人工调控微结构压电驻极体的热稳定性和电荷动态特性

曹功勋; 张晓青; 孙转兰; 王学文; 娄可行; 夏钟福

doi:10.7498/aps.59.6514

摘要

利用表面带有周期性结构的硬质模板,通过冷压工艺将周期结构图案复制到多孔聚四氟乙烯(PTFE)薄膜表面,再经过热黏合工艺与致密氟化乙丙烯共聚物(FEP)薄膜复合,制备出了高度有序的微孔结构复合膜,并用电晕充电的方法对复合膜进行极化处理,最终获得氟聚合物复合膜压电驻极体.借助对这类复合膜压电驻极体介电谐振谱的测量,得到了材料的杨氏模量.并利用等温热老化工艺对它们的压电系数d33的热稳定性进行了考察.最后通过短路热刺激放电谱的测量和分析,讨论了该复合膜在热老化处理后的电荷动态

关键词:

Abstract

The laminated fluoroethylenepropylene (FEP) and porous polytetrafluoroethylene (PTFE) films with regular void structure are prepared by using a rigid template with a periodic-structured surface. The porous PTFE film is firstly patterned with the rigid template surface by applying force on the stack of porous PTFE film and the template, then followed by the fusion bonding process to bond the FEP and patterned porous PTFE together. The corona charging technique is used to make the laminated film piezoelectric, i.e., to become piezoelectrets. The Young’s modulus of the laminated FEP/PTFE films is determined by dielectric resonance spectra. The thermal stability of the piezoelectric d33 coefficients are characterized by measuring the decay of d33 at elevated temperatures. The charge dynamics in such FEP/PTFE piezoelectrets is investigated by analying the thermally stimulated discharge current spectra in short circuit. The results show that laminated FEP/PTFE films with very regular void structure can be made by using rigid template and fusion bonding process. The Young's modulus of such films is about 0.53 MPa. The maximum quasi-static piezoelectric d33 coefficient up to 500 pC/N is achieved. The laminated FEP/PTFE films show improved thermal stability. For example, the remnant d33value is around 22% of the initial value for the sample annealed at 150 ℃ for 5000 min. For the samples after annealing treatment, the main drift path of the detrapped charges is through the solid dielectric layer.

Keywords:

作者及机构信息

1.
同济大学物理系波耳固体物理研究所,上海 200092

基金项目: 国家自然科学基金(批准号:50873078)资助的课题.

Authors and contacts

1.
Pohl Institute of Solid State Physics, Tongji University, Shanghai 200092, China

参考文献

[1]	Bauer S, Gerhard-Multhaupt R, Sessler G M 2004 Phys. Today 57 37
[2]	Gerhard-Multhaupt R 2002 IEEE Trans. Dielectr. Insul. 9 850
[3]	Bauer S 2006 IEEE Trans. Dielectr. Insul. 13 953
[4]	Paajanen M, Lekkala J, Kirjavainen K 2000 Sen. Act. 84 95
[5]	Neugschwandtner G S, Schwdiauer R, Bauer-Gogonea S, Bauer S 2000 Appl. Phys. A: Mater. Sci. Process. 70 1
[6]	Zhang X, Hillenbrand J, Sessler G M 2006 Appl. Phys. A: Mater. Sci. Process. 84 139
[7]	Zhang X, Hillenbrand J, Sessler G M 2004 J. Phys. D: Appl. Phys. 37 2146
[8]	Hu Z, Seggern H V 2006 J. Appl. Phys. 99 024102
[9]	Zhang X Q, Huang J F, Wang F P ,Xia Z F 2008 Acta Phys. Sin. 57 1902 (in Chinese) [张晓青、黄金峰、王飞鹏、夏钟福 2008 57 1902]
[10]	Zhang X Q, Huang J F, Wang X W, Xia Z F 2009 Acta Phys. Sin. 58 3525 (in Chinese) [张晓青、黄金峰、王学文、夏钟福 2009 58 3525]
[11]	Zhang X Q, Wang X W, Cao G X, Pan D S, Xia Z F 2009 Appl. Phys. A: Mater. Sci. Process. 97 859
[12]	Zhang X Q, Huang J F, Chen J B, Wan Z M, Wang S, Xia Z F 2007 Appl. Phys. Lett. 91 182901
[13]	Zhang X Q, Hillenbrand J, Sessler G M 2007 J. Appl. Phys. 101 054114
[14]	Qiu X L, Xia Z F, An Z L, Wu X Y 2005 Acta Phys. Sin. 54 402 (in Chinese) [邱勋林、夏钟福、安振连、吴贤勇 2005 54 402]
[15]	Zhang P F, Xia Z F, Qiu X L, Wu X Y 2005 Acta Phys. Sin. 54 397 (in Chinese) [张鹏锋、夏钟福、邱勋林、吴贤勇 2005 54 397]
[16]	Wang F P, Xia Z F, Qiu X M, Lü H, Qiu X L, Shen J 2005 Acta Phys. Sin. 54 4400 (in Chinese) [王飞鹏、夏钟福、裘晓敏、吕航、邱勋林、沈军 2005 54 4400]
[17]	Bovtun V, Dring J, Wegener M, Bartusch J, Beck U, Erhard A, Borisov V 2008 Ferroelectrics 370 11
[18]	Sun Z L, Zhang X Q, Cao G X, Wang X W, Xia Z F Acta Phys. Sin. (in Chinese) [孙转兰、张晓青、曹功勋、王学文、夏钟福 ](已接受)
[19]	Wang F P, Xia Z F, Qiu X L, Shen J 2006 Acta Phys. Sin. 55 3705 (in Chinese)[王飞鹏、夏钟福、邱勋林、沈军 2006 55 3705]
[20]	Qiu X L, Xia Z F, Wang F P 2006 Acta Phys. Sin. 55 2578 (in Chinese) [邱勋林、夏钟福、王飞鹏 2006 55 2578]
[21]	Sessler G M, Hillenbrand J 1999 Appl. Phys. Lett. 75 3405
[22]	Nicolson A M 1919 AIEE Transactions 38 1467
[23]	Cady W G 1922 Phys. Rev. Lett. 19 1
[24]	Ohigashi H 1976 J. Appl. Phys. 47 949
[25]	Mellinger A 2003 IEEE Trans. Dielectr. Insul. 10 842
[26]	Zhang X, Wang X, Huang J, Xia Z 2009 J. Materials Sci. 44 2459
[27]	Altafim R A P, Qiu X, Wirges W, Gerhard R, Altafim R A C, Basso H C, Jenninger W, Wagner J 2009 J. Appl. Phys. 106 014106

施引文献

[1]	Bauer S, Gerhard-Multhaupt R, Sessler G M 2004 Phys. Today 57 37
[2]	Gerhard-Multhaupt R 2002 IEEE Trans. Dielectr. Insul. 9 850
[3]	Bauer S 2006 IEEE Trans. Dielectr. Insul. 13 953
[4]	Paajanen M, Lekkala J, Kirjavainen K 2000 Sen. Act. 84 95
[5]	Neugschwandtner G S, Schwdiauer R, Bauer-Gogonea S, Bauer S 2000 Appl. Phys. A: Mater. Sci. Process. 70 1
[6]	Zhang X, Hillenbrand J, Sessler G M 2006 Appl. Phys. A: Mater. Sci. Process. 84 139
[7]	Zhang X, Hillenbrand J, Sessler G M 2004 J. Phys. D: Appl. Phys. 37 2146
[8]	Hu Z, Seggern H V 2006 J. Appl. Phys. 99 024102
[9]	Zhang X Q, Huang J F, Wang F P ,Xia Z F 2008 Acta Phys. Sin. 57 1902 (in Chinese) [张晓青、黄金峰、王飞鹏、夏钟福 2008 57 1902]
[10]	Zhang X Q, Huang J F, Wang X W, Xia Z F 2009 Acta Phys. Sin. 58 3525 (in Chinese) [张晓青、黄金峰、王学文、夏钟福 2009 58 3525]
[11]	Zhang X Q, Wang X W, Cao G X, Pan D S, Xia Z F 2009 Appl. Phys. A: Mater. Sci. Process. 97 859
[12]	Zhang X Q, Huang J F, Chen J B, Wan Z M, Wang S, Xia Z F 2007 Appl. Phys. Lett. 91 182901
[13]	Zhang X Q, Hillenbrand J, Sessler G M 2007 J. Appl. Phys. 101 054114
[14]	Qiu X L, Xia Z F, An Z L, Wu X Y 2005 Acta Phys. Sin. 54 402 (in Chinese) [邱勋林、夏钟福、安振连、吴贤勇 2005 54 402]
[15]	Zhang P F, Xia Z F, Qiu X L, Wu X Y 2005 Acta Phys. Sin. 54 397 (in Chinese) [张鹏锋、夏钟福、邱勋林、吴贤勇 2005 54 397]
[16]	Wang F P, Xia Z F, Qiu X M, Lü H, Qiu X L, Shen J 2005 Acta Phys. Sin. 54 4400 (in Chinese) [王飞鹏、夏钟福、裘晓敏、吕航、邱勋林、沈军 2005 54 4400]
[17]	Bovtun V, Dring J, Wegener M, Bartusch J, Beck U, Erhard A, Borisov V 2008 Ferroelectrics 370 11
[18]	Sun Z L, Zhang X Q, Cao G X, Wang X W, Xia Z F Acta Phys. Sin. (in Chinese) [孙转兰、张晓青、曹功勋、王学文、夏钟福 ](已接受)
[19]	Wang F P, Xia Z F, Qiu X L, Shen J 2006 Acta Phys. Sin. 55 3705 (in Chinese)[王飞鹏、夏钟福、邱勋林、沈军 2006 55 3705]
[20]	Qiu X L, Xia Z F, Wang F P 2006 Acta Phys. Sin. 55 2578 (in Chinese) [邱勋林、夏钟福、王飞鹏 2006 55 2578]
[21]	Sessler G M, Hillenbrand J 1999 Appl. Phys. Lett. 75 3405
[22]	Nicolson A M 1919 AIEE Transactions 38 1467
[23]	Cady W G 1922 Phys. Rev. Lett. 19 1
[24]	Ohigashi H 1976 J. Appl. Phys. 47 949
[25]	Mellinger A 2003 IEEE Trans. Dielectr. Insul. 10 842
[26]	Zhang X, Wang X, Huang J, Xia Z 2009 J. Materials Sci. 44 2459
[27]	Altafim R A P, Qiu X, Wirges W, Gerhard R, Altafim R A C, Basso H C, Jenninger W, Wagner J 2009 J. Appl. Phys. 106 014106

[1]	郑鹏飞, 柳志旭, 王超, 刘卫芳. 基团替代调控无铅有机钙钛矿铁电体的极化和压电特性的第一性原理研究. , 2024, 73(12): 126202. doi: 10.7498/aps.73.20240385
[2]	安志鸿, 黄林敏, 赵锦波, 胡倩倩, 孙转兰, 郑欢, 张晓青. 面向空耦电声换能器应用的高性能FEP/PTFE复合膜压电驻极体. , 2022, 71(2): 027701. doi: 10.7498/aps.71.20211609
[3]	张冠杰, 杨豪, 张楠. 利用X射线衍射技术对压电材料本征与非本征起源探究的研究进展. , 2020, 69(12): 127711. doi: 10.7498/aps.69.20200301
[4]	郭宇琦, 潘俊星, 张进军, 孙敏娜, 王宝凤, 武海顺. 在光敏性三元聚合物混合物中构造多尺度有序图案. , 2016, 65(5): 056401. doi: 10.7498/aps.65.056401
[5]	何建平, 吕文中, 汪小红. Ba0.5Sr0.5TiO3有序构型的第一性原理研究. , 2011, 60(9): 097102. doi: 10.7498/aps.60.097102
[6]	孙转兰, 张晓青, 曹功勋, 王学文, 夏钟福. 有序结构氟聚合物压电驻极体的制备和压电性研究. , 2010, 59(7): 5061-5066. doi: 10.7498/aps.59.5061
[7]	张晓青, 黄金峰, 王学文, 夏钟福. 聚四氟乙烯和氟化乙丙烯共聚物复合膜的压电性. , 2009, 58(5): 3525-3531. doi: 10.7498/aps.58.3525
[8]	张晓青, 黄金峰, 王飞鹏, 夏钟福. 氟聚合物压电驻极体的压电性及其电荷的动态行为. , 2008, 57(3): 1902-1907. doi: 10.7498/aps.57.1902
[9]	宋庆功, 姜恩永, 裴海林, 康建海, 郭英. 插层化合物LixTiS2中Li离子-空位二维有序结构稳定性的第一性原理研究. , 2007, 56(8): 4817-4822. doi: 10.7498/aps.56.4817
[10]	张永炬, 余森江, 葛洪良, 邬良能, 崔玉建. 硅油基底表面铁薄膜的生长机理及表面有序结构. , 2006, 55(10): 5444-5450. doi: 10.7498/aps.55.5444
[11]	邱勋林, 夏钟福, 王飞鹏. 压力膨化后的热处理温度对PP蜂窝膜驻极体机电性质的影响. , 2006, 55(5): 2578-2583. doi: 10.7498/aps.55.2578
[12]	张鹏锋, 夏钟福, 邱勋林, 王飞鹏, 吴贤勇. 充电参数对聚丙烯蜂窝膜驻极体压电性的影响. , 2006, 55(2): 904-909. doi: 10.7498/aps.55.904
[13]	张永炬, 余森江. 准自由支撑铝薄膜中有序表面结构的自组织生长. , 2005, 54(10): 4867-4873. doi: 10.7498/aps.54.4867
[14]	夏阿根, 杨波, 金进生, 张亦文, 汤凡, 叶高翔. 液体基底表面金薄膜中的有序结构和自组装现象. , 2005, 54(1): 302-306. doi: 10.7498/aps.54.302
[15]	邱勋林, 夏钟福, 安振连, 吴贤勇. 热膨胀处理的聚丙烯蜂窝膜驻极体的压电性. , 2005, 54(1): 402-406. doi: 10.7498/aps.54.402
[16]	张鹏锋, 夏钟福, 邱勋林, 吴贤勇. 聚丙烯蜂窝膜驻极体压电系数的测量及压电性的改善. , 2005, 54(1): 397-401. doi: 10.7498/aps.54.397
[17]	胡隐樵. 强迫耗散系统的有序结构和系统的发展(Ⅰ)，最小熵产生原理和有序结构. , 2003, 52(6): 1379-1384. doi: 10.7498/aps.52.1379
[18]	夏钟福, 马珊珊, 朱伽倩, 邱勋林, 张冶文, Reimund Gerhard-Multhaupt, Wolfgang Kuenstler. 聚四氟乙烯多孔膜的压电活性及其稳定性. , 2003, 52(8): 2075-2080. doi: 10.7498/aps.52.2075
[19]	宋庆功, 丛选忠, 张庆军, 莫文玲, 戴占海. 六角蜂窝晶格的有序结构. , 2000, 49(10): 2011-2016. doi: 10.7498/aps.49.2011
[20]	宋庆功, 戴占海, 丛选忠, 魏环, 张庆军. 六方密堆二元合金的有序结构. , 2000, 49(11): 2201-2209. doi: 10.7498/aps.49.2201

计量

文章访问数: 8514
PDF下载量: 1020
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板