钛宝石飞秒激光器用色散补偿Gires-Tournois镜的研究

马群; 章岳光; 沈伟东; 罗震岳; 张青; 张淑娜; 叶蓬; 袁文佳; 刘旭; 魏志义

doi:10.7498/aps.60.027804

摘要

根据钛宝石飞秒激光器的色散补偿要求设计了单次反射平均补偿量为-60 fs2的GT(Gires-Tournois)镜,采用离子束辅助沉积技术结合光学监控技术制作了器件.用分光光度计对650—950 nm波段薄膜反射率进行测试,结果表明反射率测试曲线与设计曲线十分符合,同时利用白光干涉系统对群延迟色散进行了测试,测试结果与设计符合得很好,实际的色散曲线振荡基本控制在±20 fs2以内.应用该GT镜进行钛宝石飞秒激光系统的色散补偿,取得了很好的锁模效果,得到了29 fs的超短脉冲.

关键词:

Abstract

A Gires-Tournois(GT) mirror with a group delay dispersion (GDD) of -60 fs2 in one reflection was designed according to the requirement of dispersion compensation in the Ti-sapphire femtosecond laser system. It was manufactured by ion assisted deposition combined with the optical monitoring in transmission. The reflectance of the mirror was measured by a spectrophometer working in the range from 650 nm to 950 nm with a resolution of 1 nm. The results were consistent with the design. Furthermore, a home-made white light interferometry system was employed to test the reflection GDD and the result also agreed well with the design. The experimental GDD oscillation was less than ± 20 fs2. The GT mirror was applied in the Ti-sapphire femtosecond laser system and a good clamping result was obtained. Finally a 29 fs ultra-short pulse was acquired.

Keywords:

作者及机构信息

(1)浙江大学现代光学仪器国家重点实验室,杭州 310027; (2)中国科学院物理研究所光物理重点实验室,北京 100190

基金项目: 国家自然科学基金(批准号:60708013,60608014)资助的课题.

Authors and contacts

(1)Laboratory of Optical Physics,Institute of Physics, Chinese Academy of Sciences, Beijing 100190,China; (2)State Key Laboratory of Modern Optical Instrumentation, Zhejiang University, Hangzhou 310027,China

参考文献

[1]	www.layertec.de
[2]	Cao S Y, Zhang Z G, Chai L, Wang Q Y 2008 Acta Phys. Sin. 57 2971 (in Chinese) [曹士英、张志刚、柴路、王清月 2008 57 2971]
[3]	Wang Y L, Zhou X G, Wu H, Ding L E 2009 Chin. Phys. B 18 4308
[4]	Zhao Y Y, Han H N, Teng H, Wei Z Y 2009 Acta Phys. Sin. 58 1709(in Chinese)[赵研英、韩海年、滕浩、魏志义 2009 58 1709]
[5]	Szipcs R, Koházi-Kis A 1997 Appl.phys.B 65 115
[6]	Steinmeyer G 2006 Appl.Opt. 45 1490
[7]	Tian J R, Han H N, Zhao Y Y, Wang P, Zhang W, Wei Z Y 2006 Acta Phys. Sin. 55 4725 (in Chinese) [田金荣、韩海年、赵研英、王鹏、张炜、魏志义 2006 55 4725]
[8]	Szipcs R, Ferencz K, Splielmann C, Krausz F 1994 Opt.Lett. 19 203
[9]	Luo Z Y, Liu X, Shen W D, Xue H, Zhang Y G, Gu P F 2009 Acta Opt. Sin. 9 2619(in Chinese) [罗震岳、刘旭、沈伟东、薛晖、章岳光、顾培夫 2009 光学学报 9 2619]
[10]	Luo Z Y, Shen W D, Liu X, Gu P F, Xia C 2010 Chin. Opt. Lett. 3 342 (in Chinese)[罗震岳、沈伟东、刘旭、顾培夫、夏梣 2010 中国光学快报 3 342]
[11]	Pervak V, Tikhonravov V, Trubetskov M K, Naumov S, Krausz F, Apolonski A 2007 Appl. Phys. B 87 5
[12]	Szipcs R, Koházi-Kis A, Lakó S, Apai P, Kovács A P, DeBell G, Mott L, Louderback A W, Tikhonravov A V, Trubetskov M K 2000 Appl. Phys. B 70 S51
[13]	Xie X D, Wang Q Y, Wang Z, Zhang W L, Chai L 2005 Acta Phys. Sin. 54 3159(in Chinese)[谢旭东、王清月、王专、张伟力、柴路 2005 54 3159]
[14]	Tikhonov A N, Tikhonravov A V, Trubetskov M K 1993 Comp. Maths. Math. Phys. 33 1339
[15]	Tikhonravov A V, Trubetskov M K, DeBell G W 1996 Appl. Opt. 35 5493
[16]	Bischoff M, Stenzel O, Gbler D, Kaiser N 2005 Proc. SPIE 5963 59631N-1
[17]	Tang J F,Gu P F,Liu X,Li H F 2006 Modern Optical Thin Film Technology (Hangzhou:Zhejiang University Press)p262(in Chinese)[唐晋发、顾培夫、刘旭、李海峰 2006 现代光学薄膜技术(杭州:浙江大学出版社)第262页]
[18]	Xue H, Shen W D, Gu P F, Luo Z Y, Zhang Y G, Liu X 2009 Chin. Opt. Lett. 7 446 (in Chinese)[薛晖、沈伟东、顾培夫、罗震岳、章岳光、刘旭 2009 中国光学快报 7 446 ]
[19]

施引文献

[1]	www.layertec.de
[2]	Cao S Y, Zhang Z G, Chai L, Wang Q Y 2008 Acta Phys. Sin. 57 2971 (in Chinese) [曹士英、张志刚、柴路、王清月 2008 57 2971]
[3]	Wang Y L, Zhou X G, Wu H, Ding L E 2009 Chin. Phys. B 18 4308
[4]	Zhao Y Y, Han H N, Teng H, Wei Z Y 2009 Acta Phys. Sin. 58 1709(in Chinese)[赵研英、韩海年、滕浩、魏志义 2009 58 1709]
[5]	Szipcs R, Koházi-Kis A 1997 Appl.phys.B 65 115
[6]	Steinmeyer G 2006 Appl.Opt. 45 1490
[7]	Tian J R, Han H N, Zhao Y Y, Wang P, Zhang W, Wei Z Y 2006 Acta Phys. Sin. 55 4725 (in Chinese) [田金荣、韩海年、赵研英、王鹏、张炜、魏志义 2006 55 4725]
[8]	Szipcs R, Ferencz K, Splielmann C, Krausz F 1994 Opt.Lett. 19 203
[9]	Luo Z Y, Liu X, Shen W D, Xue H, Zhang Y G, Gu P F 2009 Acta Opt. Sin. 9 2619(in Chinese) [罗震岳、刘旭、沈伟东、薛晖、章岳光、顾培夫 2009 光学学报 9 2619]
[10]	Luo Z Y, Shen W D, Liu X, Gu P F, Xia C 2010 Chin. Opt. Lett. 3 342 (in Chinese)[罗震岳、沈伟东、刘旭、顾培夫、夏梣 2010 中国光学快报 3 342]
[11]	Pervak V, Tikhonravov V, Trubetskov M K, Naumov S, Krausz F, Apolonski A 2007 Appl. Phys. B 87 5
[12]	Szipcs R, Koházi-Kis A, Lakó S, Apai P, Kovács A P, DeBell G, Mott L, Louderback A W, Tikhonravov A V, Trubetskov M K 2000 Appl. Phys. B 70 S51
[13]	Xie X D, Wang Q Y, Wang Z, Zhang W L, Chai L 2005 Acta Phys. Sin. 54 3159(in Chinese)[谢旭东、王清月、王专、张伟力、柴路 2005 54 3159]
[14]	Tikhonov A N, Tikhonravov A V, Trubetskov M K 1993 Comp. Maths. Math. Phys. 33 1339
[15]	Tikhonravov A V, Trubetskov M K, DeBell G W 1996 Appl. Opt. 35 5493
[16]	Bischoff M, Stenzel O, Gbler D, Kaiser N 2005 Proc. SPIE 5963 59631N-1
[17]	Tang J F,Gu P F,Liu X,Li H F 2006 Modern Optical Thin Film Technology (Hangzhou:Zhejiang University Press)p262(in Chinese)[唐晋发、顾培夫、刘旭、李海峰 2006 现代光学薄膜技术(杭州:浙江大学出版社)第262页]
[18]	Xue H, Shen W D, Gu P F, Luo Z Y, Zhang Y G, Liu X 2009 Chin. Opt. Lett. 7 446 (in Chinese)[薛晖、沈伟东、顾培夫、罗震岳、章岳光、刘旭 2009 中国光学快报 7 446 ]
[19]

[1]	张鹏, 滕浩, 杨浩, 吕仁冲, 王柯俭, 朱江峰, 魏志义. 基于Herriott型多通结构的块材料展宽与棱栅对色散补偿的啁啾脉冲放大. , 2022, 71(11): 114202. doi: 10.7498/aps.71.20212381
[2]	王楠, 阮双琛. 啁啾脉冲放大激光系统中展宽器色散的解析算法. , 2020, 69(2): 024201. doi: 10.7498/aps.69.20191587
[3]	黄沛, 方少波, 黄杭东, 侯洵, 魏志义. 基于平衡光学互相关方法的超短脉冲激光相干合成技术. , 2018, 67(24): 244204. doi: 10.7498/aps.67.20181851
[4]	陈翔, 张心贲, 祝贤, 程兰, 彭景刚, 戴能利, 李海清, 李进延. 色散补偿光子晶体光纤结构参数对其色散的影响. , 2013, 62(4): 044222. doi: 10.7498/aps.62.044222
[5]	王胭脂, 邵建达, 易葵, 齐红基, 王玎, 冷雨欣. 宽带啁啾镜对的设计和制备. , 2013, 62(20): 204207. doi: 10.7498/aps.62.204207
[6]	钟东洲, 佘卫龙. 铌酸锂晶体中飞秒激光脉冲线性电光效应及其色散补偿. , 2012, 61(6): 064214. doi: 10.7498/aps.61.064214
[7]	张立超, 侯蓝田, 周桂耀. 八边形光子晶体光纤色散补偿特性分析. , 2011, 60(5): 054217. doi: 10.7498/aps.60.054217
[8]	王胭脂, 邵建达, 董洪成, 晋云霞, 贺洪波, 易葵, 范正修, 宋有建, 王思佳, 胡明列, 柴路, 王清月. 高色散镜的设计和制备. , 2011, 60(11): 117801. doi: 10.7498/aps.60.117801
[9]	王胭脂, 邵建达, 董洪成, 晋云霞, 贺洪波, 易葵, 范正修, 宋有建, 胡明列, 柴路, 王清月. 钛宝石激光器9.5 fs脉冲输出中的啁啾镜色散补偿. , 2011, 60(1): 018101. doi: 10.7498/aps.60.018101
[10]	开花, 李运超, 郭德成, 李双, 李之杰. 斜入射离子束辅助沉积对类金刚石薄膜结构影响的分子动力学模拟. , 2009, 58(7): 4888-4894. doi: 10.7498/aps.58.4888
[11]	陈立宝, 虞红春, 许春梅, 王太宏. 离子束辅助沉积硅薄膜负极材料的研究. , 2009, 58(7): 5029-5034. doi: 10.7498/aps.58.5029
[12]	谭中伟, 曹继红, 陈勇, 刘艳, 宁提纲, 简水生. 低串扰的多波长光纤光栅色散补偿器. , 2007, 56(1): 274-279. doi: 10.7498/aps.56.274
[13]	孙振红, 柴路, 张志刚, 王清月, 张伟力, 袁晓东, 黄小军. 马丁内兹型啁啾脉冲放大系统高阶色散的混合补偿. , 2005, 54(2): 777-781. doi: 10.7498/aps.54.777
[14]	裴丽, 宁提纲, 李唐军, 董小伟, 简水生. 高速光通信系统中光纤光栅色散补偿研究. , 2005, 54(4): 1630-1635. doi: 10.7498/aps.54.1630
[15]	李之杰, 潘正瑛, 朱靖, 魏启, 王月霞, 臧亮坤, 周亮, 刘提将. 离子束辅助沉积对类金刚石膜结构影响的计算机模拟. , 2005, 54(5): 2233-2238. doi: 10.7498/aps.54.2233
[16]	谭中伟, 郑凯, 刘艳, 傅永军, 陈勇, 曹继红, 宁提纲, 董小伟, 马丽娜, 简水生. 基于啁啾光纤光栅的色散补偿器在超长距离密集波分复用系统中的应用. , 2005, 54(11): 5218-5223. doi: 10.7498/aps.54.5218
[17]	李曙光, 刘晓东, 侯蓝田. 光子晶体光纤色散补偿特性的数值研究. , 2004, 53(6): 1880-1886. doi: 10.7498/aps.53.1880
[18]	裴丽, 简水生, 延凤平, 宁提纲, 简伟, 李唐军. 4×10Gb/s 400km 啁啾光纤光栅色散补偿研究. , 2003, 52(3): 615-619. doi: 10.7498/aps.52.615
[19]	刘永军, 柴路, 王清月, 张志刚. 对于具有一定宽度的光束通过展宽器的色散误差的评价. , 2002, 51(6): 1291-1294. doi: 10.7498/aps.51.1291
[20]	张志刚, 孙虹. 飞秒脉冲放大器中色散的计算和评价方法. , 2001, 50(6): 1080-1086. doi: 10.7498/aps.50.1080

计量

文章访问数: 9734
PDF下载量: 779
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板