LaFe11.5Si1.5化合物氢化特性及稳定性的研究

张登魁; 赵金良; 张红国; 岳明

doi:10.7498/aps.63.197501

摘要

系统研究了温度、时间、压力等因素对LaFe11.5Si1.5化合物吸氢过程的影响以及效果. 结果表明：吸氢处理会增大化合物的晶格常数，但不会改变其晶体结构. 在温度为423 K，氢气压力为0.0987 MPa时，可以制备出氢分布均匀的LaFe11.5Si1.5H1.6间隙化合物. 氢化处理可以明显提高化合物的居里温度，降低热滞后，并且使磁熵变保持在较高值. LaFe11.5Si1.5H1.6样品随着在空气中暴露时间的延长，居里温度和磁熵值的变化非常小，氢化合金的磁热性能具有良好的时间稳定性.

关键词:

Abstract

We have studied systematically the effects of temperature, time, and pressure on the process of hydrogen absorption in LaFe11.5Si1.5 compound. Results show that hydrogen absorption can increase the lattice parameter of the compound without changing its crystal structure. The LaFe11.5Si1.5H1.6 compound can be prepared at a hydrogen pressure of 0.0987 MPa at 423 K with uniform distribution of hydrogen. Hydrogen absorption can also increase the Curie temperature obviously, decrease the thermal hysteresis and maintain the magnetic entropy change at a high standard. With prolonged exposure time in air, the variation of the Curie temperature and magnetic entropy change of LaFe11.5Si1.5H1.6 compound are very small, implying that the magnetic thermal performance of hydride alloy has a good time stability.

Keywords:

作者及机构信息

1.
北京工业大学材料科学与工程学院, 北京 100124;

2.
北京工业大学应用数理学院, 北京 100124

基金项目: 国家自然科学基金青年科学基金（批准号：51301008）和国家自然科学基金（批准号：51071007，51171003）资助的课题.

Authors and contacts

1.
College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China;

2.
College of Applied Sciences, Beijing University of Technology, Beijing 100124, China

Funds: Project supported by the Young Scientists Fund of the National Natural Science Foundation of China (Grant No. 51301008), and the National Natural Science Foundation of China (Grant Nos. 51071007, 51171003).

参考文献

[1]	Warburg E, Untersuchungen M, Magnetische Untersuchungen 1881 Ann. Phys. 13 141
[2]	Zhao X, Chen W, Li A J, Ma L M, Zong Y 2009 Chin. Phys. Lett. 26 87401
[3]	Hui X D, Xu Z Y, Wang E R, Chen G L, Lu Z P 2010 Chin. Phys. Lett. 27 117502
[4]	Zhang G Y, Chen H, Yang D, Hu F, Liu H S 2012 Chin. Phys. Lett. 29 27502
[5]	Wang F, Yuan F Y, Wang J Z 2013 Acta. Phys. Sin. 62 167501[王芳, 原凤英, 汪金芝 2013 62 167501]
[6]	Hu F X, Shen B G, Sun J R 2013 Chin. Phys. B 22 037505
[7]	Shen B G, Sun J R, Hu F X, Zhang H W, Cheng Z H 2009 Adv. Mater. 21 4545
[8]	Shen J, Li Y X, Wang F, Wang G J, Zhang S Y 2004 Chin. Phys. 13 1134
[9]	Wang F, Chen Y F, Wang G J, Sun J R, Shen B G 2004 Chin. Phys. 13 1344
[10]	Shen J, Gao B, Yan L Q, Li Y X, Zhang H W, Hu F X, Sun J R 2007 Chin. Phys. 16 3848
[11]	Wang F, Wang G J, Sun J R, Shen B G 2008 Chin. Phys. B 17 3087
[12]	Shen B G, Hu F X, Dong Q Y, Sun J R 2013 Chin. Phys. B 18 017502
[13]	Tishin A M 1999 Handbook of Magnetic Materials (Vol. 12) (Amsterdam: Elsevier) pp395–524
[14]	Gschneidner K A, Pecharsky V K, Tsokol A O 2005 Rep. Prog. Phys. 68 1479
[15]	Hu F X, Qian X L, Sun J R, Wang G J, Zhang X X, Cheng Z H, Shen B G 2002 J. Appl. Phys. 92 3620
[16]	Balli M, Fruchart D, Gignoux D 2007 J. Phys.: Condens. Matter 19 236230
[17]	Shen J, Li Y X, Zhang J, Gao B, Hu F X, Zhang H W, Chen Y Z, Rong C B, Sun J R 2008 J. Appl. Phys. 103 07B317
[18]	Yan A, Mller K H, Gutfleisch O 2008 J. Alloys Compd. 450 18
[19]	Liu G J, Sun J R, Shen J, Gao B, Zhang H W, Hu F X, Shen B G 2007 Appl. Phys. Lett. 90 032507
[20]	Wang F, Chen Y F, Wang G J, Sun J R, Shen B G 2004 Chin. Phys. 13 393
[21]	Chen J, Zhang H W, Zhang L G, Dong Q Y, Wang R W 2006 Chin. Phys. 15 845
[22]	Zhao J L, Shen J, Hu F X, Li Y X, Sun J R, Shen B G 2010 J. Appl. Phys. 107 113911
[23]	Chen Y F, Wang F, Shen B G, Hu F X, Cheng Z H, Wang G J, Sun J R 2002 Chin. Phys. 11 741
[24]	Fu B, Long Y, Shi P J, Ma T, Bao B, Yan A R, Chen R J 2009 Chin. Phys. B 18 4506
[25]	Zhao J L 2010 Ph. D. Dissertation (Tianjin: Hebei University of Technology) (in Chinese) [赵金良2010博士学位论文(天津: 河北工业大学)]
[26]	Zhao J L, Shen J, Shen B G, Hu F X, Sun J R 2010 Solid State Commun. 150 2330

施引文献

[1]	Warburg E, Untersuchungen M, Magnetische Untersuchungen 1881 Ann. Phys. 13 141
[2]	Zhao X, Chen W, Li A J, Ma L M, Zong Y 2009 Chin. Phys. Lett. 26 87401
[3]	Hui X D, Xu Z Y, Wang E R, Chen G L, Lu Z P 2010 Chin. Phys. Lett. 27 117502
[4]	Zhang G Y, Chen H, Yang D, Hu F, Liu H S 2012 Chin. Phys. Lett. 29 27502
[5]	Wang F, Yuan F Y, Wang J Z 2013 Acta. Phys. Sin. 62 167501[王芳, 原凤英, 汪金芝 2013 62 167501]
[6]	Hu F X, Shen B G, Sun J R 2013 Chin. Phys. B 22 037505
[7]	Shen B G, Sun J R, Hu F X, Zhang H W, Cheng Z H 2009 Adv. Mater. 21 4545
[8]	Shen J, Li Y X, Wang F, Wang G J, Zhang S Y 2004 Chin. Phys. 13 1134
[9]	Wang F, Chen Y F, Wang G J, Sun J R, Shen B G 2004 Chin. Phys. 13 1344
[10]	Shen J, Gao B, Yan L Q, Li Y X, Zhang H W, Hu F X, Sun J R 2007 Chin. Phys. 16 3848
[11]	Wang F, Wang G J, Sun J R, Shen B G 2008 Chin. Phys. B 17 3087
[12]	Shen B G, Hu F X, Dong Q Y, Sun J R 2013 Chin. Phys. B 18 017502
[13]	Tishin A M 1999 Handbook of Magnetic Materials (Vol. 12) (Amsterdam: Elsevier) pp395–524
[14]	Gschneidner K A, Pecharsky V K, Tsokol A O 2005 Rep. Prog. Phys. 68 1479
[15]	Hu F X, Qian X L, Sun J R, Wang G J, Zhang X X, Cheng Z H, Shen B G 2002 J. Appl. Phys. 92 3620
[16]	Balli M, Fruchart D, Gignoux D 2007 J. Phys.: Condens. Matter 19 236230
[17]	Shen J, Li Y X, Zhang J, Gao B, Hu F X, Zhang H W, Chen Y Z, Rong C B, Sun J R 2008 J. Appl. Phys. 103 07B317
[18]	Yan A, Mller K H, Gutfleisch O 2008 J. Alloys Compd. 450 18
[19]	Liu G J, Sun J R, Shen J, Gao B, Zhang H W, Hu F X, Shen B G 2007 Appl. Phys. Lett. 90 032507
[20]	Wang F, Chen Y F, Wang G J, Sun J R, Shen B G 2004 Chin. Phys. 13 393
[21]	Chen J, Zhang H W, Zhang L G, Dong Q Y, Wang R W 2006 Chin. Phys. 15 845
[22]	Zhao J L, Shen J, Hu F X, Li Y X, Sun J R, Shen B G 2010 J. Appl. Phys. 107 113911
[23]	Chen Y F, Wang F, Shen B G, Hu F X, Cheng Z H, Wang G J, Sun J R 2002 Chin. Phys. 11 741
[24]	Fu B, Long Y, Shi P J, Ma T, Bao B, Yan A R, Chen R J 2009 Chin. Phys. B 18 4506
[25]	Zhao J L 2010 Ph. D. Dissertation (Tianjin: Hebei University of Technology) (in Chinese) [赵金良2010博士学位论文(天津: 河北工业大学)]
[26]	Zhao J L, Shen J, Shen B G, Hu F X, Sun J R 2010 Solid State Commun. 150 2330

[1]	刘冰心, 李宗良. CrO₂单层: 一种兼具高居里温度和半金属特性的二维铁磁体. , 2024, 73(10): 106102. doi: 10.7498/aps.73.20240246
[2]	孙敬淇, 吴绪才, 阙志雄, 张卫兵. 基于材料组分信息的高居里温度铁磁材料预测. , 2023, 72(18): 180202. doi: 10.7498/aps.72.20230382
[3]	王海宇, 刘英杰, 寻璐璐, 李竞, 杨晴, 田祺云, 聂天晓, 赵巍胜. 大面积二维磁性材料的制备及居里温度调控. , 2021, 70(12): 127301. doi: 10.7498/aps.70.20210223
[4]	张浩杰, 张茹菲, 傅立承, 顾轶伦, 智国翔, 董金瓯, 赵雪芹, 宁凡龙. 一种具有“1111”型结构的新型稀磁半导体(La_1–xSr_x)(Zn_1–xMn_x)SbO. , 2021, 70(10): 107501. doi: 10.7498/aps.70.20201966
[5]	黄玉昊, 张贵涛, 王如倩, 陈乾, 王金兰. 二维双金属铁磁半导体CrMoI₆的电子结构与稳定性. , 2021, 70(20): 207301. doi: 10.7498/aps.70.20210949
[6]	孙晓东, 徐宝, 吴鸿业, 曹凤泽, 赵建军, 鲁毅. Tb掺杂双层锰氧化物La4/3Sr5/3Mn2O7的磁熵变和电输运性质. , 2017, 66(15): 157501. doi: 10.7498/aps.66.157501
[7]	郑新奇, 沈俊, 胡凤霞, 孙继荣, 沈保根. 磁热效应材料的研究进展. , 2016, 65(21): 217502. doi: 10.7498/aps.65.217502
[8]	刘忠深, 特古斯, 欧志强, 范文迪, 宋志强, 哈斯朝鲁, 伟伟, 韩睿. 在永磁体强磁场中Mn1.2Fe0.8P1-xSix系列化合物热磁发电研究. , 2015, 64(4): 047103. doi: 10.7498/aps.64.047103
[9]	黄逸佳, 张国营, 胡风, 夏往所, 刘海顺. PrNi2的磁和磁热性能研究. , 2014, 63(22): 227501. doi: 10.7498/aps.63.227501
[10]	鲁峰, 陈朗, 冯长根. 冲击波诱导Nd2Fe14B磁相变的理论计算研究. , 2014, 63(16): 167501. doi: 10.7498/aps.63.167501
[11]	王芳, 汪金芝, 冯唐福, 孙仁兵, 余盛. La(Fe, Si)13化合物的居里温度机制. , 2014, 63(12): 127501. doi: 10.7498/aps.63.127501
[12]	蔡培阳, 冯尚申, 陈卫平, 薛双喜, 李志刚, 周英, 王海波, 王古平. Ni47Mn32Ga21多晶合金的磁熵变和磁感生应变. , 2011, 60(10): 107501. doi: 10.7498/aps.60.107501
[13]	郝延明, 王玲玲, 严达利, 安力群. 电弧炉制备的Sm2Fe17-xCrx化合物的结构与磁性. , 2009, 58(10): 7222-7226. doi: 10.7498/aps.58.7222
[14]	王叶安, 秦福文, 吴东江, 吴爱民, 徐茵, 顾彪. 基于电子回旋共振-等离子体增强金属有机物化学气相沉积技术生长GaMnN稀磁半导体的研究. , 2008, 57(1): 508-513. doi: 10.7498/aps.57.508
[15]	申晔, 邢怀中, 俞建国, 吕斌, 茅惠兵, 王基庆. 极化诱导的内建电场对Mn δ掺杂的GaN/AlGaN量子阱居里温度的调制. , 2007, 56(6): 3453-3457. doi: 10.7498/aps.56.3453
[16]	刘喜斌, 沈保根. Mn5Ge2.7M0.3 (M=Ga，Al，Sn) 化合物的磁性和磁熵变. , 2005, 54(12): 5884-5889. doi: 10.7498/aps.54.5884
[17]	熊昌民, 孙继荣, 王登京, 沈保根. 厚度与应变效应对La0.67Ca0.33MnO3薄膜电输运与居里温度的影响. , 2004, 53(11): 3909-3915. doi: 10.7498/aps.53.3909
[18]	郝延明, 赵伟, 高艳. Y2(Fe1-x-y,Coy,Crx)17化合物的结构及居里温度. , 2003, 52(10): 2612-2615. doi: 10.7498/aps.52.2612
[19]	沈俊, 李养贤, 胡凤霞, 王光军, 张绍英. Ce2Fe16Al化合物在居里温度附近的磁性和磁熵变. , 2003, 52(5): 1250-1254. doi: 10.7498/aps.52.1250
[20]	陈伟, 钟伟, 潘成福, 常虹, 都有为. La0.8-xCa0.2MnO3纳米颗粒的居里温度与磁热效应. , 2001, 50(2): 319-323. doi: 10.7498/aps.50.319

计量

文章访问数: 5767
PDF下载量: 346
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板