ZnO纳米棒的低温溶液法制备、光电特性研究及其在有机/无机复合电致发光中的应用

黄金昭; 李世帅; 冯秀鹏

doi:10.7498/aps.59.5839

摘要

利用水热法制备了垂直于衬底的定向生长的ZnO纳米棒,利用扫描电子显微镜及光致发光的方法对其形貌及光学特性进行了表征,利用场发射性能测试装置对ZnO纳米棒的场发射性能进行了测试.结果表明:利用水热法在较低的温度(95 ℃) 下生长了具有较好形貌和结构的ZnO纳米棒,并表现出了较好的场发射特性,当电流密度为1 μA/cm2时,开启电场是2.8 V/μm,当电场为6.4 V/μm时,电流密度可以达到0.67 mA/cm2,场增强因子为3360.稳定性测试表明,在5 h内,4.5 V/μm的电场下,其波动不超过25%.将制备的ZnO纳米棒应用到有机/无机电致发光中,其中ZnO纳米棒为电子传输层,m-MTDATA(4,4',4″-tris{N,(3-methylphenyl)-N-phenylamino}-triphenylamine) 为空穴传输层,得到了ZnO的342 nm的紫外电致发光,此发光较ZnO纳米棒光致发光的紫外发射有约40 nm的蓝移.

关键词:

Abstract

The ZnO nanorods, primarily aligned perpendicular to the substrate, have been fabricated by hydrothermal decomposition. The scanning electron microscopy and photoluminescence method were used to characterize their morphology and optical properties, respectively. The field emission properties were also studied. The results indicate that the ZnO nanorods present good morphology, structure and good field emission property. The on-set field is 2.8 V/μm at a current density of 1 μA/cm2. The emission current density can reach 0.67 mA/cm2 at 6.4 V/μm. The field emission enhancement factor is 3660. Fluctuation of the current density is less than 25% at 4.5 V/μm for 5 hours. In the organic/inorganic electroluminescence heterostructure, with the ZnO nanorods as the electron transport layer and the m-MTDATA(4,4',4″-tris{N,(3-methylphenyl)-N-phenylamino}-triphenylamine) as the hole transport layer, the ultra-violet emission of ZnO nanorods was obtained with a 40 nm blue-shift compared with the photoluminescence of the ZnO nanorods.

Keywords:

ZnO nanorods /
field emission /
hydrothermal decomposition /
organic/inorganic electroluminescence heterostructure

作者及机构信息

1.
济南大学理学院,济南 250022

基金项目: 济南大学博士基金(批准号:XBS0845),北京交通大学发光与光信息技术教育部重点实验室开放基金(批准号:2010L0101),山东省自然科学基金(批准号:Y2008A21,SZR0704),山东省教育厅基金(批准号:J08LI12)资助的课题.

Authors and contacts

1.
School of Science, University of Jinan, Jinan 250022, China

参考文献

[1]	Wang Z L 2009 Mat.Sci. Eng. R 64 33
[2]	Chang Y L, Zhang Q F, Sun H, Wu J L 2007 Acta Phys. Sin. 56 2399(in Chinese)[常艳玲、张琦锋、孙晖、吴锦雷 2007 56 2399]
[3]	Willander M, Nur O, Zhao Q X, Yang L L, Lorenz M, Cao B Q, Pérez Zúniga J, Czekalla C, Zimmermann G, Grundmann M, Bakin A, Behrends A, Al-Suleiman M, El-Shaer A, Mofor Che A, Postels B, Waag A, Boukos N, Travlos A, Kwack H S, Guinard J, Dang Si Le D 2009 Nanotechnology 20 332001
[4]	Wang J X, Sun X W, Wei A, Lei Y, Cai X P, Li C M, Dong Z L 2006 Appl. Phys. Lett. 88 233106
[5]	Lee Y J, Lloyd T M, Olson C D, Grubbs K R, Lu P, Davis J R, Voigt A J, Hsu P W J 2009 J. Phys. Chem. C 113 15778
[6]	Zhang Q F, Rong Y, Chen X X, Zhang G M, Zhang Z X, Xue Z Q, Zhang C Q, Wu J L 2006 Chinese Journal of Semiconductors 27 1225 (in Chinese) [张琦锋、戎懿、陈贤祥、张耿民、张兆祥、薛增泉、陈长琦、吴锦雷 2006 半导体学报 27 1225]
[7]	Chang M, Cao X L, Zeng H B 2009 J. Phys. Chem. C 113 15544
[8]	Wu X, Cai W, Qu F Y 2009 Acta Phys. Sin. 58 8044(in Chinese)[武祥、蔡伟、曲凤玉2009 58 8044]
[9]	Wang C, Wang F F, Fu X Q, Wang T H 2007 Chin. Phys. B16 3545
[10]	Jeong SH, Hwang HY, Lee KH, Jeong Y 2001 Appl. Phys. Lett. 78 2052
[11]	Li C, Yang Y, Sun X W, Lei W, Zhang X B, Wang B P, Wang J X, Tay B K, Ye J D, Lo G Q, Kwong D L 2007 Nanotechnology 18 135604
[12]	Hsieh YP, Chen H Y, Lin M Z, Shiu S C, Hofmann M, Chern M Y, Jia X, Yang Y J, Chang H J, Huang H M, Tseng S C, Chen L C, Chen K H, Lin C F, Liang C T, Chen Y F 2009 Nano Lett. 9 1839
[13]	Li X, Zhai F F, Liu Y, Cao M S, Wang F C, Zhang X X 2007 Chin. Phys. 16 2769
[14]	Wang Y X, zhang Q F, Sun H, Chang Y L, Wu J L 2008 Acta Phys. Sin. 57 1141 (in Chinese) [王艳新、张琦锋、孙晖、常艳玲、吴锦雷 2008 57 1141]
[15]	Sun X W, Huang J Z, Wang J X, Xu Z 2008 Nano Lett. 8 1219
[16]	Chang C C, Chang C S 2005 Solid State Commun. 135 765
[17]	Lee C J, Lee T J, Lyu S C, Zhang Y, Ruh H, Lee H J 2002 Appl. Phys. Lett. 81 3648
[18]	Suh J S, Jeong K S, Lee J S, Han I 2002 Appl. Phys. Let. 80 2392
[19]	Wei A, Sun X W, Xu C X, Dong Z L, Yu M B, Huang W 2006 Appl. Phys. Lett. 88 213102
[20]	Cheng J P, Guo R Y, Wang Q M 2004 Appl. Phys. Lett. 85 5140
[21]	Yang Y H, Wang C X, Wang B, Xu N S, Yang G W 2005 Chem. Phys. Lett. 403 248
[22]	Lu J G, Fujita S, Kawaharamura T, Nishinaka H, Kamada Y, Ohshima T, Ye Z Z, Zeng Y J, Zhang Y Z, Zhu L P, He H P, Zhao B H 2007 J. Appl. Phys. 101 083705
[23]	Nadarajah A, Word R C, Meiss J, Knenkamp R 2008 Nano Lett. 8 534

施引文献

[1]	Wang Z L 2009 Mat.Sci. Eng. R 64 33
[2]	Chang Y L, Zhang Q F, Sun H, Wu J L 2007 Acta Phys. Sin. 56 2399(in Chinese)[常艳玲、张琦锋、孙晖、吴锦雷 2007 56 2399]
[3]	Willander M, Nur O, Zhao Q X, Yang L L, Lorenz M, Cao B Q, Pérez Zúniga J, Czekalla C, Zimmermann G, Grundmann M, Bakin A, Behrends A, Al-Suleiman M, El-Shaer A, Mofor Che A, Postels B, Waag A, Boukos N, Travlos A, Kwack H S, Guinard J, Dang Si Le D 2009 Nanotechnology 20 332001
[4]	Wang J X, Sun X W, Wei A, Lei Y, Cai X P, Li C M, Dong Z L 2006 Appl. Phys. Lett. 88 233106
[5]	Lee Y J, Lloyd T M, Olson C D, Grubbs K R, Lu P, Davis J R, Voigt A J, Hsu P W J 2009 J. Phys. Chem. C 113 15778
[6]	Zhang Q F, Rong Y, Chen X X, Zhang G M, Zhang Z X, Xue Z Q, Zhang C Q, Wu J L 2006 Chinese Journal of Semiconductors 27 1225 (in Chinese) [张琦锋、戎懿、陈贤祥、张耿民、张兆祥、薛增泉、陈长琦、吴锦雷 2006 半导体学报 27 1225]
[7]	Chang M, Cao X L, Zeng H B 2009 J. Phys. Chem. C 113 15544
[8]	Wu X, Cai W, Qu F Y 2009 Acta Phys. Sin. 58 8044(in Chinese)[武祥、蔡伟、曲凤玉2009 58 8044]
[9]	Wang C, Wang F F, Fu X Q, Wang T H 2007 Chin. Phys. B16 3545
[10]	Jeong SH, Hwang HY, Lee KH, Jeong Y 2001 Appl. Phys. Lett. 78 2052
[11]	Li C, Yang Y, Sun X W, Lei W, Zhang X B, Wang B P, Wang J X, Tay B K, Ye J D, Lo G Q, Kwong D L 2007 Nanotechnology 18 135604
[12]	Hsieh YP, Chen H Y, Lin M Z, Shiu S C, Hofmann M, Chern M Y, Jia X, Yang Y J, Chang H J, Huang H M, Tseng S C, Chen L C, Chen K H, Lin C F, Liang C T, Chen Y F 2009 Nano Lett. 9 1839
[13]	Li X, Zhai F F, Liu Y, Cao M S, Wang F C, Zhang X X 2007 Chin. Phys. 16 2769
[14]	Wang Y X, zhang Q F, Sun H, Chang Y L, Wu J L 2008 Acta Phys. Sin. 57 1141 (in Chinese) [王艳新、张琦锋、孙晖、常艳玲、吴锦雷 2008 57 1141]
[15]	Sun X W, Huang J Z, Wang J X, Xu Z 2008 Nano Lett. 8 1219
[16]	Chang C C, Chang C S 2005 Solid State Commun. 135 765
[17]	Lee C J, Lee T J, Lyu S C, Zhang Y, Ruh H, Lee H J 2002 Appl. Phys. Lett. 81 3648
[18]	Suh J S, Jeong K S, Lee J S, Han I 2002 Appl. Phys. Let. 80 2392
[19]	Wei A, Sun X W, Xu C X, Dong Z L, Yu M B, Huang W 2006 Appl. Phys. Lett. 88 213102
[20]	Cheng J P, Guo R Y, Wang Q M 2004 Appl. Phys. Lett. 85 5140
[21]	Yang Y H, Wang C X, Wang B, Xu N S, Yang G W 2005 Chem. Phys. Lett. 403 248
[22]	Lu J G, Fujita S, Kawaharamura T, Nishinaka H, Kamada Y, Ohshima T, Ye Z Z, Zeng Y J, Zhang Y Z, Zhu L P, He H P, Zhao B H 2007 J. Appl. Phys. 101 083705
[23]	Nadarajah A, Word R C, Meiss J, Knenkamp R 2008 Nano Lett. 8 534

[1]	傅重源, 邢淞, 沈涛, 邰博, 董前民, 舒海波, 梁培. 水热法合成纳米花状二硫化钼及其微观结构表征. , 2015, 64(1): 016102. doi: 10.7498/aps.64.016102
[2]	王长远, 杨晓红, 马勇, 冯媛媛, 熊金龙, 王维. 水热合成ZnO：Cd纳米棒的微结构及光致发光特性. , 2014, 63(15): 157701. doi: 10.7498/aps.63.157701
[3]	胡小颖, 王淑敏, 裴艳慧, 田宏伟, 朱品文. 碳纳米片-碳纳米管复合材料的一步合成及其场发射性质研究. , 2013, 62(3): 038101. doi: 10.7498/aps.62.038101
[4]	陈先梅, 郜小勇, 张飒, 刘红涛. 醋酸锌热解温度对ZnO纳米棒的结构及光学性质的影响. , 2013, 62(4): 049102. doi: 10.7498/aps.62.049102
[5]	陈先梅, 王晓霞, 郜小勇, 赵显伟, 刘红涛, 张飒. 掺银氧化锌纳米棒的水热法制备研究. , 2013, 62(5): 056104. doi: 10.7498/aps.62.056104
[6]	张培增, 李瑞山, 谢二庆, 杨华, 王璇, 王涛, 冯有才. 电化学方法制备ZnO纳米颗粒掺杂类金刚石薄膜及其场发射性能研究. , 2012, 61(8): 088101. doi: 10.7498/aps.61.088101
[7]	王世伟, 朱明原, 钟民, 刘聪, 李瑛, 胡业旻, 金红明. 脉冲磁场对水热法制备Mn掺杂ZnO稀磁半导体的影响. , 2012, 61(19): 198103. doi: 10.7498/aps.61.198103
[8]	刘佳, 徐玲玲, 张海霖, 吕威, 朱琳, 高红, 张喜田. 一步水热法在Al掺杂ZnO纳米盘上可控自组装合成ZnO纳米棒阵列. , 2012, 61(2): 027802. doi: 10.7498/aps.61.027802
[9]	孙家跃, 曹纯, 杜海燕. NaLa(MoO4)2∶Eu3+的水热调控合成与发光特性研究. , 2011, 60(12): 127801. doi: 10.7498/aps.60.127801
[10]	闫悦, 赵谡玲, 徐征, 龚伟, 王大伟. 多环类苝四甲酸二酐插入层对ZnO纳米棒和聚合物复合太阳电池性能的影响. , 2011, 60(8): 088803. doi: 10.7498/aps.60.088803
[11]	王马华, 朱汉青, 朱光平. 水热法制备注射器样纳米氧化锌场发射特性的研究. , 2011, 60(7): 077305. doi: 10.7498/aps.60.077305
[12]	杨延宁, 张志勇, 张富春, 张威虎, 闫军锋, 翟春雪. 纳米金刚石的变温场发射. , 2010, 59(4): 2666-2671. doi: 10.7498/aps.59.2666
[13]	新梅, 曹望和. 水热法制备ZnS:Cu,Tm超细X射线发光粉. , 2010, 59(8): 5833-5838. doi: 10.7498/aps.59.5833
[14]	胡利勤, 林志贤, 郭太良, 姚亮, 王晶晶, 杨春建, 张永爱, 郑可炉. 取向和非取向In2O3纳米线的场发射研究. , 2006, 55(11): 6136-6140. doi: 10.7498/aps.55.6136
[15]	李强, 梁二军. 碳、碳氮和硼碳氮纳米管场发射性能的比较研究. , 2005, 54(12): 5931-5936. doi: 10.7498/aps.54.5931
[16]	王新庆, 王淼, 李振华, 杨兵, 王凤飞, 何丕模, 徐亚伯. 单根纳米导线场发射增强因子的计算. , 2005, 54(3): 1347-1351. doi: 10.7498/aps.54.1347
[17]	李海钧, 顾长志, 窦艳, 李俊杰. 单根准直碳纳米纤维的场发射特性. , 2004, 53(7): 2258-2262. doi: 10.7498/aps.53.2258
[18]	宋教花, 张耿民, 张兆祥, 孙明岩, 薛增泉. 多壁碳纳米管阵列场发射研究. , 2004, 53(12): 4392-4397. doi: 10.7498/aps.53.4392
[19]	张兆祥, 张耿民, 侯士敏, 张浩, 顾镇南, 刘惟敏, 赵兴钰, 薛增泉. 利用场发射显微镜研究O2对单壁碳纳米管场发射的影响. , 2003, 52(5): 1282-1286. doi: 10.7498/aps.52.1282
[20]	孙建平, 张兆祥, 侯士敏, 赵兴钰, 施祖进, 顾镇南, 刘惟敏, 薛增泉. 用场发射显微镜研究单壁碳纳米管场发射. , 2001, 50(9): 1805-1809. doi: 10.7498/aps.50.1805

计量

文章访问数: 9751
PDF下载量: 1195
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板