Recent research progress of two-dimensional intrinsic ferroelectrics and their multiferroic coupling

Ye Qian; Shen Yang; Yuan Ye; Zhao Yi-Feng; Duan Chun-Gang

doi:10.7498/aps.69.20201433

Abstract

Ferroelectric materials have become a research focus of condensed matter physics because of their electric polarization state which can be regulated by external field and has potential applications in sensors, optoelectronic devices and information memory devices. With the rapid development of microelectronic integration technology, electronic devices are becoming more and more miniaturized, integrated and multifunctional. Due to the size effect and interface effect, the traditional bulk ferroelectric materials are difficult to meet the requirements for this development. Therefore, low-dimensional ferroelectric materials have received extensive attention of the academic circle. In recent years, stable room temperature intrinsic two-dimensional ferroelectric materials have been successfully prepared. The prediction and design of new materials in theoretical method such as first principles calculation also promote the development of two-dimensional ferroelectric materials. At the same time, the multiferroic coupling effect of two-dimensional ferroelectricity, ferrovalley and magnetism can be used to realize the electronic valley polarization, electronic magnetic control and other regulatory mechanisms. The coupling of multiple degrees of freedom will produce strange physical properties such as optical selectivity of circular (linear) polarization between energy valleys and quantum spin Hall effect, which is of great significance for developing spintronics, valley electronics and optics. In this paper, the recent progress of theoretical and experimental research of new two-dimensional ferroelectric materials is introduced, and the applications of two-dimensional ferroelectric materials in two-dimensional ferroelectric devices such as ferroelectric tunnel junctions and ferroelectric diodes are presented. Secondly, the multiferroic coupling effect of two-dimensional electrically controlled ferroelectric valley and electronically controlled magnetism and their derived new physical phenomena and mechanisms are described. Finally, the rich physical connotation and broad application prospects of coupling two-dimensional ferroelectric materials with other physical properties are analyzed and discussed.

Keywords:

two-dimensional ferroelectric materials /
two-dimensional ferroelectric devices /
multiferroic coupling /
first-principles caculation

Authors and contacts

1.
Key Laboratory of Polarized Materials and Devices of Ministry of Education, School of Physics and Electronic Science, East China Normal University, Shanghai 200241, China
2.
Collaborative Innovation Center of Extreme Optics, Shanxi University, Taiyuan 030006, China

Corresponding author: Duan Chun-Gang, cgduan@clpm.ecnu.edu.cn

Funds: Project supported by the National Key R&D Program of China (Grant No. 2017YFA0303403), the Shanghai Science and Technology Innovation Action Plan, China (Grant No. 19JC1416700), and the National Natural Science Foundation of China (Grant No.11774092)

FullText HTML : translate this paragraph

References

[1]	Hoffman J, Pan X, Reiner J W, Walker F J, Han J P, Ahn C H, Ma T P 2010 Adv. Mater. 22 2957 Google Scholar
[2]	Lu H D, Bark C W, Ojos D E L, Alcala J, Eom C, Catalan G, Gruverman A 2012 Science 336 59 Google Scholar
[3]	Garcia V, Bibes M 2014 Nat. Commun. 5 4289 Google Scholar
[4]	Sharma P, Zhang Q, Sando D, Lei C H, Liu Y Y, Li J Y, Nagarajan V, Seidel J 2017 Sci. Adv. 3 e1700512 Google Scholar
[5]	Wu J B, Chen H Y, Yang N, Cao J, Yan X D, Liu F X, Sun Q B, Ling X, Guo J, Wang H 2020 Nat. Electron. 3 466 Google Scholar
[6]	Wang X W, Yu P, Lei Z D, Zhu C, Cao X, Liu F C, You L, Zeng Q S, Deng Y, Zhu C, Zhou J D, Fu Q D, Wang J L, Huang Y Z, Liu Z 2019 Nat. Commun. 10 3037 Google Scholar
[7]	Wang X D, Liu C S, Chen Y, Wu G J, Yan X, Huang H, Wang P, Tian B B, Hong Z C, Wang Y T, Sun S, Shen H, Lin T, Hu W D, Tang M H, Zhou P, Wang J L, Sun J L, Meng X J, Chu J H, Li Z 2017 2D Mater. 4 025036 Google Scholar
[8]	Haleoot R, Paillard C, Kaloni T P, Mehboudi M, Xu B, Bellaiche L, Barrazalopez S 2017 Phys. Rev. Lett. 118 227401 Google Scholar
[9]	Martin L W, Rappe A M 2017 Nat. Rev. Mater. 2 16087 Google Scholar
[10]	Catalan G, Lubk A, Vlooswijk A H G, Snoeck E, Magen C, Janssens A, Rispens G, Rijnders G, Blank D H A, Noheda B 2011 Nat. Mater. 10 963 Google Scholar
[11]	Sai N, Kolpak A M, Rappe A M 2005 Phys. Rev. B 74 059901 Google Scholar
[12]	Tenne D A, Turner P, Schmidt J D, Biegalski M D, Li Y L, Chen L Q, Soukiassian A, Troliermckinstry S, Schlom D G, Xi X X 2009 Phys. Rev. Lett. 103 177601 Google Scholar
[13]	Tenne D A, Bruchhausen A, Lanzillottikimura N D, Fainstein A, Katiyar R S, Cantarero A, Soukiassian A, Vaithyanathan V, Haeni J H, Tian W 2006 Science 313 1614 Google Scholar
[14]	Maksymovych P, Huijben M, Pan M, Jesse S, Balke N, Chu Y H, Chang H J, Borisevich A Y, Baddorf A P, Rijnders G 2012 Phys. Rev. B 85 014119 Google Scholar
[15]	Seidel J, Martin L W, He Q, Zhan Q, Chu Y H, Rother A, Hawkridge M E, Maksymovych P, Yu P, Gajek M 2009 Nat. Mater. 8 229 Google Scholar
[16]	Spaldin N A 2004 Science 304 1606 Google Scholar
[17]	Junquera J,Ghosez P 2003 Nature 422 506 Google Scholar
[18]	Duan C G, Sabirianov R F, Mei W N, Jaswal S S, Tsymbal E Y 2006 Nano Lett. 6 483 Google Scholar
[19]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Katsnelson M I, Grigorieva I V, Dubonos S V, Firsov A A 2005 Nature 438 197 Google Scholar
[20]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Zhang Y, Dubonos S V, Grigorieva I V, Firsov A A 2004 Science 306 666 Google Scholar
[21]	Guan Z, Hu H, Shen X W, Xiang P H, Zhong N, Chu J H, Duan C G 2020 Adv. Electron. Mater. 6 1900818 Google Scholar
[22]	Tang X, Kou L Z 2019 J. Phys. Chem. Lett. 10 6634 Google Scholar
[23]	丁宁, 董帅 2020 南通大学学报(自然科学版) 19 1 Google Scholar Ding N, Dong S 2020 Journal of Nantong University (Natural Science Edition) 19 1 Google Scholar
[24]	Wu M H, Dong S, Yao K L, Liu J M, Zeng X C 2016 Nano Lett. 16 7309 Google Scholar
[25]	Kan E J, Wu F, Deng K M, Tang W H 2013 Appl. Phys. Lett. 103 193103 Google Scholar
[26]	Wu M H, Burton J D, Tsymbal E Y, Zeng X C, Jena P 2013 Phys. Rev. B 87 081406 Google Scholar
[27]	Yang Q, Xiong W, Zhu L, Gao G Y, Wu M H 2017 J. Am. Chem. Soc. 139 11506 Google Scholar
[28]	Shirodkar S N, Waghmare U V 2014 Phys. Rev. Lett. 112 157601 Google Scholar
[29]	Yuan S G, Luo X, Chan H L, Xiao C C, Dai Y W, Xie M H, Hao J H 2019 Nat. Commun. 10 1775 Google Scholar
[30]	Belianinov A, He Q, Dziaugys A, Maksymovych P, Eliseev E A, Borisevich A Y, Morozovska A N, Banys J, Vysochanskii Y, Kalinin S V 2015 Nano Lett. 15 3808 Google Scholar
[31]	Liu F C, You L, Seyler K L, Li X, Yu P, Lin J H, Wang X W, Zhou J D, Wang H, He H Y, Pantelides S T, Zhou W, Sharma P, Xu X D, Ajayan P M, Wang J L, Liu Z 2016 Nat. Commun. 7 12357 Google Scholar
[32]	Xu B, Xiang H, Xia Y D, Jiang K, Wan X G, He J, Yin J, Liu Z G 2017 Nanoscale 9 8427 Google Scholar
[33]	Fei Z Y, Zhao W J, Palomaki T A, Sun B S, Miller M, Zhao Z Y, Yan J Q, Xu X D, Cobden D H 2018 Nature 560 336 Google Scholar
[34]	Fei R X, Kang W, Yang L 2016 Phys. Rev. Lett. 117 097601 Google Scholar
[35]	Wu M H, Zeng X C 2016 Nano Lett. 16 3236 Google Scholar
[36]	Wang H, Qian X F 2017 2D Mater. 4 015042 Google Scholar
[37]	Chang K, Liu J W, Lin H C, Wang N, Zhao K, Zhang A M, Jin F, Zhong Y, Hu X P, Duan W H, Zhang Q M, Fu L, Xue Q K, Chen X, Ji S H 2016 Science 353 274 Google Scholar
[38]	Liu C, Wan W H, Ma J, Guo W, Yao Y G 2018 Nanoscale 10 7984 Google Scholar
[39]	Xiao C C, Wang F, Yang S Y A, Lu Y H, Feng Y P, Zhang S B 2018 Adv. Funct. Mater. 28 1707383 Google Scholar
[40]	Ai H Q, Song X H, Qi S Y, Li W F, Zhao M W 2019 Nanoscale 11 1103 Google Scholar
[41]	Tan H X, Li M L, Liu H T, Liu Z R, Li Y C, Duan W H 2019 Phys. Rev. B 99 195434 Google Scholar
[42]	Ding W J, Zhu J B, Wang Z, Gao Y F, Xiao D, Gu Y, Zhang Z Y, Zhu W G 2017 Nat. Commun. 8 14956 Google Scholar
[43]	Zhou Y, Wu D, Zhu Y H, Cho Y J, He Q, Yang X, Herrera K, Chu Z D, Han Y, Downer M C, Peng H, Lai K J 2017 Nano Lett. 17 5508 Google Scholar
[44]	Cui C J, Hu W J, Yan X X, Addiego C, Gao W P, Wang Y, Wang Z, Li L Z, Cheng Y C, Li P, Zhang X X, Alshareef H N, Wu T, Zhu W G, Pan X Q, Li L J 2018 Nano Lett. 18 1253 Google Scholar
[45]	Choi T, Lee S, Choi Y J, Kiryukhin V, Cheong S W 2009 Science 324 63 Google Scholar
[46]	Wan S Y, Li Y, Li W, Mao X Y, Zhu W G, Zeng H L 2018 Nanoscale 10 14885 Google Scholar
[47]	Kohlstedt H, Pertsev N A, Contreras J R, Waser R 2005 Phys. Rev. B 72 125341 Google Scholar
[48]	Zhuravlev M Y, Sabirianov R F, Jaswal S S, Tsymbal E Y 2005 Phys. Rev. Lett. 94 246802 Google Scholar
[49]	Shen X W, Fang Y W, Tian B B, Duan C G 2019 ACS Appl. Electron. Mater. 1 1133 Google Scholar
[50]	Gao Y C, Duan C G, Tang X D, Hu Z G, Yang P X, Zhu Z Q, Chu J H 2013 J. Phys.: Condens. Matter 25 165901 Google Scholar
[51]	Neto A H C, Guinea F, Peres N M R, Novoselov K S, Geim A K 2009 Rev. Mod. Phys. 81 109 Google Scholar
[52]	Rycerz A, Tworzydlo J, Beenakker C W J 2007 Nat. Phys. 3 172 Google Scholar
[53]	Sanjose P, Prada E, Mccann E, Schomerus H 2009 Phys. Rev. Lett. 102 247204 Google Scholar
[54]	Tong W Y, Gong S J, Wan X, Duan C G 2016 Nat. Commun. 7 13612 Google Scholar
[55]	Shen X W, Tong W Y, Gong S J, Duan C G 2017 2D Mater. 5 011001 Google Scholar
[56]	Hu H, Tong W Y, Shen Y H, Duan C G 2020 J. Mater. Chem. C 8 8098 Google Scholar
[57]	Datta S, Das B 1990 Appl. Phys. Lett. 56 665 Google Scholar
[58]	Zhang X W, Liu Q H, Luo J W, Freeman A J, Zunger A 2014 Nat. Phys. 10 387 Google Scholar
[59]	Bychkov Y A, Rashba É I 1984 JETP Lett. 39 78
[60]	Picozzi S 2014 Front. Phys. 2 10 Google Scholar
[61]	You L, Liu F C, Li H S, Hu Y Z, Zhou S, Chang L, Zhou Y, Fu Q D, Yuan G L, Dong S, Fan H J, Gruverman A, Liu Z, Wang J L 2018 Adv. Mater. 30 e1803249 Google Scholar
[62]	Hou Y C, Wu C C, Yang D, Ye T, Honavar V G, van Duin A C T, Wang K, Priya S 2020 J. Appl. Phys. 128 060906 Google Scholar
[63]	Kepenekian M, Robles R, Katan C, Sapori D, Pedesseau L, Even J 2015 ACS Nano 9 11557 Google Scholar
[64]	Kim M, Im J, Freeman A J, Ihm J, Jin H 2014 PNAS 111 6900 Google Scholar
[65]	Ai H Q, Ma X K, Shao X F, Li W F, Zhao M W 2019 Phys. Rev. Mater. 3 054407 Google Scholar
[66]	Katsura H, Nagaosa N, Balatsky A V 2005 Phys. Rev. Lett. 95 057205 Google Scholar
[67]	Bhattacharjee S, Rahmedov D, Wang D, Iniguez J, Bellaiche L 2014 Phys. Rev. Lett. 112 147601 Google Scholar
[68]	Xu C S, Chen P, Tan H X, Yang Y R, Xiang H J, Bellaiche L 2020 Phys. Rev. Lett. 125 037203 Google Scholar
[69]	Cheong S, Mostovoy M 2007 Nat. Mater. 6 13 Google Scholar
[70]	Dong S, Liu J M, Cheong S W, Ren Z F 2015 Adv. Phys. 64 519 Google Scholar
[71]	Luo W, Xu K, Xiang H J 2017 Phys. Rev. B 96 235415 Google Scholar
[72]	Zhang J J, Lin L F, Zhang Y, Wu M H, Yakobson B I, Dong S 2018 J. Am. Chem. Soc. 140 9768 Google Scholar
[73]	Qi J S, Wang H, Chen X F, Qian X F 2018 Appl. Phys. Lett. 113 043102 Google Scholar
[74]	Lai Y F, Song Z G, Wan Y, Xue M Z, Wang C S, Ye Y, Dai L, Zhang Z D, Yang W Y, Du H L, Yang J B 2019 Nanoscale 11 5163 Google Scholar
[75]	Gong C, Kim E M, Wang Y, Lee G, Zhang X 2019 Nat. Commun. 10 2657 Google Scholar

Cited By

图 1 (a) CIPS晶体结构侧视图^[31]; (b) 三维层状1 T′WTe₂的结构示意图^[33]

Figure 1. (a) The side view of CuInP₂S₆ (CIPS)^[31]; (b) structure of three-dimensional 1 T′WTe₂^[33].

DownLoad: Full-Size Img PowerPoint

图 2 (a) 单层第Ⅳ主族单硫属化合物MX铁电相结构俯视图; (b) 两个等价的极性相B和B′及高对称性非极性相A的侧视图^[34]; (c) VOCl₂单层结构的俯视图及侧视图^[40]

Figure 2. (a) Top view of the structure of monolayer group-IV monochalcogenides; (b) the schematic side views of the two distorted degenerate polar structures (B and B′) and the high symmetry nonpolar phase (A)^[34]; (c) the top view along the vertical direction and side views of the VOCl₂ monolayer^[40].

DownLoad: Full-Size Img PowerPoint

图 3 (a) 层状In₂Se₃的三维晶体结构示意图; (b) 沿垂直方向的俯视图; (c)—(h) quintuple layer (QL) In₂Se₃的几种典型结构的侧视图^[42]

Figure 3. (a) Three-dimensional crystal structure of layered In₂Se₃; (b) top view of the system along the vertical direction; (c)–(h) side views of several representative structures of one quintuple layer (QL) In₂Se₃^[42].

DownLoad: Full-Size Img PowerPoint

图 4 (a) 基于α-In₂Se₃薄层铁电二极管示意图; (b) 器件的光学图像; (c), (d) 可切换的有整流特性的铁电二极管的I-V曲线^[46]

Figure 4. (a) Schematic and (b) optical image of the device; (c), (d) I-V curves of the ferroelectric diode with switchable rectifying behavior^[46].

DownLoad: Full-Size Img PowerPoint

图 5 (a) 二维铁电同质FTJ器件模型示意图; (b) 二维FTJ In∶SnSe/SnSe/Sb∶SnSe结构示意图; (c) 二维同质FTJ In∶SnSe/SnSe/Sb∶SnSe中, 系统总能随铁电位移λ变化的关系图^[49]

Figure 5. (a) Schematic diagram of a two-dimensional ferroelectric tunnel junction (2D-FTJ) device based on homostructure; (b) the schematic diagram (shaded regions) of 2D-FTJ In∶SnSe/SnSe/Sb∶SnSe; (c) asymmetric potential energy profile as a function of ferroelectric distortions in the 2D-FTJ In∶SnSe/SnSe/Sb∶SnSe^[49].

DownLoad: Full-Size Img PowerPoint

图 6 (a) 石墨烯的晶格结构及布里渊区; (b) 蜂窝晶格中的电子能带色散图^[51]; (c)—(e) 2H相TMDS单层能谷K₊与K_–附近的能带结构示意图: (c)不含SOC效应, (d)含SOC效应, (e)同时存在SOC效应与为正的交换场作用, 即对应谷极化情况^[54]

Figure 6. (a) Honeycomb lattice and its Brillouin zone; (b) electronic dispersion in the honeycomb lattice^[51]; (c)–(e) the schematic band structures at valleys K₊ and $ K_- $ of representative 2H-phase TMD monolayers: (c) without SOC effect, (d) with SOC effect and (e) with SOC effect and a positive exchange field, that is, the valley-polarized case^[54].

DownLoad: Full-Size Img PowerPoint

图 7 铁电GeSe单层(a) p_x相和(b) p_y相的能带结构; (c) p_x相和(d) p_y相GeSe单层中, 在$ \widehat{x} $和$ \widehat{y} $线偏振光激发下的复介电函数虚部ε₂; (e) 基于铁谷GeSe单层提出的电控起偏器工作原理示意图^[55]

Figure 7. The band structure of ferroelectric phase GeSe monolayer in (a) p_x and (b) p_y state; the imaginary parts of complex dielectric function ε₂ excited by linearly x-polarized light and y-polarized light of ferrovalley GeSe monolayer of (c) p_x and (d) p_y state; (e) proposed electrically tunable polarizer based on the ferrovalley GeSe monolayer^[55].

DownLoad: Full-Size Img PowerPoint

图 8 (a), (b) CuInP₂S₆/MnPS₃异质结构图; (c)—(e) 不同铁磁序和铁电序异质结的能带图; (f), (g) 异质结中左旋圆偏振光σ₊和右旋圆偏振光σ_–激发下的复介电函数虚部ε₂; (h), (i) CuInP₂S₆/MnPS₃异质结构的电控谷自由度器件^[56]

Figure 8. (a), (b) Structure configurations of CuInP₂S₆/MnPS₃ heterostructures; (c)–(e) band structures of CuInP₂S₆/MnPS₃ heterostructures; the imaginary parts of complex dielectric function ε₂ for CuInP₂S₆/MnPS₃ heterostructure with (f) downward and (g) upward ferroelectric polarization; electrical switch of valley degree in CuInP₂S₆/MnPS₃ heterostructures in (h) upward ferroelectricity and (i) downward ferroelectricity^[56].

DownLoad: Full-Size Img PowerPoint

图 9 (a) 考虑SOC作用时, 使用PBE泛函和HSE06泛函计算的单层弱铁电WO₂Cl₂的能带图; (b) [110] Dresselhaus型自旋分裂能带CBM处的能量分布图, 其中上方图对应“外”分支, 下方图对应“内”分支; (c)不同极化方向的单层WO₂Cl₂的三种自旋分量S_x, S_y和S_z在kx, ky平面内的自旋织构分布图, 能量截面位于CBM+0.2 eV处^[65]

Figure 9. (a) Electronic band structures of the WFE WO₂Cl₂ monolayer in the PBE and HSE06 approximations with SOC; (b) DFT energy profiles for the CBM outer (top) and inner (bottom) branches of the [110] Dresselhaus-type spin split bands; (c) out-of-plane and in-plane spin component distributions with different ferroelectric polarizationon the constant energy contours corresponding to a cut at 0.2 eV above the CBM^[65].

DownLoad: Full-Size Img PowerPoint

图 10 (a) 分别有向上和向下的垂直电偶极矩的In₂Se₃单层的Cr₂Ge₂Te₆/ In₂Se₃二维异质结构图; (b) Cr₂Ge₂Te₆/ In₂Se₃二维异质结构中Cr₂Ge₂Te₆的磁晶各向异性与范德瓦耳斯层间距离的关系图; (c) 接近Cr₂Ge₂Te₆的表面(Se1)和次表面(In1)原子层的自旋状态密度; (d) 由磁邻近效应引起的原子Se1和原子In1自旋磁矩随层间距的变化图^[75]

Figure 10. (a) Heterostructure side views with the In₂Se₃ ferroelectric dipole moment directed upward and downward (P_up and P_dn), respectively; (b) calculated magnetocrystalline anisotropy of Cr₂Ge₂Te₆ in the heterostructure versus the van der Waals interlayer distance; (c) projected spin density of states for the surface (Se1) and subsurface (In1) atomic layers close to Cr₂Ge₂Te₆; (d) interlayer distance dependence of the proximity-induced Se1 and In1 spin moments^[75].

DownLoad: Full-Size Img PowerPoint

map

[1]	Hoffman J, Pan X, Reiner J W, Walker F J, Han J P, Ahn C H, Ma T P 2010 Adv. Mater. 22 2957 Google Scholar
[2]	Lu H D, Bark C W, Ojos D E L, Alcala J, Eom C, Catalan G, Gruverman A 2012 Science 336 59 Google Scholar
[3]	Garcia V, Bibes M 2014 Nat. Commun. 5 4289 Google Scholar
[4]	Sharma P, Zhang Q, Sando D, Lei C H, Liu Y Y, Li J Y, Nagarajan V, Seidel J 2017 Sci. Adv. 3 e1700512 Google Scholar
[5]	Wu J B, Chen H Y, Yang N, Cao J, Yan X D, Liu F X, Sun Q B, Ling X, Guo J, Wang H 2020 Nat. Electron. 3 466 Google Scholar
[6]	Wang X W, Yu P, Lei Z D, Zhu C, Cao X, Liu F C, You L, Zeng Q S, Deng Y, Zhu C, Zhou J D, Fu Q D, Wang J L, Huang Y Z, Liu Z 2019 Nat. Commun. 10 3037 Google Scholar
[7]	Wang X D, Liu C S, Chen Y, Wu G J, Yan X, Huang H, Wang P, Tian B B, Hong Z C, Wang Y T, Sun S, Shen H, Lin T, Hu W D, Tang M H, Zhou P, Wang J L, Sun J L, Meng X J, Chu J H, Li Z 2017 2D Mater. 4 025036 Google Scholar
[8]	Haleoot R, Paillard C, Kaloni T P, Mehboudi M, Xu B, Bellaiche L, Barrazalopez S 2017 Phys. Rev. Lett. 118 227401 Google Scholar
[9]	Martin L W, Rappe A M 2017 Nat. Rev. Mater. 2 16087 Google Scholar
[10]	Catalan G, Lubk A, Vlooswijk A H G, Snoeck E, Magen C, Janssens A, Rispens G, Rijnders G, Blank D H A, Noheda B 2011 Nat. Mater. 10 963 Google Scholar
[11]	Sai N, Kolpak A M, Rappe A M 2005 Phys. Rev. B 74 059901 Google Scholar
[12]	Tenne D A, Turner P, Schmidt J D, Biegalski M D, Li Y L, Chen L Q, Soukiassian A, Troliermckinstry S, Schlom D G, Xi X X 2009 Phys. Rev. Lett. 103 177601 Google Scholar
[13]	Tenne D A, Bruchhausen A, Lanzillottikimura N D, Fainstein A, Katiyar R S, Cantarero A, Soukiassian A, Vaithyanathan V, Haeni J H, Tian W 2006 Science 313 1614 Google Scholar
[14]	Maksymovych P, Huijben M, Pan M, Jesse S, Balke N, Chu Y H, Chang H J, Borisevich A Y, Baddorf A P, Rijnders G 2012 Phys. Rev. B 85 014119 Google Scholar
[15]	Seidel J, Martin L W, He Q, Zhan Q, Chu Y H, Rother A, Hawkridge M E, Maksymovych P, Yu P, Gajek M 2009 Nat. Mater. 8 229 Google Scholar
[16]	Spaldin N A 2004 Science 304 1606 Google Scholar
[17]	Junquera J,Ghosez P 2003 Nature 422 506 Google Scholar
[18]	Duan C G, Sabirianov R F, Mei W N, Jaswal S S, Tsymbal E Y 2006 Nano Lett. 6 483 Google Scholar
[19]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Katsnelson M I, Grigorieva I V, Dubonos S V, Firsov A A 2005 Nature 438 197 Google Scholar
[20]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Zhang Y, Dubonos S V, Grigorieva I V, Firsov A A 2004 Science 306 666 Google Scholar
[21]	Guan Z, Hu H, Shen X W, Xiang P H, Zhong N, Chu J H, Duan C G 2020 Adv. Electron. Mater. 6 1900818 Google Scholar
[22]	Tang X, Kou L Z 2019 J. Phys. Chem. Lett. 10 6634 Google Scholar
[23]	丁宁, 董帅 2020 南通大学学报(自然科学版) 19 1 Google Scholar Ding N, Dong S 2020 Journal of Nantong University (Natural Science Edition) 19 1 Google Scholar
[24]	Wu M H, Dong S, Yao K L, Liu J M, Zeng X C 2016 Nano Lett. 16 7309 Google Scholar
[25]	Kan E J, Wu F, Deng K M, Tang W H 2013 Appl. Phys. Lett. 103 193103 Google Scholar
[26]	Wu M H, Burton J D, Tsymbal E Y, Zeng X C, Jena P 2013 Phys. Rev. B 87 081406 Google Scholar
[27]	Yang Q, Xiong W, Zhu L, Gao G Y, Wu M H 2017 J. Am. Chem. Soc. 139 11506 Google Scholar
[28]	Shirodkar S N, Waghmare U V 2014 Phys. Rev. Lett. 112 157601 Google Scholar
[29]	Yuan S G, Luo X, Chan H L, Xiao C C, Dai Y W, Xie M H, Hao J H 2019 Nat. Commun. 10 1775 Google Scholar
[30]	Belianinov A, He Q, Dziaugys A, Maksymovych P, Eliseev E A, Borisevich A Y, Morozovska A N, Banys J, Vysochanskii Y, Kalinin S V 2015 Nano Lett. 15 3808 Google Scholar
[31]	Liu F C, You L, Seyler K L, Li X, Yu P, Lin J H, Wang X W, Zhou J D, Wang H, He H Y, Pantelides S T, Zhou W, Sharma P, Xu X D, Ajayan P M, Wang J L, Liu Z 2016 Nat. Commun. 7 12357 Google Scholar
[32]	Xu B, Xiang H, Xia Y D, Jiang K, Wan X G, He J, Yin J, Liu Z G 2017 Nanoscale 9 8427 Google Scholar
[33]	Fei Z Y, Zhao W J, Palomaki T A, Sun B S, Miller M, Zhao Z Y, Yan J Q, Xu X D, Cobden D H 2018 Nature 560 336 Google Scholar
[34]	Fei R X, Kang W, Yang L 2016 Phys. Rev. Lett. 117 097601 Google Scholar
[35]	Wu M H, Zeng X C 2016 Nano Lett. 16 3236 Google Scholar
[36]	Wang H, Qian X F 2017 2D Mater. 4 015042 Google Scholar
[37]	Chang K, Liu J W, Lin H C, Wang N, Zhao K, Zhang A M, Jin F, Zhong Y, Hu X P, Duan W H, Zhang Q M, Fu L, Xue Q K, Chen X, Ji S H 2016 Science 353 274 Google Scholar
[38]	Liu C, Wan W H, Ma J, Guo W, Yao Y G 2018 Nanoscale 10 7984 Google Scholar
[39]	Xiao C C, Wang F, Yang S Y A, Lu Y H, Feng Y P, Zhang S B 2018 Adv. Funct. Mater. 28 1707383 Google Scholar
[40]	Ai H Q, Song X H, Qi S Y, Li W F, Zhao M W 2019 Nanoscale 11 1103 Google Scholar
[41]	Tan H X, Li M L, Liu H T, Liu Z R, Li Y C, Duan W H 2019 Phys. Rev. B 99 195434 Google Scholar
[42]	Ding W J, Zhu J B, Wang Z, Gao Y F, Xiao D, Gu Y, Zhang Z Y, Zhu W G 2017 Nat. Commun. 8 14956 Google Scholar
[43]	Zhou Y, Wu D, Zhu Y H, Cho Y J, He Q, Yang X, Herrera K, Chu Z D, Han Y, Downer M C, Peng H, Lai K J 2017 Nano Lett. 17 5508 Google Scholar
[44]	Cui C J, Hu W J, Yan X X, Addiego C, Gao W P, Wang Y, Wang Z, Li L Z, Cheng Y C, Li P, Zhang X X, Alshareef H N, Wu T, Zhu W G, Pan X Q, Li L J 2018 Nano Lett. 18 1253 Google Scholar
[45]	Choi T, Lee S, Choi Y J, Kiryukhin V, Cheong S W 2009 Science 324 63 Google Scholar
[46]	Wan S Y, Li Y, Li W, Mao X Y, Zhu W G, Zeng H L 2018 Nanoscale 10 14885 Google Scholar
[47]	Kohlstedt H, Pertsev N A, Contreras J R, Waser R 2005 Phys. Rev. B 72 125341 Google Scholar
[48]	Zhuravlev M Y, Sabirianov R F, Jaswal S S, Tsymbal E Y 2005 Phys. Rev. Lett. 94 246802 Google Scholar
[49]	Shen X W, Fang Y W, Tian B B, Duan C G 2019 ACS Appl. Electron. Mater. 1 1133 Google Scholar
[50]	Gao Y C, Duan C G, Tang X D, Hu Z G, Yang P X, Zhu Z Q, Chu J H 2013 J. Phys.: Condens. Matter 25 165901 Google Scholar
[51]	Neto A H C, Guinea F, Peres N M R, Novoselov K S, Geim A K 2009 Rev. Mod. Phys. 81 109 Google Scholar
[52]	Rycerz A, Tworzydlo J, Beenakker C W J 2007 Nat. Phys. 3 172 Google Scholar
[53]	Sanjose P, Prada E, Mccann E, Schomerus H 2009 Phys. Rev. Lett. 102 247204 Google Scholar
[54]	Tong W Y, Gong S J, Wan X, Duan C G 2016 Nat. Commun. 7 13612 Google Scholar
[55]	Shen X W, Tong W Y, Gong S J, Duan C G 2017 2D Mater. 5 011001 Google Scholar
[56]	Hu H, Tong W Y, Shen Y H, Duan C G 2020 J. Mater. Chem. C 8 8098 Google Scholar
[57]	Datta S, Das B 1990 Appl. Phys. Lett. 56 665 Google Scholar
[58]	Zhang X W, Liu Q H, Luo J W, Freeman A J, Zunger A 2014 Nat. Phys. 10 387 Google Scholar
[59]	Bychkov Y A, Rashba É I 1984 JETP Lett. 39 78
[60]	Picozzi S 2014 Front. Phys. 2 10 Google Scholar
[61]	You L, Liu F C, Li H S, Hu Y Z, Zhou S, Chang L, Zhou Y, Fu Q D, Yuan G L, Dong S, Fan H J, Gruverman A, Liu Z, Wang J L 2018 Adv. Mater. 30 e1803249 Google Scholar
[62]	Hou Y C, Wu C C, Yang D, Ye T, Honavar V G, van Duin A C T, Wang K, Priya S 2020 J. Appl. Phys. 128 060906 Google Scholar
[63]	Kepenekian M, Robles R, Katan C, Sapori D, Pedesseau L, Even J 2015 ACS Nano 9 11557 Google Scholar
[64]	Kim M, Im J, Freeman A J, Ihm J, Jin H 2014 PNAS 111 6900 Google Scholar
[65]	Ai H Q, Ma X K, Shao X F, Li W F, Zhao M W 2019 Phys. Rev. Mater. 3 054407 Google Scholar
[66]	Katsura H, Nagaosa N, Balatsky A V 2005 Phys. Rev. Lett. 95 057205 Google Scholar
[67]	Bhattacharjee S, Rahmedov D, Wang D, Iniguez J, Bellaiche L 2014 Phys. Rev. Lett. 112 147601 Google Scholar
[68]	Xu C S, Chen P, Tan H X, Yang Y R, Xiang H J, Bellaiche L 2020 Phys. Rev. Lett. 125 037203 Google Scholar
[69]	Cheong S, Mostovoy M 2007 Nat. Mater. 6 13 Google Scholar
[70]	Dong S, Liu J M, Cheong S W, Ren Z F 2015 Adv. Phys. 64 519 Google Scholar
[71]	Luo W, Xu K, Xiang H J 2017 Phys. Rev. B 96 235415 Google Scholar
[72]	Zhang J J, Lin L F, Zhang Y, Wu M H, Yakobson B I, Dong S 2018 J. Am. Chem. Soc. 140 9768 Google Scholar
[73]	Qi J S, Wang H, Chen X F, Qian X F 2018 Appl. Phys. Lett. 113 043102 Google Scholar
[74]	Lai Y F, Song Z G, Wan Y, Xue M Z, Wang C S, Ye Y, Dai L, Zhang Z D, Yang W Y, Du H L, Yang J B 2019 Nanoscale 11 5163 Google Scholar
[75]	Gong C, Kim E M, Wang Y, Lee G, Zhang X 2019 Nat. Commun. 10 2657 Google Scholar

[1]	Zhang Qiao, Tan Wei, Ning Yong-Qi, Nie Guo-Zheng, Cai Meng-qiu, Wang Jun-Nian, Zhu Hui-Ping, Zhao Yu-Qing. Prediction of Magnetic Janus Materials Based on Machine Learning and First-Principles Calculations. Acta Physica Sinica, 2024, 73(23): 230201. doi: 10.7498/aps.73.20241278
[2]	Shi Xiao-Hong, Hou Bin-Peng, Li Zhi-Shuo, Chen Jing-Jin, Shi Xiao-Wen, Zhu Zi-Zhong. Formation of oxygen vacancy clusters in Li-rich Mn-based cathode Materials of lithium-ion batteries: First-principles calculations. Acta Physica Sinica, 2023, 72(7): 078201. doi: 10.7498/aps.72.20222300
[3]	Jin Xin, Tao Lei, Zhang Yu-Yang, Pan Jin-Bo, Du Shi-Xuan. Research progress of novel properties in several van der Waals ferroelectric materials. Acta Physica Sinica, 2022, 71(12): 127305. doi: 10.7498/aps.71.20220349
[4]	Wu Hong-Fen, Feng Pan-Jun, Zhang Shuo, Liu Da-Peng, Gao Miao, Yan Xun-Wang. First-principles study of Fe atom adsorbed biphenylene monolayer. Acta Physica Sinica, 2022, 71(3): 036801. doi: 10.7498/aps.71.20211631
[5]	Wang Zhi-Qing, Yao Xiao-Ping, Shen Jie, Zhou Jing, Chen Wen, Wu Zhi. Micromechanism of ferroelectric fatigue and enhancement of fatigue resistance of lead zirconate titanate thin films. Acta Physica Sinica, 2021, 70(14): 146302. doi: 10.7498/aps.70.20202196
[6]	Liang Ting, Wang Yang-Yang, Liu Guo-Hong, Fu Wang-Yang, Wang Huai-Zhang, Chen Jing-Fei. First-principles investigations on gas adsorption properties of V-doped monolayer MoS₂. Acta Physica Sinica, 2021, 70(8): 080701. doi: 10.7498/aps.70.20202043
[7]	Liu Zi-Yuan, Pan Jin-Bo, Zhang Yu-Yang, Du Shi-Xuan. First principles calculation of two-dimensional materials at an atomic scale. Acta Physica Sinica, 2021, 70(2): 027301. doi: 10.7498/aps.70.20201636
[8]	Wang Yan, Chen Nan-Di, Yang Chen, Zeng Zhao-Yi, Hu Cui-E, Chen Xiang-Rong. Thermoelectric transport properties of two-dimensional materials XTe₂ (X = Pd, Pt) via first-principles calculations. Acta Physica Sinica, 2021, 70(11): 116301. doi: 10.7498/aps.70.20201939
[9]	. First principles study of Fe atom adsorbed biphenylene monolayer. Acta Physica Sinica, 2021, (): . doi: 10.7498/aps.70.20211631
[10]	Yan Xiao-Tong, Hou Yu-Hua, Zheng Shou-Hong, Huang You-Lin, Tao Xiao-Ma. First-principles study of effects of Ga, Ge and As doping on electrochemical properties and electronic structure of Li₂CoSiO₄ serving as cathode material for Li-ion batteries. Acta Physica Sinica, 2019, 68(18): 187101. doi: 10.7498/aps.68.20190503
[11]	Zheng Lu-Min, Zhong Shu-Ying, Xu Bo, Ouyang Chu-Ying. First-principles study of rare-earth-doped cathode materials Li₂MnO₃ in Li-ion batteries. Acta Physica Sinica, 2019, 68(13): 138201. doi: 10.7498/aps.68.20190509
[12]	Huang Bing-Quan, Zhou Tie-Ge, Wu Dao-Xiong, Zhang Zhao-Fu, Li Bai-Kui. Properties of vacancies and N-doping in monolayer g-ZnO: First-principles calculation and molecular orbital theory analysis. Acta Physica Sinica, 2019, 68(24): 246301. doi: 10.7498/aps.68.20191258
[13]	Zhang Wei, Chen Kai-Bin, Chen Zhen-Dong. First-principles study on Jahn-Teller effect in Cr monolayer film. Acta Physica Sinica, 2018, 67(23): 237301. doi: 10.7498/aps.67.20181669
[14]	Yang Ming-Yu, Yang Qian, Zhang Bo, Zhang Xu, Cai Song, Xue Yu-Long, Zhou Tie-Ge. Electronic structures, magnetic properties and spin-orbital coupling effects of aluminum nitride monolayers doped by 5d transition metal atoms: possible two-dimensional long-range magnetic orders. Acta Physica Sinica, 2017, 66(6): 063102. doi: 10.7498/aps.66.063102
[15]	Ye Hong-Jun, Wang Da-Wei, Jiang Zhi-Jun, Cheng Sheng, Wei Xiao-Yong. Ferroelectric phase transition of perovskite SnTiO3 based on the first principles. Acta Physica Sinica, 2016, 65(23): 237101. doi: 10.7498/aps.65.237101
[16]	Gao Miao, Kong Xin, Lu Zhong-Yi, Xiang Tao. First-principles study of electron-phonon coupling and superconductivity in compound Li2C2. Acta Physica Sinica, 2015, 64(21): 214701. doi: 10.7498/aps.64.214701
[17]	Liu Yue-Ying, Zhou Tie-Ge, Lu Yuan, Zuo Xu. First principles caculations of h-BN monolayer with group IA/IIA elements replacing B as impurities. Acta Physica Sinica, 2012, 61(23): 236301. doi: 10.7498/aps.61.236301
[18]	Li Xue-Mei, Han Hui-Lei, He Guang-Pu. Lattice dynamical, dielectric and thermodynamic properties of LiNH2 from first principles. Acta Physica Sinica, 2011, 60(8): 087104. doi: 10.7498/aps.60.087104
[19]	Zhang Xue-Jun, Gao Pan, Liu Qing-Ju. First-principles study on electronic structure and optical properties of anatase TiO2 codoped with nitrogen and iron. Acta Physica Sinica, 2010, 59(7): 4930-4938. doi: 10.7498/aps.59.4930
[20]	Song Qing-Gong, Jiang En-Yong, Pei Hai-Lin, Kang Jian-Hai, Guo Ying. First principles computational study on the stability of Li ion-vacancy two-dimensional ordered structures in intercalation compounds LixTiS2. Acta Physica Sinica, 2007, 56(8): 4817-4822. doi: 10.7498/aps.56.4817

Catalog

Vol. 69, Issue 21 - 2020-11-05

Metrics

Abstract views: 14896
PDF Downloads: 1382
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板