发光层厚度对联苯乙烯衍生物蓝色有机发光器件性能的影响

吴有智; 张文林; 倪蔚德; 张材荣; 张定军

doi:10.7498/aps.61.098101

摘要

本文制备了联苯乙烯衍生物(4, 4'-bis(2, 2'-diphenylvinyl)-1, 1'-biphenyl, DPVBi)为发光层的蓝色有机电致发光器件. 器件性能随发光层厚度变化而变. 在DPVBi厚度为1050 nm范围内, 同样电流密度下器件亮度及效率随DPVBi厚度增加先增后减, 40 nm时最佳, 最高亮度达到15840 cd/m2, 最高外量子效率达到3.2%, 器件色坐标(Commission Internationale de l'Eclairage (CIE) co-ordinates) 为(0.15, 0.15). DPVBi厚度超过40 nm时器件发光光谱出现红移而致色度变差, 其原因可归于微腔效应所致. 同时, 通过实验结果分析表明DPVBi中激子扩散长度位于2030 nm范围.

关键词:

Abstract

Thickness of emissive layer in organic electroluminescent device is one of the important factors affecting the device performance. In this report, a blue electroluminescent device with an active layer of 4, 4'-bis(2, 2'-diphenylvinyl) -1, 1'- biphenyl (DPVBi) is fabricated. The device performance varies with the thickness of DPVBi. With the increase of the DPVBi thickness between 1050 nm, the device luminance and efficiency at the same current density first increase and then decrease, the device with a DPVBi thickness of 40 nm exhibits the highest luminance of 15840 cd/m2 and a maximum external quantum efficiency of 3.2%, with Commission Internationale de l'Eclairage (CIE) co-ordinates being (0.15, 0.15). The luminescent spectral red shift and the color purity deteriorate when the thickness is over 40 nm, which can be attributed to a result of microcavity effect. In the meantime, the analysis from experimental results shows that the exciton diffusion length in DPVBi is between 2030 nm.

Keywords:

作者及机构信息

1.
甘肃省有色金属新材料省部共建国家重点实验室, 兰州理工大学材料科学与工程学院, 兰州 730050;

2.
兰州理工大学理学院应用物理系, 兰州 730050

基金项目: 甘肃省自然科学基金(批准号:　1010RJZA035), 教育部留学回国人员科研启动基金(批准号:　第40批)和国家自然科学基金(批准号:　11164015, 11164016)资助的课题.

Authors and contacts

1.
State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials, School of Materials Science & Engineering, Lanzhou University of Technology, Lanzhou 730050, China;

2.
Department of Applied Physics, School of Science, Lanzhou University of Technology, Lanzhou 730050, China

Funds: Project supported by the Natural Science Foundation of Gansu Province, China (Grant No. 1010RJZA035), the Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry (Grant No. 40), and the National Natural Science Foundation of China (Grant Nos. 11164015, 11164016).

参考文献

[1]	Zhou Y C, Zhou J, Zhao J M, Zhang S T, Zhan Y Q, Wang X Z, Wu Y, Ding X M, Hou X Y 2006 Appl. Phys. A 83 465
[2]	Jiao B, Wu Z X, Yan X W, Hou X 2010 Appl. Phys. A 98 239
[3]	Yap C C, Yahaya M, Salleh M M 2008 Curr. Appl. Phys. 8 637
[4]	Xie W F, Hou J Y, Liu S Y 2003 Semicond. Sci. Technol. 18 L42
[5]	Hosokawa C, Higashi H, Nakamura H, Kusumoto T 1995 Appl. Phys. Lett. 67 3853
[6]	Wu Y Z, Zheng X Y, Zhu W Q, Zhang B X, Jiang X Y, Zhang Z L, Xu S H 2002 Semiconductor Optoelectronics 23 253 (in Chinese) [吴有智, 郑新友, 朱文清, 张步新, 蒋雪茵, 张志林, 许少鸿 2002 半导体光电 23 253]
[7]	Cao J, Jiang X Y, Zhang Z L 2006 Appl. Phys. Lett. 89 252108
[8]	Matsushima T, Kinoshita Y, Murata H 2007 Appl. Phys. Lett. 91 253504
[9]	Zhang Y, Li Y, Duan L, Zhang D Q, Qiu Y 2007 Acta Phys. Chim. Sin. 23 455 (in Chinese) [张锐, 李杨, 段炼, 张德强, 邱勇 2007 物理化学学报 23 455]
[10]	Gebler D D, Wang Y Z, Blatchford J W, Jessen S W, Fu D K, Swager T M, MacDiarmid A G, Epstein A J 1997 Appl. Phys. Lett. 70 1644
[11]	So S K, Choi W K, Leung L M, Neyts K 1999 Appl. Phys. Lett. 74 1939
[12]	Jiang W L, Wang J, Ding G Y, Wang J, Wang L Z, Han Q, Liu S Y 2006 Chi. J. Lum. 27 561 (in Chinese) [姜文龙, 王静, 丁桂英, 汪津, 王立忠, 韩强, 刘式墉 2006 发光学报 27 561]
[13]	Tse S C, Kwok K C, So S K 2006 Appl. Phys. Lett. 89 262102
[14]	Lin C L, Lin H W, Wu C C 2006 Appl. Phys. Lett. 87 021101
[15]	Dodabalapur A, Rothberg L J, Jordan R H, Miller T M, Slusher R E, Phillips J M 1996 J. Appl. Phys. 80 6954
[16]	Chen S F, Deng L L, Xie J, Peng L, Xie L H, Fan Q L, Huang W 2010 Adv. Mater. 22 5227
[17]	Tang C W, Van Slyke S A, Chen C H 1989 J. Appl. Phys. 65 3610
[18]	Kalinowski J, Fattori V, Marco P D 2001 Chem. Phys. 266 85

施引文献

[1]	Zhou Y C, Zhou J, Zhao J M, Zhang S T, Zhan Y Q, Wang X Z, Wu Y, Ding X M, Hou X Y 2006 Appl. Phys. A 83 465
[2]	Jiao B, Wu Z X, Yan X W, Hou X 2010 Appl. Phys. A 98 239
[3]	Yap C C, Yahaya M, Salleh M M 2008 Curr. Appl. Phys. 8 637
[4]	Xie W F, Hou J Y, Liu S Y 2003 Semicond. Sci. Technol. 18 L42
[5]	Hosokawa C, Higashi H, Nakamura H, Kusumoto T 1995 Appl. Phys. Lett. 67 3853
[6]	Wu Y Z, Zheng X Y, Zhu W Q, Zhang B X, Jiang X Y, Zhang Z L, Xu S H 2002 Semiconductor Optoelectronics 23 253 (in Chinese) [吴有智, 郑新友, 朱文清, 张步新, 蒋雪茵, 张志林, 许少鸿 2002 半导体光电 23 253]
[7]	Cao J, Jiang X Y, Zhang Z L 2006 Appl. Phys. Lett. 89 252108
[8]	Matsushima T, Kinoshita Y, Murata H 2007 Appl. Phys. Lett. 91 253504
[9]	Zhang Y, Li Y, Duan L, Zhang D Q, Qiu Y 2007 Acta Phys. Chim. Sin. 23 455 (in Chinese) [张锐, 李杨, 段炼, 张德强, 邱勇 2007 物理化学学报 23 455]
[10]	Gebler D D, Wang Y Z, Blatchford J W, Jessen S W, Fu D K, Swager T M, MacDiarmid A G, Epstein A J 1997 Appl. Phys. Lett. 70 1644
[11]	So S K, Choi W K, Leung L M, Neyts K 1999 Appl. Phys. Lett. 74 1939
[12]	Jiang W L, Wang J, Ding G Y, Wang J, Wang L Z, Han Q, Liu S Y 2006 Chi. J. Lum. 27 561 (in Chinese) [姜文龙, 王静, 丁桂英, 汪津, 王立忠, 韩强, 刘式墉 2006 发光学报 27 561]
[13]	Tse S C, Kwok K C, So S K 2006 Appl. Phys. Lett. 89 262102
[14]	Lin C L, Lin H W, Wu C C 2006 Appl. Phys. Lett. 87 021101
[15]	Dodabalapur A, Rothberg L J, Jordan R H, Miller T M, Slusher R E, Phillips J M 1996 J. Appl. Phys. 80 6954
[16]	Chen S F, Deng L L, Xie J, Peng L, Xie L H, Fan Q L, Huang W 2010 Adv. Mater. 22 5227
[17]	Tang C W, Van Slyke S A, Chen C H 1989 J. Appl. Phys. 65 3610
[18]	Kalinowski J, Fattori V, Marco P D 2001 Chem. Phys. 266 85

[1]	王银霞, 白小川, 张勇, 李国庆. Al纳米颗粒高频局域等离激元效应对BCzVBi深蓝光有机发光器件发光效率的影响. , 2024, 73(3): 037802. doi: 10.7498/aps.73.20230858
[2]	肖心明, 朱龙山, 关宇, 华杰, 王洪梅, 董贺, 汪津. 低效率滚降、发光颜色稳定的磷光白色有机电致发光器件. , 2020, 69(4): 047202. doi: 10.7498/aps.69.20191594
[3]	王党会, 许天旱, 王荣, 雒设计, 姚婷珍. InGaN/GaN多量子阱结构发光二极管发光机理转变的低频电流噪声表征. , 2015, 64(5): 050701. doi: 10.7498/aps.64.050701
[4]	王雪松, 冀子武, 王绘凝, 徐明升, 徐现刚, 吕元杰, 冯志红. 关于InGaN/GaN多量子阱结构内量子效率的研究. , 2014, 63(12): 127801. doi: 10.7498/aps.63.127801
[5]	陈海涛, 徐征, 赵谡玲, 赵玲, 刘志民, 高松, 杨一帆, 刘志方, 申崇渝, 徐叙瑢. PCDTBT作为发光层的有机电致发光器件研究. , 2014, 63(16): 167802. doi: 10.7498/aps.63.167802
[6]	曹东兴, 郭志友, 梁伏波, 杨小东, 黄鸿勇. GaN基高压直流发光二极管制备及其性能分析. , 2012, 61(13): 138502. doi: 10.7498/aps.61.138502
[7]	高利岩, 赵谡玲, 徐征, 张福俊, 孙钦军, 张天慧, 闫光, 徐叙瑢. 水溶性CuPc旋涂转速及退火方式对蓝色有机电致发光器件性能的影响. , 2011, 60(3): 037203. doi: 10.7498/aps.60.037203
[8]	汪津, 赵毅, 谢文法, 段羽, 陈平, 刘式墉. 利用DPVBi插层提高蓝色荧光有机电致发光器件的效率. , 2011, 60(10): 107203. doi: 10.7498/aps.60.107203.2
[9]	汪津, 姜文龙, 华杰, 王广德, 韩强, 常喜, 张刚. 磁场对基于Co铁磁薄膜的有机发光器件效率和电流的影响. , 2010, 59(11): 8212-8217. doi: 10.7498/aps.59.8212
[10]	王兴军, 董斌, 周治平. Er硅酸盐化合物薄膜的相转变和光致发光特性研究. , 2010, 59(5): 3554-3557. doi: 10.7498/aps.59.3554
[11]	汪津, 华杰, 丁桂英, 常喜, 张刚, 姜文龙. 磁场作用下的有机电致发光. , 2009, 58(10): 7272-7277. doi: 10.7498/aps.58.7272
[12]	胡玥, 饶海波, 李君飞. ITO/有机半导体/金属结构OLED器件的数值模拟. , 2008, 57(9): 5928-5932. doi: 10.7498/aps.57.5928
[13]	张丽娟, 华玉林, 吴晓明, 张国辉, 王宇, 印寿根. 同时掺杂磷光和荧光染料的白色有机电致发光器件性能研究. , 2008, 57(3): 1913-1917. doi: 10.7498/aps.57.1913
[14]	吴晓明, 华玉林, 印寿根, 张国辉, 惠娟利, 张丽娟, 王宇. 不同主体双发光层白色有机电致发光器件的性能研究. , 2008, 57(2): 1150-1154. doi: 10.7498/aps.57.1150
[15]	王振, 何正红, 谭兴文, 陶敏龙, 李国庆, 熊祖洪. 磁场对有机电致发光的影响. , 2007, 56(5): 2979-2985. doi: 10.7498/aps.56.2979
[16]	张秀龙, 杨盛谊, 娄志东, 侯延冰. 有机电致发光器件的动态电学特性. , 2007, 56(3): 1632-1636. doi: 10.7498/aps.56.1632
[17]	委福祥, 曹进, 张晓波, 刘向, 蒋雪茵, 张志林, 朱文清, 许少鸿. 新型苯乙烯衍生物掺杂的蓝色及白色有机电致发光器件. , 2006, 55(4): 2008-2013. doi: 10.7498/aps.55.2008
[18]	刘明, 衣立新, 滕枫, 徐征, 徐叙. SiO2/C9-PPV异质结中类阴极射线发光及有机电致发光的交互增强. , 2003, 52(4): 1013-1018. doi: 10.7498/aps.52.1013
[19]	杨盛谊, 徐征, 刘姗姗, 董金凤, 章婷, 徐叙瑢, 张莉, 杨展澜, 吴谨光. 窄谱带绿色有机电致发光器件. , 2001, 50(5): 973-976. doi: 10.7498/aps.50.973
[20]	杨盛谊, 王振家, 陈晓红, 侯延冰, 董金凤, 徐叙. 高场下界面势垒对双层有机器件复合发光的影响. , 2000, 49(8): 1627-1631. doi: 10.7498/aps.49.1627

计量

文章访问数: 7787
PDF下载量: 758
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板