退火温度和退火气氛对Ni/Au与p-GaN之间欧姆接触性能的影响

李晓静; 赵德刚; 何晓光; 吴亮亮; 李亮; 杨静; 乐伶聪; 陈平; 刘宗顺; 江德生

doi:10.7498/aps.62.206801

摘要

研究了不同退火温度和气氛对Ni/Au与p-GaN之间欧姆接触性能的影响. 采用圆形传输线模型方法得到不同退火温度和不同退火气氛下的比接触电阻率. 结果表明, 较适宜的退火温度为500 ℃左右, 退火温度太高或太低都会导致比接触电阻率的增大; 较适宜的退火气氛为适量含氧的氮气气氛, 且氧气含量对比接触电阻率大小的影响并不显著. 经过对退火条件的优化, 得到的比接触电阻率可达7.65×10-4 Ω·cm2.

关键词:

Abstract

In this paper, we investigate the effect of annealing conditions on the characteristic of Ni/Au Ohmic contact to p-GaN. The specific contact resistivities under different annealing temperature and different annealing atmosphere are tested using the circular transmission line model. It is found that the best annealing temperature is about 500 ℃. The annealing atmosphere of nitrogen-oxygen gas mixture can lead to lower specific contact resistivity than that of pure nitrogen, and the specific contact resistivity has no relationship with the content of oxygen. Finally, we obtain the lowest specific contact resistivity to be 7.65×10-4 Ω·cm2 at the best annealing temperature and atmosphere.

Keywords:

作者及机构信息

1.
中国科学院半导体所, 集成光电子学国家重点实验室, 北京 100083

基金项目: 国家杰出青年科学基金(批准号: 60925017)、国家自然科学基金(批准号: 10990100, 61176126) 和清华大学信息科学与技术国家实验室(筹)学科交叉基金资助的课题.

Authors and contacts

1.
State Key Laboratory on Integrated Optoelectronics, Institute of Semiconductors, Chinese Academy of Sciences, Beijing 100083, China

Funds: Project supported by the National Science Fund for Distinguished Young Scholars of China (Grant No. 60925017), the National Natural Science Foundation of China (Grant Nos. 10990100, 61176126), and the Cross-Discipline Foundation of Tsinghua National Laboratory for Information Science and Technology (TNList) Cross-Discipline Foundation, China.

参考文献

[1]	Mayes K, Yasan A, McClintock R, Shiell D, Darvish S R, Kung P, Razeghi M 2004 Appl. Phys. Lett. 84 1046
[2]	Li G, Cao Y, Xing H G, Jena D 2010 Appl. Phys. Lett. 97 222110
[3]	Butun B, Tut T, Ulker E, Yelboga T, Ozbay E 2008 Appl. Phys. Lett. 92 033507
[4]	Xue Z Q, Huang S R, Zhang B P, Chen C 2010 Acta Phys. Sin. 59 1268 (in Chinese) [薛正群, 黄生荣, 张保平, 陈朝 2010 59 1268]
[5]	Fan Z, Mohammad S N, Kim W, Aktas Ö, Botchkarev A E, Morkoc H 1996 Appl. Phys. Lett. 68 1672
[6]	Ho J K, Jong C S, Chiu C C, Huang C N, Chen C Y, Shih K K 1999 Appl. Phys. Lett. 74 1275
[7]	Zhang A P, Luo B, Johnson J W, Ren F, Han J, Pearton S J 2001 Appl. Phys. Lett. 79 3636
[8]	Chary I, Chandolu A, Borisov B, Kuryatkov V, Nikishin S, Holtz M 2009 J. Electron. Mater. 38 545
[9]	Wang L J, Zhang S M, Zhu J H, Zhu J J, Zhao D G, Liu Z S, Jiang D S, Wang Y T, Yang H 2010 Chin. Phys. B 19 017307
[10]	Chen L C, Chen F R, Kai J J, Chang L, Ho J K, Jong C S, Chiu C C, Huang C N, Chen C Y, Shih K K 1999 J. Appl. Phys. 86 3826
[11]	Ding Z B, Wang K, Chen T X, Chen D, Yao S D 2008 Acta Phys. Sin. 57 2445 (in Chinese) [丁志博, 王坤, 陈田祥, 陈迪, 姚淑德 2008 57 2445]
[12]	Qiao D, Yu L S, Lau S S, Lin J Y, Jiang H X, Haynes T E 2000 J. Appl. Phys. 88 4196
[13]	Smalc-Koziorowska J, Grzanka S, Litwin-Staszewska E, Piotrzkowski R, Nowak G, Leszczynski M, Perlin P, Talik E, Kozubowski J, Krukowski S 2010 Solid State Electron 54 701
[14]	Lin Y J 2005J. Vac. Sci. Technol. B 23 48
[15]	Gregory S, MARLOW, DAS M B 1982 Solid State Electron 25 91
[16]	Liday J, Hotový I, Sitter H, Vogrinčič P, Vincze A, Vávra I, Šatka A, Ecke G, Bonanni A, Breza J, Simbrunner C, Plochberger B 2007 J. Mater. Sci. Mater. Electron. 19 855
[17]	Greco G, Prystawko P, Leszczyński M, Nigro R L, Raineri V, Roccaforte F 2011 J. Appl. Phys. 110 123703

施引文献

[1]	Mayes K, Yasan A, McClintock R, Shiell D, Darvish S R, Kung P, Razeghi M 2004 Appl. Phys. Lett. 84 1046
[2]	Li G, Cao Y, Xing H G, Jena D 2010 Appl. Phys. Lett. 97 222110
[3]	Butun B, Tut T, Ulker E, Yelboga T, Ozbay E 2008 Appl. Phys. Lett. 92 033507
[4]	Xue Z Q, Huang S R, Zhang B P, Chen C 2010 Acta Phys. Sin. 59 1268 (in Chinese) [薛正群, 黄生荣, 张保平, 陈朝 2010 59 1268]
[5]	Fan Z, Mohammad S N, Kim W, Aktas Ö, Botchkarev A E, Morkoc H 1996 Appl. Phys. Lett. 68 1672
[6]	Ho J K, Jong C S, Chiu C C, Huang C N, Chen C Y, Shih K K 1999 Appl. Phys. Lett. 74 1275
[7]	Zhang A P, Luo B, Johnson J W, Ren F, Han J, Pearton S J 2001 Appl. Phys. Lett. 79 3636
[8]	Chary I, Chandolu A, Borisov B, Kuryatkov V, Nikishin S, Holtz M 2009 J. Electron. Mater. 38 545
[9]	Wang L J, Zhang S M, Zhu J H, Zhu J J, Zhao D G, Liu Z S, Jiang D S, Wang Y T, Yang H 2010 Chin. Phys. B 19 017307
[10]	Chen L C, Chen F R, Kai J J, Chang L, Ho J K, Jong C S, Chiu C C, Huang C N, Chen C Y, Shih K K 1999 J. Appl. Phys. 86 3826
[11]	Ding Z B, Wang K, Chen T X, Chen D, Yao S D 2008 Acta Phys. Sin. 57 2445 (in Chinese) [丁志博, 王坤, 陈田祥, 陈迪, 姚淑德 2008 57 2445]
[12]	Qiao D, Yu L S, Lau S S, Lin J Y, Jiang H X, Haynes T E 2000 J. Appl. Phys. 88 4196
[13]	Smalc-Koziorowska J, Grzanka S, Litwin-Staszewska E, Piotrzkowski R, Nowak G, Leszczynski M, Perlin P, Talik E, Kozubowski J, Krukowski S 2010 Solid State Electron 54 701
[14]	Lin Y J 2005J. Vac. Sci. Technol. B 23 48
[15]	Gregory S, MARLOW, DAS M B 1982 Solid State Electron 25 91
[16]	Liday J, Hotový I, Sitter H, Vogrinčič P, Vincze A, Vávra I, Šatka A, Ecke G, Bonanni A, Breza J, Simbrunner C, Plochberger B 2007 J. Mater. Sci. Mater. Electron. 19 855
[17]	Greco G, Prystawko P, Leszczyński M, Nigro R L, Raineri V, Roccaforte F 2011 J. Appl. Phys. 110 123703

[1]	汤家鑫, 李占海, 邓小清, 张振华. GaN/VSe₂范德瓦耳斯异质结电接触特性及调控效应. , 2023, 72(16): 167101. doi: 10.7498/aps.72.20230191
[2]	刘伟, 平云霞, 杨俊, 薛忠营, 魏星, 武爱民, 俞文杰, 张波. 微波退火和快速热退火下钛调制镍与锗锡反应. , 2021, 70(11): 116801. doi: 10.7498/aps.70.20202118
[3]	王苏杰, 李树强, 吴小明, 陈芳, 江风益. 热退火处理对AuGeNi/n-AlGaInP欧姆接触性能的影响. , 2020, 69(4): 048103. doi: 10.7498/aps.69.20191720
[4]	王尘, 许怡红, 李成, 林海军, 赵铭杰. 基于两步退火法提升Al/n⁺Ge欧姆接触及Ge n⁺/p结二极管性能. , 2019, 68(17): 178501. doi: 10.7498/aps.68.20190699
[5]	何天立, 魏鸿源, 李成明, 李庚伟. n型GaN过渡族难熔金属欧姆电极对比. , 2019, 68(20): 206101. doi: 10.7498/aps.68.20190717
[6]	唐文昕, 郝荣晖, 陈扶, 于国浩, 张宝顺. 1000 V p-GaN混合阳极AlGaN/GaN二极管. , 2018, 67(19): 198501. doi: 10.7498/aps.67.20181208
[7]	卢吴越, 张永平, 陈之战, 程越, 谈嘉慧, 石旺舟. 不同退火方式对Ni/SiC接触界面性质的影响. , 2015, 64(6): 067303. doi: 10.7498/aps.64.067303
[8]	魏政鸿, 云峰, 丁文, 黄亚平, 王宏, 李强, 张烨, 郭茂峰, 刘硕, 吴红斌. 低接触电阻率Ni/Ag/Ti/Au反射镜电极的研究. , 2015, 64(12): 127304. doi: 10.7498/aps.64.127304
[9]	朱彦旭, 曹伟伟, 徐晨, 邓叶, 邹德恕. GaN HEMT欧姆接触模式对电学特性的影响. , 2014, 63(11): 117302. doi: 10.7498/aps.63.117302
[10]	黄亚平, 云峰, 丁文, 王越, 王宏, 赵宇坤, 张烨, 郭茂峰, 侯洵, 刘硕. Ni/Ag/Ti/Au与p-GaN的欧姆接触性能及光反射率. , 2014, 63(12): 127302. doi: 10.7498/aps.63.127302
[11]	张孝富, 李豫东, 郭旗, 罗木昌, 何承发, 于新, 申志辉, 张兴尧, 邓伟, 吴正新. 60Coγ射线对高铝组分Al0.5Ga0.5N基p-i-n日盲型光探测器理想因子的影响. , 2013, 62(7): 076106. doi: 10.7498/aps.62.076106
[12]	王晓勇, 种明, 赵德刚, 苏艳梅. p-GaN/p-AlxGa1-xN异质结界面处二维空穴气的性质及其对欧姆接触的影响. , 2012, 61(21): 217302. doi: 10.7498/aps.61.217302
[13]	潘书万, 亓东峰, 陈松岩, 李成, 黄巍, 赖虹凯. Si(100)表面Se薄膜生长及其在Ti/Si欧姆接触中的应用. , 2011, 60(9): 098108. doi: 10.7498/aps.60.098108
[14]	周梅, 赵德刚. 一种测量p-GaN载流子浓度的方法. , 2011, 60(3): 037804. doi: 10.7498/aps.60.037804
[15]	封飞飞, 刘军林, 邱冲, 王光绪, 江风益. 硅衬底GaN基LED N极性n型欧姆接触研究. , 2010, 59(8): 5706-5709. doi: 10.7498/aps.59.5706
[16]	黄维, 陈之战, 陈博源, 张静玉, 严成锋, 肖兵, 施尔畏. 氢氟酸刻蚀对Ni/6H-SiC接触性质的作用. , 2009, 58(5): 3443-3447. doi: 10.7498/aps.58.3443
[17]	吕玲, 龚欣, 郝跃. 感应耦合等离子体刻蚀p-GaN的表面特性. , 2008, 57(2): 1128-1132. doi: 10.7498/aps.57.1128
[18]	丁志博, 王坤, 陈田祥, 陈迪, 姚淑德. 氧气氛中p-GaN/Ni/Au电极在相同温度不同合金时间下的欧姆接触形成机制和扩散行为. , 2008, 57(4): 2445-2449. doi: 10.7498/aps.57.2445
[19]	王永谦, 陈维德, 陈长勇, 刁宏伟, 张世斌, 徐艳月, 孔光临, 廖显伯. 快速热退火和氢等离子体处理对富硅氧化硅薄膜微结构与发光的影响. , 2002, 51(7): 1564-1570. doi: 10.7498/aps.51.1564
[20]	王印月, 甄聪棉, 龚恒翔, 阎志军, 王亚凡, 刘雪芹, 杨映虎, 何山虎. 传输线模型测量Au/Ti/p型金刚石薄膜的欧姆接触电阻率. , 2000, 49(7): 1348-1351. doi: 10.7498/aps.49.1348

计量

文章访问数: 8411
PDF下载量: 1294
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板