不依赖激发光偏振方向的芯帽异构二聚体

洪昕; 王晓强; 李冬雪; 商云晶

doi:10.7498/aps.71.20211381

摘要

各向异性贵金属纳米结构所特有的表面增强电场和近红外性能在纳米光电和生医传感等领域具有重要的应用, 但是其最佳光学性能的激发受限于结构姿态与光电场偏振方向的匹配. 本文基于芯帽颗粒特有的两个表面等离子体共振模式, 提出引入补偿结构, 利用二聚体结构间的局部表面等离子体共振耦合作用补偿电场偏转时缺失的近红外性能, 实现解除对激发光偏振方向的依赖关系. 基于有限元法数值求解了光与三维复杂异构二聚体作用后的电磁场分布, 分析了芯帽-芯壳异构二聚体间的作用模式, 从理论上明确了补偿结构去除偏振依赖的机理. 补偿后, 芯帽异构二聚体可在任意姿态下产生稳定的近红外高吸收性能, 在传感、成像、药物释放与光热疗法中具有广泛的应用潜力.

关键词:

Abstract

The plasmonic anisotropic nanostructure possesses the enhanced surface electric field and unique optical properties in near-infrared spectrum, thus it has potential applications in nano-optoelectronics and medical sensing. To obtain the best property, the excitation polarization normally needs to match the orientation of the structure. The strong polarization dependence, however, greatly limits the excitation efficiency. In this work, a patchy structure is introduced to release the dependence of polarization. In the proposed method here in this work, the lost properties due to unmatched polarizations are compensated for by the plasmonic resonance coupling between the patch and capped structure in the heterozygous dimer. By overlapping the two modes at the same wavelength, the absorption keeps rather stable undisturbed status during the variation of incident polarization. This work focuses on the theoretical exploration of the feasibility. Electromagnetic field in the interaction between light and heterozygous dimer is essential before extinction coefficient is calculated. The field of the model is obtained by solving Maxwell equations through using the finite element method. The numerical calculation presents a good understanding of the mechanism of the plasmonic interactions in the dimer, based on which the nanostructure with optimized configuration parameters can achieve the stable and high absorption in the near infrared wavelength.

Keywords:

作者及机构信息

大连理工大学, 电子信息与电气工程学部, 生物医学工程学院, 大连　116024

通信作者: 洪昕, hongxin@dlut.edu.cn

基金项目: 国家自然科学基金(批准号: 31271064, 11874100)资助的课题

Authors and contacts

School of Biomedical Engineering, Faculty of Electronic Information and Electrical Engineering, Dalian University of Technology, Dalian 116024, China

Corresponding author: Hong Xin, hongxin@dlut.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 31271064, 11874100)

文章全文 : translate this paragraph

参考文献

[1]	Petryayeva E, Krull U J 2011 Anal. Chim. Acta 706 8 Google Scholar
[2]	Zhang X, Chen Y L, Liu R S, Tsai D P 2013 Rep. Prog. Phys. 76 046401 Google Scholar
[3]	Mayer K M, Hafner J H L 2011 Chem. Rev. 111 3828 Google Scholar
[4]	Lim D K, Jeon K S, Kim H M, Nam J M, Suh Y D 2010 Nat. Mater. 9 60 Google Scholar
[5]	LiuY, Huang W, Chen W, Wang X, Guo J, Tian H, Zhang H, Wang Y, Yu B, Ren T L 2019 Appl. Surf. Sci. 481 1127 Google Scholar
[6]	MaX, Sun H, Wang Y, Wu X, Zhang J 2018 Nano Energy 53 932 Google Scholar
[7]	Sarah U, Ian B, He J, Laura S 2015 Sensors 15 15684 Google Scholar
[8]	Loiseau A, Asila V, Boitel-Aullen G, Lam M, Salmain M, Boujday S 2019 Biosensors 9 78 Google Scholar
[9]	Mejía-Salazar J R, Oliveira O N 2018 Chem. Rev. 118 10617 Google Scholar
[10]	Cobley C, Chen J, Cho E, Wang L, Xia Y 2010 Chem. Soc. Rev. 40 44 Google Scholar
[11]	He M Q, Yu Y L, Wang J H 2020 Nano Today 35 101005 Google Scholar
[12]	Ren Q Q, Bai L Y, Zhang X S, Ma Z Y, Bo L, Zhao Y D, Cao Y C 2015 J. Nanomater. 2015 1 Google Scholar
[13]	Dickerson E B, Dreaden E C, Huang X, El-Sayed I H, Chu H, Pushpanketh S 2008 Cancer Lett. 269 57 Google Scholar
[14]	AustinL A, Mackey M A, Dreaden E C, El-Sayed M A 2014 Arch. Toxicol. 88 1391 Google Scholar
[15]	Lin H C, Hsu K F, Lai C L, Wu T C, Lai C H 2020 Molecules 25 1853 Google Scholar
[16]	Sun M, Lee, Joon H, Kim, You J, Ha, Nyun Y, Park, Kon S, Beom Y 2013 ACS Nano 7 50 Google Scholar
[17]	Qin Z, Bischof J C 2012 Chem.Soc.Rev 41 1191 Google Scholar
[18]	Mie G 1908 Ann. Phys. 330 337 Google Scholar
[19]	Kelly K L, E C oronado, Lin L Z, Schatz G C 2003 J. Phys. Chem. B 107 668 Google Scholar
[20]	Kabashin A V, Evans P, Pastkovsky S, HenDren W, Wurtz G A, Atkinson R, Pollard R, Podolskiy V A, Zayats A V 2009 Nat. Mater. 8 867 Google Scholar
[21]	Kenneth, Grattan, Tong, Sun, Jie, Cao 2014 Sensors and Actuators, B. Chemical 195 332 Google Scholar
[22]	Nehl C L, Liao H, Hafner J H 2006 Nano Lett. 6 683 Google Scholar
[23]	Kumar R, Badilescu S, Packirisamy M 2019 J. Nanosci. Nanotechnol. 19 4617 Google Scholar
[24]	Lee D, Yoon S 2015 J. Phys. Chem. C 119 7873 Google Scholar
[25]	Boerigter C, Campana R, Morabito M 2015 Nat. Commun. 7 10545 Google Scholar
[26]	Funston A M, Novo C, Davis T J, Mulvanet P 2009 Nano Lett. 9 1651 Google Scholar
[27]	Zhu X P, Chen Y Q, Shi H M, Zhang S, Liu Q H, Duan H G 2017 J. Appl. Phys. 121 213105 Google Scholar
[28]	Cui Y, Zhou J, Tamma V A, Park W 2012 ACS Nano 6 2385 Google Scholar
[29]	Lovera A, Gallinet B, Nordlander P, Martin O J F 2013 ACS Nano 7 4527 Google Scholar
[30]	Lassiter J B, Sobhani H, Fan J A, Kundu J, Capasso F, Nordlander P, Halas N J 2010 Nano Lett. 10 3184 Google Scholar
[31]	Liu N, Weiss T, Mesch M, Langguth L, Eigenthaler U, Hirscher M, Nnichsen C, Giessen H 2010 Nano Lett. 10 1103 Google Scholar
[32]	Dijk M A V, Tchebotareva A L, Orrit M, Lippitz M, Lounis B 2006 Phys. Chem. Chem. Phys. 8 3486 Google Scholar
[33]	Gans R, Über D 1912 Ann. Phys. 342 881 Google Scholar
[34]	Ye J, Dorpe P V, Roy W V, Lodewijks K, Vlaminck I D, Maes G, Borghs G 2009 J. Phys. Chem. C 113 3110 Google Scholar
[35]	Nordlander P, Oubre C 2004 Nano Lett. 4 899 Google Scholar
[36]	Kerker M 1985 J. Colloid Interface Sci. 105 297 Google Scholar
[37]	Knight M W, Halas N J 2008 New J. Phys. 10 119 Google Scholar
[38]	Chen Q, Qi H, Ren Y T, Sun J P, Ruan L M 2017 AIP Adv. 7 065115 Google Scholar
[39]	Lassiter J B, Knight M W, Mirin N A, Halas N J 2009 Nano Lett. 9 4326 Google Scholar
[40]	洪昕, 王晨晨 2018 光学学报 38 0524001 Google Scholar Hong X, Wang C C 2018 Acta Opti. Sin. 38 0524001 Google Scholar
[41]	Ye J, Kong Y, Liu C 2016 J. Phys. D:Appl. Phys. 49 205106 Google Scholar
[42]	Cortie M, Ford M 2007 Nanotechnology 18 235704 Google Scholar
[43]	洪昕 2020 中国专利 ZL202010038295.7 Hong X 2020 Chinese Patent CN111204705A (in Chinese)

施引文献

图 1 纳米颗粒物与光作用的电磁场有限元仿真计算模型结构示意图

Fig. 1. Schematic diagram of numerical calculation of electromagnetic field based on finite element method for the interaction between nanoparticles and light.

下载: 全尺寸图片幻灯片

图 2 芯壳结构纳米单颗粒的LSPR 振动模式　(a) 线偏振光激发下的芯壳结构单颗粒的吸收谱线; (b) 715 nm峰值吸收谱线上的电场分布, 插图中的电荷极化分布图表明该振动为电偶极子模式; (c) 在吸收谱线600 nm处的电场分布, 插图中的电荷极化分布图表明该振动为四极子模式

Fig. 2. Plasmonic resonance mode of an individual core-shell nano-structure:(a) The absorption spectrum excited by a linear polarization; (b) the electric field distribution at 715 nm is a dipolar mode indicated by the charge distribution shown in the inset; (c) the electric field distribution at 600 nm is a quadripolar mode indicated by the charge distribution shown in the inset.

下载: 全尺寸图片幻灯片

图 3 芯帽结构纳米单颗粒的LSPR 振动模式　(a) 线偏振光激发下芯帽结构单颗粒的吸收谱线随偏振方向的变化曲线; (b)对应谱线615 nm处的电场分布, 插图中的电荷极化分布图表明该振动模式为电偶极子; (c) 对应谱线840 nm处的电场分布集中在帽沿上, 插图中电荷极化分布图表明该模式受激于平行于帽沿平面的电场; (d) 对应谱线670 nm处的电场分布和电荷极化分布, 表明该模式为四极子模式

Fig. 3. Plasmonic resonance mode of an individual capped nano-structure: (a) The absorption spectrum variation with polarization rotating from 0° to 90°; (b) the electric field distribution at 615 nm is a dipolar mode indicated by the charge distribution shown in the inset; (c) at 840 nm, the resonance is known as a magnetic mode with electric field accumulated at the brim, while the charge distribution in the inset indicates the polarization direction along the brim; (d) the electric field distribution at 670 nm is a quadripolar mode indicated by the charge distribution shown in the inset.

下载: 全尺寸图片幻灯片

图 4 芯帽-芯壳异构二聚体的LSPR耦合作用　(a)在线偏振光激发下二聚体颗粒的吸收谱线随偏振方向旋转的变化关系; (b) 对应谱线峰值845 nm处0°电场激发下的异构体的电场分布及电荷极化分布; (c) 异构体间隙A点处电场随激发光偏振方向旋转的变化谱线; (d) 对应谱线峰值850 nm处90°电场激发下异构体的电场分布及电荷极化分布; (e) 帽沿B点处电场随偏振方向的变化谱线; (f) 对应谱线730 nm处异构体间LSPR耦合作用的电场及电荷极化分布图

Fig. 4. Plasmonic interaction between the patch/capped structures in the heterozygous dimer: (a) Excited by linear polarization, the absorption spectrum variation with polarization rotation; (b) at 845 nm, the “hot spot” at the gap in the electric field distribution shows the strong plasmonic coupling between the two modes, as shown in the inset; (c) the electric field at the point A of gap varies with the polarization direction; (d) at 850 nm, the strong electric field is contributed by the capped structure and the distribution at the brim clearly indicates the magnetic mode when the polarization is 90°; (e) the spectrum variation at point B on the brim with polarization rotation from 0° to 90°; (f) at 730 nm, the electric field distribution clear shows the shell dominates the contribution.

下载: 全尺寸图片幻灯片

图 5 芯帽异构二聚体的近红外吸收性能　(a) 芯帽异构二聚体与芯帽单颗粒的近红外吸收性能对偏振态依赖关系的对比; (b) 芯帽异构二聚体在空间随机角度入射下产生稳定的高吸收

Fig. 5. Absorption properties of the heterozygous dimer at near infrared: (a) The dimer exhibits a rather “flat” line compared to the individual capped structure during the polarization rotation; (b) with random incident angle, the dimer still keeps a stable high absorption at the near infrared wavelength when the polarization rotates.

下载: 全尺寸图片幻灯片

map

[1]	Petryayeva E, Krull U J 2011 Anal. Chim. Acta 706 8 Google Scholar
[2]	Zhang X, Chen Y L, Liu R S, Tsai D P 2013 Rep. Prog. Phys. 76 046401 Google Scholar
[3]	Mayer K M, Hafner J H L 2011 Chem. Rev. 111 3828 Google Scholar
[4]	Lim D K, Jeon K S, Kim H M, Nam J M, Suh Y D 2010 Nat. Mater. 9 60 Google Scholar
[5]	LiuY, Huang W, Chen W, Wang X, Guo J, Tian H, Zhang H, Wang Y, Yu B, Ren T L 2019 Appl. Surf. Sci. 481 1127 Google Scholar
[6]	MaX, Sun H, Wang Y, Wu X, Zhang J 2018 Nano Energy 53 932 Google Scholar
[7]	Sarah U, Ian B, He J, Laura S 2015 Sensors 15 15684 Google Scholar
[8]	Loiseau A, Asila V, Boitel-Aullen G, Lam M, Salmain M, Boujday S 2019 Biosensors 9 78 Google Scholar
[9]	Mejía-Salazar J R, Oliveira O N 2018 Chem. Rev. 118 10617 Google Scholar
[10]	Cobley C, Chen J, Cho E, Wang L, Xia Y 2010 Chem. Soc. Rev. 40 44 Google Scholar
[11]	He M Q, Yu Y L, Wang J H 2020 Nano Today 35 101005 Google Scholar
[12]	Ren Q Q, Bai L Y, Zhang X S, Ma Z Y, Bo L, Zhao Y D, Cao Y C 2015 J. Nanomater. 2015 1 Google Scholar
[13]	Dickerson E B, Dreaden E C, Huang X, El-Sayed I H, Chu H, Pushpanketh S 2008 Cancer Lett. 269 57 Google Scholar
[14]	AustinL A, Mackey M A, Dreaden E C, El-Sayed M A 2014 Arch. Toxicol. 88 1391 Google Scholar
[15]	Lin H C, Hsu K F, Lai C L, Wu T C, Lai C H 2020 Molecules 25 1853 Google Scholar
[16]	Sun M, Lee, Joon H, Kim, You J, Ha, Nyun Y, Park, Kon S, Beom Y 2013 ACS Nano 7 50 Google Scholar
[17]	Qin Z, Bischof J C 2012 Chem.Soc.Rev 41 1191 Google Scholar
[18]	Mie G 1908 Ann. Phys. 330 337 Google Scholar
[19]	Kelly K L, E C oronado, Lin L Z, Schatz G C 2003 J. Phys. Chem. B 107 668 Google Scholar
[20]	Kabashin A V, Evans P, Pastkovsky S, HenDren W, Wurtz G A, Atkinson R, Pollard R, Podolskiy V A, Zayats A V 2009 Nat. Mater. 8 867 Google Scholar
[21]	Kenneth, Grattan, Tong, Sun, Jie, Cao 2014 Sensors and Actuators, B. Chemical 195 332 Google Scholar
[22]	Nehl C L, Liao H, Hafner J H 2006 Nano Lett. 6 683 Google Scholar
[23]	Kumar R, Badilescu S, Packirisamy M 2019 J. Nanosci. Nanotechnol. 19 4617 Google Scholar
[24]	Lee D, Yoon S 2015 J. Phys. Chem. C 119 7873 Google Scholar
[25]	Boerigter C, Campana R, Morabito M 2015 Nat. Commun. 7 10545 Google Scholar
[26]	Funston A M, Novo C, Davis T J, Mulvanet P 2009 Nano Lett. 9 1651 Google Scholar
[27]	Zhu X P, Chen Y Q, Shi H M, Zhang S, Liu Q H, Duan H G 2017 J. Appl. Phys. 121 213105 Google Scholar
[28]	Cui Y, Zhou J, Tamma V A, Park W 2012 ACS Nano 6 2385 Google Scholar
[29]	Lovera A, Gallinet B, Nordlander P, Martin O J F 2013 ACS Nano 7 4527 Google Scholar
[30]	Lassiter J B, Sobhani H, Fan J A, Kundu J, Capasso F, Nordlander P, Halas N J 2010 Nano Lett. 10 3184 Google Scholar
[31]	Liu N, Weiss T, Mesch M, Langguth L, Eigenthaler U, Hirscher M, Nnichsen C, Giessen H 2010 Nano Lett. 10 1103 Google Scholar
[32]	Dijk M A V, Tchebotareva A L, Orrit M, Lippitz M, Lounis B 2006 Phys. Chem. Chem. Phys. 8 3486 Google Scholar
[33]	Gans R, Über D 1912 Ann. Phys. 342 881 Google Scholar
[34]	Ye J, Dorpe P V, Roy W V, Lodewijks K, Vlaminck I D, Maes G, Borghs G 2009 J. Phys. Chem. C 113 3110 Google Scholar
[35]	Nordlander P, Oubre C 2004 Nano Lett. 4 899 Google Scholar
[36]	Kerker M 1985 J. Colloid Interface Sci. 105 297 Google Scholar
[37]	Knight M W, Halas N J 2008 New J. Phys. 10 119 Google Scholar
[38]	Chen Q, Qi H, Ren Y T, Sun J P, Ruan L M 2017 AIP Adv. 7 065115 Google Scholar
[39]	Lassiter J B, Knight M W, Mirin N A, Halas N J 2009 Nano Lett. 9 4326 Google Scholar
[40]	洪昕, 王晨晨 2018 光学学报 38 0524001 Google Scholar Hong X, Wang C C 2018 Acta Opti. Sin. 38 0524001 Google Scholar
[41]	Ye J, Kong Y, Liu C 2016 J. Phys. D:Appl. Phys. 49 205106 Google Scholar
[42]	Cortie M, Ford M 2007 Nanotechnology 18 235704 Google Scholar
[43]	洪昕 2020 中国专利 ZL202010038295.7 Hong X 2020 Chinese Patent CN111204705A (in Chinese)

[1]	赵富, 胡渝曜, 王鹏, 刘军. 偏振复用散射成像. , 2023, 72(15): 154201. doi: 10.7498/aps.72.20230551
[2]	霍永胜. 基于偏振的暗通道先验去雾. , 2022, 71(14): 144202. doi: 10.7498/aps.71.20220332
[3]	郝鹏, 张丽丽, 丁明明. 高分子囊泡在微管流中惯性迁移现象的有限元分析. , 2022, 71(18): 188701. doi: 10.7498/aps.71.20220606
[4]	洪昕, 王晓强, 李冬雪, 商云晶. 不依赖激发光偏振方向的芯帽异构二聚体. , 2021, (): . doi: 10.7498/aps.70.20211381
[5]	洪昕, 王晨晨, 刘江涛, 王晓强, 尹雪洁. 芯帽纳米颗粒的光热性质. , 2018, 67(19): 195202. doi: 10.7498/aps.67.20180909
[6]	吕浩, 尤凯, 兰燕燕, 高冬, 赵秋玲, 王霞. 非对称光束干涉制备二维微纳光子结构研究. , 2017, 66(21): 217801. doi: 10.7498/aps.66.217801
[7]	孙明健, 程星振, 王艳, 章欣, 沈毅, 冯乃章. 基于光声信号的高铁钢轨表面缺陷检测方法. , 2016, 65(3): 038105. doi: 10.7498/aps.65.038105
[8]	张保磊, 王家序, 肖科, 李俊阳. 石墨烯-纳米探针相互作用有限元准静态计算. , 2014, 63(15): 154601. doi: 10.7498/aps.63.154601
[9]	刘磊, 张锁良, 马亚坤, 吴国浩, 郑树凯, 王永青. 平板集热太阳热电器件建模及结构优化. , 2013, 62(3): 038802. doi: 10.7498/aps.62.038802
[10]	胡海涛, 肖立志, 吴锡令. 核磁共振测井仪探头设计中的数值方法. , 2012, 61(14): 149302. doi: 10.7498/aps.61.149302
[11]	王伟, 杨博. 菱形纤芯光子晶体光纤色散与双折射特性分析. , 2012, 61(6): 064601. doi: 10.7498/aps.61.064601
[12]	钟明亮, 李山, 熊祖洪, 张中月. 十字形银纳米结构的表面等离子体光子学性质. , 2012, 61(2): 027803. doi: 10.7498/aps.61.027803
[13]	李山, 钟明亮, 张礼杰, 熊祖洪, 张中月. 偏振方向及结构间耦合作用对空心方形银纳米结构表面等离子体共振的影响. , 2011, 60(8): 087806. doi: 10.7498/aps.60.087806
[14]	厉以宇, 王媛媛, 陈浩, 朱德喜, 胡川, 瞿佳. 基于二维结构薄膜的偏振选择相位光栅的研究. , 2010, 59(7): 5110-5115. doi: 10.7498/aps.59.5110
[15]	刘小毅, 张方迪, 张民, 叶培大. 基于谐振吸收效应的单模单偏振光子晶体光纤研究. , 2007, 56(1): 301-307. doi: 10.7498/aps.56.301
[16]	郑国梁, 佘卫龙. 偏振方向对THz电光探测影响的理论研究. , 2006, 55(3): 1061-1067. doi: 10.7498/aps.55.1061
[17]	周剑平, 施展, 刘刚, 何泓材, 南策文. 铁电/铁磁1-3型结构复合材料磁电性能分析. , 2006, 55(7): 3766-3771. doi: 10.7498/aps.55.3766
[18]	周国泉. 任意线偏振高斯光束的非傍轴传输. , 2005, 54(10): 4710-4717. doi: 10.7498/aps.54.4710
[19]	李蓉, 任坤, 任晓斌, 周静, 刘大禾. 一维光子晶体带隙结构对不同偏振态的角度和波长响应. , 2004, 53(8): 2520-2525. doi: 10.7498/aps.53.2520
[20]	杜启振, 杨慧珠. 方位各向异性黏弹性介质波场有限元模拟. , 2003, 52(8): 2010-2014. doi: 10.7498/aps.52.2010

计量

文章访问数: 3577
PDF下载量: 40
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板

不依赖激发光偏振方向的芯帽异构二聚体