Pr掺杂DyFeO3体系的自旋重取向相变、晶格畸变与Raman光谱研究

刘明; 曹世勋; 袁淑娟; 康保娟; 鲁波; 张金仓

doi:10.7498/aps.62.147601

摘要

利用固相反应法制备了Dy1-xPrxFeO3系列化合物. X射线粉末衍射晶体结构分析表明, 随着Pr掺杂量x的增加, 样品晶胞体积逐渐增大, 晶格畸变减弱. Raman光谱测量表明稀土离子有效质量[meff=xmPr+(1-x)mDy] 与晶格结构的变化共同导致该体系Raman光谱的变化. 随Pr掺杂量的增加, 波数小于200 cm-1的振动模式基本保持不变, 而波数大于200 cm-1的振动模式(除420 cm-1处的B3u模式外)向低频移动. 磁测量结果表明, 由Dzyaloshinsky-Moriya 相互作用导致的宏观磁性随Pr掺杂量增加逐渐减弱. 稀土离子与铁离子磁晶格的耦合作用以及晶格结构畸变的变化共同导致该体系自旋重取向相变温度在一定的掺杂量 (x=0.3)前后先升高后降低.

关键词:

Abstract

Pr doped rare-earth orthoferrites DyFeO3 is synthesized by solid state reaction. X-ray diffraction shows that the lattice parameters of Dy1-xPrxFeO3increase and distortion of lattice decreases with Pr content x increasing. Raman spectroscopy reveals that the change of effective mass (meff) [meff=xmPr+(1-x)mDy] together with lattice structure change results in the shift of vibration modes. With the increase of Pr content, Raman modes of wave number less than 200 cm-1 remain constant, but the modes of wave number greater than 200 cm-1 decrease with Pr content increasing (except the mode B3u near 420 cm-1). The weak ferromagnetic ordering, created by Dzyaloshinsky-Moriya interaction, is reduced with doping level increasing. The interaction of rare earth ions with Fe3+ ion, together with the change of lattice distortion, results in the increasing of spin reorientation phase transition temperature when xx increasing to over 0.3.

Keywords:

作者及机构信息

1.
上海大学理学院物理系, 上海 200444;

2.
上海大学微结构实验室, 上海 200444

基金项目: 国家自然科学基金(批准号: 50932003, 11274221, 11074163)和上海市教育委员会科技创新基金重点项目(批准号12YZ018, 12ZZ097)资助的课题.

Authors and contacts

1.
Department of Physics, Shanghai University, Shanghai 200444, China;

2.
Laboratory for Microstructures, Shanghai University, Shanghai 200444, China

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 50932003, 11274221, 11074163) and the Science and Technology Innovation Fund of the Shanghai Education Committee, China (Grant Nos. 12YZ018, 12ZZ097).

参考文献

[1]	Tsymbal L T, Bazaliy Y B, Derkachenko V N, Kamenev V I, Kakazei G N, Palomares F J, Wigen P E 2007 J. Appl. Phys. 101 123919
[2]	Iida R, Satoh T, Shimura T, Kuroda K, Ivanov B A, Tokunaga Y, Tokura Y 2011 Phys. Rev. B 84 064402
[3]	Hur N, Park S, Sharma P A, Ahn J S, Guha S, Cheong S W 2004 Nature 429 392
[4]	Ikeda N, Ohsumi H, Ohwada K, Ishii K, Inami T, Kakurai K, Murakami Y, Yoshii K, Mori S, Horibe Y, Kitô H 2005 Nature 436 1136
[5]	Wang J, Neaton J B, Zheng H, Nagarajan V, Ogale B, Liu B, Viehland D, Vaithyanathan V, Schlom D G, Waghmare U V, Spal-din N A, Rabe K M, Wuttig M, Ramesh R 2003 Science 299 1719
[6]	Cheng Z X, Li A H, Wang X L, Dou S X, Ozawa K, Kimura H, Zhang S J, Shrout T R 2008 J. Appl. Phys. 103 07E507
[7]	Fennie C J 2008 Phys. Rev. Lett. 100 167203
[8]	Tokunaga Y, Iguchi S, Arima T, Tokura Y 2008 Phys. Rev. Lett. 101 097205
[9]	Tokunaga Y, Taguchi Y, Arima T, Tokura Y 2012 Nature Phys. 8 838
[10]	Dzyaloshinskii I 1958 J. Phys. Chem. Solids 4 241
[11]	Moriya T 1960 Phys. Rev. 120 91
[12]	Gorodetsky G, Sharon B, Shtrikman S 1968 J. Appl. Phys. 39 1371
[13]	White R L 1969 J. Appl. Phys. 40 1061
[14]	Song G L, Zhou X H, Su J, Yang H G, Wang T X, Chang F G 2012 Acta Phys. Sin. 61 177501 (in Chinese) [宋桂林, 周晓辉, 苏键, 杨海刚, 王天兴, 常方高 2012 61 177501]
[15]	Du Y, Cheng Z X, Wang X L, Dou S X 2010 J. Appl. Phys. 107 09D908
[16]	Guptake H C, Singh M K, Tiwari L M 2002 J. Raman Spectrosc. 33 67
[17]	Venugopalan S, Dutta M, Ramdas A K, Remeika J P 1985 Phys. Rev. B 31 1490
[18]	Traversa E, Nunziante P 2000 J. Am. Ceram. Soc. 85 108792
[19]	Venugopalan S, Becker M M 1990 J. Chem. Phys. 93 15
[20]	Rao G V S, Rao C N R 1970 Appl. Spectrosc. 24 4
[21]	Hong F, Cheng Z X, Zhao H Y, Kimura H, Wang X L 2011 Appl. Phys. Lett. 99 092502

施引文献

[1]	Tsymbal L T, Bazaliy Y B, Derkachenko V N, Kamenev V I, Kakazei G N, Palomares F J, Wigen P E 2007 J. Appl. Phys. 101 123919
[2]	Iida R, Satoh T, Shimura T, Kuroda K, Ivanov B A, Tokunaga Y, Tokura Y 2011 Phys. Rev. B 84 064402
[3]	Hur N, Park S, Sharma P A, Ahn J S, Guha S, Cheong S W 2004 Nature 429 392
[4]	Ikeda N, Ohsumi H, Ohwada K, Ishii K, Inami T, Kakurai K, Murakami Y, Yoshii K, Mori S, Horibe Y, Kitô H 2005 Nature 436 1136
[5]	Wang J, Neaton J B, Zheng H, Nagarajan V, Ogale B, Liu B, Viehland D, Vaithyanathan V, Schlom D G, Waghmare U V, Spal-din N A, Rabe K M, Wuttig M, Ramesh R 2003 Science 299 1719
[6]	Cheng Z X, Li A H, Wang X L, Dou S X, Ozawa K, Kimura H, Zhang S J, Shrout T R 2008 J. Appl. Phys. 103 07E507
[7]	Fennie C J 2008 Phys. Rev. Lett. 100 167203
[8]	Tokunaga Y, Iguchi S, Arima T, Tokura Y 2008 Phys. Rev. Lett. 101 097205
[9]	Tokunaga Y, Taguchi Y, Arima T, Tokura Y 2012 Nature Phys. 8 838
[10]	Dzyaloshinskii I 1958 J. Phys. Chem. Solids 4 241
[11]	Moriya T 1960 Phys. Rev. 120 91
[12]	Gorodetsky G, Sharon B, Shtrikman S 1968 J. Appl. Phys. 39 1371
[13]	White R L 1969 J. Appl. Phys. 40 1061
[14]	Song G L, Zhou X H, Su J, Yang H G, Wang T X, Chang F G 2012 Acta Phys. Sin. 61 177501 (in Chinese) [宋桂林, 周晓辉, 苏键, 杨海刚, 王天兴, 常方高 2012 61 177501]
[15]	Du Y, Cheng Z X, Wang X L, Dou S X 2010 J. Appl. Phys. 107 09D908
[16]	Guptake H C, Singh M K, Tiwari L M 2002 J. Raman Spectrosc. 33 67
[17]	Venugopalan S, Dutta M, Ramdas A K, Remeika J P 1985 Phys. Rev. B 31 1490
[18]	Traversa E, Nunziante P 2000 J. Am. Ceram. Soc. 85 108792
[19]	Venugopalan S, Becker M M 1990 J. Chem. Phys. 93 15
[20]	Rao G V S, Rao C N R 1970 Appl. Spectrosc. 24 4
[21]	Hong F, Cheng Z X, Zhao H Y, Kimura H, Wang X L 2011 Appl. Phys. Lett. 99 092502

[1]	张颖, 李卓霖, 沈保根. 磁畴壁拓扑结构研究进展. , 2024, 73(1): 017504. doi: 10.7498/aps.73.20231612
[2]	王宁, 黄峰, 陈盈, 朱国锋, 苏浩斌, 郭翠霞, 王向峰. 磁场诱导的TmFeO₃单晶自旋重取向. , 2024, 73(1): 017801. doi: 10.7498/aps.73.20231322
[3]	任壮, 成龙, 谢尔盖·固瑞特斯基, 那泽亚·柳博奇科, 李江涛, 尚加敏, 谢尔盖·巴里洛, 武安华, 亚历山大·卡拉什尼科娃, 马宗伟, 周春, 盛志高. Ho_1–xY_xFeO₃单晶自旋重取向的掺杂效应与磁控效应的太赫兹光谱. , 2020, 69(20): 207802. doi: 10.7498/aps.69.20201518
[4]	方雨青, 金钻明, 陈海洋, 阮舜逸, 李炬赓, 曹世勋, 彭滟, 马国宏, 朱亦鸣. 高通量制备的Sm_xPr_1–xFeO₃晶体中反铁磁自旋模式和晶体场跃迁的太赫兹光谱. , 2020, 69(20): 209501. doi: 10.7498/aps.69.20200732
[5]	宁凯杰, 张庆礼, 周鹏宇, 杨华军, 许兰, 孙敦陆, 殷绍唐. Yb3+:Gd2SiO5晶体的结构和光谱性能. , 2012, 61(12): 128102. doi: 10.7498/aps.61.128102
[6]	张山丽, 曾繁明, 王欣桐, 李春, 王成伟, 张莹, 林海, 秦杰明, 刘景和. Cr4+:Ca2 GeO4激光晶体生长及结构表征. , 2010, 59(10): 7214-7218. doi: 10.7498/aps.59.7214
[7]	陈怡, 申江. 稀土金属间化合物RFe2Zn20-xInx的结构属性研究. , 2009, 58(13): 146-S150. doi: 10.7498/aps.58.146
[8]	汪丽莉, 熊锐, 魏伟, 胡妮, 林颖, 朱本鹏, 汤五丰, 余祖兴, 汤征, 石兢. 缺氧条件下准一维自旋梯状结构化合物(Sr1-xCax)14Cu24O41-δ的磁化率特性研究. , 2008, 57(7): 4334-4340. doi: 10.7498/aps.57.4334
[9]	郑小平, 张佩峰, 范多旺, 李发伸, 郝远. Tb0.3Dy0.7－xPrx(Fe0.9Al0.1)1.95合金的磁致伸缩、自旋重取向和穆斯堡尔谱研究. , 2007, 56(1): 535-540. doi: 10.7498/aps.56.535
[10]	王文全, 徐世峰, 徐钦英, 张文梁, 陈东风. (Nd1－xGdx)3Fe27.31Ti1.69化合物的结构和磁性. , 2006, 55(7): 3531-3535. doi: 10.7498/aps.55.3531
[11]	王英伟, 王自东, 程灏波. 新型激光晶体Yb:KY(WO4)2的结构与光谱. , 2006, 55(9): 4803-4808. doi: 10.7498/aps.55.4803
[12]	胡妮, 谢卉, 汪丽莉, 林颖, 熊锐, 余祖兴, 汤五丰, 石兢. Fe掺杂对自旋梯状化合物Sr14(Cu1－yFey)24O41的结构和电输运性质的影响. , 2006, 55(7): 3480-3487. doi: 10.7498/aps.55.3480
[13]	杨柳, 殷春浩, 焦扬, 张雷, 宋宁, 茹瑞鹏. 掺入Ni元素的LiCoO2晶体光谱结构及电子顺磁共振g因子. , 2006, 55(4): 1991-1996. doi: 10.7498/aps.55.1991
[14]	张礼杰, 雷鸣, 王宇明, 李建立, 孙彧, 刘景和. Yb3+掺杂KY(WO4)2激光晶体生长、结构与光谱分析. , 2006, 55(6): 3141-3146. doi: 10.7498/aps.55.3141
[15]	郑小平, 张佩峰, 范多旺, 李发伸, 郝远. Tb0.3Dy0.7(Fe0.9T0.1)1.95合金的结构、自旋重取向和穆斯堡尔谱. , 2006, 55(2): 879-883. doi: 10.7498/aps.55.879
[16]	郭光华, 张海贝. 化合物HoMn6Sn6的磁晶各向异性及自旋重取向相变研究. , 2005, 54(12): 5879-5883. doi: 10.7498/aps.54.5879
[17]	严成锋, 赵广军, 杭寅, 张连翰, 徐军. Ce:Lu2Si2O7闪烁晶体的结构和光谱特性. , 2005, 54(8): 3745-3748. doi: 10.7498/aps.54.3745
[18]	王文全, 闫羽, 王向群, 王学凤, 金汉民. (Nd1-xErx)3Fe273Ti17化合物的结构与磁性. , 2003, 52(3): 641-646. doi: 10.7498/aps.52.641
[19]	卢贵武, 夏海瑞, 孟宪林, 刘雪松, 杨卫兵. 掺Nd锆石类激光晶体的Raman光谱研究. , 2002, 51(2): 424-429. doi: 10.7498/aps.51.424
[20]	李刘合, 张海泉, 崔旭明, 张彦华, 夏立芳, 马欣新, 孙跃. X射线光电子能谱辅助Raman光谱分析类金刚石碳膜的结构细节. , 2001, 50(8): 1549-1554. doi: 10.7498/aps.50.1549

计量

文章访问数: 6594
PDF下载量: 620
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板