Co基熔体抽拉非晶丝进行了普通炉内退火和不同磁场强度（500 Oe，1600 Oe，4000 Oe）下的横向和纵向磁场退火，利用HP4192阻抗分析仪和Lakeshore7407VSM分析了退火态样品的巨磁阻抗（GMI）效应和软磁性能.研究结果表明，纵向磁场降低了环向各向异性，纵向磁场退火样品GMI效应降低且GMI曲线为单峰，最大阻抗变化率ΔZ/Z为131%，磁场响应灵敏度为7%/Oe；而横向磁场提高了环向畴体积，增加了环向各向异性场，导致退火样品GMI曲线随频率升高由单峰转

关键词:

非晶丝 /
巨磁阻抗效应 /
退火

Abstract

In order to investigate the influence of anneal treatment on the Co-based melt extraction wires, the soft magnetic properties and giant magnet-impedance （GMI） effect of the annealed Co75Fe40Si8B12Nb1 wire are investigated. Samples are prepared using melt extraction technology in vacuum and annealed at 450℃ without magnetic field or with miagntic field either longitudinal or transverse to the axis of wire of strength from 500 Oe to 4000 Oe，respectively. The magnetic softness and GMI response are measured using HP4192 Impedance Analyzer and Lakeshore7407 VSM. Test results show that the circular anisotropy and GMI response are reduced after longitudinal field anneal treatment. GMI profiles are single-peaked and the maximum impedance ratio ΔZ/Z is 131% and field sensitivity is 7%/Oe. The circular permeability and GMI response are improved after transverse field anneal treatments because of the increased circular anisotropy. At higher frequencies，the GMI profiles change from single-peaked to two-peaked after being annealed in strong transverse field. The circular permeability is increased and GMI effect gets stronger with the increase of current frequency and anneal field. The largest impedance ratio of 190% with a field sensitivity of 26%/Oe is obtained for the Co-based transverse field annealed wires at 10 MHz. The correlations between the circular permeability，the GMI effect and the current frequency are discussed in the light of a skin effect model.

Keywords:

作者及机构信息

1.
哈尔滨工业大学材料科学与工程学院，哈尔滨 150001

Authors and contacts

1.
哈尔滨工业大学材料科学与工程学院，哈尔滨 150001

参考文献

[1]	［1］Mohri K，Kohzawa T 1992 IEEE Trans Magn. 28 3150
[2]	［2］Phan M H，Peng H X 2008 Prog Mate Sci. 53 323
[3]	［3］Wang W J，Xiao S Q，Jiang S，Yuan H M，Wu Z Y，Ji G，Yan S S，Liu Y H，Mei L M 2005 Thin Solid Films. 484 299
[4]	［4］Phan M H，Peng H X， Wisnom M R，Yu S C 2005 J. Appl. Phys. 98 014316
[5]	［5］Li Y F，Chen D X，Guo H Q，Vazquez M，Hernando A 2000 Acta Phys. Sin. 49 1591 （in Chinese）［李印峰、陈笃行、郭慧群、Vazquez M，Hernando A 2000 49 1591］
[6]	［6］Li Y F，Yin S Z，Vazquez M 2005 Acta Phys. Sin. 54 3391 （in Chinese）［李印峰、尹世忠、Vazquez M 2005 54 3391］
[7]	［7］Yelon A，Menard D，Britel M，Ciureanu P 1996 Appl. Phys. Lett. 69 3084
[8]	［8］Kamruzzaman M，Rahman I Z，Rahman M A 2001 J. Mater. Proc. Tech. 119 312
[9]	［9］Vazquez M 2001 J. Magn. Magn. Mater. 226-230 693
[10]	］Zhukov A，Zhukova V，Blanco J M，Gonzalez J 2005 J. Magn. Magn. Mater. 294 182
[11]	］Vinai F，Coisson M，Tiberto P 2006 J. Magn. Magn. Mater. 300 e82
[12]	］Wang W J，Yuan H M，Xiao S Q，Jiang S，Yan S S 2006 Acta Phys. Sin. 55 6108 （in Chinese）［王文静、袁慧敏、姜山、萧淑琴、颜世申 2006 55 6108］
[13]	］Vazquez M，Chen D X 1995 IEEE Trans Magn. 31 1229［14］Chen D X，Pascual L，Castano F J，Vazquez M，Hernando A 2001 IEEE Trans on Magn. 37 994
[14]	］Chizhik A，Gonzalez J，Zhukov A，Blanco J M 2007 Sens. Acta. A 126 235
[15]	］Li Y F，Yin S Z，Zhao S Y，Feng S Q，Vazquez M 2000 J. Hebei Normal University （Natural Science） 24 455 （in Chinese）［李印峰、尹世忠、赵双义、封素芹、Vazquez M 2000 河北师范大学学报（自然科学版） 24 455］
[16]	］Zhang J C，Liu L P，Zhao Z J，Yang X L，Wang Q 2007 J. East Normal University （Natural Science） 1 107 （in Chinese）［张军车、刘龙平、赵振杰、杨燮龙、王清江 2007 华东师范大学学报（自然科学版） 1 107］
[17]	］Chen D X，Munoz J，Hernando A，Vazquez M 1998 Phys. Rev. B 57 10699

施引文献

[1]	［1］Mohri K，Kohzawa T 1992 IEEE Trans Magn. 28 3150
[2]	［2］Phan M H，Peng H X 2008 Prog Mate Sci. 53 323
[3]	［3］Wang W J，Xiao S Q，Jiang S，Yuan H M，Wu Z Y，Ji G，Yan S S，Liu Y H，Mei L M 2005 Thin Solid Films. 484 299
[4]	［4］Phan M H，Peng H X， Wisnom M R，Yu S C 2005 J. Appl. Phys. 98 014316
[5]	［5］Li Y F，Chen D X，Guo H Q，Vazquez M，Hernando A 2000 Acta Phys. Sin. 49 1591 （in Chinese）［李印峰、陈笃行、郭慧群、Vazquez M，Hernando A 2000 49 1591］
[6]	［6］Li Y F，Yin S Z，Vazquez M 2005 Acta Phys. Sin. 54 3391 （in Chinese）［李印峰、尹世忠、Vazquez M 2005 54 3391］
[7]	［7］Yelon A，Menard D，Britel M，Ciureanu P 1996 Appl. Phys. Lett. 69 3084
[8]	［8］Kamruzzaman M，Rahman I Z，Rahman M A 2001 J. Mater. Proc. Tech. 119 312
[9]	［9］Vazquez M 2001 J. Magn. Magn. Mater. 226-230 693
[10]	］Zhukov A，Zhukova V，Blanco J M，Gonzalez J 2005 J. Magn. Magn. Mater. 294 182
[11]	］Vinai F，Coisson M，Tiberto P 2006 J. Magn. Magn. Mater. 300 e82
[12]	］Wang W J，Yuan H M，Xiao S Q，Jiang S，Yan S S 2006 Acta Phys. Sin. 55 6108 （in Chinese）［王文静、袁慧敏、姜山、萧淑琴、颜世申 2006 55 6108］
[13]	］Vazquez M，Chen D X 1995 IEEE Trans Magn. 31 1229［14］Chen D X，Pascual L，Castano F J，Vazquez M，Hernando A 2001 IEEE Trans on Magn. 37 994
[14]	］Chizhik A，Gonzalez J，Zhukov A，Blanco J M 2007 Sens. Acta. A 126 235
[15]	］Li Y F，Yin S Z，Zhao S Y，Feng S Q，Vazquez M 2000 J. Hebei Normal University （Natural Science） 24 455 （in Chinese）［李印峰、尹世忠、赵双义、封素芹、Vazquez M 2000 河北师范大学学报（自然科学版） 24 455］
[16]	］Zhang J C，Liu L P，Zhao Z J，Yang X L，Wang Q 2007 J. East Normal University （Natural Science） 1 107 （in Chinese）［张军车、刘龙平、赵振杰、杨燮龙、王清江 2007 华东师范大学学报（自然科学版） 1 107］
[17]	］Chen D X，Munoz J，Hernando A，Vazquez M 1998 Phys. Rev. B 57 10699

[1]	孟绍怡, 郝奇, 吕国建, 乔吉超. La基非晶合金β弛豫行为: 退火和加载应变的影响. , 2023, 72(7): 076101. doi: 10.7498/aps.72.20222389
[2]	张建强, 秦彦军, 方峥, 范晓珍, 马云, 李文忠, 杨慧雅, 邝富丽, 翟耀, 师应龙, 党文强, 叶慧群, 方允樟. 多场耦合Fe基合金巨磁阻抗效应调控机制. , 2022, 71(23): 237501. doi: 10.7498/aps.71.20221376
[3]	邵先亦, 徐爱娇, 王天乐. 外磁场与带轴夹角对非晶FeSiB/Cu/FeSiB三明治薄带巨磁阻抗特性的影响. , 2019, 68(6): 067501. doi: 10.7498/aps.68.20181806
[4]	姜柯, 陆妩, 胡天乐, 王信, 郭旗, 何承发, 刘默涵, 李小龙. 电子辐射环境中NPN输入双极运算放大器的辐射效应和退火特性. , 2015, 64(13): 136103. doi: 10.7498/aps.64.136103
[5]	陈剑辉, 杨静, 沈艳娇, 李锋, 陈静伟, 刘海旭, 许颖, 麦耀华. 后退火增强氢化非晶硅钝化效果的研究. , 2015, 64(19): 198801. doi: 10.7498/aps.64.198801
[6]	胡天乐, 陆妩, 席善斌, 郭旗, 何承发, 吴雪, 王信. PNP输入双极运算放大器在不同辐射环境下的辐射效应和退火特性. , 2013, 62(7): 076105. doi: 10.7498/aps.62.076105
[7]	方允樟, 许启明, 郑金菊, 吕葆华, 潘日敏, 叶慧群, 郑建龙, 范晓珍. FeCo基磁芯螺线管巨磁阻抗效应与磁芯长度关系的研究. , 2011, 60(12): 127501. doi: 10.7498/aps.60.127501
[8]	田雪雁, 赵谡玲, 徐征, 姚江峰, 张福俊, 贾全杰, 陈雨, 龚伟, 樊星. 高分子有机场效应晶体管中退火引起的自组织微观结构变化的研究. , 2011, 60(5): 057201. doi: 10.7498/aps.60.057201
[9]	李印峰, 封素芹, 王建勇. 交流电流对铁基纳米晶丝巨磁阻抗效应形貌的影响. , 2011, 60(3): 037306. doi: 10.7498/aps.60.037306
[10]	宋超, 陈谷然, 徐骏, 王涛, 孙红程, 刘宇, 李伟, 陈坤基. 不同退火温度下晶化硅薄膜的电学输运性质. , 2009, 58(11): 7878-7883. doi: 10.7498/aps.58.7878
[11]	蒋爱华, 肖剑荣, 王德安. 退火对含氮氟非晶碳膜结构及光学带隙的影响. , 2008, 57(9): 6013-6017. doi: 10.7498/aps.57.6013
[12]	潘海林, 程金科, 赵振杰, 何家康, 阮建中, 杨燮龙, 袁望治. LC共振型巨磁阻抗效应的研究. , 2008, 57(5): 3230-3236. doi: 10.7498/aps.57.3230
[13]	庞浩, 李根, 王赞基. 磁环中非晶丝的阻抗效应分析. , 2008, 57(11): 7194-7199. doi: 10.7498/aps.57.7194
[14]	辛宏梁, 袁望治, 程金科, 林宏, 阮建中, 赵振杰. NiFeCoP/BeCu复合结构丝的巨磁阻抗效应和磁化频率特性. , 2007, 56(7): 4152-4157. doi: 10.7498/aps.56.4152
[15]	王文静, 袁慧敏, 姜山, 萧淑琴, 颜世申. FeCuCrVSiB单层和多层膜的横向巨磁阻抗效应. , 2006, 55(11): 6108-6112. doi: 10.7498/aps.55.6108
[16]	刘龙平, 赵振杰, 黄灿星, 吴志明, 杨燮龙. 复合结构丝中的电流密度分布和巨磁阻抗效应. , 2006, 55(4): 2014-2020. doi: 10.7498/aps.55.2014
[17]	陈卫平, 萧淑琴, 王文静, 姜山, 刘宜华. FeCuCrVSiB多层膜巨磁阻抗效应的研究. , 2005, 54(6): 2929-2933. doi: 10.7498/aps.54.2929
[18]	杨全民, 王玲玲, 孙德成. 介观结构对纳米晶软磁合金巨磁阻抗效应影响的理论分析. , 2005, 54(12): 5730-5737. doi: 10.7498/aps.54.5730
[19]	钟智勇, 兰中文, 张怀武, 刘颖力, 王豪才. 铁磁/非铁磁/铁磁层状薄膜的巨磁阻抗效应的计算. , 2001, 50(8): 1610-1615. doi: 10.7498/aps.50.1610
[20]	李印峰, 陈笃行, 郭慧群, M. Vazquez, A. Hernando. 铁基非晶丝样低频涡流损耗分析. , 2000, 49(8): 1591-1594. doi: 10.7498/aps.49.1591

计量

文章访问数: 8661
PDF下载量: 1116
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板